NZ615650B2 - Flexible shoe sole - Google Patents

Abstract

Disclosed are a sole (22) for an article of footwear and a method of forming the sole. The disclosure notes that it is important that footwear is lightweight and durable so that it maintains performance and support for a variety of activities. The sole (22) comprises a toe region (26), forefoot region (30), arch region (34) and a heel region (38). At least one of the toe region (26), arch region (34) and heel region (38) comprises at least one pliable fibre reinforced layer. The forefoot region (30) comprises at least one rigid fibre-reinforced layer interposed with at least one playable fibre reinforced layer. on (30), arch region (34) and a heel region (38). At least one of the toe region (26), arch region (34) and heel region (38) comprises at least one pliable fibre reinforced layer. The forefoot region (30) comprises at least one rigid fibre-reinforced layer interposed with at least one playable fibre reinforced layer.

Description

/030308 FLEXIBLE SHOE SOLE CROSS REFERENCE TO RELATED ATIONS The present application claims the benefit ofUS. Provisional Application No. 61/467,807, filed March 25, 2011, the entire contents of which are hereby incorporated herein by this reference.

FIELD OF THE INVENTION This disclosure relates generally to a sole for footwear and, more particularly, to a composite element for footwear and a method for making the same.

BACKGROUND People need different amounts of t for their footwear depending on their characteristics, such as weight and gait, and upon the intended use of the footwear. For example, in some situations, such as during cross-training, it may be beneficial to have udinal and lateral support in the ar. Alternatively, in some situations, such as sprinting, it may be beneficial to have udinal support, but not lateral t.

In addition to providing footwear that meets a wearer’s support needs, the footwear needs to provide maximum performance and maintain comfort, efficiently transferring energy and providing flexibility. Furthermore, footwear needs to be lightweight and durable. For example, a bicyclist needs footwear that provides adequate t in the area surrounding the ball of the foot to reduce foot fatigue and provide flexibility both while bicycling and when nted from the bicycle. Additionally, the footwear needs to be lightweight and have the ability to flex according to the flexure of the wearer’s foot.

Thus, there is a need for a sole support system that provides a wearer with the d flexure characteristics while maintaining the desired level of mance and support.

SUMMARY These and other needs are addressed by the various s, embodiments, and configurations of the present disclosure. This disclosure relates generally to footwear, more particularly to a footwear sole, and even more particularly to a footwear composite element and a method of manufacturing the same.

Embodiments of the present disclosure generally relate to footwear utilizing a composite element with tuned rigidity. In one embodiment, an article of ar includes a sole attached to a shoe upper. Some embodiments of the invention are a midsole, an outsole or an innersole of an article of footwear, comprising a composite element of the invention. Another embodiment of the invention is an article of footwear sing a midsole, an outsole or an innersole sing a composite element of the invention.

Another embodiment ofthe invention is an article of footwear comprising a midsole, an e and an innersole, each sing a composite element of the ion.

In one embodiment, the first portion is positioned in a first region of a composite element, and the second portion is positioned in a , different region of the ite t. In another embodiment, the first portion and the second portion are at least lly disposed within the same region of the composite element. In one embodiment, a composite element comprises a toe region, a forefoot region, an arch region, a heel region, or any combination thereof. In one embodiment, a composite element includes a first portion having a first rigidity and a second portion having a second rigidity that is ent than the first rigidity. The first n and the second portion of the composite element may be formed in various shapes. For example, in one embodiment, the first portion and/or the second portion is circular, gular, triangular, or u-shaped when viewed from a al viewpoint. Further, the first portion and/or the second portion may be formed in various sizes. For example, in one embodiment, the first portion and/or the second portion extend approximately a full width of a sole. In another embodiment, a more rigid portion extends a partial width of a shoe sole. In this embodiment, a less rigid portion may surround the sides of the more rigid portion when viewed from a proximal viewpoint. In yet another embodiment, the first portion has a different thickness than the second portion. Moreover, the first portion and/or the second portion may be positioned in various regions within a composite element.

In one embodiment, a composite element es a deformable n and a substantially non-deformable portion. In one embodiment, the able portion comprises at least one fiber-reinforced layer, and the ntially non-deformable portion comprises at least one fiber-reinforced layer. In one embodiment, the deformable portion comprises a different number of layers than the substantially non-deformable portion. In one embodiment, the deformable portion and the substantially non-deformable portion each comprise a plurality of fiber-reinforced layers configured to provide a footwear sole with the desired flexure characteristics according to the characteristics of the wearer and the intended use. The orientation, the shape, the thickness, and/or the number of layers, for example, of each portion may be altered to provide the desired flexure characteristics for that portion of the composite element.

WO 35007 In one embodiment, a composite t has at least one deformable toe region, arch region, and heel region having a first plurality of fiber-reinforced layers, and a substantially non-deformable ot region having a second plurality of fiber—reinforced layers. The forefoot region lly is positioned between the toe region and the arch region, and the arch region generally is positioned between the forefoot region and the heel region. The second plurality of fiber-reinforced layers may have a greater number of layers than the first plurality of fiber-reinforced layers. The first and second pluralities of fiber-reinforced layers may form the composite element.

In one embodiment, an outsole may include at least one lug protruding ly from the outsole. The lug(s) may be an integral component of the outsole, or, alternatively, the lug(s) may be a separate ent attached to the outsole. In addition, the position and composition of the lug(s) may vary. In yet another embodiment, an outsole may include a cleat attachment void, cut or drilled into the outsole to accommodate the attachment of a cleat.

In another ment, a method of manufacturing a composite element is provided. The method comprises: providing one or more sole prepreg layers, each sole layer having a forefoot region and at least one of a toe, arch and heel , wherein the forefoot region is positioned between the toe and arch region and the arch region is located between the forefoot and heel s; providing one or more forefoot prepreg layers; positioning, in a first mold, the one or more sole prepreg layers and the one or more forefoot layers one on top of another to form a first assembly having each of the forefoot prepreg layers oned about the forefoot region of the one or more sole g layers; and applying one or both of heat and pressure to the first assembly to form a composite.

Additionally, the method may further comprise molding the composite element with an outsole element to form an outsole, a midsole element to form a midsole, and an innersole element to form an innersole. Moreover, the method may comprise g the sole to a shoe upper.

The foregoing and other ives, features, and advantages of embodiments of the disclosure will be more y understood upon consideration of the following detailed description, taken in conjunction with the accompanying drawings.

The preceding is a simplified summary to provide an understanding of some aspects of the disclosure. This y is neither an extensive nor exhaustive overview of various embodiments of the present disclosure. It is intended neither to identify key or critical elements of the disclosure nor to delineate the scope of the disclosure but to 2012/030308 present selected ts of the disclosure in a simplified form as an introduction to the more ed description presented below. As will be appreciated, other embodiments are possible utilizing, alone or in combination, one or more of the features set forth above or described in detail below.

BRIEF DESCRIPTION OF THE DRAWINGS The accompanying drawings are incorporated into and form a part of the specification to illustrate several examples. These drawings, together with the description, explain the principles of various embodiments of the present sure. The drawings simply illustrate preferred and alternative es of how various embodiments can be made and used and are not to be construed as limiting the claimed subject matter to only the illustrated and described examples.

Fig. l is a side elevation View of an e of footwear; Fig. 2 is a side elevation View of one embodiment of an outsole; Fig. 3 is a top plan view ofthe outsole ofFig. 2; Fig. 4 is a bottom plan View of the outsole of Fig. 2; Fig. 5 is a top plan View of one embodiment of a composite element; Fig. 6 is a bottom plan View of the composite element of Fig. 5; Fig. 7 is a cross-sectional view of the composite element of Fig. 5 taken along line A-A of Fig. 5; Fig. 8 is an exploded cross-sectional view of the composite element of Fig. 5 taken along line A-A of Fig. 5; Fig. 9 is a top plan view of another embodiment of a composite element; Fig. 10 is a top plan view of one ment of a fiber—reinforced layer that may be utilized to form a composite element; Fig. ll is a top plan view of one embodiment of a first fiber-reinforced layer associated with a second fiber-reinforced layer that may be utilized to form a composite element; Fig. 12 is a top plan view of one embodiment of a fiber—reinforced layer including a woven fabric that may be utilized to form a composite t; Fig. 13 is a top plan view of one embodiment of a first woven fabric fiber- reinforced layer associated with a second woven fabric fiber-reinforced layer that may be ed to form a composite t; and Figure 14 is a flow diagram of a method ofmanufacturing a composite element according to one embodiment ofthe present disclosure. r features and advantages will become apparent from the following, more detailed, description of some embodiments of the disclosure, as illustrated by the gs referenced below.

ED PTION As used herein, the term “a” or “an” entity refers to one or more of that entity. As such, the terms “a” (or “an”), “one or more” and “at least one” can be used hangeably herein. It is also to be noted that the terms “comprising”, “including”, and “having” can be used interchangeably.

As used herein, “at least one”, “one or more”, and r” are open—ended expressions that are both conjunctive and disjunctive in operation. For example, each of the sions “at least one of A, B and C”, “at least one of A, B, or C”, “one or more of A, B, and C”, “one or more ofA, B, or C” and “A, B, and/or C” means A alone, B alone, C alone, A and B together, A and C together, B and C together, or A, B and C together.

As used herein, the term “longitudinal” refers to a direction extending a length of a footwear component. For example, the longitudinal direction may extend from a heel region of a footwear ent to a toe region of the footwear component. Also, as used herein, the term “lateral” refers to a direction extending a width of a footwear component.

Further, as used herein, the term “vertical” refers to a ion generally perpendicular to the longitudinal and the lateral direction.

As used herein, the term “proximal” refers to a position that is closer to a portion of a foot when an article of footwear is worn. The term “distal” refers to a position that is further from a portion of a foot when an article of footwear is worn. Each of these directional terms may be applied to individual portions of a footwear component.

As used , the term, “fiber” refers to at least one of the ing list: single- walled carbon—nanotubes, multi-walled carbon nanotubes, graphene nanoribbons, carbon- fibers, metal fibers, glass fibers, rayon fibers, silk fibers, nylon fibers, olefin fibers, acrylic fibers, polyester fibers, and aramid fibers.

As used herein, the term, “innersole” refers to a removable portion of the sole of an article of footwear, which is inserted into the article of footwear from the opening in the upper and which is designed to provide support to the wearer’s foot, depending upon the wearer’s anatomy and the intended use of the article of footwear.

As used herein, the term “lug” refers to a ion either integral to the outsole or attached to the outsole that aids in providing traction for the wearer of an article of footwear.

As used herein, the term, “midsole” refers to that portion of the sole of an article of footwear sandwiched between the innersole and the outsole, to which is attached the outsole.

As used herein, the term, “outsole” refers to that portion of the sole of an article of footwear that is furthest from the upper.

As used herein, the term, eric material,” refers to one or more of vinyl , s, polyolefins, polystyrenes, polyvinyls, polyacrylics, lo-olefms, polydienes, polyoxides, polyesthers, polyacetals, polysulfides, polythioesters, polyamides, polythioamides, polyurethanes, polythiourethanes, polyureas, polythioureas, polyimides, polythioimides, polyanhydrides, polythianhydrides, polycarbonates, polythiocarbonates, polyimines, polysiloxanes, polysilanes, polyphosphazenes, polyketones, polythioketones, polysulfones, polysulfoxides, polysulfonates, polysulfoamides, polyphylenes, and combinations and/or mixtures thereof.

As used herein, the term, “prepreg layer” refers to a layer of polymeric material that has previously been impregnated with fibers.

As used herein, the term, “resin,” refers to a polymeric material that is a homopolymer, copolymer, polymer alloy or a combination thereofFig. l is a side elevation View of an article of footwear, lly referred to as a shoe 2. As illustrated, the shoe 2 comprises a shoe upper 6 attached to a sole 10. The upper 6 generally encloses the foot and can comprise any upper now known or later developed in the art. The sole 10 may include, but is not limited to, an innersole, a e, and/or an outsole.

Figs. 2-14 depict specific ments of the present invention. Figs. 2—4 illustrate embodiments of a composite element integrally formed with an outsole element to form an outsole. Figs. 5-9 illustrate ments of a composite element that may be associated with both left and right forms of a sole designed to fit a man, a woman, or both.

Embodiments may be associated with soles having a shoe size according to any international shoe size ation. Embodiments may be associated with soles attached to a wide range of athletic footwear, including but not limited to g shoes, tennis shoes, basketball shoes, cross-training shoes, weightlifting shoes, bicycling shoes, track , soccer shoes, football shoes, roller skates, clap skates and other ice skates, Nordic skiing boots, downhill skiing boots, and snowboard boots, for example. In addition, ments may be associated with soles attached to a wide range of non-athletic footwear, including but not limited to work boots, sandals, loafers, and dress shoes.

Accordingly, embodiments of the present invention apply to footwear generally. Figs. 10— 13 illustrate embodiments of a fiber—reinforced layer(s) that may be utilized to form a composite t. Figure 14 rates one embodiment of a method of manufacturing a composite element.

Referring now to Figs. 2-4, embodiments of a composite element 14 joined to an outsole element 18 to form an outsole 22 are provided. As illustrated, the outsole 22 is divided into four general s: a toe region 26 that generally corresponds with a wearer’s toes, a forefoot region 30 that generally corresponds with a wearer’s metatarsal bones and the joint between the rsal bones and the phalanges, an arch region 34 that generally corresponds with a wearer’s foot arch, and a heel region 38 that generally corresponds with a wearer’s foot heel. As illustrated, the forefoot region 30 is positioned between the toe region 26 and the arch region 34, and the arch region 34 is positioned between the forefoot region 30 and heel region 38. The depicted regions are not ed to demarcate precise areas of the ite element 14, the outsole element 18, or the outsole 22. Instead, the regions are intended to define general areas that aid in the following discussion.

As rated, the ite t 14 and the outsole t 18 have been contoured to lly conform to the shape of a foot. Accordingly, the composite element 14 and/or the outsole element 18 may have a raised arch. Additionally, the composite element 14 and/or the outsole element 18 may have a raised peripheral area that extends around the sides of a foot. Further, the composite element 14 and/or the outsole element 18 may have a depression for receiving a heel. In some embodiments, the composite element 14 may be integrally formed with the outsole element 18, such as in Figs. 2—4, to provide additional stiffness. In other embodiments, the composite element 14 may be formed as a separate article and connected to the outsole element 18 using known methods of attachment, such as adhesives, molding, stitching, mechanical ers, and the like. In addition, the composite element 14 may be connected to the bottom surface of a midsole such that the ite element 14 is visible and, in some instances, accessible from the bottom of the article of footwear.

The composite element 14 shown in Figs. 2—4 includes portions with different rigidities. For example, the composite element 14 includes a more rigid portion 42 associated with the forefoot region 30 of the composite element 14 and a less rigid portion 46 associated with the toe region 26, the forefoot region 30, the arch region 34, and the heel region 38 of the composite element 14. The more rigid portion 42 can be formed, for example, in s shapes and thicknesses to tune the flexure characteristics of the more rigid portion 42 with the wearer’s characteristics and the ed use of the footwear.

The depicted more rigid portion 42 is formed in the shape of a shield when viewed from a distal viewpoint. Alternative shapes include, but are not limited to, circular, triangular, rectangular, trapezoidal, and combinations thereof. As shown in Fig. 2, the more rigid portion 42 has a greater thickness than the less rigid portion 46. In Fig. 2, the added thickness generally des distally from the composite element 14. However, in alternative embodiments, the more rigid portion 42 may include a thickness that protrudes proximally from a less rigid portion 46 of the composite element 14 or protrudes proximally and distally from a less rigid portion 46 of the ite element 14. In some embodiments, a more rigid portion 42 may have the same thickness as a less rigid n 46. In some embodiments, the more rigid portion 42 may be substantially rigid and substantially non—deformable.

In Figs. 2-4, the size, shape, and thickness of the regions of the composite element 14 in the less rigid n 46 of the composite element 14 is adjusted to vary the rigidity of the regions. For example, the altered size and shape of the toe region 26 in Fig. 4 provides a different rigidity, including torsional and/or bending, in the toe region 26 as compared to the other regions of the less rigid portion 46 of the composite element 14. In one embodiment, the less rigid n 46 may be deformable. In another embodiment, the less rigid portion 46 may be deformable by torsional and/or shear stresses.

As illustrated in Fig. 2, the outsole element 18 may contain one or more lugs 50 extending distally from the outsole element 18. The one or more lugs 50 may be an al ent of the outsole element 18, or, alternatively, the one or more lugs 50 may be a separate piece attached to the outsole t 18. Additionally, the position and composition of the one or more lugs 50 may vary depending on the type of footwear that the outsole element 18 will be incorporated into. For example, the one or more lugs 50 may be composed of a polymeric al. onally, the ric material of the one or more lugs 50 may differ from the polymeric material of the outsole element 18 when the one or more lugs is attached to rather than an integral component of the outsole element 18.

In n embodiments, the outsole element 18 is a polymeric material, comprising one or more of a homopolymer, copolymer, polymer alloy or a combination thereof, and n the polymeric material comprises one or more of Vinyl esters, s, polyolefins, polystyrenes, polyvinyls, polyacrylics, polyhalo-oleflns, polydienes, polyoxides, polyesthers, polyacetals, polysulfides, polythioesters, polyamides, polythioamides, ethanes, polythiourethanes, polyureas, polythioureas, polyimides, polythioimides, polyanhydrides, polythianhydrides, polycarbonates, polythiocarbonates, polyimines, polysiloxanes, polysilanes, polyphosphazenes, polyketones, polythioketones, polysulfones, polysulfoxides, lfonates, polysulfoamides, polyphylenes, and combinations and/or mixtures f.

The ite element 14 and the outsole element 18 in Figs. 2-4 can include several cleat attachment voids. For example, in the forefoot region 30 two slots 54 are provided and adapted to accommodate a bicycle pedal cleat. In this configuration, a more rigid portion 42 of the forefoot region provides a stiff interaction point to transfer energy from the outsole 22 to a bicycle pedal. onally, a cleat attachment void may be ed in one or both of the toe region 26 and the heel region 38. For example, in Figs. 2-4, apertures 58 are provided in the toe region 26 and the heel region 38. While the attachment voids are illustrated with reference to a bicycling shoe, it can be iated that the location and configuration of one ation of the attachment voids will vary depending on the type of shoe. For example, a Nordic ski shoe can have a cleat attachment void ent from a bicycling shoe. It can be further appreciated that the shoe may not include a cleat attachment void. Additionally, a second plurality of fiber- reinforced layers may be added to the toe and heel region of composite element 14 to provide extra rigidity to the areas surrounding a cleat attachment void.

Further, as depicted in Fig. 3, an outsole 22 may include one or more depressed areas surrounding the proximal side of a cleat attachment void. The illustrated depressed areas 62 surround the slots 54 formed in the forefoot region 30 and the apertures 58 formed in the toe region 26. The depressed area 62 surrounding the slots 54 can be ioned to accommodate a bicycling cleat mounting plate, and the depressed area 62 surrounding the apertures 58 can be dimensioned to accommodate ng plates for other types of cleats.

Referring now to Fig. 5, a composite element 14 is depicted and divided into four general s: a toe region 26 that generally corresponds with a wearer’s toes, a forefoot region 30 that generally corresponds with a wearer’s foot front sole, an arch region 34 that lly corresponds with a wearer’s foot arch, and a heel region 38 that generally corresponds with a ’s foot heel. As illustrated, the forefoot region 30 is positioned between the toe region 26 and the arch region 34, and the arch region 34 is positioned between the forefoot region 30 and the heel region 38. The depicted regions are not intended to demarcate precise areas of the composite element 14.

WO 35007 According to n embodiments, the ite t 14 may not include all of the ted regions. Rather, the ite element 14 may include a toe region 26, a forefoot region 30, an arch region 34, or a heel region 38, dually or in any combination thereof. For example, in Fig. 9, the composite element 14 has a toe region 26, a forefoot region 30, and an arch region 34; however, the composite element 14 does not have a heel region 38. Additionally, the regions may vary in size and shape. For example, in Fig. 9, the toe region 26 is shaped in the form of a strip, rather than the l curve-shape of a toe portion of a sole. Adjusting the size and shape of the various regions varies the rigidity of the regions. For example, the d size and shape of the toe region 26 in Fig. 9 allows more torsional and/or bending deformation than the toe region 26 and heel region 38 shown in Fig. 5.

Figs. 7-8 illustrate embodiments of a composite element 14 having a more rigid portion 42, which may be substantially rigid and non-deformable, and at least one less rigid portion 46, which may be able. As illustrated, the more rigid portion 42 is oned in the forefoot region 30, whereas the less rigid portion 46 is positioned in one or more of the toe region 26, the arch region 34, and the heel region 38. In Fig. 8, the less rigid portion 46 is comprised of at least one fiber-reinforced layer 66 in the toe region 26, the arch region 34, and/or the heel region 38. The at least one fiber-reinforced layer 66 of the less rigid portion 46, as depicted in Fig. 8, may be configured to deform in response to normal wear as well as shear and torsional stresses, or any combination thereof. For example, where only moderate lateral, or transverse, loads are encountered, the at least one fiber-reinforced layer 66 of the less rigid portion 46 may have minimal stiffness, thereby increasing the flexibility of the less rigid portion 46 of the composite element 14, as shown in Fig. 8. Alternatively, where large lateral loads are encountered, the at least one fiber- reinforced layer 66 of the less rigid portion 46, as depicted in Fig. 8, may have increased stiffness.

The more rigid portion 42 of the forefoot region 30 may include at least one fiber- reinforced layer 66 and at least one additional fiber-reinforced layer 70 to increase the stiffness of the forefoot region 30, as shown in Fig. 8. The additional stiffness improves energy and/or power transfer. For example, in a bicycling shoe, as in Fig. 7, a more rigid portion 42 may be positioned in the forefoot region 30 to se energy and/or power transfer from the rider to the pedal. As illustrated, at least one additional fiber-reinforced layer 70 may be interposed with the at least one fiber—reinforced layer 66. In one embodiment, a more rigid portion 42 of the forefoot region 30 provides maximum energy 2012/030308 and/or power transfer while the less rigid portion 46 of the toe region 26, the arch region 34, and the heel region 38 provides flexibility. This varying rigidity in s regions of a sole is particularly useful for many athletic and other shoes that need to transfer energy and/or power efficiently and/or need to provide protection and/or comfort to specific areas of a wearer’s foot. It can be appreciated that, the number and the ng configuration, including orientation, of the fiber-reinforced layers 66 and 70, as depicted in Fig. 8, may be altered as desired. For example, the flexure characteristics of composite element 14 may be altered by varying the number of einforced layers 66 and 70, the configuration and thickness of each layer 66 and 70, and the ation of each layer 66 and 70. In this manner, the ite element 14 is adapted to the characteristics of the wearer and the intended use.

In one embodiment, the at least one fiber—reinforced layer 66 has from about one to about four fiber-reinforced layers 66. As discussed above, depending on the configuration, the composite element 14 might not extend to or comprise all regions.

Accordingly, in some configurations, the toe region 26, the forefoot region 30, the arch region 34, and the heel region 38, or any combination thereof, will not have a fiber- rced layer.

Another factor affecting the flexure characteristics of the ite element 14 is the configuration and thickness of each fiber-reinforced layer. In certain embodiments, each fiber—reinforced layer comprises a resin ent and a fiber—containing component. The resin component may include one or more of a homopolymer, copolymer, polymer alloy or a combination thereof, and wherein the polymeric material comprises one or more of vinyl esters, epoxies, polyolefins, polystyrenes, polyvinyls, polyacrylics, polyhalo-olefins, polydienes, polyoxides, polyesthers, polyacetals, polysulfides, polythioesters, ides, polythioamides, polyurethanes, polythiourethanes, polyureas, polythioureas, polyimides, polythioimides, polyanhydrides, polythianhydrides, polycarbonates, polythiocarbonates, polyimines, polysiloxanes, polysilanes, polyphosphazenes, polyketones, polythioketones, polysulfones, polysulfoxides, polysulfonates, polysulfoamides, polyphylenes, and combinations and/or mixtures thereof. The fiber-containing component may include -walled carbon- bes, multi-walled carbon nanotubes, graphene nanoribbons, carbon—fibers, glass fibers, rayon fibers, silk fibers, metal fibers, nylon fibers, olefin fibers, acrylic fibers, polyester fibers, aramid fibers, and ations thereof. 2012/030308 The fiber-containing component and the resin, alone or together, can determine the final rigidity of the composite. The fiber-containing component may contain fibers that are randomly oriented, unidirectionally oriented, layered, woven, or any combination thereof.

Fig. 10 illustrates one embodiment of a fiber-reinforced layer 66 having a plurality of fibers 74 randomly oriented with respect to a line A-A. The random orientation of the fibers 74 can provide one or both longitudinal and transverse stiffness.

Fig. 11 illustrates one embodiment of a composite element 14 having at least one fiber-reinforced layer 66 and at least one additional einforced layer 70. A plurality of fibers 74 within the at least one fiber-reinforced layer 66 is substantially oriented at a first angle with t to a longitudinal axis A—A that extends from the toe region to the heel region of the composite element 14. A plurality of fibers 74 within the at least one additional fiber-reinforced layer 70 is substantially oriented at a second, differing angle with respect to the longitudinal axis A-A. By altering the orientation of the rcing fibers 74 in different fiber-reinforced layers, each fiber-reinforced layer may have one or both of a different directional flexure teristic and stiffness. By using multiple fiber reinforced layers, the longitudinal and transverse flexure characteristics of the composite element can be tailored for a specific activity in which the human wearer is expected to engage.

As indicated, the stiffness of a composite t 14 can be ed to specific applications by varying the number of the fiber-reinforced layers, as well as the angular orientations of the layers. Further, the flexure characteristics of the at least one fiber- reinforced layer 66 and the at least one additional fiber-reinforced layer 70 may customize the localized regional ess to accommodate a specific application. The particular fiexure characteristic to be incorporated in any given article of footwear may be tuned to the wearer and/or activity the wearer is to be engaged in.

Thus, in one embodiment, a fiber—reinforced layer 66 is ed at a first predetermined angle with respect to another einforced layer 66, and an onal fiber-reinforced layer 70 is oriented at a second predetermined angle with respect to a fiber-reinforced layer 66 and/or another additional fiber-reinforced layer 70. The layer(s) of the at least one einforced layer 66 and the at least one additional fiber-reinforced layer 70 can be arranged at various offsets corresponding to rotations relative to the longitudinal axis A-A. For example, in one specific ment, the layer(s) of the at least one fiber-reinforced layer 66 is arranged at offsets corresponding to rotations of approximately 10 degrees from the longitudinal axis A-A, and the s) of the at least one additional fiber-reinforced layer 70 is arranged at offsets corresponding to rotations of approximately 45 degrees from the longitudinal axis A-A. Accordingly, the fiber- reinforced layers can provide varying degrees of ess or atively flexibility in a specific region of a sole. One of skill in the art will appreciate that individual layers 66 and 70 may be oriented from 0 degrees to 180 degrees, in either a clockwise or counterclockwise direction, from the longitudinal axis A-A, depending on the desired flexure characteristics.

Fig. 12 illustrates one embodiment of a einforced layer 66 ing a woven fabric 78. The alignment and weave of the woven fabric 78 can provide strength and stiffness properties in certain portions of the composite element 14 and flexibility in other portions of the composite element 14. These variations in strength and stiffness between the portions of the composite element may be lished by varying the number of layers of fabric within the einforced layer(s), or the orientation of the layers of fabric within the fiber-reinforced layer(s). Preferably, the strength and stiffness properties are about the forefoot region 30 and the flexibility is about one or more of the toe region 26, the arch region 34, and the heel region 38. The woven fabric 78 may e at least one fiber selected from single-walled carbon-nanotubes, multi—walled carbon bes, graphene nanoribbons, carbon-fibers, metal fibers, glass fibers, rayon fibers, silk fibers, nylon fibers, olefin fibers, acrylic fibers, polyester fibers, and aramid fibers. The fibers making up the fabric may be d to at least one polymeric material.

The polymeric material may comprise at least one of a vinyl ester, epoxy, polyolefin, polydiene, polyoxide, polyesther, polyamide, polythioamide, polyurethane, ide, polythioimide, polycarbonate, polythiocarbonate, polyketone, and polythioketone.

Fig. 13 illustrates embodiments of a composite element 14 having at least one fiber-reinforced layer 66 and at least one additional fiber-reinforced layer 70. The fiber- reinforced layers may contain a woven fabric 78 having a bias. The woven fabric 78 within the at least one fiber-reinforced layer 66 can be substantially oriented at a first angle with respect to a longitudinal axis A-A. The woven fabric 78 within the at least one additional fiber-reinforced layers 70 can be substantially oriented at a second angle with respect to the longitudinal axis A-A. As sed above in relation to Fig. ll, the orientation of the woven fabric within a fiber-reinforced layer, the number of fiber- reinforced layers, and the orientation of the fiber-reinforced layers may be adjusted for a particular wearer and intended use. This includes adjusting the relative flexure teristics of a substantially deformable portion and a ntially non-deformable portion of the composite element 14.

Fig. 14 illustrates a method 100 of forming a composite element 14 according to one embodiment of the t invention. With reference to Fig. 14 and Figs. 5-8, the method 100 comprises providing one or more sole prepreg layers (step 104) and one or more forefoot prepreg layers (step 108). Each prepreg layer can contain one or more fiber-reinforced layers. Each sole prepreg layer 66 has a forefoot region 30 and optionally at least one of a toe region 26, an arch region 34, and a heel region 38. The forefoot region 30 is positioned between the toe region 26 and the arch region 34, and the arch region 34 is positioned between the ot region 30 and heel region 38. At least one sole prepreg layer 66 and at least one forefoot prepreg layer 70 are positioned in a first mold (step 112), one on top of another to form a first assembly having each of the forefoot prepreg layers 70 positioned about the forefoot region 30 of the one or more sole prepreg layers 66. The hierarchy of sole prepreg layers 66 and forefoot prepreg layers 70 may vary. For example, several sole prepreg layers 66 may be d on top of each other before adding a forefoot g layer 70 or Vice versa. Additionally, several forefoot prepreg layers 70 may be stacked on top of each other before adding a sole prepreg layer 66. Then, heat or pressure, or a combination of both, are applied (step 116) to form a composite element 14, i.e., a laminate composite.

Optionally, the composite element 14 could be molded to an outsole element 18 to form an outsole 22, as depicted, for example, in Fig. 3. Molding processes e cast, injection, reaction injection, compression, transfer, laminate, or combinations thereof. As depicted in Figs. 2 and 4, for example, one or more lugs 50 may be formed as an integral component ofthe outsole 18 during the molding step. Alternatively, one or more lugs 50 may be attached to the outsole 22 after the molding step. Additionally, one or more cleat attachment voids 54, 58 may be formed in the outsole 22. Additionally, this method may be used to form a midsole or an ole.

The present disclosure, in s ments, configurations, or aspects, includes components, methods, processes, systems and/or apparatus substantially as depicted and described herein, including various s embodiments, rations, sub—combinations, and subsets thereof. Those of skill in the art will understand how to make and use the s aspects, embodiments, rations, sub-combinations, and subsets of the present disclosure after tanding the disclosure. The present disclosure, in various aspects, embodiments, and configurations, includes providing devices and processes in the absence of items not depicted and/or bed herein or in various s, embodiments, or rations hereof, including in the absence of such items as may have been used in previous devices or processes, e.g., for ing performance, achieving ease and\or reducing cost of implementation.

The foregoing discussion of the disclosure has been presented for purposes of illustration and description. The foregoing is not intended to limit the disclosure to the form or forms disclosed herein. In the foregoing Detailed Description for example, various features of the disclosure are grouped together in one or more aspects, embodiments, or configurations for the purpose of streamlining the disclosure. The features of the aspects, embodiments, or configurations ofthe disclosure may be combined in alternate aspects, ments, or configurations other than those discussed above. This method of disclosure is not to be interpreted as ing an intention that the claims require more features than are expressly recited in each claim. Rather, as the following claims , inventive aspects lie in less than all features of a single ing disclosed aspect, embodiment, or configuration. Thus, the following claims are hereby incorporated into this Detailed Description, with each claim standing on its own as a separate preferred embodiment.

Moreover, though the description of the disclosure has included description of one or more aspects, embodiments, or configurations and certain variations and modifications, other variations, combinations, and modifications are within the scope of the invention, e. g., as may be within the skill and knowledge of those in the art, after understanding the present sure. It is intended to obtain rights which include alternative aspects, embodiments, or configurations to the extent permitted, including ate, interchangeable and/or equivalent structures, functions, ranges or steps to those d, whether or not such alternate, hangeable and/or equivalent structures, fimctions, ranges or steps are disclosed herein, and without intending to ly dedicate any patentable subject matter.

Claims (20)

1. A sole for an article of footwear, sing: a toe region, a ot region, an arch region, and a heel region, wherein at least one of the toe region, arch region, and heel region, comprise at least one pliable reinforced layer; and wherein the forefoot region comprises at least one rigid fiber-reinforced layer interposed with at least one pliable fiber-reinforced layer.

2. The sole of claim 1, wherein the at least one pliable fiber-reinforced layer and the at least one rigid fiber-reinforced layer comprise a polymer component selected from the group consisting of a homopolymer, a copolymer, a polymer alloy, and a combination thereof.

3. The sole of claim 1, wherein the at least one e fiber-reinforced layer and the at least one rigid fiber-reinforced layer comprise a polymer component selected from the group consisting of vinyl esters, epoxies, polyolefins, polystyrenes, polyvinyls, polyacrylics, polyhaloolefins , polydienes, polyoxides, polyesthers, polyacetals, polysulfides, polythioesters, polyamides, ioamides, polyurethanes, polythiourethanes, polyureas, polythioureas, polyimides, polythioimides, polyanhydrides, polythianhydrides, polycarbonates, polythiocarbonates, polyimines, polysiloxanes, polysilanes, polyphosphazenes, polyketones, polythioketones, polysulfones, polysulfoxides, polysulfonates, polysulfoamides, polyphylenes, and a combination thereof.

4. The sole of claim 1, wherein the at least one pliable fiber-reinforced layer and the at least one rigid fiber-reinforced layer comprise a fiber selected from the group ting of single-walled carbon-nanotubes, multi-walled carbon bes, graphene nanoribbons, carbonfibers , glass fibers, rayon fibers, silk fibers, metal fibers, nylon fibers, olefin fibers, acrylic fibers, ter fibers, aramid fibers, and ations thereof.

5. The sole of claim 1, wherein the rigid reinforced layer is at least as thick as the pliable fiber-reinforced layer.

6. The sole of claim 1, wherein the rigid fiber-reinforced layer is substantially nondeformable.

7. The sole of claim 1, wherein the pliable fiber-reinforced layer is able.

8. The sole of claim 1, further comprising 1 to 4 of the pliable fiber-reinforced layers and 1 to 11 of the rigid fiber-reinforced layers.

9. The sole of claim 1, wherein the toe region, the arch region, and the heel region of the pliable reinforced layer comprise a different number of the at least one pliable fiberreinforced layers.

10. The sole of claim 1, wherein the pliable fiber-reinforced layers and the rigid fiberreinforced layers differ in thickness.

11. The sole of claim 1, wherein the at least one pliable fiber-reinforced layer is configured to deform in response to at least one of normal wear, shear stresses, torsional stresses, and combinations thereof.

12. The sole of claim 1, wherein the pliable fiber-reinforced layer is configured to have minimal stiffness in response to moderate lateral loads, transverse loads, and combinations

13. The sole of claim 1, n the pliable fiber-reinforced layer and the rigid fiberreinforced layer comprise fibers oriented at an angle between 0 degrees and 180 degrees to an axis.

14. The sole of claim 1, wherein one fiber-reinforced layer ses fibers randomly oriented with respect to an axis.

15. The sole of claim 1 formed as an outsole of an article of footwear.

16. The sole of claim 1 formed as a midsole of an article of footwear.

17. The sole of claim 1 formed as an innersole of an article of footwear.

18. The sole of claim 1 formed as a midsole of an article of ar: wherein the forefoot region is positioned between the toe region and the arch region, wherein the arch region is positioned n the forefoot region and the heel , and wherein at least two regions ed from the group consisting of the toe region, the forefoot , the arch region and the heel region differ from each other in rigidity due to at least one difference in at least one material selected from the group consisting of a number of fibers, an orientation of fibers, a number of layers, a shape of layers, and an orientation of layers.

19. The sole of claim 18, r comprising at least one lug and at least one cleat attachment void.

20. A method of forming the sole of claim 1, the method comprising: providing one or more prepreg layers of the forefoot region to a mold; providing one or more second prepreg layers selected from the group consisting of the forefoot region, the toe region, the arch region, the heel region and combinations thereof to the mold to form a first assembly; applying at least one of heat and pressure to the first assembly to form the composite element.