ramming refractoryとは 意味・読み方・使い方

To obtain a homogeneous construction body in a short time even if a material to be constructed is a low fluidity refractory, e.g. a plastic refractory, ramming material or the like.例文帳に追加

プラスチック耐火物、ラミング材等の流動性の低い耐火物であっても短時間で均質な施工体を得ることを課題とする。 - 特許庁

In the runner inner diameter control method of the groove type induction heating device provided for the induction furnace which stores molten iron and formed with a runner by using refractory, alumina system ramming material is used for the refractory when the molten iron is melted by charging iron scrap containing metal aluminum.例文帳に追加

溶鉄を貯蔵する誘導炉に設けられ、耐火物を用いて湯道を形成した溝型誘導加熱装置の湯道内径制御方法において、溶鉄に金属アルミニウムを含む鉄スクラップを装入して溶解するに際し、耐火物にアルミナ系ラミング材を用いる。 - 特許庁

To provide a refractory constructing method of a channel induction heating device capable of holding molten iron without breaking a sintered layer with which the molten iron is kept into contact in a sintering operation of a ramming material by power distribution to a metallic core.例文帳に追加

金属製中子への通電によるラミング材の焼結運転に際し、溶鉄が接触した焼結層を破壊することなく溶鉄を保持できる溝型誘導加熱装置の耐火物築造方法を提供する。 - 特許庁

To provide a ramming material for an induction furnace for melting cast steel or cast iron preventing defects such as the clogging of grooves due to the deposit from a molten metal bath and improving the resistance to infiltration of a molten metal to refractory.例文帳に追加

鋳鋼・鋳鉄溶解用の誘導炉において、浴場からの析出物による溝の閉塞等の不具合を防止するとともに耐火物中への浴湯の耐浸潤性を向上させることのできる誘導炉用ラミング材を提供する。 - 特許庁

The ramming material for the blast furnace, having the elastically deforming property is obtained by adding 1 to 10 mass %, expressed in terms of outer percentage, of metal fibers having lengths of 10 to 30 mm into a composition comprising 15 to 25 mass % liquid phenol resin and the balance being a refractory raw material mainly containing graphite.例文帳に追加

液状フェノール樹脂１５〜２５質量％、残部が黒鉛主体の耐火原料とした配合物に、長さ１０〜３０ｍｍの金属ファイバーを外掛け１〜１０質量％添加してなる弾性変形性を有する高炉用ラミング材である。 - 特許庁

To provide ramming material for an induction furnace which is an induction furnace for melting cast steel/cast iron and is preventing refractory buckling in initial receiving of molten metal by securing strength in an initial sintering operation and being stably used by suppressing the over sintering in use to hardly cause crack and by securing the sufficient thickness of a non-sintered layer to prevent the risk of liquid leakage.例文帳に追加

鋳鋼・鋳鉄溶解用の誘導炉において、初期の焼結運転に際し強度を確保することにより初受湯の際に耐火物挫屈を防止し、使用中の過焼結を抑制して亀裂が発生し難く安定して使用でき、充分な厚みの未焼結層を確保して溶湯漏れの危険性が低く安定して使用できる誘導炉用ラミング材を提供する。 - 特許庁