JP3411226B2 - Decorative body and method of manufacturing decorative body - Google Patents
Decorative body and method of manufacturing decorative bodyInfo
- Publication number
- JP3411226B2 JP3411226B2 JP28401998A JP28401998A JP3411226B2 JP 3411226 B2 JP3411226 B2 JP 3411226B2 JP 28401998 A JP28401998 A JP 28401998A JP 28401998 A JP28401998 A JP 28401998A JP 3411226 B2 JP3411226 B2 JP 3411226B2
- Authority
- JP
- Japan
- Prior art keywords
- layer
- decorative body
- stainless steel
- colored layer
- steel plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【発明の属する技術分野】この発明は、例えば黒色被膜
が形成されたステンレス鋼板の表面に赤色の着色層を形
成して装飾を施した装飾体及び装飾体の製造方法に関す
るものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative body in which a red colored layer is formed on the surface of a stainless steel sheet on which a black coating is formed, and a decorative body, and a method for manufacturing the decorative body. It is a thing.
【０００２】[0002]
【従来の技術】従来、この種の装飾体においては、金属
基材として例えば黒色の発色ステンレス板が用いられ
る。このステンレス板上に赤色の着色層を形成して装飾
を施す場合、ステンレス板表面に直接赤色の着色層を形
成したときには、隠蔽性が悪いために下地の黒色が影響
した赤黒い色に仕上がる。そこで、通常は赤色の着色層
を形成する前にステンレス板表面に白色の着色層を形成
し、その上に赤色の着色層を形成することにより、赤色
の鮮やかな色合いを出すことを可能としている。2. Description of the Related Art Conventionally, in this type of decorative body, for example, a black coloring stainless steel plate is used as a metal substrate. When a red colored layer is formed on this stainless steel plate for decoration, when the red colored layer is formed directly on the surface of the stainless steel plate, the hiding property is poor and the black color of the base affects the reddish black color. Therefore, it is usually possible to form a bright red tint by forming a white colored layer on the surface of the stainless steel plate before forming the red colored layer and then forming the red colored layer on the white colored layer. .
【０００３】[0003]
【発明が解決しようとする課題】ところが、予め形成さ
れた白色の着色層の上に赤色の着色層を形成した場合、
赤色の鮮やかな色合いを出すことは可能であるが、その
赤色に金属感を与えることができず、装飾性に欠けると
いう問題があった。However, when a red colored layer is formed on a previously formed white colored layer,
Although it is possible to produce a vivid red shade, there is a problem in that the red color cannot give a metallic feel and lacks decorativeness.
【０００４】この発明は、上記のような従来技術に存在
する問題点に着目してなされたものである。その目的と
するところは、金属感を与えることができ、装飾性を向
上させることができる装飾体及び装飾体の製造方法を提
供することにある。The present invention has been made by paying attention to the problems existing in the prior art as described above. An object of the invention is to provide a decorative body and a method for manufacturing the decorative body, which can give a metallic feeling and can improve decorativeness.
【０００５】[0005]
【課題を解決するための手段】上記の目的を達成するた
めに、請求項１に記載の発明の装飾体の製造方法は、ス
テンレス鋼製の基材表面に着色被膜をクロム酸で処理す
ることにより形成し、その一部を硫酸水溶液で電解除去
して基材表面を露出させ、その露出した基材表面に透明
又は半透明の着色層を形成したものである。In order to achieve the above-mentioned object, the method for producing a decorative body of the invention according to claim 1 is to treat a colored film on a surface of a stainless steel substrate with chromic acid. By electrolysis, part of which is removed electrolytically with a sulfuric acid solution.
Then, the surface of the base material is exposed, and a transparent or semitransparent colored layer is formed on the exposed surface of the base material.
【０００６】請求項２に記載の発明の装飾体の製造方法
は、請求項１に記載の発明において、前記着色被膜は暗
色系の色調を有し、透明又は半透明の着色層は明色系の
色調を有するものである。According to a second aspect of the present invention, there is provided the method for producing a decorative body according to the first aspect, wherein the colored film has a dark color tone and is transparent or semitransparent. Has a light color tone.
【０００７】[0007]
【０００８】[0008]
【発明の実施の形態】以下、この発明の実施形態を図１
〜図４に従って説明する。図１及び図２に示すように、
装飾体１１は、基材としての四角板状のステンレス鋼板
１２と、そのステンレス鋼板１２の表面中央に設けられ
た装飾部１３とにより構成されている。装飾部１３は、
ステンレス鋼板１２表面に形成された着色被膜としての
黒色被膜１４と透明又は半透明の着色層としての赤色の
着色層１５及びメッキ層１６とにより所定の模様を描く
ように形成されている。BEST MODE FOR CARRYING OUT THE INVENTION An embodiment of the present invention will be described below with reference to FIG.
~ It demonstrates according to FIG. As shown in FIGS. 1 and 2,
The decorative body 11 includes a square plate-shaped stainless steel plate 12 as a base material and a decorative portion 13 provided at the center of the surface of the stainless steel plate 12. The decorative portion 13 is
A black coating 14 as a colored coating formed on the surface of the stainless steel plate 12, a red colored layer 15 as a transparent or translucent colored layer, and a plating layer 16 are formed so as to draw a predetermined pattern.
【０００９】黒色被膜１４は、ステンレス鋼板１２表面
をクロム酸で処理することにより形成されたクロム酸被
膜である。この黒色被膜１４は、赤色の着色層１５とメ
ッキ層１６とともに装飾部１３の所定の模様を構成する
ように形成されるとともに、装飾部１３以外の部分を覆
うように形成されている。The black coating 14 is a chromic acid coating formed by treating the surface of the stainless steel plate 12 with chromic acid. The black coating 14 is formed together with the red colored layer 15 and the plating layer 16 so as to form a predetermined pattern of the decorative portion 13, and is formed so as to cover the portion other than the decorative portion 13.
【００１０】赤色の着色層１５は、ステンレス鋼板１２
表面にスクリーン印刷によって顔料の粒子径が２μｍ以
下のオフセット印刷用のインクが塗布形成されたもので
あり、黒色被膜１４とメッキ層１６とともに装飾部１３
の所定の模様を構成するように形成されている。この赤
色の着色層１５を形成するインクとしては、焼付け用の
インクとして東洋インク（株）製の商品名ニューＭＤＫ
が使用される。赤色の着色層１５の厚みは好ましくは３
〜３０μｍ、さらに好ましくは１０〜２０μｍである。The red colored layer 15 is a stainless steel plate 12.
An ink for offset printing having a pigment particle size of 2 μm or less is applied and formed on the surface by screen printing, and the decorative portion 13 together with the black coating 14 and the plating layer 16 is formed.
Are formed so as to form a predetermined pattern. The ink for forming the red colored layer 15 is a new ink MDK manufactured by Toyo Ink Co., Ltd. as a printing ink.
Is used. The thickness of the red colored layer 15 is preferably 3
-30 μm, more preferably 10-20 μm.
【００１１】メッキ層１６は、複数のメッキ層が積層形
成されたものであり、下層から下地メッキ層、銅メッキ
層、ニッケルメッキ層及び金メッキ層の順にステンレス
鋼板１２表面に形成されている。このメッキ層１６は、
黒色被膜１４と赤色の着色層１５とともに装飾部１３の
所定の模様を構成するように形成されている。The plating layer 16 is formed by laminating a plurality of plating layers, and is formed on the surface of the stainless steel plate 12 in the order from the lower layer to the base plating layer, the copper plating layer, the nickel plating layer and the gold plating layer. This plating layer 16 is
The black coating 14 and the red colored layer 15 are formed so as to form a predetermined pattern of the decorative portion 13.
【００１２】なお、図２〜図４において、黒色被膜１
４、赤色の着色層１５及びメッキ層１６の厚みは構成を
明確に表すために誇張して描かれている。次に、前記の
ように構成された装飾体１１の製造方法を説明する。2 to 4, the black coating 1
4. The thicknesses of the red colored layer 15 and the plated layer 16 are exaggerated in order to clearly show the configuration. Next, a method of manufacturing the decorative body 11 configured as described above will be described.
【００１３】まず、図３（ａ）に示すように、ステンレ
ス鋼板１２をクロム酸で処理することによりステンレス
鋼板１２の表面に黒色被膜１４を形成する。次に、図３
（ｂ）に示すように、黒色被膜１４上にシルクスクリー
ンを用いたシルク印刷又はロールコータ等により感光性
樹脂を均一に塗布して樹脂層１７を形成する。この感光
性樹脂としては、アルカリ剥離型のアクリル系樹脂等が
使用される。First, as shown in FIG. 3A, a black coating 14 is formed on the surface of the stainless steel plate 12 by treating the stainless steel plate 12 with chromic acid. Next, FIG.
As shown in (b), a photosensitive resin is uniformly applied onto the black coating 14 by silk printing using a silk screen, a roll coater or the like to form a resin layer 17. As the photosensitive resin, an alkali peeling acrylic resin or the like is used.
【００１４】続いて、図３（ｃ）に示すように、樹脂層
１７の形成されたステンレス鋼板１２の上方にネガフィ
ルム１８を配置し、その上方から紫外線（ＵＶ）を照射
する。すると、紫外線の照射された部分の感光性樹脂の
みが硬化する。その後、１〜３％の炭酸ナトリウム水溶
液によって未硬化樹脂を洗浄除去することにより、図３
（ｄ）に示すように、硬化樹脂層１９のみが黒色被膜１
４上に形成される。Subsequently, as shown in FIG. 3C, the negative film 18 is arranged above the stainless steel plate 12 on which the resin layer 17 is formed, and ultraviolet rays (UV) are irradiated from above. Then, only the photosensitive resin in the portion irradiated with ultraviolet rays is cured. After that, the uncured resin is removed by washing with a 1 to 3% aqueous solution of sodium carbonate.
As shown in (d), only the cured resin layer 19 has the black coating 1
4 is formed.
【００１５】次いで、硬化樹脂層１９の形成されたステ
ンレス鋼板１２を硫酸の５０％水溶液中で陽極電解する
ことにより、図４（ａ）に示すように、硬化樹脂層１９
の形成されていない部分の黒色被膜１４が除去されて凹
所２０が形成される。続いて、この露出したステンレス
鋼板１２表面の一部にスクリーン印刷法により赤色のイ
ンクを塗布し、１３０℃の温度で１０分間加熱して焼付
けることにより、図４（ｂ）に示すように、赤色の着色
層１５が形成される。Next, the stainless steel plate 12 on which the cured resin layer 19 is formed is subjected to anodic electrolysis in a 50% aqueous solution of sulfuric acid, so that the cured resin layer 19 is formed as shown in FIG. 4 (a).
The black coating film 14 in the portion where the concave portions are not formed is removed to form the recesses 20. Subsequently, a red ink is applied to a part of the exposed surface of the stainless steel plate 12 by a screen printing method, and is heated and baked at a temperature of 130 ° C. for 10 minutes, so that as shown in FIG. The red colored layer 15 is formed.
【００１６】次に、露出したステンレス鋼板１２表面の
残りの部分に電解メッキが施される。図４（ｃ）に示す
ように、メッキ層１６は、硬化樹脂層１９及び赤色の着
色層１５が不導体であるため硬化樹脂層１９及び赤色の
着色層１５の形成されていない部分にのみ形成される。
このメッキ層１６は、下地メッキ層、銅メッキ層、ニッ
ケルメッキ層及び金メッキ層の順に積層形成される。Next, electrolytic plating is applied to the remaining portion of the exposed surface of the stainless steel plate 12. As shown in FIG. 4C, the plating layer 16 is formed only on a portion where the cured resin layer 19 and the red colored layer 15 are not formed because the cured resin layer 19 and the red colored layer 15 are non-conductors. To be done.
The plating layer 16 is formed by laminating a base plating layer, a copper plating layer, a nickel plating layer, and a gold plating layer in this order.
【００１７】まず、表面に硬化樹脂層１９及び赤色の着
色層１５の形成されたステンレス鋼板１２を下地メッキ
液中に浸漬し、下地メッキが行われる。この下地メッキ
処理により、露出したステンレス鋼板１２表面にのみ下
地メッキ層が形成される。この下地メッキ層の厚みは
０．１〜０．２μｍ程度である。First, the stainless steel plate 12 on the surface of which the cured resin layer 19 and the red colored layer 15 are formed is immersed in an undercoat plating solution to carry out undercoat plating. By this base plating treatment, the base plating layer is formed only on the exposed surface of the stainless steel plate 12. The thickness of this base plating layer is about 0.1 to 0.2 μm.
【００１８】次に、銅メッキ液中に下地メッキを施した
ステンレス鋼板１２を浸漬し、銅メッキが行われる。こ
の銅メッキ処理により、下地メッキ層上に銅メッキ層が
形成される。このメッキ処理により形成される銅メッキ
層の厚みは４０〜８０μｍであり、肉厚に形成される。Then, the stainless steel plate 12 plated with the undercoat is immersed in a copper plating solution to perform copper plating. By this copper plating treatment, a copper plating layer is formed on the base plating layer. The copper plating layer formed by this plating process has a thickness of 40 to 80 μm and is formed thick.
【００１９】続いて、ニッケルメッキ液中に銅メッキを
施したステンレス鋼板１２を浸漬し、ニッケルメッキが
行われる。このニッケルメッキ処理により、銅メッキ層
上にニッケルメッキ層が形成される。このニッケルメッ
キ層の厚みは２〜３μｍ程度である。Subsequently, the stainless steel plate 12 plated with copper is immersed in a nickel plating solution to perform nickel plating. By this nickel plating treatment, a nickel plating layer is formed on the copper plating layer. The nickel plating layer has a thickness of about 2 to 3 μm.
【００２０】最後に、金メッキ液中にニッケルメッキを
施したステンレス鋼板１２を浸漬し、金メッキが行われ
る。この金メッキ処理により、ニッケルメッキ層上に金
メッキ層が形成される。この金メッキ層の厚みは０．１
μｍ程度である。Finally, the nickel-plated stainless steel plate 12 is immersed in a gold plating solution to perform gold plating. By this gold plating treatment, a gold plating layer is formed on the nickel plating layer. The thickness of this gold plating layer is 0.1
It is about μm.
【００２１】そして、メッキ終了後、５％水酸化ナトリ
ウム水溶液でステンレス鋼板１２表面が洗浄されて硬化
樹脂層１９が除去されると、実施形態の装飾体１１が得
られる。After the plating is completed, the surface of the stainless steel plate 12 is washed with a 5% sodium hydroxide aqueous solution to remove the hardened resin layer 19, so that the decorative body 11 of the embodiment is obtained.
【００２２】以上のように、この実施形態によれば次の
ような効果が発揮される。
・実施形態の装飾体１１によれば、ステンレス鋼板１２
の表面に形成された黒色皮膜１４が除去された状態で透
明又は半透明の着色層である赤色の着色層１５が形成さ
れている。このため、赤色の着色層１５はその下に位置
するステンレス鋼板１２の光沢が透過状態で視認できて
金属感を与えることができ、装飾性を向上させることが
できる。As described above, according to this embodiment, the following effects are exhibited. According to the decorative body 11 of the embodiment, the stainless steel plate 12
A red colored layer 15 which is a transparent or translucent colored layer is formed in a state where the black film 14 formed on the surface of the is removed. Therefore, in the red colored layer 15, the gloss of the stainless steel plate 12 located therebelow can be visually recognized in a transparent state to give a metallic feeling, and the decorative property can be improved.
【００２３】・実施形態の装飾体１１によれば、ステン
レス鋼板１２の表面には暗色系の色調を有する黒色被膜
１４と明色系の色調を有する赤色の着色層１５とが形成
されている。このため、コントラストが鮮明であり、装
飾性をより向上させることができる。According to the decorative body 11 of the embodiment, the black coating 14 having a dark color tone and the red colored layer 15 having a light color tone are formed on the surface of the stainless steel plate 12. Therefore, the contrast is clear and the decorativeness can be further improved.
【００２４】・実施形態の装飾体１１によれば、ステン
レス鋼板１２の表面には黒色被膜１４及び赤色の着色層
１５に加えてメッキ層１６が形成されている。このた
め、表面に金属光沢を与えることができ、装飾性をより
向上させることができる。According to the decorative body 11 of the embodiment, the plating layer 16 is formed on the surface of the stainless steel plate 12 in addition to the black coating 14 and the red colored layer 15. Therefore, a metallic luster can be given to the surface, and the decorative property can be further improved.
【００２５】・実施形態の装飾体１１によれば、メッキ
層１６は複数のメッキ層により積層形成されているた
め、立体的に形成することができ、装飾性をより向上さ
せることができる。According to the decorative body 11 of the embodiment, since the plating layer 16 is formed by laminating a plurality of plating layers, it can be formed three-dimensionally and the decorativeness can be further improved.
【００２６】・実施形態の装飾体１１によれば、赤色の
着色層１５は、顔料の粒径が小さいオフセット印刷用の
インクによって形成されている。このため、赤色の着色
層１５の表面を平滑に仕上げることができるとともに、
グラデーションを表現するのに好適である。According to the decorative body 11 of the embodiment, the red colored layer 15 is formed by the ink for offset printing in which the particle size of the pigment is small. Therefore, the surface of the red colored layer 15 can be finished to be smooth, and
It is suitable for expressing gradation.
【００２７】・実施形態の装飾体１１によれば、赤色の
着色層１５は、スクリーン印刷法によって形成されてい
る。このため、赤色の着色層１５を最大３０μｍ程度の
厚さに形成することができ、耐久性を向上させることが
できる。また、赤色の着色層１５とメッキ層１６との高
低差を小さくすることができ、赤色の着色層１５及びメ
ッキ層１６の耐久性を向上させることができる。According to the decorative body 11 of the embodiment, the red colored layer 15 is formed by the screen printing method. Therefore, the red colored layer 15 can be formed with a maximum thickness of about 30 μm, and the durability can be improved. Further, the height difference between the red colored layer 15 and the plated layer 16 can be reduced, and the durability of the red colored layer 15 and the plated layer 16 can be improved.
【００２８】なお、前記実施形態を次のように変更して
構成することもできる。
・ステンレス鋼板１２に代えて、基材としてチタンコー
ティングした鉄、ステンレス鋼等を使用すること。The above embodiment may be modified as follows. -Instead of the stainless steel plate 12, use titanium-coated iron, stainless steel, or the like as a base material.
【００２９】・スクリーン印刷法に代えて、オフセット
印刷法によって赤色の着色層１５を形成すること。この
ように構成した場合、赤色の着色層１５は実施形態と同
様の効果を奏することができるほか、スクリーン印刷法
の場合に比べて厚みを薄くすることができる。Forming the red colored layer 15 by an offset printing method instead of the screen printing method. With such a configuration, the red colored layer 15 can achieve the same effect as that of the embodiment, and can be thinner than the case of the screen printing method.
【００３０】・赤色の着色層１５の上に透明の保護層を
積層形成すること。このように構成した場合、赤色の着
色層１５を保護することができるとともに、メッキ層１
６との高低差を小さくすることができ、耐久性をより向
上させることができる。Laminating a transparent protective layer on the red colored layer 15. When configured in this way, the red colored layer 15 can be protected and the plated layer 1
It is possible to reduce the difference in height with respect to 6 and further improve durability.
【００３１】・黒色被膜１４を除去して露出させたステ
ンレス鋼板１２表面に赤色の着色層１５とメッキ層１６
を形成するとき、先にメッキ層１６を形成してから赤色
の着色層１５を形成するように変更すること。即ち、ま
ず、ステンレス鋼板１２表面のうち赤色の着色層１５を
形成したい部分にマスキング層を形成する。その状態で
メッキ層１６を形成した後、マスキング層を除去し、そ
の露出面に赤色の着色層１５を形成する。A red colored layer 15 and a plated layer 16 on the surface of the stainless steel plate 12 exposed by removing the black coating film 14.
When forming, the plating layer 16 is formed first, and then the red colored layer 15 is formed. That is, first, a masking layer is formed on a portion of the surface of the stainless steel plate 12 where the red colored layer 15 is to be formed. After the plating layer 16 is formed in this state, the masking layer is removed and the red colored layer 15 is formed on the exposed surface.
【００３２】・黒色被膜１４を除去して露出させたステ
ンレス鋼板１２表面に赤色をはじめとする各色の着色層
を形成し、メッキ層１６を省略すること。次に、前記実
施形態から把握できる技術的思想について以下に記載す
る。A colored layer of each color including red is formed on the surface of the stainless steel plate 12 exposed by removing the black coating 14, and the plating layer 16 is omitted. Next, technical ideas that can be understood from the above-described embodiment will be described below.
【００３３】（１）金属製の基材表面に着色被膜を形成
し、その一部を除去して基材表面を露出させ、その露出
した基材表面に透明又は半透明の着色層を形成する装飾
体の製造方法。(1) A colored coating film is formed on the surface of a metallic substrate, a part of the colored coating film is removed to expose the surface of the substrate, and a transparent or semitransparent colored layer is formed on the exposed surface of the substrate. A method for manufacturing a decorative body.
【００３４】このように構成した場合、基材表面に形成
された着色皮膜が除去された状態で透明又は半透明の着
色層が形成されているため、金属感を与えることがで
き、装飾性を向上させることができる。In the case of such a constitution, since the transparent or semi-transparent coloring layer is formed in a state where the coloring film formed on the surface of the base material is removed, it is possible to give a metallic feeling and decorativeness. Can be improved.
【００３５】（２）前記透明又は半透明の着色層は、ス
クリーン印刷法によって形成されたものである請求項１
〜３のいずれかに記載の装飾体。このように構成した場
合、透明又は半透明の着色層は最大３０μｍ程度の厚さ
に形成することができ、耐久性を向上させることができ
る。また、透明又は半透明の着色層とメッキ層の高低差
を小さくすることができ、着色層及びメッキ層の耐久性
を向上させることができる。(2) The transparent or semitransparent colored layer is formed by a screen printing method.
The decorative body according to any one of to 3. With this structure, the transparent or semi-transparent colored layer can be formed with a maximum thickness of about 30 μm, and the durability can be improved. Further, the height difference between the transparent or semi-transparent colored layer and the plated layer can be reduced, and the durability of the colored layer and the plated layer can be improved.
【００３６】（３）前記スクリーン印刷法はオフセット
印刷用のインクを用いて行われるものである上記（２）
に記載の装飾体。このように構成した場合、顔料の粒子
径が小さいため、表面を平滑にすることができ、仕上が
りがきれいである。(3) The screen printing method is performed by using an ink for offset printing.
The decorative body according to. With such a configuration, since the particle size of the pigment is small, the surface can be made smooth and the finish is beautiful.
【００３７】[0037]
【発明の効果】この発明は、以上のように構成されてい
るため、次のような効果を奏する。請求項１に記載の発
明の装飾体の製造方法によれば、ステンレス鋼製の基材
表面にクロム酸で処理することにより形成された着色皮
膜が硫酸水溶液で電解除去された状態で透明又は半透明
の着色層が形成されているため、金属感を与えることが
でき、装飾性を向上させることができる。Since the present invention is constructed as described above, it has the following effects. According to the method for producing a decorative body of the invention as set forth in claim 1, the colored film formed by treating the surface of the stainless steel substrate with chromic acid is transparent or semi-transparent while being electrolytically removed with an aqueous sulfuric acid solution. Since the transparent colored layer is formed, a metallic feeling can be given and the decorativeness can be improved.
【００３８】請求項２に記載の発明の装飾体の製造方法
によれば、基材表面には暗色系の色調を有する着色被膜
と明色系の色調を有する透明又は半透明の着色層とが形
成されている。このため、請求項１に記載の発明の効果
に加え、コントラストが鮮明であり、装飾性をより向上
させることができる。According to the method for producing a decorative article of the invention as defined in claim 2, a colored coating film having a dark color tone and a transparent or translucent film having a light color tone are formed on the surface of the substrate. The colored layer is formed. Therefore, in addition to the effect of the invention described in claim 1, the contrast is clear and the decorativeness can be further improved.
【００３９】[0039]
【図１】この発明の装飾体の一実施形態を示す一部を切
欠いた平面図。FIG. 1 is a partially cutaway plan view showing an embodiment of a decorative body of the present invention.
【図２】同じく装飾体の一実施形態を示す断面図。FIG. 2 is a sectional view showing an embodiment of a decorative body.
【図３】（ａ）はステンレス鋼板上に黒色被膜を形成し
た状態を示す断面図、（ｂ）は黒色被膜上に樹脂層を形
成した状態を示す断面図、（ｃ）は樹脂層に紫外線を照
射した状態を示す断面図、（ｄ）は未硬化樹脂を除去し
た状態を示す断面図。3A is a sectional view showing a state in which a black coating is formed on a stainless steel plate, FIG. 3B is a sectional view showing a state in which a resin layer is formed on the black coating, and FIG. 3C is an ultraviolet ray on the resin layer. Is a cross-sectional view showing a state where the uncured resin is removed, and FIG.
【図４】（ａ）はステンレス鋼板上の黒色被膜の一部を
除去した状態を示す断面図、（ｂ）はステンレス鋼板表
面に赤色の着色層を形成した状態を示す断面図、（ｃ）
はステンレス鋼板表面にメッキ層を形成した状態を示す
断面図。FIG. 4A is a cross-sectional view showing a state where a part of a black coating on a stainless steel plate is removed, FIG. 4B is a cross-sectional view showing a state where a red colored layer is formed on the surface of the stainless steel plate, and FIG.
FIG. 3 is a cross-sectional view showing a state where a plating layer is formed on the surface of a stainless steel plate.
１１…装飾体、１２…基材としてのステンレス鋼板、１
４…着色被膜としての黒色被膜、１５…透明又は半透明
の着色層としての赤色の着色層、１６…メッキ層。11 ... Decorative body, 12 ... Stainless steel plate as a base material, 1
4 ... Black coating as a colored coating, 15 ... Red coloring layer as a transparent or translucent coloring layer, 16 ... Plating layer.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 松波 廣三 岐阜県岐阜市市橋４丁目９番５号 華陽 技研工業 株式会社 内 (56)参考文献 特開 昭63−144072（ＪＰ，Ａ) 特開 昭53−134859（ＪＰ，Ａ) 特開 平10−172378（ＪＰ，Ａ) 特開 平７−313934（ＪＰ，Ａ) 特開 平２−133581（ＪＰ，Ａ) 特開 平１−265904（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B41M 1/28 B05D 5/06 B05D 7/14 ─────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Hirozo Matsunami 4-9-5, Ichihashi, Gifu City, Gifu Prefecture Kayo Giken Kogyo Co., Ltd. (56) Reference JP-A-63-144072 (JP, A) JP-A Sho 53-134859 (JP, A) JP 10-172378 (JP, A) JP 7-313934 (JP, A) JP 2-133581 (JP, A) JP 1-265904 (JP, A) (58) Fields surveyed (Int.Cl. 7 , DB name) B41M 1/28 B05D 5/06 B05D 7/14
Claims (2)
クロム酸で処理することにより形成し、その一部を硫酸
水溶液で電解除去して基材表面を露出させ、その露出し
た基材表面に透明又は半透明の着色層を形成する装飾体
の製造方法。 1. A colored film is formed on a surface of a stainless steel substrate by treating with chromic acid, and a part of the colored film is sulfuric acid.
A decorative body that is electrolytically removed with an aqueous solution to expose the surface of a base material and forms a transparent or semitransparent colored layer on the exposed surface of the base material.
Manufacturing method.
明又は半透明の着色層は明色系の色調を有するものであ
る請求項１に記載の装飾体の製造方法。 Wherein said colored coating has a color tone of dark color, the colored layer of transparent or translucent has a color tone of bright color Monodea
The method for manufacturing the decorative body according to claim 1.