JP3471259B2 - Floor material - Google Patents
Floor materialInfo
- Publication number
- JP3471259B2 JP3471259B2 JP18642999A JP18642999A JP3471259B2 JP 3471259 B2 JP3471259 B2 JP 3471259B2 JP 18642999 A JP18642999 A JP 18642999A JP 18642999 A JP18642999 A JP 18642999A JP 3471259 B2 JP3471259 B2 JP 3471259B2
- Authority
- JP
- Japan
- Prior art keywords
- sheet
- cork
- kgf
- expansion
- stretch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、家屋等の床に貼り
付けられるコルクを用いた床材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a flooring material using cork that is attached to the floor of a house or the like.
【０００２】[0002]
【従来の技術】従来、家屋等に用いられる床材には、部
屋に自然な雰囲気を作り出すために、天然素材、例えば
コルクを用いたものがある。この種の床材は、コルクを
主成分とするコルクシートに、緩衝シートを貼り付けて
形成されている。そして、この床材は、貼付領域に対応
した大きさに切り取られた後、部屋の床に貼り付けられ
る。2. Description of the Related Art Conventionally, there is a flooring material used in a house or the like which uses a natural material such as cork in order to create a natural atmosphere in a room. This type of flooring material is formed by attaching a cushioning sheet to a cork sheet containing cork as a main component. Then, this floor material is cut into a size corresponding to the sticking area and then stuck to the floor of the room.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、コルク
シートは、湿度や環境温度の変化により伸縮する特性が
ある。このため、この種の床材は、床に貼り付けられた
後、コルクシートが温度や湿度の変化により伸縮するこ
とで、床から浮き上がり、剥がれてしまうことがあっ
た。However, the cork sheet has the property of expanding and contracting due to changes in humidity and environmental temperature. For this reason, this kind of flooring material may be lifted from the floor and peeled off after the cork sheet expands and contracts due to changes in temperature and humidity after being attached to the floor.
【０００４】そこで、本発明は、床に貼り付けた後、温
度や湿度の環境変化でコルクシートが伸縮し、床から剥
がれることを防止する新規な床材を提供することを目的
とする。Therefore, it is an object of the present invention to provide a novel flooring material which prevents the cork sheet from expanding and contracting due to environmental changes in temperature and humidity after being attached to the flooring.
【０００５】[0005]
【課題を解決するための手段】本発明に係る床材は、上
述のような課題を解決すべく、コルク材からなるシート
材又は粉砕したコルク材を合成樹脂と混合して形成した
シート材からなるコルクシートと、コルクシートの裏面
に貼着されるコルク材とゴム材とを混合した緩衝シート
と、経糸及緯糸にガラス繊維を用いたガラスシートに、
ガラス繊維が全体の７０ｗｔ％となるように熱可塑性樹
脂を含浸させてなり、撓み変形をし、緩衝シートのコル
クシートが貼着されない側の面に熱可塑性接着剤によっ
て貼着されてコルクシートの伸縮を防止する伸縮防止シ
ートと、コルクシートの表面に貼着されて床材の表面を
構成する透明又は半透明の可撓性を有する保護シートと
を備える。伸縮防止シートは、引張り強度が８５Ｋｇｆ
／ｍｍ２、引張り弾性率が３，８００Ｋｇｆ／ｍｍ２、
伸び率が２．２％、曲げ強さが９０Ｋｇｆ／ｍｍ２、曲
げ弾性係数が３，５００Ｋｇｆ／ｍｍ２、線膨張係数が
５×１０−６／℃といった物性を有し、伸縮しにくく、
撓み変形しやすい。したがって、これを用いた床材は、
温度や湿度変化によっても、コルクシートが伸縮するこ
とによって、床より剥がれることを防止することができ
る。また、床材は、コルクシートに伸縮防止シートを容
易に貼着することができる。また、床材は、ロール状に
巻いて持ち運びがし易くなる。更に、この伸縮防止シー
トによって、コルク材とゴム材とを混合した緩衝シート
の伸縮も防止することができる。緩衝シートは、コルク
材とゴム材とを混合してなることから、衝撃を吸収する
ことができる。更に、床材の表面を保護シートとするこ
とで、脆弱なコルクシートの表面を保護することができ
る。In order to solve the above-mentioned problems, the flooring material according to the present invention comprises a sheet material made of cork material or a sheet material formed by mixing crushed cork material with a synthetic resin. A cork sheet, a buffer sheet that is a mixture of a cork material and a rubber material that is attached to the back surface of the cork sheet, and a glass sheet that uses glass fibers for the warp and the weft,
The glass fiber is impregnated with a thermoplastic resin so as to make up 70% by weight of the whole, and is deformed flexibly, and is adhered with a thermoplastic adhesive to the surface of the buffer sheet on which the cork sheet is not adhered. An expansion prevention sheet for preventing expansion and contraction, and a transparent or semitransparent flexible protection sheet which is attached to the surface of the cork sheet and constitutes the surface of the flooring material. The stretch preventive sheet has a tensile strength of 85 kgf
/ Mm 2 , the tensile elastic modulus is 3,800 Kgf / mm 2 ,
It has physical properties such as an elongation of 2.2%, a bending strength of 90 Kgf / mm 2 , a bending elastic modulus of 3,500 Kgf / mm 2 , and a linear expansion coefficient of 5 × 10 −6 / ° C., and is difficult to expand and contract.
Easy to bend and deform. Therefore, the flooring material using this is
It is possible to prevent the cork sheet from peeling off the floor due to expansion and contraction of the cork sheet even when the temperature or humidity changes. Moreover, as for the flooring material, the stretch prevention sheet can be easily attached to the cork sheet. In addition, the floor material is wound in a roll shape and is easy to carry. Furthermore, the expansion / contraction sheet can prevent expansion / contraction of the buffer sheet in which the cork material and the rubber material are mixed. Since the cushioning sheet is made of a mixture of cork material and rubber material, it can absorb impact. Further, by using the surface of the floor material as the protective sheet, the surface of the fragile cork sheet can be protected.
【０００６】また、本発明に係る床材は、上述した課題
を解決すべく、コルク材からなるシート材又は粉砕した
コルク材を合成樹脂と混合して形成したシート材からな
るコルクシートと、上記コルクシートに貼着されて床材
の表面を構成する透明又は半透明の可撓性を有する保護
シートと、経糸及び緯糸にガラス繊維を用いたガラスシ
ートに、ガラス繊維が全体の７０ｗｔ％となるように熱
可塑性樹脂を含浸させてなり、撓み変形をし、一方の面
が上記コルクシートの上記保護シートが貼着されない面
に熱可塑性接着剤によって貼着されて上記コルクシート
の伸縮を防止する伸縮防止シートと、上記伸縮防止シー
トの他方の面に熱可塑性接着剤によって貼着されるコル
ク材とゴム材とを混合した緩衝シートとを備え、伸縮防
止シートは、上述と同様な物性を有し、伸縮しにくく、
撓み変形しやすい。この床材は、コルクシートと緩衝シ
ートとの間に伸縮防止シートが介在されていることか
ら、伸縮防止シートの機能がコルクシートと緩衝シート
に作用し、コルクシートと緩衝シートの伸縮を防止する
ことができる。また、床材の表面を保護シートとするこ
とで、脆弱なコルクシートの表面を保護することができ
る。Further, in order to solve the above-mentioned problems, the flooring material according to the present invention comprises a sheet material made of cork material or a cork sheet made of sheet material formed by mixing crushed cork material with a synthetic resin, and A transparent or semi-transparent flexible protective sheet that is attached to a cork sheet to form the surface of a flooring material, and a glass sheet that uses glass fibers for warp and weft yarns will have 70 wt% of glass fibers. It is impregnated with a thermoplastic resin so as to be flexurally deformed, and one side is attached by a thermoplastic adhesive to the side of the cork sheet on which the protective sheet is not attached to prevent expansion and contraction of the cork sheet. A stretch prevention sheet and a cushioning sheet obtained by mixing a cork material and a rubber material, which are attached to the other surface of the stretch prevention sheet with a thermoplastic adhesive, are provided. Have similar physical properties, hardly stretchable,
Easy to bend and deform. In this floor material, since the expansion / contraction preventing sheet is interposed between the cork sheet and the cushioning sheet, the function of the expansion / contraction preventing sheet acts on the cork sheet and the cushioning sheet to prevent the cork sheet and the cushioning sheet from expanding and contracting. be able to. Further, by using the surface of the floor material as the protective sheet, the surface of the fragile cork sheet can be protected.
【０００７】[0007]
【発明の実施の形態】以下、本発明が適用された床材に
ついて、図面を参照して説明する。本発明が適用された
床材は、コルクシートのバックシートに伸縮防止シート
を用いることで、温度や湿度の変化によりコルクシート
が伸縮することを防止し、床に貼着された後、床より剥
がれることを防止するものである。BEST MODE FOR CARRYING OUT THE INVENTION Floor materials to which the present invention is applied will be described below with reference to the drawings. The flooring material to which the present invention is applied, by using a stretch-preventing sheet for the back sheet of the cork sheet, prevents the cork sheet from stretching due to changes in temperature and humidity, and after being attached to the floor, from the floor It is to prevent peeling.
【０００８】先ず、本発明が適用された床材の説明に先
だって、図１を用いて本発明の前提となる床材を説明す
る。この床材１は、表面を構成するコルクシート２と、
このコルクシート２の伸縮を防止する伸縮防止シート３
とを備える。First, prior to the description of the floor material to which the present invention is applied, the floor material which is the premise of the present invention will be described with reference to FIG. This floor material 1 includes a cork sheet 2 that constitutes the surface,
Expansion / contraction sheet 3 for preventing expansion / contraction of the cork sheet 2
With.
【０００９】コルクシート２は、床材１の表面を構成す
るものであり、コルク材のみからなるシート材又は粉砕
したコルク材を合成樹脂と混合して形成されたシート材
によりなる。The cork sheet 2 constitutes the surface of the floor material 1, and is made of a sheet material composed only of cork material or a sheet material formed by mixing crushed cork material with a synthetic resin.
【００１０】伸縮防止シート３は、経糸及び緯糸にガラ
ス繊維を用いたガラスシートに熱可塑性樹脂を含浸させ
て形成されている。この伸縮防止シート３は、ガラス繊
維を全体の７０ｗｔ％程度含有させて形成されている。
伸縮防止シート３は、ガラス繊維を全体の７０ｗｔ％程
度用いることで、熱膨張や吸湿乾燥に伴う寸法変化を防
止している。また、伸縮防止シート３は、熱可塑性樹脂
を含浸させることで、熱加工成形を行うことができるよ
うにしている。このようなガラスシートに含有される熱
可塑性樹脂としては、ポリプロピレンが用いられてい
る。なお、熱可塑性樹脂としては、ポリプロピレンの他
に、ポリスチレン、ポリ塩化ビニル、高密度ポリエチレ
ン、ポリプロピレン、ナイロン、ポリカーボネート、ポ
リプチレンテレフタレート、ポリエチレンテレフタレー
ト等を用いてもよい。The stretch-preventing sheet 3 is formed by impregnating a thermoplastic resin into a glass sheet using glass fibers as warp and weft. The stretch-preventing sheet 3 is formed by containing glass fiber in an amount of about 70 wt% of the whole.
The stretch-preventing sheet 3 uses glass fibers in an amount of about 70% by weight to prevent dimensional changes due to thermal expansion and moisture absorption drying. Further, the stretch-preventing sheet 3 is impregnated with a thermoplastic resin so that it can be thermoformed. Polypropylene is used as the thermoplastic resin contained in such a glass sheet. In addition to polypropylene, polystyrene, polyvinyl chloride, high-density polyethylene, polypropylene, nylon, polycarbonate, polypropylene terephthalate, polyethylene terephthalate, or the like may be used as the thermoplastic resin.
【００１１】以上のように形成される伸縮防止シート３
は、次のような物性を有する。
引張り強度 ８５Ｋｇｆ／ｍｍ２
引張り弾性率 ３，８００Ｋｇｆ／ｍｍ２
伸び率 ２．２％Stretch prevention sheet 3 formed as described above
Has the following physical properties. Tensile strength 85 Kgf / mm 2 Tensile modulus 3,800 Kgf / mm 2 Elongation 2.2%
【００１２】すなわち、この伸縮防止シート３は、全体
の７０ｗｔ％程度をガラス繊維で構成することで、引張
り強度や引張り弾性率を高くしている。したがって、伸
縮防止シート３は、伸縮しにくくなり、コルクシート２
を容易に貼着することができる。That is, the stretch-preventing sheet 3 has a high tensile strength and a high tensile elastic modulus by constituting about 70 wt% of the entire glass fiber. Therefore, the stretch prevention sheet 3 is less likely to stretch and the cork sheet 2
Can be easily attached.
【００１３】また、伸縮防止シート３は、次のような物
性を有する。
曲げ強さ ９０Ｋｇｆ／ｍｍ２
曲げ弾性係数 ３，５００Ｋｇｆ／ｍｍ２ The stretch prevention sheet 3 has the following physical properties. Flexural strength 90 Kgf / mm 2 Flexural modulus 3,500 Kgf / mm 2
【００１４】すなわち、この伸縮防止シート３は、撓み
変形しやすい特性を有し、加工性に優れる特性を有して
いる。That is, the stretch-preventing sheet 3 has a characteristic of being easily bent and deformed, and has a characteristic of excellent workability.
【００１５】更には、この伸縮防止シート３は、線膨張
係数が５×１０−６／℃であり、温度変化によっても変
形しにくい特性を有している。Further, the expansion / contraction preventing sheet 3 has a coefficient of linear expansion of 5 × 10 −6 / ° C., and has a characteristic that it is difficult to be deformed by a temperature change.
【００１６】以上のような伸縮防止シート３には、一方
の面側に接着剤４を介してコルクシート２が貼着され、
床材１が形成される。ここで、伸縮防止シート３は、引
っ張っても伸びにくいことから、コルクシート２を容易
に貼着することができる。また、このように形成された
床材１は、撓み変形しやすいことから、例えばロール状
に巻くことで容易に持ち運びをすることができる。On the stretch prevention sheet 3 as described above, the cork sheet 2 is attached to one surface side with the adhesive 4 interposed therebetween.
Floor material 1 is formed. Here, since the stretch prevention sheet 3 is difficult to stretch even when pulled, the cork sheet 2 can be easily attached. Further, since the flooring material 1 formed in this way is easily bent and deformed, it can be easily carried by rolling it in a roll shape, for example.
【００１７】このように形成された床材１は、伸縮防止
シート３の他方の面側に接着剤５を介して床６に貼着さ
れる。このとき、床材１は、撓み変形しやすいことか
ら、床６への貼付作業を容易に行うことができる。ま
た、床材１は、温度や湿度の変化により伸縮しやすい特
性を有するコルクシート１に、温度や湿度の変化により
伸縮しにくい伸縮防止シート３が貼着されていることか
ら、床６の所定領域に貼り付けられた後にも、温度や湿
度の変化でコルクシート２が伸縮することがない。した
がって、床材１が床６に貼り付けられた後に、伸縮によ
り剥がれることを防止することができる。The flooring material 1 thus formed is attached to the floor 6 via the adhesive 5 on the other surface side of the expansion / contraction preventing sheet 3. At this time, since the floor material 1 is easily bent and deformed, it is possible to easily attach the floor material 1 to the floor 6. Further, since the flooring material 1 has the cork sheet 1 which has the property of easily expanding and contracting due to changes in temperature and humidity, the expansion and contraction preventing sheet 3 which does not easily expand and contract due to changes in temperature and humidity is attached, so Even after being attached to the area, the cork sheet 2 does not expand or contract due to changes in temperature and humidity. Therefore, it is possible to prevent the floor material 1 from being peeled off due to expansion and contraction after being attached to the floor 6.
【００１８】また、本発明の前提となる床材としては、
図２に示すようなものもある。なお、上述した床材１と
同一の部材については、同一の符号を付してその詳細は
省略する。この床材１０は、コルクシート２に接着剤４
を介して伸縮防止シート３を貼着し、コルクシート２の
表面に、コルクシート２の表面を保護する保護シート１
１が接着剤１２を介して貼着されてなる。この保護シー
ト１１は、床材１０の表面を構成するものであり、コル
クシート２の見栄えを害さないように透明又は半透明の
シート材が用いられ、例えば可撓性を有する合成樹脂製
のシート材が用いられる。Further, as the floor material which is the premise of the present invention,
There is also one as shown in FIG. In addition, about the member same as the floor material 1 mentioned above, the same code | symbol is attached | subjected and the detail is abbreviate | omitted. The floor material 10 includes a cork sheet 2 and an adhesive 4
Protective sheet 1 for sticking a stretch-prevention sheet 3 on the surface of the cork sheet 2 to protect the surface of the cork sheet 2
1 is attached via an adhesive 12. The protective sheet 11 constitutes the surface of the flooring material 10, and a transparent or translucent sheet material is used so as not to impair the appearance of the cork sheet 2, and for example, a flexible synthetic resin sheet. Wood is used.
【００１９】すなわち、コルクシート２は、コルク材に
より形成されていることから、脆弱である。そこで、床
材１０は、コルクシート２の表面に保護シート１１を貼
着することで、コルクシート２の保護を図っている。そ
して、コルクシート２と伸縮防止シート３と保護シート
１１とから構成された床材１０は、伸縮防止シート３の
他方の面が接着剤５により床６の所定領域に貼着され
る。That is, the cork sheet 2 is fragile because it is made of cork material. Therefore, the floor material 10 protects the cork sheet 2 by attaching the protective sheet 11 to the surface of the cork sheet 2. Then, the floor material 10 composed of the cork sheet 2, the expansion / contraction preventing sheet 3, and the protective sheet 11 has the other surface of the expansion / contraction preventing sheet 3 adhered to a predetermined area of the floor 6 with the adhesive 5.
【００２０】更に、本発明の前提となる床材としては、
図３に示すようなものもある。なお、上述した床材１と
同一の部材については、同一の符号を付してその詳細は
省略する。この床材２０は、コルクシート２と、コルク
シート２の裏面側に貼着される伸縮防止シート３と、伸
縮防止シート３のコルクシート２の貼付面と対向する面
側に貼着される衝撃を緩衝する緩衝シート２１とを備え
る。すなわち、この床材２０は、伸縮防止シート３の一
方の面側にコルクシート２を貼着し、他方の面側に緩衝
シート２１を貼着したことを特徴とする。Furthermore, the flooring material on which the present invention is based includes
There is also one as shown in FIG. In addition, about the member same as the floor material 1 mentioned above, the same code | symbol is attached | subjected and the detail is abbreviate | omitted. This floor material 20 is a cork sheet 2, an expansion / contraction preventing sheet 3 attached to the back surface side of the cork sheet 2, and an impact applied to the surface side of the expansion / contraction preventing sheet 3 opposite to the attaching surface of the cork sheet 2. And a cushioning sheet 21 for cushioning. That is, this flooring 20 is characterized in that the cork sheet 2 is attached to one surface side of the expansion / contraction preventing sheet 3 and the buffer sheet 21 is attached to the other surface side thereof.
【００２１】緩衝シート２１は、衝撃吸収性に優れた材
料により形成され、例えばコルク材とゴム材を混合し、
ポリウレタン系の接着剤で固化したシート材が用いられ
る。そして、伸縮防止シート３には、一方の面に、接着
剤２２を介して床材２０の表面を構成するコルクシート
２が貼着され、他方の面に、接着剤２３を介して緩衝シ
ート２１が貼着される。床材２０は、緩衝シート２１の
他方の面が接着剤２４により床の所定領域に貼着され
る。以上のように構成された床材２０は、コルクシート
２と緩衝シート２１との間に伸縮防止シート３が介在さ
れていることから、コルクシート２と緩衝シート２１の
両方の伸縮を防止することができる。したがって、温度
や湿度の変化があっても、床材２０が床６から剥がれる
ことを防止することができる。The cushioning sheet 21 is made of a material having a good shock absorbing property, and, for example, a cork material and a rubber material are mixed,
A sheet material solidified with a polyurethane adhesive is used. The stretch prevention sheet 3 has one surface on which the cork sheet 2 constituting the surface of the flooring material 20 is attached via the adhesive 22, and on the other surface, the buffer sheet 21 via the adhesive 23. Is attached. The floor material 20 has the other surface of the cushioning sheet 21 adhered to a predetermined area of the floor with an adhesive 24. In the flooring material 20 configured as described above, since the expansion / contraction preventing sheet 3 is interposed between the cork sheet 2 and the cushioning sheet 21, both the cork sheet 2 and the cushioning sheet 21 are prevented from expanding and contracting. You can Therefore, even if there is a change in temperature or humidity, the flooring material 20 can be prevented from peeling off from the floor 6.
【００２２】そこで、本発明が適用された床材は、図４
に示すように形成される。なお、上述した床材２０と同
一の部材については、同一の符号を付してその詳細は省
略する。この床材３０は、コルクシート２の一方の面側
に、接着剤３２を介して保護シート３１を貼着したこと
を特徴とする。この保護シート３１は、上述した床材１
０の保護シート１１と同様な機能を有するものであり、
コルクシート２の見栄えを害さないように透明又は半透
明のシート材が用いられ、例えば可撓性を有する合成樹
脂製のシート材により形成されている。床材３０は、脆
弱なコルクシート２の表面に保護シート３１を貼着する
ことで、コルクシート２の保護を図っている。そして、
床材３０は、緩衝シート２１の他方の面が接着剤２４を
介して床６の所定領域に貼着される。Therefore, the floor material to which the present invention is applied is shown in FIG.
Is formed as shown in FIG. The same members as those of the floor material 20 described above are designated by the same reference numerals, and the details thereof will be omitted. The floor material 30 is characterized in that a protective sheet 31 is attached to one surface side of the cork sheet 2 via an adhesive 32. The protective sheet 31 is the floor material 1 described above.
0 has the same function as the protective sheet 11 of
A transparent or translucent sheet material is used so as not to impair the appearance of the cork sheet 2, and is formed of, for example, a flexible synthetic resin sheet material. The floor material 30 protects the cork sheet 2 by attaching a protective sheet 31 to the surface of the fragile cork sheet 2. And
The floor material 30 is attached to a predetermined area of the floor 6 via the adhesive 24 on the other surface of the cushioning sheet 21.
【００２３】また、この床材３０は、伸縮防止シート３
の他方の面側に緩衝シート２１が貼着されている。この
緩衝シート２１は、衝撃吸収性に優れた材料により形成
され、例えばコルク材とゴム材を混合し、ポリウレタン
系の接着剤で固化したシート材が用いられる。そして、
伸縮防止シート３には、他方の面に、接着剤２３を介し
て緩衝シート２１が貼着されている。床材３０は、緩衝
シート２１の他方の面が接着剤２４により床の所定領域
に貼着される。以上のように構成された床材３０は、コ
ルクシート２と緩衝シート２１との間に伸縮防止シート
３が介在されていることから、コルクシート２と緩衝シ
ート２１の両方の伸縮を防止することができる。したが
って、温度や湿度の変化があっても、床材３０が床６か
ら剥がれることを防止することができる。The floor material 30 is made up of the expansion and contraction prevention sheet 3
The buffer sheet 21 is attached to the other surface side of the. The cushioning sheet 21 is formed of a material having excellent shock absorbing properties, and for example, a sheet material obtained by mixing a cork material and a rubber material and solidifying with a polyurethane adhesive is used. And
A buffer sheet 21 is attached to the other surface of the stretch-preventing sheet 3 via an adhesive 23. The floor material 30 has the other surface of the cushioning sheet 21 attached to a predetermined area of the floor with an adhesive 24. In the flooring material 30 configured as described above, since the expansion / contraction preventing sheet 3 is interposed between the cork sheet 2 and the buffer sheet 21, both the cork sheet 2 and the buffer sheet 21 are prevented from expanding and contracting. You can Therefore, even if there is a change in temperature or humidity, the floor material 30 can be prevented from peeling off from the floor 6.
【００２４】以上詳述した本発明が適用された床材３０
は、コルクシート２と伸縮防止シート３とを組み合わせ
ることで、温度や環境の変化による伸縮することを防止
することができる。この点、本発明が適用された床材の
温度及び湿度の変化に伴う伸び率について、以下の実験
により確認した。この実験で用いた本発明が適用された
床材４０は、図５に示すように、コルクシート４１の上
層に接着剤４５を介して保護シート４２を貼着し、下層
に接着剤４６を介して緩衝シート４３を貼着し、この緩
衝シート４３の下層に接着剤４７を介して伸縮防止シー
ト４４を貼着したものである。ここで、コルクシート４
１の厚さは２．０ｍｍであり、保護シート４２の厚さは
０．５ｍｍであり、緩衝シート４３の厚さは２．５ｍｍ
であり、伸縮防止シート４４の厚さは０．２ｍｍであ
る。また、比較例として、厚さ５．０ｍｍのコルクシー
トのみからなる床材を用いた。Floor material 30 to which the present invention detailed above is applied.
By combining the cork sheet 2 and the expansion / contraction preventing sheet 3, expansion and contraction due to changes in temperature and environment can be prevented. In this regard, the elongation rate of the flooring material to which the present invention was applied due to changes in temperature and humidity was confirmed by the following experiments. As shown in FIG. 5, the flooring material 40 to which the present invention is applied, which is used in this experiment, has the protective sheet 42 attached to the upper layer of the cork sheet 41 via the adhesive 45 and the adhesive layer 46 to the lower layer. The cushioning sheet 43 is adhered thereto, and the expansion / contraction preventing sheet 44 is adhered to the lower layer of the cushioning sheet 43 via the adhesive 47. Here, cork sheet 4
1 has a thickness of 2.0 mm, the protective sheet 42 has a thickness of 0.5 mm, and the buffer sheet 43 has a thickness of 2.5 mm.
The thickness of the stretch prevention sheet 44 is 0.2 mm. In addition, as a comparative example, a flooring material made of only a cork sheet having a thickness of 5.0 mm was used.
【００２５】床材４０とコルクシートの温度変化特性を
調べる実験では、チャンバ内を湿度６５％で一定にし、
温度が５，１５，２５，３５，４５，５５℃のときの床
材４０とコルクシートの伸び率を測定した。また、床材
４０とコルクシートの湿度変化特性を調べる実験では、
温度を２５℃で一定にし、湿度が３０，５０，７０，９
０％のときの床材４０とコルクシートの伸び率を測定し
た。ここで、温度変化特性に関する実験結果を図６に示
し、湿度変化特性に関する実験結果を図７に示す。In an experiment for examining the temperature change characteristics of the floor material 40 and the cork sheet, the inside of the chamber was kept constant at a humidity of 65%,
The elongation rates of the floor material 40 and the cork sheet at the temperatures of 5, 15, 25, 35, 45 and 55 ° C were measured. In addition, in the experiment for examining the humidity change characteristics of the floor material 40 and the cork sheet,
The temperature is kept constant at 25 ° C and the humidity is 30, 50, 70, 9
The elongation of the floor material 40 and the cork sheet at 0% was measured. Here, the experimental result regarding the temperature change characteristic is shown in FIG. 6, and the experimental result regarding the humidity change characteristic is shown in FIG.
【００２６】図６に示すように、床材４０は、温度が上
昇しても比較例であるコルクシートより伸び率が小さい
ことが分かる。また、図７に示すように、床材４０は、
湿度が上昇しても比較例であるコルクシートより伸び率
が小さいことが分かる。すなわち、本発明が適用された
床材４０のように、伸縮防止シート４４をコルクシート
４１に貼り付けることで、コルクシート４１の温度や湿
度の変化に伴う伸縮を防止することができることが分か
る。As shown in FIG. 6, it can be seen that the flooring material 40 has a smaller elongation than the cork sheet of the comparative example even when the temperature rises. Further, as shown in FIG. 7, the floor material 40 is
It can be seen that even if the humidity rises, the elongation rate is smaller than that of the cork sheet which is the comparative example. That is, it can be seen that by attaching the expansion / contraction preventing sheet 44 to the cork sheet 41 like the flooring material 40 to which the present invention is applied, it is possible to prevent the expansion / contraction of the cork sheet 41 due to changes in temperature and humidity.
【００２７】ところで、以上のような本発明が適用され
た床材は次のように製造することができる。以下、上述
した床材１の製造方法を例に取り説明する。床材１は、
図８に示すように、コルクシート２と伸縮防止シート３
とをプレスすることにより形成することができる。すな
わち、図８（Ａ）に示すように、伸縮防止シート３が対
向配置された接着剤塗布ローラ５１と回転ローラ５２と
の間を図８中矢印Ｄ１方向に走行される。接着剤塗布ロ
ーラ５１と回転ローラ５２とは、伸縮防止シート３の送
り方向である図８中矢印Ｒ１方向に回転されている。そ
して、接着剤塗布ローラ５１には、接着剤供給部５３よ
り順次接着剤４が供給され、伸縮防止シート３には、こ
の接着剤４が接着剤塗布ローラ５１が回転することで、
伸縮防止シート３に転写される。By the way, the flooring material to which the present invention as described above is applied can be manufactured as follows. Hereinafter, the manufacturing method of the floor material 1 described above will be described as an example. Floor material 1 is
As shown in FIG. 8, the cork sheet 2 and the stretch prevention sheet 3
It can be formed by pressing and. That is, as shown in FIG. 8 (A), the expansion / contraction preventing sheet 3 travels in the direction of arrow D1 in FIG. The adhesive application roller 51 and the rotation roller 52 are rotated in the direction of the arrow R1 in FIG. Then, the adhesive 4 is sequentially supplied to the adhesive applying roller 51 from the adhesive supplying portion 53, and the adhesive applying roller 51 rotates the adhesive applying roller 51 to the expansion / contraction preventing sheet 3.
It is transferred to the stretch prevention sheet 3.
【００２８】次いで、伸縮防止シート４の接着剤４が塗
布された面には、図８（Ｂ）に示すように、コルクシー
ト２が貼り合わされる。次いで、図８（Ｃ）に示すよう
に、コルクシート２と伸縮防止シート３とは、プレスさ
れる。すなわち、コルクシート２と伸縮防止シート３と
をプレスするプレス金型５４は、上金型５４ａと下金型
５４ｂとを備え、コルクシート２と伸縮防止シート３と
は、上金型５４ａと下金型５４ｂとが互いに近接する方
向に移動することで、所定時間、所定の圧力で全面が圧
接される。具体的に、プレス金型５４は、１０Ｋｇ／ｃ
ｍ２の圧力でコルクシート２と伸縮防止シート３とをプ
レスする。また、プレス時間は、例えば６時間、１２時
間、２４時間であり、用いられる接着剤４の特性に応じ
て定められる。そして、互いに貼り合わされプレス加工
されたコルクシート２と伸縮防止シート３とは、図８
（Ｄ）に示すように、乾燥装置５５に搬送され、４０℃
〜５０℃の環境で乾燥され安定化される。Next, as shown in FIG. 8B, the cork sheet 2 is attached to the surface of the expansion / contraction preventing sheet 4 to which the adhesive 4 is applied. Next, as shown in FIG. 8C, the cork sheet 2 and the stretch prevention sheet 3 are pressed. That is, the press die 54 that presses the cork sheet 2 and the stretch prevention sheet 3 includes an upper die 54a and a lower die 54b, and the cork sheet 2 and the stretch prevention sheet 3 have the upper die 54a and the lower die 54a. The mold 54b and the mold 54b move toward each other, so that the entire surface is pressed with a predetermined pressure for a predetermined time. Specifically, the press die 54 is 10 kg / c
The cork sheet 2 and the stretch prevention sheet 3 are pressed with a pressure of m 2 . The pressing time is, for example, 6 hours, 12 hours, and 24 hours, and is determined according to the characteristics of the adhesive 4 used. Then, the cork sheet 2 and the stretch-prevention sheet 3 which are attached to each other and pressed are shown in FIG.
As shown in (D), it is conveyed to the drying device 55 and 40 ° C.
It is dried and stabilized in an environment of ~ 50 ° C.
【００２９】以上の工程を経て、床材１は形成される。
このようなプレス金型５４を用いた製造方法では、図８
（Ｂ）に示す工程で貼り合わされたコルクシート２と伸
縮防止シート３とが、図８（Ｃ）において、プレス金型
５４がコルクシート２と伸縮防止シート３の主面に対し
て直交する方向から圧力を加えることから、プレス時に
コルクシート２と伸縮防止シート３との貼り合わせ位置
がずれることを防止することができる。The flooring 1 is formed through the above steps.
In the manufacturing method using such a press die 54, as shown in FIG.
The cork sheet 2 and the expansion / contraction prevention sheet 3 which are bonded together in the step shown in FIG. 8 (B) have a direction in which the press die 54 is orthogonal to the main surfaces of the cork sheet 2 and the expansion / contraction prevention sheet 3 in FIG. 8 (C). Since the pressure is applied from the above, it is possible to prevent the bonding positions of the cork sheet 2 and the expansion-contraction preventing sheet 3 from being displaced during pressing.
【００３０】ところで、コルクシート２は、多孔質であ
ることから、圧接ローラを用いてコルクシート２に伸縮
防止シート３を圧着するときには、空気を巻き込み、こ
のためコルクシート２と伸縮防止シート３との貼り合わ
せ位置がずれてしまうことがある。そこで、床材１は、
図９に示すように、伸縮防止シート３の熱可塑性樹脂を
溶融し、次いでプレス金型によりプレスすることでコル
クシート２と伸縮防止シート３とを貼り合わせて形成さ
れる。すなわち、コルクシート２は、水平方向に図９中
矢印Ｄ２方向に順次走行され、伸縮防止シート３は、コ
ルクシート２の上側を、回転ローラ６２が伸縮防止シー
ト３の送り方向である図９中矢印Ｒ２方向に回転される
ことで、コルクシート２と平行に図９中矢印Ｄ３方向に
走行されている。そして、伸縮防止シート３は、熱可塑
性接着剤４が塗布され、この熱可塑性接着剤４は、加熱
機構６４により１００℃〜１２０℃に加熱され、溶融さ
れる。そして、更に、伸縮防止シート３は、図９中矢印
Ｄ３方向に走行されると、加熱機構６４により加熱され
ることで熱可塑性接着剤４の溶融状態が保持され、更に
図９中矢印Ｄ３方向に走行されると、ガイドローラ６５
によりガイドされ、溶融面側がコルクシート２と近接し
た状態でコルクシート２と同方向に走行される。By the way, since the cork sheet 2 is porous, when the expansion prevention sheet 3 is pressure-bonded to the cork sheet 2 by using a pressure contact roller, air is entrained, and therefore the cork sheet 2 and the expansion prevention sheet 3 are combined. The bonding position of may be misaligned. Therefore, the floor material 1 is
As shown in FIG. 9, the thermoplastic resin of the stretch-prevention sheet 3 is melted and then pressed by a press die to bond the cork sheet 2 and the stretch-prevention sheet 3 to each other. That is, the cork sheet 2 is sequentially run horizontally in the direction of arrow D2 in FIG. 9, the expansion / contraction preventing sheet 3 is above the cork sheet 2, and the rotation roller 62 is the feeding direction of the expansion / contraction preventing sheet 3 in FIG. By being rotated in the direction of arrow R2, the vehicle is running parallel to the cork sheet 2 in the direction of arrow D3 in FIG. Then, the stretch prevention sheet 3 is coated with the thermoplastic adhesive 4, and the thermoplastic adhesive 4 is heated to 100 ° C. to 120 ° C. by the heating mechanism 64 and melted. Further, when the stretch-preventing sheet 3 travels in the direction of arrow D3 in FIG. 9, it is heated by the heating mechanism 64 to maintain the molten state of the thermoplastic adhesive 4, and further in the direction of arrow D3 in FIG. Guide roller 65 when driven to
The corrugated sheet 2 is guided in the same direction and is run in the same direction as the cork sheet 2 with the melting surface side being close to the cork sheet 2.
【００３１】この状態で、コルクシート２と伸縮防止シ
ート３とは、プレスされる。すなわち、コルクシート２
と伸縮防止シート３とをプレスするプレス金型６６は、
上金型６６ａと下金型６６ｂとを備え、コルクシート２
と伸縮防止シート３とは、上金型６６ａと下金型６６ｂ
とが互いに近接する方向に移動することで、所定時間、
所定の圧力で圧接される。具体的に、プレス金型６６
は、１０Ｋｇ／ｃｍ２の圧力でコルクシート２と伸縮防
止シート３の全面をプレスする。また、プレス時間は、
用いられる接着剤４の特性に応じて定められる。そし
て、互いに貼り合わされプレス加工されたコルクシート
２と伸縮防止シート３とは、冷却機構６７により冷却さ
れ溶融された熱可塑性接着剤４が硬化され、床材１は形
成される。In this state, the cork sheet 2 and the expansion / contraction preventing sheet 3 are pressed. That is, cork sheet 2
The press die 66 for pressing the expansion prevention sheet 3 and
A cork sheet 2 including an upper mold 66a and a lower mold 66b.
The expansion and contraction prevention sheet 3 is composed of an upper mold 66a and a lower mold 66b.
By moving and in the direction of approaching each other,
It is pressed at a predetermined pressure. Specifically, press die 66
Is to press the entire surfaces of the cork sheet 2 and the stretch prevention sheet 3 with a pressure of 10 Kg / cm 2 . Also, the press time is
It is determined according to the characteristics of the adhesive 4 used. Then, the cork sheet 2 and the stretch-preventing sheet 3 which are pasted together and pressed are cured by the thermoplastic adhesive 4 that is cooled and melted by the cooling mechanism 67, and the flooring 1 is formed.
【００３２】以上のように図９に示す製造工程によれ
ば、プレス金型６６がコルクシート２と伸縮防止シート
３の主面に対して直交する方向から圧力を加えることか
ら、圧接ローラを用いてコルクシート２と伸縮防止シー
ト３とを圧接する場合と異なり、プレス時にコルクシー
ト２と伸縮防止シート３との貼り合わせ位置がずれるこ
とを防止することができる。また、走行する伸縮防止シ
ート３とコルクシート２とを連続的に接着することがで
きることから、容易に床材１を製造することができる。As described above, according to the manufacturing process shown in FIG. 9, since the press die 66 applies pressure from the direction orthogonal to the main surfaces of the cork sheet 2 and the expansion / contraction preventing sheet 3, the pressure roller is used. Unlike the case where the cork sheet 2 and the expansion / contraction prevention sheet 3 are pressed against each other, it is possible to prevent the position where the cork sheet 2 and the expansion / contraction prevention sheet 3 are bonded from deviating during pressing. Further, since the running stretch-preventing sheet 3 and the cork sheet 2 can be continuously adhered to each other, the flooring 1 can be easily manufactured.
【００３３】なお、上述した本発明を適用した床材３
０，４０のように複数のシートを重畳するときには、予
め重畳されるシートを貼り合わせた後、一度のプレスで
重畳されたシートが接着固定される。The floor material 3 to which the present invention described above is applied.
When a plurality of sheets such as 0 and 40 are superposed, the superposed sheets are pasted and then the superposed sheets are bonded and fixed by one press.
【００３４】[0034]
【発明の効果】本発明に係る床材によれば、伸縮防止シ
ートは、ガラス繊維が全体の７０ｗｔ％を占めることか
ら、伸縮しにくく、撓み変形しやすい。したがって、こ
れを用いた床材は、温度や湿度変化によっても、コルク
シートが伸縮することによって、床より剥がれることを
防止することができる。また、床材は、コルクシートに
伸縮防止シートを容易に貼着することができる。また、
床材は、ロール状に巻いて持ち運びがし易くなる。更
に、この伸縮防止シートによって、コルク材とゴム材と
を混合した緩衝シートの伸縮も防止することができる。
緩衝シートは、コルク材とゴム材とを混合してなること
から、衝撃を吸収することができる。更に、床材の表面
を保護シートで構成することで、脆弱なコルクシートの
表面を保護することができる。According to the flooring material of the present invention, since the stretch-preventing sheet contains 70 wt% of the entire glass fiber, it is difficult to stretch and flexibly deform. Therefore, the flooring material using this can be prevented from peeling off the floor due to the expansion and contraction of the cork sheet even when the temperature or humidity changes. Moreover, as for the flooring material, the stretch prevention sheet can be easily attached to the cork sheet. Also,
The flooring material is wound in a roll shape to facilitate portability. Furthermore, the expansion / contraction sheet can prevent expansion / contraction of the buffer sheet in which the cork material and the rubber material are mixed.
Since the cushioning sheet is made of a mixture of cork material and rubber material, it can absorb impact. Furthermore, by constructing the surface of the flooring material with a protective sheet, the surface of the fragile cork sheet can be protected.
【００３５】また、本発明に係る床材によれば、この床
材は、コルクシートと緩衝シートとの間に伸縮防止シー
トが介在されていることから、伸縮防止シートの機能が
コルクシートと緩衝シートに作用し、コルクシートと緩
衝シートの伸縮を防止することができる。また、床材の
表面を保護シートとすることで、脆弱なコルクシートの
表面を保護することができる。Further, according to the flooring material of the present invention, since the expansion / contraction preventing sheet is interposed between the cork sheet and the cushioning sheet, the functioning of the expansion / contraction preventing sheet is that of the cork sheet and the cushioning sheet. It acts on the seat and can prevent the cork seat and the cushion seat from expanding and contracting. Further, by using the surface of the floor material as the protective sheet, the surface of the fragile cork sheet can be protected.
【図１】本発明の前提となる床材の断面図である。FIG. 1 is a cross-sectional view of a floor material that is a premise of the present invention.
【図２】図１に示した床材の表面に保護シートを取り付
けた例を示す断面図である。FIG. 2 is a cross-sectional view showing an example in which a protective sheet is attached to the surface of the floor material shown in FIG.
【図３】図１に示した床材に緩衝シートを介在させた例
を示す断面図である。FIG. 3 is a cross-sectional view showing an example in which a cushioning sheet is interposed in the floor material shown in FIG.
【図４】本発明が適用された床材の断面図である。FIG. 4 is a sectional view of a flooring material to which the present invention is applied.
【図５】伸縮防止シートを用いた床材の伸縮特性を測定
する実験に用いた本発明が適用された床材の断面図であ
る。FIG. 5 is a cross-sectional view of a flooring material to which the present invention is applied, which is used in an experiment for measuring the stretching property of a flooring material using a stretch-preventing sheet.
【図６】温度に対する床材の伸縮特性を示す特性図であ
る。FIG. 6 is a characteristic diagram showing expansion / contraction characteristics of a floor material with respect to temperature.
【図７】湿度に対する床材の伸縮特性を示す特性図であ
る。FIG. 7 is a characteristic diagram showing expansion and contraction characteristics of a floor material with respect to humidity.
【図８】プレス金型を用いたコルクシートと伸縮防止シ
ートとを貼り合わせる工程を説明する図である。FIG. 8 is a diagram illustrating a step of bonding a cork sheet and a stretch prevention sheet using a press die.
【図９】プレス金型とホットメルト接着とを用いてコル
クシートと伸縮防止シートとを貼り合わせる工程を説明
する図である。FIG. 9 is a diagram illustrating a step of bonding a cork sheet and a stretch prevention sheet by using a press die and hot melt bonding.
３０，４０ 床材、２ コルクシート、３ 伸縮防止シ
ート、４，５ 接着剤、６ 床、１１ 保護シート、２
１ 緩衝シート30,40 Floor materials, 2 Cork sheets, 3 Stretch prevention sheets, 4,5 Adhesives, 6 floors, 11 Protective sheets, 2
1 buffer sheet
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭57−180745（ＪＰ，Ａ) 特開2000−25015（ＪＰ，Ａ) 実開 平２−60152（ＪＰ，Ｕ) 実開 平１−80328（ＪＰ，Ｕ) ─────────────────────────────────────────────────── ─── Continued front page (56) Reference JP-A-57-180745 (JP, A) JP 2000-25015 (JP, A) Actual Kaihei 2-60152 (JP, U) Actual Kaihei 1-80328 (JP, U)
Claims (2)
コルク材を合成樹脂と混合して形成したシート材からな
るコルクシートと、 上記コルクシートの裏面に貼着されるコルク材とゴム材
とを混合した緩衝シートと、 経糸及び緯糸にガラス繊維を用いたガラスシートに、ガ
ラス繊維が全体の７０ｗｔ％となるように熱可塑性樹脂
を含浸させてなり、撓み変形をし、上記緩衝シートの上
記コルクシートが貼着されない側の面に熱可塑性接着剤
によって貼着されて上記コルクシートの伸縮を防止する
伸縮防止シートと、 上記コルクシートの表面に貼着されて床材の表面を構成
する透明又は半透明の可撓性を有する保護シートとを備
え、上記伸縮防止シートは、引張り強度が８５Ｋｇｆ／ｍｍ
２ 、引張り弾性率が３，８００Ｋｇｆ／ｍｍ ２ 、伸び率
が２．２％、曲げ強さが９０Ｋｇｆ／ｍｍ ２ 、曲げ弾性
係数が３，５００Ｋｇｆ／ｍｍ ２ 、線膨張係数が５×１
０ −６ ／℃である 床材。1. A cork sheet made of a sheet material made of cork material or a sheet material formed by mixing crushed cork material with a synthetic resin, and a cork material and a rubber material attached to the back surface of the cork sheet. mixed with the buffer sheet, a glass sheet using a glass fiber warp and weft, moth
A thermoplastic resin is impregnated with a thermoplastic resin so that the lath fibers make up 70 wt% of the whole, and is deformed flexibly, and a thermoplastic adhesive is applied to the surface of the buffer sheet on which the cork sheet is not attached.
It is adhered a protective sheet having a stretch preventing sheet for preventing expansion and contraction of the cork sheet, a transparent or translucent flexible constituting the surface of the adhered on the surface of the cork sheet flooring by The stretch prevention sheet has a tensile strength of 85 kgf / mm.
2 , tensile elastic modulus is 3,800 Kgf / mm 2 , elongation rate
Is 2.2%, bending strength is 90 Kgf / mm 2 , bending elasticity
Coefficient is 3,500 Kgf / mm 2 , linear expansion coefficient is 5 × 1
Flooring is 0 -6 / ° C..
コルク材を合成樹脂と混合して形成したシート材からな
るコルクシートと、 上記コルクシートに貼着されて床材の表面を構成する透
明又は半透明の可撓性を有する保護シートと、 経糸及び緯糸にガラス繊維を用いたガラスシートに、ガ
ラス繊維が全体の７０ｗｔ％となるように熱可塑性樹脂
を含浸させてなり、撓み変形をし、一方の面が上記コル
クシートの上記保護シートが貼着されない面に熱可塑性
接着剤によって貼着されて上記コルクシートの伸縮を防
止する伸縮防止シートと、 上記伸縮防止シートの他方の面に熱可塑性接着剤によっ
て貼着されるコルク材とゴム材とを混合した緩衝シート
とを備え、上記伸縮防止シートは、引張り強度が８５Ｋｇｆ／ｍｍ
２ 、引張り弾性率が３，８００Ｋｇｆ／ｍｍ ２ 、伸び率
が２．２％、曲げ強さが９０Ｋｇｆ／ｍｍ ２ 、曲げ弾性
係数が３，５００Ｋｇｆ／ｍｍ ２ 、線膨張係数が５×１
０ −６ ／℃である 床材。2. A cork sheet made of a sheet material made of cork material or a sheet material formed by mixing crushed cork material with a synthetic resin, and transparent or affixed to the cork sheet to form a surface of a floor material. a protective sheet having a translucent flexible, the glass sheet using a glass fiber warp and weft, moth
It is made by impregnating a thermoplastic resin so that the lath fibers make up 70 wt% of the whole, and is deformed flexibly, and one surface is thermoplastic with the surface of the cork sheet to which the protective sheet is not attached.
A stretch prevention sheet is adhered by the adhesive to prevent the expansion and contraction of the cork sheet, depending on the thermoplastic adhesive to the other surface of the stretchable prevention sheet
And a buffer sheet of a mixture of cork and rubber material is bonded Te, the stretch preventing sheet, the tensile strength of 85 kgf / mm
2 , tensile elastic modulus is 3,800 Kgf / mm 2 , elongation rate
Is 2.2%, bending strength is 90 Kgf / mm 2 , bending elasticity
Coefficient is 3,500 Kgf / mm 2 , linear expansion coefficient is 5 × 1
Flooring is 0 -6 / ° C..