AU2013309038B2

AU2013309038B2 - Acid-soluble cement compositions comprising cement kiln dust and methods of use

Info

Publication number: AU2013309038B2
Application number: AU2013309038A
Authority: AU
Inventors: James Robert Benkley; Darrell Chad Brenneis; Craig Wayne Roddy
Original assignee: Halliburton Energy Services Inc
Current assignee: Halliburton Energy Services Inc
Priority date: 2012-08-27
Filing date: 2013-08-27
Publication date: 2016-03-31
Anticipated expiration: 2033-08-27
Also published as: WO2014035923A1; IN2015DN01221A; EP2888335A1; EP2888335A4; MX2015002469A; AU2013309038A1; CA2881910A1; MY171131A; BR112015004026A2; MX390148B

Abstract

The present invention relates to acid-soluble cement compositions that comprise cement kiln dust ("CKD") and associated methods of use. An embodiment provides a method of cementing comprising: providing an acid-soluble cement composition comprising a kiln dust and water; allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass; and contacting the acid-soluble hardened mass with an acid.

Description

Docket No. 2005-017636U5P1D1P1P1P2P1 PCT ACID-SOLUBLE CEMENT COMPOSITIONS COMPRISING CEMENT KILN DUST AND METHODS OF USE BACKGROUND [0001] The present disclosure relates to cementing operations and, more particularly, in certain embodiments, to acid-soluble cement compositions that comprise cement kiln dust ("CKD") and associated methods of use. [0002] Cement compositions may be used in a variety of subterranean applications. For example, in subterranean well construction, a pipe string (e.g., casing, liners, expandable tubulars, etc.) may be run into a well bore and cemented in place. The process of cementing the pipe string in place is commonly referred to as "primary cementing." In a typical primary cementing method, a cement composition may be pumped into an annulus between the walls of the well bore and the exterior surface of the pipe string disposed therein. The cement composition may set in the annular space, thereby forming an annular sheath of hardened, substantially impermeable cement (i.e., a cement sheath) that may support and position the pipe string in the well bore and may bond the exterior surface of the pipe string to the subterranean formation. Among other things, the cement sheath surrounding the pipe string functions to prevent the migration of fluids in the annulus, as well as protecting the pipe string from corrosion. Cement compositions also may be used in remedial cementing methods, for example, to seal cracks or holes in pipe strings or cement sheaths, to seal highly permeable formation zones or fractures, to place a cement plug, and the like. Cement compositions also may be used in surface applications, for example, construction cementing. [0003] In some applications, it may be desirable for the cement composition to be acid soluble. For instance, an acid-soluble cement composition may be desirable in applications where it is anticipated that the hardened cement will be removed in subsequent well bore operations. One particular application includes use of an acid-soluble cement composition to plug permeable zones in a formation that may allow the undesired flow of fluid into, or from, the well bore. For example, the permeable zones may result in the loss of circulation of fluids, such as a drilling fluid or a cement composition, in the well bore or an undesired influx of gas or water into the well bore. The permeable zones include, for example, vugs, voids, fractures (natural or otherwise produced) and the like. Other applications for acid-soluble cement compositions include, for example, the formation of annular plugs and isolation of gravel-packed well bore 1 intervals. Examples of acid-soluble cement compositions include those comprising Sorel cements and Portland cements. SUMMARY [0004] The present embodiments relate to cementing operations and, more particularly, in certain embodiments, to acid-soluble cement compositions that comprise CKD and associated methods of use. [0005] One embodiment provides a method of cementing comprising: providing an acid-soluble cement composition comprising a kiln dust and water; wherein the acid-soluble cement composition is free of any additional cementitious components other than the kiln dust; allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass; and contacting the acid-soluble hardened mass with an acid. [0006] Another embodiment provides a method of cementing. The method of cementing may comprise placing an acid-soluble cement composition in a subterranean formation. The acid-soluble cement composition may comprise cement kiln dust in an amount of 100% by weight of a total amount of cementitious components in the acid-soluble cement composition and water. The method further may comprise allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass. The method further may comprise contacting the acid-soluble hardened mass with an acid. [0007] Another embodiment provides a method of cementing. The method may comprise placing an acid-soluble cement composition in a subterranean formation. The acid soluble cement composition may comprise cement kiln dust and water, wherein the acid-soluble cement composition is free of any acid-soluble fillers. The method further may comprise allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass. The method further may comprise contacting the acid-soluble hardened mass with an acid. [0008] The features and advantages of the embodiments will be readily apparent to those skilled in the art. While numerous changes may be made by those skilled in the art, such changes are within the spirit of the embodiments. DESCRIPTION OF PREFERRED EMBODIMENTS [0009] The description relates to cementing operations and, more particularly, in certain embodiments, to acid-soluble cement compositions that comprise CKD and associated methods of use. There may be several potential advantages to the methods and compositions of 2 the embodiments, only some of which may be alluded to herein. One of the many potential advantages of some embodiments is that the inclusion of the CKD in the acid-soluble cement compositions should reduce the amount of, or potentially eliminate, a higher cost additive, such as Portland or Sorel cement, resulting in a more economical cement composition. Another potential advantage of some embodiments is that reduction of the amount of Portland cement should reduce the carbon footprint of the acid-soluble cement compositions. [0010] Embodiments of the acid-soluble cement compositions may comprise CKD. Additional embodiments of the acid-soluble cement compositions may comprise a hydraulic cement; a component selected from the group consisting of CKD, a natural pozzolan, and a combination thereof; and water. In an embodiment, the hydraulic cement may comprise Sorel cement. In another embodiment, the cement compositions may further comprise an acid-soluble filler. In additional embodiments, the cement compositions may comprise CKD and be free of any acid-soluble fillers. In yet another embodiment, the cement compositions may further comprise a source of calcium ions (e.g., hydrated lime). Other optional additives may also be included in embodiments of the cement compositions of the present invention as desired, including, but not limited to, fly ash, slag cement, metakaolin, shale, zeolite, combinations thereof, and the like. Additionally, embodiments of the cement compositions of the present invention may be foamed and/or extended as desired by those of ordinary skill in the art. [0011] The acid-soluble cement compositions should have a density suitable for a particular application as desired by those of ordinary skill in the art, with the benefit of this disclosure. In some embodiments, the cement compositions may have a density in the range of from about 8 pounds per gallon ("ppg") to about 16 ppg. In other embodiments, the cement compositions may be foamed to a density in the range of from about 8 ppg to about 13 ppg. [0012] Embodiments of the acid-soluble cement compositions may comprise a hydraulic cement. A variety of hydraulic cements may be utilized including, but not limited to, those comprising calcium, aluminum, silicon, oxygen, iron, and/or sulfur, which set and harden by reaction with water. Suitable hydraulic cements include, but are not limited to, Sorel cements, Portland cements, pozzolana cements, gypsum cements, high alumina content cements, slag cements, silica cements, and combinations thereof. In certain embodiments, the hydraulic cement may comprise a Portland cement. In some embodiments, the Portland cements that are suited for use are classified as Classes A, C, G, and H cements according to American Petroleum 3 Institute, API Specification for Materials and Testing for Well Cements, API Specification 10, Fifth Ed., July 1, 1990. In addition, in some embodiments, cements suitable for use may be classified as ASTM Type I, II, or III. As will be discussed in more detail below, acid-soluble fillers can be used with hydraulic cements (such as Portland cement) that do harden into an acid soluble mass. [0013] Where present, the hydraulic cement generally may be included in the acid soluble cement compositions in an amount sufficient to provide the desired compressive strength, density, and/or cost. In accordance with embodiments, at least a portion of the hydraulic cement and potentially even all of the hydraulic cement may be replaced with CKD and/or a natural pozzolan. In an embodiment, at a least a portion of the hydraulic cement is replaced with CKD and/or a natural pozzolan. In some embodiments, the hydraulic cement may be present in the cement compositions in an amount in the range of 0% to about 99% by weight of cementitious components. As used herein, the term "by weight of cementitious components" refers to the concentration of the particular component by weight of a total amount of cementitious components included in the cement composition. Cementitious components include those components or combinations of components of the cement compositions that hydraulically set, or otherwise harden, to develop compressive strength, including, for example, Sorel cement, Portland cement, CKD, fly ash, pumice, slag, lime, shale, and the like. For example, the cementitious components may comprise the hydraulic cement and any additional cementitious components that may be present in the acid-soluble cement composition. The hydraulic cement may be present, in certain embodiments, in an amount of about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 90%, or about 95%. In an embodiment, the hydraulic cement may be present in an amount in the range of 0% to about 95% by weight of cementitious components. In another embodiment, the hydraulic cement may be present in an amount in the range of about 20% to about 95% by weight of cementitious components. In yet another embodiment, the hydraulic cement may be present in an amount in the range of about 50% to about 90% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the hydraulic cement to include for a chosen application. 4 [0014] An example of a suitable hydraulic cement comprises a Sorel cement. Sorel cements typically include magnesia-based cement systems formed from a mixture of magnesium oxide and magnesium chloride. However, as used herein, the term "Sorel cement" is intended to encompass any of a variety of metal oxides and soluble salts which together form a hydraulic cement. In the presence of water, the metal oxide and the soluble salt forming the Sorel cement should solidify into an acid-soluble mass. Embodiments of the Sorel cements should rapidly develop a desirable compressive strength. In accordance with embodiments, at least a portion of the Sorel cement may be replaced with CKD and/or a natural pozzolan. In an embodiment, at a least a portion of the soluble salt is replaced with CKD and/or a natural pozzolan. [0015] In an embodiment, the Sorel cement comprises a metal oxide. In one particular embodiment, the Sorel cement comprises an alkaline earth metal oxide, such as magnesium oxide. A suitable metal oxide is THERMATEK T LT additive, available from Halliburton Energy Services, Inc. The metal oxide present in the Sorel cement should have an activity level sufficient to provide the desired reactivity. For example, the higher the activity level of the metal oxide, the faster the reaction of the metal oxide with the other components of the Sorel cement to form the hardened mass. The activity level of the metal oxide may vary based on a number of factors. For example, the particle size differential of the metal oxide particles may affect the activity level. A smaller particle size differential may result in a higher activity level due, inter alia, to a greater surface area. Another factor that may affect the activity level of the metal oxide is a sintering process. By varying the heat applied during, and time of, the sintering process, metal oxide with varying activity levels may be provided. Metal oxide that has not been treated by a sintering process may have a very high activity level, and thus it may be highly reactive in the Sorel cements. In an embodiment, a relatively more reactive metal oxide may be desired, such as where it may be desired to have a cement composition with a relatively short set time, for example, when desired to rapidly seal off a permeable zone. In an alternative embodiment, a relatively less reactive metal oxide may be desired, for example, where a delay may be desired between mixing the cement composition and the formation of a hardened mass. [0016] A wide variety of soluble salts are suitable for use in the Sorel cement, including metal chlorides. In one embodiment, the Sorel cement comprises an alkaline earth metal chloride, such as magnesium chloride. An example of a suitable magnesium chloride is C 5 TEK additive, available from Halliburton Energy Services, Inc. In an alternative embodiment, the Sorel cement comprises magnesium sulfate or ammonium mono or dibasic phosphate. [0017] In an embodiment, the Sorel cement may comprise the metal oxide and the soluble salt in a metal-oxide-to-soluble-salt ratio of about 3:1 to about 1:3. In another embodiment, the metal-oxide-to-soluble-salt ratio may range from about 2:1 to about 1:2. In yet another embodiment, the metal-oxide-to-soluble-salt ratio may range from about 1.5:1 to about 1:1.5. One of ordinary skill in the art will recognize the appropriate ratio of the metal oxide and soluble salt to include for a particular application. [0018] Embodiments of the acid-soluble cement compositions generally may comprise CKD, which is a material generated in the manufacture of cement. CKD, as that term is used herein, refers to a partially calcined kiln feed which is removed from the gas stream and collected, for example, in a dust collector during the manufacture of cement. Usually, large quantities of CKD are collected in the production of cement that are commonly disposed of as waste. Disposal of the CKD as waste can add undesirable costs to the manufacture of the cement, as well as the environmental concerns associated with its disposal. The chemical analysis of CKD from various cement manufactures varies depending on a number of factors, including the particular kiln feed, the efficiencies of the cement production operation, and the associated dust collection systems. CKD generally may comprise a variety of oxides, such as SiO 2 , A1 2 0 3 , Fe 2 0 3 , CaO, MgO, S03, Na 2 0, and K 2 0. The term "CKD" is used herein to mean cement kiln dust made as described above and equivalent forms of cement kiln dust made in other ways. [0019] The CKD generally may exhibit cementitious properties, in that it may set and harden in the presence of water. In accordance with some embodiments, the CKD may be used, among other things, to replace higher cost cementitious components, such as Portland cement and/or Sorel cement, resulting in more economical cement compositions. In addition, substitution of the CKD for the Portland and/or Sorel cement should result in a cement composition with a reduced carbon footprint. [0020] The CKD may be included in the acid-soluble cement compositions in an amount sufficient to provide the desired compressive strength, density, cost reduction, and/or reduced carbon footprint. In some embodiments, the CKD may be present in the cement compositions in an amount in the range of from about 1% to 100% by weight of cementitious 6 components. For example, the CKD may be present in an amount of about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 90%, or about 95%. In one embodiment, the CKD may be present in an amount in the range of from about 5% to about 99% by weight of cementitious components. In another embodiment, the CKD may be present in an amount in the range of from about 5% to about 80% by weight of cementitious components. In yet another embodiment, the CKD may be present in an amount in the range of from about 50% to about 80% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of CKD to include for a chosen application. [0021] While the preceding description describes CKD, the embodiments are broad enough to encompass the use of other partially calcined kiln feeds that may be present in embodiments of the cement compositions in an amount in a range of from about 1% to about 100% by weight of cementitious components. For example, embodiments of the acid-soluble cement compositions may comprise lime kiln dust, which is a material that is generated during the manufacture of lime. The term "lime kiln dust" typically refers to a partially calcined kiln feed which can be removed from the gas stream and collected, for example, in a dust collector during the manufacture of lime. The chemical analysis of lime kiln dust from various lime manufactures varies depending on a number of factors, including the particular limestone or dolomitic limestone feed, the type of kiln, the mode of operation of the kiln, the efficiencies of the lime production operation, and the associated dust collection systems. Lime kiln dust generally may comprise varying amounts of free lime and free magnesium, lime stone, and/or dolomitic limestone and a variety of oxides, such as SiO 2 , A1 2 0 3 , Fe 2 0 3 , CaO, MgO, SO 3 , Na 2 0, and K 2 0, and other components, such as chlorides. [0022] Embodiments of the acid-soluble cement compositions may further comprise a natural pozzolan. Natural pozzolans are generally present on the Earth's surface and set and harden in the presence of hydrated lime and water. Examples of natural pozzolans include pumicite, diatomaceous earth, volcanic ash, opaline shale, tuff, and combinations thereof. Generally, pumicite is a volcanic rock that exhibits cementitious properties, in that it may set and harden in the presence of a source of calcium ions and water. Hydrated lime may be used in combination with the pumicite, for example, to provide sufficient calcium ions for the 7 pumicite to set. The natural pozzolan may be used, among other things, to replace higher cost cementitious components, such as Portland or Sorel cement, in embodiments of the sealant compositions, resulting in more economical sealant compositions. In addition, substitution of the natural pozzolan for the Portland cement and/or Sorel cement should result in a cement composition with a reduced carbon footprint. [0023] Where present, the natural pozzolan may be included in an amount sufficient to provide the desired compressive strength, density, cost reduction and/or reduced carbon footprint for a particular application. In some embodiments, the natural pozzolan may be present in the acid-soluble cement compositions of the present invention in an amount in the range of from about 1% to about 100% by weight of cementitious components. For example, the natural pozzolan may be present in an amount of about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, about 80%, about 90%, or about 95%. In one embodiment, the natural pozzolan may be present in an amount in the range of from about 5% to about 99% by weight of cementitious components. In another embodiment, the natural pozzolan may be present in an amount in the range of from about 5% to about 80% by weight of cementitious components. In yet another embodiment, the natural pozzolan may be present in an amount in the range of from about 10% to about 50% by weight of cementitious components. In yet another embodiment, the natural pozzolan may be present in an amount in the range of from about 25% to about 50% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the natural pozzolan to include for a chosen application. [0024] The water that may be used in embodiments of the cement compositions may include, for example, freshwater, saltwater (e.g., water containing one or more salts dissolved therein), brine (e.g., saturated saltwater produced from subterranean formations), seawater, or combinations thereof. Generally, the water may be from any source, provided that the water does not contain an excess of compounds that may undesirably affect other components in the cement composition. In some embodiments, the water may be included in an amount sufficient to form a pumpable slurry. In some embodiments, the water may be included in the cement compositions of the present invention in an amount in the range of about 40% to about 200% by weight of cementitious components. In some embodiments, the water may be 8 included in an amount in the range of about 40% to about 150% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of water to include for a chosen application. [0025] Embodiments of the cement compositions may further comprise a source of calcium ions, such as lime. In certain embodiments, the source of calcium ions may include hydrated lime. The source of calcium ions may be included in embodiments of the cement compositions, for example to, form a hydraulic composition with other components of the cement compositions, such as the pumice, fly ash, slag, and/or shale. Where present, the lime may be included in the cement compositions in an amount sufficient for a particular application. In some embodiments, the lime may be present in an amount in the range of from about 1% to about 40% by weight of cementitious components. For example, the lime may be present in an amount of about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, or about 35%. In one embodiment, the lime may be present in an amount in the range of from about 5% to about 20% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the lime to include for a chosen application. [0026] Embodiments of the acid-soluble cement compositions may further comprise an acid-soluble filler. The acid-soluble filler may be used, for example, in compositions that comprise Portland cement with the acid-soluble filler providing an acid soluble component so that the compositions can be dissolved and removed. In an embodiment, the acid-soluble filler is present in a cement composition comprising a Sorel cement. Examples of suitable acid-soluble filler materials that are non-reactive with other components in the compositions, including without limitation dolomite, magnesium carbonate, calcium carbonate, and zinc carbonate. Where used, the acid-soluble filler may be present in the acid-soluble cement composition in an amount of from about 0.1% to about 300% by weight of the cementitious component. In an embodiment, the acid-soluble filler is present in an amount of from about 50% to about 400% by weight of the cementitious component. In an embodiment, the acid-soluble filler is present in an amount of from about 100% to about 300% by weight of the cementitious component. In alternative embodiments, the acid-soluble cement compositions may be free of the acid-soluble filler in that the acid-soluble cement compositions comprises the acid-soluble filler in an amount of about 0% by weight of the cementitious component. One of 9 ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the acid-soluble filler to include for a chosen application. [0027] Embodiments of the acid-soluble cement compositions may further comprise fly ash. A variety of fly ashes may be suitable, including fly ash classified as Class C and Class F fly ash according to American Petroleum Institute, API Specification for Materials and Testing for Well Cements, API Specification 10, Fifth Ed., July 1, 1990. Class C fly ash comprises both silica and lime so that, when mixed with water, it should set to form a hardened mass. Class F fly ash generally does not contain sufficient lime, so an additional source of calcium ions is required for the Class F fly ash to form a hydraulic composition. In some embodiments, lime may be mixed with Class F fly ash in an amount in the range of about 0.1% to about 25% by weight of the fly ash. In some instances, the lime may be hydrated lime. Suitable examples of fly ash include, but are not limited to, POZMIX* A cement additive, commercially available from Halliburton Energy Services, Inc., Duncan, Oklahoma. [0028] Where present, the fly ash generally may be included in the acid-soluble cement compositions in an amount sufficient to provide the desired compressive strength, density, and/or cost. In some embodiments, the fly ash may be present in the cement compositions in an amount in the range of about 5% to about 75% by weight of cementitious components. In some embodiments, the fly ash may be present in an amount in the range of about 10% to about 60% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the fly ash to include for a chosen application. [0029] Embodiments of the acid-soluble cement compositions may further comprise a slag cement. In some embodiments, a slag cement that may be suitable for use may comprise slag. Slag generally does not contain sufficient basic material, so slag cement may further comprise a base to produce a hydraulic composition that may react with water to set to form a hardened mass. Examples of suitable sources of bases include, but are not limited to, sodium hydroxide, sodium bicarbonate, sodium carbonate, lime, and combinations thereof. [0030] Where present, the slag cement generally may be included in the acid soluble cement compositions in an amount sufficient to provide the desired compressive strength, density, and/or cost. In some embodiments, the slag cement may be present in the cement compositions in an amount in the range of about 0.1% to about 99% by weight of 10 cementitious components. In some embodiments, the slag cement may be present in an amount in the range of about 5% to about 75% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the slag cement to include for a chosen application. [0031] Embodiments of the acid-soluble cement compositions may further comprise metakaolin. Generally, metakaolin is a white pozzolan that may be prepared by heating kaolin clay, for example, to temperatures in the range of about 600'C to about 800'C. In some embodiments, the metakaolin may be present in the cement compositions of the present invention in an amount in the range of about 5% to about 95% by weight of cementitious components. In some embodiments, the metakaolin may be present in an amount in the range of about 10% to about 50% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the metakaolin to include for a chosen application. [0032] Embodiments of the acid-soluble cement compositions may further comprise shale. Among other things, shale included in the cement compositions may react with excess lime to form a suitable cementing material, for example, calcium silicate hydrate. A variety of shales may be suitable, including those comprising silicon, aluminum, calcium, and/or magnesium. An example of a suitable shale comprises vitrified shale. Suitable examples of vitrified shale include, but are not limited to, PRESSUR-SEAL FINE LCM material and PRESSUR-SEAL COARSE LCM material, which are commercially available from TXI Energy Services, Inc., Houston, Texas. Generally, the shale may have any particle size distribution as desired for a particular application. In certain embodiments, the shale may have a particle size distribution in the range of about 37 micrometers to about 4,750 micrometers. [0033] Where present, the shale may be included in the acid-soluble cement compositions in an amount sufficient to provide the desired compressive strength, density, and/or cost. In some embodiments, the shale may be present in the cement compositions of the present invention in an amount in the range of about 5% to about 75% by weight of cementitious components. In some embodiments, the shale may be present in an amount in the range of about 10% to about 35% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the shale to include for a chosen application. 11 [0034] Embodiments of the acid-soluble cement compositions may further comprise zeolite. Zeolites generally are porous alumino-silicate minerals that may be either a natural or synthetic material. Synthetic zeolites are based on the same type of structural cell as natural zeolites, and may comprise aluminosilicate hydrates. As used herein, the term "zeolite" refers to all natural and synthetic forms of zeolite. Examples of suitable zeolites are described in more detail in U.S. Patent No. 7,445,669. An example of a suitable source of zeolite is available from the C2C Zeolite Corporation of Calgary, Canada. In some embodiments, the zeolite may be present in the cement compositions in an amount in the range of about 5% to about 65% by weight of cementitious components. In certain embodiments, the zeolite may be present in an amount in the range of about 10% to about 40% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the zeolite to include for a chosen application. [0035] Embodiments of the acid-soluble cement compositions may further comprise a set-retarding additive. As used herein, the term "set-retarding additive" refers to an additive that retards the setting of the acid-soluble cement compositions of the present invention. Examples of suitable set-retarding additives include, but are not limited to, ammonium, alkali metals, alkaline earth metals, metal salts of sulfoalkylated lignins, organic acids (e.g., hydroxycarboxy acids), copolymers that comprise acrylic acid or maleic acid, and combinations thereof. One example of a suitable sulfoalkylated lignin comprises a sulfomethylated lignin. Suitable set-retarding additives are disclosed in more detail in United States Patent No. Re. 31,190, the entire disclosure of which is incorporated herein by reference. Suitable set-retarding additives are commercially available from Halliburton Energy Services, Inc. under the 0 0 00 0 0TM trademarks HR*-4, HR -5, HR -7, HR -12, HR -15, HR -25, HR -601, SCR -100, and SCRTM_500 retarders. Generally, where used, the set-retarding additive may be included in the cement compositions of the present invention in an amount sufficient to provide the desired set retardation. In some embodiments, the set-retarding additive may be present in the cement compositions an amount in the range of about 0.1% to about 5% by weight of cementitious components. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the set-retarding additive to include for a chosen application. [0036] Optionally, other additional additives may be added to the acid-soluble cement compositions of the present invention as deemed appropriate by one skilled in the art, 12 with the benefit of this disclosure. Examples of such additives include, but are not limited to, strength-retrogression additives, set accelerators, weighting agents, lightweight additives, gas generating additives, mechanical-property-enhancing additives, lost-circulation materials, filtration-control additives, dispersants, fluid-loss-control additives, defoaming agents, foaming agents, oil-swellable particles, water-swellable particles, thixotropic additives, and combinations thereof. Specific examples of these, and other, additives include crystalline silica, amorphous silica, fumed silica, salts, fibers, hydratable clays, microspheres, rice husk ash, elastomers, elastomeric particles, resins, latex, combinations thereof, and the like. A person having ordinary skill in the art, with the benefit of this disclosure, will readily be able to determine the type and amount of additive useful for a particular application and desired result. [0037] The components of the acid-soluble cement compositions may be combined in any order desired to form an acid-soluble cement composition that can be placed into a subterranean formation. In addition, the components of the acid-soluble cement compositions may be combined using any mixing device compatible with the composition, including a bulk mixer, for example. In some embodiments, a dry blend may first be formed by dry blending dry components comprising, for example, CKD and/or hydraulic cement. The dry blend may then be combined with water to form the acid-soluble cement composition. Other suitable techniques may be used for preparation of the acid-soluble cement compositions as will be appreciated by 13 Docket No. 2005-017636U5P1D1P1P1P2P1 PCT those of ordinary skill in the art in accordance with embodiments described herein. [0038] As will be appreciated by those of ordinary skill in the art, the acid-soluble cement compositions may be used in subterranean operations in accordance with embodiments described herein. Without limitation, the cement composition may be used to seal off one or more subterranean zones from a well bore; to plug a void or crack in a conduit disposed in the well bore; to plug a void or crack in a cement sheath disposed in the well bore; to plug an opening between the cement sheath and the conduit; to prevent the loss of fluid from the well bore into loss circulation zones such as a void, vug, or fracture; to form an annular plug; to isolate a gravel packed interval of the well bore; or combinations thereof. In an embodiment, the acid-soluble cement composition may be used to form an acid-soluble barrier (e.g., a plug, a seal, etc.) in a subterranean formation. For example, the acid-soluble cement composition may be introduced into a well-bore annulus and allowed to set to form an acid-soluble cement sheath. [0039] An example of a method comprises placing an acid-soluble cement composition in a subterranean formation, and allowing the acid-soluble cement composition to set in the formation. It is intended to be understood that the phrase "placing an acid-soluble cement composition in the subterranean formation" encompasses placement of the cement composition in the well bore and/or placement of the cement composition in rock surrounding the well bore with the well bore penetrating the subterranean formation, among others. The cement composition should form an acid-soluble hardened mass in the subterranean formation. The acid-soluble hardened mass can be left in the subterranean formation permanently or can be removed. Removal of the hardened mass may be desired so that the subterranean formation can be utilized in subsequent hydrocarbon production in accordance with embodiments described herein. In an embodiment, removal of the hardened mass includes contacting the hardened mass with an aqueous acid composition to at least partially dissolve the hardened mass. In some embodiments, the hardened mass may be completed removed. In other embodiments, the hardened mass may be partially removed. For example, the aqueous acid composition may contact the hardened mass to form through openings in the hardened mass to place the subterranean formation in communication with the interior of a pipe string, for example. The aqueous acid composition may include, for example, from about 7.5% to about 28% hydrochloric acid by weight of the composition. In an embodiment, the aqueous acid composition includes hydrochloric acid in an amount of about 15% by weight. 13a Docket No. 2005-017636U5P1D1P1P1P2P1 PCT [0040] Another example of a method comprises placing an acid-soluble cement composition in a well-bore annulus (e.g., an annulus between a pipe string disposed in a well bore and a wall of the well bore); and allowing the acid soluble cement composition to set. For example, the acid-soluble cement composition may set in the well-bore annulus to form an acid soluble cement sheath. The acid-soluble cement sheath can be left in the subterranean formation permanently or can be removed. Removal of the hardened mass may be desired so that the subterranean formation can be utilized in subsequent hydrocarbon production in accordance with embodiments of the present invention. In an embodiment, removal of the hardened mass includes contacting the hardened mass with an aqueous acid composition to at least partially dissolve the hardened mass. For example, the aqueous acid composition may contact the hardened mass to form through openings in the hardened mass to place the subterranean formation in communication with the interior of a pipe string, for example. In some embodiment, the aqueous acid composition may be placed into the well bore and allowed to contact the hardened mass through one or more openings in the pipe string. [0041] To facilitate a better understanding of the disclosure, the following examples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or define, the scope of the embodiments. EXAMPLE 1 [0042] A series of acid-soluble cement compositions was prepared at room temperature and subjected to crush strength and solubility testing. Each of the samples contained sufficient water to provide the density provided in the table below and comprised various quantities of Class H Portland cement, Holcim CKD, and/or calcium carbonate, as indicated in the table below. [0043] Solubility Testing: For the solubility testing, each sample was poured into a 2-inch cube and allowed to cure in a water bath at 150'F for either 48 hours (Samples 1-5) or 72 hours (Samples 6-10). After curing, the sample cubes are placed in an 80'F water bath for at least 30 minutes and then weighed to determine an initial weight. Each sample cube was then submerged in 2,000 milliliters of a 15% by weight hydrochloric acid solution in a 3,000 milliliter beaker. The sample cube was supported in the acid solution above a magnetic stir bar. The 14 Docket No. 2005-017636U5P1D1P1P1P2P1 PCT magnetic stir bar was rotated to create a slight vortex on the surface of the acid solution. After 30 minutes, the sample cube was removed from the acid solution and weighed to determine a final weight. The acid solubility of each composition was calculated by the following formula: 14a WO 2014/035923 PCT/US2013/056719 Acid Solubility = initiall Weight - Final Weight) / Initial Weight x 100 [0044] Crush Strength Testing: For the crush strength testing each sarnpl was poured into a 2-inch cube, allowed to cure in a water bath at 150*F for 48 hours (Sanples 1 5) or 72 hours (Samples 6-10). and then crushed, The crush strengths were determined using 5 a Tinius Olson tester in accordance with A1I Specification 10. [0043] The results of the tests are set forth in the table below In the flowing table, percent by weight is based on the weight of the cement and the CKD in the samples. TABLE I 10 Crush Strength Tests: Cement, CKD, and CaCO3 Portland Dissolution Acis CKD CaMO Acid Strength DensPtv Cement Time in Sample (% by (% by 1%H1 Solubility (pp~g) (% bv .15%t HO wt) Wt) (%) Wt) (m n) 48 Hr 72 Hr S575 25 1007 306 2 550 50 003990 523 _____ 5i 30 J 99MI01 3 15 2 75 too 30 99,88 353 4 15 0 100 1 20 9925 6712 5 50 0 100 30 66146 004 6 14.5 75 25 300 30 90 152 7 45 50 300 30 92,61 I 8 14,5 75 300 30 93,55 61 9 14,5 0 100 300 30 99,38 - 20 10 1485 0 3 30 1'.45 [0046] Example I thus indicates that acid-soluble cement compositions containing 15 from 25% to 100% CKD by weight, from 0% to 75% Portland cement by weight, and from 1.00% to 300% calcium carbonate by weigA may have properties suitable for use in acid soluble operations. EXAMPLE 2 [0047] An additional series of acid-soluble cement composiions was prepared and 20 subjected to thickening time, force resistance, and theological tests. Each of the samples contained sufficient water to provide the density provided in the table below and comprised various quantities of Class - Portdand cement, Hocin CKD, calcium carbonate, a dispersant (CFR>3 cement friction reducer> and/or a set-retarding additive, as indicated in the table 15 WO 2014/035923 PCT/US2013/056719 below. In the following tables, percent by weight is based on the weight of the cement and the CKI) in the samples, [00481 The samples were prepared at room temperature with thickening time tests conducted at 140'F on a portion of each composition in accordance with API Specification 5 10. The crush strength of Sample 12 was determined by pouring the sample into a 2-inch cube, allowing it to cure in a water bath at 160'F for 72 hours, and then crushing the cured cube. The crush strength was determined using a Tinius Olson tester in accordance with API Specification 10. The results of the thickening time and force resistance tests are provided in the table below, 1 0 TABLE2 Thickening Time Tests: Cement, CKD, and CaCO 3 Portland CKD Thickening 72-Hr aCO Retarder Densitv Cement (% C O 3 DRspersant Time Crush Sample % b (% by! (ppg) (%jby by (% by wt to 70 be Strength (ppg)O (% in 1wv jIN% by Wti~) wt)0 wt) 12 I' ~ 0 O 100- 3:7054 135 0 50 100 - 2 3 1 12 15 50 50 00 - II327 545 H1R 3 5 25 1,00 1,41 SCR-5 " % 14 16 75 25 1.00 8,42 15 [0049] For the rheological tests, additional portions of the acid-soluble cement compositions were conditioned in an atmospheric consistometer to the test temperature. After conditioning, the rheology of the compositions was determined using a Fann Model 35 viscometer at the temperature indicated in the table below using a bob and sleeve and spring 41 in accordance with the procedure set forth in AP). Specification 10 The results of the 20 theological tests are set forth in the table below. In the following table, percent by weight is based on the weight of the cement and the CKD in the samples. 16 WO 20 14/035923 PCT/US2013/056719 TABLE 3 -Rheological Tests Wotl D CK)ilptv Retard IRotal iois, Per Miututt Dest cuen 0 ~ 1 Ca(7t zr 1.tp, I% by by by (% 1w ( bv o" H 60 30 20 Z Ut 6 z WU W ~ nl wt) 0 )~ 6 3 75 O 6 41 30 1 6 5 4 12 1 50 50 to() HR. 7K 1> 15 11 1 40 48 : 795 54 26 7 1 1S 2 16 5 2 100 (v SCh ~ [1 6 1 7 i I4 16 75 25 10 0 12 WO 2014/035923 PCT/US2013/056719 [0050] Example 2 thus indicates that acid-solubl cement compositions containing from 25% to 50% CKD by weight, from 50% to 75% Portland cement by weight, and 100% calcium carbonate by weight may have properties suitable for use in acid-soluble operations, EXAMPLE 3 5 [0051] An additional acid-soluble cement composition was prepared to determine force resistance properties of compositions comprising pimicite. The composition contained sufficient water to provide the density provided in the table below and comprised Class 1 Portland cement, 200-mesh purnicite; calcium carbonate, a set-retarding additive (1-S retarded), and hydrated lime, as indicated in the table below, For the acid solubility testing 10 the composition was poured into a 2-inch cube and cured at 1.809 for 24 hours. The acid solubility of the composition was then determined by submerging the cured cube in a 15% by hydrochloric acid solution in accordance with the procedure described above in Example L For the crush strength testing, the composition was poured into a 2-inch cube, allowed to cure in a water bath for 24 hours at I 80T, and then crushed. The 24-hour crush 15 strength was determined using a Tinius Olson tester in accordance with API Specification 10, The results of the tests are set forth in the table below, In the following table, percent by weight is based on the weight of the cement and the CKD in the samples. 18 WO 2014/035923 PCT/US2013/056719 TABLE 4 Crush Strength Tests Cement, Pumicite, and CaCOs ardadCaC'Ok tre idae Acd Samp e Cement (%by ( by UIv (%tSelabib %PP by by t) w y s (%~ z 15 1 15 50 SO 100 30 98,62 1400 HR-5 5 19 WO 2014/035923 PCT/US2013/056719 [0052] Example 3 thus hidicates that acid-soluble cement compositions containing Portland cement, pumicite, and calcium carbonate may have properties suitable For use in acid-soluble operations. EXAMPLE 4 [0053] An additional series of acid-soluble cement compositions was prepared at room temperature to determine foree resistance properties of compositions comprising Sorei cement (e.g., a mixture of magnesium chloride and magnesiun oxide), CK.D, and/or pumicite. Each of the samples contained water, magnesium chloride (C-TEK). magnesium Oxide (THERM ATEK' LT additive), Holcim CKD, 200-mesh pumicite, and/or hydrated 10 ilme, as indicated in the table below. The crush strength of the compositions was determined by pouring each composition into a 2-inch cube. allowing the cube to cure in a water bath at 140' for either 24 or 48 hours, and then crushing the cured cube, The crush strengths were determined using a Tinius Olson tester in accordance with API Specification 10. The results of the tests are set forth in the table below. 15 TABLES Crush Strength Tests: Sorel Cement CKD, and/or Pumicite Crush Water MgC2 MgO CKD Pumieite Hydrated Strength Sample Lsi (g) (9) W4 14W (4 iAme 24 Hr 72 Hr 16 200 300 300 - 460 17 200 300 285 Is 2430 18 200 300 270 30 22'8W 9 200 300 225 7 1116 0 200 200 2.25 12 125 I 82 21_1_ 200 300 300 7----- ;- - 1864 22 200 300 285 3080 200 300 270 30 2790 24 200 300 15 75 -- 2360 ~~ 2 300 2255 7 75 2360 20 [0054] Example 4 thus indicates that acid-soluble cement compositions containing Sorel cement, cement kiln dust, and/or puticite may have properties suitable for use in acid soluble operations. 20 WO 2014/035923 PCT/US2013/056719 EXAMPLE 5 [0055] An additional series of acid-soIuble cement compositons was prepared at room temperature to determine force resistance properties of lightweight compositions compnsing Sorel cement (eg, a mixture of magnesium chloride and magiesium oxide) and 5 CKD. Each of the samples contained water, irmagneswim chloride (C-EK additive), magnesium oxide (UTERMATEKT additive)5 Holcim CKD, a set-retarding additive (R TEK inhibitor), and. glass bubbles (JGS 2000 glass bubbles), as indicated in the table below. he crush strength of the compositions was determined by pouring each composition into a 2 inch cube, allowing the cube to cure in a water bath at 40"F for 24 hours, and then crushing 10 the cured cube, The crush strengths were determined using a Tinius Olson tester in accordance with API Specification 10, The results of the tests ar set forth in the table below. TABLE 6 Crush Strength Tests: 15 Sorel Cement and CK) 24-Hr Density Water MgC 12 MgO CKD Retarder Crush Sample Bubbles (PPg) (g) (g) (g) (g) (g) Strenth 26 123 200 300 300 18 50 923 27 W84 200 300 225 75 J 8 50 663 [0056]' example 5 thus indicates that acid-solubl cement compositions having a lightweight and containing Sorel cement and cement kiln dust may have properties suitable for use in acid-soluble operatons. 20 EXAMPLE 6 [0057] An additional series of acid-soluble cement compositions was prepared at room temperature and subjected to thickening time tests at 1404F in accordance with API Specification I0. Each of the samples contained water, magnesium chloride (C-TEK additive), matnesium oxide (THUE"RMATE..K " LT additive), Holcim CKD and a retarder (R 25 TEK inhibitor) as indicated in the table beow. The results of the tests are set forth in the table below. 30 21 WO 2014/035923 PCT/US2013/056719 TABLE 7 Thickening Time Tests: Sorel Cenent and CKD Thickenin Water MgCI2 Mg( CKD Retarder Time Samplz (g) (g) (g) (g) to 70 be (hr:min) 28....... 200 300 225 75 5 00:36 29 200 300 225 75 9 1 13 30 200 300 225 75 18 11 5 [0058] Example 6 thus indicates that acid-soluble cement compositions containing Sorel cement and cement kiln dust may have properdes suitable for use in acid-soluble operations. EXAMPLE 7 [0059] An additional. acid-soluble cement composition was prepared at room 10 temperature and subjected to crush strength and solubility testing. 'This sample was prepared to test the solubility of an acd-sOiluble cement composition conprising CKD and free of any acidsoluble ilsThe sample comprised Holcim CKD (25% bwob), Te xa Lehigh C - ass H Portland cement (25% bwob), fly ash (POZMN A cemnent additive, 25% bwob), bentonite (2.5% bwob), a set-retarding additive (H R* 800 retarded, 0.4% beob) a fluid-loss 15 control additive (HALAD 447, 0 25% bwob), a free-water-control additive (WG-17 EXP free-water control agent, 0 2% bwob ) and fresh water ( 6.2 gal/sk). The abbreviation "% bwob" indicates the percent of the component by weight of a cement blend comprising the CKD, Portland cement, and fly ash, The abbreviation "gal/sk" indicates gallons per 895 pound sack of the cement blend. The samnpl had a density of 14 pounds per gallon. 20 [0060] Crush Strength Testing: For the crush strength testing a portion of the sample was poured into a 2-inch cube and allowed to cure in a water bath at 140*F for 7 days. After curing the sample cubes were placed in an 80" water bath for at least 30 minutes and then crushed. The crush strengths were determined using a Tinius Olson tester in accordance with API Specification 10. The determined crush strength was 2,200 psi. 25 [0061] Solubility 'esting: For the solubility testing, a portion of the sample was poured into a 2-inch cube and allowed to cure in a water bath at 1401F for 48 hours. After curing, the sample cubes were placed in an 804F water bath for at least 30 minutes and then weighed to determine an initial weight. Each sample cube was then submerged in 2,000 milliliters of a 15% by weight hydrochloric acid solution in a 3,000 milliliter beaker at 30 ambient conditions. The sample cube was supported in the acid solution above a magnetic 22~ WO 2014/035923 PCT/US2013/056719 stir bar. The magnetic stir bar was rotated to create a slight vortex on the surface of the acid solution. At specified intervals, the saniple cube was removed from the acid solution and weighed to determine an interval weight. Weight loss of the cube was determined by subtracting the interval weight from the initial weight, The sample cube was then returned 5 to the acid solution. The acid solubility of each composition was calculated by the following formula: Acid Solubility = Weight Loss / initial Weight x 100 After 2 hours, the testing was completed. The results of the solubility testing are set forth in the table below, 10 TABLE 8 Acid-Solability Tests: 25% CKDt 50% Cement, and 25% Fly Ash in 15% H4CL Interval Interval Time Weight Loss Acid Sohibility z Weight (hrnmin) (gM) % (gul) 0:00 213.76 0 0 0:05 18944 24,32 4 0:10 166,04 47 72 223 t:2 10736 106.0 49.6 0:30 82.64 131.12 61,33 0:45 60.57 153.19 71.66 1:00 40,69 173,07 80.96 1:15 27,24 186. 52 87.25 1:30 1592 197,84 92.6 2:00 7,21 206.55 96.6 [0062] The solubility testing was repeated using a 75% by weight hydrochloric acid 15 solution. The results of this test are set forth below. 23; WO 2014/035923 PCT/US2013/056719 TABLE 9 Acid-Soiubility Tests: 25% CKD, 50% Cement, and 25% Fly Ash in 7.5% HCL Interval i rterva Time Weight Loss Acid Solubiity (hr~in) eight (hr an) (g) (% (gil) 0:00 202. 73 0 0 0,05 185.08 17.65 1 71 0:10 2 "1 3062 1510 0:20 1475 4 55.19 27.22 o:0 l l68 87.05 42593 0:45 92 85 109.88 5420 100 85 65 117,08 5775 115 7986 122 87 60.60 1,30 7k 6 12707 1 62 68 00 71 M3) 131,70 64,96 5 [0063] Exmkple 7 thus indicates that acid-soluble cement compositions containing CKD and free of an additional acid-soluble filler may have solibitity properties suitable for use in acid-soluble operations, EXAMPLE 8 [0064] An additional acid-soluble cement composition was prepared at room 10 temperature and subjeed to crush strength anid solubility testing. This sample was prepared to further test the solubility of an acid-soluble cement composition com-lprising CKD and free of any acid-soluble fillers. The sample comprised fHolcin CKD (100% bwob) ckIum chloride (3% bwob), and fresh. water (6.67 gal/sk), The abbreviation "% bwob" indicates the percent of the component by \ wiht of a cement Ilend consisting of the CKI), The samipe 15 had a density of 13 pounds per gallon. [0065] Crush Strength Testing: For the crush strength testing, a portion of the sample was poured into a 2-inch x 4-inch cylinder and alkiwed to cure in a water bath at 170"F for 24 hours. Ater curing, thesatple cubes were placed in an 80"F water bath for at least 30 minutes and then crushed, The crush strengths were determined using a Tinius 20 Olson tester in accordance with AP1 Specification 10, The determined crush strength was 345 psi. [0066] Solubility Testiing: For the solubility testing. a portion of the sample was poured into a 2-inch x 4-inch cylinder and. allowed to cure in a water bath at 1401F for 24 hours. A fier caring, the sample cylinders were placed in an 80'F water badh for at least 30 25 minutes and then weighed to determine an initial weight. Each sample cylinder was thenl 24 WO 2014/035923 PCT/US2013/056719 submerged in 2,000 milliliters of a 7.5% by weight hydrochloric acid solution at 140GF in a 3;000 milliliter beaker. The sample cylinder was supported in the acid solition above a niagnetic stir bar. The magnetic stir bar was rotated to create a slight vortex on the surface of the acid solution, The sample cylinder was observed, and the time for complete 5 dissolution of the sample cylinder was recorded, If not completely dissolved, the sample cylinder was removed from the acid solution after 2 hours and weighed to determine a final weight. The acid solubility was then was calculated by the following formula: Acid Solubility = (Initial Weight - Final Weight) / Initial Weight x 100 The solubility testing was repeated using a 7,.5% by weight hydrochloric acid solution and a 10 1 5% by weight hydrochloric acid solution. The results of the solubility testing are set forth in the table below. TABLE 10 Acid-Solubility Tests: 100% CKD HCI Solution Dissolution Time Acid Solublity (hr min) (%) 3.0% 2:00 8 5 % 1:45 100 15% 0:12 100 15 [0067] Example 8 thus indicates that acid-soluble cement compositions containing CKD and free of an additional acid-soluble filler may have solubility properties suitable for use in acid-soluble operations. [0068] It should be understood that the compositions and methods are described in terms of "comprising," "containing," or "including" various components or steps, the 20 compositions and methods can also "consist essentially of' or "consist of" the various components and steps. Moreover, the indefinite articles "a" or "an," as used in the claims, are defined herein to mean one or more than one of the element that it introduces. [0069] For the sake of brevity, only certain ranges are explicitly disclosed herein. llowever, ranges from any lower limit may be combined with any upper limit to recite a 25 range not explicitly recited, as vell as, ranges from any lower limit may be combined with any other lower limit to recite a range not explicitly recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite a range not explicitly recited. Additionally, whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range fidling within the range are specifically 30 disclosed. In particular, every range of values (of the form, "from about a to about b " or, 25 equivalently, "from approximately a to b," or, equivalently, "from approximately a-b") disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values even if not explicitly recited. Thus, every point or individual value may serve as its own lower or upper limit combined with any other point or individual value or any other lower or upper limit, to recite a range not explicitly recited. [0071] Therefore, the present disclosure is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as they may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Although individual embodiments are discussed, the disclosure covers all combinations of all those embodiments. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the present invention. If there is any conflict in the usages of a word or term in this specification and one or more patent(s) or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted. 26

Claims

1. A method of cementing comprising: providing an acid-soluble cement composition comprising a kiln dust and water, wherein the acid-soluble cement composition is free of any additional cementitious components other than the kiln dust; allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass; and contacting the acid-soluble hardened mass with an acid.

2. A method according to claim 1 wherein the acid-soluble cement composition has a density of about 8 pounds per gallon to about 16 pounds per gallon.

3. A method according to claim 1 or claim 2 wherein the kiln dust comprises cement kiln dust and/or lime kiln dust.

4. A method according to any one of the preceding claims wherein the kiln dust comprises cement kiln dust present in an amount in a range of from about 1% to 100% by weight of a total amount of cementitious components present in the acid-soluble cement composition.

5. A method according to any one of the preceding claims wherein the acid-soluble cement composition is free of an acid-soluble filler.

6. A method according to any one of the preceding claims wherein the acid-soluble cement composition is free of an acid-soluble filler selected from the group consisting of dolomite, magnesium carbonate, calcium carbonate, zinc carbonate, and any combination thereof.

7. A method according to any one of the preceding claims wherein the acid-soluble cement composition further comprises an additive selected from the group consisting of metakaolin, crystalline silica, amorphous silica, fumed silica, salt, fiber, hydratable clay, microsphere, rice husk ash, an elastomer, an elastomeric particle, a resin, a latex, and any combination thereof.

8. A method according to any one of the preceding claims wherein the acid-soluble cement composition further comprises an additive selected from the group consisting of a set retarding additive, a strength-retrogression additive, a set accelerator, a weighting agent, a lightweight additive, a gas-generating additive, a mechanical-property-enhancing additive, a lost circulation material, a filtration-control additive, a dispersant, a fluid-loss-control additive, a 28 defoaming agent, a foaming agent, an oil-swellable particle, a water-swellable particle, a thixotropic additive, and any combination thereof.

9. A method according to any one of the preceding claims wherein contacting the acid-soluble hardened mass with an acid comprises contacting the acid-soluble hardened mass with an aqueous acid composition, wherein the aqueous acid composition comprises hydrochloric acid present in the aqueous acid composition in an amount of about 7.5% to about 28% by weight of the aqueous acid composition.

10. A method according to any one of the preceding claims further comprising: placing the acid-soluble cement composition into a subterranean formation.

11. A method according to claim 10 wherein the acid-soluble cement composition is allowed to set in a well-bore annulus in the subterranean formation, wherein the acid contacts the acid-soluble hardened mass through one or more openings in a pipe string disposed in the subterranean formation.

12. A method of cementing comprising: placing an acid-soluble cement composition in a subterranean formation, the acid soluble cement composition comprising: cement kiln dust in an amount of 100% by weight of a total amount of cementitious components in the acid-soluble cement composition; and water; allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass; and contacting the acid-soluble hardened mass with an acid.

13. A method according to claim 17 wherein the acid-soluble cement composition is free of an acid-soluble filler.

14. A method according to claim 12 or claim 14 wherein the acid-soluble cement composition is free of an acid-soluble filler selected from the group consisting of dolomite, magnesium carbonate, calcium carbonate, zinc carbonate, and any combination thereof.

15. A method according to any one of claims 12-14wherein the acid-soluble cement composition further comprises an additive selected from the group consisting of a set-retarding additive, a strength-retrogression additive, a set accelerator, a weighting agent, a lightweight additive, a gas-generating additive, a mechanical-property-enhancing additive, a lost-circulation 29 material, a filtration-control additive, a dispersant, a fluid-loss-control additive, a defoaming agent, a foaming agent, an oil-swellable particle, a water-swellable particle, a thixotropic additive, and any combination thereof.

16. A method according to any one of claims 12-15 wherein contacting the acid soluble hardened mass with an acid comprises contacting the acid-soluble hardened mass with an aqueous acid composition, wherein the aqueous acid composition comprises hydrochloric acid present in the aqueous acid composition in an amount of about 7.5% to about 28% by weight of the aqueous acid composition.

17. A method according to any one of claims 12-16wherein the placing the acid soluble composition comprises placing the acid-soluble composition in a well-bore annulus between a pipe string disposed in the subterranean formation and a wall of a well bore.

18. A method according to any one of claims 12-17 wherein the acid-soluble cement composition is allowed to set in a well-bore annulus in the subterranean formation, wherein the acid contacts the acid-soluble hardened mass through one or more openings in a pipe string disposed in the subterranean formation.

19. A method according to claim 12 wherein the acid-soluble cement composition further comprises an acid-soluble filler.

20. A method of cementing comprising: placing an acid-soluble cement composition in a subterranean formation, the acid soluble cement composition comprising cement kiln dust and water, wherein the acid-soluble cement composition is free of any acid-soluble fillers; allowing the acid-soluble cement composition to set to form an acid-soluble hardened mass; and contacting the acid-soluble hardened mass with an acid.

21. A method according to claim 20 wherein the cement kiln dust is present in an amount in a range of from about 1% to 100% by weight of a total amount of cementitious components present in the acid-soluble cement composition.

22. A method according to any one of claim 20 wherein the acid-soluble cement composition is free of any additional cementitious components other than the cement kiln dust.

23. A method according to claim 20 or claim 21 wherein the acid-soluble cement composition further comprises an additive selected from the group consisting of a fly ash, a slag 30 cement, metakaolin, shale, zeolite, crystalline silica, amorphous silica, fumed silica, salt, fiber, hydratable clay, microsphere, rice husk ash, an elastomer, an elastomeric particle, a resin, a latex, and any combination thereof.

24. A method according to any one of claims 20-23 wherein the acid-soluble cement composition further comprises an additive selected from the group consisting of a set-retarding additive, a strength-retrogression additive, a set accelerator, a weighting agent, a lightweight additive, a gas-generating additive, a mechanical-property-enhancing additive, a lost-circulation material, a filtration-control additive, a dispersant, a fluid-loss-control additive, a defoaming agent, a foaming agent, an oil-swellable particle, a water-swellable particle, a thixotropic additive, and any combination thereof.

25. A method according to any one of claims 20-24wherein contacting the acid soluble hardened mass with an acid comprises contacting the acid-soluble hardened mass with an aqueous acid composition, wherein the aqueous acid composition comprises hydrochloric acid present in the aqueous acid composition in an amount of about 7.5% to about 28% by weight of the aqueous acid composition.

26. A method according to any one of claims 20-25wherein the acid-soluble cement composition is allowed to set in a well-bore annulus in the subterranean formation, wherein the acid contacts the acid-soluble hardened mass through one or more openings in a pipe string disposed in the subterranean formation. 31