solutionizedとは 意味・読み方・使い方

For example, the carbon atoms are solutionized by corburizing treatment, etc.例文帳に追加

例えば浸炭処理等により炭素原子を固溶させる。 - 特許庁

The surface treatment layer 8 is selected among a CrN film by means of ion plating, CrN film solutionized with oxygen, a film composed of a mixture of CrN or CrN solutionized with oxygen and Cr, a DLC film, a Cr plating film, a nitrided layer or the like.例文帳に追加

表面処理層８は、イオンプレーティングによるＣｒＮ皮膜、酸素を固溶したＣｒＮ皮膜、ＣｒＮ又は酸素を固溶したＣｒＮとＣｒとの混合物からなる皮膜、ＤＬＣ皮膜、Ｃｒめっき皮膜、又は窒化層等から選択される。 - 特許庁

The Al2O3 and MgO which are not solutionized into the perovskite ceramics are uniformly dispersed at the matrix grain boundaries, by which the progression of the crack is suppressed and the mechanical strength is improved.例文帳に追加

またペロブスカイト系セラミックスに固溶しないＡｌ_2 Ｏ_3 やＭｇＯがマトリックス粒界に均一に分散することにより、亀裂の進展が抑制されて機械強度が向上する。 - 特許庁

The ornamental parts consist of austenitic stainless steel, and the hardened layers solutionized with carbon atoms are formed on the surfaces of the stainless steel.例文帳に追加

オーステナイト系ステンレス鋼からなり、該ステンレス鋼表面に炭素原子が固溶された硬化層が形成され、かつ、該硬化層表面に１２０〜２６０Åの厚さの陽極酸化被膜が形成されている。 - 特許庁

The improvement in the mechanical strength by the solid solution of the SrTiO3 occurs in the induction of the tensile stress at the grain boundaries when the SrTiO3 is solutionized to CaTiO3 in firing and the crystal particles of the sintered compact are smaller.例文帳に追加

ＳｒＴｉＯ_3 の固溶による機械強度の向上は、焼結時にＳｒＴｉＯ_3 がＣａＴｉＯ_3 に固溶する際に粒界に引っ張り応力が誘起され、焼結体の結晶粒子が小さくなることに起因する。 - 特許庁

The Ni-Sn-P based copper has the structure which is subjected to, for example, aging treatment at 375 to 570°C in a solutionized state that the copper alloy is rapidly cooled after being held at 580 to 850°C and is thereafter not subjected to a heat history above the recrystallization temperature.例文帳に追加

この合金は、例えば、５８０〜８５０℃に保持後急冷された溶体化状態で３７５〜５７０℃の時効処理を受け、その後再結晶温度以上の熱履歴を経ていない組織をもつＮｉ−Ｓｎ−Ｐ系銅合金。 - 特許庁

To provide perovskite type titanium-containing multiple oxide particles which are small in grain sizes, are narrow in a grain size distribution, having excellent dispersibility, high crystallinity and excellent electrical characteristics, contain particularly less impurities and are solutionized with atoms of an A site at an arbitrary ratio and a method for manufacturing the same.例文帳に追加

粒径が小さく粒径分布の狭い、分散性に優れ、結晶性が高く、電気特性に優れた、特に不純物が少なく、Ａサイトの原子を任意の比に固溶させたペロブスカイト型チタン含有複合酸化物粒子及びその製造方法を提供する。 - 特許庁