JP2709747B2 - Reflective sheet and method of manufacturing the same - Google Patents
Reflective sheet and method of manufacturing the sameInfo
- Publication number
- JP2709747B2 JP2709747B2 JP2214828A JP21482890A JP2709747B2 JP 2709747 B2 JP2709747 B2 JP 2709747B2 JP 2214828 A JP2214828 A JP 2214828A JP 21482890 A JP21482890 A JP 21482890A JP 2709747 B2 JP2709747 B2 JP 2709747B2
- Authority
- JP
- Japan
- Prior art keywords
- reflective
- reflection
- layer
- transparent film
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、透明フィルムの上に反射効果を有する反射
部分が表れた反射シート及びその製造方法に関する。Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a reflection sheet in which a reflection portion having a reflection effect appears on a transparent film, and a method for manufacturing the same.
従来、第６図に示すように反射材シート（ロ）の上
に、反射効果を有する文字、図形、記号（図ではアルフ
ァベットの「TA」）などが反射部分（ハ）として表れた
反射シート（イ）が知られている。この反射シート
（イ）は、第７図に示すように、反射材シート（ロ）の
上にインキでもって反射部分（ハ）を印刷したものであ
る。Conventionally, as shown in FIG. 6, a reflection sheet (b) in which characters, figures, symbols (in the figure, "TA" in the alphabet) etc. having a reflection effect appear as reflection portions (c) on a reflection material sheet (b). B) is known. As shown in FIG. 7, the reflection sheet (a) is obtained by printing a reflection portion (c) with ink on a reflection material sheet (b).
この反射シート（イ）は、それ自体を商品等に貼付す
ればステッカーとして機能する。しかし、反射部分
（ハ）の周囲の反射材シート（ロ）を除去して反射部分
（ハ）のみをステッカーとして商品等に貼付したいとい
う要望がある。その場合には反射部分（ハ）を反射シー
ト（イ）から打ち抜き、これを透明なシートに貼付して
ステッカーとすればよく、このステッカーを商品等に貼
付することにより視覚的に反射部分（ハ）のみが商品等
に付着しているような効果を得ることができる。This reflection sheet (a) functions as a sticker if it is attached to a product or the like. However, there is a demand for removing the reflector sheet (b) around the reflective portion (c) and attaching only the reflective portion (c) to a product or the like as a sticker. In such a case, the reflecting portion (c) may be punched out of the reflecting sheet (a), and the stamped portion may be pasted on a transparent sheet to form a sticker. ) Can be obtained as if it were attached to a product or the like.
しかし、これまでは反射シート（イ）から反射部分
（ハ）を打ち抜く作業を要するので、その分だけ手間が
かかると共にコスト的に高くつく。However, hitherto, an operation of punching out the reflecting portion (c) from the reflecting sheet (a) is required, which is troublesome and costly.
また、上記従来のものでは反射材シート（ロ）で反射
して反射部分（ハ）の印刷インキを通過した光によって
固有の色彩、模様が表れ、これが反射部分の風合とな
る。Further, in the above-described conventional device, light reflected by the reflector sheet (b) and passed through the printing ink of the reflecting portion (c) gives rise to a unique color and pattern, which is the feeling of the reflecting portion.
本発明はこのような点に着目してなされたものであ
り、その目的とするところは、透明な下地の上に反射部
分が下地と一体的に表れ、且つ独特の風合を有する反射
シート及びその製造方法を提供することにある。The present invention has been made in view of such a point, and an object of the present invention is to provide a reflection sheet in which a reflection portion appears integrally on a transparent base, and has a unique feeling, and It is to provide a manufacturing method thereof.
上記目的を達成するため、本発明の講じた解決手段
は、請求項１では、アルミニウムが蒸着された透明フィ
ルムから形成される反射シートを対象とする。そして、
透明フィルムの上に反射効果を有する反射部分が形成さ
れており、上記反射部分が、少なくとも、透明フィルム
に残存するアルミニウム蒸着層と、このアルミニウム蒸
着層の上にバインダーと共にスクリーン印刷された反射
ビーズにより形成された反射ビーズ層とを備えており、
上記反射部分の周囲ではアルミニウム蒸着層が除去され
ている構成としている。In order to achieve the above object, a solution taken by the present invention is directed to a reflective sheet formed of a transparent film on which aluminum is deposited. And
A reflective portion having a reflective effect is formed on the transparent film, and the reflective portion is at least an aluminum deposited layer remaining on the transparent film, and reflective beads screen-printed with a binder on the aluminum deposited layer. And a formed reflective bead layer,
The configuration is such that the aluminum vapor deposition layer is removed around the reflective portion.
また、請求項２では、透明フィルムの上に反射効果を
有する反射部分を形成する反射シートの製造方法とし
て、アルミニウム蒸着層が形成された透明フィルムに反
射ビーズとバインダー溶液との混合液をスクリーン印刷
して上記反射部分の形状の反射ビーズ層を形成し、その
後、全体をアンモニア液で洗浄して反射ビーズ層の周囲
に露出したアルミニウム蒸着層を除去し、次いで、全体
を硝酸及び水で洗浄する構成としている。According to a second aspect of the present invention, as a method of manufacturing a reflective sheet for forming a reflective portion having a reflective effect on a transparent film, a mixed solution of reflective beads and a binder solution is screen-printed on a transparent film having an aluminum vapor-deposited layer formed thereon. To form a reflective bead layer having the shape of the above-mentioned reflective portion, and thereafter, the whole is washed with an ammonia solution to remove the aluminum deposition layer exposed around the reflective bead layer, and then the whole is washed with nitric acid and water. It has a configuration.
上記の構成により、請求項１の反射シートは、透明フ
ィルムとこの透明フィルム上に形成された反射部分とか
らなるので、これをステッカーとしてそのまま商品等に
貼付すると、反射部分のみが商品等に付着しているよう
に視覚される。According to the above configuration, the reflection sheet of claim 1 is composed of a transparent film and a reflection portion formed on the transparent film. If the reflection sheet is directly attached to a product or the like as a sticker, only the reflection portion adheres to the product or the like. Visualized as you are.
また、アルミニウム蒸着層で反射して反射ビーズ層を
通過した光によって固有の色彩、模様が表れ、従来のも
のとは違った独特の風合が得られる。In addition, the light reflected by the aluminum vapor-deposited layer and passed through the reflective bead layer gives a unique color and pattern, giving a unique feel different from the conventional one.
そして、請求項２の反射シートの製造方法によれば、
印刷工程及び洗浄工程により透明フィルム上に直接に反
射部分を形成するので、従来のように反射材シートから
反射部分を打ち抜く作業を要せず、その分、反射シート
が簡単に製造されると共に製造コストが低減される。And according to the manufacturing method of the reflection sheet of claim 2,
Since the reflective portion is formed directly on the transparent film by the printing process and the washing process, there is no need to punch out the reflective portion from the reflective material sheet as in the conventional case, and the reflective sheet is easily manufactured and manufactured accordingly. Cost is reduced.
以下、実施例を図面に基づいて詳細に説明する。 Hereinafter, embodiments will be described in detail with reference to the drawings.
第１図および第２図は実施例の反射シート１を示す。
この反射シート１は、ポリエステル製の透明フィルム２
と、この透明フィルム２の上に形成され、且つ反射効果
を有する反射部分３とからなる。この反射部分３は、平
面視でアルファベットの「TA」の形状をしている。1 and 2 show a reflection sheet 1 according to an embodiment.
This reflection sheet 1 is made of a transparent film 2 made of polyester.
And a reflective portion 3 formed on the transparent film 2 and having a reflective effect. The reflection portion 3 has the shape of the letter “TA” in plan view.
そして、第２図に示すように、上記反射部分３は、透
明フィルム側に形成されたアルミニウム層3aと、のアル
ミニウム層3aの上に形成された第１インキ層3bと、第１
インキ層3bの上に形成された反射ビーズ層3cとによって
構成されている。As shown in FIG. 2, the reflective portion 3 includes an aluminum layer 3a formed on the transparent film side, a first ink layer 3b formed on the aluminum layer 3a, and a first ink layer 3b.
A reflective bead layer 3c formed on the ink layer 3b.
上記第１インキ層3bは透明度の高いインキ、例えばプ
ロセスインキなどで形成されている。なお、反射部分３
に色をつける必要がないときには第１インキ層3bを形成
しなくてもよい。反射ビーズ層3cは反射ビーズをバイン
ダーで固めて形成されている。また、多色刷にしたいと
きは反射ビーズ層3cの上に印刷によって第２インキ層を
形成してもよい。The first ink layer 3b is formed of a highly transparent ink, for example, a process ink. The reflection part 3
When it is not necessary to color the first ink layer 3b, the first ink layer 3b need not be formed. The reflective bead layer 3c is formed by solidifying reflective beads with a binder. When multicolor printing is desired, a second ink layer may be formed on the reflective bead layer 3c by printing.
次に、この反射シート１の製造方法を説明する。ま
ず、第３図に示すようなアルミニウム蒸着層3aが形成さ
れた透明フィルム２の上にインキを印刷して上記反射部
分３の形状の第１インキ層3bを形成する。次に、この第
１インキ層3bの上に反射ビーズとバインダー溶液との混
合液をスクリーン印刷して上記反射部分３の形状の反射
ビーズ層3cを形成する（第４図参照）。この場合、第１
インキ層3bを形成しないときは透明フィルム２のアルミ
ニウム蒸着層3aの上に直接に反射ビーズ層3cを形成す
る。さらに、必要に応じて反射ビーズ層3cの上に印刷に
より第２インキ層を形成してもよい。Next, a method for manufacturing the reflection sheet 1 will be described. First, an ink is printed on the transparent film 2 on which the aluminum vapor-deposited layer 3a is formed as shown in FIG. 3 to form a first ink layer 3b having the shape of the reflection portion 3. Next, a liquid mixture of reflective beads and a binder solution is screen-printed on the first ink layer 3b to form a reflective bead layer 3c having the shape of the reflective portion 3 (see FIG. 4). In this case, the first
When the ink layer 3b is not formed, the reflective bead layer 3c is formed directly on the aluminum deposition layer 3a of the transparent film 2. Further, if necessary, a second ink layer may be formed on the reflective bead layer 3c by printing.
次いで、第４図の状態で全体をアンモニア液で洗浄し
て反射ビーズ層3cの周囲に露出したアルミニウム蒸着層
3aを除去する。その後、全体を硝酸及び水で洗浄する
と、第５図に示すように透明フィルム２の上に反射部分
３が「TA」の形状で表れて反射シート１が完成する。Next, in the state shown in FIG. 4, the entire surface is washed with an ammonia solution, and the aluminum deposition layer exposed around the reflective bead layer 3c is formed.
Remove 3a. Thereafter, when the whole is washed with nitric acid and water, the reflection portion 3 appears in the form of “TA” on the transparent film 2 as shown in FIG. 5, and the reflection sheet 1 is completed.
したがって、上記実施例によれば、反射シート１は、
透明フィルム２とこの透明フィルム上に形成された反射
部分３とからなるので、これをステッカーとしてそのま
ま商品等に貼付すると、視覚的には反射部分３のみが商
品等に付着しているような効果が得られる。Therefore, according to the above embodiment, the reflection sheet 1
Since it is composed of the transparent film 2 and the reflective portion 3 formed on the transparent film, if this is affixed to a product or the like as it is as a sticker, the effect is such that only the reflective portion 3 visually adheres to the product or the like. Is obtained.
またアルミニウム層3aで反射して反射ビーズ層3cを通
過した光によって固有の色彩、模様が表れ、従来のもの
とは違った独特の風合が得られる。In addition, light reflected by the aluminum layer 3a and passing through the reflective bead layer 3c causes a unique color and pattern to appear, giving a unique feel different from the conventional one.
そして、反射シート１は、印刷工程及び洗浄工程によ
り透明フィルム上に直接に反射部分３を形成するので、
従来のように反射材シートから反射部分を打ち抜く作業
を要せず、その分、反射シート１を簡単に製造できると
共に製造コストを低減できる。And since the reflection sheet 1 forms the reflection part 3 directly on a transparent film by a printing process and a washing process,
It is not necessary to punch out the reflecting portion from the reflecting material sheet as in the related art, so that the reflecting sheet 1 can be easily manufactured and the manufacturing cost can be reduced accordingly.
以上説明したように、請求項１の反射シートによれ
ば、アルミニウムが蒸着された透明フィルムから形成さ
れる反射シートであって、透明フィルムの上に反射効果
を有する反射部分が形成されており、上記反射部分が、
少なくとも、透明フィルムに残存するアルミニウム蒸着
層と、このアルミニウム蒸着層の上にバインダーと共に
スクリーン印刷された反射ビーズにより形成された反射
ビーズ層とを備えており、上記反射部分の周囲ではアル
ミニウム蒸着層が除去されているので、これをステッカ
ーとしてそのまま商品等に貼付することによって視覚的
に反射部分のみが商品等に付着しているような効果が得
られると共に、アルミニウム層で反射して反射ビーズを
通過した光によって独特の風合が得られる。しかも、従
来のように反射材シートから反射部分を打ち抜く作業を
要せず、その分、反射シートを簡単に製造できると共に
製造コストを低減できる。As described above, according to the reflective sheet of claim 1, the reflective sheet is formed of a transparent film on which aluminum is deposited, and a reflective portion having a reflective effect is formed on the transparent film. The reflection part is
At least, an aluminum deposited layer remaining on the transparent film, and a reflective bead layer formed by reflective beads screen-printed together with a binder on the aluminum deposited layer, and an aluminum deposited layer is provided around the reflective portion. Since it has been removed, by sticking it as it is on a product etc. as a sticker, it is possible to obtain the effect that only the reflective part is adhered to the product etc. visually, and it is reflected by the aluminum layer and passes through the reflective beads The unique light is obtained by the light. Moreover, it is not necessary to punch out the reflective portion from the reflective material sheet as in the related art, so that the reflective sheet can be easily manufactured and the manufacturing cost can be reduced.
また、請求項２の反射シートの製造方法によれば、ア
ルミニウム蒸着層が形成された透明フィルムに反射ビー
ズとバインダー溶液との混合液をスクリーン印刷して上
記反射部分の形状の反射ビーズ層を形成し、その後、全
体をアンモニア液で洗浄して反射ビーズ層の周囲に露出
したアルミニウム蒸着層を除去し、次いで、全体を硝酸
及び水で洗浄する構成としたので、従来のように反射材
シートから反射部分を打ち抜く作業を要せず、その分、
反射シートを簡単に製造できると共に製造コストを低減
できる。According to the method of manufacturing a reflection sheet of claim 2, a mixture of reflection beads and a binder solution is screen-printed on the transparent film on which the aluminum vapor deposition layer is formed to form a reflection bead layer having the shape of the reflection portion. Then, the whole was washed with an ammonia solution to remove the aluminum deposition layer exposed around the reflective bead layer, and then the whole was washed with nitric acid and water. No need to punch through the reflective part,
The reflection sheet can be easily manufactured and the manufacturing cost can be reduced.
第１図〜第５図は実施例を示し、第１図は反射シートの
斜視図、第２図は反射シートの拡大断面図、第３図〜第
５図は製造過程における反射シートの拡大断面図であ
る。第６図は従来例の斜視図、第７図はその拡大断面図
である。 尚、図中１……反射シート、２……透明フィルム、３…
…反射部分、3a……アルミニウム層、3b……第１インキ
層、3c……反射ビーズ層。1 to 5 show an embodiment, FIG. 1 is a perspective view of a reflective sheet, FIG. 2 is an enlarged sectional view of the reflective sheet, and FIGS. 3 to 5 are enlarged sectional views of the reflective sheet in a manufacturing process. FIG. FIG. 6 is a perspective view of a conventional example, and FIG. 7 is an enlarged sectional view thereof. In the drawings, 1 ... reflective sheet, 2 ... transparent film, 3 ...
... Reflection portion, 3a... Aluminum layer, 3b... First ink layer, 3c... Reflection bead layer.
Claims (2)
ら形成される反射シートであって、 透明フィルムの上に反射効果を有する反射部分が形成さ
れており、上記反射部分が、少なくとも、透明フィルム
に残存するアルミニウム蒸着層と、このアルミニウム蒸
着層の上にバインダーと共にスクリーン印刷された反射
ビーズにより形成された反射ビーズ層とを備えており、
上記反射部分の周囲ではアルミニウム蒸着層が除去され
ていることを特徴とする反射シート。1. A reflection sheet formed from a transparent film on which aluminum is deposited, wherein a reflection portion having a reflection effect is formed on the transparent film, and the reflection portion remains at least on the transparent film. An aluminum deposited layer to be provided with a reflective bead layer formed by reflective beads screen-printed together with a binder on the aluminum deposited layer,
A reflective sheet, wherein an aluminum deposition layer is removed around the reflective portion.
部分を形成する反射シートの製造方法であって、 アルミニウム蒸着層が形成された透明フィルムに反射ビ
ーズとバインダー溶液との混合液をスクリーン印刷して
反射部分の形状の反射ビーズ層を形成し、 その後、全体をアンモニア液で洗浄して反射ビーズ層の
周囲に露出したアルミニウム蒸着層を除去し、 次いで、全体を硝酸及び水で洗浄することを特徴とする
反射シートの製造方法。2. A method for producing a reflection sheet, wherein a reflection portion having a reflection effect is formed on a transparent film, wherein a mixture of reflection beads and a binder solution is screen-printed on the transparent film on which an aluminum vapor deposition layer is formed. To form a reflective bead layer in the shape of a reflective portion, and then wash the whole with an ammonia solution to remove the aluminum deposition layer exposed around the reflective bead layer, and then wash the whole with nitric acid and water. A method for manufacturing a reflection sheet, comprising: