AU2004233501B2 - Structured occlusive dressings - Google Patents

Description

P/00/011 Regulation 3.2

AUSTRALIA

Patents Act 1990 COMPLETE SPECIFICATION STANDARD PATENT Invention Title: Structured occlusive dressings The following statement is a full description of this invention, including the best method of performing it known to us: -2- STRUCTURED OCCLUSIVE DRESSINGS Field of the Invention 0 Z This invention relates to a structured wound dressing which remains in c place and does not flow, but has an ointment-like feel. The invention also relates to adhesive bandages comprising the aforementioned structured SBackground of the Invention For many years, people have cared for wounds or other skin insults using c absorbent bandages as coverings. It is well-documented ("Epidermal Wound Healing", H.I. Maibach, D.T. Rovee, editors, Year Book Medical Publishers, Inc. 1972) that wounds heal faster when covered and kept moist while being protected from additional abrasion and exposure.

In order to protect the wound further from becoming infected, some individuals apply antiseptic or antibiotic agents to the wound prior to bandaging. These medicinal agents may be applied in the form of a liquid, or a water-in-oil emulsion such as an ointment or cream. However, these formulations tend to run, in the case of liquids, or ooze out from under the bandage. Thus, maintaining the position of the medicinal agent in close proximity to the wound in order to impart medicinal activity to the wound is quite difficult. It would be desirable for such consumers to be able to apply a medicament which will not migrate from the wound, a "structured" dressing.

This object, however, is quite difficult to achieve. For example, many of the ointments used in antiseptic and antibiotic formulations are petrolatum-based. However, by their nature, ointments, particularly ointments based on petrolatum, flow fairly easily. Consumers feel comfortable using such petrolatum-based products and are accustomed to the sensation of wearing the ointment in conjunction with adhesive bandages. Thus, any attempt at creating a stable, "structured" base for medicinal application should have an ointment "feel".

IN Many individuals apply adhesive bandages to their smaller cuts and

(N

abrasions. Similarly, they apply gauze or other types of coverings to larger skin wounds. It would be highly desirable for such wound- Scoverings to have, incorporated within their structures, medicinal agents 1 to combat wound infection. This would afford consumers a great convenience. Conventional ointments and pretrolatum-based formulations tend to be too runny and messy for incorporation with a wound-covering material.

Therefore, it is an object of this invention to provide a composition for making a structured dressing as well as a structured occlusive dressing incorporating the composition.

Additional objects will become evident in the ensuing description of the invention.

Summary of the Invention This invention thus provides a composition for making a structured dressing comprising: a) about 50 to 95% by weight of at least one a hydrophobic solvent base compound; b) about 0.5 to 10% by weight of at least one a network polymer; and c) about 0.5 to 40% by weight of a flow control agent; and Melbourne\004481212 Printed 7 October 2004 (9:42) d) at least one agent selected from the group consisting of antiseptics, antibiotics, anaesthetics, anti-inflammatories, 0 Z antimicrobials, skin care agents and therapeutics and antipyretics.

(N

The invention further provides a structured occlusive dressing comprising a composition as defined in the preceding paragraph.

The structured occlusive dressings of this invention may be applied directly to the skin, or they may be incorporated into a combination (I dressing and be attached directly to a substrate such as a covering material or bandage. The covering material may be a woven or nonwoven fabric or a film material, or a combination thereof.

Brief Description of the Drawings Figure 1 is a plot showing viscosity as a function of temperature for petrolatum and for one of the occlusive compositions of the present invention; Figure 2 is a plot showing viscosity as a function of shear rate for petrolatum and for another of the occlusive compositions of the present invention; Figure 3 is a semi-log plot showing viscosity as a function of temperature for yet another occlusive composition of the present invention and a composition (Comparative Example A) prepared for purposes of comparison; Melbourne\004481212 Printed 7 October 2004 (9:42) S Figure 4 is a semi-log pl-ot similar to that shown in Z Figure 3;

ID

Figure 5 is a log-log plot showing the shear compliance of petrolatum, six occlusive compositions of the present O invention and a composition (Comparative Example B) Sprepared for purposes of comparison; Figure 6 is a perspective,, with portions cut away, of an adhesive bandage comprising- one of the occlusive compositions of the present invention; Figure 7 is a side view, partially in section, of the adhesive bandage illustrated in Figure 6 wherein the adhesive bandage further comprises release tabs; Figure 7A is a fragmentary view, greatly enlarged and partially in section, of a portion of the adhesive bandage of Figure 7; Figure 8 is a sectional side view of a typical test specimen; Figure 9 is a graph of the release force required to remove a release tab from a porous covering material as a function of the percent open.area of the porous covering material; Figure 10 is a schematic view showing the manufacture of the adhesive bandage shown in Figure 7; and Figure 11 is a longitudinal section of another embodiment of an adhesive bandage of the present invention in which 6 the porous covering-material has been given an alternative

O

0 configuration.

DO

Cl Detailed Description of the Preferred Embodiments The compositions of this invention generally contain a V hydrophobic solvent or a combination of hydrophobic c solvents and other additives resulting in a structured dressing that does not readily flow.. The structured dressings of this invention may be an oil-phase CI composition or a water-in-oil emulsion.

The hydrophobic solvent may be a hydrocarbon material, such as petrolatum, mineral oil or the like. It may also be composed of fatty acids such as castor oil or similar material. Alternatively, the hydrophobic solvent constituent may contain a wax in addition to other solvents,, such- as paraffin wax, microcrystalline wax, beeswax or the like. This element of the composition serves as the "oil base" of the solvent or the emulsion and makes up a large proportion of the composition, up to This solvent imparts.the ointment "feel" to the composition. The solvent also provides occlusion, contributes to the regulation of drug delivery and is the primary means by which the dressings of this invention achieve superior wound release characteristics.

Preferably, it is a fluid, semi-solid or solid at room or skin temperature (from-about 550F to about 100°F) having a viscosity of from about 1 to about 100,000 centipoise.

Thus, any hydrocarbon material or combination of materials which have the appropriate- viscosity at .the desired temperatures may be 'used in the products of this invention.

c 7- O A combination of members of two classes of polymers and/or Z additives should be added to the hydrophobic solvent to IND make the compositions of this invention. The first class of polymers can be generally termed "network" polymers.

These polymers increase the viscosity of the- solvent or emulsion and provide gel strength to. the solvent or Semulsion. The second class of polymers can be generally termed "flow control" polymers, which assist in controlling the flow characteristics of the dressings of 10 this invention.

c-i Gel strength can be measured by the relationship between the viscosity of the composition and temperature. Network polymers show a "plateau" in this type of measurement, the viscosity of the composition displays little or no change over a wide temperature range. The value of the viscosity at this plateau is defined as the gel strength.

Preferably, in the compositions of this invention, the gel strength-should be from about 1000 to about 10,000 poise over a temperature range of from about 50 0 C to 95 0

C.

Gel strength is particularly important in manufacturing and processing sterile bandages and wound dressings. The products are often subjected to ethylene oxide sterilization processes at high temperatures (about 175- 180 0 F, 80-82 0 The products of this invention should be able to withstand such temperatures without causing the structured ointments of this invention to flow readily into the primary packaging or into the pressure sensitive adhesive. Such ready flow would compromise sterility or affect the ability of adhesive to adhere to skin.

Preferably, the polymers that are useful in the compositions of this invention to create gel strength are -1 8 block copolymers. Di-, tri- and multiarm block copolymers Z of polystyrene and synthetic rubber where the rubber is 0 preferably isoprene, ethylene butadiene, ethylene propylene or the like or combinations thereof are useful as network polymers in the dressings of.this invention.

Examples of such polymers are Kraton* di- and tri-block copolymers commercially available from the Shell Chemical SCompany and the like. The Kraton* polymers are described by the Shell Chemical Company as elastomers which have a combination of high strength and low viscosity. These polymers contain block segments of styrene monomer units and rubber monomer units.

Polyacrylic acids which are slightly crosslinked such as the Carbopols*, commercially available from B.F. Goodrich, are .also useful as network polymers in the products of this invention. Polyacrylic acids of this type and other polymers such as polyethylene oxide, cellulosics and polysaccharides act as network polymers and may also contribute to maintaining moisture in the wound.. The Aquasorb-D series from Hercules Corporation, which is modified guar gums are examples of .modified polysaccharides which are useful in the compositions of this invention by maintaining gel strength. Preferably, one Carbopol* polyacrylic acid that would be useful in the compositions of this invention is 934P, It contains the following monomers: acrylic acid monomers with aikyl sucrose as.the crosslinker.

The second class of polymers or additives useful in the compositions of this invention are the "flow control polymer'", which are chosen to assist in controlling flowability in processing the structured ointment at or about room temperature and film-forming capacity. This 9 >lends a more film-like structure to the dressings of this

O

z invention as opposed to a gel-like structure. Film-like ND characteristics are important so as to lend greater CI integrity at usage temperatures. However, the flowability should not be so great as to permit the compositions to migrate from their desired positions in use on a wound.

SThe second class of.agents, polymers or additives useful in the compositions of this invention also assist in achieving an "ointment *feel" to the dressings of this CI invention. This "ointment feel" can be quantified as the value- of the shear elastic compliances and loss compliances of the compositions measured at skin temperatures, (approximately 35 0 C) at a testing frequency of 10 radians/second as measured on a Rheometrics RDS 7700 rheometer.

Petrolatum, for example, has a very high .shear compliance, greater than 5 x 10 5cm 2 /dyne and has a loss compliance greater than 1 x 10 5 cm 2 /dyne. Though petrolatum has an "ointment feel", it is also extremely fluid and therefore unacceptable for use by itself in the dressings of this invention. The balance of "controlled flow" and "ointment feel" falls within the following desirable band of shear compliances: the elastic compliance ranges from about 2 to about 20 x 10- cm 2 /dyne and the loss compliance ranges from 3 to 20 x 10- cm 2 /dyne.

Above this range, the formulation may have an ointment feel, but its flowability is very high. The desired balance of controlled flow and ointment feel. is present within this range.- Below this.range, the flow is wellcontrolled, but the composition has a considerably reduced ointment feel.

10 Preferably, the flow control polymers assist in assuring Z that, at low temperatures, the viscosity dependence of the \D compositions of this invention is linear on- .a log-log plot. This indicates 'that the compositions of this .invention have a controlled, predictable attribute at low, usage temperatures.

M Those polymers that assist in controlling flow at low temperatures may be selected from polymers such as polyolefins. .Preferably, they are homopolymers, copolymers or polymers composed of several monomers and are not crosslinked. More preferably, this second class of polymers or additives includes the following: ethylene vinyl acetate, or polyalkylenes such as polyisobutylene, ethylene propylene copolymers, polyethylenes and the like.

Flow control additives may also preferably be a stearate or palmitate ester, such as a alcohol ester of a fatty acid. Preferably, such an additive may be stearyl alcohol. This class of polymers or additives may also be used to impart some "stickiness" to the composition or may even detackify the composition, depending upon the polymers chosen and their concentrations. For example, polyethylenes added at a'concentration of at least 5% may aid in detackifying a composition whereas ethylene vinyl acetate added at a concentration of at least 5% may increase the tackiness of the composition.

Additives may be introduced into the compositions of this invention .to influence the "feel" of the final product.

The -composition should mimic the sensation of ointment products as fully as possible, in order to ensure that the consumer who is accustomed to prior ointment products is comfortable wearing the composition. For example, silicone waxes, common emollients known to those of skill -11 in the art polyethylene glycol esters), most

O

z preferably, emollients having a stearate or palmitate IO functional end-groups or the like may be used for this (1 purpose in the dressings of this invention. Dow Corning 580 wax available from Dow Corning, a stearoxy trimethyl silane polymer enhances the ointment feel of the Scomposition by reducing the drag created by the addition C of the network and flow control polymers.

Other compounds may be added to the compositions of this (C invention to increase its hydrophilicity and, still assist in wound healing by maintaining a moist wound environment.

For example, castor oil, wool wax alcohol, glycerin, polyethylene glycols, block copolymers of polypropylene oxide and polyethylene oxide and propylene glycol. These compositions absorb a certain amount of water and/or wound fluids, although the rate of absorption is relatively slow. The slow rate of absorption allows the composition to be considered occlusive and, therefore, beneficial to wound healing.

Other compounds may also be added to the compositions of this invention to lend medicinal properties to the product or otherwise cause modification. For example, antiseptics, antibiotics, anesthetics or other medicaments may be added to the composition to assist in 'woundhealing. Examples of -such compounds are: neomycin sulfate, polymixin-B sulfate, zinc bacitracin, benzalkonium chloride, cetylpyridium chloride, lidocaine, benzocaine, silver sulfur diazine, hydrocortisone and the combinations thereof and the like. Likewise, skin care agents and therapeutics may be added to the compositions of 'this invention, for example, retinoid compounds such as tretinoin, retinol, retinaldehyde or the like, alpha -12hydroxy acids or other products that are well-known Z Preferably, the hydrophobic solvent base should be present IND in the dressings of this invention in an amount from about to about 95% by weight of the composition; more preferably, they should be present in an amount from about to about 85% of the composition; most preferably, they V' should be present in an amount from about 75 to about C(f of the composition.

The network polymers should be present in the dressings of this invention in an amount from about 0.5 to about 10% by weight of the composition; more preferably, they should be present in an amount from about 2 to about 8% of the composition; most preferably, they should be present in an amount from about 5 to about 7% of the composition.

The flow control agents should be present in the dressings of this invention in an amount from about 0.5 to about by weight of the composition; more preferably, they should be present in an amount from about 3 to about 20% of the composition; most preferably, they should be present.in an amount from about 5. to about 10% of the composition.

The predominantly hydrophobic base, in concert with the structured polymer network reduces the dissolution of the active medicaments in the matrix, thereby slowing their leaving the matrix solution. .The predominance of an oilphase in the structure does not allow the wound.fluids to readily leach the active ingredients from the structure.

The hydrophobicity prevents the material from being completely bioactive, but rather permits it at a controlled rate. For example, neomycin in a completely hydrophilic environment is 100% bioactive and totally available to the wound. This can be extremely irritating S- 13.to the wound and skin. Furthermore, the hydrophobic

O

z structure does not readily break down when in contact with the wound bed. A hydrophilic structure would be more CI soluble in the hydrophilic wound fluid.

The dressings of the invention can be applied directly to na wound, or may be coated directly onto a film or fiber M substrate which is, in turn, applied to the wound and surrounding skin. Such films may be composed of one or S 10 more of the following polymers: polyethylene, Ci polypropylene, polyesters, polyvinylacetate. Films useful in the products of this invention may be continuous or discontinuous, reticulated or having some other regular pattern of "holes".

The dressings of this invention may also be coated onto a fiber substrate which, in turn, is adhesively or otherwise attached to a film 'substrate. Examples of fiber substrates are fabrics that are knitted such as modified entangled fiber composed of rayon polyesters, or those that are woven, such as flexible fabrics composed of rayon-nylon blends. Nonwoven fiber substrates may also be used, such as 90:10 polypropylehe-rayon blends, or the like. These dressings can be .coated onto a film or fiber material and then further applied to a secondary substrate which holds the dressing in place over the wound. Types of secondary substrates are films or woven or nonwoven fabrics with pressure'sensitive adhesives.

The products of this invention are preferably -made by blending the constituents in conventional batch mixers such as Brabender Plasticorders, Hobart mixers, Groen mixers, Baker Perkins and the like.. Other batch mixers may be used that are capable of applying high shear at i 14 >elevated temperatures and completely "sweeping" the

O

z surface of the bowl or container such that there are no S"dead" spots. Continuous mixers may also be used such as Werner Pfleiderer ZSK-30 or American Leistritz Preferably, the hydrophobic solvent base and optional additives are heated to a suitable temperature, from about V) 80°C to about 150°C, prior to addition of the network C polymer and flow control polymers. The network and flow control. polymers are then blended with the hydrophobic solvent base until they are completely dissolved, i.e. the Cl system is homogeneous and free of gelations. The blend is then preferably coated onto a substrate and cooled to room temperature, resulting in an occlusive structured dressing.

The following examples are merely illustrative of the products' of this invention, methods of making such products and methods of using the products. The examples are not intended to limit-the scope of the invention.

Example 1.

To a Brabender Plasticorder heated to 125 0 C was added 180 grams of U.S. White petrolatum, 90 grams of Elvax 40W, a poly-vinylacetate from Dupont, 15 grams of mineral oil and 15-grams of Kraton G 1702, a diblock copolymer from the Shell Company composed of polystyrene .and ethylenepropylene copolymer. This composition was mixed for 60 minutes and then the temperature was dropped to 80 0

C

and-mixing was continued for another 30 minutes. The formulation was coated onto a nonwoven substrate while still warm (at 80 0 C) using a draw down method. Squares approximately 3/4 inch in length were centered onto a 3/4 inch by 3 inch adhesive strip. A release film with a low release surface was placed onto the strip covering the 15 adhesive and ointment surface. The strips were subjected 0 to a standard ethylene oxide sterilization cycle Z minutes at 175 0 F) in the presence of water. No oozing or

IO

(C flowing out of the ointment from the adhesive strip was observed. No ointment was seen on the adhesive strip..

Referring to Figure i, the ethylene oxide sterilization c temperature is indicated as a vertical dashed line CA intersecting the "gelling plateau" region of the viscosity S 10 plot, thus indicating that the composition is stable at that temperature and unlikely to flow. In :comparison, there is also a dashed line indicating the viscositytemperature relationship for petrolatum. As indicated by the dashed line, petrolatum would flow readily at about 48 0 C, far lower that the sterilization temperature. In fact, petrolatum melts at 55 0 C and, therefore, would be unacceptable in the products of this invention.

Example 2 Using the method of example 1, 210 grams of White Petrolatum, 60 grams of Elvax 40W, 15 grams of Kraton G1702 and 15 grams of Lanolin Alcohol were coated onto a nonwoven substrate. No oozing or flowing of the ointment was also observed. The composition was. tested for hydrophilic properties by the observation 'of the slow absorption of water droplets placed on the coating of this example.

Examples 3-6 and Comparative Example A The following five compositions were made according to the method of example 1 and also coated onto a nonwoven substrate.,

O

(N

Cc Cc 0 5 16 Compound 3 4 5 6. A Kraton G 1702 11.1 7.7 11.5 11.1 Petrolatum 74.1 76.9 77.0 74.1 83.3 Elvax 40W 14.8 15.4 11.5 11.1 12.5 Elvay 150W 3.7 4.2 The viscosity of the composition of Example 3 as a function of shear rate was measured on a Rheometrics RDS 7700 rheometer at 35 0 C and compared to the viscosity of white petrolatum as a function of shear rate. A graph of the results of this measurement is set forth in Figure 2.

An increase in viscosity of a factor of 10 between the White petrolatum and the composition of Example 3 was noted.

The temperature dependence of the viscosity of compositions of Example 6 and Comparative Example A were compared, the latter containing no "network" polymer. The results of this measurement are set forth as a log-log graph in Figure 3. As Figure 3 illustrates, the viscositytemperature response of Example A is that which would be expected from essentially linear, noncrosslinked polymers in the melt or in .solution: on a log-log plot, the relationship between viscosity and temperature over a limited temperature range is linear. However, the relationship for Example 6 is different. As set forth in Figure 3, at elevated temperatures, the viscosity plateaus. This is what would be expected from a slightly crosslinked or network polymer or a di-or tri-block copolymer. This plateau is called the gelling region; a fairly stable gel or network is apparent at these -17 0 17 >temperatures. The network is destroyed only at extremely z high temperatures.

Example 7 and Comparative Example B 7 B SKraton G1702 10.0 10.7 in USP White Petrolatum 83.3 89.3 Elvax 40W 6.7 Example 7 was made in accordance with the process q1 described in Example 1 and contains a network polymer, Kraton G1702, petrolatum and-a linear polymer, which is a polyvinylacetate.. Example B does not include a linear polymer. Comparisons were made between Example 7 and Comparative Example B using the same method as set forth in Examples 6 to 9. In Figure 4 at low temperatures, Example 7, which has a total polymer content of 16.7%, has a higher viscosity than Comparative Example B with a total polymer content of 10.7%. As the temperature increase, the viscosity curves "crossover"; both sets of data exhibit the gelling plateau, but comparative Example B has a higher plateau viscosity than Example 7. This data indicates that the gelling or network polymer has an important influence .at elevated temperatures and the linear polymers find its significance at lower temperatures.

Examples 8-12 Hydrophilic compositions of this invention were'made in accordance with the procedure set f orth in Example 1. The following compositions were made:

I

18 Compound 8 9 10 11 12 Wool'Wax Alcohol 17g 12g Petrolatum 40g 51g 69.2g 61.5g 72.7g Mineral Oil 21g 10g Kraton G1702 12g 12g 7.7g 7.7g 9.1g Elvax 40W 10g 5g 7.7g 9.1g Glycerine log 15.4g 15.4g Pluronic .7g 7.7g 9.3g These compositions exhibited hydrophilic characteristics while maintaining an ointment feel and structured properties. The hydrophilic characteristics were demonstrated by placing a drop of distilled water and timing how long it took for the hydrophilic compositions to absorb water. Typically it took 3-4 minutes. In a comparable test using 100% petrolatum, there was no any perceivable absorption after 30 minutes.

Examples 13-18 The following compositions were made utilizing the method of Example 1. The figures represent the weight percent of the ingredients set forth below in each composition:

O

O

C 5 19 13 14 15 16 17 18 Kraton .G1650 2 2 4 3 Kratbn G1702 10 7 10 10 5 6 USP.petrolatum 88 81 60 70 '81 81 Steroxytrimethyl-silane 10 10 10 10 Lanolin Alcohol 20 Stearyl alcohol 10 All the above examples provide non-flowing ointment characteristics at elevated temperatures. Esthetics and release from a silicone coated facing paper or adhesion to skin were modified by adjusting ratios of the Kraton diblock and triblock copolymers. Alternatively, additives such as steroxytrimethylsilane or stearyl alcohol enhance release characteristics from the release paper at ambient temperature and reduce greasiness or tackiness of the ointment .on skin. All the above formulations are water insoluble with the exception of Example 15, which includes lanolin alcohol that imparts a water absorption characteristic to the base.

Example 19 The composition of Example 16 was used as a base for the following triple antibiotic-containing dressing in accordance with this invention.

Example 19

O

zw/w ID Kraton G 1650 2 SKraton G 1702 7 Petrolatum, USP 79.5 Steroxytrimethylsilane Bacitracin Zinc 0.80 Polymyxin B Sulfate 0.13 Neomycin Sulfate 0.57 c A concentrate of the active ingredients was made by adding the antibiotic powders into petrolatum at 60 0 C; 2.40 Kg of Bacitracin Zinc, 0.39 Kg of Polymyxin B Sulfate and 1.71 Kg of Neomycin Sulfate was dispersed in 50 Kg of US White Petrolatum using a Ross homogenizer set at 60 0 C. This concentrate was cooled to room temperature. Separately, 6 Kg of Kraton G1650, 21 Kg of Kraton G1702 and 30 Kg of Steroxytrimethylsilane were compounded in 188.5 Kg of USP White Petrolatum in a sweep kettle at 120 0 C until complete solution was obtained. 'This was cooled down to 80 0 C and the antibiotic concentrate was added and mixed for minutes and then cooled. The ointment was heated to 60 0

C

and.extruded onto a padstock where it was finished into a complete product. The antibiotic was tested for antimicrobial activity and retained its activity for at least three months.

Example The compositions of this invention exhibit a good ointment feel" while maintaining their integrity during use.

Figure 5 depicts a plot of the elastic compliances and loss shear compliances of compositions of this invention at 35°C. J' represents the elastic, shear compliance and J" represents the loss shear compliance.

21 Point 1 represents USP Petrolatum, Point 2 represents 0 z Comparative Example B, Point 3 represents Example 7, Point ND 4 represents Example 14, Point 5 represents Example 18, cq Point 6 represents Example 6, Point 7 represents Example 17 and Point 8 represents Example 4. The curve indicates the direction of increased flow and soft feel. The area which is shaded, indicates the area of the graph at (f which products become excessively flowable for use in processing. To the right of the shaded area, the products are too soft for processing. To the left of the shaded q area, the products have an ointment feel, but are less flowable and maintain their stability under shear stress.

The area marked B represents the preferred balance of controlled flow and "ointment feel"; Example 15 represents such a formula. To the left of B, there is another transition where flow is decreased, which assists the processing of the ointment, but where the desired .9ointment feel" is lost. Examples 5 and 6 are at the borderline of acceptability of controlled flow and Itointment feel". In area C the flow is reduced considerably and the "ointment feel" is considerably reduced. *Thus, the compositions of this invention exhibit an ointment feel while retaining stability.

Example 21 An adhesive bandage was made using one of the occlusive compositions described earlier herein. This adhesive bandage is illustrated in Figure 6 of the drawings. As seen in Figure 6, adhesive bandage 100 comprises a backing material 105 having apertures 106 therein; a support material 110; occlusive composition 115; and a porous covering material 120. The upper surface 105a of the backing material was coated with a layer of a pressuresensitive acrylic adhesive 107, It will be understood -22 that any of the adhesives well known in the art for use Z with adhesive bandages may be used in place of this I\ adhesive. The adhesive may,.if desired, be deposited on the backing layer in a continuous or discontinuous pattern rather than as an overall coating as illustrated in the drawing.

CM As is illustrated in the drawings, support material 110 is preferably provided in the.form of a fibrous pad which is centered from end-to-end of the backing material and c extends from one side of the backing material, to the other. It will be understood that support material 110 is secured to the backing material by the aforementioned adhesive 107. The support material 110 used in the bandage .of this Example 21 was a nonwoven fabric comprising about 90% by weight of polypropylene fibers and about 10% by weight of rayon fibers. The basis weight of this fabric was 3.7 oz/yd 2 and had a thickness -of about 34 mils. It will be understood that the support material may comprise nonwoven fabrics other the one described above. In addition, other materials, such as foams, woven fabrics gauze), knitted fabrics and the like may be used.

As will also be seen in the drawings, the upper surface ll0a of fibrous support material 110 carries and has adhered thereto occlusive composition 115. The occlusive composition is coextensive in length and width with support material 110. As suggested by its name, the function of the support material is to support the occlusive. composition which overlies its upper surface.

In -addition, the" support material tends to provide a desirable cushioning effect when the adhesive bandage is applied over a wound site. The upper surface 115a of 23occlusive composition 115 is covered by a porous covering Z material 120. In the specific embodiment of this Example ks0 21, .porous covering material 120 comprised a porous polyethylene film available from Hercules, Inc., Wilmington, Delaware, U.S.A. under the designation DELNET

M

X-550. Other porous covering materials can be used in Splace of the aforementioned porous polyethylene films rn available under the DELNET .name. For example, the porous covering material can be made of polyvinyl chloride, polypropylene, polyester, nylon or the like polymeric materials instead of polyethylene.

The occlusive composition 115 used in adhesive bandage 100 of this Example 21 was the occlusive composition set forth in foregoing Example 19. The occlusive composition was applied to support material 110 in accordance with the procedure set forth in Example 19 hereinabove. The porous covering material 120 overlies upper 'surface 115a, of occlusive composition 115 and is coextensive in length and width with the occlusive composition and underlying support material 110.

Release tabs 125, 126 which comprise silicone-coated polystyrene, were placed over the exposed portions of adhesive 107 and the upper surface of porous' covering material 120 in .the fashion shown in Figure 7 of the drawings.

The adhesive bandage shown in Figure 7 is made according to a process in which the bandage is oriented at right angles to the direction of travel of the raw materials through the manufacturing apparatus. Briefly, as shown in Figure 9, the backing material 105 coated with adhesive 107 is conveyed, from right-to-left as viewed in Figure 0 24 12, on top of a conveyor belt (not shown) A web 150 Z comprising the support material 110 onto which occlusive O composition 115 had been previously applied by an extrusion coating process is led off roll 155 and placed on top of the adhesive coated backing material 105. The O width of web 150 corresponds to the length, L, of backing Smaterial 105 (see Figure 6).

Porous covering material 120 is led off. supply roll 160 and placed on top of web 150. It will be understood that, in the process being described, the width of covering material 120 corresponds substantially to the.width of web 150. Release material 126, supplied from roll 165, is folded to the configuration shown in Figure 7 and applied to the exposed adhesive area at one side of the adhesive coated backing material. Release material 125, supplied from roll 170, is then applied so as to cover the exposed adhesive area at the other side of the adhesive coated backing material as well as the upper surface of porous covering material 120. Release material 125 extends beyond the edge of the porous covering material to provide a grasping tab 125a as illustrated in Figure 7 of the drawings.

The combined raw materials, assembled as just described, are then passed through the nip of cutter rollers 175, 176, Rollers 175, 176 perform two functions, they compress the previously assembled raw materials at a pressure of about 10-20 pounds per square inch and, at the same-time, cut the traveling, assembled raw materials into individual adhesive bandages 100. The individual adhesive bandages are subsequently wrapped, packaged and sterilized, all according to procedures which are well known in the art.

0 25 SAs a result of the.just described manufacturing process, Z particularly as a result of the passage of the raw \D materials through the nip of rolls 175, 176, the occlusive composition 115 is pressed upwardly into holes 121 in covering material 120 so that said occlusive composition is disposed within said holes and is in intimate contact Swith the lower surface 125c of release tab 125.. This is M illustrated in Figure 7B. Thus, after the release tabs are removed preparatory to use, and the adhesive bandage is applied over a wound site, the wound surface is contacted by the portions of occlusive composition 115 which had. previously been in intimate contact with the lower surface 125c of release tab 125. Such contact of the wound surface by the aforementioned portions of occlusive composition 115 is important especially in those instances where said occlusive composition includes a medicament for treatment of the wound..

It will be understood that in some instances, depending on such factors as the manufacturing conditions employed and the-rheological characteristics of occlusive composition 115, the occlusive composition 115, after passing upwardly into holes 121, may spread to some extent over the upper surface 120a of porous covering.material 120 and beneath the release materials 125. Portions, of occlusive composition 115 which have spread over the upper surface of the porous covering material are identified by numeral 127 in Figure 7A.

Example 22 Seven different test specimens, identified by.numeral .130 in Figure 8, were prepared. Test specimens 1-30 comprised fibrous support material 110, an occlusive composition 115, porous covering material 120, and a portion 125b of 26 a release sheet material. Fibrous support material 110 0 z was the 90:10 (weight percentage) polypropylene rayon IND fabric described earlier. Occlusive composition 115 was c that described in Example 19. Each of the seven test specimens 130 used a different porous covering material 120 as described in Table I. The release sheet material tt 125b used for these seven test specimens was a clear M untreated polyethylene film having a thickness of about 4 mils as described in Table I.

C Three controls were also used. Control #1 consisted of fibrous support material 110, occlusive composition 115, and release sheet material 125b. No porous covering material 120 was employed. The release sheet material 125b for Control #i was a silicone coated polystyrene film having a thickness of about 4 mils.

Control #2 consisted of fibrous support material 110, occlusive composition 115, and release sheet material 125b. No porous covering material 120 was employed. "The release sheet material 125b for Control #2 was a clear untreated polyethylene film having a thickness of 4 mils.

Control #3 consisted of fibrous support material 110, occlusive composition 115, a nonporous covering material 120 consisting of polyethylene, and release sheet material 125b. In Control both the nonporous covering material 120 and the release sheet material 125b were. a clear untreated polyethylene film having a thickness of 4 mils.

The material used for the porous covering material 120 comprised a porous polyethylene film known as DELNET Tm available from Hercules, Inc. Various porous polyethylene films available under the DELNET'

T

trademark were used to 1 0 27prepare test specimens 22.3 and 22.5-22.10 inclusive.

O these are listed in TABLE I, second column from the left.

These materials had various open areas (TABLE I, third Ci column from the left) and various hole shapes (TABLE I, fifth column from the left). In addition, TABLE I, fourth column from the left, shows maximum included circle if diameters for the various DELNETm materials.. The term M "maximum included circle diameter" refers to the diameter of the largest circle which can be inscribed in the O 10 opening of each porous covering material.

The individual test specimens listed in TABLE I were tested under conditions similar to those, encountered during manufacture and use of the bandage. Each test specimen was rolled twice once forward and once backward) with a ten pound roller to press the release sheet 125b into contact with the porous covering material 120 to simulate the pressure to which a bandage product would be exposed during manufacture. The test specimens were then conditioned by placing them under, a 0.25 lb load, in an oven at 37 0 .C for eight hours.

The conditioned specimens were then tested as follows.

Each of test specimens 22.3 and 22.5-22.10 inclusive was tested by removing its release sheet material 125b from the top surface 120a of its porous covering material 120..

Control #1 (Example 22.1) and Control #2 (Example -22.2) were tested by removing their respective release sheet materials 125b from the upper surface of their respective occlusive compositions 115a. Control #3 (Example 22.4) was tested by removing its release sheet material 125b from its underlying nonporous covering material 120. The force necessary for removal was measured for the seven test specimens containing the DELNET" porous covering C 28 materials and for control specimens #2 and All

O

Z specimens were observed to determine whether the occlusive ND composition 115 had delaminated from its underlying fibrous support material 110 during removal of the release sheet material 125b. The occlusive composition 115 was considered to have delaminated from its underlying support Smaterial 110 if the underlying support material was Cvisible to the eye as viewed from a direction perpendicular to the top surface 115a of the underlying support material.

2004233501 26 Nov 2004 TABLE I Example Porous covering Material Open (120) area 22.1 None (Control 100% *1 Max Included circle diameter i S hap :e of :hol]e Release material .Release f orce grams D elIam ioccurs 22.2 22.3 22.4 22.5 22.6 22.7 22.8 22.9 22.10 None (Control 12) DELNET RB0404-28 Nonporogs (Control 03) DELNET P520 DELNET CKX215 DELNET D220 DELNET X530 DELNET X550 DELNET KX215 .100% 88% Zero 15% 28% 31% 42% 55%

N'

N

1350 260' one None Silicone- Not Yes Coated Measured Polystyrene one None Polyethylene 2.31 .Yes microns Rectangle ._Polyethylene 2.22 No one None Polyethylene 0.00 No nicrons Triangle Polyethylene 0.00 No 1040 mfcrons 310 microns 371 microns 441 microns Oval I Polyethylene 0.27 No 0.32 No Polyethylene Oval Triangle Polyethylene 0.27 -No TriangleI Polyethylene 0.55 1 No Tringe Plyehyen 10.88 No Ip I I 62% t -n e" a o yth ln 1380 microns .1 r~jiveunvjenp I I 14 I IJ,~ I 1. 1 Example 22.1 O The' first specimen tested was. Control Specimen The -Z specimen contained no porous cover material 120 as

\D

described in Table I. The release sheet material 125b was silicone-coated polystyrene as described in Table I.

Silicone-coated polystyrene is the release material which is preferred for an actual bandage product. It was Sobserved that the occlusive composition 115 delaminated from its-underlying fibrous support 110 a portion of the time.

In view of the delamination observed in Control Specimen it became necessary to determine if a porous covering material 120 could be used to prevent such delamination.

Furthermore, should a porous covering material 120 prevent delamination, it is then necessary to determine the maximum percent open area for the porous covering material 120 at which delamination does not occur'. To ensure that the determined maximum' percent open area would prevent delamination, clear untreated polyethylene was used as the release sheet material 125b for the remaining specimens as described in Table Polyethylene creates a greater release force than the silicone-coated polystyrene, and hence amplifies the occurrence of delamination.

Therefore, should delamination of the occlusive composition 115 from its underlying fibrous support 110 no occur with the removal of the polyethylene release sheet it is virtually certain it will not occur with the removal of the silicone-coated polystyrene release sheet material 125b which is preferred for an actual product.

Example 22.2 The second specimen tested was Control Specimen The specimen has no porous covering as described in Table I.

I 8 31- The release sheet material 125b was a clear untreated O polyethylene film. as described in Table I. The force Z necessary for removal of the release sheet material 125b Sfrom the occlusive composition 115 was 2.31 grams. It was observed that the occlusive composition 115 delaminated from its underlying fibrous support 110.

c Example 22.3 c- The third specimen tested contained a porous cover S 10 material 120 with a percent open area of 88% as described Sin Table I. The porous covering material 120 was identified as DELNET RB0404-28P as described in Table I.

The release sheet material 125b was a clear untreated polyethylene film as described in Table I. The force necessary for removal of the release sheet material 125b from the porous covering material 120 was 2.22 grams. The occlusive composition 115 did not delaminate from its underlying support 110. This example shows that the critical upper limit for the percent open area of the porous covering material 120 to prevent delamination is 88% or greater.

Examples 22.4-22.10 The fourth specimen tested (Example 22.4) was Control Specimen The specimen had a nonporous covering material 120 was polyethylene. The release sheet material 125b was a clear untreated polyethylene film. The force necessary for removal of the release sheet material 125b from the nonporous covering material 120 was zero grams.

The occlusive composition 115 did not delaminate from its underlying support 110.

The fifth specimen tested (Example 22.5) contained a porous cover material 120 with a percent open area of -32as described in Table I. The porous covering material 120 0 was identified as DELNET P520. The release sheet material Z 125b was a clear untreated polyethylene film. The force

\O

IND necessary for removal of the release sheet material 125b from the.porous covering material 120 was 0.0 grams. The Socclusive composition 115 did not delaminate from its O underlying support 110.

C- The sixth specimen tested (Example 22.6) contained a porous cover material 120 with a percent open area of 28% Sas described in Table I. The porous covering material 120 was identified as DELNET CKX215. The release sheet material 125b was a clear untreated polyethylene film.

The force necessary for removal of the release sheet material 125b from the porous covering .material 120 was 0.27 grams. The occlusive composition 115 did not delaminate from its underlying support 110.

The seventh specimen tested (Example 22.7) contained a porous cover material 120 with a percent open area of 31% as described in Table I. The porous covering material 120 was identified as DELNET D220. The release sheet material 125b was a clear untreated polyethylene film. The force necessary for removal of the release sheet material 125b from the porous covering material 120 was 0.32 grams. The occlusive composition 115 did not delaminate from its underlying support 110.

The eighth specimen tested (Example 22.8) contained a porous cover material 120 with a percent open area of 42% as described in Table I. The porous covering material 120 was identified as DELNET X530. The release sheet material 125b was a clear untreated polyethylene film. The force necessary for removal of the release sheet material 125b -33 from the porous covering material 120 was 0.55 grams. The 0 occlusive composition 115 did not delaminate from its underlying support 110.

\D

The ninth specimen tested (Example 22.9) contained a porous cover material 120 with a percent open area of Sas described in Table I. The porous covering material 120 Swas identified as DELNET X550. The release sheet material 125b was a clear untreated polyethylene film. The force necessary for removal of the release sheet material 125b from the porous covering material 120 was 0.88 grams. The occlusive composition 115 did not delaminate from its underlying support 110.

The tenth specimen tested (Example 22.10) contained a porous cover material 120 with a percent open area of 62% as described in Table I. The porous covering material 120 was identified as DELNET KX215. The release' sheet material 125b was a clear untreated polyethylene film.

The force necessary for removal of the release sheet material 125b from the -porous covering material 120 was 1.23 grams. The occlusive composition 115 did not delaminate from its underlying support 110.

Figure 10 graphically displays the force necessary for removal of the release sheet material 125b from the porous covering material 120a (hereinafter called release force) versus the percent open area for examples 22.2 through 22.10.

Certain regions appear in Fig. 10, each region characterized by a different slope. Region I contains Examples 22.4 and 22.5, and includes percent open areas of the porous covering material 120, from zero to about I -34 (-i The release force in this region was measured as zero.

O The zero release force of Examples within this region reflects a percent open area of the porous covering material 120 which is too small to permit the occlusive composition 115 to penetrate through the holes 121 of the porous covering material 120 and contact the lower side of Sthe release sheet material 125c. As described in Example M 21, it is important that the occlusive composition 115 penetrate through the holes 121 of the porous covering O 10 material 120 for an effective bandage application.

Therefore, the percent open areas of Examples within this region are not suitable for the occlusive composition 115 of the preferred viscosity range.

Region II contains Examples 22.6, 22.7, 22.8, 22.9, 2210 and 22.3, and inci=ludes percent open areas of the porous covering material 120 of about 20% to about 88%. This region is characterized by all measured release forces exceeding zero, and by a linear increase in release force with percent open area. The release forces exceeding zero indicates that for all Examples within this region the occlusive composition does penetrate through the holes 121 of the porous covering and does contact the lower side of the release sheet material 125c. hence, the percent open areas of the Examples in this region are suitable for an effective bandage application. Although measurements were made for representative opening shapes in the porous covering material 120 and representative opening sizes in the porous covering material 120, the results from these measurements were found to correlate on percent open area alone. To determine the minimum percent open area of the porous covering material 120 required for the occlusive composition 115 to penetrate through the holes 121 of the porous covering material 120 and to contact the lower side of the release sheet material 125c to the covering O surface, a linear regression curve was fitted to the data Z in this region. The regression line intercepts the zero

\O

I-O release force axis at about 20 percent open area. These data indicate that the critical minimum open area permitted by the invention for the porous covering material 120 is about c- Although the Examples Z1 and 22 have focused on the preferred properties of the occlusive composition, those skilled in the art will recognize that the porous coating material can be used at other viscosities, pressures, and temperatures. Although such conditions have not been actually tested, those skilled in the art will realize that the inventive concepts described within Examples 21 and 22 remain valid.

Referring now to Figure 11, there is illustrated in longitudinal section an adhesive bandage 200 in which porous covering material 120 has been given an alternative configuration. As was the case with adhesive bandage 100 illustrated in Figure. 6, adhesive bandage 200 comprises backing 105; adhesive layer 107; fibrous support material 110; occlusive composition 115; and porous covering material 120. In bandage 100' disclosed in Figure 6, porous covering material 120 was coextensive in its length and width with both occlusive composition 115 and with fibrous support material 110. In the alternative embodiment illustrated in Figure 11, porous covering material 120 comprises downwardly extending portions 122a, 122b and longitudinally extending tab portions 123a, 123b.

Downwardly extending portions 122a, 122b serve to cover the ends 112a, 112b, respectively, of fibrous support material 110 and the ends 117a, 117b, respectively, of

I

0 0 36occlusive composition 115. As will be seen by reference O to Figure 11, ends 112a and 117a face end edge 200a of Z adhesive bandage 200, while ends 112b and 117b face end C edge 200b of the adhesive bandage. Tab portion 123a of porous cover material 120 extends longitudinally for a short distance, about one-eighth of an inch, toward end edge 200a of bandage 200 while tab portion 123b Sextends a short distance toward end edge 200b.

The advantage of providing porous cover material 120 with -q downwardly extending portions 122a, 122b and tab portions 123a, 123b is that longitudinal movement of occlusive composition 115 movement toward either or both of ends 200a, 200b of, bandage 200) is substantially prevented.

In addition, this configuration of porous covering material 120 helps to insure that support material 110 remains firmly in its centered location between ends 200a, 200b of the bandage.

Claims (32)

1. A composition for making a structured dressing comprising: a) about 50 to 95% by weight of one or more hydrocarbons selected from the group of petrolatum, mineral oil, waxes and fatty acids and combinations thereof; b) about 0.5 to 10% by weight of at least one network polymer selected from the group of block copolymers, polyacrylic acids and polysacchardies; and c) about 0.5 to 40% by weight of a flow control agent; and d) at least one agent selected from the group consisting of antiseptics, antibiotics, anaesthetics, anti-inflammatories, antimicrobials, skin care agents and therapeutics and antipyretics.

2. The composition of claim 1, wherein the hydrophobic solvent is present in an amount of about 65 to 85% by weight of the composition.

3. The composition of claim 1, wherein the hydrophobic solvent is present in an amount of about 75 to 85% by weight of the composition.

4. The composition of any one of claims 1-3, wherein the network polymer is present in an amount of about 2-8% by weight.

The composition of any one of claims 1-3, wherein the network polymer is present in an amount of about 5-7% by weight of the composition.

6. The composition of any one of claims 1-5, wherein the flow control agent is present in an amount of about 3-20% by weight of the composition.

7. The composition of any one of claim 1-5, wherein the flow control agent is present in an amount of about 5-10% by weight of the I composition.

8. A composition according to any one of the preceding claims, wherein said hydrophobic solvent base compound comprises one z or more hydrocarbons. (1

9. A composition according to Claim 8 wherein said hydrocarbons are selected from the group consisting of petrolatum, mineral oil, waxes and 0fatty acids. C

10. A composition according to Claim 8 wherein said hydrocarbon has a viscosity at 30'C of from about 1 to about 100,000 centipoise.

11. A composition according to any one of the preceding claims wherein said composition has a gel strength of from about 1000 to about 10,000 poises over a temperature range of from about 50 to about 95 0 C.

12. A composition according to any one of the preceding claims wherein said network polymer is a block copolymer.

13. A composition according to Claim 12 wherein said block copolymer is selected from the group of di-block copolymers and tri-block and multi- arm block copolymers containing styrene and rubber monomer units.

14. A composition according to any one of the preceding claims wherein said network polymer is a polyacrylic acid.

A composition according to any one of the preceding claims wherein said network polymer is a polysaccharide.

16. A composition according to any one of the preceding claims wherein said composition has a shear compliance of from about 2 x 106 cm 2 /dyne to about 20 x 106 cm 2 /dyne at a temperature range of from about 55 0 F to about 100°F. 004576722

17. A composition according to any one of the preceding claims wherein said composition has a loss compliance of from about 3 x 106 cm 2 /dyne to 0 z about 20 x 106 cm 2 /dyne at a temperature range of from about 55°F to Iabout 100°F. (N

18. A composition according to any one of the preceding claims wherein 0said flow control agent is a polyolefin. Cc, C

19. A composition according to Claim 18 wherein said flow control agent Sis selected from the group consisting of homopolymers, copolymers and noncrosslinked polymers comprising different monomers.

20. A composition according to Claim 19 wherein said flow control agent is selected from the group consisting of ethylene vinyl acetate, polyisobutylene, ethylene propylene copolymers and polyethylene.

21. A composition according to any one of the preceding claims wherein said flow control agent is selected from the group consisting of fatty acids.

22. A composition according to Claim 21 wherein said flow control agent is stearoxytrimethylsilane.

23. A composition according to any one of the preceding claims which further comprises one or more of the compounds selected from the group consisting of antibiotics, anaesthetics, anti-inflammatories, antimicrobials and antipyretics.

24. A composition according to any one of the preceding claims which further comprises a hydrophilic agent.

A composition according to Claim 24 wherein said hydrophilic agent is selected from the group consisting of castor oil, wool wax alcohol, glycerine, polyethylene glycols, block copolymers of polypropylene oxide 004576722 and polyethylene oxide, propylene glycol, cellulosics, and combinations thereof. 0 z

26. A composition for making a structured dressing comprising: IN a) about 50 to 95% by weight of at least one hydrophobic solvent base compound selected from the group consisting of petroleum, mineral Cc oil, waxes and fatty acids; b) about 0.5 to 10% by weight of at least one network polymer selected from di-, tri, or multiarm block copolymers of polystyrene and synthetic rubber, cross linked poly(acrylic acids), polyethylene oxide, cellulosics and polysaccharides; c) about 0.5 to 40% by weight of a flow control agent selected from poly(ethylene vinyl acetate), polyalkylenes, ester of fatty acids, silicone waxes and emollients; and d) at least one agent selected from the group consisting of antiseptics, antibiotics, anaesthetics, anti-inflammatories, antimicrobials, skin care agents and therapeutics and antipyretics.

27. A structured occlusive dressing comprising a composition according to any one of the preceding claims.

28. A structured occlusive dressing comprising a composition according to any one of the preceding claims and a substrate.

29. A structured occlusive dressing according to Claim 28 wherein said substrate is a film.

A structured occlusive dressing according to Claim 29 wherein said substrate is a woven or nonwoven fabric. 004576722 004776967, 41

31. A structural occlusive dressing according to Claim 28 wherein said composition and said substrate are adhesively affixed to a film.

32. A composition for making a structured dressing according to claim 1 or 26 substantially as hereinbefore described with reference to the accompanying drawings and the specific examples. Dated: 20 February 2006 Freehills Patent Trade Mark Attorneys Patent Attorneys for the Applicants: Johnson Johnson Consumer Products Inc