JP3239627B2 - Manufacturing method of inorganic plate - Google Patents
Manufacturing method of inorganic plateInfo
- Publication number
- JP3239627B2 JP3239627B2 JP20471994A JP20471994A JP3239627B2 JP 3239627 B2 JP3239627 B2 JP 3239627B2 JP 20471994 A JP20471994 A JP 20471994A JP 20471994 A JP20471994 A JP 20471994A JP 3239627 B2 JP3239627 B2 JP 3239627B2
- Authority
- JP
- Japan
- Prior art keywords
- inorganic plate
- cement
- lightweight aggregate
- green sheet
- warpage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は無機質板の製造方法に関
し、詳しくは外装材などに好適なセメント系の無機質板
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing an inorganic plate, and more particularly to a cement-based inorganic plate suitable for an exterior material.
【０００２】[0002]
【従来の技術】従来より、外装材などに用いられるセメ
ント系の無機質板は、抄造によって連続的に形成したグ
リーンシートを用いる抄造法、または押出成形もしくは
注形成形などによって製造されている。抄造法によれ
ば、生産性の点で有利であるが、グリーンシートが固い
ため表面に深い凹凸模様を形成することが困難であっ
た。そこで、抄造して形成したグリーンシート上に、５
０％以下の低含水率の粉体材料を散布して二層としたの
ち模様付け成形し、表面に意匠性の高い深い凹凸模様を
形成している。2. Description of the Related Art Conventionally, a cement-based inorganic plate used for an exterior material or the like has been manufactured by a papermaking method using a green sheet formed continuously by papermaking, or by extrusion molding or casting. The papermaking method is advantageous in terms of productivity, but it is difficult to form a deep uneven pattern on the surface because the green sheet is hard. Therefore, on a green sheet formed by papermaking, 5
A powder material having a low water content of 0% or less is sprinkled to form two layers, and thereafter, a pattern is formed, and a deep irregular pattern having a high design property is formed on the surface.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、上記の
従来例にあっては、グリーンシート上の粉体材料に配合
する軽量骨材がガラス質であり、養生中にセメントと反
応して寸法が変化するのである。たとえば、軽量骨材と
してパーライトなどを用いた場合、粉体材料によって形
成した上層が膨張し、寸法変化の少ないグリーンシート
とこの上層とで寸法が異なることになるので、反りが発
生しやすくなる。However, in the above-mentioned conventional example, the lightweight aggregate mixed with the powder material on the green sheet is vitreous, and changes its size by reacting with the cement during curing. You do it. For example, when pearlite or the like is used as the lightweight aggregate, the upper layer formed of the powder material expands, and the dimensions of the green sheet having little dimensional change are different from those of the upper layer, so that warpage is likely to occur.
【０００４】本発明は、以上のような問題点を解決する
ためになされたものであり、その目的は、反りの発生し
にくい抄造法によるセメント系の無機質板の製造方法の
提供にある。[0004] The present invention has been made to solve the above problems, and an object of the present invention is to provide a method for producing a cement-based inorganic plate by a papermaking method which is less likely to warp.
【０００５】[0005]
【課題を解決するための手段】上記課題を解決する請求
項１記載の発明は、スラリーを抄造してグリーンシート
を形成し、このグリーンシート上に低含水率の粉体材料
を散布し、プレス後、養生硬化させるセメント系の無機
質板の製造方法において、保護材料としてアクリルシリ
コン系塗料によって軽量骨材を被覆し、この軽量骨材を
粉体材料に添加することを特徴として構成している。According to the first aspect of the present invention, a green sheet is formed by forming a slurry, and a low moisture content powder material is sprayed on the green sheet. After that, in a method of manufacturing a cement-based inorganic plate that is cured and hardened , acrylic silicone is used as a protective material.
It is characterized in that the lightweight aggregate is coated with a concrete paint and the lightweight aggregate is added to the powder material.
【０００６】請求項１記載の発明において、保護材料を
溶液またはエマルジョンの状態にして軽量骨材に付着さ
せ、乾燥して被覆することを特徴として構成している。The invention according to claim 1 is characterized in that the protective material is in the form of a solution or an emulsion, adheres to the lightweight aggregate, and is dried and coated.
【０００７】請求項１記載の発明において、保護材料と
してアクリル系塗料を用いたことを特徴として構成して
いる。The invention according to claim 1 is characterized in that an acrylic paint is used as a protective material.
【０００８】[0008]
【作用】請求項１記載の発明では、保護材料によって軽
量骨材が被覆されて粉体材料に添加されるので、この軽
量骨材とセメントとが直接接触していない。したがっ
て、グリーンシート上の粉体材料によって形成される上
層は、養生時に軽量骨材とセメントとが反応して寸法が
変化することが少なくなり、反りが発生しにくくなって
いる。According to the first aspect of the present invention, since the lightweight aggregate is coated with the protective material and added to the powder material, the lightweight aggregate does not directly contact the cement. Therefore, the upper layer formed of the powder material on the green sheet is less likely to change its dimensions due to the reaction between the lightweight aggregate and the cement during curing, and is less likely to be warped.
【０００９】請求項１記載の発明では、保護材料を溶液
またはエマルジョンの状態として軽量骨材に付着させる
ので、軽量骨材の表面に均一に薄く付着させて被覆する
ことができる。According to the first aspect of the present invention, since the protective material is attached to the lightweight aggregate in the form of a solution or an emulsion, the protective material can be uniformly and thinly attached to the surface of the lightweight aggregate for coating.
【００１０】請求項１記載の発明では、アクリルシリコ
ン系塗料が撥水性を有し、無機質板を吸水しにくくして
いる。According to the first aspect of the present invention, the acrylic silicone paint has water repellency, and makes it difficult for the inorganic plate to absorb water.
【００１１】[0011]
【実施例】本発明の一実施例を以下に添付図を参照して
説明する。DESCRIPTION OF THE PREFERRED EMBODIMENTS One embodiment of the present invention will be described below with reference to the accompanying drawings.
【００１２】図１はこの実施例の製造方法によって得ら
れる無機質板の構成を模式的に示した断面図である。FIG. 1 is a sectional view schematically showing the structure of an inorganic plate obtained by the manufacturing method of this embodiment.
【００１３】この無機質板の製造方法は、外装材などに
用いられるセメント系の無機質板の製造方法であって、
最初にスラリーを抄造してグリーンシート１を形成す
る。スラリーとしてはセメントを主成分とし、ケイ石
粉、フライアッシュまたはパルプなどを添加して成るも
のを用いている。This method for producing an inorganic plate is a method for producing a cement-based inorganic plate used for an exterior material or the like,
First, a green sheet 1 is formed by forming a slurry. As the slurry, a slurry containing cement as a main component and adding silica powder, fly ash or pulp is used.
【００１４】そして、このグリーンシート１上に含水率
５０％以下の粉体材料２を散布して、二層の構成として
いる。粉体材料２としては、スラリーと同様にセメント
を主成分とし、ケイ石粉、パルプ粉、軽量骨材３などを
添加して成るものを用いている。この上層はプレス成形
による模様付けを容易にするためのものであり、グリー
ンシート１のみでは固すぎて３mm以上の深い凹凸模様を
形成することが困難なため、このような二層の構成とし
ているのである。A powder material 2 having a water content of 50% or less is sprayed on the green sheet 1 to form a two-layer structure. As the powder material 2, a material containing cement as a main component similarly to the slurry and added with silica stone powder, pulp powder, lightweight aggregate 3 and the like is used. This upper layer is for facilitating the patterning by press molding. Since the green sheet 1 alone is too hard to form a deep uneven pattern of 3 mm or more, such an upper layer has such a two-layer structure. It is.
【００１５】そして、この実施例においては、軽量骨材
３を保護材料４によって被覆して添加するようにしてい
る。保護材料４としてはアクリル樹脂、アクリルシリコ
ン樹脂またはフッ素樹脂などを用いることができる。こ
れらの保護材料４を溶液またはエマルジョンの状態と
し、希釈して溶液濃度またはエマルジョン濃度を調整
し、軽量骨材３の粒子に雰霧して付着させるか、また
は、浸漬して付着させ、乾燥して軽量骨材３に被覆させ
るのである。特に、アクリルシリコン系塗料を用い、コ
ンベアー上に広げた軽量骨材３に雰霧するようにすれ
ば、付着量を調整して被覆することを容易に行うことが
できる。また、アクリルシリコン系塗料は撥水性を有
し、無機質板を吸水しにくくしている。In this embodiment, the lightweight aggregate 3 is covered with the protective material 4 and added. An acrylic resin, an acrylic silicon resin, a fluorine resin, or the like can be used as the protective material 4. These protective materials 4 are made into a solution or an emulsion state, diluted to adjust the solution concentration or the emulsion concentration, and adhered to the particles of the lightweight aggregate 3 by atomization or by immersion, and dried. Thus, the lightweight aggregate 3 is coated. In particular, if an acrylic silicone paint is used and the lightweight aggregate 3 spread on the conveyor is muffled, the coating can be easily performed by adjusting the amount of adhesion. In addition, the acrylic silicone paint has water repellency, and makes it difficult for the inorganic plate to absorb water.
【００１６】また、軽量骨材３としては、たとえばパー
ライト微細物などを用いることができ、かさ比重が0.3k
g/リットル以下のものが好ましく、５〜15％程度添加するこ
とによって、粉体材料２の比重を0.9 〜1.3 程度として
いる。Further, as the lightweight aggregate 3, for example, fine pearlite can be used, and the bulk specific gravity is 0.3 k.
The specific gravity of the powder material 2 is set to about 0.9 to 1.3 by adding about 5 to 15%.
【００１７】このような保護材料４による軽量骨材３の
被覆は、軽量骨材３とセメントとを接触しにくくしてい
るので、養生時に軽量骨材３とセメントとが反応して寸
法が変化することが少なくなり、グリーンシート１上の
粉体材料２によって形成される上層の寸法変化が抑えら
れ、反りを発生しにくくしているのである。つまり、こ
の保護材料４を用いないと、軽量骨材３としてパーライ
トなどのガラス質を用いると、養生中にセメントと反応
して膨張するのである。このため、粉体材料２によって
形成した上層と寸法変化の小さいグリーンシート１とで
寸法が異なることになり、反りが発生しやすくなる。The coating of the lightweight aggregate 3 with the protective material 4 makes it difficult for the lightweight aggregate 3 and the cement to come into contact with each other. Therefore, the dimensional change of the upper layer formed by the powder material 2 on the green sheet 1 is suppressed, and warpage is hardly generated. That is, if the protective material 4 is not used, if a vitreous material such as pearlite is used as the lightweight aggregate 3, it reacts with the cement during curing and expands. Therefore, the dimensions of the upper layer formed of the powder material 2 are different from those of the green sheet 1 having a small dimensional change, and warpage is likely to occur.
【００１８】こののち、以上のようにして形成した二層
の材料をプレス成形して表面に凹凸模様を形成し、蒸気
養生およびオートクレーブ養生を行って硬化させ、無機
質板を得ているのである。After that, the two-layered material formed as described above is press-molded to form an uneven pattern on the surface, and cured by steam curing and autoclave curing to obtain an inorganic plate.
【００１９】以下に、さらに具体的な実施例を挙げ、こ
の具体的な実施例の無機質板の性能評価を説明する。Hereinafter, performance evaluation of the inorganic plate of this specific example will be described with reference to more specific examples.
【００２０】（実施例１）表１に示すように、セメント
材料として日本セメント（株）製のポルトランドセメン
トを５０部、宇部興産（株）製のケイ石粉を２５部、九
州電力（株）製のフライアッシュを１８部およびパルプ
として兵庫パルプ（株）製の品番Ｎ−ＵＫＰのものを７
部配合してセメントスラリーを調整し、長綱抄造機にて
成型後１２mm厚みとなるグリーンシート１を抄造した。(Example 1) As shown in Table 1, as a cement material, 50 parts of Portland cement manufactured by Nippon Cement Co., Ltd., 25 parts of silica stone powder manufactured by Ube Industries, Ltd., manufactured by Kyushu Electric Power Co., Ltd. 7 pieces of N-UKP manufactured by Hyogo Pulp Co., Ltd.
The mixture was mixed to prepare a cement slurry, and a green sheet 1 having a thickness of 12 mm after being molded by a rope paper making machine was formed.
【００２１】このグリーンシート１上に、表２の実施例
１の欄に示すように、セメント材料として日本セメント
（株）製のポルトランドセメントを５０部、宇部興産
（株）製のケイ石粉を３７部、兵庫パルプ（株）製のパ
ルプ粉３部および軽量骨材３であるパーライトとして宇
部興産（株）製の１型Ｆｂを１０部配合した粉体材料２
を散布して二層構造を形成した。As shown in the column of Example 1 in Table 2, 50 parts of Portland cement manufactured by Nippon Cement Co., Ltd. and 37 parts of silica stone powder manufactured by Ube Industries, Ltd. were used on the green sheet 1 as a cement material. 3 parts of pulp powder manufactured by Hyogo Pulp Co., Ltd. and 10 parts of 1 type Fb manufactured by Ube Industries, Ltd. as a pearlite which is a lightweight aggregate 3
Was sprayed to form a two-layer structure.
【００２２】パーライトの保護材料４による被覆処理
は、保護材料４としてアクリルシリコン塗料（イサム塗
料（株）製ネオシリカ＃１０００）を専用シンナーで１
０倍に希釈し、コンベアー上に広げたパーライトにエア
レススプレーで雰霧し、乾燥させながら攪拌することに
より行った。粉体材料２の散布は成型後の厚みが３mmに
なる厚さとした。The coating treatment of the pearlite with the protective material 4 is performed by using an acrylic silicon paint (Neosilica # 1000 manufactured by Isamu Paint Co., Ltd.) as the protective material 4 with a special thinner.
It was carried out by agitating the pearlite which had been diluted to 0-fold and spread on a conveyor with airless spray, and dried while stirring. The powder material 2 was sprayed so that the thickness after molding became 3 mm.
【００２３】以上のようにして二層構造の材料を形成
し、この材料を圧力５０kg/cm2で５秒間模様付け成型
し、７０℃で２０時間蒸気養生し、こののち１７２℃で
４時間オートクレーブ養生して硬化させ、無機質板を得
た。A material having a two-layer structure is formed as described above, and the material is patterned and molded at a pressure of 50 kg / cm 2 for 5 seconds, steam-cured at 70 ° C. for 20 hours, and then autoclaved at 172 ° C. for 4 hours. After curing and curing, an inorganic plate was obtained.
【００２４】この無機質板をスパンを３００mmとして反
り測定すると、反り量は１．２mmであった。When the warpage of this inorganic plate was measured with a span of 300 mm, the warpage was 1.2 mm.
【００２５】（実施例２）実施例１において抄造したグ
リーンシート１上に、表２の実施例２の欄に示すよう
に、実施例１の配合に代えて、セメント材料として日本
セメント（株）製のポルトランドセメントを５５部と
し、軽量骨材３であるパーライトとして宇部興産（株）
製の１型Ｆｂを５部として配合した粉体材料２を散布し
て二層構造を形成した。(Example 2) As shown in the column of Example 2 in Table 2, Nippon Cement Co., Ltd. was used as a cement material on the green sheet 1 produced in Example 1, as shown in the column of Example 2 in Table 2. Portland cement made of 55 parts, Ube Industries, Ltd. as pearlite, lightweight aggregate 3
A powder material 2 containing 5 parts of Type 1 Fb manufactured by Co. was sprayed to form a two-layer structure.
【００２６】また、パーライトの保護材料４による被覆
処理は、保護材料４として油化バーデェシェ社製の商標
アクロナール、品番ＹＪ１００を水で２０倍に希釈し、
この希釈液にパーライトを浸漬して取り出し、乾燥させ
ながら攪拌することにより行った。粉体材料２の散布は
成型後の厚みが３mmになる厚さとした。Further, the coating treatment of the pearlite with the protective material 4 is performed by diluting, as the protective material 4, Acronal (trade name, manufactured by Yuka Badeche), part number YJ100 20 times with water.
Perlite was immersed in the diluted solution, taken out, and stirred while drying. The powder material 2 was sprayed so that the thickness after molding became 3 mm.
【００２７】このあと、実施例１と同様の工程を行い、
無機質板を得た。この無機質板の反り量は０．６mmであ
った。Thereafter, the same steps as in Example 1 are performed.
An inorganic plate was obtained. The amount of warpage of this inorganic plate was 0.6 mm.
【００２８】（実施例３）粉体２の配合を、セメント材
料として日本セメント（株）製のポルトランドセメント
を５０部とし、軽量骨材３であるパーライトとして宇部
興産（株）製の１型Ｆｂを１０部とした他は、実施例２
と全く同様にして行った。(Example 3) Powder 2 was mixed with 50 parts of Portland cement manufactured by Nippon Cement Co., Ltd. as a cement material, and 1 type Fb manufactured by Ube Industries, Ltd. as pearlite, a lightweight aggregate 3. Example 2 except that 10 parts were used.
Was carried out in exactly the same way.
【００２９】この無機質板の反り量は１．１mmであっ
た。 （実施例４）粉体２の配合を、セメント材料として日本
セメント（株）製のポルトランドセメントを４５部と
し、軽量骨材３であるパーライトとして宇部興産（株）
製の１型Ｆｂを１５部とした他は、実施例２と全く同様
にして行った。The amount of warpage of the inorganic plate was 1.1 mm. (Example 4) Powder 2 was mixed with Portland cement manufactured by Nippon Cement Co., Ltd. as 45 parts as cement material, and Ube Industries, Ltd. as pearlite as lightweight aggregate 3.
Except that 15 parts of Type 1 Fb was used, and the procedure was the same as in Example 2.
【００３０】この無機質板の反り量は１．３mmであっ
た。 （実施例５）粉体２の配合を、セメント材料として日本
セメント（株）製のポルトランドセメントを５５部と
し、軽量骨材３であるパーライトとして宇部興産（株）
製の１型Ｆｂを５部とした他は、実施例１と全く同様に
して行った。The amount of warpage of the inorganic plate was 1.3 mm. (Example 5) The powder 2 was mixed with 55 parts of Portland cement manufactured by Nippon Cement Co., Ltd. as a cement material, and Ube Industries, Ltd. as a pearlite as a lightweight aggregate 3.
Except that 5 parts of Type 1 Fb was used, the procedure was the same as in Example 1.
【００３１】この無機質板の反り量は０．５mmであっ
た。 （比較例１）実施例１において、パーライトの保護材料
４による被覆処理を行わず作業して無機質板を得た。The amount of warpage of the inorganic plate was 0.5 mm. (Comparative Example 1) An inorganic plate was obtained in the same manner as in Example 1, except that the pearlite protective material 4 was not coated.
【００３２】この無機質板の反り量は４．５mmであっ
た。 （比較例２）実施例４において、パーライトの保護材料
４による被覆処理を行わず作業して無機質板を得た。The amount of warpage of the inorganic plate was 4.5 mm. (Comparative Example 2) An inorganic plate was obtained by working in the same manner as in Example 4 without performing the coating treatment with the pearlite protective material 4.
【００３３】この無機質板の反り量は７．４mmであっ
た。The amount of warpage of the inorganic plate was 7.4 mm.
【００３４】[0034]
【表１】 [Table 1]
【００３５】[0035]
【表２】 [Table 2]
【００３６】また、図２は反り測定方法を示す説明図で
あって、（Ａ）は反り測定治具を無機質板に当てている
状態を示す断面図であり、（Ｂ）は反り測定位置を示す
平面図である。（Ａ）に示すように、この反り測定治具
は、水平棒５の両端に、測定する試料の両端に接触する
接触片６を立設し、水平棒５の中心に設けたマイクロメ
ーター７によって、反り量を計測するものである。すな
わち、 反り量＝（ｂ＋ｃ）／２−ａ として求めている。ここに、ｂおよびｃは両側の接触片
６の長さであり、ａはマイクロメーター７によって測定
される水平棒５と無機質板中央部との距離である。ま
た、両側の接触片６間の距離である測定スパンは３００
mmとしている。FIGS. 2A and 2B are explanatory views showing a warpage measuring method. FIG. 2A is a cross-sectional view showing a state in which a warpage measuring jig is applied to an inorganic plate, and FIG. FIG. As shown in (A), the warp measuring jig has a contact piece 6 erected at both ends of a horizontal bar 5 for contacting both ends of a sample to be measured, and a micrometer 7 provided at the center of the horizontal bar 5. , The amount of warpage is measured. That is, the warpage amount is obtained as (b + c) / 2-a. Here, b and c are the lengths of the contact pieces 6 on both sides, and a is the distance between the horizontal bar 5 measured by the micrometer 7 and the center of the inorganic plate. The measurement span, which is the distance between the contact pieces 6 on both sides, is 300.
mm.
【００３７】また、（Ｂ）に示すように、無機質板の二
つの対角線方向に測定し、この値を平均して反り量とし
ている。Further, as shown in (B), the measurement is performed in two diagonal directions of the inorganic plate, and the average is defined as the amount of warpage.
【００３８】以上に説明したように、いずれの実施例に
おいても、パーライトの保護材料４による被覆処理を行
わない比較例よりも、反り量は極めて小さくなってお
り、反りの発生しにくい無機質板が抄造法によって得ら
れている。As described above, in any of the examples, the amount of warpage is extremely smaller than that of the comparative example in which the coating treatment with the pearlite protective material 4 is not performed. Obtained by the papermaking method.
【００３９】[0039]
【発明の効果】請求項１記載の発明は、保護材料によっ
て軽量骨材が被覆されて保護されるので、グリーンシー
ト上の粉体材料によって形成される上層は、養生時に軽
量骨材とセメントとが反応して寸法が変化することが少
なくなり、反りが発生しにくくなっている。また、この
発明の方法は、抄造して形成したグリーンシート上に粉
体材料を用いて上層を形成するので生産性が高く、その
上、上層には深い凹凸模様を形成することができるもの
である。According to the first aspect of the present invention, since the lightweight aggregate is covered and protected by the protective material, the upper layer formed by the powder material on the green sheet is formed by curing the lightweight aggregate and cement during curing. Change in the dimensions due to the reaction, and warpage is less likely to occur. Further, the method of the present invention forms an upper layer using a powder material on a green sheet formed by papermaking, so that productivity is high, and further, a deep uneven pattern can be formed in the upper layer. is there.
【００４０】したがって、意匠性の高い凹凸模様を有す
る無機質板を、反りが発生しないようにして、能率よく
生産することのできる製造方法になっている。Therefore, the production method is capable of efficiently producing an inorganic plate having an irregular pattern with high designability without warping.
【００４１】請求項１記載の発明は、保護材料を軽量骨
材の表面に均一に薄く付着させて被覆することができ、
反りの発生をうまく抑えることができる。According to the first aspect of the present invention, the protective material can be uniformly and thinly adhered to the surface of the lightweight aggregate to cover it.
Warpage can be effectively suppressed.
【００４２】請求項１記載の発明は、アクリルシリコン
系塗料が撥水性を有しているので、無機質板を吸水しに
くくし、外壁などのように水に晒される用途に好適にな
ものになっている。According to the first aspect of the present invention, since the acrylic silicone paint has water repellency, the inorganic plate is hardly absorbed by water, and is suitable for use such as an outer wall exposed to water. ing.
【図１】本発明の一実施例における無機質板の構成を模
式的に示した断面図である。FIG. 1 is a cross-sectional view schematically illustrating a configuration of an inorganic plate according to an embodiment of the present invention.
【図２】同上実施例における反り測定方法を示す説明図
であって、（Ａ）は反り測定治具を無機質板に当ててい
る状態を示す断面図であり、（Ｂ）は反り測定位置を示
す平面図である。FIGS. 2A and 2B are explanatory views showing a warpage measuring method in the embodiment, wherein FIG. 2A is a cross-sectional view showing a state in which a warpage measuring jig is applied to an inorganic plate, and FIG. FIG.
１ グリーンシート ２ 粉体材料 ３ 軽量骨材 ４ 保護材料 ５ 水平棒 ６ 接触片 ７ マイクロメーター DESCRIPTION OF SYMBOLS 1 Green sheet 2 Powder material 3 Lightweight aggregate 4 Protective material 5 Horizontal bar 6 Contact piece 7 Micrometer
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ Ｃ０４Ｂ 18:08 Ｃ０４Ｂ 18:08 Ｂ 16:02 16:02 Ｚ 14:18 14:18 24:26） 24:26） Ｅ (56)参考文献 特開 昭61−171313（ＪＰ，Ａ) 特開 平６−135751（ＪＰ，Ａ) 特開 昭61−21942（ＪＰ，Ａ) 特開 昭59−131405（ＪＰ，Ａ) 特公 昭41−15197（ＪＰ，Ｂ１) (58)調査した分野(Int.Cl.7，ＤＢ名) B28B 3/02 B28B 1/52 B28B 11/06 ────────────────────────────────────────────────── ─── Continued on the front page (51) Int.Cl. 7 Identification code FI C04B 18:08 C04B 18:08 B 16:02 16:02 Z 14:18 14:18 24:26) 24:26) E ( 56) References JP-A-61-171313 (JP, A) JP-A-6-1355751 (JP, A) JP-A-61-21942 (JP, A) JP-A-59-131405 (JP, A) 41-41197 (JP, B1) (58) Fields investigated (Int. Cl. 7 , DB name) B28B 3/02 B28B 1/52 B28B 11/06
Claims (1)
成し、このグリーンシート上に低含水率の粉体材料を散
布し、プレス後、養生硬化させるセメント系の無機質板
の製造方法において、保護材料としてアクリルシリコン
系塗料によって軽量骨材を被覆し、この軽量骨材を粉体
材料に添加することを特徴とする無機質板の製造方法。1. A method for producing a cement-based inorganic plate, comprising forming a green sheet by forming a slurry, spraying a powder material having a low water content on the green sheet, pressing and curing after curing. As acrylic silicon
A method for producing an inorganic plate, comprising coating a lightweight aggregate with a system paint and adding the lightweight aggregate to a powder material.