JP2575670B2 - Divider - Google Patents
DividerInfo
- Publication number
- JP2575670B2 JP2575670B2 JP61257844A JP25784486A JP2575670B2 JP 2575670 B2 JP2575670 B2 JP 2575670B2 JP 61257844 A JP61257844 A JP 61257844A JP 25784486 A JP25784486 A JP 25784486A JP 2575670 B2 JP2575670 B2 JP 2575670B2
- Authority
- JP
- Japan
- Prior art keywords
- woven
- partition plate
- synthetic resin
- woven fabric
- integrated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、コンピュータやワードプロセッサ、あるい
はファクシミリ等、一般にITEと呼ばれる各種電子機器
から輻射される漏洩電磁波を遮蔽し、ITEの誤動作を防
止するのに好適な仕切板に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial Application Field) The present invention is intended to shield a leaked electromagnetic wave radiated from various electronic devices generally called ITE, such as a computer, a word processor, a facsimile, etc., to prevent a malfunction of the ITE. The present invention relates to a suitable partition plate.
（従来の技術） 近年、上記したようなITEの発展は目覚ましく、今や
ほとんどのオフィースに普及しているが、その一方でIT
Eから輻射される電磁波や、通信機器等からの各種ノイ
ズによるITEの誤動作が問題になってきている。(Prior art) In recent years, the development of ITE as described above has been remarkable, and is now spreading to most offices.
Malfunctions of ITE due to electromagnetic waves radiated from E and various noises from communication devices and the like have become a problem.
ところで、オフィース内においては、普通、仕切板に
よって室内が使用目的に応じた複数の小部屋に仕切られ
ており、上述したようなITEを設置する場合にもそうし
た小部屋をITEのために設けることが一般に行われてい
る。このようにオフィース内を複数の小部屋に仕切る場
合に使用される仕切板としては、従来、表面に塗装を施
した薄板鉄板の中空パネルからなる仕切板や、上方の一
部または全面にガラスを嵌め込んでなる仕切板、あるい
はガラスに替えて透明な合成樹脂板を用いた仕切板等が
一般的であった。By the way, in the office, the room is usually divided into a plurality of small rooms according to the purpose of use by a partition plate, and when installing the ITE as described above, such a small room should be provided for the ITE Is commonly done. Conventionally, as a partition plate used to partition the inside of the office into a plurality of small rooms, conventionally, a partition plate consisting of a hollow panel of a thin iron plate coated on the surface, or glass on a part or the entire upper surface. A partition plate fitted therein, a partition plate using a transparent synthetic resin plate instead of glass, and the like were generally used.
（発明が解決しようとする問題点） ところが、薄板鉄板の中空パネルからなる仕切板の場
合は、電磁波遮蔽性を有し、前記ITEから輻射される電
磁波や他からの各種ノイズを遮蔽することができる反
面、不透明であるため仕切板の向う側が見えないといっ
た不都合があった。またそれとともに、仕切板自体が非
常に重いため、運搬および設置等に多大の労力を要する
といった問題もあった。また、ガラスを用いた仕切板の
場合は、仕切板の向う側が見えないといったことはない
ものの、電磁波遮蔽性が全くないため、ITEから輻射さ
れる電磁波や他からの各種ノイズを遮蔽することができ
ず、ITEの誤動作を防止することができないといった問
題があるとともに、薄板鉄板からなる仕切板と同様重量
が大であるといった問題があった。さらに、合成樹脂板
を用いた仕切板の場合は、軽量で運搬および設置等が楽
に行えるといった利点を有するものの、やはりガラスを
用いた仕切板と同様電磁波遮蔽性が全くないといった不
都合があった。なお、合成樹脂板を用いたもののうち、
帯電防止性を付与するために帯電防止剤を添加したり、
塗布した合成樹脂板を使用した仕切板があるが、これは
静電気の帯電を防ぎ、埃等の付着による汚損を防止する
ことを目的としたものであって、電磁波遮蔽性を有する
ものではない。(Problems to be Solved by the Invention) However, in the case of a partition plate made of a hollow panel made of a thin iron plate, the partition plate has an electromagnetic wave shielding property, and may shield electromagnetic waves radiated from the ITE and various noises from other sources. On the other hand, there was a disadvantage that the side opposite to the partition plate could not be seen because of the opacity. At the same time, the partition plate itself is very heavy, so that there is a problem that much labor is required for transportation and installation. In addition, in the case of a partition plate using glass, the side opposite to the partition plate is not visible, but there is no electromagnetic wave shielding, so it is possible to shield electromagnetic waves radiated from ITE and various other noises. In addition to this, there is a problem that ITE malfunctions cannot be prevented, and there is a problem that the weight is large like a partition plate made of a thin iron plate. Further, in the case of a partition plate using a synthetic resin plate, there is an advantage that it is lightweight and can be easily transported and installed, but there is also a disadvantage that there is no electromagnetic wave shielding property like the partition plate using glass. In addition, among those using a synthetic resin plate,
Add antistatic agent to impart antistatic properties,
There is a partition plate using a coated synthetic resin plate, which is intended to prevent electrostatic charging and to prevent contamination due to adhesion of dust and the like, and does not have electromagnetic wave shielding properties.
（問題点を解決するための手段） 本発明の仕切板は、フィラメント糸からなる導電性織
布もしくは不織布であって、次式で定義される開孔率が
0.5以上の織布もしくは不織布と、全光線透過率が70％
以上の透明合成樹脂板とが溶融一体化されるとともに、
この溶融一体化された織布もしくは不織布の隅角部にア
ース端子が貫設されてアースされてなる仕切板である。(Means for Solving the Problems) The partition plate of the present invention is a conductive woven or nonwoven fabric made of a filament yarn, and has a porosity defined by the following formula.
Woven or non-woven fabric of 0.5 or more and total light transmittance of 70%
While the above transparent synthetic resin plate is melted and integrated,
An earth terminal is provided at a corner of the melt-integrated woven or nonwoven fabric to be earthed.
A:メッシュ（本／インチ） D:繊維径（μｍ） （作用） 導電性フィラメント糸からなるアースされた織布もし
くは不織布により、ITEから輻射される電磁波や他から
の各種ノイズが遮蔽される。また、合成樹脂板が全光線
透過率70％以上と透明であり、しかも上式で定義された
織布もしくは不織布の開孔率が0.5以上であり、そのう
え織布もしくは不織布を構成する繊維が紡績糸ではなく
フィラメントであって、繊維自身の表面平滑性に優れ、
そのため織布もしくは不織布自体も光の透過性を有して
いることにより、仕切板自体の光の透過性が確保され
る。さらに、織布もしくは不織布と透明合成樹脂板とを
溶融一体化しているので、透明性を損なわずに仕切板の
軽量化が図られる。さらに、合成樹脂板と溶融一体化し
た織布もしくは不織布の隅角部にアース端子を貫設して
いるので、フィラメント糸で構成された織布もしくは不
織布の強度不足も懸念されることなく、この織布もしく
は不織布にアース端子を確実に設けることができる。 A: Mesh (books / inch) D: Fiber diameter (μm) (Action) Electromagnetic waves radiated from the ITE and various other noises are shielded by a grounded woven or nonwoven fabric made of conductive filament yarn. In addition, the synthetic resin plate is transparent with a total light transmittance of 70% or more, and the porosity of the woven or nonwoven fabric defined by the above formula is 0.5 or more, and the fibers constituting the woven or nonwoven fabric are spun. It is a filament, not a yarn, and has excellent surface smoothness of the fiber itself,
Therefore, since the woven or nonwoven fabric itself also has light transmittance, the light transmittance of the partition plate itself is ensured. Furthermore, since the woven or nonwoven fabric and the transparent synthetic resin plate are melted and integrated, the weight of the partition plate can be reduced without impairing the transparency. Furthermore, since the ground terminal is provided at the corner of the woven or non-woven fabric that is melt-integrated with the synthetic resin plate, the strength of the woven or non-woven fabric made of filament yarn is not a concern. The ground terminal can be reliably provided on the woven or nonwoven fabric.
（実施例） 以下、本発明の実施例を図面を参照して説明する。Hereinafter, embodiments of the present invention will be described with reference to the drawings.
第１図は本発明に係る仕切板をフレームに嵌め込んで
使用した場合を示す全体斜視図、第２図は第１図で示す
Ａ−Ａ線断面図、第３図はアース部分を示す部分拡大断
面図、第４図は織布を示す拡大部分正面図である。FIG. 1 is an overall perspective view showing a case where a partition plate according to the present invention is fitted into a frame and used, FIG. 2 is a sectional view taken along line AA shown in FIG. 1, and FIG. FIG. 4 is an enlarged partial front view showing the woven fabric.
第１図において、仕切板１は、導電体からなるフレー
ム２の上部に形成した空所にパッキング３を介して嵌め
込まれており、フレーム２はその下端部に複数枚の脚板
４…が設けられ自立可能になされている。In FIG. 1, a partition plate 1 is fitted via a packing 3 into a space formed above a frame 2 made of a conductor, and the frame 2 is provided with a plurality of leg plates 4 at its lower end. It is made self-sufficient.
仕切板１は、第２図に示すように、２枚の透明な合成
樹脂板5,6の間に、導電性フィラメント糸からなる織布
７が介在されるとともに、これら３者が一体的に固着さ
れたものである。また、織布７は、第３図に示すよう
に、仕切板１の隅角部に貫設されたアース端子８と接続
されており、このアース端子８に接続された導電線９を
介してアースされている。As shown in FIG. 2, the partition plate 1 has a woven fabric 7 made of conductive filament yarn interposed between two transparent synthetic resin plates 5 and 6, and these three members are integrally formed. It is fixed. As shown in FIG. 3, the woven fabric 7 is connected to an earth terminal 8 penetrating through the corner of the partition plate 1 and via a conductive wire 9 connected to the earth terminal 8. Grounded.
上記合成樹脂板5,6としては、全光線透過率が70％以
上のものが仕切板１の透明性を得る上で必要であり、例
えばポリ塩化ビニル、ポリメチルメタクリレート、ポリ
カーボネイト、ポリスチレン、ABS樹脂等が好適に用い
られる。As the synthetic resin plates 5 and 6, those having a total light transmittance of 70% or more are necessary to obtain the transparency of the partition plate 1. For example, polyvinyl chloride, polymethyl methacrylate, polycarbonate, polystyrene, ABS resin Etc. are preferably used.
上記織布７を構成する導電性フィラメント糸として
は、例えば銅やステンレス等の金属繊維、あるいは銅、
ニッケル等を無電解メッキさせたポリエステルやアクリ
ル等の有機繊維が好適に用いられる。Examples of the conductive filament yarn constituting the woven fabric 7 include metal fibers such as copper and stainless steel, or copper,
Organic fibers such as polyester and acryl which are electrolessly plated with nickel or the like are preferably used.
なお、図示例では２枚の合成樹脂板5,6の間に導電性
フィラメント糸からなる織布７が介在されているが、こ
れに限らず、織布７が１枚の合成樹脂板の表面もしくは
裏面、あるいは表裏両面に設けられていてもよく、また
複数枚の織布が２枚の合成樹脂板間に介在されていても
よい。さらに、仕切板１を上述のようにフレーム２に嵌
め込むことなく、仕切板１単独で自立可能になしても、
また所望の形状に曲げ加工を施すか、あるいは複数枚の
仕切板１を接着等の手段により連設して自立可能になし
てもよい。In the illustrated example, the woven fabric 7 made of conductive filament yarn is interposed between the two synthetic resin plates 5 and 6, but is not limited thereto. Alternatively, it may be provided on the back surface or on both the front and back surfaces, and a plurality of woven fabrics may be interposed between two synthetic resin plates. Furthermore, even if the partition plate 1 can be made independent by itself without being fitted into the frame 2 as described above,
Further, a bending process may be performed to a desired shape, or a plurality of partition plates 1 may be connected to each other by means such as bonding so as to be self-supporting.
また、織布７は不織布であってもよい。不織布として
は、導電性フィラメント糸が、ほぼ等間隔に縦横に交叉
して重ね合わされ、フィラメント糸の交叉部分におい
て、フィラメント同士が接触するようにして接着剤で固
定されているものである。フィラメント糸は必ずしも直
交交叉していなくてもよい。Further, the woven fabric 7 may be a non-woven fabric. As the nonwoven fabric, conductive filament yarns are vertically and horizontally crossed and superposed at substantially equal intervals, and are fixed with an adhesive so that the filaments contact each other at the crossing portions of the filament yarns. The filament yarns need not necessarily cross at right angles.
次に上記した如き仕切板１の製造方法の一例を説明す
る。Next, an example of a method for manufacturing the above-described partition plate 1 will be described.
まず、２枚の透明な合成樹脂板の間に導電性フィラメ
ント糸からなる織布を挟み、次に合成樹脂板を加熱溶融
させ、加圧した後冷却し、これにより３者を一体成形せ
しめる。なお、合成樹脂板を溶融させる際、直接熱板等
を用いて加熱してもよいし、高周波あるいは超音波等に
より加熱してもよい。また加圧時の圧力としては、10〜
50kg/cm2が好ましく、加圧手段としては、プレス機によ
り平面で加圧しても、あるいはロール等により線状に加
圧しても、つまり面圧、線圧のいずれであってもよい。
さらに、上記したように２枚の合成樹脂板の間に織布を
挟んでおいてから３者を一体化するに限らず、例えば一
方の合成樹脂板の押出成形時に、他方の合成樹脂板と織
布とを送り込んでそれらを直接一体成形してもよい。以
上述べた製造方法は、前記したような、織布が１枚の合
成樹脂板の表面もしくは裏面、あるいは表裏両面に設け
られた仕切板を製造する場合にも、また複数枚の織布が
２枚の合成樹脂板間に介在された仕切板を製造する場合
にも適用できる。First, a woven fabric made of conductive filament yarn is sandwiched between two transparent synthetic resin plates, and then the synthetic resin plate is heated and melted, pressurized and then cooled, whereby the three members are integrally formed. When the synthetic resin plate is melted, it may be heated directly using a hot plate or the like, or may be heated by high frequency or ultrasonic waves. The pressure during pressurization is 10 ~
The pressure is preferably 50 kg / cm 2 , and the pressing means may be a flat press by a press machine or a linear press by a roll or the like, that is, any of a surface pressure and a linear pressure.
Further, as described above, the present invention is not limited to integrating the three members after sandwiching the woven fabric between the two synthetic resin plates. For example, at the time of extruding one synthetic resin plate, the other synthetic resin plate and the woven fabric may be integrated. And may be directly molded integrally. The manufacturing method described above is applicable to a case where a woven fabric is used to manufacture a partition plate provided on the front surface or the back surface of one synthetic resin plate, or both front and back surfaces, as described above. The present invention is also applicable to a case where a partition plate interposed between two synthetic resin plates is manufactured.
ここで、開孔率について簡単に説明する。開孔率と
は、織布の単位面積当たりに占める繊維のない部分（す
なわち繊維間の間隙面積）の比率であって、 で定義される。つまり、メッシュＡ、繊維径Ｄを有する
25.4mm四方の織布を想定した場合、この織布には縦横そ
れぞれ直径Ｄμｍの繊維がＡ本ずつ存在するので、縦繊
維の占める面積は Ａ×Ｄ×10-3×25.4（mm2） 横繊維の占める面積も同じく Ａ×Ｄ×10-3×25.4（mm2） 繊維の交絡部分の占める面積は A2×D2×10-6（mm2） となる。したがって、 と立式され、これを整理すると前記式となる。Here, the aperture ratio will be briefly described. The porosity is a ratio of a fiber-free portion (that is, a gap area between fibers) occupying a unit area of the woven fabric, Is defined by That is, it has a mesh A and a fiber diameter D.
Assuming a 25.4 mm square woven fabric, this woven fabric has A fibers each having a diameter of D μm in each of the vertical and horizontal directions. Therefore, the area occupied by the vertical fibers is A × D × 10 −3 × 25.4 (mm 2 ) The area occupied by the fiber is also A × D × 10 −3 × 25.4 (mm 2 ) The area occupied by the entangled portion of the fiber is A 2 × D 2 × 10 -6 (mm 2 ). Therefore, The above equation is obtained by rearranging the equations.
以下に、本発明に係る仕切板の具体例を挙げる。 Hereinafter, specific examples of the partition plate according to the present invention will be described.
〈具体例１〉 導電性フィラメント糸織布として、金属含有率が13.3
wt％、繊維径45μｍ（繊度20デニール）、135メッシュ
よりなる開孔率0.58のニッケル無電解メッキポリエステ
ルモノフィラメント糸織布（株式会社高瀬染工場製メッ
タス＃401−Ｄ）１枚を用い、合成樹脂板として、厚み1
mmで全光線透過率80％の硬質塩化ビニル板２枚を用いた
ものの場合、次に示すように優れた透明性と電磁波遮蔽
性とが得られた。<Example 1> As a conductive filament yarn woven fabric, the metal content was 13.3.
wt%, fiber diameter 45μm (denier 20 denier), 135 mesh, nickel electroless plating polyester monofilament yarn woven cloth (Mettasu # 401-D, manufactured by Takase Dyeing Co., Ltd.) As a board, thickness 1
In the case of using two hard vinyl chloride plates having a total light transmittance of 80% in mm, excellent transparency and electromagnetic wave shielding properties were obtained as shown below.
透明性：全光線透過率 53％ 曇 価 8％ 電磁波遮蔽性:30〜1000MHzに対し、30〜60dB 〈具体例２〉 導電性フィラメント糸織布として、金属含有率が16.7
wt％、繊維径71μｍ（繊度50デニール）、106本／イン
チ×83本／インチのメッシュを有する開孔率0.54のニッ
ケル無電解メッキポリエステルモノフィラメント糸織布
（株式会社高瀬染工場製メッタス＃301）１枚を用い、
合成樹脂板として、厚み1mmで全光線透過率80％の硬質
塩化ビニル板２枚を用いたものの場合、次に示すよう
に、透明性ではわずかながら具体例１のものより劣るも
のの優れた電磁波遮蔽性が得られた。Transparency: Total light transmittance 53% Haze value 8% Electromagnetic shielding: 30 to 60 dB for 30 to 1000 MHz <Specific Example 2> As a conductive filament yarn woven fabric, the metal content is 16.7.
wt%, fiber diameter 71μm (50 denier fineness), nickel electroless plated polyester monofilament yarn woven fabric with 106 / inch x 83 / inch mesh and opening rate of 0.54 (Mettasu # 301 manufactured by Takase Dyeing Factory) Using one,
In the case of using two hard vinyl chloride plates each having a thickness of 1 mm and a total light transmittance of 80% as the synthetic resin plate, as shown below, the electromagnetic wave shielding was excellent although the transparency was slightly inferior to that of Example 1. Sex was obtained.
透明性：全光線透過率 40％ 曇 価 12％ 電磁波遮蔽性:30〜1000MHzに対し、30〜60dB （発明の効果） 以上述べたように、本発明の仕切板は導電性フィラメ
ント糸からなり、開孔率が0.5以上の織布もしくは不織
布と全光線透過率が70％以上の透明合成樹脂板とが溶融
一体化されるとともに、この溶融一体化された織布もし
くは不織布の隅角部がアースされてなるものであるか
ら、ITEから輻射される電磁波や他からの各種ノイズを
遮蔽することができ、そのような電磁波や各種ノイズに
起因するITEの誤動作を確実に防止することができると
ともに、仕切板自体の光の透過性が確保され、従来のよ
うに仕切板の向う側が見えないといったことがない。さ
らに、織布もしくは不織布と透明合成樹脂板とを溶融一
体化しているので、軽量で、運搬および設置等が容易に
行える等優れた効果を奏するものである。Transparency: Total light transmittance 40% Haze value 12% Electromagnetic wave shielding property: 30 to 60 MHz, 30 to 60 dB (Effect of the invention) As described above, the partition plate of the present invention is made of conductive filament yarn. A woven or nonwoven fabric having an aperture ratio of 0.5 or more is fused and integrated with a transparent synthetic resin plate having a total light transmittance of 70% or more, and the corners of the woven or nonwoven fabric thus integrated are grounded. It is possible to shield electromagnetic waves radiated from the ITE and various other noises from the ITE, and to reliably prevent malfunction of the ITE caused by such electromagnetic waves and various noises, The light transmittance of the partition plate itself is ensured, and the side opposite to the partition plate is not seen as in the related art. Furthermore, since the woven or non-woven fabric and the transparent synthetic resin plate are melted and integrated, excellent effects such as light weight and easy transportation and installation can be achieved.
図は本発明に係る仕切板の一実施例を示し、第１図は仕
切板をフレームに嵌め込んで使用した場合を示す全体斜
視図、第２図は第１図で示すＡ−Ａ線断面図、第３図は
アース部分を示す部分拡大断面図、第４図は織布を示す
拡大部分正面図である。 １……仕切板、5,6……透明合成樹脂板 ７……織布、８……アース端子1 shows an embodiment of a partition plate according to the present invention. FIG. 1 is an overall perspective view showing a case where the partition plate is fitted into a frame and used, and FIG. 2 is a cross-sectional view taken along line AA shown in FIG. FIG. 3 is a partially enlarged sectional view showing a grounding portion, and FIG. 4 is an enlarged partial front view showing a woven fabric. 1 ... partition plate, 5,6 ... transparent synthetic resin plate 7 ... woven cloth, 8 ... earth terminal
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭57−154898（ＪＰ，Ａ) 特開 昭61−225014（ＪＰ，Ａ) 実開 昭52−52759（ＪＰ，Ｕ) ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-57-154898 (JP, A) JP-A-61-225014 (JP, A) JP-A 52-52759 (JP, U)
Claims (4)
は不織布であって、次式で定義される開孔率が0.5以上
の織布もしくは不織布と、全光線透過率が70％以上の透
明合成樹脂板とが溶融一体化されるとともに、この溶融
一体化された織布もしくは不織布の隅角部にアース端子
が貫設されてアースされてなる仕切板。 A:メッシュ（本／インチ） D:繊維径（μｍ）1. A conductive woven or non-woven fabric comprising a filament yarn, wherein the woven or non-woven fabric has a porosity defined by the following formula of 0.5 or more, and a transparent synthetic resin having a total light transmittance of 70% or more. A partition plate that is melt-integrated with a plate and grounded by providing a ground terminal at the corner of the woven or non-woven fabric that has been melt-integrated. A: Mesh (book / inch) D: Fiber diameter (μm)
に介在された状態で溶融一体化されてなる特許請求の範
囲第１項に記載の仕切板。2. The partition plate according to claim 1, wherein a woven fabric or a nonwoven fabric is melted and integrated while being interposed between two synthetic resin plates.
しくは裏面、あるいは表裏両面に溶融一体化されてなる
特許請求の範囲第１項に記載の仕切板。3. The partition plate according to claim 1, wherein the woven or non-woven fabric is melt-integrated on the front surface, the back surface, or both the front and back surfaces of the synthetic resin plate.
樹脂板間に介在された状態で溶融一体化されてなる特許
請求の範囲第１項に記載の仕切板。4. The partition plate according to claim 1, wherein a plurality of woven or nonwoven fabrics are melted and integrated while being interposed between two synthetic resin plates.