AU2003277964B2

AU2003277964B2 - Fire resistant material

Info

Publication number: AU2003277964B2
Application number: AU2003277964A
Authority: AU
Inventors: Stuart Arthur Bateman; Matthew Jon Partlett; Dong Yang Wu
Original assignee: Commonwealth Scientific and Industrial Research Organization CSIRO; Boeing Co
Current assignee: Commonwealth Scientific and Industrial Research Organization CSIRO; Boeing Co
Priority date: 2002-10-31
Filing date: 2003-10-31
Publication date: 2009-08-20
Anticipated expiration: 2023-10-31
Also published as: AU2003277964A1

Description

WO 2004/039916 PCT/AU2003/001443 FIRE RESISTANT MATERIAL The present invention relates to inorganic organic hybrids (IOHs), methods for their preparation and 5 their use as fire resistant materials or components of fire resistant materials. More specifically, the invention relates to polyamide fire resistant formulations containing IOHs which have application in the production of fire resistant articles or parts thereof for use in the 10 transportation, building, construction and electrical or optical industries. BACKGROUND OF THE INVENTION Materials based on organic polymeric systems 15 (plastics) are widely used in the transportation, building and construction industries. A drawback of many types of organic polymers is flammability which limits their suitability in applications requiring flammability resistance and where regulatory authorities govern 20 flammability standards. In commercially produced polymeric systems, flame-retarding species may be added during processing or forming of the materials to reduce the end products flammability. Conventional flame-retardants may be 25 divided into different categories including: Halogen based: which consist of either brominated or chlorinated chemicals such as brominated polystyrene or phenylene oxide (Dead Sea Bromine or Great Lakes CC) or bis(hexachlorocyclopentadieno) cyclooctane 30 (Occidental CC). Phosphorus based: which consist of a range of different chemistries from elemental phosphorus (Clarient), phosphonates (A&W antiblaze 1045), phosphonate esters (Akzo Nobel), phosphites, phosphates and 35 polyphosphates including melamine phosphite and phosphate, ammonium and melamine polyphosphate (DSM Melapur).

WO 2004/039916 PCT/AU2003/001443 -2 Nitrogen based: such as melamine and its salts (US 4,511,684 Schmidt & Hoppe). Intumescent agents: incorporating (i) an acid source (carbonization catalyst) such as ammonium 5 polyphosphate; (ii) a carbonization reagent e.g. polyhydric alcohols such as pentaerythritol; and (iii) a blowing reagent like melamine. Expandable graphite is also known to undergo thermal expansion on addition of heat. 10 Inorganic additives: such as magnesium hydroxide and aluminum hydroxide (Martinswerk), zinc borate (Fire Brake ZB, US Borax) and antimony trioxide. Although the addition of fire retardants to polymeric systems may improve their fire performance other 15 important properties are often adversely effected for example: e Mechanical performance * Surface finish e Durability 20 e Rheology e Stability e Smoke generation * Toxicity e Cost 25 e Recyclability Furthermore, there has been considerable recent impetus to reduce the use of some flame-retardant classes due to toxicological or environmental concerns. Such legislation has placed pressure on the use of halogenated 30 compounds and certain metal oxide synergists. Phosphorus based flame-retardants such as phosphonates and elemental (red) phosphorus are also undesirable due to their regulation under chemical weapon acts and considerable manufacturing danger. 35 As far back as 1965, Jonas (GB .1114,174) teaches that the incorporation of organically modified clay into plastics reduces melt dripping during combustion.

WO 2004/039916 PCT/AU2003/001443 -3 More recently it has been shown that under certain synthetic or processing conditions, organically modified clay may be nano-dispersed into polymeric materials to improve mechanical and fire performance. 5 Okada et al, (US 4,739,007 (1988) Toyota) teaches that nylon 6 materials with improved mechanical and heat distortion temperature can be prepared by adding suitably modified clay during the synthesis of nylon 6. In this case the growing nylon chains force apart the clay 10 platelets to form intercalated or exfoliated nanomaterial structures (so called in 'situ polymerisation' method). A more commercially desirable method of nano dispersing modified clay is described by Maxfield, et al, (WO 93/04118 WO 93/04117 (1993) Allied Signal). Maxfield 15 teaches that clay-plastic nanomaterials with improved mechanical and heat distortion performance may be prepared by subjecting functionalised clay and molten plastics such as nylon6, nylon66 and PBT to shear forces. Others have investigated the fire performance of 20 plastics incorporating clay nano particles. Gilman has studied the fire performance of nylon-nanomaterials prepared through the 'in situ' polymerisation pathway using cone calorimetry (Proc. 43. Int. SAMPE Sympos., (1998), p1053-1066, Fire and Materials, 24, (2000), p201 25 208, Applied Clay Science, 15, (1999), p31-49). Improved heat release rates were achieved with the addition of commercially modified clay, without increasing toxic gas or smoke generation. Gilman teaches that the improved fire performance results from the nanoparticles both 30 mechanically stabilizing the char and enhancing its barrier properties. Although Gilman's cone calorimetry tests suggest improved performance in terms of a reduction in heat release rate, no mention was made of other aspects of the materials fire performance in common tests 35 described by bodies such as ASTM and FAA which are used to assess, regulate and qualify the fire worthiness of materials.

WO 2004/039916 PCT/AU2003/001443 -4 Other groups have reported that traditional flame-retardants and nano-dispersed clays can act synergistically to improve fire performance. Klatt (WO 98/36022, (1998) BASF) teaches that 5 nylon materials incorporating organically modified clay and red phosphorus synergistically improve fire performance to produce a VO rating in UL94 type vertical burn tests. However, such compositions are undesirable due to the danger associated with handling of elemental 10 phosphorus. Morton (WO 99/43747, (1999) General Electric Company) teaches that in certain polyester blends, phosphorus based flame retardants especially resorcinol diphosphate and organically modified clay act 15 synergistically to improve fire performance. No mention, however, is made of other important aspect such as the effect on mechanical performance, smoke and toxic gas emission. Takekoshim (US 5,773,502 (1998) General Electric 20 Company) teaches that conventional halogenated-Sb 2 0 3 flame retardant systems and organically modified clay can act synergistically. Takekoshim claims that nano-dispersed clay allows for reductions in the amount of Sb 2 03 and halogenated flame retardant required to maintain a VO 25 rating in the UL 94 flammability test. Clearly any use of halogenated flame retardant is undesirable. Masaru, T (JP 10182141 (1998) Sumitoma, Chem Co.) disclose a fire resistant and thermally expandable material at temperatures between 100 to 150 0 C whereby 30 blowing reagents such as those containing azo, diazo, azide or triazine compound are located between the layers of the silicate. In many polymeric systems, however, this flame retarding system is undesirable since they require moulding or forming at temperatures between 100C to 150 C. 35 Inoue and Hosokawa (JP 10081510 (1998) Showa Denko K.K.) investigated the use of fluorinated synthetic mica exchanged with melamine (0.1 - 40%) and melamine WO 2004/039916 PCT/AU2003/001443 -5 salts (<10%) as a means of flame proofing plastics in a two step extrusion process. They claim that a VO rated Nylon6 (UL94 vertical burn test) was achieved at a loading of 5 percent-modified mica when greater than 80% 5 exfoliation occurred. The use of synthetic clays and multiple step processing is clearly undesirable from a commercial viewpoint. Inoue and Hosokawa do not disclose highly desirable chemistries and methodologies associated with triazine based formulations which effect mechanical 10 and fire performance. Furthermore, they do not disclose important methodologies to flame retarded thin parts known by those in the art to be extremely difficult to render flame resistant whilst simultaneously reducing toxic gas and smoke generation during combustion. 15 In a later disclosure Inoue, H., and co-workers (US 6294599 (2001) Showa Denko K.K.) also teach that polyamides reinforced with fibrous additives may be rendered flame resistant through the addition of triazine modified clay and additional flame retardant. They 20 describe a highly rigid flame-retardant polyamide comprising a polyamide, silicate - triazine compound reinforcement and flame retardant/adjunct. The poor rheological properties of highly rigid polyamide formulations limit the inventions usefulness in preparing 25 components made by conventional processing techniques such as rotational or blow moulding, that are complex or thin walled or which require high ductility or impact performance. Brown, S.C. et al (WO 00/66657, Alcan 30 International) disclose a polymeric material incorporating Cloisite montmorillonite in combination with Al(OH) 3 for the production of fire resistant cables. This strategy is clearly only suitable for plastics that are processed at low temperatures considering that Al (OH) 3 decomposes to 35 release water vapor at temperatures above approximately 190 C.

PCT/AU20031001443 Received 25 January 2005 Accordingly, there is a need for the development of new flame retarding systems which both meet the performance criteria associated with specific applications and address the above concerns. 5 SUMMARY OF THE INVENTION According to one aspect of the present invention there is provided an inorganic-organic hybrid (IOH) which comprises: 10 (i) an expandable or swellable layered inorganic component; and (ii) an organic component including at least one ionic organic component and one or more neutral organic components which are intercalated between and/or 15 associated with the layer(s) of the inorganic component, the ionic or neutral organic components being capable of decomposing or subliming endothermically, and/or releasing volatiles with low combustibility on decomposition and/or inducing charring of organic species 20 during thermal decomposition or combustion. According to another aspect of the present invention there is provided a method for the preparation of the IOH defined above which comprises mixing components (i) and (ii) defined above or constituents thereof in one 25 or more steps. The present invention also provides the use of the IOH defined above as a fire resistant material. According to a further aspect of the present invention there is provided a fire resistant formulation 30 which comprises: (i) the IOH defined above; and (ii) one or more flame retardants. According to a still further aspect of the present invention there is provided a method for the 35 preparation of the fire resistant formulation defined above which comprises mixing components (i) and (ii) as defined above or constituents thereof in one or more steps. The present invention also provides a polyamide 40 fire resistant formulation which comprises either: H:\annamAngtddi~hgg23 CSIRO-BOEING - A4DED PAGES FOR WO.doc 24/01/05

]PEAIAU-

WO 2004/039916 PCT/AU2003/001443 -7 (A) (i) the IOH defined above; and (ii) a polyamide based matrix; or (B) (i) the fire resistant formulation defined above; and 5 (ii) a polyamide based matrix. The present invention further provides a method for the preparation of the polyamide fire resistant formulation defined above which comprises dispersing the IOH or the fire resistant formulation defined above or 10 constituents thereof into the polyamide based matrix in one or more steps. The IOH and/or fire resistant formulations of the present invention may be used to produce fire resistant articles or parts thereof. 15 Thus, the present invention provides a fire resistant article or parts thereof which is composed wholly or partly of the IOH and/or fire resistant formulations defined above. The present invention also provides a method of 20 preparing the fire resistant article or parts thereof defined above which comprises moulding or forming the IOH and/or fire resistant formulations defined above. DETAILED DESCRIPTION OF THE INVENTION 25 For the purposes of this specification it will be clearly understood that the word "comprising" means "including but not limited to", and that the word "comprises" has a corresponding meaning. It should also be noted that for the purposes of this specification the 30 terms "swellable" and "expandable" relating to the layered inorganic component are interchangeable. The inorganic component is a swellable/expandable layered inorganic based material, rendered positively (or negatively) charged due to 35 isomorphic substitution of elements within the layers, such as, those based on a 1:1 layered silicate structure such as kaolin and serpentine and a 2:1 layered silicate WO 2004/039916 PCT/AU2003/001443 -8 structure such as phyllosilicates, talc and pyrophyllite. Other useful layered minerals include layered double hydroxides of the general formula Mg 6 Al 3 .4 (OH) 18.8 (CO 3 ) 1

.

7

.H

2 0 including hydrotalcites and synthetically prepared layered 5 materials including synthetic hectorite, montmorillonite, fluorinated synthetic mica and synthetic hydrotalcite. The group consisting of naturally occurring or synthetic analogues of phyllosilicates is particularly preferred. This group includes smectite clays such as 10 montmorillonite, nontronite, beidellite, volkonskoite, hectorite, bentonite, saponite, sauconite, magadiite, kenyaite, laponite, vermiculite, synthetic micromica (Somasif) and synthetic hectorite (Lucentite). Other useful layered minerals include illite minerals such as 15 ledikite and mixtures of illite minerals with said clay minerals. Naturally occurring phyllosilicates such as bentonite, montmorillonite, and hectorite are most preferred. Such phyllosilicates with platelet thicknesses 20 less than about 5 nanometers and aspect ratios greater than about 10:1, more preferably greater than about 50:1 and most preferably greater than about 100:1 are particularly useful. The preferred inorganic materials generally 25 include interlayer or exchangable metal cations to balance the charge, such as, alkali metals or alkali earth metals, for example, Na*, K', Mg 2 + or Ca 2 +, preferably Na+. The cation exchange capacity of the inorganic material should preferably be less than about 400 milli-equivalents per 30 100 grams, most preferably about 50 to about 200 milli equivalents per 100 grams. The organic component includes one or more ionic species that may be exchanged with the exchangeable metal ions associated with the inorganic component and 35 optionally one or more neutral organic species which are intercalated between and/or associated with the layer(s) PCT/AU20031001443 Received 25 January 2005 of the inorganic component and/or one or more coupling reagents. The term "associated with" is used herein in its broadest sense and refers to the neutral organic component 5 being attached to the layer(s) of the inorganic component, for example, by secondary bonding interactions, such as, Van der Waals interactions or hydrogen bonding or trapped by steric limitation. Suitable examples of ionic species include those 10 that contain onium ions such as ammonium (primary, secondary, tertiary and quaternary), phosphonium or sulfonium derivatives of aliphatic, aromatic or aryl aliphatic amines, phosphines and sulfides. Such compounds may be prepared by any method 15 known to those skilled in the art. For example, salts prepared by acid-base type reactions with mineral or organic acids including hydrochloric, sulfuric, nitric, phosphoric, acetic and formic acids, by Lewis-acid Lewis-base type reactions or by reaction with alkyl 20 halides to form quaternary salts for example using Menschutkin type methodology. Ionic or neutral compounds which are known to decompose or sublime endothermically, and/or which release volatiles with low combustibility on decomposition and/or 25 induce charring of organic species during thermal decomposition or combustion are used in the IOH of the present invention. Suitable species include neutral or ionic derivatives of nitrogen based molecules, such as, triazine 30 based species, for example, melamine, triphenyl melamine, melam (1,3,5-triazine-2,4,6-triamine-n-(4,6-diamino-1,3,5 triazine-yl)), melem ((-2,5,8-triamino-1,3,4,6,7,9,9b heptaazaphenalene)), melon (poly{8-amino-1, 3 ,4,6,7,9,9b heptaazaphenalene-2,5-diyl)imino}), bis and 35 triaziridinyltriazine, trimethylsilyltriazine, melamine cyanurate, melamine phthalate, melamine phosphate, melamine phosphite, melamine phthalimide, dimelamine phosphate, phosphazines and/or low molecular weight H:\anna)M4 M ]gg623 CSIRO-BOEING - AMDED PAGES FOR WO.doc 24/01/05

IPEA/AU

WO 2004/039916 PCT/AU2003/001443 - 10 polymers with triazine and phosphazine repeat units or salts or derivatives of the above molecules including onium ion derivatives or salts or derivatives of isocyanuric acid, such as, isocyanuric acid, cyanuric 5 acid, triethyl cyanurate, melamine cyanurate, trigylcidylcyanurate, triallyl isocyanurate, trichloroisocyanuric acid, 1,3,5-tris(2 hydroxyethyl)triazine-2,4,6-trione, hexamethylenentetramine. melam cyanurate, melem cyanurate 10 and melon cyanurate. Reagents known to .induce charring of organic species include derivatives of phosphoric acid or boric acid, such as ammonia polyphosphate and melamine polyphosphate, melamine phosphate ammonium borate. 15 In another embodiment of the invention, the preferred ionic compounds may be optionally used in combination with other ionic compounds, for example, those known to improve compatibility and dispersion between the layered inorganic material and polymeric matrices such as 20 those described in WO 93/04118 for the preparation of nanomaterials. Amphiphilic molecules that incorporate a hydrophilic ionic group along with hydrophobic alkyl or aromatic moieties are preferred. One or more coupling reagents may also be 25 associated with the inorganic component. Suitable coupling reagents include organically functionalised silanes, zirconates and titanates. Examples of silane coupling reagents include tri-alkoxy, acetoxy and halosilanes functionalised with amino, epoxy, isocyanate, 30 hydroxyl, thiol, mercapto and/or methacryl reactive moieties or modified to incorporate functional groups based on triazine derivatives, long chain alkyl, aromatic or alkylaromatic moieties. Examples of zirconate and titanate coupling reagents include Teaz and Titanl. 35 It is known in the art that metal cations or anions associated with layered inorganic materials may be exchanged with organic ions through ion exchange WO 2004/039916 PCT/AU2003/001443 - 11 processes. In a typical process, the layered inorganic material is first swollen or expanded in a suitable solvent(s) prior to ion exchange and then collected from the swelling solvent following agglomeration using methods 5 such as filtration, centrifugation, evaporation or sublimation of the solvent. Ion exchange techniques with suitable molecules are known to be a useful method of increasing the compatibility between clay and organic polymeric binders, thus aiding dispersion of clay 10 platelets into polymeric based matrices on a nanometer scale. We have discovered that the ion exchange process may be optionally carried out in the presence of one or more types of organic ion to produce an inorganic-organic 15 hybrid with a plurality of functions. Without wishing to limit the present invention, such functions may include the presence of ions which promote dispersion, compatibility and interactions with the plastic matrix and ions useful to improve other properties such as fire 20 performance. Generally during ion exchange the organic ions are added in molar excess of the ion exchange capacity of the inorganic material, preferably less than about 10-fold excess, more preferably less than about a 5 fold excess is required. 25 It has also been unexpectedly discovered that the ion exchange processes may be carried out in the presence of functional dissolved or partially dissolved neutral species. Without being limited by theory, it is proposed that at least a portion of the neutral species 30 are trapped in the intergallery region or otherwise associated with the layered inorganic material following ion exchange. Such a process provides a useful mechanism of dispersing neutral additives on a molecular level into plastics. Again without being limited by theory, during 35 melt processing at least partial exfoliation of the inorganic-organic hybrid allows the neutral molecules to diffuse away and become homogeneously dispersed with the WO 2004/039916 PCT/AU2003/001443 - 12 matrix on a molecular level. This has a major impact on the performance of the resultant material since it is well known that efficient dispersion of all components in a plastic formulation, preferably on a nano- or molecular 5 scale, is an important factor for achieving optimum performance. In another aspect of the invention, the IOH may be treated prior, during or following ion exchange with one or more coupling reagents as described above. The 10 coupling reagents are derivatized to improve, for example, the compatibility and interactions between the inorganic phase and polymeric matrix or to attach other desirable functionalities to the inorganic layered phase. Suitable flame retardants which retard flame 15 propagation, heat release and/or smoke generation which may be added singularly or optionally synergistically to the IOH include: e Phosphorus derivatives such as molecules containing phosphate, polyphosphate, phosphites, 20 phosphazine and phosphine functional groups, for example, melamine phosphate, dimelamine phosphate, melamine polyphosphate, ammonia phosphate, ammonia polyphosphate, pentaerythritol phosphate, melamine phosphite and triphenyl phosphine. 25 0 Nitrogen containing derivatives such as melamine, melamine cyanurate, melamine phthalate, melamine phthalimide, melam, melem, melon, melam cyanurate, melem cyanurate, melon cyanurate, hexamethylene tetraamine, imidazole, adenine, guanine, cytosine and thymine. 30 0 Molecules containing borate functional groups such as ammonia borate and zinc borate. e Molecules containing two or more alcohol groups such as pentaerythritol, polyethylene alcohol, polyglycols and carbohydrates, for example, glucose, sucrose and 35 starch. e Molecules which endothermically release non combustible decomposition gases, such as, metal WO 2004/039916 PCT/AU2003/001443 - 13 hydroxides, for example, magnesium hydroxide and aluminum hydroxide. Expandable graphite The polyamide based matrix may be included in 5 the fire resistant formulation in pellet, granule, flake or powdered form. Suitable polyamides comprise generic groups with repeat units based on amides, such as, Nylon4, Nylon6, Nylon7, Nylon 11 and Nylonl2, Nylon46, Nylon66, Nylon 68, Nylon610, Nylon612 and aromatic polyamides, for 10 example, poly'm'phenyleneisophthalamine and poly'p'phenylene'terephthalmamide. It will be appreciated that the polyamide based matrix may include co-polymers, blends and alloys. The co-polymers may be made up of two or more different repeat 15 units one of which is an amide. Such co-polymers may be prepared by any suitable methods known in the art, for example, at the point of initial polymerisation or later through grafting or chain extension type reactions during processing. The polyamide blends and alloys may be 20 prepared using any method known to those skilled in the art including melt or solution blending. Blending or alloying the polyamide with other polymers may be desirable to improve properties such as toughness, modulus, strength, creep, durability, thermal resistance, 25 conductivity or fire performance. Nylon12, Nylon6 and Nylon66 and their respective co-polymers, alloys and blends are particularly preferred. The polyamide formulation can also optionally contain one or more additives known in the art of polymer 30 processing, such as, polymeric stabilisers, for example, UV, light and thermal stabilisers; lubricants; antioxidants; pigments, dyes or other additives to alter the materials optical properties or colour; conductive fillers or fibers; release agents; slip agents; 35 plasticisers; antibacterial or fungal agents, and processing agents, for example, dispersing reagents, foaming or blowing agents, surfactants, waxes, coupling WO 2004/039916 PCT/AU2003/001443 - 14 reagents, rheology modifiers, film forming reagents and free radical generating reagents. A particularly preferred formulation comprises Nylon12, Nylon6 and/or Nylon66; montmorillonite modified 5 with melamine hydrochloride and/or melamine; melamine cyanurate and/or melam (1,3,5-triazine-2,4,6-triamine-n (4,6-diamino-1,3,5-triazine-yl)) cyanurate, and/or melem ((-2,5,8-triamino-1,3,4,6,7,9,9b-heptaazaphenalene)) cyanurate and/or melon (poly{8-amino-1,3,4,6,7,9,9b 10 heptaazaphenalene-2,5-diyl)iminol) cyanurate; magnesium hydroxide; and one or more additives. The polyamide formulation preferably contains a polyamide based matrix in an amount of from about 50 to about 95% w/w, an IOH in an amount less than about 25% w/w 15 and optionally a flame retardant and/or additives in an amount less than about 30% w/w, but in some cases preferably above about 10% w/w. It has been discovered that the IOH may be readily dispersed into the polyamide based matrix during 20 the compounding (mixing) stage. Without wishing to be limited by theory, it is proposed that ion exchange enhances the layered IOHs compatibility with polyamides compared with unmodified inorganic layered materials. This heightened compatibility in combination with 25 sufficient mixing forces, appropriate mixing sequence, screw design and time allows the organically modified platelets associated with the IOH to be at least partially exfoliated into the polyamide and hence dispersed at least partially on a nanometer scale. This process also 30 provides a useful mechanism of dispersing into the polyamide any neutral molecules associated with the IOH on a molecular level. Dispersion of the various components of the fire resistant formulation including the IOH is aided by 35 grinding prior to mixing. Grinding is achieved using any suitable grinding equipment including ball mills, ring mills and the like. It is preferable that the components WO 2004/039916 PCT/AU2003/001443 - 15 including the IOH is ground to a particle size less than about 200 microns, more preferably less than about 50 microns, most preferably less than about 20 microns. The hybrid material may also be ground using specialty 5 grinding equipment allowing grinding to nanometer sizes. Dispersion may be affected using any suitable melt, solution or powder based mixing process allowing sufficient shear rate, shear stress and residence time to disperse the IOH at least partially on a nanometer scale. 10 Such processes may be conducted using milling procedures such as ball milling, in a batch mixer using internal mixers, such as, Banbury and Brabender/Haake type mixers, kneaders, such as, BUS kneaders, continuous mixing processes including continuous compounders, high intensity 15 single and twin screw extrusion. Melt processing is preferred and in a particularly preferred embodiment, twin screw extruders with an L:D ratio of at least about 24, preferably more than about 30 equipped with at least one and preferably 20 multiple mixing and venting zones are employed for dispersion. Such screw configurations useful for dispersive and distributive mixing are well known to those in the art. A particularly useful system has been found to be that illustrated in Figure 1. 25 The components of the formulation may be added in any order or at any point along the extruder barrel. Since polyamides are susceptible to hydrolysis it is preferable that the components are dried prior to processing and/or mechanisms to remove water vapor such as 30 vents or vacuum ports available during processing. In a preferred embodiment, all of the components are added at one end of the extruder. In another preferred embodiment, a polymeric binder and optionally minor components are added at one end of the extruder and the IOH and 35 optionally minor components at a later point/s. In still another preferred embodiment, the IOH portion of the polymeric binder and optionally minor components are added WO 2004/039916 PCT/AU2003/001443 - 16 at one end of the extruder with the remaining portion of the polymeric binder and optionally minor components are added at a later point/s. Following extrusion the molten composition is cooled by means of water bath, air knife or 5 atmospheric cooling and optionally cut into pellets. Preferably all of the major and minor components of the system can be combined in as few a mixing steps as possible, most preferably in a single mixing step. The moulding or forming of the polyamide 10 formulation into fire resistant articles or parts thereof can be carried out using any method known to those in the art including processes such as extrusion, injection moulding, compression moulding, rotational moulding, blow moulding, sintering, thermoforming, calending or 15 combinations thereof. In one embodiment of the invention the fire resistant polyamide system containing the major and minor components is moulded or formed into parts having wall thickness less than about 25 mm, preferably less than 20 about 5 mm, most preferably less than 1.5 mm. Such parts include but are not limited to tubes, complex moulded hollow parts, sheets and complex moulded sheets and other complex objects that are moulded or formed using techniques, such as, extrusion, injection moulding 25 thermoforming and rotational moulding. In the simplest process, the article or part is directly produced during compounding for example by locating a die at the end of the extruder allowing the shape of the extrudate to be modified as required. 30 Examples of such components include simple parts such as film, tape, sheet, tube, rod or string shapes. The process may also involve multiple layers of different materials one of which being the said polymeric system built up by processes known to those in the art including 35 co-extrusion. In another preferred embodiment, the formulation is moulded or formed in a separate step using techniques WO 2004/039916 PCT/AU2003/001443 - 17 such as injection, compression or blow moulding. Such parts are generally more complex in nature compared with parts formed by extrusion alone, their design only limited by the requirements of the moulding tool / process 5 employed. Suitable examples include but are not limited to stowage bin hinge covers, ECS duct spuds, latches, brackets, passenger surface units and the like. It is noted that for certain applications it may be preferable that the fire resistant polyamide 10 formulation is ground to a powder. In such cases it has unexpectedly been found that grinding of the said formulation using cryogenic or atmospheric grinding techniques known to those in the art may be carried out without significantly effecting the performance of the 15 system. Such moulding applications include selective laser sintering, rotational moulding, and extrusion. Suitable examples including but not limited to environmental control systems (air-conditioning ducts) and the like. 20 In other preferred applications, the polymeric formulation may be first formed into a sheet or film, for example, through extrusion, blow moulding, compression moulding or calending. The sheet may be subsequently moulded to a desired shape using thermoforming techniques. 25 In yet another application, the sheet or film may be used to prepare reinforced thermoplastic laminates with woven fabrics prepared from surface modified or natural glass, carbon or aramid using techniques such as compression moulding or resin infusion/transfer. Again, the laminate 30 sheet hence formed may be further moulded to a desired shape using techniques such as thermoforming. Alternatively the formulation may be spun into fibres by any method known to those skilled in the art. Such a process provides a method for producing fire 35 resistant fabrics, carpets and alike The present invention is useful for producing polyamide materials with favourable rheological properties WO 2004/039916 PCT/AU2003/001443 - 18 for moulding including thin or intricate articles or parts thereof which maintain mechanical properties close to or exceeding that of the virgin polyamide matrix and which show improved fire performance in standard tests through 5 resisting combustion by self-extinguishing when ignited, limiting flame propagation, and generating low smoke and toxic gas emissions. Such articles or parts thereof are useful for applications which require superior fire performance and in industries that are regulated for fire 10 performance including transport, for example, air, automotive, aerospace and nautical; building and construction; and electrical or optical, for example, cables, wires and fibres. 15 BRIEF DESCRIPTION OF THE DRAWINGS In the examples, reference will be made to the accompanying drawings in which: Figure 1 is a diagram showing the twin screw extruder screw and barrel configuration; 20 Figure 2 is a graph showing the XRD results and transmission electron microscope (TEM) image for Example 7; Figure 3 is a graph showing the XRD results for Example 8; 25 Figure 4 is a graph showing the XRD results for Example 9; Figure 5 is a graph showing XRD results for Example 17; and Figure 6 is a picture of complex hollow fire 30 resistant components moulded with formulations 13 and 34. EXAMPLES The invention will now be described with reference to the following non-limiting examples. 35 General Conditions & Reagents WO 2004/039916 PCT/AU2003/001443 - 19 Tables 1, 2 and 3 Outline General Reagents, Conditions & Procedures associated with the examples.

WO 2004/039916 PCT/AU2003/001443 - 20 Table 1: Commercially Available Reagents Reagent Trade name Supplier Montmorillonite - organic Cloisite 93A Southern Clay modified Montmorillonite - organic Cloisite 30B Southern Clay modified Montmorillonite Cloisite Na Southern Clay Synthetic Hectorite Laponite Southern Clay Nylon12 Vestamid 9005 Degussa Nylon 12 FR (Flame Vestamid 7166 Degussa retarded) Polyetherimide Ultem 9075 GE Plastics Nylon6 Akulon PA6 DSM Nylon66 Akulon PA66 DSM Cyanuric acid Cyanuric acid Aldrich Melamine cyanurate Fyrol MC Akzo-Nobel Melamine phosphate Fyrol MP Akzo-Nobel Melamine polyphosphate Melapur 200 DSM Melapur Melamine Melamine Aldrich Pentaerythritol Pentaerythritol Aldrich Magnesium hydroxide Magnifin Martinswerk Ammonia polyphosphate Antiblaze MC Rhodia Pentaerythritol phosphate NH- 1197 Great Lakes Pentaerythritol phosphate NH-1511 Great Lakes Blend Zinc borate Fire Brake ZB US Borax Zn Stearate Zincum Baerlocher Ca Stearate Ceasit 'Baerlocher Int 38 Synthetic resin AXEL LuWax EasI Ethylene co-polymer BASF Irganox b1 171 Phosphite/hindered phenol CIBA blend WO 2004/039916 PCT/AU2003/001443 - 21 Table 2: Processing Equipment and Conditions Equipment Type Twin screw Berstorff ZE 25 mm modular co-rotating twin screw extruder coupled extruder to a Haake Rheocord motor drive and torque cell for rheology measurement L:D ratio = 36:1 Screw and barrel configuration presented in Figure 1, Screw speed 300 rpm Feed rate -1.2 Kg/hour Residence time average 2 min Flat 200'C temperature profile from throat to die (nylon12) Flat 250'C temperature profile from throat to die (nylon6) Flat 275"C temperature profile from throat to die (nylon66) Batch Mixer Haake R3000 batch mixer connected to torque rheological load cell, pneumatic ram, roller rotors Rotor speed - 5 min 60 rpm, 10 min 120 rpm Temperature 190'C Injection Battenfeld 80 ton BA 800 CDC injection moulding machine Moulding Temperature profile: Nylon 12 Zone 1 2 3 Nozzle Die Temp ("C) 215 220 225 225 70 0 C Nylon6 Zone 1 2 3 Nozzle Die Temp ('C) 230 230 250 260 90 0 C Nylon 66 Zone 1 2 3 Nozzle Die Temp ('C) 260 260 280 290 90 0 C ASTM test samples: Injection pressure gradient 800 to 600 bar, cavity pressure 400 bar, Holding pressures 600 to 0 bar Cooling time 30sec Cone Calorimetry Samples: Injection pressure gradient 950 to 650 bar, cavity pressure 325 bar, Holding pressures 650 to 0 bar Cooling tine 60 sec WO 2004/039916 PCT/AU2003/001443 - 22 Table 2 cont Equipment Type Compression Assett 2.5 MPa pneumatic press, 45 cm platens, heating (400 0 C) Moulding and cooling Moulding platen temperature 220"C nylon 12 Moulding platen temperature 260"C nylon6 Moulding platen temperature 290"C nylon66 WO 2004/039916 PCT/AU2003/001443 - 23 Table 3: Characterization Techniques, Conditions and Sample Preparations Equipment Type X-ray diffraction Phillips PW 1729, CuKoa source X = 0.154 nm (XRD) Powders were ground to a particle size of less than 100 micron, Plastics were compression moulded (210'C) to a thickness of 100 micron Transmission Hitachi H-7500 operating at an electron potential of 120 kV Electron 100 nm thick sections were prepared by ultra microtomy Microscopy (TEM) Differential Cryogenic TA 2920 MDSC employing Advantage Scanning software,10 C and 20'C/min ramp rate rates for heating and Calorimetry (DSC) cooling for general thermal and glass transition respectively. Calibrated against, Indium, distilled water, cyclohexane and sapphire Powders were ground to a particle size of less than 100 micron. Plastics were compression moulded (210'C) to a thickness of 100 micron with quench cooling, 5mm diameter specimens were punched from the moulded sheet Thermal Thermal Sciences, PL-STA, referenced against A1 2 0 3 Gravimetric Heating rate ramp 10 C / min Analysis (TGA) Powders were ground to a particle size of less than 100 micron Plastics were compression moulded (210'C) to a thickness of 100 micron with quench cooling, 4mm diameter specimens were punched from the moulded sheet Cone Calorimetry ASTM E 1354 - 92 Testing Modified from the original Stanton-Redcroft model, employing CSIRO developed software Radiant flux 35 kW/m 2 '3 repeats per sample, ASTM E1356 Following injection moulding, samples (100x100x6mm) were conditions for 7 days at 23C at 50% RH. Heat release, smoke, mass loss and gas emission were measured Radiant Panel Conducted as per FAA specification (DOT FAA/AR-0012) & as outlined in ASTM E648 - 93a WO 2004/039916 PCT/AU2003/001443 - 24 Table 3 cont. Equipment Type Specific Optical ASTM E662 - 93 for optical density with gas released by Density of smoke samples during the test analyzed for HF, HCl, HCN, H 2 S, NO, Generated By HBr, P0 4 , SO 2 combustion Solid Materials and gas emission Vertical Burn Vertical burn tests according to UL94 or FAA specifications. UL94 specification One 10 sec application of flame from a 10 mm burner to 125x12.3x3.2 mm samples according to UL specifications 2000. Flame extinguish times were monitored over at least 3 samples Extinguishing times, VO <10s, V1 <30s, V2 <30s Cotton Wool Ignition No No Yes FAA (DOT FAA/AR-0012) and ASTM F501-93 12 s burn One 12s application of flame from a 10 mm burner to 300x75 mm samples according to FAA specification 2000: sample thickness specified Pass FAA test requirement: Flame extinguished <15sec Drip extinguished <5 sec Burn height <203 mm 60 s burn One 60s application of flame from a 10 mm burner to 300x75 mm samples according to FAA specification 2000 Pass FAA test requirement: Flame extinguished <15sec Drip extinguished <3 sec Burn height <150 mm Sample thickness specified WO 2004/039916 PCT/AU2003/001443 - 25 Table 3 cont. Equipment Type IZOD Notched Radmana ITR 2000 instrumented impact tester Impact Testing Izod mode, Iact strain rate 3.5 ± 0.2 m/sec 10 repeats per sample, ASTM 256 Following injection moulding, samples were stored for 24 h in desiccated containers, notched according to the ASTM 256 standard and tested 'dry as moulded standard deviation generally less than 8% Tensile Testing Instron tensile testing apparatus (5565) utilizing a 30 kN load cell, 50 mm/min strain rate 5 repeats per sample as per ASTM D638 External extensometer used for independent modulus measurements ASTM D5938 Following injection moulding, samples were stored for 24 h in desiccated containers and tested 'dry as moulded Generally standard deviation less than 2% for modulus and strength results MFI MFI testing was completed according to ASTM D1238 standards employing 2.16 load at a temperature of 235C, Employing a Davenport Melt Flow Indexer apparatus Parallel Plate The viscosities of samples were measured over a wide range of Rheology shear rate range of 102 to 101 s 4 at 240 0 C. Tests of shear rate sweep were carried out using a shear strain-controlled rheometer, RDA II (Rheometric Scientific Inc.). The test fixture geometry used was 25 mm parallel-plate with a constant gap between 0.6 - 0.8 mm. The nitrogen gas was used to provide an inert testing environment to reduce sample degradation due to oxidation of samples.

WO 2004/039916 PCT/AU2003/001443 - 26 Methods for Preparing Inorganic-Organic hybrids (IOH) Examples 1-6 Example 1: Preparation of melamine hydrochloride 5 modified montmorillonite (IOH1) Montmorillonite exchanged Na' (Cation Exchange Capacity (CEC) = 92 meq/100g) was suspended in 80 0 C DI water (2% w/w) and mechanically stirred at 1500 rpm for 60 min. 10 Melamine monohydrochloride salt (1.4 mmol/100g montmorillonite) was then added to the solution and the resultant suspension allowed to cool with continued stirring for a further 150 min. Following filtration of the suspension, the precipitate was thoroughly washed with 15 warm DI water and then preliminary dried (60 - 80'C). The resultant granular organically modified clay was ground to a particle size of less than 50 micron and then further dried at 75 0 C prior to processing or analysis. 20 XRD (CuKai source 0.154 nm) Cation Na+ Melamine.HCl modified Montmorillonite XRD doo, 1.10 nm 1.27 nm Results indicate that with ion exchange montmorillonite's intergallery spacing is increased from 25 1.10 nm to 1.27 nm. This result is consistent with sodium ions being replaced by protonated melamine ions in the intergallery region during ion exchange.

WO 2004/039916 PCT/AU2003/001443 - 27 Example 2a: Preparation of melamine hydrochloride modified montmorillonite in the presence of melamine (IOH2) 5 Montmorillonite exchanged Na' (Cation Exchange Capacity (CEC) = 92 meq/100g) was suspended in 80 0 C DI water (2% w/w), melamine added (1.4 mmol/100 g montmorillonite) and the solution mechanically stirred at 1500 rpm for 60 min. Melamine monohydrochloride salt (1.4 mmol/100g 10 montmorillonite ) was then added to the solution and the resultant suspension allowed to cool with continued stirring for a further 150 min. Following filtration of the suspension, the precipitate was thoroughly washed with warm DI water and then preliminary dried (60 - 80 0 C). The 15 resultant granular organically modified clay was ground to a particle size of less than 50 micron and then further dried at 75 0 C prior to processing or analysis. XRD (CuKai source = 0.154 nm) 20 Cation Na* Melamine and Melamine.HCl modified montmorillonite XRD doo, 1.10 nm 1.39 nm Results indicate that montmorillonite modified by melamine hydrochloride in the presence of melamine has an expanded intergallery spacing compared with both 25 montmorillonite that is modified with melamine hydrochloride or sodium ions alone. The result is consistent association/entrapment of the neutral melamine with the clay during ion exchange.

WO 2004/039916 PCT/AU2003/001443 - 28 Example 2b: Preparation of melamine hydrochloride modified montmorillonite in the presence of melamine (IOH2) 5 3.0Kg of sodium montmorillonite was dispersed into 200L de-ionized water at 60 0 C with vigorous stirring (200 rpm) adding the powder slowly over a period of approximately one hour to assist wetting out of the individual particles/platelets. After the suspension had stirred at 10 that temperature for approximately 2 hours, an aqueous solution (35L) containing 1.39 Kg melamine and 0.92L HCl (9.65M) at 85 0 C was rapidly added whilst the impeller speed was simultaneously increased to 300 rpm. After an initial period of high viscosity whilst the modified 15 montmorillonite aggregated, the viscosity decreased and the clay solution was allowed to stir for a further 3 hours at 60'C. Following filtration of the suspension the collected modified clay was re-dispersed into de-ionized water (150L) and allowed to stir for 1 hour at 60'C before 20 an aqueous solution (10 L) containing 0.385Kg melamine and 0.26 L HCl (9.65M) at approx 85 0 C was added. At this point the mixture was stirred for a further two hours before it was filtered. Next the modified clay was re-dispersed into de-ionized water (150L) and stirred for a further 1 25 hour at 60 0 C prior to filtration, drying and grinding of the modified clay to a particle size less than 50 micron. XRD (CuKai source A = 0.154 nm) Cation Na* Melamine and Melamine.HCl modified Montmorillonite XRD dooi 1.10 nm 1.40 nm 30 These results illustrate that the robustness of the modification procedure to-variation in mole ratio of montmorillonite CEC to melamine salt and melamine and the reaction conditions employed to carry out the modification WO 2004/039916 PCT/AU2003/001443 - 29 procedure. This result is consistent association/entrapment of the neutral melamine with the clay during ion exchange. 5 Example 2c: Preparation of melamine hydrochloride modified montmorillonite in the presence of melamine (IOH2) 15.0Kg of montmorillonite was dispersed into 200L de 10 ionized water at 60'C with vigorous stirring (200 rpm) adding the powder slowly over a period of approximately 2 hours to assist wetting out of the individual particles/platelets. After the suspension had stirred at that temperature for approximately 4 hours, an aqueous 15 solution (50L) containing 2.78Kg melamine and 1.84 L HCl (9.65 M) at 85 0 C was rapidly added whilst the impeller speed was simultaneously increased to 300 rpm. After an initial period of high viscosity whilst the modified montmorillonite aggregated, the viscosity decreased and 20 the clay solution was allowed to stir for a further 3 hours at 60 0 C. Following filtration of the suspension the collected modified clay was re-dispersed into de-ionized water (150L) and allowed to stir for 1 hour at 60 0 C before an aqueous solution (25L) containing 1.925 Kg melamine and 25 1.3 L HCl (9.65M) at approx 85 0 C was added. At this point the mixture was stirred for a further two hours before it was filtered. Next the modified clay was re-dispersed into de-ionized water (200L) and stirred for a further 1 hour at 60'C prior to filtration, drying and grinding of 30 the modified clay to a particle size less than 50 micron. XRD (CuKa 1 source X = 0.154 nm) Cation Na* Melamine and Melamine.HCl modified Montmorillonite XRD dool 1.10 nm 1.40 nm WO 2004/039916 PCT/AU2003/001443 - 30 Results illustrate the robustness of the modification procedure to variation in reaction conditions employed to carry out the modification procedure. This result is consistent with association / entrapment of the 5 neutral melamine molecules with the clay during ion exchange. Example 3: Preparation of melamine cyanurate hydrochloride modified montmorillonite 10 (IOH3) Na' exchanged montmorillonite (Cation Exchange Capacity (CEC) = 92 meq/100g) was suspended in 95 0 C distilled water (2% w/w), cyanuric acid added (1.4 mmol/100g 15 montmorillonite) and the solution mechanically stirred at 1500 rpm for 60 min. Melamine mono-hydrochloride salt (1.4 mmol/100g montmorillonite) was then added to the solution and the resultant suspension with continued stirring for a further 150 min. Following filtration of 20 the suspension, the precipitate was thoroughly washed with warm distilled water and then preliminary dried (75 0 C). The resultant granular organically modified clay was ground to a particle size of less than 45 micron and then further dried at 60 - 80 0 C prior to processing or analysis. 25 XRD (CuKai source = 0.154 nm) Cation Na* Melamine cyanurate.HCl modified montmorillonite XRD do 0 1.10 1.42 nm nm Results from Example 3 indicate that the 30 intergallery spacing of montmorillonite is expanded further when exchanged with melamine cyanurate ion compared with sodium ion or melamine ion modified WO 2004/039916 PCT/AU2003/001443 - 31 montmorillonite alone (Example 1) due to its larger size and hence steric impact. Example 4: Preparation of melamine and melamine 5 cyanurate modified montmorillonite in presence of melamine and melamine cyanurate (IOH4) Montmorillonite exchanged Na* (Cation Exchange Capacity 10 (CEC) = 92 meq/100g) was suspended in 95 0 C distilled water (2% w/w), cyanuric acid added (1.4 mmol/100 g montmorillonite) and the solution mechanically stirred at 1500 rpm for 60 min. Melamine monohydrochloride salt (1.4 mmol/100g montmorillonite) and melamine (1.4 mmol/100g 15 montmorillonite) was then added to the solution and the resultant suspension continued stirring for a further 150 min. Following filtration of the suspension, the precipitate was thoroughly washed with warm distilled water and then preliminary dried under vacuum (75 0 C) . The 20 resultant granular organically modified clay was ground to a particle size of less than 45 micron and then further dried at 60 - 80 0 C prior to processing or analysis. XRD (CuKai source = 0.154 nm) 25 Cation Na+ Melamine and Melamine cyanurate.HCl modified montmorillonite XRD 1.10 1.53 nm dooi nm I The results from Example 4 indicate that the intergallery spacing of montmorillonite exchanged with melamine cyanurate ion in the presence of melamine and 30 melamine cyanurate is larger than both sodium ion or melamine cyanurate ion exchanged montmorillonite alone (Example 3). This result is consistent with WO 2004/039916 PCT/AU2003/001443 - 32 association/entrapment of the neutral melamine and melamine cyanurate with the clay during ion exchange. Example 5: Preparation of melamine and trimethyl 5 cetylammonium and melamine hydrochloride modified montmorillonite -(IOH5) Montmorillonite exchanged Na+ (Cation Exchange Capacity (CEC) = 92 meq/100g) was suspended in 90 0 C distilled water 10 (2% w/w), and the solution mechanically stirred at 1500 rpm for 60 min. Melamine monohydrochloride salt (1.4 mmol/100g montmorillonite) and trimethylcetylammoniun chloride (1.4 mmol/100g montmorillonite) was then added to the solution and the resultant suspension allowed to cool 15 with continued stirring for a further 150 min. Following filtration of the suspension, the precipitate was thoroughly washed with warm distilled water and then preliminary dried under vacuum (75 0 C) . The resultant granular organically modified clay was ground to a 20 particle size of less than 45 micron and then further dried at 60 - 80 0 C prior to processing or analysis. XRD (CuKai source 2 = 0.154 nm) Cation XRD doo 1 Na+ 1.10 nm Trimethylcetylammonium chloride 1.84 nm Melamine and Trimethylcetylammonium chloride 1.68 nm modified montmorillonite 25 The results from Example 5 indicate that the intergallery spacing of montmorillonite exchanged with both trimethylcetylammonium chloride and melamine hydrochloride is larger than sodium but smaller than 30 trimethylcetylammonium ion exchanged montmorillonite. This result is consistent with trimethylcetylammonium chloride WO 2004/039916 PCT/AU2003/001443 - 33 and melamine hydrochloride being present in the intergallery spacing of the modified montmorillonite. Example 6: Preparation of melamine and melamine 5 hydrochloride modified synthetic hetorite, laponite (IOH6) Hectorite clay (Synthetic Laponite RD) was modified using the same general procedure as employed in Example 2 taking 10 into consideration its lower cation exchange capacity (CEC) of 55 mmol/100g and employing a 1% solution for modification. Strict control was placed over the mole ratio of hectorite CEC and melamine salt to encourage platelet agglomeration. Following treatment with the 15 melamine salt/melamine, the modified synthetic clay was separated from the treatment solution by filtration. XRD (CuKai source = 0.154 nm) Cation Na'/Li* Melamine and Melamine.HCl Modified Hectorite XRD doo3 1.20 nm 1.33 nm 20 The results from Example 6 indicate that the intergallery spacing of synthetic hectorite exchanged with melamine hydrochloride in the presence of melamine is larger than sodium changed montmorillonite. 25 Melt Dispersion of Components and Formulation of Fire resistant Materials Examples 7-20 While each of the following examples use Nylon12, Nylon6 or Nylon66 as the polyamide based matrix, 30 the person skilled in the art will appreciate that the examples for fire retarding nylon12, nylon6 and nylon66 are also applicable to other types of polyamides, polyamide co-polymers, polyamide blends, alloys and the like.

WO 2004/039916 PCT/AU2003/001443 - 34 The formulation constituents employed in Examples 7 to 20 are provided in Tables 4a to 4e.

WO 2004/039916 PCT/AU2003/001443 - 35 I-q VI Hd +4*, 01 0 nC n 1k - )Nt P4C 6V) i - tt)N mI t\ or 0C, Ct( , ONCS0 0 00 00 0w000 00 1 NC 0, 0Ii * o- zqZe n0 Nr ?- - r - - - - - *rI ~ f 1 n\10I WO 2004/039916 PCT/AU2003/001443 -36 04 0 4J 1 rdn 0D N 0 0 E-1 WO 2004/039916 PCT/AU2003/001443 -37 A Cli A .2 * xn W0 xn 0 4 C - n W - - 4J I rC.' ta0 .2 in in t A~ 'n 0n ' -i Ci C in D 2'-' 0q~ ND moV T ~ I WO 2004/039916 PCT/AU2003/001443 - 38 in Ci n ni Rin in in 4.) xnV)kn 00 ro WO 2004/039916 PCT/AU2003/001443 -39 0 0 ( ;Ir (d ~ 00 - C1 WO 2004/039916 PCT/AU2003/001443 - 40 Example 7: Processing rheology (Table 5), XRD & TEM (Figure 2), mechanical (Table 6) and fire performance (Tables 7 & 8) of nylon12 modified with commercially available clay 5 during melt processing. The following example indicates that the processing rheology of Nylon 12 is not affected by the melt dispersion of commercially available 'organoclay' at least 10 partially on a nanometer scale (XRD). This dispersion results in improved mechanical performance and heat release rate as determined by cone calorimetry but poor performance compared with conventional flame retarded nylon 12(Nylon12 FR) in terms of vertical burn results 15 which is a primary tool used to discriminate material fire performance by governing bodies such as UL, ASTM, FAA and the like. As such these materials do not meet such performance s-tandards 20 Table 5 Torque Rheology Extrusion Torque Rheology Formulation Nylon12 1 2 3 4 Torque (Nm) 105 100 95 91 87 Batch mixer torque rheology Formulation Nylon12 3 5 6 Torque (Nm) 47 44 47 49 WO 2004/039916 PCT/AU2003/001443 - 41 Table 6 Mechanical Performance Formulation Nylon12 Nylon12 1 2 3 4 FR Modulus (MPa) 1110 1712 1187 1227 1470 1700 Tensile 36 48 53 52.3 57 44.6 Strength (MPa) I I I I I Impact (k/m 2 ) 4006 2200 6200 8100 6700 3700 Table 7 Fire Testing Cone Results 5 Formulation Peak Heat Mass Loss CO Prod" CO 2 Prod" SEA Reld Rate Kg/Kg Kg/Kg (Smoke) kW/m 2 g/m 2 s m 2 /Kg Nylon 12 FR 1800 18.6 0.01 1.2 100 Nylon12 1344 17.1 0.03 1.6 385 1 740 13.3 0.01 1.0 360 2 620 12.8 0.02 1.5 382 3 536 10.8 0.02 1.5 382 4 447 10.0 0.02 1.5 410 Table 8 Vertical Burn Results Formulation UL94 (3.2 mm) FAA (1.6 mm) Nylon 12 FR VO Pass Nylon12 LV HB Fail 1 V2 Fail 2 V2 Fail 3 Vi Fail 4 Vi Fail WO 2004/039916 PCT/AU2003/001443 - 42 Example 8: Processing (Table 9), XRD (Figure 3), mechanical (Table 10) and fire performance (Table 11-14) of nylon12 modified with commercially available clay and flame 5 retarding additives (melamine cyanurate) during melt processing The following example indicates that the processing rheology of Nylon 12 is not effected by the melt 10 dispersion of commercially available 'organoclay' at least partially on a nanometer scale (XRD) and flame retardant. This dispersion results in improved mechanical performance reduced heat release results via cone calorimetry and vertical burn performance for specimens greater than 1.6 15 mm thickness compared with conventionally flame retarded nylon12. Although samples of 0.75mm thickness provide good smoke and toxic gas release results they fail FAA type 12 sec vertical burn testing and perform badly in radiant panel tests. This indicates that the strategy is not 20 satisfactory to meet the performance of thin parts to the performance requirements of governing bodies such as the FAA. Table 9 Processing Rheology 25 Formulation Torque (Nm) Nylon 12 105 7 102 8 104 9 107 WO 2004/039916 PCT/AU2003/001443 - 43 Table 10 Mechanical Performance Formulation Tensile Tensile Strength Elongation Notched Impact Modulus (MPa) (MPa) at break (%) Strength (J/m 2 ) Nylon12 1110 36 640 4600 Nylon12 FR 1712 48.1 77 2100 7 1505 38.5 54 3100 8 1471 38.1 222 4100 9 1380 38.1 291 4600 Standard Deviation -Modulus<4%, Strength<3%, Elongation<10%, Impact <11% 5 Table 11 Fire Testing Cone Calorimetry Formulation Peak Heat Reld Mass Loss CO Prod" CO 2 Prod" SEA (Smoke) kW/m 2 Rate Kg/Kg Kg/Kg m 2 /Kg g/m 2 s Nylon 12 FR 1800 18.6 0.01 1.2 100 Nylon12 1344 17.1 0.03 1.6 385 7 670 13.9 0.01 1.6 220 8 695 14.1 0.01 1.6 240 9 782 16.1 0.01 1.7 280 Table 12 Vertical Burn Results 10 Formulation UL94 FAA 12s FAA 12s (3.2 mm) (1.6 mm) (0.75 nun) Nylon 12 FR VO Pass Fail Nylonl2 HB Fail Fail 7 VO Pass Fail 8 VO Pass Fail 9 VO Pass Fail WO 2004/039916 PCT/AU2003/001443 - 44 Table 13 Vertical Burn, Radiant Panel and Smoke Test Results (0.75mm) Formulation FAA 12s (0.75mm) Smoke Radiant Panel Ds 9 Fail 4.88 Full length burn 8 Fail 11.86 Full length burn 7 Fail 21.45 Full length burn 5 Table 14 Toxic Gas Emission Toxic Gas Formulation (ppm) 9 8 7 HF 3 3 5 HC1 1 1 3 HCN 4 4 4

H

2 S - NO, 2 2 1 HBr 1 1 1 P04 - SO 2 1 1 1 WO 2004/039916 PCT/AU2003/001443 - 45 Example 9: Processing rheology (Table 15), XRD (Figure 4), mechanical (Table 16) and fire performance (Table 17-19) of nylon12 modified with IOH2 incorporating 5 montmorillonite modified with melamine hydrochloride/melamine and flame retarding additives (melamine cyanurate) during melt processing 10 The following example indicates that the processing rheology of Nylon 12 is not effected by the melt dispersion of IH2 and flame retardant at least partially on a nanometre scale (XRD). Such dispersion results in improved mechanical and vertical burn results compared 15 with conventionally flame retarded nylon12. Samples of 0.75 mm provide good smoke and toxic gas release results, pass FAA type 12s vertical burn tests and perform better in radiant panel tests. It is known to those in the art that flame retarding thin polymeric based materials is 20 much more difficult than flame retarding thicker materials and as such meeting performance requirements at thin thickness'is an indication of superior fire retarding performance. 25 Table 15 Processing Rheology Formulation Extruder Torque (Nm) Nylon 12 105 11 105 12 106 13 103 WO 2004/039916 PCT/AU2003/001443 - 46 Table 16 Mechanical Performance Formulation Tensile Tensile Elongation at Notched Impact Modulus Strength break (%) Strength (J/m 2 ) (MPa) (MPa) Nylonl2 1110 36 640 4600 Nylonl2 FR 1712 48.1 77 2100 11 1443 39.7 140 3900 12 1398 39.0 215 4200 13 1349 38.9 375 4700 Standard Deviation -Modulus<3%, Strength<3%, Elongation<8%, Impact <9% 5 Table 17 Fire Performance - Vertical Burn Formulation UL94 12s FAA 12s FAA 60s FAA (3.2 mm) (1.6 mm) (0.75 mm) (0.75mm) Nylon12 FR VO Pass Fail Fail Nylon12 HB Fail Fail Fail 11 VO Pass Pass Pass 12 VO Pass Pass Pass 13 VO Pass Pass Pass WO 2004/039916 PCT/AU2003/001443 - 47 Table 18 Fire Performance (O.75um) Formulation FAA 12s Vertical Burn Smoke Radiant Panel Extinguishment time Ds Extinguishment Burn length time & Drip Extinguishment time Burn length 11 4.9s 6.79 5 sec 46mm 25 mm Os 12 2s 9.83 3 sec 19mm 25mm Os 13 OS 3.31 1 sec 21 mm 12.5 mm OS Table 19 Toxic Gas Emission 5 Toxic Gas Formulation Emission 13 12 11 (ppm) HF 6 4 3 HC 1 1 1 HCN 8 7 7

H

2 S NOx 3 2 2 HBr 1 1 1

PO

4 _- So 2 1 1 1 WO 2004/039916 PCT/AU2003/001443 - 48 Example 10: The following example illustrates the effect of different processing parameters on the mechanical performance (Table 20) and vertical burn performance (Table 21) of 5 formulation 13 which incorporates IOH2 + conventional flame retardant melamine cyanurate Results indicate the robustness of the formulation in 10 terms of mechanical and fire performance to different processing conditions such as through-put, temperature profile, screw speed for the given screw and barrel configuration provided in Figure 1. 15 Table 20 Mechanical Performance Conditions Tensile Tensile Notched Modulus Strength Impact (MPa) (MPa) Strength (J/m 2 ) Processing Screw Through Temp. speed put (Kg/h) (OC) (rpm) 180 300 1.5 1300 37.6 5100 190 300 1.5 1420 37.9 5300 200 300 1.5 1420 38.4 4800 210 300 1.5 1520 38.8 4600 200 150 1.5 1500 37.7 5300 200 400 1.5 1530 39.6 4100 200 300 15 1540 39.4 4100 Standard Deviation -Modulus<3%, Strength<3%, Impact <9% WO 2004/039916 PCT/AU2003/001443 - 49 Table 21 FAA 12s Vertical Burn Performance (0.75mm thickness) Conditions Result Flame out Time (sec) Processing Screw speed Through-put Temp.( 0 C) (rpm) (Kg/h) 180 300 1.5 Pass 5 190 300 1.5 Pass 4 200 300 1.5 Pass 2 210 300 1.5 Pass 6 200 150 1.5 Pass 2 200 400 1.5 Pass 7 200 300 15 Pass 3 5 Example 11: The following example illustrates the effect of different IOH2 (Example 2) and melamine cyanurate concentrations on mechanical and vertical burn performance of nylon12 (Table 22) 10 Results indicate that preferably more than 10% melamine cyanurate is required to pass FAA 12 s vertical burn test requirements at 0.75 mm thickness. Results also indicate that unlike classically flame retarded nylon12 this fire 15 performance is achievable whilst maintaining excellent mechanical properties relative to nylon12.

WO 2004/039916 PCT/AU2003/001443 - 50 Table 22 Performance of Formulations incorporating different concentrations of 1OH2 and Melamine cyanurate Formulation Tensile Tensile Notched Impact FAA 12s Vertical burn Modulus Strength Strength (Jim 2 ) (0.75mm) (MPa) (MPa) Ext. Time (s) Nylonl2 1100 36 4600 Fail (62) Nylon12 FR 1712 48.1 2100 Fail (24) 11 1443 39.7 3900 Pass (5) 12 1398 39.0 4200 Pass (5) 13 1349 38.9 4700 Pass (2) 14 1480 37.9 4200 Pass (14) 15 1410 39.4 4400 Pass (7) 16 1386 40.1 4800 Pass (6) 17 1483 37.9 3900 Fail (18) 18 1476 39.4 5050 Fail (19) 19 1404 40.1 5200 Fail (19) 20 1445 37.8 4200 Fail (32) 21 1420 39.7 4500 Fail (28) 22 1361 40.1 5200 Fail (32) 5 Example 12: The following example illustrates the effect of different conventional flame retardants on the performance (Table 23) of nylon12 incorporating an IOH2 (Example 2) 10 The results presented in Table 23 demonstrate that materials incorporating the IOH and melamine cyanurate provide both excellent mechanical and fire performance. Formulations containing melamine phthalate and pentaerythritol phosphate also provide excellent fire 15 performance with lower mechanical performance. Samples containing IOH with melamine cyanurate and Mg(OH) 2 provide the excellent mechanical performance in terms of impact, modulus, and strength also excellent vertical burn performance.

WO 2004/039916 PCT/AU2003/001443 - 51 Table 23 Performance of formulations incorporation 1OH2 and various conventional flame retardants Formulation Tensile Tensile Notched FAA 12s UL 94 Modulus Strength Impact vertical burn 3.2 mm (MPa) (MPa) Strength (0.75mm) (Jim 2 ) Ext. Time (sec) 12 1460 39 4800 Pass (2) VO 23 1500 41 3900 Fail (31) V2 24 1540 41.9 2500 Fail (26) V2 25 1500 40.4 3000 Fail (29) V2 26 - - - Pass (7) VO 27 1410 41.0 4100 Fail (24) V2 28 1420 43.5 1500 Fail (32) V2 29 1160 43.6 800 Pass (10) VO 30 1628 43.6 4800 Pass (4) VO 5 Example 13: The following example illustrates the effect of removing components of the fire resistant formulation on resultant fire performance (Table 24) 10 The results indicate that removal of either the modified inorganic-organic hybrid or melamine cyanurate from the formulation provides unsatisfactory vertical burn performance following FAA 12 s type testing at 0.75mm 15 thickness.

WO 2004/039916 PCT/AU2003/001443 - 52 Table 24 FAA type Vertical Burn Performance (0.75mm) Formulation Ext. Time (s) FAA requirement Nylon12 65 ±9 Fail 31 31±4 Fail 32 32 ±13 Fail 15 7 ±4 Pass Example 14: The following example illustrates the 5 mechanical and 12s vertical burn performance (Table 25) and cone calorimetry results (Table 26) of Nylon12 formulations prepared with IOH2 (Example 2), melamine cyanurate and magnesium hydroxide. Table 10 27 provides radiant panel, smoke, and 60s FAA type vertical burn results for the above mentioned formulations. Mechanical and vertical burn performance of Nylon12 formulations incorporating IOH2, melamine 15 cyanurate and magnesium hydroxide of different surface functionality and particle size distribution is provided in Table 28. 20 Results from Example 14 show that excellent processability, mechanical, vertical burn, and heat release results are obtainable with formulations incorporating IOH2, melamine cyanurate and low concentrations of magnesium hydroxide in particular 25 formulations incorporating IOH dispersed at least partially on a nanometre scale, melamine cyanurate and' 2.5% magnesium hydroxide which provides excellent mechanical, vertical burn and peak and average heat release results. The results also indicate that Mg(OH 2 ) of 30 different grades may be employed in conjunction with IOH2 and melamine cyanurate to produce formulations with excellent processability, mechanical and fire performance.

WO 2004/039916 PCT/AU2003/001443 - 53 Table 25 Mechanical Performance of nylon materials with various amounts of 1OH2 and conventional flame retardants Formulation MFI Tensile Tensile Notched FAA 12s Vertical (g/min) Modulus Strength Impact burn (MPa) (MPa) Strength Ext. Time (s) (J/m 2 ) (0.75mm) Nylon12 44 1100 36 4600 Fail (62) Nylon12 FR 32 1712 48.1 2100 Fail (24) 33 12.6 1470 41.8 4500 Fail (18) 34 12.0 1460 41.1 4700 Pass (10) 35 11.5 1430 39.9 5200 Pass (9) 36 13.4 1578 43 3800 Pass (6) 30 13.5 1509 42 4800 Pass (4) 37 13.5 1543 40.5 5300 Pass (6) 38 13.4 1529 41 3900 Fail (41) 39 13 1520 40.6 4200 Fail (19) 40 13.1 1510 41.6 4600 Pass (4) 5 Table 26 Cone Calorimeter Heat Release Results Formulation Peak Heat 300s Average Release Heat Release (kW/m 2 ) (kW/m 2 ) Nylon12 1100 748 Nylon12 FR 1712 640 18 1314 707 21 1643 680 12 1595 676 39 1147 552 30 1001 578 34 885 491 WO 2004/039916 PCT/AU2003/001443 - 54 Table 27 Comparison of fire performance of various formulations containing IOH2 dispersed at least partially on a nanometre scale, melamine cyanurate and optionally magnesium hydroxide H7 5 Formulation Radiant Panel Smoke Toxic Gas FAA 60 Second Extinguishment Ds (FAA Vertical burn time & requirement) (0.75mm) Burn length (Extinguishment time (average) seconds) Nylon12 - 21 Pass 22 - 11.7 Pass 21 - 10.4 Pass 20 - 7.8 Pass 19 - 11.3 Pass 18 - 11.4 Pass Fail (20) 17 - 8.1 Pass Pass (9) 13 1 second 14.5 Pass Pass (0) 12.4 mm 12 - 14.4 Pass Pass (0) 11 - 7.5 Pass Fail (133) 39 - 15 Pass Fail (58) 30 - 14.5 Pass Pass (15) 34 2.5 second 11.3 Pass Pass (7) 15.0 mm WO 2004/039916 PCT/AU2003/001443 - 55 Table 28 Performance of materials. incorporating 1OH2 melamine cyanurate and Mg(OH) 2 with various particle size and surface functionality Formulation MFI Tensile Tensile Notched FAA 12s (g/min) Modulus Strength Impact Vertical burn (MPa) (MPa) Strength Ext. Time (s) (J/m 2 ) (0.75mm) 34 13.5 1480 40.4 5100 Pass (6) 41 11.5 1420 41 5000 Pass (6) 42 16.2 1470 40.2 5300 Pass (13) 44 12.4 1470 40.4 5300 Pass (14) 5 Example 15: The following example illustrates the mechanical and vertical burn performance (Table 29) of Nylon12 formulations prepared with the inorganic-organic hybrids outlined 10 in Examples 1, 2 & 4 and melamine cyanurate The results indicate superior fire performance of nylon12 formulations containing the intercalated and modified IOH (Examples 2 and 4) compared with that prepared with just 15 melamine hydrochloride modified IOH (Example 1). Table 29 Mechanical and Vertical Burn Performance Formulation Tensile Tensile Notched 0.75 mm FAA 12 sec Strength Modulus Impact Vertical Burn (MPa) (MPa) Strength J/m 2 (Ext. time sec) 44 41.7 1490 5000 Fail (22) 45 39.5 1531 4100 Pass (12) 46 40.1 1580 4600 Pass (2) 47 39.2 1550 4100 Pass (5) 18 40.4 1590 4700 Fail (19) 12 39.3 1628 4000 Pass (3) Standard Deviation -Modulus<5%, Strength<5%, Impact <10% WO 2004/039916 PCT/AU2003/001443 - 56 Example 16: The following example illustrates the performance of nylon6 and nylon66 formulations incorporating IOH2 and 5 melamine cyanurate The results indicate that IOH2 at least partially dispersed on a nanometre scale in conjunction with melamine cyanurate provides excellent mechanical and 10 vertical burn performance relative to nylon6 and nylon66. Table 30 Mechanical .and Vertical Burn Performance Formulation Tensile Tensile Notched FAA 12s Vertical Modulus Strength Impact burn (MPa) (MPa) Strength Ext. Time (s) (J/m 2 ) (0.75mm) Nylon6 2720 76 1900 Fail (61) 48 2970 73.5 2000 Pass (1) Nylon66 2890 83.5 1900 Fail (65) 49 3500 67 1900 Pass (1) 15 Example 17: The following example shows the XRD of nylon 12 formulations incorporating modified and intercalated hectorite (Example 6) dispersed at least partially on a nanometre scale (Figure 5) and melamine 20 cyanurate and the formulations vertical burn performance (Table 31) The XRD results indicate that hectorite is modified owing to its larger intergallery spacing compared with the 25 starting material. Nylon12 incorporating IOH5 at least partially dispersed on a nanometre scale (Figure 5) and melamine cyanurate show excellent fire performance.

WO 2004/039916 PCT/AU2003/001443 - 57 Table 31 Vertical Burn Performance Formulation FAA 12s Vertical burn, Ext. Time (s)(0.75mm) Nylon12 Fail (68) 50 Pass (2) Example 18: This example shows the rheology (Table 32) 5 and mechanical and vertical burn performance (Table 33) of formulations incorporating IOH2, conventional flame retardant and minor processing additives. 10 This example illustrates that reductions in viscosity across a range of shear rates of the formulations incorporating nylon12, IOH2 and conventional flame retardants through the addition of (additional) minor processing additives during processing. This reduction in 15 viscosity is possible with out a significant reduction in mechanical performance and generally without compromising fire performance particularly under the stringent conditions required to fire retard thin materials to meet performance standards outlined by various regulatory 20 bodies.

WO 2004/039916 PCT/AU2003/001443 - 58 Table 32 Rheology of formulations at different shear rates and corresponding MFI data Formulation Shear rate MFI 10.2 10-1 100 101 Viscosity (Pas) g/min Nylon12 223 169 106 108 35 13 13100 1750 300 124 29 34 719 624 560 502 13 51 4800 1040 226 128 34 52 1920 6590 1560 95 39 53 1100 865 168 95 39 54 554 865 162 95 41 55 98300 1930 335 143 33 56 13500 1870 284 106 31 5 Table 33 Mechanical and Vertical Burn Performance Formulation Tensile Tensile Notched 0.75 mm FAA 12 sec Modulus Strength Impact Vertical Burn (MPa) (MPa) Strength (Extinguishment (J/m 2 ) time (s)) Nylon12 1100 36 4600 Fail (62) 13 1349 38.9 4700 Pass (2) 34 1480 40.4 5100 Pass (6) 51 1215 35.8 3500 Pass (3) 52 1165 35.5 3500 Pass (2) 53 1233 36.4 3500 Pass (13) 54 1176 35.3 3300 Fail (25) 55 1168 33.3 3300 Pass (8) 56 1241 35 3700 Pass (10) WO 2004/039916 PCT/AU2003/001443 - 59 Example 19: This example provides the mechanical and fire performance (Table 34) of nylon12 formulations incorporating IOH2, conventional flame retardants and minor 5 component of stabilizer. The results indicate that the mechanical and vertical burn performance of formulations containing nylon12, 1OH2 conventional flame retardant is not significantly reduced 10 by addition of additional stabilizer to the formulation during compounding. Table 34 Mechanical and Vertical Burn Performance Formulation Tensile Tensile Notched 0.75 mm FAA 12 Modulus Strength Impact sec Vertical Burn (MPa) (MPa) Strength (Extinguishment J/m 2 time (s)) Nylon12 1100 36 4600 Fail (62) 13 1349 38.9 4700 Pass (2) 57 1394 39.1 4800 Pass (4) 15 Example 20: This example shows that formulations incorporating IOH's may not only be fabricated into materials, components and parts of components by processes such as 20 extrusion, injection moulding, compression moulding and alike but also by low shear processes such as rotational moulding (Figure 6) and selective laser sintering. 25 Figure 6 provides examples of components manufactured by rotational moulding employing formulations incorporating 1OH2, melamine cyanurate optionally magnesium hydroxide and other additives such as but not limited to formulation 13 and 34. The examples illustrate that such formulations 30 show suitable thermal / oxidative stability and melt - 60 rheology for manufacturing components under low shear and thermally demanding environments. It will be appreciated by persons skilled in the 5 art that numerous variations and/or modifications may be made to the invention as shown in the specific embodiments without departing from the spirit or scope of the invention as broadly described. The present embodiments are, therefore, to be considered in all respects as 10 illustrative and not restrictive. It is to be understood that, if any prior art publication is referred to herein, such reference does not constitute an admission that the publication forms a part of the common general knowledge in the art, in Australia 15 or any other country. N:\Melbourne\Ca0e0\Patent\47000-47999\P47669.AU.1\Specis\Amendmente.doc 10/03/09

Claims

1. An inorganic-organic hybrid (IOH) which comprises: 5 (i) an expandable or swellable layered inorganic component; and (ii) an organic component including at least one ionic organic component. 10

2. An IOH according to claim 1, in which the organic component also includes one or more neutral organic components which are intercalated between and/or associated with the layer(s) of the inorganic component. 15

3. An IOH according to claim 1 or claim 2, in which the inorganic component is rendered positively or negatively charged due to isomorphic substitution of elements within the layers. 20 4. An IOH according to any one of claims 1 to 3, in which the inorganic component is selected from a 1:1 layered silicate structure, a 2:1 layered silicate structure, a double hydroxide of the general formula Mg 6 Al3.

4 (OH)18.8 (CO 3 )1.7.H 2 0 and a synthetically prepared 25 layered material.

5. An IOH according to any one of claims 1 to 4, in which the inorganic compound is a naturally occurring or a synthetic analogue of a phyllosilicate. 30

6. An IOH according to claim 5, in which the naturally occurring or synthetic analogue of a phyllosilicate is a smectite clay. 35 7. An IOH according to claim 6, in which the smectite clay is selected from montmorillonite, nontronite, beidellite, volkonskoite, hectorite, - 62 6. An IOH according to claim 5, in which the smectite clay is selected from montmorillonite, nontronite, beidellite, volkonskoite, hectorite, bentonite, saponite, sauconite, magadiite, kenyaite, 5 laponite, vermiculite, synthetic micromica and synthetic hectorite.

7. An IOH according to claim 5 or claim 6, in which the naturally occurring phyllosilicate is selected from 10 bentonite, montmorillonite and hectorite.

8. An IOH according to any one of claims 4 to 7, in which the phyllosilicate has a platelet thickness less than about 5 nanometers and an aspect ratio greater than 15 about 10:1, greater than about 50:1 or greater than about 100:1.

9. An IOH according to any one of claims 1 to 8, in which the inorganic component includes interlayer or 20 exchangeable metal cations to balance the charge.

10. An IOH according to claim 9, in which the metal cation is selected from an alkali metal and alkali earth metal. 25

11. An IOH according to claim 10, in which the alkali or alkali earth metal is selected from Na*, K+, Mg 2 . and Ca2. 30

12. An IOH according to any one of claims 9 to 11, in which the cation exchange capacity of the inorganic component is less than about 400 milli-equivalents per 100 grams. 35

13. An IOH according to any one of claims 9 to 12, in which the ionic organic component is exchanged with the exchangeable metal ions of the inorganic component. N:\Melbourne\Ca0eo\Patent\47000-47999\P47669.AU.1\Specio\Amendmento.doc 10/03/09 - 63

14. An IOH according to any one of claims 1 to 13, in which the ionic species contains onium ion(s). 5

15. An IOH according to claim 14, in which the ionic species containing onium ion(s) is an ammonium, phosphonium or sulfonium derivative of an aliphatic, aromatic or aryl-aliphatic amine, phosphine or sulfide. 10

16. An IOH according to any one of claims 1 to 15, in which the ionic or neutral organic component is a neutral or ionic derivative of a nitrogen based molecule.

17. An IOH according to claim 16, in which the 15 nitrogen based molecule is a triazine based species.

18. An IOH according to claim 17, in which the triazine based species is selected from melamine, triphenyl melamine, melam (1,3,5-triazine-2,4,6-triamine 20 n-(4,6-diamino-1,3,5-triazine-yl)), melem ((-2,5,8 triamino-1,3,4,6,7,9,9b-heptaazaphenalene)), melon (poly{8-amino-1,3,4,6,7,9,9b-heptaazaphenalene-2,5 diyl)imino}), bis and triaziridinyltriazine, trimethylsilyltriazine, melamine cyanurate, melamine 25 phthalate, melamine phosphate, melamine phosphite, melamine phthalimide, dimelamine phosphate, phosphazines, low molecular weight polymers with triazine and phosphazine repeat units and isocyanuric acid and salts or derivatives thereof. 30

19. An IOH according to claim 18, in which isocyanuric acid and salts or derivatives thereof are selected from isocyanuric acid, cyanuric acid, triethyl cyanurate, melamine cyanurate, trigylcidylcyanurate, 35 triallyl isocyanurate, trichloroisocyanuric acid, 1,3,5 tris(2-hydroxyethyl)triazine-2,4,6-trione, hexamethylenentetramine.melam cyanurate, melem cyanurate N: \Melbourne\Cases\Patent\47000-47999\P47669.AU. 1\Specie\Amendmentn.doc 10/03/09 - 64 and melon cyanurate.

20. An IOH according to any one of claims 16 to 19, in which the organic component is a derivative of 5 phosphoric acid or boric acid.

21. An IOH according to claim 20, in which the derivative of phosphoric acid or boric acid is selected from ammonia polyphosphate, melamine polyphosphate and 10 melamine phosphate ammonium borate.

22. An IOH according to any one of claims 1 to 21, in which the ionic organic component is used in combination with other ionic compounds which are capable of improving 15 compatibility and dispersion between the inorganic and organic components.

23. An IOH according to claim 22, in which the other ionic compound is an amphiphilic molecule that 20 incorporates a hydrophilic ionic group along with hydrophobic alkyl or aromatic moieties.

24. An IOH according to any one of the preceding claims, which further comprises one or more coupling 25 reagents.

25. An IOH according to claim 24, in which the coupling reagent is selected from an organically functionalised silane, zirconate and titanate. 30

26. An IOH according to claim 25, in which the silane coupling reagent is tri-alkoxy, acetoxy or halosilanes functionalised with amino, epoxy, isocyanate, hydroxyl, thiol, mercapto and/or methacryl reactive moieties or 35 modified to incorporate functional groups based on triazine derivatives, long chain alkyl, aromatic or alkylaromatic moieties. N:\Melbourne\Cases\Patent\47000-47999\P42669.AU.1\Specis\Amndmento-doc 10/03/09 - 65

27. A method for the preparation of the IOH defined in any one of claims 1 to 26, which comprises mixing components (i) and (ii) defined in any one of claims 1 to 5 28 or constituents thereof in one or more steps.

28. A method according to claim 27, in which mixing is achieved using melt, solution or powder processing. 10

29. A method according to claim 27 or claim 28, in which the mixing is achieved using solution processing.

30. Use of the IOH defined in any one of claims 1 to 26 as a fire resistant material. 15

31. A fire resistant formulation which comprises: (i) the IOH defined in any one of claims 1 to 26; and (ii) one or more flame retardants. 20

32. A formulation according to claim 31, in which the flame retardant is selected from phosphorus derivatives, nitrogen containing derivatives, molecules containing borate functional groups, molecules containing two or more alcohol groups, molecules which endothermically release 25 non-combustible decomposition gases and expandable graphite.

33. A formulation according to claim 32, in which the phosphorus derivatives are selected from melamine 30 phosphate, dimelamine phosphate, melamine polyphosphate, ammonia phosphate, ammonia polyphosphate, pentaerythritol phosphate, melamine phosphite and triphenyl phosphine.

34. A formulation according to claim 32 or claim 33, 35 in which the nitrogen containing derivatives are selected from melamine, melamine cyanurate, melamine phthalate, melamine phthalimide, melam, melem, melon, melam N:\Melbourne\CaseO\Patent\47000-47999\P42669.AU.1\Specie\Amendmenta.doc 10/03/09 - 66 cyanurate, melem cyanurate, melon cyanurate, hexamethylene tetraamine, imidazole, adenine, guanine, cytosine and thymine. 5

35. A formulation according to any one of claims 32 to 34, in which the molecules containing borate functional groups are selected from ammonia borate and zinc borate.

36. A formulation according to any one of claims 32 10 to 35, in which the molecules containing two or more alcohol groups are selected from pentaerythritol, polyethylene alcohol, polyglycols and carbohydrates.

37. A formulation according to any one of claims 32 15 to 36, in which the molecules which endothermically release non-combustible decomposition gases are selected from magnesium hydroxide and aluminum hydroxide.

38. A method for the preparation of the fire 20 resistant formulation defined in any one of claims 31 to 37, which comprises mixing components (i) and (ii) as defined in any one of claims 1 to 28 or constituents thereof in one or more steps. 25

39. A method according to claim 38, in which mixing is achieved using melt, solution or powder processing.

40. A method according to claim 38 or claim 39, in which the mixing is achieved using melt processing in a 30 twin screw extruder or batch mixer; or powder processing using a high shear powder mixer or milling procedures.

41. A polyamide fire resistant formulation which comprises either: 35 (A) (i) the IOH defined in any one of claims 1 to 26; and (ii) a polyamide based matrix; or N:\Melbourne\Caaeo\Patent\47000-47999\P47669.A.1\Specis\Amendments.doc 10/03/09 - 67 (B) (i) the fire resistant formulation defined in any one of claims 31 to 37; and (ii) a polyamide based matrix. 5

42. A formulation according to claim 41, in which the polyamide based matrix comprises generic groups with repeat units based on amides selected from Nylon4, Nylon6, Nylon7, Nylon 11, Nylon12, Nylon46, Nylon66, Nylon 68, Nylon610, Nylon612 and aromatic polyamides and co 10 polymers, blends or alloys thereof.

43. A formulation according to claim 41 or claim 42, in which the polyamide based matrix is selected from Nylon12, Nylon6 and Nylon66 and co-polymers, alloys or 15 blends thereof.

44. A formulation according to any one of claims 41 to 43, which further comprises one or more additives. 20

45. A formulation according to claim 44, in which the additives are selected from polymeric stabilisers; lubricants; antioxidants; pigments, dyes or other additives to alter the materials optical properties or colour; conductive fillers or fibers; release agents; slip 25 agents; plasticisers; antibacterial or fungal agents; and processing agents.

46. A formulation according to claim 45, in which the polymeric stabiliser is a UV, light or thermal stabilizer. 30

47. A formulation according to claim 45 or claim 46, in which the processing agents are selected from dispersing reagents, foaming or blowing agents, surfactants, waxes, coupling reagents, rheology modifiers, 35 film forming reagents and free radical generating reagents. N:\Melbourne\Cases\Patent\47000-47999\P47669.AU.l\Specis\Amendmenta.doc 10/03/09 - 68

48. A formulation according to any one of claims 41 to 47, in which the polyamide based matrix is Nylon12, Nylon6 and/or Nylon66; the IOH is montmorillonite or hectorite modified with melamine hydrochloride and/or 5 melamine cyanurate hydrochloride and/or melamine and/or melamine cyanurate; and the flame retardant is melamine cyanurate and/or magnesium hydroxide; and the additive is a processing agent and/or a polymeric stabiliser. 10

49. A formulation according to any one of claims 44 to 48, in which the polyamide based matrix is present in an amount of about 45 to about 95% w/w, the IOH is present in an amount less than about 25% w/w and the flame retardant and/or additives are present in an amount less 15 than about 30% w/w.

50. A formulation according to any one of claims 44 to 49, in which the polyamide based matrix is present in an amount greater than about 75% w/w, the IOH is present 20 in an amount less than about 3% w/w, the melamine cyanurate flame retardant is present in an amount of about 11 to about 15% w/w and additives are present in an amount of about less than about 4% w/w. 25

51. A formulation according to any one of claims 44 to 49, in which the polyamide based matrix is present in an amount greater than about 75% w/w, the IOH is present in an amount less than about 3% w/w, the melamine cyanurate flame retardant is present in an amount of about 30 11 and about 15% w/w, magnesium hydroxide flame retardant present in an amount of about 1 and about 5% w/w and additives are present in an amount less than about 4% w/w.

52. A method for the preparation of the polyamide 35 fire resistant formulation defined in any one of claims 41 to 51, which comprises dispersing the IOH as defined in any one of claims 1 to 26 or the fire resistant N:\Melbourne\Cases\Patent\47000-47999\P4 7669.AU.1\Specia\Amendm ta. doc 10/03/09 - 69 formulation defined in any one of claims 31 to 37 or constituents thereof into the polyamide based matrix in one or more steps. 5

53. A method according to claim 52, in which at least some of the components are ground prior to mixing.

54. A method according to claim 53, in which the components are ground to a particle size less than about 10 200 microns.

55. A method according to claim 53 or claim 54, in which dispersion is achieved using melt, solution or powder processing. 15

56. A method according to any one of claims 53 to 55, in which the dispersion is achieved using melt processing in a single or twin screw extruder, batch mixer or continuous compounder. 20

57. A method according to claim 56, in which the melt processing is conducted in a twin screw extruder.

58. A method according to any one of claims 52 to 57, 25 in which the dispersion occurs at a sufficient shear rate, shear stress and residence time to disperse the IOH at least partially on a nanometer scale.

59. A fire resistant article or parts thereof which 30 is composed wholly or partly of the IOH as defined in any one of claims 1 to 26 and/or fire resistant formulation defined in any one of claims 31 to 37 and claims 41 to 51.

60. A fire resistant article or parts thereof as 35 defined in claim 59, which is used in transport, building, construction, electrical or optical applications. N:\Melbourne\Caoe\Patent\47000-47999\P47669.AU.\Speci\Amendmente.doc 10/03/09 - 70

61. A fire resistant article or parts thereof as defined in claim 60, in which the transport application is air, automotive, aerospace or nautical. 5

62. A fire resistant article or parts thereof as defined in any one of claims 59 to 61, which is a hollow article or sheet.

63. A fire resistant article or parts thereof as 10 defined in any one of claims 59 to 63 which is selected from pipes, ducts, fabric, carpet, cables, wires, fibres, Environmental control systems, stowage bin hinge covers, cable trays, ECS duct spuds, latches, brackets, passenger surface units and thermoplastic laminate sheet. 15

64. A fire resistant hollow article or parts thereof which is composed wholly or partly of he fire resistant formulation defined in claim 50 or claim 51 and manufactured by rotational moulding or extrusion. 20

65. A fire resistant fibre, fabric, carpet or parts thereof which is composed wholly or partly of the fire resistant formulation defined in claim 50 or claim 51 and manufactured by melt spinning or extrusion. 25

66. A fire resistant article or parts thereof which is composed wholly or partly of the formulation defined in claim 50 or claim 51 and manufactured by sintering. 30

67. A fire resistant article or parts thereof which is composed wholly or partly of the fire resistant formulation defined in claim 50 or claim 51 and manufactured by injection or compression moulding. 35

68. A method of preparing the fire resistant article or parts thereof defined in any one of claims 59 to 67, which comprises moulding or forming the IOH as defined in N:\Melbourne\Case0\Patent\47000-47999\P47669.AU.l\Speci/\Amendmento.doc 10/03/09 - 71 any one of claims 1 to 28 and/or the fire resistant formulation or constituents thereof as defined in any one of claims 31 to 37 and claims 41 to 47. 5

69. A method according to claim 68, in which the moulding or forming is carried out using extrusion, injection moulding, compression moulding, rotational moulding, blow moulding, sintering, thermoforming, calending or combinations thereof. 10

70. Inorganic-organic hybrids (IOHs), methods for their preparation, fire resistant formulations containing them or fire resistant articles or parts thereof composed wholly or partly of them, substantially as herein 15 described with reference to the accompanying examples. N:\Melbourne\Caseo\Patent\470DO-47999\P47669.AU.1\Specio\Amendmenta.doc 10/03/09