The manufacturing method of a polyacrylic acid ammonium salt-based water-absorbing resin comprises a polymerization step of a monomer aqueous solution having ammonium acrylate as a main component, and a drying step of a hydrous gelatinous polymer obtained, wherein the monomer concentration of the monomer aqueous solution is controlled to be 50 to 80 wt.%, and the moisture content of the water-absorbing resin is controlled to be 4 to 25 wt.%.例文帳に追加

アクリル酸アンモニウムを主成分とする単量体水溶液の重合工程と、得られた含水ゲル状重合体の乾燥工程とを含む、ポリアクリル酸アンモニウム塩系吸水性樹脂の製造方法であって、上記単量体水溶液の単量体濃度が５０〜８０重量％であり、かつ、得られる吸水性樹脂の含水率が４〜２５重量％となるように制御されることを特徴とする、ポリアクリル酸アンモニウム塩系吸水性樹脂の製造方法。 - 特許庁

In this method for producing an aqueous dispersion of a fluorine- containing copolymer by adding an emulsified solution containing a part or the whole of a mixture of two or more kinds of monomers copolymerizable with a fluoroolefin monomer to an aqueous medium in the presence of the fluoroolefin monomer and subjecting the monomers to emulsion polymerization, the composition of the monomer mixture in the emulsified solution is continuously or discontinuously changed.例文帳に追加

フルオロオレフィン単量体存在下、フルオロオレフィン単量体と共重合可能な２種類以上の単量体混合物の一部または全部を含む乳化液を、水性媒体中に添加して乳化重合させる含フッ素共重合体の水性分散液を製造する方法において、前記乳化液中の単量体混合物の組成を連続的または非連続的に変化させることを特徴とする含フッ素共重合体の水性分散液の製造方法。 - 特許庁

The curable resin solution composition for the color filter is characterized by containing an oxetane ring compound, an epoxy compound with a planar structural group in the side chain and a cationic polymerization initiator, and the color filter is characterized by having a transparent protection layer resulting from the curing of the curable resin solution composition for the color filter or by having 30-60 indentation hardness and 1.6-1.8 refractive index.例文帳に追加

本発明のカラーフィルター用硬化性樹脂溶液組成物は、オキセタン環を有する化合物と、側鎖に平面構造基を有するエポキシ化合物と、カチオン性重合開始剤とを含有することを特徴とするものであり、また、本発明のカラーフィルターは、かかるカラーフィルター用硬化性樹脂溶液組成物を硬化させてなる透明保護膜を有するものであるか、あるいは、該透明保護膜の押し込み硬度が３０〜６０、屈折率が１．６〜１．８であることを特徴とするものである。 - 特許庁

This cosmetic emulsifier is composed of a silylated peptide-silane compound copolymer composition produced by condensation polymerization of at least one kind selected from silylated peptides each having two hydroxyl groups directly combined with silicon atom with at least one kind selected from silane compounds each causing two or more hydroxyl groups directly combining with silicon atom through hydrolysis in an aqueous solution.例文帳に追加

ケイ素原子に直結する水酸基を２個有するシリル化ペプチドの１種以上と、加水分解によってケイ素原子に直結する水酸基が２個以上生じるシラン化合物の１種以上とを水溶液中で縮重合させて製造したシリル化ペプチド−シラン化合物共重合組成物で化粧品用乳化剤を構成する。 - 特許庁

This emulsion and dispersion stabilizer comprises a vinyl ester resin (A) contg. polyoxyalkylene groups, which contains 1-20 mol% polyoxyalkylene groups having 5-100 repeating unit of an oxyalkylene group and has 30-80% average saponification, 50-500 average polymerization degree and not less than 70°C clouding point of its 4 wt.% aq. solution.例文帳に追加

オキシアルキレン基の繰り返し単位が５〜１００のポリオキシアルキレン基を１〜２０モル％含有し、更に平均ケン化度が３０〜８０モル％、平均重合度が５０〜５００で、かつ、４重量％水溶液の曇点が７０℃以上であるポリオキシアルキレン基含有ビニルエステル系樹脂（Ａ）からなる乳化分散安定剤及びエマルジョン、再分散性エマルジョン粉末。 - 特許庁

This method for producing the alkali cellulose of which degree of polymerization is controlled, is provided by depolymerizing the alkali cellulose obtained by bringing the pulp in contact with an alkali solution in the presence of oxygen-containing gas flow, while measuring the supplied amount of oxygen in the supplied oxygen-containing gas flow and the discharged oxygen amount of the discharged oxygen-containing gas flow.例文帳に追加

パルプとアルカリ溶液を接触させて得られるアルカリセルロースを、酸素含有ガス流の存在下、供給される上記酸素含有ガス流中の酸素供給量と排出される上記酸素含有ガス流の酸素排出量を測定しながら解重合させる、重合度制御アルカリセルロースの製造方法を提供する。 - 特許庁

In the toner containing at least a bonding resin and >5 to <20 parts by mass of a wax based on 100 parts by mass of the bonding resin, when the polymerization conversion rate of a polymer as the bonding resin is partly different, the bonding resin is produced by adding part or the whole of the wax contained in the toner to a solution.例文帳に追加

少なくとも結着樹脂、及び結着樹脂１００質量部に対し５質量部を超え２０質量部未満のワックスを含有するトナーにおいて、該結着樹脂としての重合体の重合転化率が異なる時に、トナー中に含まれるワックスの一部または全部を溶液中に添加して製造された結着樹脂であることを特徴とする。 - 特許庁

The polishing compound for CMP preferably contain a polymer, for which the degree of polymerization is 100 to 4,000 and the K factor is 12 to 150 in grafting NVP to PVA of which the degree of saponification is 70 to 100 mol%, and the polymer is obtained by blending NVP in a PVA solution and polymerizing it, while using hydrogen peroxide, organic peroxide, or azo compound as an initiator.例文帳に追加

ＣＭＰ用研磨剤は、重合度が１００〜４０００であり、けん化度が７０〜１００ｍｏｌ％であるＰＶＡにＮＶＰがグラフトした、Ｋ値が１２〜１５０である重合体を含有することが好ましく、重合体はＰＶＡ溶液にＮＶＰを配合し、開始剤として過酸化水素、有機過酸化物又はアゾ化合物を用いて重合して得られる。 - 特許庁

To provide a method for polymerizing α-olefins wherein catalyst residues and other halogen-containing compounds are removed from a polymerization reaction product obtained by polymerizing a raw material being an α-olefin-containing liquid hydrocarbon in the presence of a halogen-containing acid catalyst not relying on a step of deactivation and separation by treatment with an aqueous treating agent such as an aqueous alkali solution.例文帳に追加

α−オレフィンを含む液状の炭化水素を原料としハロゲン含有酸触媒存在下に重合して得られる重合反応生成物から、アルカリ性水溶液等による水系の失活・分離工程に依存することなく、触媒残渣および他のハロゲン含有化合物の除去を行うα—オレフィンの重合方法を提供すること。 - 特許庁

In the cellulose acylate film produced by a solution film casting method, the cellulose acylate film is produced by processes comprising a film casting process for casting a cellulose acylate composition containing a cellulose acylate, a polymerizable group-containing monomer (A), a photothermal converting agent (IR) and a thermal polymerization initiator (I) and an infrared ray radiation process.例文帳に追加

溶液流延方法により形成されるセルロースアシレートフィルムにおいて、セルロースアシレート、重合性基含有のモノマー（Ａ）、光熱変換剤（ＩＲ）、及び熱重合開始剤（Ｉ）を含有するセルロースアシレート組成物を流延する流延工程と近赤外線照射の工程とを含む工程により作製されたことを特徴とするセルロースアシレートフィルム。 - 特許庁

The tire rubber composition contains a rubber component containing a modified natural rubber having a phosphorus content of ≤200 ppm and a diene rubber synthesized by solution polymerization, silica, and zinc oxide having an average primary particle diameter of ≤200 nm, wherein a content of the zinc oxide is 0.3-5 pts.mass relative to 100 pts.mass of the rubber component.例文帳に追加

リン含有量が２００ｐｐｍ以下の改質天然ゴム及び溶液重合で合成されたジエン系ゴムを含むゴム成分と、シリカと、平均一次粒子径が２００ｎｍ以下の酸化亜鉛とを含み、前記ゴム成分１００質量部に対して、前記酸化亜鉛の含有量が０．３〜５質量部であるタイヤ用ゴム組成物に関する。 - 特許庁

This rubber comprising a diolefin, characterized by having 1 to 22C non-polar side group saturated linear, branched or cyclic hydrocarbon groups or 6 to 22C non-polar side group aromatic hydrocarbon groups through sulfur atoms in an amount of 0.1 to 40 wt.% based on the total amount of the rubber and being prepared by a solution polymerization method.例文帳に追加

ゴムは、ジオレフィンからなり、硫黄原子を介して結合され、１〜２２個の炭素原子を有する無極性側基飽和直鎖、分岐状もしくは環状炭化水素基または６〜２２個の炭素原子を有する無極性側基芳香族炭化水素基をゴムの全量に対して０．１〜４０重量％の含量で有し、溶液重合によって調製される。 - 特許庁

The toner is produced by dispersing a toner material solution, prepared by dissolving or dispersing a toner material including a polyester-based resin in an organic solvent, in an aqueous solvent containing resin fine particles, wherein the polyester-based resin includes a polyester resin prepared by condensation polymerization of an alcohol component and a carboxylic acid component including modified rosin.例文帳に追加

トナーは、樹脂微粒子を含む水性溶媒に、ポリエステル系樹脂を含むトナー材料が有機溶媒に溶解乃至分散されたトナー材料液を分散して製造されるトナーであって、ポリエステル系樹脂がアルコール成分と、変性されたロジンを含有するカルボン酸成分とが縮重合されたポリエステル樹脂を含有することを特徴とする。 - 特許庁

Cationic polycondensate and/or diallylamine based (co)polymer are added and mixed to organic sludge, then the anionic water soluble polymer consisting of the polymer dispersion produced by a dispersion polymerization method under the presence of an ionic polymer dispersing agent in a salt aqueous solution is added, mixed and dehydrated by dehydrator.例文帳に追加

有機質汚泥に対し、カチオン性重縮合物及び／またはジアリルアミン系（共）重合体を添加、混合後、塩水溶液中でイオン性高分子分散剤を共存下させる分散重合法により製造した高分子分散液からなるアニオン性水溶性高分子を添加、混合し、脱水機で脱水することにより達成できる。 - 特許庁

To provide a preparation method for a fluorine-containing copolymer which has an appropriate melt viscosity as a molding material and a controlled molecular weight distribution ensuring the dimension stability of the molded article, in the solution polymerization of tetrafluoroethylene and a fluorine- containing vinyl ether in the presence of an inert hydrochlorofluorocarbon-based solvent and a chain transfer agent.例文帳に追加

テトラフルオロエチレンと含フッ素ビニルエーテルとをヒドロクロロフルオロカーボン系不活性溶媒および連鎖移動剤の存在下で溶液重合させるに際し、成形材料として適当な溶融粘度を有し、また成形品の寸法安定性を確保させる制御された分子量分布を有する含フッ素共重合体の製造法を提供する。 - 特許庁

The manufacturing method of the proton conductive material has a polymer compound solution preparing process dissolving a slightly water soluble polymer compound having a radical polymerization starting point in an organic solvent; and a grafting process obtaining a proton conductive material slightly soluble in water and having a proton conductive functional group by graft-polymerizing vinyl monomers having the proton conductive functional group.例文帳に追加

ラジカル重合開始点をもつ水難溶性高分子化合物を有機溶剤に溶解させた高分子化合物溶液調製工程と、プロトン伝導性官能基をもつビニル単量体をグラフト重合させ、水難溶性であって且つプロトン伝導性官能基をもつプロトン伝導性材料を得るグラフト化工程と、を有することを特徴とする。 - 特許庁

The agent for preventing influenza viral infection contains, as an active ingredient, a polyglycerin fatty acid monoester having a monoester content of not less than 50% in which the constituting fatty acid is an 8-14C saturated fatty acid or a 9-22C unsaturated fatty acid and the polymerization degree of the polyglycerin is 2-5 and is preferably provided in the form of an aqueous solution or an emulsion.例文帳に追加

モノエステル含量が５０％以上であり、構成脂肪酸の炭素数が８〜１４の飽和脂肪酸もしくは炭素数９〜２２の不飽和脂肪酸であり、かつポリグリセリンの重合度が２〜５であるポリグリセリン脂肪酸モノエステルを有効成分として含有するインフルエンザ感染防止剤であり、水溶液或いは乳化液の形態で好ましく提供される。 - 特許庁

The water stop agent for cables consists of a water absorbing resin obtained by polymerizing a monomer in an aqueous solution, consisting of 50-90 mol% of a water-soluble ethylenic unsaturated monomer containing amino groups and 10-50 mol% of acrylic acid having a degree of neutralization of 40-100 mol% with an alkali metal in the presence of a crosslinking agent and a water-soluble radial polymerization initiator.例文帳に追加

アミノ基含有水溶性エチレン性不飽和単量体５０〜９０モル％、およびアルカリ金属による中和度が４０〜１００モル％であるアクリル酸１０〜５０モル％からなる単量体水溶液を架橋剤および水溶性ラジカル重合開始剤の存在下に重合して得られる吸水性樹脂よりなるケーブル用止水剤。 - 特許庁

A poiyvinyl alcohol which is copolymerized with ≥0.1 mol% of an oxyalkylene group-containing alkyl vinyl ether and has ≥10 mol% saponification degree and ≥1.5 mPa.s viscosity in 4% aqueous solution is used as a protective colloid in emulsion polymerization of one or more vinyl-based compounds selected from an aliphatic vinyl ester, an α-olefin and a halogenated olefin.例文帳に追加

オキシアルキレン基を含有するアルキルビニルエーテルが０．１モル％以上共重合され、かつケン化度が１０モル％以上で２０℃における４％水溶液粘度が１．５ｍＰａ・ｓ以上であるポリビニルアルコールを、脂肪族ビニルエステル、αオレフィン、ハロゲン化オレフィンより選ばれた１種以上のビニル系化合物の乳化重合の際に保護コロイドとして使用する。 - 特許庁

In the preparation method of the water-soluble polymer comprising polymerizing or copolymerzing at least one water-soluble monomer as a constituent monomer, the method is characterized by selecting a substance which generates a water-soluble acidic material as a polymerization initiator, using water or a water solution of a water-miscible solvent as the solvent and polymerizing the monomer in the presence of a salt.例文帳に追加

１）水溶性のモノマーの少なくとも１種以上を構成モノマーとして重合乃至は共重合させて水溶性高分子を製造する方法において、２）重合開始剤に水溶性の酸性物質を生成する物質を選択し、３）溶媒を水乃至は水混和性溶媒の水溶液とし、４）塩の存在下重合を行う。 - 特許庁

Uniform fibers having a high graft ratio in which grafting is carried out even into the interior of the fibers can readily be produced by a series of treatments for covering and sealing the fibers and the radically polymerizable compound with a film, irradiating the sealed fibers and radically polymerizable compound with the electron beams and then conducting thermal polymerization even in a solution system where the impregnation of the fibers with the radically polymerizable compound is insufficient.例文帳に追加

ラジカル重合性化合物の繊維への含浸が不十分な溶液系においても，繊維とラジカル重合性化合物をフィルムで被覆シールし，電子線を照射した後，さらに加熱重合するという一連の処理で，繊維内部までグラフトされ，均一で，かつ高いグラフト率を有する繊維を容易に製造することができる。 - 特許庁

In the method of manufacturing a solid electrolytic capacitor, a solid electrolyte layer is formed on a valve action metal where a dielectric oxide film is formed by performing chemical oxidation polymerization of a polymerizable monomer consisting of a compound represented by general formula (1) and having a moisture content of 50-500 ppm by using a dopant/oxidant solution.例文帳に追加

誘電体酸化皮膜が形成された弁作用金属上に、下記一般式（１）で示される化合物からなり、かつ、含有水分量が５０〜５００ｐｐｍである重合性モノマーを、ドーパント兼酸化剤溶液を用いて化学酸化重合することにより固体電解質層を形成することを特徴とした固体電解コンデンサの製造方法である。 - 特許庁

To provide a process for producing an ethylene/α-olefin/non-conjugated polyene copolymer with high conversion of a non-conjugated polyene and good polymerization activity, whereby unreacted monomers and a hydrocarbon solvent can be removed from a solution containing the copolymer obtained by copolymerization using a transition metal compound catalyst in the hydrocarbon solvent without removing the residual catalyst.例文帳に追加

非共役ポリエン転化率の高く、炭化水素溶媒中、遷移金属化合物触媒を用いて共重合して得られた共重合体を含む溶液から、触媒残渣を除去することなく未反応単量体および炭化水素溶媒を除去可能なエチレン・α−オレフィン・非共役ポリエン共重合体を良好な重合活性で提供すること。 - 特許庁

The ink jet recording medium has the ink acceptance layer formed by applying the coating solution for the ink acceptance layer containing a pigment, a binder and an antifoaming agent, on a support and then drying, wherein the binder is polyvinyl alcohol having 85 to 95% of saponification degree and 2,000 to 4,000 polymerization degree and the antifoaming agent contains hydrophobic silica.例文帳に追加

支持体上に、顔料とバインダーと消泡剤とを含むインク受理層用塗工液を塗布、乾燥してなるインク受理層が形成されているインクジェット記録媒体であって、前記バインダーは、鹸化度８５〜９５％、重合度２０００以上４０００以下のポリビニルアルコールであり、前記消泡剤は疎水性シリカを含有するインクジェット記録媒体である。 - 特許庁

In the manufacturing method of the microcapsule, a water-soluble color developing agent as a core material and a water-soluble polymer aqueous solution of concentration of 15 wt.% to 30 wt.% are dispersed into organic solvent and are subjected to interfacial polymerization with a reaction agent to form a microcapsule wall film, and a hygroscopic coated film is formed on the microcapsule wall film by using hygroscopic liquid.例文帳に追加

有機溶媒中に、芯物質となる水溶性発色剤と、濃度１５重量％乃至３０重量％の水溶性高分子水溶液を分散させ、反応試薬により界面重合反応をさせてマイクロカプセル壁膜を形成し、このマイクロカプセル壁膜に吸湿性液体で吸湿性被膜を形成するマイクロカプセルの製造方法。 - 特許庁

A water-soluble polymer is produced by irradiating with light an aqueous solution of a monomer mixture containing a water-soluble acryloyl- group-containing monomer and a water-soluble methacryloyl-group-containing monomer under conditions including an irradiation intensity of 0.5-7 W/m^2 in the presence of an azoic polymerization initiator and an inorganic phosphorus compound.例文帳に追加

アゾ系重合開始剤および無機リン化合物の存在下に、アクリロイル基を有する水溶性単量体及びメタクリロイル基を有する水溶性単量体を含有する単量体混合物の水溶液に、光照射強度０．５〜７Ｗ／ｍ^2の条件下に光を照射して重合して水溶性重合体を製造する。 - 特許庁

In this method of manufacturing a solid electrolytic capacitor in which a solid-state electrolyte layer is formed by forming a conductive polymer layer 3 through chemical oxidative polymerization on a dielectric oxide film layer 2 obtained by anodizing a surface of a valve action metal 1, a solution of ammonium peroxodisulfate with pH adjusted to 6-8 is used as an oxidizer in forming the conductive polymer layer.例文帳に追加

弁作用金属１の表面を陽極酸化して得た誘電体酸化皮膜層２上に、化学酸化重合させて導電性高分子層３を形成し固体電解質層とする固体電解コンデンサの製造方法において、導電性高分子層形成で、酸化剤としてｐＨを６〜８に調整したペルオキソ二硫酸アンモニウムの溶液を用いる。 - 特許庁

Such a wiring circuit substrate is obtained by coating a metal foil with a solution obtained by preferably dissolving the polyimide obtained by the condensation polymerization of the 2,2'-dichloro-4,4',5,5'-biphenyl tetrapod carboxylic acid dianhydride and the aromatic diamine in an organic solvent, heating and drying, and forming the insulating film made of the polyimide on the metal foil.例文帳に追加

このような配線回路基板は、好ましくは、２，２’−ジクロロ−４，４’，５，５’−ビフェニルテトラカルボン酸二無水物と芳香族ジアミンとを重縮合して得られるポリイミドを有機溶媒に溶解させてなる溶液を金属箔上に塗布し、加熱乾燥して、ポリイミドからなる絶縁膜を金属箔上に形成することによって得ることができる。 - 特許庁

The method for producing the metal salt of the radically polymerizable compound having a low water content comprises heating (A) an aqueous solution of the alkali metal salt such as sodium methacrylate, potassium methacrylate, etc., the alkaline earth metal salt or the zinc salt in the presence of (B) a water-soluble polymerization inhibitor under reduced pressure to distill away water in the component (A).例文帳に追加

（Ａ）メタクリル酸ナトリウム、メタクリル酸カリウム等のアルカリ金属塩、アルカリ土類金属塩または亜鉛塩の水溶液を、（Ｂ）水溶性の重合禁止剤の存在下、減圧下で加熱して、前記（Ａ）成分中の水を留去せしめることを特徴とする、水分含有量の小さいラジカル重合性化合物の金属塩の製造方法。 - 特許庁

To provide a process of manufacturing particles prepared by granulating an oil-based polymerizable monomer in aqueous medium followed by suspension-polymerization or particles prepared by carrying out granulation in an aqueous medium using a solution where an oil-based polycondensate is dissolved into an oil-based solvent, followed by elimination of the solvent portion, wherein the particle obtained can be amorphized.例文帳に追加

水系媒体中にて油性重合性単量体を造粒後に懸濁重合してなる粒子又は油性重縮合物を油系溶剤に溶解した溶液を水系媒体中に造粒後、溶剤分を除去して得られる粒子の製造法において、得られる粒子を不定形化させることのできる製造方法を提供する。 - 特許庁

To provide a method for purifying N-isopropylacrylamide by which a polymerization inhibitor can be efficiently removed from the N-isopropylacrylamide and to provide a purification method by which an aqueous N-isopropylacrylamide solution high in purity and useful as a raw material for e.g., a temperature-sensitive hydrogen polymer.例文帳に追加

Ｎ−イソプロピルアクリルアミドに含有する重合禁止剤を効率よく、除去することができるＮ−イソプロピルアクリルアミドの精製方法を提供することを目的とし、加えて純度が高く、例えば感温性ヒドロゲル重合体原料として有用であるＮ−イソプロピルアクリルアミド水性溶液を製造することができる精製方法を提供する。 - 特許庁

The invention provides the reactive hot melt coating composition comprising a crystalline oligomer component with 10-100°C of melting point and 1-10% by mass of photo radical polymerization initiator, wherein the composition is solid or a solid solution at 20-50°C, and provides the coated wooden material having a cured coating of the coating composition.例文帳に追加

融点が１０〜１００℃の結晶性を有するオリゴマー成分及び該オリゴマー成分に対して１〜１０質量％の光ラジカル重合開始剤を含有し、２０〜５０℃で固体又は固溶体であることを特徴とする反応性ホットメルト塗料組成物及び木質基材表面に該塗料組成物の硬化塗膜を有する塗装木質基材を提供する。 - 特許庁

In the method for producing an aqueous polyvinyl alcohol solution of ≥5 mass % solid concentration by use of polyvinyl alcohol powders of which at least one kind of the powders has an average polymerization degree of ≥3,000, ≥90 mass %, based on the total mass, of the polyvinyl alcohol powder is characterized by having a particle size distribution of 0.3-1.0 μm.例文帳に追加

少なくとも１種が平均重合度３０００以上のポリビニルアルコール粉体を用いて、固形濃度５質量％以上のポリビニルアルコール水溶液を製造する製造方法において、前記ポリビニルアルコール粉体が、全質量の９０％以上が０．３〜１．０μｍの粒度分布を有することを特徴とするポリビニルアルコール水溶液の製造方法。 - 特許庁

The electrophotographic toner is obtained by a method, including a step of granulating a source material comprising a binder resin in a solution, wherein the binder resin comprises a resin obtained, by polymerizing a source monomer of a polycondensation resin and a source monomer of an addition polymerization resin in the presence of wax.例文帳に追加

結着樹脂を含有してなる原料を溶液中で粒子化する工程を含む方法により得られる電子写真用トナーであって、前記結着樹脂が、ワックスの存在下、縮重合系樹脂の原料モノマー及び付加重合系樹脂の原料モノマーを重合させることにより得られる樹脂を含有してなる電子写真用トナー。 - 特許庁

The plastic rod is obtained by polymerizing, in a rod forming mold, for example: the rare earth ion complex containing at least the one rare earth ion selected from the group of Eu^3+, Tb^3+, Yb^3+, Nd^3+, Er^3+, and Sm^3+; and a solution containing a material monomer or oligomer of the transparent resin and a polymerization initiator.例文帳に追加

このプラスチックロッドは、例えば、希土類イオンとしてＥｕ^3+、Ｔｂ^3+、Ｙｂ^3+，Ｎｄ^3+，Ｅｒ^3+およびＳｍ^3+からなる群から選択される少なくとも１つを含有する希土類イオン錯体と透明樹脂の原料モノマーもしくはオリゴマーと重合開始剤とを含む溶液をロッド形成用型内で重合することにより得ることができる。 - 特許庁

The unreacted styrene monomer in the polymerization system is controlled to ≤ a specific amount and the styrene that is suppressed its feed rate is accelerated its dissolution rate and promptly copolymerizes with the water-soluble acrylic acid to give the polymer that substantially has no styrene to styrene linked area whereby an alkali salt aqueous solution of high transparency can be smoothly produced.例文帳に追加

重合系内の未反応スチレン単量体量が特定量以下に制御されることにより、供給速度が抑制されたスチレンは水中への溶解が促進されて、水溶性のアクリル酸と素早く共重合し、ポリスチレン部のほとんどない重合体になるため、透明性が高いアルカリ塩水溶液を円滑に製造できる。 - 特許庁

To provide a method for manufacturing a solid electrolytic capacitor in which a product with both stable quality and performance can be obtained by solving problems in which a polymerization solution moves up along an insulating part to reach an anode part when the solid electrolytic layer is formed to make LC and ESR worse and an element slants when laminated owing to a partial increase in thickness.例文帳に追加

固体電解質層形成時に重合溶液が絶縁部を這い上がって陽極部に達し、ＬＣやＥＳＲが悪化すると共に素子積層時に部分的な厚み増加により素子が傾斜するという課題を解決し、品質・性能共に安定した製品が得られる固体電解コンデンサの製造方法を提供することを目的とする。 - 特許庁

In the method for producing the carboxyl group-containing polymer by polymerizing a carboxyl group-containing monomer in the presence of heavy metal ions, an aqueous solution containing a heavy metal salt and a carboxyl group-containing compound is supplied when the heavy metal salt is supplied to a polymerization system.例文帳に追加

重金属イオンの存在下でカルボキシル基含有単量体を重合するカルボキシル基含有重合体の製造方法において、重金属塩を重合系内に供給する際に、重金属塩とカルボキシル基含有化合物を含む水溶液として供給することを特徴とする、カルボキシル基含有重合体の製造方法である。 - 特許庁

In this manufacturing method of a polyamideimide resin, polymerization is carried out in a solution with water content of 0.005-0.05wt.%, and the acid component of the polyamideimide resin favorably contains one or two of the compounds from the group consisting of benzophenonetetracarboxylic acid anhydride, biphenyltetracarboxylic acid anhydride, and pyromellitic acid.例文帳に追加

水分率が０．００５〜０．０５ｗｔ％の溶液中で重合することを特徴とするポリアミドイミド樹脂の製造方法、好ましくはポリアミドイミド樹脂が酸成分にベンゾフェノンテトラカルボン酸無水物、ビフェニルテトラカルボン酸無水物、ピロメリット酸のうち１種又は２種以上を含むことを特徴とするポリアミドイミド樹脂の製造方法に関する。 - 特許庁

This method for producing a highly water-absorbable resin comprises polymerizing an aqueous monomer solution containing a monovinyl monomer consisting mainly of an at least partially neutralized unsaturated carboxylic acid, a polymerization initiator and a hypophosphorous acid compound and then impregnating the produced resin with a cross-linking agent having plural functional groups capable of reacting with carboxyl groups in a state having a water content of at least 40% to cross-link the resin.例文帳に追加

少なくとも部分的に中和された不飽和カルボン酸を主体とするモノビニルモノマー、重合開始剤及び次亜リン酸化合物を含有するモノマー水溶液を重合させ、生成した樹脂に、含水率が少なくとも４０％の状態で、カルボキシル基と反応し得る官能基を複数個有する架橋剤を含浸させて架橋反応させる。 - 特許庁

The cellulose acylate film is formed by a solution casting method comprising steps including a casting step for casting a cellulose acylate composition comprising the cellulose acylate, a monomer (A) bearing a polymerizable group, a light-heat converting agent (IR) and a thermal polymerization initiator (I) and a step for irradiation with near infrared rays.例文帳に追加

溶液流延方法により形成されるセルロースアシレートフィルムにおいて、セルロースアシレート、重合性基含有のモノマー（Ａ）、光熱変換剤（ＩＲ）、及び熱重合開始剤（Ｉ）を含有するセルロースアシレート組成物を流延する流延工程と近赤外線照射の工程とを含む工程により作製されたことを特徴とするセルロースアシレートフィルム。 - 特許庁

This method for producing a polyvinylpyrroridone from vinylpyrroridone monomer by a solution polymerization initiated with a radical by using dimethyl-2,2'-azobisisobutylate as a radical-forming compound in an aqueous medium, is provided by using a vinylpyrroridone monomer from which a basic impurity in the raw material vinylpyrroridone monomer is removed by an adsorbing agent.例文帳に追加

水性媒体中ラジカル形成化合物としてジメチル−２，２’−アゾビスイソブチレートの存在下で、ラジカルにより開始される溶液重合によりビニルピロリドンモノマーからポリビニルピロリドンを製造する方法において、原料のビニルピロリドンモノマー中の塩基性不純物を吸着剤で除去したビニルピロリドンモノマーを使用することを特徴とするポリビニルピロリドンの製造方法。 - 特許庁

To provide a method for efficiently manufacturing a high-quality microcapsule which has a narrow particle size distribution in the method for manufacturing the microcapsule having a urea resin or urea/urethane resin film by means of the interfacial polymerization method by dispersing a hydrophobic core material including polyisocyanate compound into an alkaline aqueous solution of isobutylene-maleic anhydride copolymer as a dispersant.例文帳に追加

イソブチレン−無水マレイン酸共重合体のアルカリ水溶液を分散剤として使用し、多価イソシアネート化合物を含有する疎水性芯物質を分散させ、界面重合法によりウレア樹脂あるいはウレア／ウレタン樹脂膜を有するマイクロカプセルを製造する方法において、粒径分布が狭く品質の高いマイクロカプセルの効率的な製造方法を提供すること。 - 特許庁

To provide a curable fluororesin coating composition for forming a film excellent in weatherability, contaminant adhesion preventing property, adhesion to base materials, surface hardness, etc., which is produced from a solution excellent in storing stability, containing a polymeric product obtained by polymerization without gelation even in a polymerizing system in which a hydroxyl group and a hydrolyzable group co-exist.例文帳に追加

ヒドロキシル基と加水分解性基が共存している重合系であってもゲル化を起こさずに重合をすることができ、しかも、得られる重合体生成混合液はそのままで保存安定性に優れたものであり、耐候性、汚染付着防止性、基材密着性、表面硬度などに優れた被膜を与える硬化性フッ素樹脂塗料組成物を提供する。 - 特許庁

This method for producing the inorganic fine particle-applying liquid comprising the inorganic fine particles having ≤1 μm mean particle diameter and a polyvinyl alcohol having ≥2,000 degree of polymerization is characterized by mixing an aqueous inorganic fine particle dispersion with a heated aqueous polyvinyl alcohol solution, cooling the mixed liquid and then mixing a crack-preventing agent.例文帳に追加

平均粒子径が１μｍ以下の無機微粒子と、重合度が２０００以上のポリビニルアルコールを少なくとも含有する無機微粒子塗布液の製造方法において、無機微粒子水分散液と、加熱されたポリビニルアルコール水溶液を混合し、該混合液を冷却した後、ひび割れ防止剤を混合することを特徴とする無機微粒子塗布液の製造方法。 - 特許庁