JP4486899B2 - Mixed waste plastic recycling process and mixed waste plastic recycling system - Google Patents

Description

  The present invention relates to a method and a processing apparatus for recycling waste plastic mixed with polystyrene and other plastics.

2. Description of the Related Art Conventionally, waste plastic discharged from households and business establishments has been recycled and reused by recycling treatment.
In recent years, an increasing number of local governments have been obliged to separate plastic containers and packaging such as seasoning containers, egg packs, and meat / vegetable trays as “recycled plastics” when collecting household garbage for garbage collection. In order to preserve the global environment, recycling of waste plastics is becoming increasingly important.

Here, there are various types of waste plastics. For example, the above “recycled plastic” includes polyethylene, polypropylene, polystyrene (styrene foam) and the like. Moreover, PET (polyethylene terephthalate), PVC (polyvinyl chloride), etc. are also mixed. These various types of waste plastics are in a mixed state at the time of garbage collection.
Therefore, in order to recycle and recycle waste plastic, it is necessary to separate the collected waste plastic according to the type of plastic to be recycled.

As a method for such separation processing, a method for recycling mixed waste plastic according to Conventional Example 1 will be described with reference to FIG.
Conventional Example 1 separates and recycles polyethylene and polypropylene from mixed waste plastic (recycled plastic) mixed with polystyrene foam and other plastics (polyethylene, polypropylene, etc.).

When the mixed waste plastic 100 is carried into a recycling factory or the like, first, in the foreign substance removal step 101, mixed metal, wood pieces, paper, and the like are removed. Metal removal is mainly performed using magnetism, and pieces of wood, paper, etc. are removed manually. Also, styrofoam of a size that can be removed manually is removed.
Next, in the crushing step 102, the mixed waste plastic 100 is crushed.
In the levitation sorting step 103, a plastic that is a lightweight object and a heavy object (foreign matter) are selected, and the heavy object is removed.
In the centrifugation step 108, polyvinyl chloride or the like having a specific gravity of 1 or more is removed by rotating the centrifuge at high speed.
After the drying step 109, a flaky recycled plastic is completed.
Further, in the granulating step 110, the flaky recycled plastic is granulated into pellets, and finally the recycled plastic (X) 500 is completed.

Here, the main components of the recycled plastic (X) 500 are polyethylene and polypropylene, but in addition, polystyrene which is a component of expanded polystyrene is mixed.
The foamed polystyrene in the mixed waste plastic is basically removed manually by the foreign matter removing step 101, but the mixed waste plastic 100 carried into a recycling factory or the like is compressed during transportation and loosened after carrying in. This is because it becomes so fine that it cannot be removed manually.
Thus, when polystyrene is mixed in recycled plastic (X) 500 mainly composed of polyethylene and polypropylene, the purity is lowered and the quality is low.

In order to solve this problem, a mixed waste plastic recycling method according to Conventional Example 2 as shown in FIG. 3 is performed.
Conventional Example 2 separates and recycles polyethylene and polypropylene from mixed waste plastic (recycled plastic) mixed with expanded polystyrene and other plastics (polyethylene, polypropylene, etc.) and also separates polystyrene, which is a component of expanded polystyrene.
The difference between Conventional Example 2 and Conventional Example 1 is that a recovery step 104 is provided.

In the levitation sorting step 103 of the conventional example 2, the light plastic and the heavy object (foreign matter) are selected and the heavy object is removed, and at the same time, only the styrofoam of the mixed waste plastic 100 put into the stirring water tank is predetermined. It is raised while gathering at the place.
In the recovery step 104, the foamed polystyrene is recovered and discarded as non-recyclable plastic (Z) 700 mainly composed of polystyrene.
On the other hand, the mixed waste plastic after the polystyrene foam is separated in the flotation sorting step 103 is mainly composed of polyethylene and polypropylene through the centrifugal separation step 108, the drying step 109, and the granulation step 110 as in the conventional example 1. Recycled as recycled plastic (Y) 600.

In addition, as a method for treating mixed waste plastic, Patent Document 1 describes an invention in which foamed polystyrene, vinyl chloride, or the like is separated from mixed waste plastic using a difference in specific gravity.
JP 2001-328120 A

  However, the mixed waste plastic processing method according to Conventional Example 2 that solves the problems of Conventional Example 1 also has the following new problems.

The first problem is that polyethylene, polypropylene, and the like are mixed into the non-recyclable plastic (Z) 700 mainly composed of polystyrene.
In the recovery step 104, the foamed polystyrene collected in the predetermined place in the floatation sorting step 103 is basically recovered. However, since the foamed polystyrene at the time of recovery is wet, polyethylene, polypropylene, etc. are adhered and mixed. is there.
As described above, the non-recyclable plastic (Z) 700 mainly composed of polystyrene is mixed with plastics such as polyethylene and polypropylene, so that the purity is lowered and it cannot be regenerated, and is treated as waste. .

The second problem is that the yield of recycled plastic (Y) 600 decreases.
The recycled plastic (Y) 600 that has been recycled after the polystyrene foam has been separated in the flotation and sorting step 103 has higher polyethylene and polypropylene purity, and the quality is improved. However, polyethylene and polypropylene that should be recycled as the recycled plastic (Y) 600 are mixed on the non-recyclable plastic (Z) 700 side, and the recycled amount of the recycled plastic (Y) 600 is reduced.

  On the other hand, in the invention described in Patent Document 1, it is possible to separate foamed polystyrene, vinyl chloride and the like from mixed waste plastic by utilizing the difference in specific gravity, but foamed polystyrene is also a film-like plastic having a small specific gravity. At the same time, it is difficult to separate and recycle the expanded polystyrene (polystyrene) and other plastics (polyethylene, polypropylene) with high accuracy.

  Therefore, the present invention is to solve the above-mentioned conventional problems, and in the separation and recycling treatment of mixed waste plastic mixed with polystyrene foam and other plastics, the purity of the recycled plastic is increased and the quality is improved, and the recycled amount (yield) ) Is increased and the amount of waste is reduced.

In order to solve the above-described conventional problems, the mixed waste plastic recycling method of the invention according to claim 1 includes foamed polystyrene having a small impact value and being easily broken , and other plastics such as polyethylene and polypropylene having a larger impact value and less likely to break than the foamed polystyrene. contaminating the mixed waste plastics by fractionating the Styrofoam and the in mixed waste plastics recycling processing method for reproducing other plastics separately, the crushed the mixed plastic waste was poured into stirred water bath, the Styrofoam predetermined location a floating sorting step for floating (103) while collecting the, a recovery step of recovering the other plastic attached to Styrofoam and Styrofoam obtained by the floating (104), a polystyrene foam and other plastic and the recovery, the heat A pulverizing step of pulverizing in a state in which the polystyrene foam is moist enough not dissolved out (106), a polystyrene foam and other plastic and the grinding, with two and sieve sorting step for sorting or the type (107) according to the particle size It is characterized by that.

Further, the mixed waste plastic recycling treatment method of the invention according to claim 2 separates waste plastic mixed with other plastics such as polyethylene and polypropylene, which has a small impact value and is easily broken and has a shock value larger than that of the foamed polystyrene. to the Styrofoam and the in mixed waste plastics recycling processing method for reproducing other plastic separately crushed the mixed waste plastics were charged into a stirred water bath floating sorting process for floating while collecting the foam in place (103), a recovery step of recovering the other plastic attached to Styrofoam and Styrofoam obtained by the floating (104), the recovered polystyrene foam and other plastic, the Styrofoam is melted by heat A grinding step (106) to ground in the wet state to the extent otherwise, styrofoam and other plastics mentioned above grinding, in large, depending on the particle size, the sieve sorting step (107 to select the particle size of the three types of small And having a large particle size among the polystyrene foam and other plastics selected in the sieve sorting step (107) are reintroduced into the stirred water tank during the floating sorting step (103). .

In addition, the mixed waste plastic recycling apparatus of the invention according to claim 3 separates the waste plastic mixed with other plastics such as polyethylene and polypropylene, which has a small impact value and is easily broken, and has a shock value larger than that of the foamed polystyrene. Then, in the mixed waste plastic recycling apparatus for separately recycling the foamed polystyrene and the other plastics, the pulverized mixed waste plastic is put into a stirring water tank and floated while collecting the foamed polystyrene in a predetermined place. (103), the foamed polystyrene and the recovery means (104) for recovering the other plastic adhering to the foamed polystyrene, and the recovered polystyrene foam and the other plastic are melted by heat. Features and breaking means (106), that the polystyrene foam and other plastic above ground and a sieve sorting means for sorting the two or more types depending on the particle size (107) to ground in the wet state to the extent otherwise And

According to a fourth aspect of the present invention, there is provided a mixed waste plastic recycling apparatus for separating waste plastic mixed with other plastics such as polyethylene and polypropylene, which has a small impact value and is easily broken, and has a shock value larger than that of the foamed polystyrene. Then, in the mixed waste plastic recycling apparatus for separately recycling the foamed polystyrene and the other plastics, the pulverized mixed waste plastic is put into a stirring water tank and floated while collecting the foamed polystyrene in a predetermined place. (103), the foamed polystyrene and the recovery means (104) for recovering the other plastic adhering to the foamed polystyrene, and the recovered polystyrene foam and the other plastic are melted by heat. Pulverizing means (106) for pulverizing in a wet state, and sieving means (107) for selecting the pulverized foamed polystyrene and other plastics into three types of large, medium and small particle sizes according to the particle size. ), And the selected foamed polystyrene and other plastics having a large particle size are re-introduced into the stirred water tank of the floating sorting means (103) .

  The symbols in parentheses indicate the best mode for carrying out the invention and the corresponding elements or the corresponding matters described in the drawings.

According to the invention of claim 1, foamed polystyrene among crushed foamed polystyrene having a small impact value and easily cracked , and mixed waste plastic mixed with other plastics such as polyethylene and polypropylene which has a large impact value and is hard to break than the foamed polystyrene. Since it is floated while being collected at a predetermined place in the flotation sorting process, it is collected in the collection process, and the polystyrene foam is sorted and collected from the mixed waste plastic to obtain a recycled plastic (main component: other plastics) with high purity from the remaining waste plastic. be able to.
Finally, in the pulverization step, the foamed polystyrene and other plastics are pulverized in a wet state so that the foamed polystyrene does not dissolve by heat, and then sorted into two or more types according to the particle size in the sieve sorting step. It is possible to obtain a recycled plastic (main component: expanded polystyrene) having a high purity by selecting the expanded polystyrene having a diameter.

Moreover, according to invention of Claim 2, after grind | pulverizing a foamed polystyrene and other plastics in the grinding | pulverization process in the wet state to such an extent that the said polystyrene foam does not melt | dissolve with heat, according to a particle size in a sieve selection process. Since the particle size is classified into three types, large, medium and small, it is possible to obtain a high-purity recycled plastic (main component: expanded polystyrene) by selecting expanded polystyrene having a small particle size.
In addition, among the polystyrene foam and other plastics selected in the sieve selection process, those with large particle sizes are re-introduced into the stirred water tank during the floating selection process, thus preventing the yield of recycled plastic (main component: other plastics) from decreasing. be able to.

Moreover, according to the invention of claim 3, among the crushed foamed polystyrene having a small impact value and being easily cracked , and the mixed waste plastic mixed with other plastics such as polyethylene and polypropylene which has a larger impact value than the foamed polystyrene and hardly cracked, the foamed polystyrene. Is collected at the designated place by the flotation sorting means and then collected by the collection means, so the foamed polystyrene is sorted and collected from the mixed waste plastic, and the remaining waste plastic is a high purity recycled plastic (main component: other plastics) Can be obtained. Finally, in the pulverizing means, the foamed polystyrene and other plastics are crushed in a wet state to such an extent that the foamed polystyrene does not dissolve by heat, and then sorted into two or more types according to the particle size in the sieve sorting means. It is possible to obtain a recycled plastic (main component: expanded polystyrene) having a high purity by selecting the expanded polystyrene having a diameter.

In addition, according to the invention of claim 4, foamed polystyrene among crushed foamed polystyrene having a small impact value and being easily cracked , and mixed waste plastic mixed with other plastics such as polyethylene and polypropylene that has a large impact value and is hard to break than the foamed polystyrene. Is collected at the designated place by the flotation sorting means and then collected by the collection means, so the foamed polystyrene is sorted and collected from the mixed waste plastic, and the remaining waste plastic is a high purity recycled plastic (main component: other plastics) Can be obtained. Finally, in the pulverizing means, the polystyrene foam and other plastics are pulverized in a wet state to such an extent that the foamed polystyrene does not dissolve by heat, and then the three types of particles, large, medium and small, are selected according to the particle size in the sieve selecting means. Since the diameter is selected, the expanded polystyrene having a small particle diameter can be selected to obtain a recycled plastic (main component: expanded polystyrene) having high purity. Further, among the polystyrene foam and other plastics sorted by the sieve sorting means, those having a large particle size are re-introduced into the agitation water tank of the floating sorting means, thus preventing the yield of recycled plastic (main component: other plastics) from decreasing. be able to.

Next, with reference to FIG. 1, the mixed waste plastic processing method and mixed waste plastic processing apparatus which concern on embodiment of this invention are demonstrated.
FIG. 1 is a flowchart showing the steps of the mixed waste plastic processing method according to the present embodiment.
In this embodiment, “recycled plastic”, which is a plastic container and packaging such as a seasoning container, egg pack, meat / vegetable tray, etc., is recycled as mixed waste plastic.
“Recycled plastic” includes polyethylene, polypropylene, polystyrene (styrene foam), and the like. Moreover, PET (polyethylene terephthalate), PVC (polyvinyl chloride), etc. are also mixed.
Hereinafter, description will be given along the flowchart of FIG.

When the mixed waste plastic 100 is carried into a recycling factory or the like, first, in the foreign substance removal step 101, mixed metal, wood pieces, paper, and the like are removed. Metal removal is mainly performed using magnetism, and pieces of wood, paper, etc. are removed manually. It also collects and recycles expanded polystyrene that can be removed manually.
There may be a case where the mixed waste plastic 100 from which foreign matter has already been removed is carried in.

  Next, in the crushing step 102, the mixed waste plastic 100 is crushed.

Next, in the levitation sorting step 103, the light plastic and heavy object (foreign matter) are selected and the heavy object is removed, and at the same time, the foamed polystyrene is collected in a predetermined place in the mixed waste plastic 100 put into the stirring water tank. It is made to rise while being.
The equipment used in the levitation sorting step 103 includes a stirring water tank, and by using the difference in buoyancy, the plastic and light weight (foreign matter), which are light weight, are sorted to remove the heavy weight.
At the same time, by stirring the inside of the stirring water tank with a screw to generate convection, the foamed polystyrene having strong buoyancy is floated while being collected in the center.
Note that the collection location is not limited to the center as long as the foam can be floated while collecting the foam in a predetermined location.

Next, in the recovery step 104, the foamed polystyrene is recovered.
In the collection step 104, a method of sucking using a suction blower or the like may be used in order to collect the polystyrene foam that has floated on the central portion of the stirring water tank.
In the recovery step 104, it is preferable to recover only the foamed polystyrene. However, since the foamed polystyrene at the time of recovery is wet, polyethylene, polypropylene, and the like other than the foamed polystyrene are attached and mixed.

Next, in the washing and dewatering step 105, the recovered expanded polystyrene, polyethylene, polypropylene, and the like are washed and dehydrated.
Washing is performed with water, and dehydration is preferably performed by squeezing or compressing with a roller or a screw.
The washing and dehydrating step 105 is not always necessary, and may be omitted depending on the state of the recovered polystyrene foam, polyethylene, polypropylene, or the like.
However, when it is pulverized in the next pulverization step 106, if it contains a lot of water, the pulverization ability may be reduced, for example, the dispersion in the pulverization chamber may be reduced or the drying time may be prolonged. If it is too large, the foamed polystyrene may be melted and welded by the heat during pulverization and the particle size may increase. Therefore, before pulverizing the recovered expanded polystyrene, polyethylene, polypropylene, etc., the water content is adjusted to an appropriate level (the dispersion does not decrease during pulverization, the drying time does not increase, and the expanded polystyrene does not dissolve by heat). It is preferable to keep it wet.

Next, in the pulverizing step 106, the polystyrene foam, polyethylene, polypropylene, and the like that have been washed and dehydrated are pulverized.
In the pulverizing step 106, pulverization may be performed using a Henschel mixer or the like in which a blade or blade rotates in a cylindrical container. In addition, by using a Henschel mixer, polystyrene foam, polyethylene, polypropylene, and the like become high temperature during the pulverization process and can be dried simultaneously. Of course, another device may be used.
In this pulverization step 106, foamed polystyrene having a small impact value and easily cracked is pulverized to a small particle size, whereas polyethylene, polypropylene, etc. having a larger impact value than styrene foam are difficult to pulverize and pulverized to a larger particle size than polystyrene. Is done.

Next, in the sieve selection step 107, the pulverized expanded polystyrene, polyethylene, polypropylene and the like are selected according to the particle diameter.
In the sieve sorting step 107, a rotary shifter or the like that can sort using a plurality of sieves at the same time may be used.
In the present embodiment, by using two sieves in the sieve sorting step 107, polystyrene foam, polyethylene, polypropylene, and the like are sorted into three types, large 10, medium 20, and small 30.
Note that the number of sieves may be set to one, for example, and may be selected into two types of large and small particle sizes.

The main component of the large 10 is a plastic mixed with polyethylene, polypropylene or the like pulverized to a large particle size in the pulverizing step 106.
The main component of the small 30 is polystyrene, which is a polystyrene foam pulverized to a small particle size in the pulverization step 106.
In addition, the middle 20 is made by mixing polystyrene or the like into polyethylene or polypropylene as main components.

  Of those selected as described above, the small 30 is regenerated as a recycled plastic (B) 300 mainly composed of polystyrene. The recycled plastic (B) 300 may be shipped as a powder as it is, or may be shipped as pellets using a granulator.

  In addition, although the large 10 can be discarded, it may be re-introduced by, for example, placing it in a stirred water tank during the levitation sorting step 103 in order to improve the yield.

The medium 20 is regenerated as a recycled plastic (C) 400 made of plastic including polyethylene and polypropylene. However, polystyrene or the like is mixed in the recycled plastic (C) 400, which is inferior in terms of quality.
Accordingly, the medium 20 may be re-introduced, for example, in the stirring water tank at the time of the levitation sorting step 103 as in the case of the large 10.

On the other hand, the mixed waste plastic 100 after the foamed polystyrene is separated in the floatation sorting step 103 is processed as follows, and is recycled as a recycled plastic (A) 200 mainly composed of polyethylene and polypropylene.
First, in the centrifugation step 108, polyvinyl chloride or the like having a specific gravity of 1 or more is removed by rotating at a high speed in the centrifuge.
Next, through a drying process 109, a flaky recycled plastic is completed.
Further, in the granulating step 110, the flaky recycled plastic is granulated into pellets, and finally recycled as recycled plastic (A) 200.

  Recycled plastic (A) 200, recycled plastic (B) 300, recycled plastic (C) 400, recycled plastic (X) 500 in Conventional Example 1 and recycled plastic (Y) 600 in Conventional Example 2 that were recycled through the above-described steps. Table 1 shows a summary of the main components, contaminants, and quality of the non-recyclable plastic (Z) 700.

It should be noted that in Table 1, the part where the column of the contaminant is displayed as “-” indicates that it is not mixed at all and is negligible in terms of quality.
As shown in Table 1, the recycled plastic (A) 200 and the recycled plastic (B) 300 obtained in this embodiment are free from contaminants and are of high quality. Further, the recycled plastic (C) 400 is mixed with polystyrene or the like and has a low quality, but can be recovered as the recycled plastic (A) 200 and the recycled plastic (B) 300 if the recycled plastic (C) 400 is re-introduced at the time of the floating selection process 103 again. .

Moreover, in this embodiment, the component of the recycled plastic obtained will change with the magnitude | sizes of the mesh | network of the sieve used at the sieve selection process 107. FIG.
Accordingly, the mesh size may be adjusted so that the obtained recycled plastic (A) 200 and recycled plastic (B) 300 satisfy a predetermined quality standard.

According to the mixed waste plastic processing method according to the present embodiment, since the mixed waste plastic 100 is crushed in the crushing step 102, it is possible to make it easy to perform the regeneration process.
Further, in the flotation sorting process 103, the foamed polystyrene is lifted while being collected in a predetermined place in the crushed mixed waste plastic 100, and then collected in the collection process 104. Therefore, the foamed polystyrene is sorted and collected from the mixed waste plastic 100, and the remaining waste is collected. It is possible to obtain a recycled plastic (A) 200 (main component: polyethylene, polypropylene) having high purity with plastic.

Furthermore, in the washing and dewatering step 105, the recovered foamed polystyrene and the polyethylene, polypropylene, etc. adhering to the foamed polystyrene are washed and dehydrated, so that excess dirt is removed and moisture is removed so that the processing in the next grinding step 106 is facilitated. The amount can be adjusted moderately.
Finally, in the pulverization step 106, the polystyrene foam, polyethylene, polypropylene, etc. are pulverized and then sorted according to the particle size in the sieve sorting step 107. Therefore, the polystyrene foam having a small particle size of 30 is selected to produce a high-purity recycled plastic ( B) 300 (main component: polystyrene) can be obtained.

  Further, among the polystyrene foam, polyethylene, polypropylene, and the like selected in the sieve sorting step 107, those having a large particle size are re-introduced during the floating sorting step 103, so that the recycled plastic (A) 200 (main component: polyethylene, polypropylene) Yield reduction can be prevented.

  Further, in the pulverizing step 106, styrene foam, polyethylene, polypropylene, and the like can be pulverized and dried simultaneously by pulverization using a Henschel mixer or the like in which a blade or blade rotates in a cylindrical container. Therefore, in the sieve selection step 107, the water quality of the regenerated foamed polystyrene can be improved so that the particles do not stick to the sieve.

  In the present embodiment, the mixed waste plastic 100 has a configuration in which the foreign matter removal 101, the crushing 102, the flotation sorting 103, the recovery 104, and the washing and dehydration 105 are passed through the pulverization 106 and the sieve sorting. Not limited to this, even if only 107 steps of crushing 106 and screening the mixed waste plastic mixed with polystyrene foam and other plastics, the polystyrene foam with a small particle size and other plastics are separated and recycled. Is possible.

  In this embodiment, “recycled plastic” is taken as the mixed waste plastic. However, if the mixed waste plastic is mixed with foamed polystyrene and plastic other than foamed polystyrene, the foamed polystyrene can be similarly separated and recycled.

It is a flowchart which shows the process of the mixing waste plastic reproduction | regeneration processing method which concerns on embodiment of this invention. It is a flowchart which shows the process of the mixing waste plastic reproduction | regeneration processing method which concerns on the prior art example 1. FIG. It is a flowchart which shows the process of the mixed waste plastic reproduction | regeneration processing method which concerns on the prior art example 2.

Explanation of symbols

DESCRIPTION OF SYMBOLS 100 Mixed waste plastic 101 Foreign material removal process 102 Crushing process 103 Flotation sorting process 104 Collection process 105 Washing dehydration process 106 Grinding process 107 Sieve sorting process 108 Centrifugation process 109 Drying process 110 Granulation process 200 Recycled plastic (A)
300 Recycled plastic (B)
400 Recycled plastic (C)
500 Recycled plastic (X)
600 Recycled plastic (Y)
700 Non-recyclable plastic (Z)

Claims (4)

Impact value is less fragile Styrofoam, and then styrofoam fractionating the mixed waste plastics other plastic is mixed impact value such large cracks hardly polyethylene and polypropylene from the Styrofoam and mixing waste plastic which said reproducing other plastic separately In the playback processing method,
A levitation sorting step in which the crushed mixed waste plastic is put into a stirred water tank, and the foamed polystyrene is levitated while being collected in a predetermined place,
A recovery step of recovering the foamed polystyrene and the other plastic adhered to the foamed polystyrene;
Crushing step of crushing the recovered expanded polystyrene and other plastics in a wet state to such an extent that the expanded polystyrene does not melt by heat ;
A mixed waste plastic recycling method comprising a sieve sorting step of sorting the pulverized polystyrene and other plastics into two or more types according to the particle diameter. Impact value is less fragile Styrofoam, and then styrofoam fractionating the mixed waste plastics other plastic is mixed impact value such large cracks hardly polyethylene and polypropylene from the Styrofoam and mixing waste plastic which said reproducing other plastic separately In the playback processing method,
A levitation sorting step in which the crushed mixed waste plastic is put into a stirred water tank, and the foamed polystyrene is levitated while being collected in a predetermined place,
A recovery step of recovering the foamed polystyrene and the other plastic adhered to the foamed polystyrene;
Crushing step of crushing the recovered expanded polystyrene and other plastics in a wet state to such an extent that the expanded polystyrene does not melt by heat ;
A sieving step of sorting the pulverized polystyrene and other plastics into three types of particle sizes of large, medium and small according to the particle size ;
A mixed waste plastic recycling method characterized in that , among the polystyrene foam and other plastics selected in the sieve selection step, those having a large particle size are reintroduced into the stirred water tank during the floating selection step . Styrofoam with small impact value and easy cracking , and mixed waste plastic that separates waste plastic mixed with other plastics such as polyethylene and polypropylene, which has a larger impact value and hard to crack than the foamed polystyrene , and regenerates the foamed polystyrene and other plastic separately. In the playback processing device ,
Floating sorting means for charging the crushed mixed waste plastic into a stirring water tank and floating the foamed polystyrene in a predetermined place;
Recovery means for recovering the foamed polystyrene and other plastic adhered to the foamed polystyrene,
Crushing means for crushing the recovered expanded polystyrene and other plastics in a wet state to such an extent that the expanded polystyrene is not melted by heat;
A mixed waste plastic recycling apparatus comprising a sieve sorting means for sorting the pulverized polystyrene foam and other plastics into two or more types according to the particle diameter . Styrofoam foam with low impact value and easy cracking , and mixed waste plastic that separates waste plastic mixed with other plastics such as polyethylene and polypropylene, which has a larger impact value and hard to crack than the foamed polystyrene , and regenerates the foamed polystyrene and other plastic separately. In the playback processing device ,
Floating sorting means for charging the crushed mixed waste plastic into a stirring water tank and floating the foamed polystyrene in a predetermined place;
Recovery means for recovering the foamed polystyrene and other plastic adhered to the foamed polystyrene,
Crushing means for crushing the recovered expanded polystyrene and other plastics in a wet state to such an extent that the expanded polystyrene is not melted by heat;
A sieve sorting means for sorting the crushed foamed polystyrene and other plastics into three types of particle sizes of large, medium and small according to the particle size;
A mixed waste plastic recycling apparatus characterized in that, among the selected foamed polystyrene and other plastics, those having a large particle size are reintroduced into the stirred water tank of the floating sorting means .

Images