ferro-cokeとは 意味・読み方・使い方

To provide a manufacturing method for ferro-coke capable of manufacturing the ferro-coke with high strength at low cost while reducing the pulverization amount of coal, i.e., a carbon-containing substance when the ferro-coke is manufactured in an iron mill by carbonizing a molded article of the carbon-containing substance and an iron-containing substance.例文帳に追加

炭素含有物質と鉄含有物質との成型物を乾留して製鉄所内でフェロコークスを製造する際に、炭素含有物質である石炭の粉砕量を削減しながら、低コストで高強度のフェロコークスを製造できる、フェロコークスの製造方法を提供すること。 - 特許庁

The maximum temperature of the ferro coke during the carbonization is 800-900°C, preferably, 800-850°C.例文帳に追加

乾留時のフェロコークスの最高温度が８００℃以上、８５０℃以下であることが好ましい。 - 特許庁

In the method for manufacturing the ferro-coke by carbonizing the molded article of the carbon-containing substance and the iron-containing substance, the manufacturing method for the ferro-coke characterized in that a powder coke generated from a chamber oven coke manufacturing process is used as a part of the carbon-containing substance is used.例文帳に追加

炭素含有物質と鉄含有物質との成型物を乾留してフェロコークスを製造する方法であって、室炉コークス製造プロセスから発生する粉コークスを前記炭素含有物質の一部として使用することを特徴とするフェロコークスの製造方法を用いる。 - 特許庁

To provide a novel method for producing ferro coke for preventing deformation or thermal cracking of a molded product in a carbonization process and improving an original form yield on the carbonization furnace outlet side and handling strength in production of ferro coke.例文帳に追加

フェロコークスを製造するに際して、乾留工程における成型物の変形や熱割れを抑制させ、乾留炉出側での原形歩留まり、ハンドリング強度を向上させることのできる新たなフェロコークスの製造方法を提供する。 - 特許庁

To provide a method for producing ferro coke for metallurgy, wherein ferro coke having a comparatively small particle diameter and high strength can be produced while maintaining a predetermined reducibility index, by optimizing the particle size of iron ore to be used as a starting material.例文帳に追加

比較的粒径の小さいフェロコークスを製造する際に、原料となる鉄鉱石の粒度を適正化することにより、目標の還元率を維持しながら、高強度なフェロコークスを製造することのできる冶金用成型フェロコークスの製造方法を提供すること。 - 特許庁

The electric resistivity of a compact obtained by pulverizing and compacting the ferro-coke after carbonization is measured, a calibration curve of relationship of the electric resistivity of the ferro-coke and the highest arrival temperature is prepared, and the highest arrival temperature is preferably presumed using the calibration curve.例文帳に追加

乾留後のフェロコークスを粉砕して圧密化した圧密体の電気抵抗率を測定すること、フェロコークスの電気抵抗率と最高到達温度との関係の検量線を作成し、該検量線を用いて最高到達温度を推定することが好ましい。 - 特許庁

In the method for operating the blast furnace, in which the coke-layer and the ore-layer are formed while laying in the furnace by alternately charging the coke and the ore from the top part of the blast furnace; this method is particularly performed with blending the ferro-coke into the coke-layer at ≥5 mass% to the mass of the whole coke layer.例文帳に追加

高炉の炉頂からコークスと鉱石とを交互に装入することで、炉内にコークス層と鉱石層とを積層して行なう高炉操業方法であって、コークス層にフェロコークスを、コークス層全体の質量に対して５ｍａｓｓ％以上混合することを特徴とする高炉操業方法を用いる。 - 特許庁

When ferro coke is produced by carbonizing a molded material prepared by molding a molding raw material containing coal 30, an iron source raw material 31 and a binder, a carbonized molded material is sieved by a sieve 4 to separate a product ferro coke and coke powder containing metallic iron from each other, and the coke powder containing the metallic iron is used as the molding raw material of the molded material.例文帳に追加

石炭３０、鉄源原料３１およびバインダーを含む成型用原料を成型した成型物を乾留してフェロコークスを製造する際に、乾留した成型物を篩い４で篩い分けして、製品フェロコークスと金属鉄を含むコークス粉とに分離し、該金属鉄を含むコークス粉を前記成型物の成型用原料として用いることを特徴とするフェロコークスの製造方法。 - 特許庁