JP3362218B2 - Coating agent to improve knot strength of absorbable monofilament suture - Google Patents
Coating agent to improve knot strength of absorbable monofilament sutureInfo
- Publication number
- JP3362218B2 JP3362218B2 JP27675198A JP27675198A JP3362218B2 JP 3362218 B2 JP3362218 B2 JP 3362218B2 JP 27675198 A JP27675198 A JP 27675198A JP 27675198 A JP27675198 A JP 27675198A JP 3362218 B2 JP3362218 B2 JP 3362218B2
- Authority
- JP
- Japan
- Prior art keywords
- caprolactone
- lactide
- suture
- copolymer
- calcium stearate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、手術用縫合糸のコ
ーティング材料、及びコーティングを有する吸収性縫合
糸に関する。FIELD OF THE INVENTION The present invention relates to coating materials for surgical sutures and absorbable sutures having a coating.
【０００２】[0002]
【従来の技術】手術用縫合糸は古くから用いられている
医療用具の一つであるが、近年では手術後の抜糸が不要
である吸収性材料を用いた吸収性縫合糸が増加してい
る。ポリグリコール酸を主成分とする縫合糸が開発され
たが、これらの糸は剛直であるために多数のフィラメン
トから成るマルチフィラメントの縫合糸として生産され
た。2. Description of the Related Art Surgical sutures for surgery have been one of the medical instruments used for a long time, but in recent years, absorbent sutures made of absorbent materials, which do not require thread removal after surgery, are increasing. . Sutures based on polyglycolic acid have been developed, but because of their rigidity, these sutures were produced as multifilament sutures consisting of multiple filaments.
【０００３】しかしながら、マルチフィラメントは製造
工程が複雑であるばかりでなく、マルチフィラメントの
表面の粗さから操作時の滑り降ろし性能が悪いことや、
縫合時に組織を傷つけることがあり、またキャピラリー
性から感染の危険があるなどの問題点があった。However, the manufacturing process of the multifilament is not only complicated, but also the sliding performance during operation is poor due to the surface roughness of the multifilament, and
There are problems that the tissue may be damaged during suturing and that there is a risk of infection due to the capillary property.
【０００４】これらの欠点を改善すべく、例えば特開平
８−２２９１１１号公報のようなマルチフィラメント縫
合糸の表面コーティング方法がいろいろと考案されてい
る。In order to improve these disadvantages, various surface coating methods for multifilament sutures have been devised, for example, as disclosed in Japanese Patent Laid-Open No. 8-229111.
【０００５】一方、モノフィラメントは製造工程が簡素
化できるのみならず、表面が平滑であることから縫合操
作時に組織を痛めることがなく、かつキャピラリー性が
ないことから感染の危険性が格段に低くなる。On the other hand, the monofilament not only simplifies the manufacturing process but also does not damage the tissue during the suturing operation due to its smooth surface and has no capillary property, so that the risk of infection is significantly reduced. .
【０００６】前述のように縫合糸として好都合なモノフ
ィラメントであるが、結び目を作ったときに接触面の面
積が大きくなることから、糸の素材によっては結び目を
作る時の糸の滑りが悪くなり、このことが操作中の糸切
れの原因ともなり、結果として結節強力を低下させるこ
とにもなる。As described above, the monofilament is convenient as a suture thread, but since the area of the contact surface becomes large when the knot is made, slippage of the thread when making the knot becomes poor depending on the material of the knot. This may cause yarn breakage during operation, resulting in a reduction in knot strength.
【０００７】この問題を解決するために、例えば糸表面
に潤滑性を付与するシリコーン油を塗布するなどの方法
が一般的に行われている。In order to solve this problem, for example, a method of applying silicone oil which imparts lubricity to the yarn surface is generally used.
【０００８】しかしながら、縫合糸の素材が生体内で分
解・吸収される場合、生体内で分解・吸収・排泄されな
い素材を塗布することは好ましくない。However, when the material of the suture thread is decomposed and absorbed in the living body, it is not preferable to apply the material which is not decomposed, absorbed and excreted in the living body.
【０００９】本発明は、糸本体との親和性が良好でかつ
相乗的に結節強力を向上させるコーティング組成物及び
このようなコーティングを有する縫合糸を提供すること
を目的とする。An object of the present invention is to provide a coating composition having good affinity with the thread body and synergistically improving knot strength, and a suture having such a coating.
【００１０】[0010]
【課題を解決するための手段】本発明は、手術用縫合糸
のコーティング方法に関する。SUMMARY OF THE INVENTION The present invention is directed to a method of coating surgical sutures.
【００１１】項１． ε-カプロラクトンのホモポリマ
ー、あるいはε-カプロラクトンとそれ以外の吸収性単
量体からなる共重合体と、ステアリン酸カルシウムを含
む縫合糸用表面コーティング材料。Item 1. A surface coating material for sutures, which contains calcium stearate and a homopolymer of ε-caprolactone, or a copolymer of ε-caprolactone and other absorptive monomers.
【００１２】項２． それ以外の吸収性単量体がラクチ
ドである項１に記載のコーティング材料。Item 2. Item 2. The coating material according to Item 1, wherein the other absorptive monomer is lactide.
【００１３】項３． ε-カプロラクトンとラクチドの
共重合体の組成比がモル比で88〜97：12〜3％であり、
ステアリン酸カルシウムの配合比率が0.01〜1.5wt％で
ある、項１に記載のコーティング材料。Item 3. The compositional ratio of the copolymer of ε-caprolactone and lactide is 88 to 97:12 to 3% by molar ratio,
Item 2. The coating material according to Item 1, wherein the compounding ratio of calcium stearate is 0.01 to 1.5 wt%.
【００１４】項４． ε-カプロラクトンとラクチドの
共重合体の組成比がモル比で70〜80：30〜20％であり、
ステアリン酸カルシウムの配合比率が0.1〜2.5wt％であ
る、項１に記載のコーティング材料。Item 4. The composition ratio of the copolymer of ε-caprolactone and lactide is 70 to 80:30 to 20% in terms of molar ratio,
Item 2. The coating material according to Item 1, wherein the compounding ratio of calcium stearate is 0.1 to 2.5 wt%.
【００１５】項５． ε-カプロラクトンとラクチドの
共重合体の組成比が、モル比で45〜55：55〜45％であ
り、ステアリン酸カルシウムの配合比率が1.0〜3.0wt％
である、項１に記載のコーティング材料。Item 5. The composition ratio of the copolymer of ε-caprolactone and lactide is 45 to 55: 55 to 45% by molar ratio, and the mixing ratio of calcium stearate is 1.0 to 3.0 wt%.
Item 2. The coating material according to Item 1, wherein
【００１６】項６． ε-カプロラクトンのホモポリマ
ーを含み、ステアリン酸カルシウムの配合比率が0.01〜
1.0wt％である、項１に記載のコーティング材料。Item 6. Includes ε-caprolactone homopolymer and calcium stearate content of 0.01-
Item 2. The coating material according to Item 1, which is 1.0 wt%.
【００１７】項７． 項１〜６のいずれかに記載のコー
ティング材料でコーティングされた吸収性縫合糸。Item 7. Item 10. An absorbable suture coated with the coating material according to any one of items 1 to 6.
【００１８】項８． 吸収性縫合糸がモノフィラメント
縫合糸である項７に記載の縫合糸。Item 8. Item 8. The suture according to Item 7, wherein the absorbable suture is a monofilament suture.
【００１９】項９． 吸収性縫合糸がε-カプロラクト
ンとラクチドの共重合体である項８に記載の縫合糸。Item 9. Item 9. The suture according to Item 8, wherein the absorbable suture is a copolymer of ε-caprolactone and lactide.
【００２０】項１０． 吸収性縫合糸のε-カプロラク
トンとラクチドの組成比が、モル比で20〜30：80〜70％
である項９に記載の縫合糸。
項１１． コーティングにより結節強力が１０〜５０％
向上してなる項７に記載の縫合糸。Item 10. The composition ratio of ε-caprolactone and lactide in the absorbable suture is 20-30: 80-70% in molar ratio.
Item 9. The suture according to Item 9, which is Item 11. 10-50% knot strength due to coating
The improved suture according to item 7.
【００２１】[0021]
【発明の実施の形態】本発明の手術用吸収性モノフィラ
メント縫合糸コーティング材料は、ε−カプロラクトン
を必須成分とし、ε−カプロラクトンのホモポリマーで
あってもよく、ε−カプロラクトンと他の吸収性単量体
との共重合体であってもよい。他の吸収性単量体として
は、ラクチド、グリコリド、トリメチレンカーボネー
ト、ジオキサノンなどが挙げられ、特にラクチドが挙げ
られる。BEST MODE FOR CARRYING OUT THE INVENTION The surgical absorbable monofilament suture coating material of the present invention contains ε-caprolactone as an essential component and may be a homopolymer of ε-caprolactone. It may be a copolymer with a monomer. Examples of other absorptive monomers include lactide, glycolide, trimethylene carbonate, dioxanone and the like, and particularly lactide.
【００２２】好ましい共重合体は、ε−カプロラクトン
とラクチドなどの乳酸を繰り返し単位とする共重合体で
ある。ε−カプロラクトンとラクチドなどの乳酸を繰り
返し単位とする共重合体は、重大な性質への悪影響を及
ぼさない範囲で他の生体内分解吸収性の繰り返し単位を
さらに含んでいてもよい。このような他の繰り返し単位
としては例えばグリコール酸、トリメチレンカーボネー
ト、ジオキサノンが例示される。A preferred copolymer is a copolymer containing ε-caprolactone and lactic acid such as lactide as a repeating unit. The copolymer containing ε-caprolactone and lactic acid such as lactide as a repeating unit may further contain other biodegradable and absorbable repeating units as long as they do not adversely affect important properties. Examples of such other repeating units include glycolic acid, trimethylene carbonate, and dioxanone.
【００２３】本発明の手術用吸収性モノフィラメント縫
合糸コーティング材料は、ε−カプロラクトン単体ある
いは、繰り返し単位として乳酸及びε−カプロラクトン
からなる共重合体のみからなることが望ましいが、コー
ティング材料としての物性に悪影響を及ぼさない範囲に
おいて他の生体内分解吸収性重合体を含んでいてもよ
い。このような重合体の例としては、ポリグリコール
酸、トリメチレンカーボネート、ポリジオキサノンなど
が挙げられる。The surgical absorbable monofilament suture coating material of the present invention is preferably composed of ε-caprolactone alone or a copolymer of lactic acid and ε-caprolactone as a repeating unit. Other biodegradable and absorbable polymers may be contained within a range that does not have an adverse effect. Examples of such polymers include polyglycolic acid, trimethylene carbonate, polydioxanone and the like.
【００２４】本発明の手術用吸収性モノフィラメント縫
合糸コーティング材料は、ε−カプロラクトン単体ある
いは、繰り返し単位として乳酸及びε−カプロラクトン
からなる共重合体のみでも、コーティング材料としての
役割を果たすことが可能であるが、操作時の操作性をよ
り向上させるためには同時に添加物として一般的に使用
されるステアリン酸カルシウムを併用するのが好まし
い。The surgical absorbable monofilament suture coating material of the present invention can function as a coating material even with ε-caprolactone alone or a copolymer of lactic acid and ε-caprolactone as a repeating unit. However, in order to further improve the operability at the time of operation, it is preferable to use together calcium stearate which is generally used as an additive.
【００２５】使用する乳酸およびε−カプロラクトン共
重合体の組成比率は、ε−カプロラクトンと乳酸の二量
体であるラクチドのモル％で表すとき、ε−カプロラク
トン：ラクチド＝88〜97：12〜３モル％、あるいは70〜
80：30〜20モル％、もしくは45〜55：55〜45モル％であ
るのが好ましい。The composition ratio of lactic acid and ε-caprolactone copolymer used is expressed as mol% of lactide, which is a dimer of ε-caprolactone and lactic acid, and ε-caprolactone: lactide = 88-97: 12-3. Mol%, or 70 ~
It is preferably 80:30 to 20 mol%, or 45 to 55:55 to 45 mol%.
【００２６】乳酸としてはL-乳酸、D-乳酸、D,L-乳酸
（ラセミ体）のいずれを用いてもよいが、好ましくはL-
乳酸が用いられる。As lactic acid, any of L-lactic acid, D-lactic acid and D, L-lactic acid (racemic form) may be used, but L-lactic acid is preferred.
Lactic acid is used.
【００２７】本発明のコーティング材料でコーティング
される吸収性モノフィラメント縫合糸は、例えばε−カ
プロラクトンとグリコール酸の共重合体、ポリジオキサ
ノン、グリコール酸／トリメチレンカーボネート／乳酸
の共重合体、グリコール酸／トリメチレンカーボネート
／ジオキサノンの共重合体など、どのような素材でもか
まわないが、乳酸およびε−カプロラクトン共重合体か
らできている方がコーティング材料との相溶性がよい。
より好ましくはラクチド：ε−カプロラクトン＝70〜8
0：30〜20モル％である。また、適用可能な縫合糸のサ
イズは、ＵＳＰ２〜１０−０号まで可能である。The absorbable monofilament sutures coated with the coating material of the present invention include, for example, copolymers of ε-caprolactone and glycolic acid, polydioxanone, copolymers of glycolic acid / trimethylene carbonate / lactic acid, glycolic acid / tricarboxylic acid. Any material such as a methylene carbonate / dioxanone copolymer may be used, but the one made of lactic acid and ε-caprolactone copolymer has better compatibility with the coating material.
More preferably lactide: ε-caprolactone = 70-8
It is 0:30 to 20 mol%. The size of the applicable suture thread can be up to USP2-10-0.
【００２８】吸収性モノフィラメント縫合糸をε−カプ
ロラクトン単体あるいは、繰り返し単位として乳酸及び
ε−カプロラクトンからなる共重合体のみでコーティン
グすることは可能であるが、手術時の操作性の向上や、
ＵＳＰ規格による結節強力測定の破断強力向上のために
は、ステアリン酸カルシウムなどの高級脂肪酸塩を同時
に使用することが必要である。このときに使用するステ
アリン酸カルシウムの量は、使用するポリマーによって
最適値が存在する。It is possible to coat the absorbable monofilament suture only with ε-caprolactone alone or with a copolymer consisting of lactic acid and ε-caprolactone as a repeating unit, but the operability during surgery is improved and
In order to improve the breaking strength in the knot strength measurement according to the USP standard, it is necessary to simultaneously use a higher fatty acid salt such as calcium stearate. The amount of calcium stearate used at this time has an optimum value depending on the polymer used.
【００２９】添加するステアリン酸カルシウムの最適値
は、コーティング材料中の生体内分解吸収性のポリマー
がε−カプロラクトンのホモポリマーの場合0.01〜1.0w
t％、ε−カプロラクトン：ラクチド＝88〜97：12〜３
モル％の場合0.01〜1.5wt％、、70〜80：30〜20モル％
の共重合体の場合には0.1〜2.5wt％、45〜55：55〜45モ
ル％の共重合体の場合には1.0〜3.0wt%であるが、これ
はコーティング材として使用するポリマー濃度との関連
で変わることもある。The optimum value of calcium stearate to be added is 0.01 to 1.0 w when the biodegradable and absorbable polymer in the coating material is a homopolymer of ε-caprolactone.
t%, ε-caprolactone: lactide = 88 to 97:12 to 3
In the case of mol%, 0.01 to 1.5 wt%, 70 to 80:30 to 20 mol%
In the case of the copolymer of 0.1 to 2.5 wt%, and in the case of the copolymer of 45 to 55:55 to 45 mol%, it is 1.0 to 3.0 wt%. It may change in relation to.
【００３０】コーティング方法として具体的な方法とし
ては、まずポリマーを溶媒に完全に溶解させる。このと
きに用いる溶媒としては一般的な有機溶媒が使用できる
が、好ましくは縫合糸本体を強力に溶解しないアセトン
を用いる。これにより、糸にコーティング材が付着しや
すくなり、コーティングのはがれなどが少なくなる。As a specific coating method, first, the polymer is completely dissolved in a solvent. As the solvent used at this time, a general organic solvent can be used, but preferably acetone that does not strongly dissolve the suture body is used. As a result, the coating material easily adheres to the yarn, and peeling of the coating is reduced.
【００３１】ステアリン酸カルシウムなどの高級脂肪酸
塩を同時に使用する場合、前述のポリマー溶液に所定量
の高級脂肪酸塩を添加する。このとき、多くの溶媒に高
級脂肪酸塩は溶解しにくく、溶液中に分散した状態で使
用する。均質にコーティングするためには、コーティン
グ作業中常にコーティング溶液を撹拌するのが好まし
い。コーティングによる結節強力向上率は、好ましくは
１０〜５０％、より好ましくは２０％以上である。When a higher fatty acid salt such as calcium stearate is used at the same time, a predetermined amount of the higher fatty acid salt is added to the polymer solution. At this time, the higher fatty acid salt is difficult to dissolve in many solvents and is used in a state of being dispersed in the solution. For homogeneous coating, it is preferred to stir the coating solution at all times during the coating operation. The rate of improvement in knot strength by coating is preferably 10 to 50%, more preferably 20% or more.
【００３２】[0032]
【実施例】以下に本発明を実施例に基づいて説明する
が、本発明はこれら実施例に限定されない。EXAMPLES The present invention will be described below based on examples, but the present invention is not limited to these examples.
【００３３】実施例１
L-乳酸とε−カプロラクトンの共重合体（ラクチド：ε
−カプロラクトン＝25：75モル％）を使用して、ステア
リン酸カルシウム(CaSt.)を併用してコーティングを行
った。Example 1 Copolymer of L-lactic acid and ε-caprolactone (lactide: ε
-Caprolactone = 25:75 mol%) was used in combination with calcium stearate (CaSt.).
【００３４】（１） 溶媒
アセトン
（２） 共重合体（ポリマー）濃度
２W/V％
（３） ステアリン酸カルシウム濃度
0.2および２W/V％
この３成分を混合し、常に撹拌した状態の中を約10m/mi
n.の速度で糸を通過させることによりコーティングを行
った。使用した糸はラクチド：ε−カプロラクトン＝7
5：25モル％のモノフィラメントであり、ＵＳＰ規格０
号相当のものである。コーティングした糸の結節強力を
ＵＳＰの縫合糸の結節強力測定法の規定に従って測定を
行った。尚、結節破断伸度はそのときの伸度である。対
照としてコーティングをする前の糸の結節強力測定を行
った。(1) Solvent Acetone (2) Copolymer (Polymer) Concentration 2 W / V% (3) Calcium Stearate Concentration 0.2 and 2 W / V% These three components are mixed and continuously stirred for about 10 m. / mi
The coating was done by passing the yarn through at a speed of n. The yarn used is lactide: ε-caprolactone = 7
5:25 mol% monofilament, USP standard 0
It is equivalent to the issue. The knot tenacity of the coated yarn was measured according to the USP suture knot tenacity measuring method. The knot breaking elongation is the elongation at that time. As a control, the knot strength of the yarn before coating was measured.
【００３５】[0035]
【表１】 [Table 1]
【００３６】なお、結節強力向上率は向上した分の強力
をコーティング前の強力で割った値に１００を掛けたも
のである。
実施例２
L-乳酸とε−カプロラクトンの共重合体（ラクチド：ε
−カプロラクトン＝50：50モル％）を使用して、ステア
リン酸カルシウムを併用してコーティングを行った。The knot strength improvement rate is the value obtained by dividing the improved strength by the strength before coating and then multiplying by 100. Example 2 Copolymer of L-lactic acid and ε-caprolactone (lactide: ε
-Caprolactone = 50:50 mol%) was used in combination with calcium stearate.
【００３７】（１） 溶媒
アセトン
（２） 共重合体濃度
２W/V％
（３） ステアリン酸カルシウム濃度
0.2および２W/V％
この３成分を混合し、常に撹拌した状態の中を約10m/mi
n.の速度で実施例１と同じ糸を通過させることによりコ
ーティングを行った。使用した糸はラクチド：ε−カプ
ロラクトン＝75：25モル％のモノフィラメントであり、
ＵＳＰ規格０号相当のものである。コーティングした糸
の結節強力をＵＳＰの規定に従って測定を行った。対照
としてコーティングをする前の糸の結節強力測定を行っ
た。(1) Solvent Acetone (2) Copolymer Concentration 2 W / V% (3) Calcium Stearate Concentration 0.2 and 2 W / V% These three components are mixed and constantly stirred at a rate of about 10 m / mi.
The coating was carried out by passing the same yarn as in Example 1 at a speed of n. The yarn used was a lactide: ε-caprolactone = 75: 25 mol% monofilament,
It is equivalent to USP Standard No. 0. The knot tenacity of the coated yarn was measured according to USP regulations. As a control, the knot strength of the yarn before coating was measured.
【００３８】[0038]
【表２】 [Table 2]
【００３９】実施例３
L-乳酸とε−カプロラクトンの共重合体（ラクチド：ε
−カプロラクトン＝８：92モル％）を使用して、ステア
リン酸カルシウムを併用してコーティングを行った。Example 3 Copolymer of L-lactic acid and ε-caprolactone (lactide: ε
-Caprolactone = 8:92 mol%) was used in combination with calcium stearate.
【００４０】（１）溶媒
アセトン
（２）共重合体濃度
２W/V％
（３）ステアリン酸カルシウム濃度
0, 0.1, 0.2, 0.5, 1および2W/V％
この３成分を混合し、常に撹拌した状態の中を約10m/mi
n.の速度で実施例１と同じ糸を通過させることによりコ
ーティングを行った。使用した糸はラクチド：ε−カプ
ロラクトン＝75：25モル％のモノフィラメントであり、
ＵＳＰ規格2-0号相当のものである。コーティングした
糸の結節強力をＵＳＰの規定に従って測定を行った。対
照としてコーティングをする前の糸の結節強力測定を行
った。(1) Solvent Acetone (2) Copolymer concentration 2 W / V% (3) Calcium stearate concentration 0, 0.1, 0.2, 0.5, 1 and 2 W / V% These three components are mixed and constantly stirred About 10m / mi
The coating was carried out by passing the same yarn as in Example 1 at a speed of n. The yarn used was a lactide: ε-caprolactone = 75: 25 mol% monofilament,
It is equivalent to USP Standard No. 2-0. The knot tenacity of the coated yarn was measured according to USP regulations. As a control, the knot strength of the yarn before coating was measured.
【００４１】[0041]
【表３】 [Table 3]
【００４２】実施例４
ε−カプロラクトンを使用し、ステアリン酸カルシウム
を併用してコーティングを行った。Example 4 Using ε-caprolactone, coating was performed in combination with calcium stearate.
【００４３】（１）溶媒
アセトン
（２）ε−カプロラクトン濃度
0.1, 0.5, 1.0 W/V％
（３）ステアリン酸カルシウム濃度
0.1W/V％
この３成分を混合し、常に撹拌した状態の中を約10m/mi
n.の速度で実施例１と同じ糸を通過させることによりコ
ーティングを行った。使用した糸はラクチド：ε−カプ
ロラクトン＝75：25モル％のモノフィラメントであり、
ＵＳＰ規格0号相当のものである。コーティングした糸
の結節強力をＵＳＰの規定に従って測定を行った。対照
としてコーティングをする前の糸の結節強力測定を行っ
た。(1) Solvent Acetone (2) Epsilon-caprolactone concentration 0.1, 0.5, 1.0 W / V% (3) Calcium stearate concentration 0.1 W / V% These three components are mixed and the contents of the mixture are constantly stirred. 10m / mi
The coating was carried out by passing the same yarn as in Example 1 at a speed of n. The yarn used was a lactide: ε-caprolactone = 75: 25 mol% monofilament,
It is equivalent to USP Standard No. 0. The knot tenacity of the coated yarn was measured according to USP regulations. As a control, the knot strength of the yarn before coating was measured.
【００４４】[0044]
【表４】 [Table 4]
【００４５】[0045]
【発明の効果】本発明のコーティング方法で吸収性モノ
フィラメント縫合糸にコーティングを施すことにより、
糸表面の滑りが良くなり、使用時の操作性が向上する。
このことは、充分な強力があるにもかかわらず、滑りが
悪いために無理な力を加えた結果として起こる操作中の
糸切れを防ぐものである。さらにはコーティングをしな
い糸と比較して、ＵＳＰで規定された結節破断強力が10
〜50％向上する。By applying a coating to the absorbable monofilament suture by the coating method of the present invention,
The slippage of the yarn surface is improved and the operability during use is improved.
This is to prevent yarn breakage during operation which is the result of applying excessive force due to poor slippage despite having sufficient strength. Furthermore, compared to uncoated yarn, the knot breaking strength specified by USP is 10
~ 50% improvement.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平10−179723（ＪＰ，Ａ) 特開 平８−182751（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) A61L 17/00 ─────────────────────────────────────────────────── ─── Continuation of the front page (56) References JP-A-10-179723 (JP, A) JP-A-8-182751 (JP, A) (58) Fields investigated (Int.Cl. 7 , DB name) A61L 17/00
Claims (6)
単位とし、ε−カプロラクトンとラクチドの組成比がモ
ル比で88〜97：12〜3％である共重合体及びステアリン
酸カルシウムを含み、ステアリン酸カルシウムの配合比
率が0.01〜1.5wt％であるコーティング材料で、ε−カ
プロラクトンとラクチドの共重合体からなるモノフィラ
メント縫合糸をコーティングした吸収性縫合糸。1. A copolymer containing ε-caprolactone and lactide as a repeating unit, wherein the composition ratio of ε-caprolactone and lactide is 88 to 97:12 to 3% by mole, and calcium stearate, and calcium stearate is blended. An absorbable suture coated with a monofilament suture composed of a copolymer of ε-caprolactone and lactide with a coating material having a ratio of 0.01 to 1.5 wt%.
単位とし、ε−カプロラクトンとラクチドの組成比がモ
ル比で70〜80：30〜20％である共重合体及びステアリン
酸カルシウムを含み、ステアリン酸カルシウムの配合比
率が0.1〜2.5wt％であるコーティング材料で、ε−カプ
ロラクトンとラクチドの共重合体からなるモノフィラメ
ント縫合糸をコーティングした吸収性縫合糸。2. A copolymer containing ε-caprolactone and lactide as repeating units, wherein the composition ratio of ε-caprolactone and lactide is 70 to 80:30 to 20% by mole, and calcium stearate, and calcium stearate is blended. An absorbable suture coated with a monofilament suture composed of a copolymer of ε-caprolactone and lactide with a coating material having a ratio of 0.1 to 2.5 wt%.
単位とし、ε−カプロラクトンとラクチドの組成比がモ
ル比で45〜55：55〜45％である共重合体及びステアリン
酸カルシウムを含み、ステアリン酸カルシウムの配合比
率が1.0〜3.0wt％であるコーティング材料で、ε−カプ
ロラクトンとラクチドの共重合体からなるモノフィラメ
ント縫合糸をコーティングした吸収性縫合糸。3. A copolymer containing ε-caprolactone and lactide as a repeating unit, wherein the composition ratio of ε-caprolactone and lactide is 45 to 55:55 to 45% by mole, and calcium stearate, and calcium stearate is blended. An absorbable suture coated with a monofilament suture composed of a copolymer of ε-caprolactone and lactide with a coating material having a ratio of 1.0 to 3.0 wt%.
み、ステアリン酸カルシウムの配合比率が0.01〜1.0wt
％であるコーティング材料で、ε−カプロラクトンとラ
クチドの共重合体からなるモノフィラメント縫合糸をコ
ーティングした吸収性縫合糸。4. A homopolymer of ε-caprolactone, containing 0.01 to 1.0 wt% of calcium stearate.
% Of coating material, absorbable suture coated with a monofilament suture consisting of a copolymer of ε-caprolactone and lactide.
チドの組成比が、モル比で20〜30：80〜70％である請求
項１〜４のいずれかに記載の縫合糸。5. The suture according to claim 1, wherein the composition ratio of ε-caprolactone and lactide in the absorbable suture is 20 to 30:80 to 70% in terms of molar ratio.
％向上してなる請求項１〜５のいずれかに記載の縫合
糸。6. The coating has a knot strength of 10 to 50.
%, The suture according to any one of claims 1 to 5.