JP4318997B2 - Heat-resistant cushion sheet material - Google Patents
Heat-resistant cushion sheet material Download PDFInfo
- Publication number
- JP4318997B2 JP4318997B2 JP2003342251A JP2003342251A JP4318997B2 JP 4318997 B2 JP4318997 B2 JP 4318997B2 JP 2003342251 A JP2003342251 A JP 2003342251A JP 2003342251 A JP2003342251 A JP 2003342251A JP 4318997 B2 JP4318997 B2 JP 4318997B2
- Authority
- JP
- Japan
- Prior art keywords
- heat
- sheet material
- cushion sheet
- resistant cushion
- microcapsules
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、主に加熱および加圧により積層貼合せを行う製造工程で使用される耐熱クッションシート材に関するものである。 The present invention relates to a heat-resistant cushion sheet material used in a manufacturing process in which lamination is performed mainly by heating and pressing.
加熱および加圧により積層貼合せを行う製造工程の一例としてはプリント配線基板を積層する工程がある。プリント配線基板の積層工程においては、エポキシ樹脂製等の配線板を積層セットし、真空中で加熱を与えてプレスを行うが、積層したプリント配線基板に一定の圧力を均一に加えるため、クッションシート材が使用されている。一定の圧力を均一に加えるには、厚さに均一性がある酸性抄造した抄紙式シートが適していることから、このような抄紙式シートを使ったクッションシート材が多く使用されている。 An example of a manufacturing process in which lamination is performed by heating and pressurization includes a process of laminating a printed wiring board. In the printed wiring board lamination process, wiring boards made of epoxy resin or the like are laminated and pressed in a vacuum to apply heat, but a cushion sheet is used to uniformly apply a certain pressure to the laminated printed wiring board. The material is used. In order to apply a certain pressure uniformly, an acid-made paper-making sheet having a uniform thickness is suitable. Therefore, a cushion sheet material using such a paper-making sheet is often used.
ところで、前記クッションシート材は、反復的に加熱および加圧を受けながら使用されるものであるので、このような使用によっても、できるだけ長期に亘って、厚さ変化や硬化を生じることがなく、クッション性を維持していること、つまり耐久性が要求されるが、現在クッションシート材として使用されている抄紙式シートとしては、大半が植物性パルプを主体としてなる紙加工品であり、この他にも、ゴムと不織布からなるものやポリアミド系繊維のフェルトからなるもの、またはこれらの複合材等、種々の材質のものがあるが、いずれも耐熱性が乏しいことから、反復使用によって厚さ変化や硬化を生じるものであり、耐久性の要求を十分に満たすまでには至っていない。
例えば、ポリアミド系繊維のフェルトからなるものにあっては、ポリアミド系繊維自体は加工時の２００℃以下の温度には耐え得るものであるが、ポリアミド系繊維をフェルト状のシートに形成するために有機バインダを使用する必要があり、この有機バインダには耐熱性がなく、クッションシート材が徐々に劣化するという問題がある。
このような耐熱性の要求を満たし、抄紙式シートの形成が可能な材料としては、無機繊維が挙げられるが、無機繊維を抄造したシートは、加圧を繰り返すと、抄紙式シートを構成している無機繊維が折れて粉状となり、クッション性が低下するとともに、粉状となった無機繊維が異物となって、製品を汚染するという問題がある。
By the way, since the cushion sheet material is used while being repeatedly subjected to heating and pressurization, even with such use, there is no change in thickness or curing as long as possible, Maintaining cushioning properties, that is, durability is required, but most of the paper-making type sheets currently used as cushion sheet materials are paper processed products mainly made from vegetable pulp. In addition, there are various materials such as rubber and nonwoven fabric, polyamide fiber felt, or composites of these materials, but all have poor heat resistance. It does not reach the requirements for durability sufficiently.
For example, in the case of a polyamide fiber felt, the polyamide fiber itself can withstand a temperature of 200 ° C. or lower during processing, but in order to form the polyamide fiber in a felt-like sheet, It is necessary to use an organic binder. This organic binder has no heat resistance and has a problem that the cushion sheet material gradually deteriorates.
A material that satisfies such heat resistance requirements and can form a papermaking sheet includes inorganic fibers. However, a sheet made of inorganic fibers constitutes a papermaking sheet when it is repeatedly pressed. There is a problem that the inorganic fibers that are broken break down into a powder and the cushioning properties are lowered, and the powdered inorganic fibers become foreign matters and contaminate the product.
前述のような問題に対処するため、例えば、表層をパルプ（植物性パルプ、合成パルプ）を中性抄造した密度０．６５〜０．９０ｇ／ｃｍ3の層とし、内部層を前述のようなパルプと発泡性粒子を主体として抄造した密度０．２〜０．５ｇ／ｃｍ3の層とした、坪量４００ｇ／ｍ2の多層抄紙シートが提案されている（特許文献１）。
しかしながら、前記特許文献１のような多層抄紙シートをクッションシート材として用いた場合は、確かに、従来のパルプを主体として酸性抄造したクッションシート材と比べると初期のクッション性と、耐久性は改善されているものの、クッションシート材を構成する材料自体は、パルプであり、従来と変わらないため、熱による劣化の進行を防ぐことは困難であるという問題があった。
そこで、本発明は、前記問題点を解消するべく、プリント配線基板等の積層工程に用いるクッションシート材として、繰り返しの加圧および加熱によっても厚さ変化や硬化がなく、クッション性が維持される耐久性と、耐熱性を備えた耐熱クッションシート材を提供することを目的とする。
However, when the multilayer papermaking sheet as in Patent Document 1 is used as a cushion sheet material, the initial cushioning properties and durability are certainly improved as compared with the conventional cushion sheet material made by acid pulping mainly using pulp. However, since the material itself constituting the cushion sheet material is pulp and is not different from the conventional material, there is a problem that it is difficult to prevent the deterioration due to heat.
Therefore, in order to solve the above problems, the present invention is a cushion sheet material used in a lamination process of a printed wiring board or the like, so that the cushioning property is maintained without thickness change or curing even by repeated pressurization and heating. An object is to provide a heat-resistant cushion sheet material having durability and heat resistance.
本発明の耐熱クッションシート材は、前記目的を達成するべく、請求項１に記載の通り、無機繊維からなる抄紙式シート内に、熱可塑性樹脂からなる中空状のマイクロカプセルを分散状態に含有させた耐熱クッションシート材であって、前記マイクロカプセルはその外殻の溶融により、前記無機繊維の表面に接着固定されていることを特徴とする。
また、請求項２記載の耐熱クッションシート材は、前記請求項１記載の耐熱クッションシート材において、前記無機繊維が、微細ガラス繊維であることを特徴とする。
また、請求項３記載の耐熱クッションシート材は、前記請求項１または２記載の耐熱クッションシート材において、前記マイクロカプセルは、熱可塑性樹脂からなることを特徴とする。
また、請求項４記載の耐熱クッションシート材は、前記請求項１乃至３のいずれかに記載の耐熱クッションシート材において、前記耐熱クッションシート材中の前記マイクロカプセルの含有量が１〜７０質量％であることを特徴とする。
また、請求項５記載の耐熱クッションシート材は、前記請求項１乃至４のいずれかに記載の耐熱クッションシート材において、前記マイクロカプセルは、膨張性マイクロカプセルを膨張させてなるものであり、前記耐熱クッションシート材は、前記無機繊維と未膨張の前記膨張性マイクロカプセルを混合抄紙した後、該膨張性マイクロカプセルを膨張させてなるものであることを特徴とする。
また、請求項６記載の耐熱クッションシート材は、前記請求項５記載の耐熱クッションシート材において、前記膨張性マイクロカプセルは、加熱によって膨張する熱膨張性マイクロカプセルであり、前記耐熱クッションシート材は、前記無機繊維と未膨張の前記熱膨張性マイクロカプセルを混合抄紙した後、加熱処理により、該熱膨張性マイクロカプセルを膨張させるとともに、前記無機繊維の表面に前記マイクロカプセルを接着固定させてなるものであることを特徴とする。
In order to achieve the above object, the heat-resistant cushion sheet material of the present invention contains hollow microcapsules made of thermoplastic resin in a dispersed state in a paper-making sheet made of inorganic fibers as described in claim 1. The heat-resistant cushion sheet material is characterized in that the microcapsule is bonded and fixed to the surface of the inorganic fiber by melting the outer shell .
The heat-resistant cushion sheet material according to claim 2 is characterized in that, in the heat-resistant cushion sheet material according to claim 1, the inorganic fibers are fine glass fibers.
The heat-resistant cushion sheet material according to claim 3 is the heat-resistant cushion sheet material according to claim 1 or 2, wherein the microcapsules are made of a thermoplastic resin .
Moreover, the heat-resistant cushion sheet material of Claim 4 is a heat-resistant cushion sheet material in any one of the said Claim 1 thru | or 3 , Content of the said microcapsule in the said heat-resistant cushion sheet material is 1-70 mass%. It is characterized by being.
Further, the heat-resistant cushion sheet material according to claim 5 is the heat-resistant cushion sheet material according to any one of claims 1 to 4 , wherein the microcapsule is obtained by inflating an expandable microcapsule, The heat-resistant cushion sheet material is formed by mixing the inorganic fibers and the unexpanded expandable microcapsules, and then expanding the expandable microcapsules.
The heat-resistant cushion sheet material according to claim 6 is the heat-resistant cushion sheet material according to claim 5 , wherein the expandable microcapsule is a thermally expandable microcapsule that expands by heating, and the heat-resistant cushion sheet material is The paper is made by mixing the inorganic fibers and the unexpanded thermally expandable microcapsules and then expanding the thermally expandable microcapsules by heat treatment, and fixing the microcapsules to the surface of the inorganic fibers. It is characterized by being.
本発明によると、以下の効果を得ることができる。
（１）本発明の耐熱クッションシート材は、無機繊維からなる抄紙式シート内に、中空状のマイクロカプセルを分散状態に含有させてなるものであるため、クッション性を付与する中空状のマイクロカプセルを耐熱性を有する無機繊維からなる抄紙式シート中に断熱保持することができ、繰り返しの加熱および加圧によっても厚さ変化や硬化が生じにくく、クッション性の維持が可能となる耐久性を有し、従来の他の有機繊維（例えば、植物性パルプ、合成パルプ）を用いたクッションシート材よりも耐熱性が向上する。
（２）また、無機繊維からなる抄紙式シート内に、中空状のマイクロカプセルを分散状態に含有させていることから、マイクロカプセルが有する弾力性により無機繊維が折れにくくなるため、無機繊維が折れて飛散せず、耐熱クッションシート材として用いた場合にプリント配線基板等の製品を汚染しない。
（３）無機繊維とマイクロカプセルを混合抄紙してシートを形成するようにした時には、マイクロカプセルを均一に分散して均一な厚さのシートを製造することができ、このような抄紙式シートを耐熱クッションシート材として用いることにより、積層されたプリント配線基板に一定の圧力を均一に加えることができ、積層プレス品の加工精度を向上することができる。
（４）無機繊維からなる抄紙式シート内に、中空状のマイクロカプセルを含有させているため、無機繊維を減量して抄紙式シートを低密度化することができ、中空状のマイクロカプセルを含有させない同じ厚さのシートと比べて、乾燥工程へ持ち込む水分量を少なくすることができ乾燥エネルギーを低減することができ、抄造速度を向上できるなど生産性が増すとともに、製造コストを大幅に削減でき、製品単価を低減できる。
According to the present invention, the following effects can be obtained.
(1) Since the heat-resistant cushion sheet material of the present invention comprises hollow microcapsules contained in a dispersed state in a papermaking sheet made of inorganic fibers, the hollow microcapsules impart cushioning properties. Can be heat-insulated in a paper-made sheet made of heat-resistant inorganic fibers, and it is durable enough to maintain its cushioning properties due to its resistance to thickness change and hardening even with repeated heating and pressurization. And heat resistance improves rather than the cushion sheet material which used the other conventional organic fiber (for example, vegetable pulp, synthetic pulp).
(2) In addition, since the hollow microcapsules are contained in a dispersed state in the papermaking sheet made of inorganic fibers, the inorganic fibers are hardly broken due to the elasticity of the microcapsules. Does not scatter and does not contaminate products such as printed wiring boards when used as a heat-resistant cushion sheet.
(3) When a sheet is formed by mixing paper with inorganic fibers and microcapsules, the microcapsules can be uniformly dispersed to produce a sheet having a uniform thickness. By using it as a heat-resistant cushion sheet material, a constant pressure can be applied uniformly to the laminated printed wiring board, and the processing accuracy of the laminated press product can be improved.
(4) Since a hollow microcapsule is contained in the papermaking sheet made of inorganic fibers, the density of the papermaking sheet can be reduced by reducing the amount of inorganic fibers, and the hollow microcapsules are contained. Compared with the same-thickness sheets that will not be used, the amount of moisture brought into the drying process can be reduced, the drying energy can be reduced, the papermaking speed can be improved, and productivity can be increased and the manufacturing cost can be greatly reduced. , The product unit price can be reduced.
本発明の耐熱クッションシート材は、無機繊維からなる抄紙式シート内に、中空状のマイクロカプセルを含有させたものである。
前記抄紙式シートが、無機繊維からなるものであるため、パルプ等を用いた抄紙式シートと比較して耐熱性が優れている。しかも、無機繊維からなる抄紙式シート中に、クッション性を付与する中空状のマイクロカプセルを含有させているため、耐熱性を有する無機繊維中に前記マイクロカプセルを断熱保持することができ、耐熱性を低下させることなく、クッション性を維持することができる。
The heat-resistant cushion sheet material of the present invention contains hollow microcapsules in a papermaking sheet made of inorganic fibers.
Since the papermaking sheet is made of inorganic fibers, the heat resistance is superior to that of a papermaking sheet using pulp or the like. Moreover, since the paper-made sheet made of inorganic fibers contains hollow microcapsules that impart cushioning properties, the microcapsules can be heat-insulated and retained in the heat-resistant inorganic fibers. The cushioning property can be maintained without lowering.
前記抄紙式シートを構成する無機繊維としては、微細ガラス繊維、アルミナ繊維、シリカ繊維等を用いることができるが、特に、微細ガラス繊維を用いることが好ましい。
なぜならば、微細ガラス繊維は他の無機繊維に比べ、繊維化が容易でガラス固まり（ショット）が少ないため、これを用いて抄紙式シートを形成すると、より均一な厚さのシートを抄造することができ、クッションシート材として用いた場合に、積層されたプリント配線基板に一定の圧力を均一に加えることができ、加工精度を向上することが可能だからである。
前記微細ガラス繊維は、例えば、耐酸性のＣガラスを、溶融、紡糸後、バーナの火炎でエネルギーを与え、吹き飛ばして得られた平均直径が０．２〜４μｍのものが好ましい。
As the inorganic fibers constituting the papermaking sheet, fine glass fibers, alumina fibers, silica fibers and the like can be used, and it is particularly preferable to use fine glass fibers.
This is because fine glass fibers are easier to fiberize and less glass clumps (shots) than other inorganic fibers, so if you use this to form a paper-making sheet, you can make a sheet with a more uniform thickness. This is because, when used as a cushion sheet material, it is possible to uniformly apply a certain pressure to the laminated printed wiring board and improve the processing accuracy.
The fine glass fibers are preferably those having an average diameter of 0.2 to 4 μm obtained, for example, by melting and spinning acid-resistant C glass, applying energy with a flame of a burner, and blowing off.
また、前記マイクロカプセルは熱可塑性樹脂からなるものであることが好ましい。なぜならば、加熱処理により、前記マイクロカプセルの外殻を適度に溶融させ、前記マイクロカプセルを無機繊維に接着して、固定させることができるからである。
このように、抄紙式シートを構成する無機繊維に前記マイクロカプセルを接着して固定させると、繰り返しの加圧および加熱によっても、前記マイクロカプセルが移動することなく、厚さ変化（へたり）がなく、クッション性を維持して耐久性を保持することができる。また、無機繊維にマイクロカプセルが接着して固定されていると、マイクロカプセルが有する弾力性により無機繊維が折れにくくなるため、無機繊維が折れて飛散せず、耐熱クッションシート材として用いた場合にプリント配線基板等の製品を汚染しない。
前記熱可塑性樹脂としては、ポリエチレン、ポリオレフィン、ポリアクリロニトリル（ＰＡＮ）系等が挙げられるが、ガス透過が少なく、膨張後も形状を維持できる強度を有することからＰＡＮ系が好ましい。
また、前記マイクロカプセルは、膨張したもの、未膨張のものどちらでも用いることができるが、未膨張のマイクロカプセルを用いる場合は、抄紙式シートを製造後に加熱処理を必要とする。また、未膨張のマイクロカプセルを用いる場合は、熱可塑性樹脂からなるカプセル、すなわち、殻の中に加熱等によって膨張する膨張性材料、例えば、低沸点炭化水素を内包した構造のものを用いることが好ましい。
また、前記膨張性マイクロカプセルの大きさは、抄紙時の均一分散性を考慮すると、直径が数十μｍ以下であることが好ましい。
The microcapsules are preferably made of a thermoplastic resin. This is because the outer shell of the microcapsule can be appropriately melted by heat treatment, and the microcapsule can be adhered and fixed to the inorganic fiber.
As described above, when the microcapsules are bonded and fixed to the inorganic fibers constituting the papermaking sheet, the thickness changes (sagging) without moving the microcapsules even by repeated pressurization and heating. In addition, durability can be maintained while maintaining cushioning properties. In addition, when the microcapsules are bonded and fixed to the inorganic fibers, the inorganic fibers are difficult to break due to the elasticity of the microcapsules, so that the inorganic fibers do not break and scatter and are used as a heat-resistant cushion sheet material. Does not contaminate products such as printed wiring boards.
Examples of the thermoplastic resin include polyethylene, polyolefin, polyacrylonitrile (PAN), and the like, but PAN is preferable because it has a gas permeation and has a strength capable of maintaining its shape even after expansion.
The microcapsules may be either expanded or non-expanded, but when non-expanded microcapsules are used, heat treatment is required after the papermaking sheet is produced. Further, when using unexpanded microcapsules, it is necessary to use a capsule made of a thermoplastic resin, that is, an expandable material that expands by heating or the like in a shell, for example, a structure in which low-boiling hydrocarbons are included. preferable.
In addition, the size of the expandable microcapsule is preferably a diameter of several tens of μm or less in consideration of uniform dispersibility during papermaking.
前記耐熱クッションシート材中の前記マイクロカプセルの含有量は、１〜７０質量％であることが好ましい。なぜならば、前記マイクロカプセルの含有量が１質量％未満であると、クッション性を十分に付与できず、また、無機繊維が折れ易くなるため好ましくなく、７０質量％を超えると、シートを構成する無機繊維の量が少なくなりすぎ、耐熱クッションシート材の機械的強度を確保することができなくなるため好ましくないからである。 The content of the microcapsules in the heat-resistant cushion sheet material is preferably 1 to 70% by mass. This is because if the content of the microcapsule is less than 1% by mass, the cushioning property cannot be sufficiently provided, and the inorganic fibers are easily broken, and if it exceeds 70% by mass, the sheet is formed. This is because the amount of inorganic fibers becomes too small, and the mechanical strength of the heat-resistant cushion sheet material cannot be secured, which is not preferable.
本発明の耐熱クッションシート材は、例えば、次のような方法により製造することができる。
（１）所定量の無機繊維、例えば、微細ガラス繊維に、所定量の未膨張あるいは膨張させた熱可塑性樹脂からなるマイクロカプセルを添加して、ミキサー、パルパーなどの分離機により水中で均一に分散・混合する。尚、この例では、未膨張の膨張性マイクロカプセルを用いる場合は、加熱によって膨張する熱膨張性マイクロカプセルを用いるようにしている。
（２）分散・混合後、カチオン系吸着剤として、例えば、ポリアクリルアミド系吸着剤を適量添加し、前記微細ガラス繊維の表面に前記マイクロカプセルを吸着・担持させる。
（３）得られた抄紙種を丸網、長網又は傾斜式抄紙機を用いて抄紙式シートを形成する。
（４）前記抄紙式シートを乾燥して原反シートを得る。
（５）乾燥後、所定の温度に達するように、前記シートを加熱炉に通す加熱処理を行い、前記微細ガラス繊維の表面に吸着・担持された前記マイクロカプセルの熱可塑性樹脂の外殻を適度に溶融させて、無機繊維の表面に、前記マイクロカプセルを接着固定させる。未膨張の膨張性マイクロカプセルを配合した場合には、前記加熱炉の温度を前記マイクロカプセルの膨張温度に合わせて適度に設定した上で、前記加熱処理を行うことにより、前記膨張性マイクロカプセルの膨張と同時に、前記マイクロカプセルの接着固定を行うことができる。
The heat-resistant cushion sheet material of the present invention can be manufactured, for example, by the following method.
(1) A predetermined amount of microcapsules made of unexpanded or expanded thermoplastic resin is added to a predetermined amount of inorganic fiber, for example, fine glass fiber, and dispersed uniformly in water by a separator such as a mixer or a pulper.・ Mix. In this example, when an unexpanded expandable microcapsule is used, a thermally expandable microcapsule that expands by heating is used.
(2) After dispersion and mixing, for example, an appropriate amount of polyacrylamide-based adsorbent is added as a cationic adsorbent, and the microcapsules are adsorbed and supported on the surface of the fine glass fiber.
(3) A paper-making type sheet is formed from the obtained paper-making type using a round net, a long net or an inclined paper machine.
(4) The papermaking sheet is dried to obtain an original sheet.
(5) After drying, the sheet is passed through a heating furnace so as to reach a predetermined temperature, and the outer shell of the thermoplastic resin of the microcapsule adsorbed and supported on the surface of the fine glass fiber is moderately Then, the microcapsules are bonded and fixed to the surface of the inorganic fiber. When unexpanded expandable microcapsules are blended, the temperature of the heating furnace is set appropriately according to the expansion temperature of the microcapsules, and then the heat treatment is performed, so that the expandable microcapsules Simultaneously with the expansion, the microcapsules can be bonded and fixed.
次に、本発明の具体的な実施例について、従来例と共に詳細に説明するが、本発明はこの例に限定されるものではない。 Next, specific examples of the present invention will be described in detail together with conventional examples, but the present invention is not limited to these examples.
（実施例１）
平均繊維径が１μｍの微細ガラス繊維９０質量％と、ポリアクリロニトリルからなるカプセル内に低沸点炭化水素を内包した未膨張の熱膨張性マイクロカプセル（松本油脂製薬株式会社製マツモトマイクロスフェアーＦ−５５）１０質量％を水中で分散・混合後、カチオン系吸着剤であるアクリルアミド系吸着剤を添加して前記微細ガラス繊維の表面に前記マイクロカプセルを吸着・担持させた後、ｐＨ３．０の酸性条件において通常の抄紙機にてシートを形成し、９５℃で乾燥した後、さらに、１４０℃の加熱処理を行い、前記マイクロカプセルを膨張させるとともに、前記マイクロカプセルをガラス繊維の表面に接着固定させて、厚さ１．０８ｍｍの耐熱クッションシート材を得た。
Example 1
90% by mass of fine glass fibers with an average fiber diameter of 1 μm and unexpanded thermally expandable microcapsules (Matsumoto Microsphere F-55 manufactured by Matsumoto Yushi Seiyaku Co., Ltd.) encapsulating low-boiling hydrocarbons in capsules made of polyacrylonitrile. ) After dispersing and mixing 10% by mass in water, an acrylamide-based adsorbent that is a cationic adsorbent is added to adsorb and support the microcapsules on the surface of the fine glass fiber, and then an acidic condition of pH 3.0 After forming a sheet with an ordinary paper machine and drying at 95 ° C., heat treatment at 140 ° C. is performed to expand the microcapsules and adhere and fix the microcapsules to the surface of the glass fiber. A heat-resistant cushion sheet material having a thickness of 1.08 mm was obtained.
（実施例２）
実施例１において、前記微細ガラス繊維の配合量を８０質量％、前記熱膨張性マイクロカプセルの配合量を２０質量％としたこと以外は、実施例１と同様にして、厚さ１．０５ｍｍの耐熱クッションシート材を得た。
(Example 2)
In Example 1, the amount of the fine glass fiber was 80% by mass, and the amount of the thermally expandable microcapsule was 20% by mass. A heat-resistant cushion sheet material was obtained.
（実施例３）
実施例１において、前記微細ガラス繊維の配合量を５０質量％、前記熱膨張性マイクロカプセルの配合量を５０質量％としたこと以外は、実施例１と同様にして、厚さ１．０５ｍｍの耐熱クッションシート材を得た。
(Example 3)
In Example 1, the amount of the fine glass fiber was 50% by mass, and the amount of the thermally expandable microcapsule was 50% by mass. A heat-resistant cushion sheet material was obtained.
（従来例）
従来のクッションシート材は、表層と内部層の２層構造のものであり、表層として、針葉樹クラフトパルプ１００質量％を水中で分散した紙料を用意し、内部層として、針葉樹クラフトパルプ８０質量％と、実施例１で用いた前記熱膨張性マイクロカプセル２０質量％を水中で分散・混合後、アクリルアミド系吸着剤を添加して前記針葉樹クラフトパルプの表面に前記熱膨張性マイクロカプセルを吸着・担持させた紙料を用意し、これらを用いてｐＨ７．０の中性条件において円網２層抄紙機にて２層構造のシートを形成し、９５℃で乾燥した後、さらに、１４０℃の加熱処理を行い内部層の前記マイクロカプセルを膨張させるとともに、前記針葉樹クラフトパルプの表面に前記マイクロカプセルを接着固定させて、２層構造からなる厚さ１．０５ｍｍのクッションシート材を得た。
(Conventional example)
A conventional cushion sheet material has a two-layer structure of a surface layer and an inner layer. As a surface layer, a paper material in which 100% by weight of softwood kraft pulp is dispersed in water is prepared, and as an inner layer, 80% by weight of softwood kraft pulp. And 20% by mass of the thermally expandable microcapsules used in Example 1 were dispersed and mixed in water, and then an acrylamide-based adsorbent was added to adsorb and carry the thermally expandable microcapsules on the surface of the softwood kraft pulp. Prepared paper, and using these to form a two-layered sheet on a circular two-layer paper machine under neutral conditions of pH 7.0, dried at 95 ° C., and further heated at 140 ° C. The microcapsules in the inner layer are expanded by treatment, and the microcapsules are bonded and fixed to the surface of the softwood kraft pulp. To obtain a cushion sheet material of 05mm.
得られた実施例１〜３および従来例の各クッションシート材について、各種特性評価を行った。その結果を表１に示す。 Various characteristics evaluation was performed about each obtained cushion sheet material of Examples 1-3 and the prior art example. The results are shown in Table 1.
表１から以下のようなことが分かった。
（１）実施例１〜３の耐熱クッションシート材は、ガラス繊維を主体としてなるものであるため、２３０℃の高温加熱後も、変色はあるものの着火はせず、高度な耐熱性を有していることが確認できた。尚、従来例のクッションシート材は着火を起こした。
（２）また、着火温度については、実施例１および２の耐熱クッションシート材では５００℃と非常に高く優秀で、密度がやや低かった実施例３の耐熱クッションシート材においても３５０℃であり、従来例のクッションシート材に比べれば１２０℃も高い結果となり、耐熱性が優れていることが確認できた。
（３）また、２３０℃の高温加熱後も、良好なクッション性を維持しており、耐久性に優れていることが確認できた。
（４）また、２３０℃の高温加熱後も、シート形状を良好に維持しており、積層貼合せを行う製造工程で使用した場合には、積層プレス品の加工精度を向上することが可能であることが確認できた。
（５）また、実施例１〜３の耐熱クッションシート材は、無機繊維の配合量を減量できたことで、従来例のクッションシート材と比較して密度を７０〜８５％も低減することができ、抄造速度を向上できるとともに、乾燥工程へ持ち込む水分量を少なくすることができ乾燥エネルギーの大幅な削減を図ることができ、生産性が向上し、従来例のクッションシート材と比較して、製造価格を１５〜４０％削減することができた。なお、実施例１〜３の耐熱クッションシート材において、実施例１から実施例３にかけて密度が低下しているのに、製造価格が上昇しているのは、マイクロカプセルの材料単価が高いためである。
（６）これに対して、従来例のクッションシート材は、針葉樹クラフトパルプを主体としてなるものであるため、耐熱性が乏しく、２３０℃の高温加熱時に着火してしまい、クッション性を維持する中空状のマイクロカプセルをクッションシート材内に保護することができず、クッション性およびシート形状も維持することができなかった。
（７）従って、上記結果から、実施例１〜３の耐熱クッションシート材は、加熱および加圧して積層貼合せを行う製造工程で使用される耐熱クッションシート材として適しており、積層品の加工精度を向上することができ、しかも、低コストで得られることが確認できた。
Table 1 shows the following.
(1) Since the heat-resistant cushion sheet materials of Examples 1 to 3 are mainly composed of glass fiber, they have a high degree of heat resistance without being ignited even though they are discolored even after high-temperature heating at 230 ° C. It was confirmed that The conventional cushion sheet material ignited.
(2) Also, the ignition temperature is 350 ° C. even in the heat-resistant cushion sheet material of Example 3 in which the heat-resistant cushion sheet material of Examples 1 and 2 is very high and excellent at 500 ° C. and the density is slightly low. Compared to the cushion sheet material of the conventional example, the result was as high as 120 ° C., and it was confirmed that the heat resistance was excellent.
(3) In addition, it was confirmed that excellent cushioning properties were maintained even after high-temperature heating at 230 ° C. and the durability was excellent.
(4) In addition, the sheet shape is maintained well even after high-temperature heating at 230 ° C., and when used in the manufacturing process of laminating, it is possible to improve the processing accuracy of laminated press products. It was confirmed that there was.
(5) Moreover, the heat-resistant cushion sheet material of Examples 1-3 can reduce a density as much as 70 to 85% compared with the cushion sheet material of a prior art example because the compounding quantity of the inorganic fiber was able to be reduced. It can improve the paper making speed, reduce the amount of moisture brought into the drying process, can greatly reduce the drying energy, improve the productivity, compared with the cushion sheet material of the conventional example, The manufacturing price could be reduced by 15-40%. In addition, in the heat-resistant cushion sheet material of Examples 1-3, although the density has fallen from Example 1 to Example 3, the reason why the manufacturing price has increased is because the material unit price of the microcapsules is high. is there.
(6) On the other hand, since the cushion sheet material of the conventional example is mainly composed of softwood kraft pulp, the heat resistance is poor, and it is ignited when heated at a high temperature of 230 ° C. to maintain the cushioning property. The microcapsules in a shape could not be protected in the cushion sheet material, and the cushioning properties and the sheet shape could not be maintained.
(7) Therefore, from the above results, the heat-resistant cushion sheet materials of Examples 1 to 3 are suitable as a heat-resistant cushion sheet material used in a manufacturing process in which lamination is performed by heating and pressing, and processing of laminated products It was confirmed that the accuracy could be improved and that it could be obtained at low cost.
Claims (6)