NZ800094B2 - Cementitious reagents, methods of manufacturing and uses thereof - Google Patents
[go: Go Back, main page]

NZ800094B2 - Cementitious reagents, methods of manufacturing and uses thereof - Google Patents

Cementitious reagents, methods of manufacturing and uses thereof

Info

Publication number
NZ800094B2
NZ800094B2 NZ800094A NZ80009420A NZ800094B2 NZ 800094 B2 NZ800094 B2 NZ 800094B2 NZ 800094 A NZ800094 A NZ 800094A NZ 80009420 A NZ80009420 A NZ 80009420A NZ 800094 B2 NZ800094 B2 NZ 800094B2
Authority
NZ
New Zealand
Prior art keywords
cementitious
cementitious reagent
reagent
binder
methods
Prior art date
Application number
NZ800094A
Other versions
NZ800094A (en
Inventor
Donald Lake
Original Assignee
Technology Holdings Inc
Filing date
Publication date
Application filed by Technology Holdings Inc filed Critical Technology Holdings Inc
Publication of NZ800094A publication Critical patent/NZ800094A/en
Publication of NZ800094B2 publication Critical patent/NZ800094B2/en

Abstract

The present disclosure is related to cementitious reagents, and more particularly, to the creation of relatively homogeneous cementitious reagent materials and cementitious materials from abundant heterogeneous feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO2 emission associated with cement production. one such method of reducing CO2 in cement production, comprising the steps of: forming a cementitious reagent, wherein the cementitious reagent: (i) is a non-crystalline solid; (ii) has a particle distribution with D[3,2] of 20 µm or less; (iii) has less than about 10 wt% CaO; and (iv) is formed by heating an aluminosilicate material to a liquid phase temperature of about 1000-1600 °C; and adding the cementitious reagent to a binder.

Claims (15)

1. A method of reducing CO in cement production, comprising the steps of: forming a cementitious reagent, wherein the cementitious reagent: (i) is a non-crystalline solid; (ii) has a particle distribution with D[3,2] of 20 µm or less; (iii) has less than about 10 wt% CaO; and (iv) is formed by heating an aluminosilicate material to a liquid phase temperature of about 1000-1600 °C; and adding the cementitious reagent to a binder.
2. The method of claim 1, wherein the binder comprises fly ash, and the cementitious reagent is a 1:1 replacement for fly ash in the binder.
3. The method of claim 1 or claim 2, wherein the cementitious reagent has a molar composition of Si/(Fe, Al) between 1-20.
4. The method of any one of claims 1 to 3, wherein the cementitious reagent is at least 40% X-ray amorphous.
5. The method of any one of claims 1 to 4, wherein the cementitious reagent is 80-100% X- ray amorphous.
6. The method of any one of claims 1 to 5, wherein the binder is a geopolymer binder.
7. The method of any one of claims 1 to 5, wherein the binder is a hydraulic cement.
8. The method of any one of claims 1 to 7, wherein cementitious reagent has a molar composition ratio of (Ca,Mg) •(Na,K) •(Al, Fe ) •Si . 0-12 0.05-1 1 1-20
9. The method of any one of claims 1 to 8, wherein forming the cementitious reagent comprises crushing an aluminosilicate feedstock material.
10. The method of any one of claims 1 to 9, wherein the cementitious reagent is formed to comprise glassy microspheroids through in-flight melting and in-flight quenching.
11. The method of any one of claims 1 to 10, wherein forming the cementitious reagent comprises a milling step to produce a feedstock material in the form of a powder that is used to produce the cementitious reagent.
12. The method of any one of claims 1 to 11, wherein the cementitious reagent is in the form of a powder.
13. The method of any one of claims 1 to 12, wherein the cementitious reagent has a mean roundness (R) of at least 0.7.
14. The method of any one of claims 1 to 13, wherein the cementitious reagent has a mean roundness (R) of at least 0.9.
15. The method of any one of claims 1 to 14, further comprising: determining a content of Na,K in the binder; and modifying, based on the Na,K in the binder, the Na,K content in the cementitious reagent.
NZ800094A 2020-06-29 Cementitious reagents, methods of manufacturing and uses thereof NZ800094B2 (en)