JP4193663B2 - Method of joining metal members - Google Patents

Description

  The present invention relates to a method for joining metal members, and more particularly, to a joining method for joining two metal members with an adhesive interposed in an overlapping portion of two metal members.

  Conventionally, as a joining method for joining two metal members, a method of joining at least a part of each other and locally joining the overlapped part by spot welding or caulking joining has been widely used. For example, in Patent Document 1, as a kind of caulking joining method, plastic deformation at the time of pressurization is promoted by energizing and softening a caulking portion such as a protrusion inserted into a hole of a counterpart material. Thus, a so-called energizing caulking method that obtains higher bonding strength is disclosed.

  Further, in recent years, as such a local joining method, a light metal such as aluminum (Al), magnesium (Mg), or an alloy thereof is used as a target and rotated with respect to a predetermined portion of an overlapping portion of two metal members. There is known a “method using a rotary tool” in which frictional heat is generated by pushing a tool while rotating it to cause plastic flow at the predetermined location, and both metal members are joined at the predetermined location. Yes. According to such a method, the required joining strength can be obtained relatively easily and reliably by controlling the amount of pushing of the rotary tool, the holding time after pushing, and the deformation of the metal member is further suppressed. be able to.

  By the way, there are a lot of car body constituent members configured by combining a plurality of metal members. When manufacturing such car body constituent members, various joining methods as described above are applied. Yes. For example, as a door inner member of an automobile, a portion where a door hinge mounting portion or a door lock mounting portion is provided is formed by die casting such as Al or an alloy thereof, and these light metal casting members are spanned by, for example, extruded light metal members. What was joined and comprised is known. By adopting such a configuration, only a portion where high strength and rigidity are required and the shape is complicated can be formed by casting, and the other portion can be formed by a lighter extruded product. Compared to the case of casting, the entire weight of the inner member can be reduced.

In the case of joining a cast member and an extruded member with such a door inner member, generally, the various local joining methods described above can be applied, but instead of this, or in addition to this, If a bonding method using an adhesive is applied, bonding can be obtained over substantially the entire area of the overlapped portion, so that a more uniform and high-strength bonding can be obtained as compared to the local bonding method.
In such an adhesion method, in particular, a thermosetting adhesive is applied, an adhesive is interposed between the overlapping parts of both metal members, and then heated to a predetermined temperature range to obtain a high-strength joint. It is done.
Japanese Patent Laid-Open No. 11-77192

  When joining using the thermosetting adhesive as described above, after applying the adhesive and pasting the overlapping parts of both metal members, until the transition to the heating process, in the intermediate process Due to the external force being applied to the bonded part during handling or loading into the heating device, etc., there will be a position shift (position shift along the bonding surface or in the peeling direction) at the overlapping part, and after heat curing There is a possibility that a problem such as a decrease in the adhesive strength may occur.

  Therefore, even if the adhesive is applied, temporary bonding (temporary fixing) is necessary to fix the overlapping portion of both metal members until the main bonding by heating is performed. Also for this temporary joining, when the joining strength is low, it is necessary to set as many joining locations as possible, and there is a possibility that the metal member is excessively deformed.

  In view of this, the present invention is to ensure that temporary joining can be performed while suppressing deformation of the metal member when joining the two metal members with an adhesive interposed between the overlapping portions of the two metal members. The purpose of the present invention is to prevent the occurrence of problems due to the misalignment of the overlapping portions of the two metal members at fewer temporary joint locations by increasing the temporary joint strength.

For this reason, the joining method according to the first invention of the present application is a joining method in which two metal members are joined to each other by interposing an adhesive agent on an overlapping portion of two metal members which are vehicle body constituting members. A first metal member made of a light metal member provided with a protruding portion at a predetermined position of the overlapping portion, and a second metal member formed with a through hole for fitting the protruding portion into the predetermined portion of the overlapping portion . in the overlapping portions, a step of interposing a thermosetting adhesive, the (b) said predetermined position of the through hole in the projections fit was inserted superposed above were superimposed portion, by rotating the rotary tool while pressing, by Rukoto it is plastically deformed the protrusions cause plastic flow at the predetermined position by generating frictional heat, thereby joining the portions superposed the above predetermined position, thermosetting of the predetermined portion near Glue on top (C) a step of curing the uncured thermosetting adhesive in the drying step after painting of the vehicle body constituent member after the step of temporary fixing and bonding, and the step of bonding temporarily cured by frictional heat; It is characterized by having.

The second aspect of the present invention, in the first shot bright, a inner member of said vehicle body structure member of an automobile door, the first metal member, the door hinge mounting portion and / or the door lock installation section is provided It is a light metal casting member.

According to the first invention of the present application, when the two metal members are joined to each other with the adhesive interposed in the overlapping portion of the two metal members that are the vehicle body constituting members, the first metal member and the second metal member are overlapped. A thermosetting adhesive is interposed in the part, and the rotary tool is pushed into the predetermined part of the overlapping part while rotating to generate frictional heat to cause plastic flow in the predetermined part. While joining the overlapped portion, the thermosetting adhesive in the vicinity of the predetermined location is cured by the frictional heat and temporarily bonded, so that not only the bonding force by plastically deforming the predetermined location, but also to this In addition, since a bonding force (adhesive force) by curing a thermosetting adhesive in the vicinity of a predetermined location is also obtained, it is possible to securely fix and bond the metal member while suppressing deformation of the metal member. It is possible to prevent problems caused by positional deviation of I mating portion.
In this case, the required bonding strength can be obtained relatively easily and reliably by controlling the amount of pushing of the rotating tool and the holding time after pushing, and the deformation of the metal member can be further suppressed. it can.
And, since the uncured thermosetting adhesive is cured in the drying process after painting the vehicle body constituent member after the temporary bonding, the post-process is not required to provide a special process for curing the adhesive. The uncured thermosetting adhesive can be cured using the heating action.
In particular, in a state in which the protrusion provided on the first metal member made of light metal is fitted into the through hole formed in the second metal member, the predetermined portion of the overlapping portion is plastically deformed by plastic deformation of the protrusion. The joining force by deforming can be further increased.

According to the second aspect of the invention, a inner member of said vehicle body structure member of an automobile door, the first metal member is a light-metal cast members door hinge attachment portion and / or the door lock installation section is provided for some cases, basically it is possible to achieve the same effect as the first shot bright above.

Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
FIG. 1 is an explanatory front view of an inner member 1 (door inner) constituting an inner member of an automobile door according to the present embodiment. As shown in this figure, the door inner 1 includes a front member 2 provided with a door hinge mounting portion (not shown), a rear member 3 provided with a door lock mounting portion (not shown), and both the upper and lower portions 2, 3 at the top and bottom. The upper and lower connecting members 4 and 5 are connected to each other, and the base plate 6 is disposed so as to cover a region surrounded by the connecting members 4 and 5 and the front member 2 and the rear member 3. .

  The front member 2 and the rear member 3 are preferably light metal casting members cast by a die casting method using, for example, an aluminum (Al) alloy. The upper and lower connecting members 4 and 5 are preferably formed by an extrusion method using an Al alloy as a material. The base plate 6 is also made of an Al alloy.

  As described above, the casting member, the extrusion-molded product, and the plate member are combined and joined to each other, like the front member 2 provided with a door hinge attaching portion (not shown) and the rear member 3 provided with a door lock attaching portion (not shown). In addition, high strength and rigidity are required, and only the parts with complicated shapes are formed by casting, and the other parts (the connecting members 4, 5 and the berth plate 6) are formed by lighter extruded products and plate materials. It is possible to reduce the overall weight of the door inner 1 as compared with the case where the whole is manufactured by casting.

In the present embodiment, the door inner 1 is assembled by joining the members 2 to 6. However, in this joining, basically, an adhesive (particularly thermosetting) is applied to the overlapping portion of the two members. Both metal members are joined together with an adhesive) interposed therebetween.
In this way, by applying a bonding method using an adhesive, bonding can be obtained over substantially the entire area of the overlapped portion, so that more uniform and high-strength bonding can be obtained as compared with the local bonding method. In particular, by applying a thermosetting adhesive, interposing the adhesive in the overlapping portion of both metal members, and heating to a predetermined temperature range, higher strength bonding can be obtained.

  When manufacturing doors for automobiles, paint is made after assembling the door inner 1 constituting the door inner plate and the door outer (not shown) constituting the door outer plate, and drying is performed after the painting, so the heat at the time of drying is used. Thus, the thermosetting adhesive can be cured and the members of the door inner 1 can be joined.

  However, as described above, after the adhesive is applied and the overlapping portions of the members of the door inner 1 are bonded together, the intermediate process (that is, the outer panel) is performed until the heating process (that is, the drying process) is started. Misalignment (direction along the adhesive surface or peeling direction) due to external force being applied to the bonded part during handling in the assembly process and painting process) or when carrying it into the dryer. (Positional misalignment) may occur, and there may be a problem such as a decrease in adhesive strength after heat curing.

Therefore, even if the adhesive is applied, temporary bonding (temporary fixing) is necessary to fix the overlapping portion of the members of the door inner 1 until the main bonding by heating is performed.
In the present embodiment, as will be described in detail later, by increasing the bonding strength of this temporary bonding, it is possible to prevent the occurrence of problems due to misalignment of the overlapping portions of the two metal members at fewer temporary bonding locations. Yes.

  FIG. 2 is a process explanatory diagram illustrating an outline of a manufacturing process of an automobile door using the door inner 1 according to the present embodiment. As shown in this figure, when manufacturing the above-described automobile door, first, in step # 1, an adhesive is applied to the overlapping portions of the members 2 to 6 of the door inner 1, and then these overlapping portions are formed. Are pasted together. In the present embodiment, an epoxy thermosetting adhesive having a curing temperature of 150 ° C. or higher (300 ° C. or lower) is used as the adhesive. Then, each overlapping portion is temporarily bonded by a method described later (step # 3). In addition, as will be described later, the thermosetting adhesive in the vicinity of the joining portion is cured by the temporary joining.

Thereafter, in step # 4, the door inner 1 is assembled with a door outer panel (door outer: not shown), and in step # 5, the entire door is painted. Then, the painted door is dried in a drying chamber (step # 6). In this embodiment, this drying temperature was set to 190-230 degreeC.
In the drying step after the coating, the uncured thermosetting adhesive is cured. That is, the overlapping portions of the members 2 to 6 of the door inner 1 are finally joined. Therefore, it is possible to cure the uncured thermosetting adhesive by using the heating action of the subsequent process without the necessity of providing a special process for curing the adhesive.

Next, details of the above-described temporary bonding (step # 3) will be described.
In this embodiment, it is possible to reliably perform temporary bonding after suppressing deformation of the metal member, and by increasing the strength of temporary bonding, the position of the overlapping portion of the two metal members at fewer temporary bonding locations In order to prevent the occurrence of defects due to misalignment, the overlapping portion is joined at the temporary fixing portion by plastically deforming the predetermined portion (temporary fixing portion) of the overlapping portion with heat generation by a predetermined tool. At the same time, the thermosetting adhesive in the vicinity of the temporarily fixed portion is cured.

For this reason, in this embodiment, the rotary tool K which shows the principal part in FIG. 8 was used as the said predetermined tool. Such a rotary tool K is the same as a conventionally known one. A cylindrical tool body is held by a holder, and the holder is rotated by a rotation driving means (both not shown), whereby the tool K is moved along its axis. The holder is rotated around Lk, and the holder is further linked to advance / retreat means (not shown) for advancing / retreating the tool K along its axis Lk.
The tip of the rotary tool K is tapered, and the tip of the tapered portion defines the tool diameter Dk.

  By interposing an adhesive A (thermosetting adhesive) between the overlapping portions of the two metal members 10 and 20 and pushing the rotary tool K into a predetermined location (temporary fastening location) while rotating (pushing in) Amount Ek), frictional heat is generated to cause a plastic flow in the temporarily fixed portion, and the two metal members 10 and 20 are temporarily bonded together at the corresponding portion.

By applying such a “method using a rotating tool”, the required joining strength can be obtained relatively easily and reliably by controlling the pushing amount Ek of the rotating tool K, the holding time after pushing, and the like. In addition, deformation of the metal members 10 and 20 can be further suppressed.
In particular, in the overlapping portion, as will be described later, among the thermosetting adhesive A interposed between the two metal members 10 and 20, the adhesive in the vicinity of the temporary fixing joint is rotated / pushed by the rotary tool K. In addition to this, it is cured by the thermosetting adhesive in the vicinity of the temporary bonding joint, in addition to the bonding force by plastic deformation of the temporary bonding joint. A force (adhesive force) is also obtained. As a result, the temporary bonding strength is further increased, and it is possible to prevent the occurrence of problems due to the positional deviation between the overlapping portions of the two metal members 10 and 20 at a smaller number of temporary bonding locations.

Next, a specific example of this embodiment will be described.
3 (a) and 3 (b) are cross-sectional explanatory views of the joining portion showing the first specific example, FIG. 3 (a) shows a state before joining, and FIG. 3 (b) shows a state after joining. ing.
As shown in these drawings, in this specific example, a protrusion 11 is provided at a predetermined position of the overlapping portion of the first metal member 10. On the other hand, a through hole 21 is formed in a portion corresponding to the protrusion 11 in the overlapping portion of the second metal member 20. In the following description, the first metal member 10 corresponds to the front member 2 or the rear member 3 made of, for example, a light alloy casting, and the second metal member 20 corresponds to, for example, a light alloy extrusion. It corresponds to the upper connecting member 4 or the lower connecting member 5 of the molded product.

  When the first metal member 10 and the second metal member 20 are bonded (temporarily bonded) at the overlapping portion, the thermosetting adhesive A is interposed in the overlapping portion, and then FIG. As shown in (a), the protrusion 11 is inserted into the through hole 21 and the metal members 10 and 20 are overlapped. At this time, more preferably, the height of the protrusion 11 is set such that the tip of the protrusion 11 protrudes by a predetermined amount from the second metal member 20.

  And after supporting the back side corresponding to the said projection part 11 of the 1st metal member 10 with the receiving tool J, by pushing in while rotating the rotary tool K from the front end side of the projection part 11, it is due to the generated frictional heat. As shown in FIG. 3B, plastic flow occurs in the base material of the protruding portion 11, the protruding portion 11 is plastically deformed, and the tip end side of the protruding portion 11 fills the through hole 21 of the second metal member 20. , And deform so that it protrudes to the periphery. As a result, the overlapping portions of the two metal members 10 and 20 are temporarily bonded at the locations where the protrusions 11 are provided.

As described above, the protrusion 11 provided in the light metal first metal member 10 is inserted into the through hole 21 formed in the second metal member 20, and the protrusion 11 is plastically deformed to be overlapped. The joining force by plastically deforming the predetermined part of the mating portion can be further increased. That is, as compared with the case where the protrusion 11 and the through hole 21 are not provided (see a fourth specific example described later), higher bonding strength can be obtained, and the number of temporarily fixed bonding portions can be reduced.
At this time, the thermosetting adhesive A in the vicinity of the temporary bonding joint is cured by frictional heat generated by the application of the rotary tool K. That is, in addition to the bonding force obtained by plastically deforming the protrusion 11, in addition to this, a pressing pressure is applied while the thermosetting adhesive A in the vicinity of the temporary bonding portion is cured by frictional heat. Bonding strength (adhesive strength) can also be obtained.

4 (a) and 4 (b) are cross-sectional explanatory views of a joint portion showing a second specific example, FIG. 4 (a) shows a state before joining, and FIG. 4 (b) shows a state after joining. ing.
As shown in these drawings, in this specific example, a protruding portion 12 protruding to the back surface side is provided at a predetermined position of the overlapping portion of the first metal member 10. On the other hand, a through hole 22 is formed in a portion corresponding to the protrusion 12 in the overlapping portion of the second metal member 20.

  When the first metal member 10 and the second metal member 20 are bonded (temporarily bonded) at the overlapping portion, the thermosetting adhesive A is interposed in the overlapping portion, and FIG. As shown in (a), the metal members 10 and 20 are overlapped with each other so that the protrusions 12 correspond to the through holes 22.

And by supporting the surface side corresponding to the said through-hole 22 of the 2nd metal member 20 with the receiving tool J, by pushing in while rotating the rotary tool K from the front end side of the projection part 12, by the generated frictional heat, As shown in FIG. 4 (b), plastic flow occurs in the base material of the projecting portion 12, and the projecting portion 11 is plastically deformed, and the base material flows into the through hole 22 and fills up. 2 The metal member 20 is deformed so as to protrude to the surface side. As a result, the overlapping portions of the two metal members 10 and 20 are temporarily bonded at the locations where the protrusions 11 are provided.
In the second specific example, a projecting portion Kt is provided on the tip surface of the rotary tool K so as to promote plastic deformation of the projecting portion 12. Also in this specific example, compared with the case where the protrusion 12 and the through hole 22 are not provided (refer to a fourth specific example described later), higher bonding strength can be obtained, and the number of temporarily fixed bonding portions can be reduced. it can.

  At this time, the portion of the thermoplastic adhesive A corresponding to the through hole 22 is pushed to the outside of the through hole 22, and the frictional heat generated by the application of the rotary tool K together with the thermosetting adhesive A in the vicinity of the temporarily bonded joint. Cured with. That is, not only the bonding force by plastically deforming the protrusion 21 but also the thermosetting adhesive A in the vicinity of the temporarily fixed bonding portion in addition to this in the case of the first specific example by frictional heat. Bonding force (adhesive force) is also obtained by applying an indentation pressure while curing.

5 (a) and 5 (b) are cross-sectional explanatory views of a joint portion showing a third specific example, FIG. 5 (a) shows a state before joining, and FIG. 5 (b) shows a state after joining. ing.
As shown in these drawings, in this specific example, as in the case of the first specific example, the protrusion 13 is provided at a predetermined position of the overlapping portion of the first metal member 10, and the second metal member 20 A through hole 23 that is combined with the protrusion 13 is formed in the overlapping portion, but in the case of this specific example, a step 14 having a predetermined height is formed around the protrusion 13.

This step part 14 adjusts the thickness of the adhesive bond layer A after temporary bonding. That is, in the specific examples 1 and 2, when the rotary tool K is pushed in, the thermosetting adhesive A is actually pushed so as to protrude outward by the pushing pressure, and the thickness of the adhesive layer A decreases.
In this specific example, as shown in FIG. 5A, the adhesive A is applied to the outside of the step portion 14, and when the rotary tool K is pushed in, the step portion 14 is mainly used as the rotary tool. Since the pressing pressure of K is received, the thickness of the adhesive layer A on the outer side does not fall below the height of the stepped portion 14 as shown in FIG. That is, the adhesive layer A having a thickness equal to the height of the stepped portion 14 can be secured.

  Also in this specific example, after the back surface side of the first metal member 10 corresponding to the protrusion 13 is supported by the receiving tool J, the rotary tool K is inserted from the front end side of the protrusion 13 inserted into the through hole 23. By pushing while rotating, plastic flow is generated in the base material of the protrusion 13 by the generated frictional heat, and the protrusion 11 is plastically deformed as shown in FIG. The second metal member 20 is deformed so as to protrude around the through hole 23 of the second metal member 20. Thereby, the overlapping part of both the metal members 10 and 20 is temporarily fixed and joined at the place where the protrusion 13 is provided.

In this manner, the protrusions 11 provided on the first metal member 10 made of light metal are inserted into the through holes 23 formed in the second metal member 20, and the protrusions 11 are plastically deformed to overlap each other. The joining force by plastically deforming the predetermined part of the mating portion can be further increased. That is, also in this case, compared with the case where the protrusion 13 and the through hole 23 are not provided (see the fourth specific example described later), higher bonding strength can be obtained and the number of temporarily bonded bonding points can be reduced. Can do.
At this time, the thermosetting adhesive A in the vicinity of the temporary bonding joint is cured by frictional heat generated by the application of the rotary tool K. That is, not only the joining force by plastically deforming the protrusion 13, but also the joining force (adhesion force) by curing the thermosetting adhesive A in the vicinity of the temporary fixing joint location can be obtained. .

6 (a), (b) and (c) are explanatory views of a joint part showing a fourth specific example, FIG. 6 (a) shows a cross section before joining, and FIG. 6 (b) shows a part after joining. A cross section is shown. Moreover, FIG.6 (c) has shown typically the planar state of the adhesive bond layer after joining.
As shown in these drawings, in this specific example, unlike the previous specific example, the first and second metal members 10 and 20 are not provided with projections or through holes, and FIG. As shown in FIG. 2, the thermosetting adhesive A is applied to the flat overlapping portion.

In this state, after the back surface side of the first metal member 10 is supported by the support J, the second metal member 20 is pushed by rotating the rotary tool K from the front surface side of the second metal member 20 to generate the second metal by the generated frictional heat. Plastic flow occurs in the base material of the member 20, and the base material of the second metal member 20 is plastically deformed (plastic deformation portion 24) as shown in FIG. 6B. As a result, the overlapping portions of the two metal members 10 and 20 are temporarily fixed and joined at the plastic deformation portion 24.
At this time, the thermosetting adhesive A in the vicinity of the temporary bonding joint is cured by frictional heat generated by the application of the rotary tool K. That is, not only the joining force by plastically deforming the second metal member 20, but also the joining force (adhesion force) by curing the thermosetting adhesive A in the vicinity of the temporary bonding joint is obtained. It is done.

  However, in this case, since the plastic deformation portion 24 is formed by pushing the rotary tool K, the thermosetting adhesive A is pushed out so as to protrude outward, and becomes thin by the pushing pressure of the rotary tool K. As shown by cross-hatching in FIG. 6C, the adhesive layer A in the vicinity of the temporary fixing joint (plastic deformation portion 24) has a donut shape.

  Further, in this specific example, since the plastic flow of the base material due to the rotation and pushing of the rotary tool K is performed at least partly through the adhesive layer A, the temporary fixing joint is sufficient. It is generally difficult to obtain such plastic deformation, and it can be estimated that the bonding strength is lower than in the above specific examples.

7 (a) and 7 (b) are explanatory views of a joint portion showing a third specific example, FIG. 7 (a) shows a cross section before joining, and FIG. 7 (b) shows an adhesive layer after joining. A planar state is shown.
As shown in these drawings, in this specific example, the overlapping surface of the second metal member 20 is flat, but the overlapping surface of the first metal member 10 has a predetermined shape formed in a lattice shape in plan view. A number of protrusions 15 having a height are provided.

In this case, when the rotary tool K is pushed in from the surface side of the second metal member 20, the second metal member 20 plastically flows due to the generated frictional heat, and the protrusion 15 of the first metal member 10. A plastic flow is generated in the base material, and the protrusion 15 is plastically deformed. As a result, the overlapping portions of the two metal members 10 and 20 are temporarily joined by the protrusions 15.
At this time, the thermosetting adhesive A in the vicinity of the temporary bonding joint is cured by frictional heat generated by the application of the rotary tool K. That is, in addition to the plastic flow of the second metal member 20 and the joining force caused by plastic deformation of the lattice-like projections 15 of the first metal member 10, in addition to this, the thermosetting adhesion in the vicinity of the temporary joint location. Bonding force (adhesive force) by curing agent A is also obtained.

  In this case, when the rotary tool K is pushed in, the thermosetting adhesive A is held in each grid of the grid-like protrusion 15 as shown by cross hatching in FIG. The thickness equivalent to the height of the protrusion 15 can be maintained. In addition, since the temporary bonding part and the adhesive layer A in the vicinity thereof do not form a donut shape and can be bonded on the substantially front surface excluding the temporary fixing part due to plastic deformation, higher adhesive force can be secured. Therefore, similarly to the first to third specific examples, it is possible to prevent the occurrence of problems due to the positional deviation of the overlapping portions of the two metal members with a smaller number of temporary fixings than in the case of the fourth specific example. it can.

The joining strength test which confirms the joining strength by the joining method of this invention illustrated by the above specific example was done. Next, the bonding strength test will be described.
In this test, the structure of the fourth specific example, which is estimated to have the lowest bonding strength among the above specific examples, is the embodiment of the present invention, and as a comparative example, projections and through holes are provided as in the fourth specific example. A case where two flat metal plates that are not bonded are joined only by an adhesive without being temporarily bonded (that is, only by the main joining) is set.

In this test, as shown in FIGS. 9 and 10, two rectangular flat plate-shaped test pieces having a width W of 25 mm, a length L of 100 mm, and a thickness t of 1.0 mm are prepared, and the two test pieces are prepared. These end portions were overlapped by a length F (= 12.5 mm), and joining was performed by pushing the rotating tool K shown in FIG.
The material of the test piece was an aluminum alloy, and the adhesive used in the examples of the present invention was an epoxy thermosetting adhesive having a curing temperature of 150 ° C. or higher (300 ° C. or lower).

In this test, for each sample, a tensile load was applied in the longitudinal direction immediately after the temporary joining and after the thermosetting adhesive was subjected to heat curing treatment (baking treatment) (FIG. 9). The tensile shear strength at the time of shearing was obtained and evaluated by comparing them.
Table 1 shows the test conditions and test results of each test sample in this test. In Table 1, “tool diameter” indicates the diameter Dk (see FIG. 8) of the tip surface of the rotary tool K, and “push amount” indicates when the tip surface of the rotary tool K is pushed from the surface of the metal member 20. The maximum push amount is shown. Further, “holding time” indicates the holding time of rotation from the time when the pressing amount is reached.

As shown in Table 1, a bonding strength test was performed on one comparative example (sample 0) and six inventive examples (samples 1 to 6).
As can be clearly seen from the test results in Table 1, the structure of the fourth specific example (samples 1 to 6) considered to have the lowest bonding strength after the thermosetting adhesive was subjected to heat curing treatment (baking treatment). However, it was confirmed that a bonding strength comparable to that in the case of not performing temporary bonding (sample 0) (that is, the bonding strength after the main bonding) can be obtained.
Further, immediately after provisional joining, if other conditions are the same, the provisional joining strength increases as the “holding time” increases. It can be presumed that this is because the longer the “holding time” is, the more frictional heat is generated, and the plastic flow of the base material and the curing of the thermosetting adhesive are further promoted.

  According to the above-described bonding strength test, according to the present embodiment, even the structure of the fourth specific example that seems to have the lowest bonding strength can secure sufficient temporary fixing strength according to the condition setting, and temporary fixing It was confirmed that a bonding strength comparable to that obtained when the bonding was not performed (that is, the bonding strength after the main bonding) was obtained.

In the above embodiment, the first and second metal members are both made of a light alloy. However, the metal member on the side that does not necessarily need to cause plastic flow (for example, through the first to third specific examples). The second metal member 20) provided with the holes 21, 22, 23 is not particularly limited to a light alloy.
Further, in the above embodiment, the rotary tool is used as the “predetermined tool” used for the temporary fixing joining, but the present invention is not limited to such a case. The present invention can also be applied effectively when using the above tool.

Furthermore, although the above embodiment has been described mainly using an inner member (door inner) of an automobile door as an example, the present invention is not limited to such a case, and other various products or semi-finished products are used. It can also be effectively applied to the joining of products and the like.
Thus, it goes without saying that the present invention is not limited to the above-described embodiments, and various changes and improvements can be made without departing from the scope of the invention.

It is front explanatory drawing of the door inner of the door for motor vehicles based on embodiment of this invention. It is process explanatory drawing which shows the outline of the manufacturing process of the door for motor vehicles using the said door inner. It is a section explanatory view of the junction which shows the 1st example of the above-mentioned embodiment. It is sectional explanatory drawing of the junction part which shows the 2nd specific example of the said embodiment. It is sectional explanatory drawing of the junction part which shows the 3rd specific example of the said embodiment. It is explanatory drawing of the junction part which shows the 4th specific example of the said embodiment. It is explanatory drawing of the junction part which shows the 5th specific example of the said embodiment. It is sectional explanatory drawing which shows the principal part of the rotary tool used in the said embodiment. It is plane explanatory drawing of the test piece used for the joining strength test. It is side surface explanatory drawing of the said test piece.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Door inner 2 Front member 3 Rear member 4,5 Connecting member 10 1st metal member 11,12 Protrusion part 20 2nd metal member 21,22 Through-hole A Thermosetting adhesive Ek Push amount of rotary tool K Rotating tool

Claims (2)

A joining method for joining two metal members together with an adhesive interposed in an overlapping portion of two metal members that are vehicle body components,
A first metal member made of a light metal member provided with a protruding portion at a predetermined position of the overlapping portion, and a second metal member formed with a through hole for fitting the protruding portion into the predetermined portion of the overlapping portion . in the overlapping portions, a step of interposing a thermosetting adhesive,
The predetermined portion of the projections fitting was inserted superposed above superposed in part to the through hole, indentation while rotating the rotary tool, let by generating frictional heat resulting plastic flow at the predetermined position the projection the Rukoto part is plastically deformed, and the addition to joining the portions superposed above a predetermined point, the thermosetting adhesive of the predetermined portion near the temporary stop engagement cured at the frictional heat step,
A step of curing an uncured thermosetting adhesive in the drying step after painting of the vehicle body component after the step of temporarily fixing and joining;
A method for joining metal members, comprising: A inner member of said vehicle body structure member of an automobile door, the first metal member, according to claim 1, wherein the door hinge mounting portion and / or the door lock installation section is light-metal cast member provided Method for joining metal members.