AU2004261313B2

AU2004261313B2 - Multi-layer tube of improved physical properties

Info

Publication number: AU2004261313B2
Application number: AU2004261313A
Authority: AU
Inventors: Kevin Adams; Mariano Villaescusa
Original assignee: Sonoco Australia Pty Ltd
Current assignee: Sonoco Australia Pty Ltd
Priority date: 2003-07-30
Filing date: 2004-07-30
Publication date: 2011-01-27
Anticipated expiration: 2024-07-30
Also published as: AU2004261313A1

Description

WO 2005/011972 PCT/AU2004/001017 MULTI-LAYER TUBE OF IMPROVED PHYSICAL PROPERTIES FIELD OF THE INVENTION The invention relates to the field of manufacture of multi-layer tubing that 5 are manufactured via spiral winding processes commonly used for paper tubes and cores, known in the art as cardboard or fibreboard tubes. In particular, the invention relates to an improved construction of a tubular product having improved physical properties, including increased tensile strength and impact resistance, among others. 10 BACKGROUND OF THE INVENTION In the field of manufacture of tubular products formed from multi-layer paper construction, the physical strength characteristics of said products based on a particular paper material, which may relate to tensile strength, crush resistance, tear or puncture resistance or other parameters, is determined to a 15 primary extent by the number of layers of paper incorporated in the tube wall, and the properties of the adhesives used to bind the paper layers together. Typically, greater strength is achieved primarily by incorporating more layers of paper in the tube wall. Similarly, greater resistance to loss of strength in unfavourable environments, such as humid or damp environments, is achieved by using 20 stronger or moisture resistant adhesives, such as sodium silicate or PVA adhesives. Paper tubes and cores are traditionally formed by gluing multiple layers of paper (typically Kraft paper or similar fibrous paper) to each other whilst winding each layer around a steel mandrel of a given diameter. The process usually 25 involves supplying the various layers of these tubes on individual rolls or other dispensers, concurrently drawing the materials from the dispensers in a predetermined array; applying adhesive concurrently to different strands not in contact with one another; and then winding the array into a tube structure around a mandrel. This technique is known as "spiral winding" in the art and will be 30 understood as such in the following description and claims where this term is used. Equipment for performing this process is supplied, for example, by Pack Industries, of rue Gutenberg - B.P. 109 - 68170 RIXHEIM (Alsace) - FRANCE.

WO 2005/011972 PCT/AU2004/001017 2 Typically the number of layers of paper to be used depends upon the physical requirements required for the tube, eg small diameter paper tube for toilet paper cores would require a small number of thin layers of paper using cheaper dextrin adhesives; a core for rolls of paper weighing up to 2 tonnes may 5 require Brown Chip Board or Liner Board with silicate or PVA glues; or a tube for casting concrete into would require greater wall thickness with glues of greater water resistance, therefore requiring a greater number of layers of paper. However, these measures typically make the tubes heavier, more difficult to transport due to mass and/or lack of flexibility, more difficult to cut open where 10 necessary, and more difficult and expensive to manufacture. In addition, silicate based adhesives are more expensive, and present various safety issues during manufacture. For example, some silicate-based adhesives are likely to set very hard, and residues can tend to present a cut hazard. In addition, some water resistant adhesives take a longer time to cure, sometimes requiring assistance by 15 curing in ovens etc, which may increase the unit cost and capital cost of manufacturing lines. Accordingly, it is necessary to find ways of improving various of the strength parameters of paper-based tubing which overcomes some or all of these issues with respect to various of the applications to which these tubes are put. 20 For example, in the building and construction industry, the use of multiple layer paper based tubes and formwork in the casting of vertical concrete piles has become common practice in setting the foundations for buildings, especially larger multiple-storey constructions. The typical construction used in the prior art for single-use casting tubes is 25 to create a rigid tube from multiple layers of kraft or other fibrous paper. However, as discussed above, one issue encountered with kraft or other fibrous paper construction is that it tends to lose tensile strength when wetted, causing bulging or failure. Also, in humid conditions, the dimensions of the tube can tend to alter, which makes control of the dimensions of the concrete pile difficult. 30 An approach taken in the prior art to the construction of such tubes is exemplified in US Patent No. 5,376,316 (Weekers), wherein there is described a tube being made essentially from multiple layers of kraft paper. This particular casting tube also includes a layer of plastic material within the layers of kraft WO 2005/011972 PCT/AU2004/001017 3 paper for the express purpose of improving the waterproofing properties of the tube. However, this document does not suggest how the overall strength of the tube may be improved. For example, a drawback with this construction is that while the plastic layer may provide some barrier to wetting of the kraft paper 5 layers, it cannot completely prevent weakening of these layers where water might enter from both sides, or especially if water enters through the ends of the tube. In any case, there are concrete forming applications where a semi-rigid or rigid tube is necessary. The prior art does not teach any method of strengthening and/or waterproofing such tubes. Presumably, the person faced with this problem 10 must resort to the above-discussed methods involving further paper layers and/or expensive adhesives. Equally, where such paper-based tubes are to be used as packaging material for hard, sharp and/or heavy materials, such as metal components, a major issue is that these items tend to place a great deal of localised impact 15 strain on the tube wall as they shift during transport. Again, the construction disclosed in Weekers would not be sufficiently rigid to reliably be used for this kind of packaging measure, but the only other solution available in the prior art would appear to relate to the well-known route of applying more and more layers of paper to the tube. 20 Similarly, when attempting to create a tube having superior crush resistance, for example for use as a heavy duty core for rolled products such as newsprint, the prior art teaches only the familiar solution of applying more and more layers of paper to the tube and different types of paper. Therefore, it is an object of the present invention to provide a multi-layer 25 tubing material of improved physical properties, which does not require excessive paper layering or the use of expensive or hazardous adhesives, and which may be manufactured using conventional paper tube forming equipment. SUMMARY OF THE INVENTION According to one aspect of the invention, there is provided a tube having 30 walls of multi-layer construction, wherein said multi-layer construction includes one or more sub-layers, each said sub-layer consisting of a woven polymer mesh disposed in between one or more outer layers of material selected from the group consisting of paper or polymer material, wherein said tube is formed by affixing WO 2005/011972 PCT/AU2004/001017 4 said sub-layers to each other whilst said sub-layers are formed into a tube using spiral winding equipment for the manufacture of paper tubes. Preferably, the paper is kraft paper, the polymer material is high density poly-ethylene (HDPE) or poly-propylene (PP), and the paper layers are bonded to 5 the mesh via an intermediate layer of poly-ethylene (PE). The bonding between the outer paper layers of successive sub-layers may be performed by water based adhesives of the kind well known in the art. The tensile strength of the mesh material provides an effective way to increase the overall tensile and impact strength of the tube, in a manner which is 10 not susceptible of weakening due, for example, to moisture ingress. In addition, the superior dimensional stability of the mesh provides the same advantage to the tube, even in conditions of high relative humidity, thereby obviating the need to incorporate undesirable solvent-based adhesives. This increased overall tensile strength provided by the mesh allows 15 superior performance of the tube, without needing to resort to excessive paper layering, meaning that a stronger, tougher tube may be manufactured without greatly increasing the tube mass. Alternatively, a tube may be manufactured to the same strength specifications as known in the prior art, but having significantly thinner walls. 20 A further advantage of the invention is that as the paper affixed to the outside of the sub-layers is mainly present to provide a suitable adhesive surface for the bonding of successive sub-layers, the thickness of these paper layers may be reduced compared with the prior art, for example to about 40 g/m 2 , providing further opportunities to reduce the necessary tube wall thickness for the tube 25 strength desired. A further advantage of the invention is that as the bonding of successive sub-layers is to be achieved via paper-paper bonding using conventional water based adhesives, the tube according to the invention may be manufactured on conventional spiral-wound paper tube manufacturing equipment. 30 Preferably, the grammage of the HDPE or the PP mesh is between 40g/m 2 and 80g/m 2 with the overall grammage of the composite structure being approx 120 g/m 2 and 180 g/m 2 . Preferably the tensile strength of said mesh is greater than about 6.5 kN/m. The mesh may take the form of a simple cross-weave or WO 2005/011972 PCT/AU2004/001017 5 may be provided in any other suitable format. Preferably, said mesh is provided in the form of a scrim cloth having between 6 and 15 strands per inch in any direction. When applied to the casting of concrete, the inventive construction of the 5 form tube not only assists in directly arresting the ingress of water into the tube structure, but as its tensile strength is not affected by water itself, it prevents the tensile strength of the overall tube being compromised by water ingress. The invention is applicable to both rigid and flexible 'lay-flat' tubing. A preferred structure for the tubing, when used as a rigid concrete form 10 material, is one where a sufficient number of sub-layers are provided to ensure the thickness of the tube wall is between about 2.5mm and about 5mm, in order to allow the tubing material sufficient strength to be self-supporting when stood upright, while retaining an ability to be removed via relatively simple means such as cutting with a hand-held knife, and in order to provide a semi-rigid or rigid 15 structure of superior tensile strength and moisture resistance. An alternative structure, which provides a concrete forming tube having improved strength, but with sufficient flexibility to be stored and transported in a 'flattened' state, includes one or two layers of the above described 'sandwich' structure. The woven structure of the polymer mesh assists in providing a greater 20 degree of tensile strength than might be provided by a simple sheet of plastic material, as per the prior art. In addition, the preferred mesh is exceptionally good at resisting stretching or bulging when the tube is filled with concrete. This allows the provision of a lay-flat tubing which has the requisite strength for typical concrete casting operations. The total thickness of this embodiment of the 25 inventive tubing material is likely to be no greater than about 1.5mm. In a further alternative embodiment, in order to provide a suitable surface for the inner casting surface of the tube, one or more additional layers of polymer sheeting, for example polyethylene, may be bonded to the outermost sub-layers. In relation to the use of the inventive tube structure in the material 30 packaging field, a tube suitable for use as a container for, for example, metal components is provided via a tube wall structure having four or five of said 'sandwich' layers, the walls of the tube having a thickness of at least about 2.5mm, in order to allow the tubing material sufficient tensile strength to resist WO 2005/011972 PCT/AU2004/001017 6 tearing or puncturing when hard or sharp components come into the kind of violent contact with the inner surface of the tube as may be expected during transport. It is also anticipated that a tube of improved crush resistance may be 5 provided where the inventive tube wall structure is applied, as the improved tensile resistance of the wall is likely to assist in preventing deformation of a thicker version of such tubes. The improved tensile strength achieved throughout the tube wall is likely to assist in preventing differential buckling of the tube, of the kind where one side of the wall, for example the outer side, is placed under 10 compression and the immediately adjacent and corresponding section of the wall, for example the inner side, is placed under tension. The portion of the wall placed under tension is accordingly less likely to yield to the crush force. Preferably, when used as a core of this kind, a tube wall structure is provided having about 10 to 50 sub-layers, and an overall thickness of about 15 20mm. Now will be described, by way of specific, non-limiting examples, a preferred embodiment of the invention. DETAILED DESCRIPTION OF A PREFERRED EMBODIMENT In the embodiments discussed below, each will be understood to be 20 formed by the technique known in the art as 'spiral winding'. In one preferred embodiment, the invention provides a rigid concrete form tube constructed from multiple sub-layers of material, wherein each said sub layer consists of a woven HDPE mesh disposed in between one or more layers of kraft paper. Similar results may be obtained with PP mesh. The kraft paper may 25 be bonded to the mesh in a conventional manner according to the art, but it is particularly preferred that the paper is bonded to the mesh via an intermediate layer of poly-ethylene (PE). An example of the preferred kind of mesh material is that supplied by Insulation Solutions, of 127 Dandenong-Frankston Road, Dandenong, Victoria 30 3175, Australia, under the name of "Metal Wrapping", item no. 1625. This material has properties as outlined in Table 1.

WO 2005/011972 PCT/AU2004/001017 7 Table 1. Property Specification Structure Coated HDPE weave bonded to one layer of Kraft paper. Tensile strength MD 12.7 kN/m. CD 6.9 kN/m Overall Grammage 134 g/m 2 Puncture & Tear (PPT) MD 24 N CD 40 N 'Beach' Puncture 3.5 J Water Absorption (Cobb @ 15 min.) 46 g/m 2 Typically, the HDPE material is supplied in the form of a scrim cloth having between 8 and 10 strands per inch in any direction. This material is particularly 5 suited to this application due to its very high tensile strength, and in particular to its very high resistance to any level of stretching. The HDPE is then laminated with 40 gsm kraft paper via low-density polyethylene (LDPE) via conventional methods known in the art. The general type of concrete form tubes to which the invention may be 10 applied are described in detail in US Patent No. 5,376,316 discussed above, and the following description is made with reference to the general kind of structures described therein. An ideal structure for a rigid casting tube incorporating this material would consist of between four and six of the above described sub-layers, bonded 15 together by a conventional paper-paper adhesive, such as PVA. The material may be constructed using conventional spiral winding apparatus well known in the art, which involves gluing or otherwise affixing multiple layers of paper (typically Kraft paper or similar fibrous paper) to each other whilst winding each layer around a steel mandrel of a given diameter. 20 Further layers of polyethylene may be affixed to the outer surfaces of the material to provide a desired surface texture for the casting. In particular, it is preferred that there be sufficient layers of polyethylene bonded to the inside WO 2005/011972 PCT/AU2004/001017 8 surface of the tube to ensure a smooth surface of the casting. The overall thickness of the tubing material should be between 2.5mm and 5mm in order to provide sufficient rigidity to stand up without the assistance of a rigid superstructure. 5 Where different surface finishes are required, the person skilled in the art will be aware of other alternative materials which are available to achieve various finishes or surface properties. It will be appreciated by those skilled in the art that the invention is not only applicable to tubing constructed predominantly from kraft paper, and that this is 10 merely one of the more common materials used in this industry and whose properties are likely to be enhanced by the invention. For example, it would be possible to construct a casting tube by incorporating the HDPE mesh within multiple layers of another polymer material such as polyethylene. In such a case, it would be preferable to bond the layers 15 together by direct heat treatment or by using a hot-melt glue. An ideal structure for a flexible casting tube incorporating this material would consist of one or two of the above-described sub-layers, with optionally further layers of a single sided paper/mesh composite affixed to the outer surface of the tube material to provide a desired surface texture, but having an overall 20 thickness of less than 4mm in order to provide sufficient flexibility to lay flat when not in use. It will further be apparent to those skilled in the art that the invention provides an improved construction of multi-layer tubes for a variety of different applications, notwithstanding the preferred embodiments addressed above are 25 addressed to concrete forming. It is apparent that the improved tensile strength of the tubing material provided by the invention will afford improved performance in many other applications where such properties are desirable. For example, a tube of similar construction to that described above for the rigid form-work tube might equally be applied as a packaging material for metal 30 components. A tube wall structure having four or five of said inventive sub-layers, the walls of the tube having a thickness of between about 3mm and about 4mm, is anticipated to allow the tubing material sufficient tensile strength to resist tearing or puncturing when hard or sharp components come into the kind of WO 2005/011972 PCT/AU2004/001017 9 violent contact with the inner surface of the tube as may be expected during transport. It is also anticipated that a tube of improved crush resistance may be provided where the inventive tube wall structure is applied, as the improved 5 tensile resistance of the wall is likely to assist in preventing deformation of a thicker version of such tubes. As described above, the improved tensile strength achieved throughout the tube wall is likely to assist in preventing differential buckling of the tube, of the kind where one side of the wall, for example the outer side, is placed under compression and the immediately adjacent and 10 corresponding section of the wall, for example the inner side, is placed under tension. The portion of the wall placed under tension is accordingly less likely to yield to the crush force. Preferably, when used as a core of this kind, a tube wall structure is provided having 10 to 15 sub-layers, and an overall thickness of about 20mm. 15

Claims

1. A tube having walls of multi-layer construction, wherein said multi-layer construction includes one or more sub-layers, each said sub-layer consisting of a woven polymer mesh disposed in between one or more outer layers of material 5 selected from the group consisting of paper, poly-propylene and polyethylene, wherein said tube is formed by affixing said sub-layers to each other whilst said sub-layers are formed into a tube using spiral winding equipment for the manufacture of paper tubes.

2. The tube of claim 1, wherein said mesh is provided in the form of a scrim 10 cloth having between 6 and 15 strands per inch.

3. The tube of claim 2, wherein the sub-layer has a grammage of between about 120 g/m2 and about 180g/m2 and has a tensile strength of greater than about 6.5 kN/m.

4. The tube of any one of claims 1 to 3, wherein the outer layer of said sub 15 layer is a polymer material, and said polymer material is high density poly ethylene (HDPE) or poly-propylene (PP).

5. The tube of any one of claims 1 to 3, wherein the outer layer of said sub layer is paper and said paper is kraft paper.

6. The tube of claim 5, wherein the kraft paper has a minimum grammage of 20 about 40 g/m2.

7. The tube of any one of claims I to 6, wherein the outer layers of the sub layer are bonded to the mesh via an intermediate layer of poly-ethylene (PE).

8. The tube of any one of claims I to 7, being a concrete column form tube, wherein the thickness of the tube wall is at least 2.5mm and provides sufficient 25 strength to the tube to be self-supporting when stood upright. 11

9. The tube of claim 8, wherein the thickness of the tube wall is no greater than about 5mm, thereby retaining an ability to be removed via cutting with a hand-held knife.

10. The tube of any one of claims 1 to 7, being a concrete column form tube, 5 wherein the overall thickness of said tube wall is no greater than about 1.5mm thereby to provide sufficient flexibility for the tube to be stored and transported in a flattened state.

11. The tube of any one of claims 1 to 7, being a packaging tube for the transport or storage of hard or sharp materials, wherein the thickness of the tube 10 wall is at least 2.5mm and provides sufficient strength to resist puncture due to internal movement of hard or sharp materials.

12. Use of a multi-layer wall tube according to any one of claims 1 to 7, as a roll core tube for the winding of sheet materials, wherein the thickness of the tube wall is at least 2.5mm and provides sufficient strength to resist crushing forces 15 experienced during winding of sheet material onto the tube.

13. A tube having a peripheral wall of multi-layer construction, the multi-layer construction including one or more sub-layers, wherein each sub-layer is a laminate that comprises a woven polymer mesh to which is bonded on a first side thereof a paper layer by means of an intermediate layer of polyethylene or 20 polypropylene material, the sub-layers being bonded to each other through an adhesive material to provide a spirally-wound, multi-layer peripheral wall structure.

14. The tube of claim 13, wherein said mesh is provided in the form of a scrim cloth having between 6 and 15 strands per inch, and wherein the grammage of 25 the sub-layer is between about 120 g/m2 and about 180 g/m2 and has a tensile strength of greater than about 6.5 kN/m. 12

15. The tube of claim 13 or 14, wherein the paper is kraft paper that has a minimum grammage of about 40 g/m2.

16. The tube of claim 13, 14 or 15, wherein the tube is a rigid concrete column form tube of multi-layer construction and wherein the thickness of the peripheral 5 wall is either at least 2.5mm such as to provide a self-supporting rigid tube, or the thickness of the peripheral wall is no greater than about 1.5mm such as to provide a flexible foldable tube.

17. The tube of any one of claims 13 to 16, wherein the tube is formed by bonding the sub-layers to each other by a paper-paper adhesive material, whilst 10 the sub-layers are formed into the tube using spiral winding equipment.

18. A tube having a peripheral wall of multi-layer construction, the multi-layer construction including a plurality of laminated sub-layers that comprise a woven polymer mesh to which is bonded on a first side thereof a first outer layer of a material selected from paper, polyethylene or polypropylene by means of an 15 intermediate layer of polyethylene or polypropylene material, the sub-layers being bonded to each other through an adhesive material to provide a spirally-wound, multi-layer peripheral wall structure.

19. The tube of claim 18, wherein at least some of the laminated sub-layers consist of a woven polymer mesh sandwiched between and bonded to respective 20 outer layers of kraft paper by means of a respective intermediate layer of polyethylene or polypropylene material, and wherein the tube is formed by bonding the sub-layers to each other by a paper-paper adhesive material, whilst the sub-layers are formed into the tube using spiral winding equipment.

20. A tube having walls of multi-layer construction substantially as described 25 hereinbefore EZYTUBE PTY LIMITED WATERMARK PATENT AND TRADE MARKS ATTORNEYS P23060AUPC