silver firingとは 意味・読み方・使い方

The regenerating method for the silver-containing waste glass includes: a process for crushing or pulverizing the silver-containing waste glass; and a process for obtaining silver-containing foamed glass by mixing glass chips or glass powder obtained in the previous process with a foaming agent and subjecting the resulting mixture to reduction firing.例文帳に追加

銀を含有する廃ガラスを破砕または粉砕する工程と、前記工程で得られたガラス片またはガラス粉末を、発泡剤と混合して還元焼成して銀含有発泡ガラスを得る工程と、を有する銀含有廃ガラスの再生方法。 - 特許庁

To provide a glass frit composition in which discoloring does not occur around a silver electrode when an electronic circuit board is manufactured by forming the silver electrode on the surface of a green sheet composed of the glass frit composition and firing the silver electrode with the green sheet.例文帳に追加

ガラスフリット組成物からなるグリーンシート表面に銀電極を形成し、このグリーンシートとともに銀電極を焼成して電子回路基板を製造したときに銀電極周辺に着色が生じないガラスフリット組成物の提供。 - 特許庁

The thick conductor layer 2 is formed of a metal composed mainly of silver Ag or copper Cu and formed by printing and firing metal paste.例文帳に追加

厚膜導体層２は、ＡｇまたはＣｕを主体とする金属からなり、金属ペーストを印刷し焼成することにより形成されている。 - 特許庁

A design is drawn using metal clays (gold, silver, copper or the like) 5 charged into the syringe of a metallic net 6, firing is performed by an electric furnace, and it is made into a metal, and cloisonne paints are applied to the inside of the metallized contour, and firing is performed by the electric furnace.例文帳に追加

金属製の網６にシリンジに入った金属粘土（金、銀、銅等）５を使用して下絵を描き、電気炉で焼成して金属にした輪郭の中に、七宝絵具を施し電気炉で焼成する。 - 特許庁

The conductive paste using the resultant silver particles is most suitable for high temperature firing and has decreased paste viscosity and resultant superior printability, and further, a conductive circuit after firing has high denseness characteristic and surface smoothness.例文帳に追加

得られた銀粒子を用いた導体ペーストは高温焼成用に最適であり、ペースト粘性が低減されて印刷性に優れ、さらに焼成後の導電回路が高い緻密性と表面平滑性とを有する。 - 特許庁

To reduce the shrinkage percentage of a sintered compact obtained by firing silver clay containing silver powder, and to allow the shrinkage percentage of the sintered compact to be hardly changed even if it is fired in a wide temperature range of 600 to 900°C.例文帳に追加

銀粉末を含む銀粘土を焼成した焼結体の収縮率を小さくするとともに、６００〜９００℃と広い温度範囲で焼成しても焼結体の収縮率が殆ど変化しない。 - 特許庁

To provide a silver-covered copper fine particle which can be subjected to low temperature firing, can obtain low volume resistivity and is suitable for a wiring material, and to provide a dispersed liquid thereof.例文帳に追加

低温焼成が可能で、低い体積抵抗率が得られ、配線材料用として好適な銀被覆銅微粒子及びその分散液を提供する。 - 特許庁

Generation of silver sulfide (Ag_2S) is thereby suppressed, and furthermore, firing temperature is set to 520 °C or lower to prevent coloration (yellowing) of the glass substrate.例文帳に追加

これにより硫化銀（Ａｇ_２Ｓ）の生成が抑制されるとともに、さらに焼成温度を５２０℃以下としてガラス基板の着色（黄変）を防止する。 - 特許庁