JP3299081B2 - 凍結防止塗料 - Google Patents
凍結防止塗料Info
- Publication number
- JP3299081B2 JP3299081B2 JP19779895A JP19779895A JP3299081B2 JP 3299081 B2 JP3299081 B2 JP 3299081B2 JP 19779895 A JP19779895 A JP 19779895A JP 19779895 A JP19779895 A JP 19779895A JP 3299081 B2 JP3299081 B2 JP 3299081B2
- Authority
- JP
- Japan
- Prior art keywords
- acetate
- water
- soluble
- parts
- calcium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】
【発明の属する技術分野】この発明は、塗料、特に道路
標識、看板、車両等の表面に塗布して塗膜を形成し、雪
及び氷の付着を防止すると共に、一定期間後に塗膜を容
易に除去できる凍結防止塗料に関するものである。
標識、看板、車両等の表面に塗布して塗膜を形成し、雪
及び氷の付着を防止すると共に、一定期間後に塗膜を容
易に除去できる凍結防止塗料に関するものである。
【０００２】
【従来の技術】表面に雪及び氷が付着した道路標識、看
板、車両等に表示された標識又は目印を目視できないこ
とは寒冷地において通常見られる現象である。標識は、
通常鉄板又は木製板により形成されるため、標識の表面
に凝結して付着した雪又は氷は、その表面に強固に固着
するため、容易に除去することができない。約３メート
ル以上の高い位置に取り付けられる標識に雪又は氷が付
着しても除去することは困難である。また、雪又は氷に
覆われたため、標識を十分に目視できないと、交通事故
の発生原因となり又は目標地を明確に表示できない欠点
がある。例えば、特開昭６０−２０８３７１号公報に示
されるように、撥水性成分と撥油性成分とを含むフッ素
樹脂系コーティング剤は公知である。このコーティング
剤は、撥水性フッ素樹脂系成分と、撥油性フッ素樹脂系
成分と、エポキシ樹脂系成分と、反応性樹脂媒質とを含
む。
板、車両等に表示された標識又は目印を目視できないこ
とは寒冷地において通常見られる現象である。標識は、
通常鉄板又は木製板により形成されるため、標識の表面
に凝結して付着した雪又は氷は、その表面に強固に固着
するため、容易に除去することができない。約３メート
ル以上の高い位置に取り付けられる標識に雪又は氷が付
着しても除去することは困難である。また、雪又は氷に
覆われたため、標識を十分に目視できないと、交通事故
の発生原因となり又は目標地を明確に表示できない欠点
がある。例えば、特開昭６０−２０８３７１号公報に示
されるように、撥水性成分と撥油性成分とを含むフッ素
樹脂系コーティング剤は公知である。このコーティング
剤は、撥水性フッ素樹脂系成分と、撥油性フッ素樹脂系
成分と、エポキシ樹脂系成分と、反応性樹脂媒質とを含
む。
【０００３】
【発明が解決しようとする課題】しかしながら、フッ素
系樹脂を配合する従来のコーティング剤は、加工性及び
耐薬品性に優れているが、使用後に、フッ素樹脂を塗布
した表面から除去することが困難である。そこで、この
発明は、対象物の表面の凍結を防止すると共に、対象物
の表面から容易に除去できる凍結防止塗料を提供するこ
とを目的とする。
系樹脂を配合する従来のコーティング剤は、加工性及び
耐薬品性に優れているが、使用後に、フッ素樹脂を塗布
した表面から除去することが困難である。そこで、この
発明は、対象物の表面の凍結を防止すると共に、対象物
の表面から容易に除去できる凍結防止塗料を提供するこ
とを目的とする。
【０００４】
【課題を解決するための手段】この発明による凍結防止
塗料は、重量基準で、２５０〜３００部の水及び５〜１
０部の多価アルコールからなる不凍液と、水溶性の酢酸
塩１０〜５０部と、水溶性の防錆剤２.０〜５.０部と、
水溶性のバインダ６〜６５部とから成る。不凍液として
使用する多価アルコールは、エチルグリコール、ブチル
グリコール、エチレングリコール、プロピレングリコー
ル、ブチレングリコール、ポリエチレングリコール、ポ
リプロピレングリコール、エチルジグリコール、ブチル
ジグリコール、グリセリン、プロピオニルカルビノール
から選択される１種又は２種以上である。防錆剤は、水
酸化カルシウム、水酸化マグネシウム、リン酸水素カル
シウム、トリポリリン酸ナトリウム、炭酸カルシウム、
酢酸カルシウム、リン酸亜硝酸カリウムから選択される
１種又は２種以上である。水溶性のバインダは、ビスコ
ース、メチルセルロース、エチルセルロース、ヒドロキ
シエチルセルロース、カルボキシメチルセルロール、可
溶性デンプン、カルボキシメチルデンプン、ジアルデヒ
ドデンプン、ポリビニルアルコール、ポリアクリル酸ナ
トリウム、ポリエチレンオキシド、水溶性アルキド樹
脂、水溶性メラミン樹脂、水溶性尿素樹脂、水溶性フェ
ノール樹脂、水溶性アクリル樹脂、水溶性エポキシ樹
脂、水溶性ポリブタジエン樹脂から選択される１種又は
２種以上の樹脂である。
塗料は、重量基準で、２５０〜３００部の水及び５〜１
０部の多価アルコールからなる不凍液と、水溶性の酢酸
塩１０〜５０部と、水溶性の防錆剤２.０〜５.０部と、
水溶性のバインダ６〜６５部とから成る。不凍液として
使用する多価アルコールは、エチルグリコール、ブチル
グリコール、エチレングリコール、プロピレングリコー
ル、ブチレングリコール、ポリエチレングリコール、ポ
リプロピレングリコール、エチルジグリコール、ブチル
ジグリコール、グリセリン、プロピオニルカルビノール
から選択される１種又は２種以上である。防錆剤は、水
酸化カルシウム、水酸化マグネシウム、リン酸水素カル
シウム、トリポリリン酸ナトリウム、炭酸カルシウム、
酢酸カルシウム、リン酸亜硝酸カリウムから選択される
１種又は２種以上である。水溶性のバインダは、ビスコ
ース、メチルセルロース、エチルセルロース、ヒドロキ
シエチルセルロース、カルボキシメチルセルロール、可
溶性デンプン、カルボキシメチルデンプン、ジアルデヒ
ドデンプン、ポリビニルアルコール、ポリアクリル酸ナ
トリウム、ポリエチレンオキシド、水溶性アルキド樹
脂、水溶性メラミン樹脂、水溶性尿素樹脂、水溶性フェ
ノール樹脂、水溶性アクリル樹脂、水溶性エポキシ樹
脂、水溶性ポリブタジエン樹脂から選択される１種又は
２種以上の樹脂である。
【０００５】この発明による凍結防止塗料は、対象物の
表面に塗布して硬化させることにより対象物の表面の氷
結又は凍結を防止する塗膜を形成し、容易に対象物の表
面を被覆することができる。対象物の表面に形成された
塗膜は、例えば３カ月間、対象物の表面の氷結又は凍結
を防止する作用があり、雪又は氷の付着を防止する。一
定期間経過後に、塗膜を容易に除去するか塗膜の自然脱
落をまって塗膜を除去することができる。
表面に塗布して硬化させることにより対象物の表面の氷
結又は凍結を防止する塗膜を形成し、容易に対象物の表
面を被覆することができる。対象物の表面に形成された
塗膜は、例えば３カ月間、対象物の表面の氷結又は凍結
を防止する作用があり、雪又は氷の付着を防止する。一
定期間経過後に、塗膜を容易に除去するか塗膜の自然脱
落をまって塗膜を除去することができる。
【０００６】本発明の実施の形態では、不凍液はさら
に、メタノール、エタノール、プロピルアルコール、イ
ソプロピルアルコールから選択される１種又は２種以上
の乾燥促進用のアルコールを、重量基準で６０〜８０部
を含んでもよい。氷点降下を示す酢酸塩は、酢酸ナトリ
ウム、酢酸カリウム、酢酸カルシウム、酢酸ケイ素、酢
酸コバルト、酢酸カルシウム・マグネシウム、酢酸錫、
酢酸鉄、酢酸銅、酢酸銅カリウム、酢酸銅カルシウム、
酢酸ニッケル、酢酸マンガン、酢酸リチウム、酢酸マグ
ネシウムから選択される１種又は２種以上である。
に、メタノール、エタノール、プロピルアルコール、イ
ソプロピルアルコールから選択される１種又は２種以上
の乾燥促進用のアルコールを、重量基準で６０〜８０部
を含んでもよい。氷点降下を示す酢酸塩は、酢酸ナトリ
ウム、酢酸カリウム、酢酸カルシウム、酢酸ケイ素、酢
酸コバルト、酢酸カルシウム・マグネシウム、酢酸錫、
酢酸鉄、酢酸銅、酢酸銅カリウム、酢酸銅カルシウム、
酢酸ニッケル、酢酸マンガン、酢酸リチウム、酢酸マグ
ネシウムから選択される１種又は２種以上である。
【０００７】また、防錆剤２.０〜５.０部、酢酸塩１０
〜５０部を水３０〜５０部に配合して撹拌し、均一に溶
解させ添加剤を予め作る。防錆剤が２.０部未満では顕
著な防錆効果が認められず、５.０部を越えて配合して
も作用効果は向上しない。酢酸塩が１０部未満では氷点
降下が十分でなく、５０部を越えると、塗膜が不均一に
なる。添加剤を前記混合物に加えて、撹拌混合し、３０
℃以下の温度で自然冷却し、凍結防止塗料をつくる。標
識板に塗布した凍結防止塗料を硬化させるには、自然乾
燥でも加熱乾燥でもよい。
〜５０部を水３０〜５０部に配合して撹拌し、均一に溶
解させ添加剤を予め作る。防錆剤が２.０部未満では顕
著な防錆効果が認められず、５.０部を越えて配合して
も作用効果は向上しない。酢酸塩が１０部未満では氷点
降下が十分でなく、５０部を越えると、塗膜が不均一に
なる。添加剤を前記混合物に加えて、撹拌混合し、３０
℃以下の温度で自然冷却し、凍結防止塗料をつくる。標
識板に塗布した凍結防止塗料を硬化させるには、自然乾
燥でも加熱乾燥でもよい。
【０００８】この発明による凍結防止塗料は、対象物の
表面に塗布して硬化させることにより容易に対象物の表
面を被覆することができる。対象物の表面に形成された
塗膜は、例えば３カ月間、対象物の表面の氷結又は凍結
を防止する作用があり、雪又は氷の付着を防止する。一
定期間経過後に、塗膜を容易に除去するか塗膜の自然脱
落をまって塗膜を除去することができる。
表面に塗布して硬化させることにより容易に対象物の表
面を被覆することができる。対象物の表面に形成された
塗膜は、例えば３カ月間、対象物の表面の氷結又は凍結
を防止する作用があり、雪又は氷の付着を防止する。一
定期間経過後に、塗膜を容易に除去するか塗膜の自然脱
落をまって塗膜を除去することができる。
【０００９】
【実施例】実施例１ 防錆剤としてリン酸２部、亜硝酸カリウム１部、酢酸塩
として酢酸カリウム１５部を水３０部に混合して撹拌
し、均一に溶解させて、添加剤を予め作成した。また、
別途、塗膜の乾燥を促進するメタノール６０部を水２７
０部に加えた。撹拌しながら、グリセリン６部を加えて
撹拌した。次に、バインダとしての水溶性メラミン樹脂
６部を加えて、撹拌しながら溶解させた。続いて、触媒
としてのシュウ酸を０.５部加えて撹拌した。シュウ酸
が完全にかつ均一に溶解した混合液にバインダとしてポ
リビニルアルコール４５部を加え、撹拌しながら７０℃
に加温し、１時間かけて均一に溶解させた。得られた混
合物に予め作成した添加剤を加え、撹拌混合し、３０℃
以下で自然冷却し、凍結防止塗料を作った。
として酢酸カリウム１５部を水３０部に混合して撹拌
し、均一に溶解させて、添加剤を予め作成した。また、
別途、塗膜の乾燥を促進するメタノール６０部を水２７
０部に加えた。撹拌しながら、グリセリン６部を加えて
撹拌した。次に、バインダとしての水溶性メラミン樹脂
６部を加えて、撹拌しながら溶解させた。続いて、触媒
としてのシュウ酸を０.５部加えて撹拌した。シュウ酸
が完全にかつ均一に溶解した混合液にバインダとしてポ
リビニルアルコール４５部を加え、撹拌しながら７０℃
に加温し、１時間かけて均一に溶解させた。得られた混
合物に予め作成した添加剤を加え、撹拌混合し、３０℃
以下で自然冷却し、凍結防止塗料を作った。
【００１０】この凍結防止塗料の凍結防止試験を行うた
め、図１に示すように、標識板１の右半分２へハケで凍
結防止塗料を塗布した後、１００℃で３０分間で乾燥さ
せた。標識板１の左半分３には凍結防止塗料を塗布しな
かった。標識板１を長野県辰野町の山道のわきに１月１
５日から２月１４日まで３０日間放置した。この山道の
平均気温は−５℃〜−１５℃であった。凍結防止塗料を
塗布した標識板１の右半分２は雪及び氷の付着を防止す
ることができたが、左半分３は雪４が付着した。左半分
３に付着した雪４は継続する降雪により増大して、実際
には標識板１の左半分３の全面を雪４で覆われることも
あった。試験終了後、標識板１の右半分２に形成した塗
膜を標識板１に残さずに容易に除去することができた。
め、図１に示すように、標識板１の右半分２へハケで凍
結防止塗料を塗布した後、１００℃で３０分間で乾燥さ
せた。標識板１の左半分３には凍結防止塗料を塗布しな
かった。標識板１を長野県辰野町の山道のわきに１月１
５日から２月１４日まで３０日間放置した。この山道の
平均気温は−５℃〜−１５℃であった。凍結防止塗料を
塗布した標識板１の右半分２は雪及び氷の付着を防止す
ることができたが、左半分３は雪４が付着した。左半分
３に付着した雪４は継続する降雪により増大して、実際
には標識板１の左半分３の全面を雪４で覆われることも
あった。試験終了後、標識板１の右半分２に形成した塗
膜を標識板１に残さずに容易に除去することができた。
【００１１】実施例２ 防錆剤として水酸化マグネシウム５部、酢酸塩として酢
酸マグネシウム５０部を水５０部に混合し、撹拌して均
一に溶解させて添加剤を予め作った。次に、塗膜の乾燥
を促進するイソプロピルアルコール８０部を水２５０部
に加えた。撹拌しながら、多価アルコールとしてポリプ
ロピレングリコール９部を加えて、撹拌した。次に、バ
インダとしてヒドロキシエチルセルロース６５部を加
え、完全にかつ均一に溶解した後、撹拌しながら９０℃
に加温し、３０分間均一に溶解させた。その後、得られ
た混合物に予め作った添加物を撹拌混合し、３０℃以下
で自然冷却させ、凍結防止塗料を作った。
酸マグネシウム５０部を水５０部に混合し、撹拌して均
一に溶解させて添加剤を予め作った。次に、塗膜の乾燥
を促進するイソプロピルアルコール８０部を水２５０部
に加えた。撹拌しながら、多価アルコールとしてポリプ
ロピレングリコール９部を加えて、撹拌した。次に、バ
インダとしてヒドロキシエチルセルロース６５部を加
え、完全にかつ均一に溶解した後、撹拌しながら９０℃
に加温し、３０分間均一に溶解させた。その後、得られ
た混合物に予め作った添加物を撹拌混合し、３０℃以下
で自然冷却させ、凍結防止塗料を作った。
【００１２】実施例１と同様の凍結防止試験を行うた
め、得られた凍結防止塗料を図２に示す標識板１の右半
分２へハケで塗布した後、自然乾燥させた。標識板１の
左半分３には塗布しなかった。標識板１を長野県辰野町
の山道のわきに２月１０日から３月１５日まで３４日間
放置した。山道の平均気温は−５℃〜−１５℃であっ
た。標識板１の右半分２に塗布した凍結防止塗料も雪と
氷の付着を防ぐことができ、３月１０日以降の試験終了
後、塗膜が標識板に残っていないことを確認した。標識
板１の左半分３にはほぼ全面にわたり氷５が付着した。
め、得られた凍結防止塗料を図２に示す標識板１の右半
分２へハケで塗布した後、自然乾燥させた。標識板１の
左半分３には塗布しなかった。標識板１を長野県辰野町
の山道のわきに２月１０日から３月１５日まで３４日間
放置した。山道の平均気温は−５℃〜−１５℃であっ
た。標識板１の右半分２に塗布した凍結防止塗料も雪と
氷の付着を防ぐことができ、３月１０日以降の試験終了
後、塗膜が標識板に残っていないことを確認した。標識
板１の左半分３にはほぼ全面にわたり氷５が付着した。
【００１３】本実施例では、水、多価アルコール、酢酸
塩、防錆剤及び水溶性バインダの各組成の成分範囲全体
にわたり試験を行ったが、前記組成範囲ではほぼ同様の
良好な凍結防止効果が得られた。
塩、防錆剤及び水溶性バインダの各組成の成分範囲全体
にわたり試験を行ったが、前記組成範囲ではほぼ同様の
良好な凍結防止効果が得られた。
【００１４】
【発明の効果】前記のように、この発明による凍結防止
塗料は一定期間対象物の表面の氷結又は凍結を防止する
ことができかつ一定期間経過後に、塗膜を容易に除去す
るか塗膜の自然脱落をまって塗膜を除去することができ
るので、交通事故を防止すると共に、対象物の本来の機
能を保護することができる効果がある。
塗料は一定期間対象物の表面の氷結又は凍結を防止する
ことができかつ一定期間経過後に、塗膜を容易に除去す
るか塗膜の自然脱落をまって塗膜を除去することができ
るので、交通事故を防止すると共に、対象物の本来の機
能を保護することができる効果がある。
【図１】 この発明による凍結防止塗料を塗布した標識
板の正面図
板の正面図
【図２】 この発明による凍結防止塗料を塗布した他の
標識板の正面図
標識板の正面図
１・・標識板、 ２・・右半分、 ３・・左半分、 ４
・・雪、 ５・・氷、
・・雪、 ５・・氷、
フロントページの続き (56)参考文献 特開 昭60−206888（ＪＰ，Ａ) 特開 昭61−57659（ＪＰ，Ａ) 特開 平６−306650（ＪＰ，Ａ) 特公 昭44−30366（ＪＰ，Ｂ１) 米国特許5308389（ＵＳ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) C09D 1/00 - 201/10 C09K 3/00 - 3/18
Claims (3)
- 【請求項１】 重量基準で、２５０〜３００部の水及び
５〜１０部の多価アルコールからなる不凍液と、水溶性
の酢酸塩１０〜５０部と、水溶性の防錆剤２.０〜５.０
部と、水溶性のバインダ６〜６５部とから成り、 多価アルコールは、エチルグリコール、ブチルグリコー
ル、エチレングリコール、プロピレングリコール、ブチ
レングリコール、ポリエチレングリコール、ポリプロピ
レングリコール、エチルジグリコール、ブチルジグリコ
ール、グリセリン、プロピオニルカルビノールから選択
される１種又は２種以上であり、 防錆剤は、水酸化カルシウム、水酸化マグネシウム、リ
ン酸水素カルシウム、トリポリリン酸ナトリウム、炭酸
カルシウム、酢酸カルシウム、リン酸亜硝酸カリウムか
ら選択される１種又は２種以上であり、 バインダは、ビスコース、メチルセルロース、エチルセ
ルロース、ヒドロキシエチルセルロース、カルボキシメ
チルセルロール、可溶性デンプン、カルボキシメチルデ
ンプン、ジアルデヒドデンプン、ポリビニルアルコー
ル、ポリアクリル酸ナトリウム、ポリエチレンオキシ
ド、水溶性アルキド樹脂、水溶性メラミン樹脂、水溶性
尿素樹脂、水溶性フェノール樹脂、水溶性アクリル樹
脂、水溶性エポキシ樹脂、水溶性ポリブタジエン樹脂か
ら選択される１種又は２種以上の樹脂であることを特徴
とする凍結防止塗料。 - 【請求項２】 さらに、メタノール、エタノール、プロ
ピルアルコール、イソプロピルアルコールから選択され
る１種又は２種以上の乾燥促進用のアルコールを、重量
基準で６０〜８０部を含む請求項１に記載の凍結防止塗
料。 - 【請求項３】 氷点降下を示す酢酸塩は、酢酸ナトリウ
ム、酢酸カリウム、酢酸カルシウム、酢酸ケイ素、酢酸
コバルト、酢酸カルシウム・マグネシウム、酢酸錫、酢
酸鉄、酢酸銅、酢酸銅カリウム、酢酸銅カルシウム、酢
酸ニッケル、酢酸マンガン、酢酸リチウム、酢酸マグネ
シウムから選択される１種又は２種以上である請求項１
に記載の凍結防止塗料。