「retardation plate」に関連した英語例文の一覧と使い方(23ページ目) - Weblio英語例文検索

The negative C-plate consists of crosslinked product material between polyvinyl alcohol having polymerization degree of 2,000 to 5,000 and crosslinking agent and has a thickness ranging from 5μm to 60μm, wherein the optical axis is substantially parallel to the incident direction of normal incident light and the retardation value along the thickness direction is 60 nm or more.例文帳に追加

重合度２０００以上、５０００以下のポリビニルアルコールと架橋剤との架橋生成物からなったものであり、その厚みが５〜６０μｍであり、かつその光軸がノーマル入射光の入射方向に実質的に平行であり、またその厚み方向に沿う位相差値が６０ｎｍ以上であることを特徴とする負Ｃプレート、及び前記負Ｃプレートを備えていることを特徴とする光学補償フィルム。 - 特許庁

The optical retardation plate is manufactured by forming at least two optical anisotropic layers containing at least one kind of liquid crystalline compound on a support, and photo-polymerizing and fixing at least the two optical anisotropic layers sequentially from the substrate side, wherein the rate of polymerization of the layer closest to the support side among the optical anisotropic layers lies in the range of 10 to 90%.例文帳に追加

支持体上に少なくとも一種の液晶性化合物を含有する光学異方性層を少なくとも２層形成してなり、少なくとも２層の該光学異方性層を該支持体側から順次光重合させて固定化させることによって製造される位相差板において、前記光学異方性層のうち最も支持体側の層の重合率が１０〜９０％であることを特徴とする位相差板。 - 特許庁

To provide a method for producing an optical film which is excellent in dimensional stability, corner nonuniformity (light leakage), and flatness and can improve retardation stability when humidity fluctuates by drying the film by irradiating it with microwaves in a drying process when the film is produced, the optical film produced by the method, and a polarizing plate and a display device which are produced by using the film.例文帳に追加

本発明の目的は、光学フィルムの製造において乾燥工程でマイクロ波を照射するフィルム乾燥を行うことにより、寸法安定性、コーナームラ（光漏れ）、平面性に優れ、かつ湿度変動時のリターデーション安定性を改善出来る光学フィルムの製造方法、その製造方法によって製造された光学フィルム、それを用いた偏光板及び表示装置を提供することにある。 - 特許庁

The manufacturing method for the optical retardation plate having a transparent support, the alignment film formed of a polymer having a polymerizable group, and at least one optical anisotropic layer where a photosetting rod-type liquid crystal compound is fixed by polymerization in a state wherein it is aligned substantially horizontally to the alignment film surface includes a high-temperature light irradiating process of light irradiation within a temperature range of 60 to 130°C.例文帳に追加

透明支持体、重合性基を有するポリマーからなる配向膜、および光硬化型棒状液晶性化合物が配向膜面に対し実質的に水平に配向した状態に重合により固定された少なくとも１層の光学異方性層を有する位相差板の製造方法であって、温度６０℃以上１３０℃以下で光照射を行う高温光照射工程を含む位相差板の製造方法である。 - 特許庁