JP2641735B2 - Adhesive sheet having pearl effect and method for producing the same - Google Patents
Adhesive sheet having pearl effect and method for producing the sameInfo
- Publication number
- JP2641735B2 JP2641735B2 JP63131548A JP13154888A JP2641735B2 JP 2641735 B2 JP2641735 B2 JP 2641735B2 JP 63131548 A JP63131548 A JP 63131548A JP 13154888 A JP13154888 A JP 13154888A JP 2641735 B2 JP2641735 B2 JP 2641735B2
- Authority
- JP
- Japan
- Prior art keywords
- synthetic resin
- resin film
- pearl
- adhesive
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明はパール顔料を含有する装飾用接着シート及び
その製造方法に関するものである。Description: TECHNICAL FIELD The present invention relates to a decorative adhesive sheet containing a pearl pigment and a method for producing the same.
［従来の技術］ 合成樹脂フィルムにパール調の光沢を与えるには従来
から種々の方法が使用されており、それらの大多数がパ
ール顔料を主体として該フィルムに混和成型したものを
使用している。特に装飾用として使用する場合には真珠
が発する特有の色調を再現させることに努力が傾けられ
てきた。このような方法の一つに透過率の異なるフィル
ム層を接着剤層と組み合わせ使用した例があり、これを
利用した商品は真珠に近い光沢を示すことで好評を得て
いる。[Prior Art] Various methods have conventionally been used to impart a pearly luster to a synthetic resin film, and the majority of these methods use a mixture mainly formed of a pearl pigment and mixed with the film. . In particular, efforts have been made to reproduce the unique color tone of pearls when used for decoration. As one of such methods, there is an example in which a film layer having a different transmittance is used in combination with an adhesive layer, and a product using this has been well-received for exhibiting a luster close to that of a pearl.
［発明が解決しようとする課題］ しかしながらこのような商品であっても、まだパール
感を強く発揮するには至っていない。特にそのシートを
使用する被着体の種類によってはシートを透過する光の
ために下地の色調子が重畳され、シート自体のパール発
光効果が削がれることも起きる。[Problem to be Solved by the Invention] However, even with such a product, a pearly feeling has not yet been exerted strongly. Particularly, depending on the type of the adherend using the sheet, the color tone of the base is superimposed due to the light transmitted through the sheet, and the pearl light emitting effect of the sheet itself may be reduced.
このような欠点を補うには、真珠光沢を更に増強し、
被着体面に対して隠蔽性を助長させる事が必要であると
想到した。To make up for these drawbacks, further increase the pearl luster,
It has been thought that it is necessary to enhance the concealing property on the adherend surface.
［課題を解決するための手段］ 発明者は、従来品のパールフィルムは人の眺める角度
によってパール感の強弱を生じる事を認めた。これは接
着シート平面からの光の方向性によるものであるから、
表面に凹凸を設ければ眺める角度でパール感の強弱が異
なる事が少なくなると推察し、シートをエンボス加工し
たところ、表面にメリハリがついて予想以上にパール調
が増強されることが判明した。被着体面に対する隠蔽性
を助長させるためにフィルムには顔料を練り込んで不透
明化したものを使用したが、特に蒸着フィルムを介在さ
せて透過光を遮断した場合には隠蔽性が一段と向上した
ばかりでなく、蒸着面からの反射光の重畳効果も伴っ
て、パール調が一段と増強される事が分かった。[Means for Solving the Problems] The inventor has recognized that the conventional pearl film produces a pearly feeling depending on the angle at which a person views. Because this is due to the directionality of light from the adhesive sheet plane,
It was presumed that the unevenness of the surface would reduce the difference in the pearl feeling depending on the viewing angle. When the sheet was embossed, it was found that the surface was sharpened and the pearl tone was enhanced more than expected. In order to promote the concealing property on the adherend surface, the film was made opaque by kneading a pigment into the film.However, especially when the transmitted light was blocked by interposing a vapor deposition film, the concealing property was further improved. However, it was found that the pearl tone was further enhanced due to the superposition effect of the reflected light from the deposition surface.
本発明におけるパールフィルムのエンボス加工には、
合成樹脂フィルムを箔押し機で雄・雌型に挟んで加圧・
加熱する方法が使用されるが、この方法で得られた凹凸
をフィルム単独で保持することは困難なため、例えばPE
Tのように熱変形温度が比較的高いプラスチックフィル
ムをあらかじめ積層したのち該パールフィルムをエンボ
ス加工してエンボスフィルムとすることが望ましい。従
ってこの場合の熱変形温度の高い方のフィルムはエンボ
ス加工時の加熱温度より高い熱変形温度が要求される。
このフィルムには隠蔽性を助長するために不透明化した
ものを使用することが望ましいが、その片面にあらかじ
め蒸着加工を施しておけば、前述の隠蔽性をさらに助長
出来るので好都合である。In the embossing of the pearl film in the present invention,
Press the synthetic resin film between the male and female molds
A method of heating is used, but it is difficult to hold the unevenness obtained by this method alone in the film, for example, PE
After laminating a plastic film having a relatively high heat distortion temperature such as T in advance, it is desirable to emboss the pearl film to form an embossed film. Therefore, in this case, the film having a higher heat deformation temperature is required to have a higher heat deformation temperature than the heating temperature at the time of embossing.
It is desirable to use an opaque film for promoting the concealing property of the film, but it is advantageous to apply a vapor deposition process to one side of the film in advance so that the concealing property can be further promoted.
以上の方法はあらかじめパール顔料を練り込んだフィ
ルムを使用し裏面に接着剤を使用しているが、パール顔
料はフィルムあるいは接着剤のどちらに練り込む事も可
能で、得られる効果としても大差ないことは容易に想到
され、実際に試験して可能であり、かえってパール感に
一層の深みが得られる事が分かった。The above method uses a film in which a pearl pigment has been kneaded in advance and uses an adhesive on the back surface, but the pearl pigment can be kneaded into either the film or the adhesive, and the effect obtained is not much different. This was easily conceived, and it was found that it was possible by actually testing it, and that the pearly feeling could be further deepened.
次に図面にしたがって本発明の増強されたパール調効
果を有する接着シートを説明する。Next, an adhesive sheet having an enhanced pearl effect according to the present invention will be described with reference to the drawings.
第１図は本発明の接着シートの構造の一例を示す断面
略図である。FIG. 1 is a schematic sectional view showing an example of the structure of the adhesive sheet of the present invention.
エンボスフィルム１は熱可塑性合成樹脂フィルムをエ
ンボス加工したものであらかじめパール顔料が練り込ま
れたフィルムである。このエンボスフィルム１は熱可塑
性の合成樹脂フィルムの裏面全面にあらかじめ接着剤を
塗布して接着剤層２を形成し、蒸着ないし不透明の合成
樹脂フィルム３を貼り着けたのちにエンボス加工を施し
てエンボスフィルム１の積層体とするものである。蒸着
ないし不透明の合成樹脂フィルム３は熱変形温度が比較
的高い、すなわち、前記エンボス加工時の加熱温度より
も高い熱変形温度を持つ合成樹脂に顔料を練り込んで不
透明化するかあるいは片面に蒸着加工を施したものであ
る。さらにその裏面には接着剤層４を設けて接着シート
とする。なお接着剤層４には使用直前まで接着剤面を保
護するために通常は剥離紙７を貼着して商品とする。The embossed film 1 is obtained by embossing a thermoplastic synthetic resin film, and is a film in which a pearl pigment has been kneaded in advance. The embossed film 1 is preliminarily coated with an adhesive on the entire back surface of the thermoplastic synthetic resin film to form an adhesive layer 2, and is then subjected to embossing after attaching a vapor-deposited or opaque synthetic resin film 3. It is a laminate of the film 1. The heat-deformation temperature of the vapor-deposited or opaque synthetic resin film 3 is relatively high, that is, the pigment is kneaded into a synthetic resin having a heat-deformation temperature higher than the heating temperature at the time of the embossing to make it opaque, or one side is vapor-deposited. It has been processed. Further, an adhesive layer 4 is provided on the back surface to form an adhesive sheet. In addition, a release paper 7 is usually attached to the adhesive layer 4 to protect the adhesive surface until immediately before use, so that a product is obtained.
本発明の上記構造例には接着剤層２を介在せしめてい
るが、この接着剤層を省いて熱可塑性合成樹脂フィルム
を蒸着ないし不透明の合成樹脂フィルム３に直接加熱融
着したのち該熱可塑性合成樹脂フィルムをエンボス加工
してエンボスフィルム１とする方法も広く知られてお
り、殆ど同等の接着効果がえられ、エンボスフィルムの
保持の効果は十分に得られる。In the above structure example of the present invention, the adhesive layer 2 is interposed. However, after removing the adhesive layer, the thermoplastic synthetic resin film is vapor-deposited or directly heat-fused to the opaque synthetic resin film 3, and then the thermoplastic synthetic resin film 3 is heated. A method of embossing a synthetic resin film into the embossed film 1 is also widely known, and almost the same adhesive effect can be obtained, and the effect of holding the embossed film can be sufficiently obtained.
第２図は本発明の接着シートの構造の別の一例を示す
断面略図である。FIG. 2 is a schematic sectional view showing another example of the structure of the adhesive sheet of the present invention.
エンボスフィルム５は透明熱可塑性合成樹脂フィルム
を蒸着ないし不透明の合成樹脂フィルム３と接着後にエ
ンボス加工して得られたものであるが、第１図のエンボ
スフィルム１とは異なってパール顔料の練り込みはない
フィルムである。一方接着剤層６の方には接着剤層２と
異なってパール顔料が練り込み使用される。接着剤層６
は塗工によってエンボスフィルム５の凹面部を満たし空
隙を殆ど残さないから、エンボスフィルム内に含まれる
パール顔料と殆ど類似の効果を発揮しすることが可能と
なる。The embossed film 5 is obtained by vapor-depositing a transparent thermoplastic synthetic resin film or bonding to the opaque synthetic resin film 3 and then embossing. However, unlike the embossed film 1 shown in FIG. There is no film. On the other hand, unlike the adhesive layer 2, a pearl pigment is kneaded into the adhesive layer 6 and used. Adhesive layer 6
Since the coating fills the concave portion of the embossed film 5 by coating and hardly leaves a void, it is possible to exhibit almost the same effect as the pearl pigment contained in the embossed film.
［実施例１］ 熱可塑性の塩化ビニル系パール調フィルム（日本カー
バイト工業（株）製、商品名ハイエスペイント）に対し
アルミ蒸着加工したポリエステルフィルムを熱融着した
のち、加熱押型ロールにより網スクリーンのエンボス加
工を施す。次に該ポリエステルフィルムの裏面に感圧性
接着剤を40μの厚さになるように均一に塗布し、乾燥後
に剥離紙と貼り合わせてパール調接着シートを製造し
た。[Example 1] A polyester film obtained by subjecting an aluminum vapor-deposited polyester film to a thermoplastic vinyl chloride-based pearl-like film (trade name: HS Paint, manufactured by Nippon Carbide Industry Co., Ltd.) was heat-sealed and then screened by a heated press roll. Embossing. Next, a pressure-sensitive adhesive was uniformly applied on the back surface of the polyester film so as to have a thickness of 40 μm, and after drying, was bonded to a release paper to produce a pearl-like adhesive sheet.
このようにして得た接着シートの剥離紙を剥がして焼
付塗装鋼板面に貼り着けた場合、エンボス加工をしない
同様な構造の接着シートに比較して、見る方向にかかわ
らず一層輝きに富む光沢が認められた。When the release sheet of the adhesive sheet obtained in this manner is peeled off and attached to the surface of a baked coated steel sheet, the luster is richer in brightness, regardless of the viewing direction, as compared to an adhesive sheet having a similar structure without embossing. Admitted.
［実施例２］ 熱可塑性の塩化ビニル系フィルム（日本カーバイト工
業（株）製、商品名ハイエスペイント）に対しアルミ蒸
着加工したポリエステルフィルムを接着剤を介在させて
接着したのち、加熱押型ロールにより網スクリーンのエ
ンボス加工を施す。この接着剤にはパール顔料25％を混
和したものを使用した。次に該ポリエステルフィルムの
裏面に感圧性接着剤を40μの厚さになるように均一に塗
布し、乾燥後に剥離紙と貼り合わせてパール調接着シー
トを製造した。[Example 2] A polyester film, which had been subjected to an aluminum vapor deposition process, was bonded to a thermoplastic vinyl chloride film (trade name: HS Paint, manufactured by Nippon Carbide Industry Co., Ltd.) with an adhesive therebetween, and then heated with a press roll. Emboss the screen. The adhesive used was a mixture of 25% pearl pigment. Next, a pressure-sensitive adhesive was uniformly applied on the back surface of the polyester film so as to have a thickness of 40 μm, and after drying, was bonded to a release paper to produce a pearl-like adhesive sheet.
このようにして得た接着シートの剥離紙を剥がして焼
付塗装鋼板面に貼り着けた場合、エンボス加工をしない
同様な構造の接着シートに比較して、見る方向にかかわ
らず一層輝きに富む光沢が認められ、かつ深みが感じら
れた。When the release sheet of the adhesive sheet obtained in this manner is peeled off and attached to the surface of a baked coated steel sheet, the luster is richer in brightness, regardless of the viewing direction, as compared to an adhesive sheet having a similar structure without embossing. Recognized and deep.
［発明の効果］ 本発明の接着シートは以上説明したように見る角度に
よるパール感の低下をなくし、見る場所のいかんに拘わ
らず輝きに富むパール感を得ることが可能になった。[Effects of the Invention] As described above, the adhesive sheet of the present invention can prevent a decrease in pearly feeling due to a viewing angle, and can obtain a pearly feeling rich in irrespective of a viewing position.
第１図は本発明の接着シートの構造の一例を示す断面略
図、第２図は本発明の接着シートの構造の別の一例を示
す断面略図である。 １……エンボスフィルム、２……接着剤層、３……蒸着
あるいは不透明の合成樹脂フィルム、４……接着剤層、
５……エンボスフィルム、６……接着剤層、７……剥離
紙。FIG. 1 is a schematic sectional view showing an example of the structure of the adhesive sheet of the present invention, and FIG. 2 is a schematic sectional view showing another example of the structure of the adhesive sheet of the present invention. 1 ... embossed film, 2 ... adhesive layer, 3 ... vapor-deposited or opaque synthetic resin film, 4 ... adhesive layer,
5 ... embossed film, 6 ... adhesive layer, 7 ... release paper.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｃ０９Ｊ 7/02 ＪＪＡ Ｃ０９Ｊ 7/02 ＪＪＡ ＪＪＣ ＪＪＣ ＪＪＨ ＪＪＨ ＪＪＮ ＪＪＮ ＪＫＫ ＪＫＫ ──────────────────────────────────────────────────の Continuation of the front page (51) Int.Cl. 6 Identification code Agency reference number FI Technical display location C09J 7/02 JJA C09J 7/02 JJA JJC JJC JJH JJH JJN JJN JKK JKK
Claims (4)
するパール調合成樹脂フィルムの裏面に、該パール調合
成樹脂フィルムよりも熱変形温度の高い合成樹脂フィル
ムであって不透明処理又は蒸着処理の施された合成樹脂
フィルムを積層し、該不透明処理又は蒸着処理の施され
た合成樹脂フィルムの裏面に接着剤を設けてなるパール
調効果を有する接着シート。An opaque or vapor-deposited synthetic resin film having a higher thermal deformation temperature than the pearl-colored synthetic resin film is provided on the back surface of the pearl-colored synthetic resin film containing the embossed pearl pigment. An adhesive sheet having a pearl-like effect obtained by laminating applied synthetic resin films and providing an adhesive on the back surface of the synthetic resin film subjected to the opacity treatment or the vapor deposition treatment.
ルムの裏面に、パール顔料を混和した接着剤、該透明合
成樹脂フィルムよりも熱変形温度の高い合成樹脂フィル
ムであって不透明処理又は蒸着処理の施された合成樹脂
フィルム、接着剤を順次設けてなるパール調効果を有す
る接着シート。2. An adhesive mixed with a pearl pigment on the back surface of the embossed transparent synthetic resin film, a synthetic resin film having a higher heat deformation temperature than the transparent synthetic resin film, and subjected to an opaque treatment or a vapor deposition treatment. An adhesive sheet having a pearl-like effect, in which a synthetic resin film and an adhesive are sequentially provided.
りなるパール調シートの裏面に不透明処理又は蒸着処理
の施された合成樹脂フィルムを熱融着あるいは接着剤を
用いて接着したのち、該パール調シートにエンボス加工
を施してエンボスフィルムとなし、さらに該不透明処理
又は蒸着処理の施された合成樹脂フィルムの裏面に接着
剤を塗布して形成するパール調効果を有する接着シート
の製造方法であって、前記不透明処理又は蒸着処理の施
された合成樹脂フィルムとしてエンボス加工時の加熱温
度よりも高い熱変形温度を持つ合成樹脂フィルムを用い
ることを特徴とするパール調効果を有する接着シートの
製造方法。3. An opaque or vapor-deposited synthetic resin film is adhered to the back surface of a pearl-like sheet made of a synthetic resin film containing a pearl pigment by heat-sealing or using an adhesive. A method for producing an adhesive sheet having a pearl-like effect in which an embossing process is performed on a sheet to form an embossed film, and an adhesive is formed by applying an adhesive to the back surface of the opaque or vapor-deposited synthetic resin film. A method for producing an adhesive sheet having a pearl-like effect, characterized in that a synthetic resin film having a heat deformation temperature higher than a heating temperature at the time of embossing is used as the synthetic resin film subjected to the opacity treatment or the vapor deposition treatment.
顔料を混和した接着剤を塗布し、不透明処理又は蒸着処
理の施された合成樹脂フィルムと共に接着したのち、前
記透明合成樹脂フィルムにエンボス加工を施してエンボ
スフィルムとなし、さらに該不透明処理又は蒸着処理の
施された合成樹脂フィルムの裏面に接着剤を塗布して形
成するパール調効果を有する接着シートの製造方法であ
って、前記不透明処理又は蒸着処理の施された合成樹脂
フィルムとしてエンボス加工時の加熱温度よりも高い熱
変形温度を持つ合成樹脂フィルムを用いることを特徴と
するパール調効果を有する接着シートの製造方法。4. An adhesive mixed with pearl pigment is applied to the entire back surface of the transparent synthetic resin film and adhered together with the opaque or vapor-deposited synthetic resin film, and then the transparent synthetic resin film is embossed. A method for producing an adhesive sheet having a pearl-like effect of forming an embossed film by applying an adhesive to the back surface of the synthetic resin film subjected to the opacity treatment or the vapor deposition treatment. A method for producing an adhesive sheet having a pearl-like effect, wherein a synthetic resin film having a heat deformation temperature higher than a heating temperature at the time of embossing is used as a synthetic resin film subjected to a vapor deposition process.