JP3190749B2 - Manufacturing method of laminate - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a laminate in which a foam layer is formed between a core material and a skin layer, such as an interior panel of an automobile (for example, an instrument panel). The present invention relates to a material that can be manufactured with a small number of man-hours and has a high material yield.

[0002]

2. Description of the Related Art Conventionally, as a method of manufacturing a laminate of this type, there is a method shown in FIG. In FIG. 7, in this manufacturing method, as shown in FIG. 7 (a), a surface material 52 composed of a skin layer and a foam layer is supplied to a vacuum forming machine 51 as a sheet and heated and softened. Then, a vacuum is applied between the surface layer material 52 and the mold 53, and the surface layer material 52 is brought into close contact with the mold 53 to be formed into a desired shape. When the molding is completed, the surface material 52 is removed from the mold 53 and trimmed to separate unnecessary portions. And
As shown in FIG. 7B, the surface layer material 52 is mounted on an upper mold 56 of an injection molding machine 55. Then, as shown in FIG. 7 (c), the upper mold 56 with the surface material 52 mounted thereon is lowered toward the lower mold 57, and the cavity 58 is formed between the foam layer of the surface material 52 and the lower mold 57. To form A core material 59 is formed by supplying a core material of a thermoplastic resin to the cavity 58 from an injection unit (not shown).
This is a method for producing a laminate in which a foam layer is formed between a core material and a skin layer.

[0003]

The method of manufacturing a laminate described in the prior art is divided into two stages, namely, molding of a surface material 52 by a vacuum molding machine 51 and molding of a core material 59 by an injection molding machine 55. Therefore, the vacuum-formed surface layer material 52 is
1 from the mold 53, and the upper mold 56 of the injection molding machine 55.
However, it takes a lot of man-hours to remove and attach. In addition, since the surface material 52 is formed from a sheet, a large amount of material is lost. Particularly, a material having a complicated mounting shape such as an instrument panel of an automobile having a mounting portion such as an instrument panel causes a large amount of material loss. However, there is a problem that the yield is poor.

The present invention has been made in view of the above-mentioned problems of the prior art. It is an object of the present invention to provide a laminate which can be manufactured with a small number of man-hours and has a good material yield. It is intended to provide a manufacturing method.

[0005]

To solve the above object, according to the Invention The method for producing a laminate of the invention of claim 1, production of the product layer body foam layer is formed between the core material and the skin layer A method of forming a core material in a pair of molds, and maintaining the core material in one of the molds, while maintaining the balance in the equilibrium device including replacement or partial movement of the other mold. The step of forming a cavity between the core material and the mold by the maintained relative movement between the molds , and the step of injecting and filling a foam material in which foaming is suppressed by injection pressure into the cavity in which the degree of balance between the molds is maintained. Process and
Forming a foamed layer between the core layer and the cooled and solidified skin layer on the surface of the mold by relative movement between the molds including partial movement. Further, according to the second aspect of the present invention,
In the method of manufacturing a laminate, a foam layer is formed between a core material and a skin layer.
A method of manufacturing a formed laminate, comprising:
The process of forming the material and leaving this core material in one mold
The relative position between the molds including exchange or partial movement of the other mold
Forming cavities between the core and the mold by moving
And foam material that foaming was suppressed by injection pressure in this cavity
Injecting and filling the material, and the balancing device including partial movement
The relative movement between the dies maintaining the equilibrium degree
A foam layer between the cooled and solidified skin layer and the core material
And a manufacturing step. Claim 3
The method for producing a laminate of the invention according to claim 1 is the method according to claim 1 or 2.
And a relative movement between the dies including the partial movement with the balance of the pair of dies maintained by the balancing device. Further, the production of the laminate of the invention of claim 4
The manufacturing method according to claim 1 or 2, wherein the pair of molds is used.
Is relatively movable by the first cylinder,
Fine relative movement is possible by the second cylinder.
Form a foam layer between the cooled and solidified skin layer and the core material
The relative movement between the molds in the above step is performed by the second cylinder.
Done by Further, a method of manufacturing the laminate according to the invention of claim 5 is provided.
The method uses a laminate in which a foam layer is formed between the core material and the skin layer.
Manufacturing method, wherein the pair of dies is
And can move relative to each other.
Is freely fine relative movement, forming the core material in the mold of the one pair
And leaving the core material in one mold while
The relative movement between the dies including the exchange of
Forming a cavity between the core material and the mold;
Injects foamed material with suppressed foaming by injection pressure into the cavity
Filling and actuating the second cylinder
The relative movement between the dies including the partial movement
Forming a foam layer between the solidified skin layer and the core material
By operating the first cylinder, the mold is
Removing the open laminate.
You.

[0006]

According to the construction of the first , second and third aspects, the core material and the other mold are filled with a foaming material, foamed and cooled while the core material is left in the mold in which the core material is formed. A cavity whose volume to be solidified changes is formed, and a foam layer and a skin layer are integrally laminated and formed on the core material. Since the relative movement between the dies is performed in a state where the balance is maintained by the balance device, the core material, the foam layer, and the skin layer each have a uniform thickness. Further, according to the configuration of claims 4 and 5, the pressure at a predetermined pressure is
Foaming can be controlled.

[0007]

Embodiments of the present invention will be described below with reference to the drawings. FIG. 1 is a view showing a molding machine for carrying out the method of manufacturing a laminate of the present invention, FIG. 2 is a sectional view taken along line AA of FIG.
FIG. 5 to FIG. 5 are views showing a method of manufacturing a laminate according to the present invention.
First, a molding machine will be described, and then a manufacturing method will be described.

In FIG. 1 and FIG. 2, this molding machine has a frame composed of a bed 1, a crown 2, and a stand frame 3, and a first lower mold 5 and a second lower mold 5 are provided on the bed 1. A bolster 7 on which two lower dies of the dies 6 are placed is arranged.

The bolster 7 can be moved in parallel by a driving device (not shown). The first position shown by a solid line where the first lower die 5 is the center position of the molding machine and the second lower die 6 is the center position of the molding machine. And the second position shown by the two-dot chain line. Elevating cylinder 1 on crown 2
1 and an adjusting cylinder 12 are fixedly mounted, and piston rods 11a and 12
The slide 14 is fixed to the end of the “a”. And
An upper die 15 is attached to the slide 14, and the upper die 15 can be raised and lowered toward the lower dies 5 and 6 by operating the elevating cylinder 11. By operating the adjusting cylinder 12, the upper mold 15
Is slightly movable up and down toward the lower molds 5 and 6. The lifting cylinder 11 and the adjusting cylinder 12 are provided with pressure sensors 61 and 62 for detecting respective pressures. The pressure sensors 61 and 62 are connected to a control device 63.

At the four corners of the bed 1, equilibrium cylinders 18 are provided.
The slide 14 is supported at the upper end of a. Each of the four balancing cylinders 18 has a position sensor 64 for detecting the stroke amount of the piston rod 18a.
And a pressure sensor 65 for detecting the pressure acting on the balancing cylinder 18 are provided.
Is connected to the control device 63. Further, each of the four balancing cylinders 18 includes a high-speed valve 67 and a servo valve 68 that operate in response to a command from the control device 63.
By opening and closing the high-speed valve 67 at high speed, the stroke amount of the piston rod 18a can be adjusted in a short time. The control device 63 issues an operation command to the high-speed valve 67 based on the detection value of the position sensor 64, The upper and lower dies 5
(6) It is possible to ensure the degree of equilibrium of 14. The servo valve 68 is capable of adjusting the pressure acting on the balancing cylinder 18, and the control device 63
Sends an operation command to the servo valve 68 based on the detection values of the pressure sensors 61, 62, and 65 so that the actual pressure applied to the molding between the upper and lower dies 5 (6) and 14 can be set to a predetermined value. Has become. A first injection unit 20 and a second injection unit 21 for supplying a molding material to the first lower mold 5 and the second lower mold 6 are provided on the side of the molding machine.

Next, a method of manufacturing a laminate using the molding machine having the above-described structure will be described with reference to FIGS. As shown in FIG. 3A, the bolster 7 is moved to the second position, the piston rod 11a of the elevating cylinder 11 is extended, and the upper die 15 is lowered toward the second lower die 6, and The second cavity 25 is formed by the mold 15 and the second lower mold 6.
To form At this time, the position sensor 64 provided in each balancing cylinder 18 detects the stroke amount of the piston rod 18a and sends the detected value to the control device 63. The control device 63 operates the high-speed valve 67 based on the deviation between each detected value and the target value, and expands and contracts the piston rod 18a to secure the degree of balance between the upper and lower dies 6, 14. For this reason, the second cavity 25 has a uniform thickness. And FIG.
As shown in (b), a core material of a thermoplastic resin is supplied from the second injection unit 21 to the second cavity 25, and a core material 26 is formed. At this time, since the balance between the upper and lower molds 6 and 14 is ensured by the control device 63, the uniformity of the thickness of the second cavity 25 is not impaired by the injection pressure or the like, and the core 26 has a uniform thickness. Become.

When the molding is completed, the piston rod 11a of the elevating cylinder 11 is shortened while the molded core material 26 is left in the upper mold 15 as shown in FIG. 15 is raised, and the bolster 7 is moved to the first position. Then, as shown in FIG. 4 (b), the upper die 15 with the core 26 mounted thereon is extended toward the first lower die 5 by extending the piston rod 11a of the elevating cylinder 11, and 26 and the first lower mold 5 form a first cavity 28. At this time, the control device 63 operates the high-speed valve 67 based on the deviation between the detection value of each position sensor 64 and the target value, and expands and contracts the piston rod 18a to secure the degree of balance between the upper and lower dies 6, 14. The first cavity 28 has a uniform thickness.

Then, as shown in FIG. 5A, the foaming material 30 is injected and filled into the first cavity 28 at a predetermined injection pressure. The foaming material 30 is obtained by adding a foaming agent to a thermoplastic resin and melt-kneading it. The foaming material 30 is supplied from the first injection unit 20 to the first cavity 28 in a state where foaming is suppressed under the injection pressure, and the first cavity 28 is formed. In a state where the inside 28 is filled with the foaming material 30 and the injection pressure is spread, it is kept in a substantially unfoamed state. At this time, since the balance between the upper and lower dies 6 and 14 is ensured by the control device 63, the uniformity of the thickness of the first cavity 28 is not impaired by the injection pressure or the like.

Further, as shown in FIG. 5 (b), the piston rod 12a of the adjusting cylinder 12 is shortened from this state to raise the upper mold 15 by a predetermined stroke t.
When the volume of the first cavity 28 is increased, the foam material 3
The pressure of 0 is reduced to be equal to or lower than the foaming critical pressure, and foaming occurs inside the foaming material 30 to form the foamed layer 32.
In addition, the foam material 30 in the portion in contact with the first lower mold 5 is cooled and solidified in an unfoamed state, and the hard skin layer 3 without foaming is formed.
3 is formed. At this time, the position sensor 64 detects the stroke amount of the piston rod 18a of the balancing cylinder 18, and the pressure sensor 61 and the pressure sensor 62
1 and the pressure of the adjusting cylinder 12 are detected, and the pressure sensor 6
5 detects the pressure acting on the balancing cylinder 18, and the detected values are sent to the control device 63. Then, the control device 63 operates the high-speed valve 67 based on the value detected by the position sensor 64, and raises the upper mold 15 while securing the degree of balance with the lower mold 6. Therefore, the foam layer 32 has a uniform thickness. Further, the control device 63 includes a pressure sensor 61
Detection value by P _1, the detection value P ₂ by the pressure sensor 62,
The detection values P ₃ , P ₄ ,
Based on P ₅ and P ₆ , the actual pressure P applied to the foam material 30
= P ₁ + P ₂ − (P ₃ + P ₄ + P ₅ + P ₆ )
The servo valve 68 is operated to control the actual pressure P to a predetermined value. As a result, the foaming material 30 foams under a predetermined actual pressure, so that the foamed layer 32 has a desired foaming quality. (If the actual pressure is too low, the foaming rate becomes too large, and if the actual pressure is too high, the foaming becomes Will be broken).

When the foam layer 32 and the skin layer 33 are integrally laminated on the core material 26 in this manner,
The piston rod 11a of the elevating cylinder 11 is shortened, the upper die 15 is raised, and a laminate including the core material 26, the foam layer 32, and the skin layer 33 is taken out, and one cycle of molding is completed. The skin layer 33 can have a desired thickness by controlling the temperature conditions.

As described above, the upper mold 1 in which the core material 26 is formed
While the core material 26 remains in the core 5, a first cavity 28 having a variable volume is formed between the core material 26 and the first lower mold 5, the volume of the foam material 30 being filled, foamed, and cooled and solidified. Since the foam layer 32 and the skin layer 33 are integrally laminated and formed on the material 26, a laminate including the core material 26, the foam layer 32, and the skin layer 33 is continuously manufactured by one molding machine. It is possible to greatly reduce man-hours. Further, since the core material 26 is formed from a molding material, there is almost no material loss, and the yield is greatly improved. For this reason,
This method is optimal as a method for manufacturing a laminate having a large and complicated shape, such as an interior panel of an automobile or the like, particularly, an instrument panel of an automobile. Then, since the relative movement between the dies is performed while the balance is maintained by the balance cylinder 18, each layer of the laminate has a uniform thickness. Furthermore, when the same material is used for the core material, the skin layer, and the foamed layer, the adhesion between the core material and the foamed layer is improved, and the material can be recycled.

In the above-described embodiment, the case where the lower mold is used separately for the molding of the core material and the molding of the foam layer and the skin layer has been described. However, as shown in FIG. Mold 41
Are three positions of a molding position of the core material (corresponding to FIG. 3A), a filling position of the foam material (corresponding to FIG. 4B), and a foaming position of the foam material (corresponding to FIG. 5B). If it can be taken, the molding of the core material and the molding of the foam layer / skin layer can be performed with one lower mold 42. Further, FIG.
As shown in (b), even if the upper mold 43 can take three positions by the partial movement of the upper mold 43, the molding of the core material and the surface layer can be performed by one lower mold 44. The material and the foam layer can be formed.

In each of the above embodiments, the case where the upper mold moves up and down toward the lower mold has been described. However, the case where the lower mold moves up and down toward the upper mold, and one of the molds The present invention can be similarly applied to a tool that moves laterally toward the other mold, and has the same effects as those of the above embodiments.

Further, the method for molding the core material is not limited to injection molding, but may be compression molding, injection compression molding, or the like. The core material is not limited to a single layer. It is also possible to form a multilayer.

[0020]

The present invention is configured as described above, and has the following effects. Claims 1, 2, 3
According to the invention, while the core material is left in the mold in which the core material is formed, a cavity having a variable volume is formed between the core material and the other mold, in which the foam material is filled, foamed, and cooled and solidified, Since the foam layer and the skin layer are integrally laminated and molded on the core material, it becomes possible to continuously produce a laminate including the core material, the foam layer and the skin layer with one molding machine, The man-hour can be greatly reduced. Further, since the core material is molded from the molding material, there is almost no material loss, and the yield is greatly improved. For this reason, automobile interior panels,
In particular, it is optimal as a method for manufacturing a laminate having a large and complicated shape such as an instrument panel. And since relative movement between dies is performed in a state where the balance is maintained by the balance device, each layer of the laminate has a uniform thickness. Furthermore, if the core material, the skin layer and the foam layer use the same material, the adhesion between the core material and the foam layer is improved, and
Recycling is also possible. According to the invention of claims 4 and 5
And foaming at a predetermined pressure can be controlled.
Quality.

[Brief description of the drawings]

FIG. 1 is a view showing a molding machine for carrying out a method for producing a laminate of the present invention.

FIG. 2 is a sectional view taken along line AA of FIG.

FIG. 3 is a diagram showing a method for manufacturing a laminate according to the present invention.

FIG. 4 is a view showing a method for manufacturing a laminate according to the present invention.

FIG. 5 is a view showing a method for producing a laminate of the present invention.

FIG. 6 is a view showing a method of manufacturing another laminate.

FIG. 7 is a view showing a conventional method of manufacturing a laminate.

[Explanation of symbols]

 5, 6 Lower mold 11 Lifting cylinder 12 Adjusting cylinder 14 Slide 15 Upper mold 18 Equilibrium cylinder (equilibrium device) 25, 28 Cavity 26 Core material 30 Foam material 32 Foam layer 33 Skin layer

────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-6-234133 (JP, A) JP-A-1-264823 (JP, A) (58) Fields investigated (Int. Cl. ⁷ , DB name) B29C 45/00-45/84

Claims (5)

(57) [Claims] 1. A method for manufacturing a laminate in which a foam layer is formed between a core material and a skin layer, comprising the steps of: forming a core material in a pair of molds; Leave it in the mold,
By means of a balancing device involving exchange or partial movement of the other mold
The relative movement between the mold balance is maintained, a step of forming a cavity between the core and the mold, balance between mold Wei
A step of injecting and filling a foaming material is suppressed foaming in injection pressure in the lifting been cavity, by relative movement between the molds containing moiety movement, foamed between the cooling solidified skin layer and the core material of the mold surface Forming a layer. 2. A foam layer is formed between a core material and a skin layer.
A method of manufacturing a laminated body, comprising forming a core material in a pair of molds.
With the shaping process and leaving this core material in one mold,
For relative movement between molds including exchange or partial movement of the other mold
Forming a cavity between the core material and the mold;
Injects foamed material with suppressed foaming by injection pressure into the cavity
The filling and unloading process and the balancing device including partial movement
Cooling of mold surface by relative movement between molds while maintaining balance
Forming a foam layer between the solidified skin layer and the core material
And a method for producing a laminate. 3. A according to claim 1 or 2 laminate according and performing mold between relative movement including the portion moves in a state where balance degree of the pair of molds by said balancing device is maintained Production method. 4. The pair of dies are joined by a first cylinder.
It is freely movable and has fine phase by the second cylinder.
It is free to move, and the solidified skin layer and core on the mold surface are cooled and solidified.
Mold phase in the process of forming a foam layer between the mold and the material
Claim 1 or 2 wherein said pair movement is performed by said second cylinder.
Is a method for producing a laminate according to 2. 5. A foam layer is formed between a core material and a skin layer.
A method of manufacturing a laminated body, wherein the pair of molds includes a first cylinder.
The second cylinder
Is slightly movable relative to the center of the pair of molds.
The process of forming the material and leaving this core material in one mold
The relative position between the molds including exchange or partial movement of the other mold
Forming cavities between the core and the mold by moving
And foam material that foaming was suppressed by injection pressure in this cavity
Injecting and charging the material, and operating the second cylinder
Relative movement between dies including partial movement
A foam layer is formed between the core layer and the skin layer, which has been cooled and solidified on the surface.
And operating the first cylinder.
Opening the mold and removing the laminate.
How to make the body.