JP2834316B2 - Solid powder cosmetics - Google Patents
Solid powder cosmeticsInfo
- Publication number
- JP2834316B2 JP2834316B2 JP32028190A JP32028190A JP2834316B2 JP 2834316 B2 JP2834316 B2 JP 2834316B2 JP 32028190 A JP32028190 A JP 32028190A JP 32028190 A JP32028190 A JP 32028190A JP 2834316 B2 JP2834316 B2 JP 2834316B2
- Authority
- JP
- Japan
- Prior art keywords
- ester compound
- solid powder
- weight
- impact resistance
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は固型粉末化粧料に関するものであり、さらに
詳しくは本発明は肌への伸展性，付着性，化粧もち，さ
っぱり感等の実用特性が良好で、かつ、耐衝撃性に優れ
た固型粉末化粧料に関する。DETAILED DESCRIPTION OF THE INVENTION (Industrial application field) The present invention relates to a solid powder cosmetic, and more specifically, the present invention relates to practical use such as extensibility on skin, adhesion, makeup, and refreshing feeling. The present invention relates to a solid powder cosmetic having good properties and excellent impact resistance.
（従来の技術及び発明が解決しようとする課題） 固型粉末化粧料とは粉末成分を主体とし結合剤として
油性成分や界面活性剤等を添加混合して、金皿や樹脂皿
にプレス成型して得られる化粧料である。通常、パフ，
スポンジ，ブラシなどの化粧用具にて使用する。従来、
固型粉末化粧料の粉末成分としては、主として、酸化チ
タン，タルク，マイカ，セリサイト，カオリン，酸化
鉄，群青，亜鉛華，炭酸マグネシウム，スターチ，ナイ
ロンパウダー等が、また油性成分としては、流動パラフ
ィン，ワセリン，スクワラン，ミリスチン酸，ステアリ
ン酸，ラノリン，固型パラフィン，マイクロクリスタリ
ンワックス，セレシン，金属セッケン，シリコーン油等
が使用されていた。(Problems to be solved by the prior art and the invention) Solid powder cosmetics are mainly composed of powder components, and oil-based components and surfactants are added and mixed as binders, and the mixture is pressed into a metal plate or a resin plate. It is a cosmetic that can be obtained by: Usually puffs,
Use with makeup tools such as sponges and brushes. Conventionally,
The powder component of the solid powder cosmetic is mainly titanium oxide, talc, mica, sericite, kaolin, iron oxide, ultramarine, zinc white, magnesium carbonate, starch, nylon powder, and the like. Paraffin, vaseline, squalane, myristic acid, stearic acid, lanolin, solid paraffin, microcrystalline wax, ceresin, metal soap, silicone oil and the like have been used.
ところで、近年、実用特性を改善すべく種々の粉末成
分及び油性成分の開発がなされている。例えば平均粒径
が２〜20μｍの球状多孔性樹脂粉体を配合した化粧料
（特開昭57−98205号公報），球状ナイロンパウダーと
液状油分とを適度な比率にて配合した固型状粉末化粧料
（特開昭61−85309号公報），真球状二酸化チタンを配
合したメイクアップ化粧料（特開昭61−194011号公報）
等がある。By the way, in recent years, various powder components and oil components have been developed in order to improve practical characteristics. For example, a cosmetic (JP-A-57-98205) containing a spherical porous resin powder having an average particle diameter of 2 to 20 μm, a solid powder containing a spherical nylon powder and a liquid oil in an appropriate ratio. Cosmetic (JP-A-61-85309), Make-up cosmetics containing spherical titanium dioxide (JP-A-61-19401)
Etc.
しかしながら、これらの技術をもってしても、肌への
伸展性，付着性，化粧もち，さっぱり感等すべての実用
特性及び耐衝撃性において充分満足のいく固型粉末化粧
料は得られなかった。However, even with these techniques, it has not been possible to obtain a solid powder cosmetic which is sufficiently satisfactory in all practical properties such as extensibility on the skin, adhesion, make-up, freshness, and impact resistance.
本発明は、肌への伸展性，付着性，化粧もち，さっぱ
り感等の実用特性及び耐衝撃性が改善された固型粉末化
粧料を提供することを目的としている。An object of the present invention is to provide a solid powder cosmetic having improved practical properties such as extensibility on the skin, adhesion, make-up, and refreshing feeling, and impact resistance.
（課題を解決するための手段） 本発明は油性成分３〜15重量％と粉末成分85〜97重量
％を含有する固型粉末化粧料において、上記油性成分と
して、炭素数６〜８の脂肪族アルコールと12−ヒドロキ
システアリン酸のエステル化合物を１〜７重量％（総重
基準），特定の多価アルコールと炭素数８〜10の直鎖飽
和脂肪酸とのエステル化合物１〜６重量％（総量基準）
を含有し、かつ、エステル化合物双方の合計量が全油性
成分のうち、30重量％以上であることを特徴とする固型
粉末化粧料である。(Means for Solving the Problems) The present invention relates to a solid powder cosmetic containing 3 to 15% by weight of an oily component and 85 to 97% by weight of a powdery component, wherein the oily component is an aliphatic having 6 to 8 carbon atoms. 1 to 7% by weight (based on the total weight) of an ester compound of alcohol and 12-hydroxystearic acid, 1 to 6% by weight (based on the total amount) of an ester compound of a specific polyhydric alcohol and a linear saturated fatty acid having 8 to 10 carbon atoms )
, And the total amount of both ester compounds is at least 30% by weight of the total oily component.
本発明に使用される炭素数６〜８の脂肪族アルコール
とは直鎖状または側鎖状の飽和脂肪族アルコールであ
り、好ましくはヘキサノール，オクタノール，イソオク
タノールである。本発明に使用される脂肪族アルコール
と12−ヒドロキシステアリン酸とのエステル化合物と
は、オキシステアリン酸ヘキシル，オキシステアリン酸
オクチル，オキシステアリン酸イソオクチル等が好まし
いものである。The aliphatic alcohol having 6 to 8 carbon atoms used in the present invention is a linear or side chain saturated aliphatic alcohol, and is preferably hexanol, octanol, or isooctanol. As the ester compound of the aliphatic alcohol and 12-hydroxystearic acid used in the present invention, hexyl oxystearate, octyl oxystearate, isooctyl oxystearate and the like are preferable.
本発明にはこれらのエステル化合物の少なくとも一種
が使用される。脂肪族アルコールの炭素数が６未満のも
のにおいては、そのエステル化合物の粘性が低い為、そ
のエステル化合物を配合してなる固型粉末化粧料は肌へ
の付着性，耐衝撃性の点で劣る。また炭素数が８を超え
るものにおいては、そのエステル化合物の粘性が高い
為、肌への付着性，耐衝撃性は高まるものの肌への伸展
性，さっぱり感という点で劣る。In the present invention, at least one of these ester compounds is used. When the aliphatic alcohol has less than 6 carbon atoms, since the viscosity of the ester compound is low, the solid powder cosmetic composition containing the ester compound is inferior in adhesion to the skin and impact resistance. . When the number of carbon atoms exceeds 8, the viscosity of the ester compound is high, so that the adhesion to the skin and the impact resistance are enhanced, but the extensibility on the skin and the refreshing feeling are inferior.
本発明に使用される前記エステル化合物の配合量は、
化粧料の総量を基準として１〜７重量％（以下、wt％と
略記する）であり。1wt％未満の場合は肌への付着性，
耐衝撃性の点で劣り、また７％を超える場合には、肌へ
の伸展性，さっぱり感の点で劣る。The amount of the ester compound used in the present invention is,
1 to 7% by weight (hereinafter abbreviated as wt%) based on the total amount of the cosmetic. If less than 1 wt%, adhesion to skin,
If it is inferior in impact resistance, and if it exceeds 7%, it is inferior in extensibility to the skin and refreshing feeling.
本発明に使用される特定の多価アルコールと飽和脂肪
酸とのエステル化合物の構成成分である多価アルコール
とはプロピレングリコール及びグリセリンである。また
一方の構成成分である飽和脂肪酸とは炭素数８〜10の直
鎖状の脂肪酸であり、例えばカプリル酸，カプリン酸で
ある。エステル化合物としては、ジカプリン酸プロピレ
ングリコールやトリカプリル酸グリセリン等が好ましい
例として挙げられる。脂肪酸の炭素数が８未満のものに
おいては、そのエステル化合物の粘性が低い為、そのエ
ステル化合物を配合してなる固型粉末化粧料は肌への付
着性，耐衝撃性の点で劣る。また炭素数が10を超えるも
のにおいては、そのエステル化合物の粘性が高い為、肌
への付着性，耐衝撃性は高まるものの肌への伸展性，さ
っぱり感の点で劣る。The polyhydric alcohol which is a component of the ester compound of the specific polyhydric alcohol and the saturated fatty acid used in the present invention is propylene glycol and glycerin. The saturated fatty acid as one of the constituents is a linear fatty acid having 8 to 10 carbon atoms, such as caprylic acid and capric acid. Preferred examples of the ester compound include propylene glycol dicaprate and glycerin tricaprylate. When the fatty acid has less than 8 carbon atoms, the solidified cosmetic powder containing the ester compound is inferior in the adhesion to the skin and the impact resistance because the viscosity of the ester compound is low. When the number of carbon atoms exceeds 10, the viscosity of the ester compound is high, so that the adhesion to the skin and the impact resistance are enhanced, but the extensibility on the skin and the refreshing feeling are inferior.
本発明に使用される前記エステル化合物の配合量は１
〜6wt％であり、それ以外の配合量においては肌への伸
展性，付着性，化粧もち及び耐衝撃性等すべてに満足で
きるものは得られない。The amount of the ester compound used in the present invention is 1
If it is not more than 6 wt%, it will not be possible to obtain a composition that satisfies all of the extensibility on the skin, the adhesion, the makeup, and the impact resistance.
また、前記脂肪族アルコールと12−ヒドロキシステア
リン酸のエステル化合物及び多価アルコールと飽和脂肪
酸とのエステル化合物双方の配合量の合計量は、全油性
成分のうち、30wt％以上である。これよりも少ない場
合、本発明の効果、特に中でも耐衝撃性，肌への付着性
の点で好ましいものが得られない。The total amount of both the ester compound of the aliphatic alcohol and 12-hydroxystearic acid and the ester compound of the polyhydric alcohol and the saturated fatty acid is 30% by weight or more of all the oil components. If the amount is less than this, no favorable effects can be obtained from the viewpoints of the effects of the present invention, especially impact resistance and adhesion to skin.
本発明の固型粉末化粧料における油性成分としては、
上記脂肪族アルコールと12−ヒドロキシステアリン酸の
エステル化合物及び多価アルコールと飽和脂肪酸とのエ
ステル化合物を必須として、他に通常用いられる油性成
分、例えば流動パラフィン，スクワラン，ワセリン，固
型パラフィン，イソプロピルミリステート，ミリスチン
酸，ステアリン酸等を組み合わせて、油性成分として合
計３〜15wt％含有せしめる。油性成分の配合量が3wt％
より少ない場合には肌への付着性，化粧もち，しっとり
感等の実用特性及び耐衝撃性という点で満足できるもの
が得られず、また、15wt％より多い場合には肌への伸展
性，さっぱり感という点で満足できるものが得られな
い。As the oily component in the solid powder cosmetic of the present invention,
The above-mentioned ester compound of an aliphatic alcohol and 12-hydroxystearic acid and an ester compound of a polyhydric alcohol and a saturated fatty acid are essential, and other commonly used oily components such as liquid paraffin, squalane, petrolatum, solid paraffin and isopropylmill By combining state, myristic acid, stearic acid, etc., a total of 3 to 15% by weight is contained as an oily component. 3wt% of oily ingredients
If the amount is less, satisfactory properties such as adhesion to the skin, make-up, moist feeling, etc. and impact resistance cannot be obtained. I can't get anything that is refreshing.
本発明の固型粉末化粧料における粉末成分としては、
酸化チタン，タルク，マイカ，セリサイト，カオリン，
酸化鉄，群青，亜鉛華，ステアリン酸亜鉛，雲母チタ
ン，ベンガラ，黄酸化鉄，黒酸化鉄，炭酸マグネシウ
ム，スターチ，ナイロンパウダー等を用いることがで
き、これらの一種以上を85〜97wt％含有せしめる。As the powder component in the solid powder cosmetic of the present invention,
Titanium oxide, talc, mica, sericite, kaolin,
Iron oxide, ultramarine, zinc white, zinc stearate, titanium mica, red iron oxide, yellow iron oxide, black iron oxide, magnesium carbonate, starch, nylon powder, etc. can be used. .
本発明の固型粉末化粧料には、更に、界面活性剤，着
色剤，防腐剤，酸化防止剤，紫外線吸収剤，香料等も本
発明の目的を達成する範囲内で適宜配合することができ
る。The solid powder cosmetic of the present invention may further contain a surfactant, a colorant, a preservative, an antioxidant, an ultraviolet absorber, a fragrance, and the like as long as the object of the present invention is achieved. .
本発明の固型粉末化粧料は例えばフェースパウダー，
ファンデーション，アイシャドウ，チークカラー，ボデ
ィーパウダー，パヒュームパウダー，ベビーパウダー等
に適用される。The solid powder cosmetic of the present invention is, for example, face powder,
Applied to foundation, eyeshadow, cheek color, body powder, perfume powder, baby powder, etc.
（実施例） 以下、実施例によって本発明を更に詳細に説明する。(Examples) Hereinafter, the present invention will be described in more detail with reference to examples.
尚、実用特性の評価及び耐衝撃性の評価については後
述のとおりである。The evaluation of practical characteristics and the evaluation of impact resistance are as described below.
実用特性評価 20名の女性パネラーに試料を塗布し、肌への伸展性，
付着性，化粧もち，さっぱり感について評価した。Evaluation of practical characteristics The sample was applied to 20 female panelists,
Adhesion, makeup, and refreshing feeling were evaluated.
評 価 記号 17名以上が良いと回答 ◎ 12名〜16名 〃 ○ ９名〜11名 〃 △ ５名〜８名 〃 × ４名以下 〃 ×× 耐衝撃性評価 直径7.0mmφ，深さ7.0mmのアルミ製金属皿に試料をプ
レス成型し、サンプルとした。厚さ15.0mmのベニア板上
に高さ30cmからサンプルを水平状態にて落下し、破損す
るまでの落下回数を耐衝撃性とした。Evaluation symbol 17 or more respondents are good ◎ 12 to 16 〃 ○ 9 to 11 〃 △ 5 to 8 × 4 or less 〃 ×× Impact resistance evaluation Diameter 7.0mmφ, depth 7.0mm The sample was press-molded on an aluminum metal dish of No. 1 to obtain a sample. The sample was dropped horizontally from a height of 30 cm on a 15.0 mm thick veneer plate, and the number of drops until breakage was taken as impact resistance.
試験結果 実施例１〜７は炭素数６〜８の脂肪族アルコールと12
−ヒドロキシステアリン酸のエステル化合物及び多価ア
ルコールと飽和脂肪酸のエステル化合物を所定量配合し
たものであり、実用特性，耐衝撃性ともに優れたもので
あった。 Test results Examples 1 to 7 were aliphatic alcohols having 6 to 8 carbon atoms and 12 alcohols.
A mixture of a predetermined amount of an ester compound of -hydroxystearic acid and an ester compound of a polyhydric alcohol and a saturated fatty acid, which was excellent in both practical characteristics and impact resistance.
比較例1,4,7は従来技術によるものであるが、さっぱ
り感，耐衝撃性の点で劣った。Comparative Examples 1, 4, and 7 are based on the prior art, but were inferior in freshness and impact resistance.
比較例2,5は多価アルコールと飽和脂肪酸のエステル
化合物を欠いたものであるが、伸展性，さっぱり感の点
で劣った。Comparative Examples 2 and 5 lacked the ester compound of a polyhydric alcohol and a saturated fatty acid, but were inferior in extensibility and freshness.
比較例3,6は脂肪族アルコールと12−ヒドロキシステ
アリン酸のエステル化合物を欠いたものであるが、耐衝
撃性の点で劣った。Comparative Examples 3 and 6 lacked an ester compound of an aliphatic alcohol and 12-hydroxystearic acid, but were inferior in impact resistance.
（発明の効果） 以上記載のごとく、本発明は肌への伸展性，付着性，
化粧もち，さっぱり感等の実用特性が良好でかつ耐衝撃
性に優れた有用なる固型粉末化粧料を提供することは明
らかである。(Effects of the Invention) As described above, the present invention is applicable to skin extensibility, adhesion,
It is apparent that there is provided a useful solid powder cosmetic which has good practical properties such as make-up and refreshing feeling and excellent impact resistance.
Claims (1)
量％を含有する固型粉末化粧料において、上記油性成分
として、炭素数６〜８の脂肪族アルコールと12−ヒドロ
キシステアリン酸のエステル化合物を１〜７重量％（総
量基準），特定の多価アルコールと炭素数８〜10の直鎖
飽和脂肪酸とのエステル化合物１〜６重量％（総量基
準）を含有し、かつエステル化合物双方の合計量が全油
性成分のうち30重量％以上であることを特徴とする固型
粉末化粧料。1. A solid powder cosmetic containing 3 to 15% by weight of an oily component and 85 to 97% by weight of a powdery component, wherein the oily component is an aliphatic alcohol having 6 to 8 carbon atoms and 12-hydroxystearic acid. 1 to 7% by weight (based on the total amount), 1 to 6% by weight (based on the total amount) of an ester compound of a specific polyhydric alcohol and a linear saturated fatty acid having 8 to 10 carbon atoms, and an ester compound A solid powder cosmetic, wherein the total amount of both is at least 30% by weight of the total oily component.