JP5082040B2 - Method for producing organohalogen compound decomposing agent - Google Patents

Description

  The present invention relates to a method for producing a decomposing agent for decomposing an organic halogen compound contained in soil, groundwater or the like.

In recent years, in order to purify soil, groundwater and the like contaminated with organic halogen compounds, technological development for decomposing the compounds to reduce the concentration of contamination has been progressing. The basis is to obtain a decomposing agent with high resolution of organic halogen compounds which are pollutants. An example of a typical decomposition agent is iron powder. For example, in Patent Document 1, when iron powder containing a specific surface area of 500 cm ² / g or more and C (carbon) of 0.1 wt% or more is mixed with soil contaminated with an organic halogen compound such as trichlorethylene, It teaches that trichlorethylene and the like in soil can be effectively decomposed.

  According to Patent Document 2, C: less than 0.1% by mass, Si: less than 0.25% by mass, Mn: less than 0.60% by mass, P: less than 0.03% by mass, S: 0.03% by mass Less than 0, less than 0.5% by mass of high purity iron powder contaminated with refractory organohalogen compounds such as cis-1,2-dichloroethylene (cis-1,2-DCE) and water Teaching that it is effective for purification.

However, a higher resolution degradation agent was sought. In response to this request, Patent Document 3, Patent Document 4, and Patent Document 5 related to the same applicant as the present application proposed a copper-containing iron powder in which metallic copper is deposited on the surface of the iron powder particles. When such copper-containing iron powder is added to and mixed with soil or groundwater contaminated with an organic halogen compound, the organic halogen compound can be efficiently decomposed. However, there is still a need for a decomposition agent with higher resolution .
Japanese Patent Application Laid-Open No. 11-235577 JP 2002-316050 A JP 2000-005740 A Japanese Patent Laid-Open No. 2002-069425 JP 2003-339902 A

  An object of the present invention is to efficiently and at low cost obtain a decomposing agent that exhibits higher resolution than ever for organic halogen compounds such as cis-1,2-DCE which are hardly decomposable.

  In the present invention, first, when the reduced iron powder and the copper sulfate powder are mechanically mixed in a ball mill to produce a copper salt-containing iron powder in which particles of both powders are joined, the mechanical mixing described above is performed. Is a method for producing an organohalogen compound decomposing agent characterized in that the iron powder is plastically deformed so that the particle shape becomes flat. Second, the reduced iron powder and the copper sulfate powder are mixed in a ball mill. When producing a copper salt-containing iron powder in which particles of both powders are mechanically mixed with each other, the iron base material inside the iron powder particles is exposed on the surface by the mechanical mixing, and the particle shape Is a method for producing an organic halogen compound decomposing agent characterized in that the iron powder is plastically deformed so as to be flat, and thirdly, the particle shape is flattened with a plate ratio of 2 or more. Production of the organohalogen compound decomposing agent according to the first or second aspect, wherein the iron powder is plastically deformed. Fourth, mechanical mixing of the reduced iron powder and copper sulfate powder is a method for producing an organohalogen compound decomposing agent according to any one of the first to third methods, and fifthly, , A decomposition agent for organic halogen compounds obtained by the production method according to any one of the first to fourth, and sixthly, obtained by the production method according to any one of the first to fourth. This is a method for decomposing organic halogen compounds contained in soil or water using a degrading agent.

  According to the present invention, a decomposing agent having high resolution can be obtained efficiently and at a low cost even for hardly decomposable organic halogen compounds such as cis-1,2-DCE. It can greatly contribute to purification of soil contaminated with compounds and water such as groundwater.

  The organic halogen compounds to be decomposed in the present invention include those of so-called VOCs, such as dichloromethane, carbon tetrachloride, 1,2-dichloroethane, 1,1-DCE, cis-1,2-DCE, 1, 1,1-trichloroethane, 1,1,2-trichloroethane, TCE, tetrachloroethylene, 1,3-dichloropropene, trans-1,2-dichloroethylene, trihalomethane, PCB, dioxin and the like. One or more kinds of organic halogen compounds may be used. The decomposing agent according to the present invention exhibits a catalytic action in the dehalogenation reaction of an organic halogen compound. The halogen element is typically fluorine or chlorine, but the decomposing agent of the present invention is particularly suitable for decomposing organochlorine compounds.

  The decomposing agent of the present invention can decompose these organic halogen compounds as targets such as water, soil, inorganic substances, organic substances, or composites thereof contaminated with the above organic halogen compounds. In particular, in the environmental field, it can be used to purify wastewater, groundwater, soil, exhaust gas and the like contaminated with the above organic halogen compounds.

  When using the decomposing agent of the present invention to purify wastewater, groundwater, soil, exhaust gas, etc. contaminated with organic halogen compounds as described above, for example, heavy machinery for civil engineering machinery such as earth augers used in conventional purification methods Commercially available packaging containers such as flexible containers and paper bags are sufficient for storage of the decomposition agent. Therefore, the decomposition agent according to the present invention is good both in handling and storage.

  In the production of the decomposing agent according to the present invention, as the raw iron powder, for example, reduced iron powder produced by reduction of iron ore or atomized iron powder produced by atomizing molten iron or the like can be used. The particle size of the raw iron powder is not particularly limited. The raw iron powder only needs to contain iron as a main component, but it is desirable that the raw iron powder does not contain components such as chromium and lead which are secondary sources of contamination. As a raw material for the copper source to be joined to the iron powder, copper salt powder is preferable, and for example, copper sulfate can be used as the copper salt powder. In place of the copper salt, copper oxide or metallic copper can also be used.

The gist of the production of the decomposing agent of the present invention is that the raw iron powder particles are subjected to plastic deformation and processed into a flat shape, specifically, the iron particles are crushed and processed into a flat shape. For example, an iron powder raw material is put into a mill and the particles are processed flat. As the mill to be used, a vibration ball mill of a system in which vibration is applied to the housing in a state where a large number of hard balls having a diameter of several millimeters are filled inside the housing is preferable. When vibration is applied to the housing, vibration and collision occur in the internal ball, and when the raw iron powder is present therein, the iron powder particles are crushed and extended. By adjusting the vibration time, amplitude, ball filling amount, raw material input amount, and atmosphere, iron powder processed into a target flat shape can be obtained. At that time, when an appropriate amount of copper salt powder is allowed to coexist, a flat iron powder containing copper salt is obtained. In order to effectively perform plastic deformation by the ball mill, it is preferable to suppress the slip between the ball and the powder, and for this purpose, it is used for smooth mixing and pulverization in a normal ball mill. Such dispersants and lubricants should not be used in the present invention.

The copper salt powder is preferably copper sulfate powder. Copper sulfate is usually available in the form of CuSO ₄ .5H ₂ O with crystal water, but it is better to remove crystal water as much as possible when used in the method for producing a decomposing agent of the present invention. Moisture from crystal water, moisture adhering to the mill surface, moisture in the atmosphere, etc., are produced by an aqueous copper sulfate solution during mixing of iron powder and copper sulfate, and Cu ions in the aqueous solution are reduced on the iron particle surface. And deposited as metallic copper, and the surface of the iron particles may be coated with the deposited metallic copper film. If the surface of the iron powder particles is completely covered with metallic copper, the function as a decomposing agent may be lowered. Therefore, it is preferable to remove the copper sulfate crystal water as much as possible, and it is better to mix with iron powder in a dry manner so that moisture does not mix as much as possible, and to mix in an inert gas atmosphere. . CuSO ₄ .5H ₂ O can remove crystal water by heating. For example, 2 molecules can be removed by heating at 45 ° C., 4 molecules can be removed by heating at 110 ° C., and all molecules can be removed by heating at 250 ° C.

The decomposition agent according to the present invention comprises iron particles having a flat shape with a plate ratio of 2 or more. When the plate ratio is less than 2, the decomposition reaction rate constant k _obs (simply expressed as k) described later does not reach 0.2, and the decomposition ability with respect to the organic halogen compound is low. On the other hand, if the plate ratio exceeds 15, the k value is saturated. Therefore, the plate ratio should be in the range of 2-15. The plate ratio is the ratio of the planar diameter and thickness of each particle observed with an electron microscope (SEM). In the measurement, 50 particles are selected at random in the SEM image, and their plate ratios are averaged. When measuring based on a photograph of an SEM image, it is preferable to enlarge the photograph so that the maximum diameter of one particle is about 10 mm. More specifically, SEM observation can be performed at a magnification of 100 to 150 times, and the image can be directly measured using a scale such as a digital caliper.

  At that time, the average diameter of the flat particles is obtained as follows. Measure the major axis in the flat plane direction and the minor axis orthogonal to this for the 50 powder particles in the field of view, and obtain the plane diameter = (major axis + minor axis) / 2 to determine the average plane diameter for the 50 particles. . Further, the thickness of the particles is also measured, and the average thickness for 50 particles is obtained. And the average diameter of a flat particle is calculated | required by following Formula.

Average diameter of flat particles = (average plane diameter × 2 + average thickness) / 3
Further, the plate ratio is obtained by the following equation.
Plate ratio = average plane diameter / average thickness

  The average diameter of the flat particles according to the present invention is 1 to 500 μm, preferably 25 to 250 μm. Typically, the average plane diameter is in the range of 50 to 500 μm, the average thickness is in the range of 1 to 50 μm, and the plate ratio is preferably 2 to 15. By having such a flat shape, excellent resolution can be exhibited, but if it is too flat, the fluidity as a powder is deteriorated and not only is inconvenient to handle, but also has a higher decomposition performance. Since improvement cannot be expected, the flat shape and particle size as described above are preferable.

  In the decomposing agent according to the present invention, the surface area of the particles is larger than that of the raw iron powder particles before plastic deformation, and by this increase in surface area due to plastic deformation, a new surface is formed in which the structure inside the particles is exposed to the surface. This leads to an increase in the decomposition performance of iron powder with respect to the organic halogen compound. The reason for this is not clear, but a new surface is formed on the particle surface, the reaction site increases, the specific surface area of the iron powder increases, and the surface state of the particle is the adhesion of volatile organic compounds (VOCs). It is considered that the change is made so as to improve the wettability with water and the wettability with water to improve the contact with pollutants. Moreover, when copper, sulfur, or an acid group exists on or near the surface of the iron powder, the decomposition performance is further improved.

Examples are given below. The resolution of the organohalogen compound decomposing agent in the examples is determined by the test method according to the following procedures (a) to (f), and the decomposition reaction rate constant k _obs for cis-1,2-DCE. (Simply written as k) and evaluated.

(I) Put 10 g of white clay (kaolin) and 0.1 g of decomposing agent into a 20 mL vial and mix uniformly.
(B) After adding 6 g of ion exchange water to the above mixed powder and blending well, a butyl rubber stopper with a fluororesin liner is tightened with an aluminum cap so that it can be sealed tightly.
(C) Further, 1 μL each of cis-1,2-DCE and benzene is injected using a micro syringe and sealed.
(D) The cis-1,2-DCE gas that was left in a constant temperature bath at 25 ° C., and 0.1 mL of headspace gas was sampled after 1 hour and was injected in (c) with a gas chromatograph. to determine the concentration, and this concentration as an initial value C _0.
(E) After (d), the gas concentration C of cis-1,2-DCE is measured by gas chromatographic analysis of the headspace gas at regular intervals for 4 days, and cis-1,2- Evaluate concentration decay of DCE.
(F) Decomposition reaction rate constant k (unit: day ^-1 ) of cis-1,2-DCE is represented by the following equation (t represents the number of days elapsed from the initial value).
ln (C / C ₀ ) = − k × t

[Example 1]
The raw iron powder has an average particle size of 100 μm, an apparent density of 2.7 g / cm ³ , a specific surface area of 0.17 m ² / g according to the BET method, and a composition of S: 0.012% and C: 0.26%. , O: 1.61%, reduced iron powder with the balance substantially consisting of iron was used. Along with 100 g of this reduced iron powder, copper sulfate (CuSO ₄ .5H ₂ O) powder is added in an amount that makes the amount of copper 1 mass% with respect to the amount of iron in the reduced iron powder (ie, the ratio Cu / Fe = 0.01). ) Was loaded into a vibrating ball mill. The vibrating ball mill was filled with zirconia balls having a diameter of 5 mm in an amount of 50% by volume with respect to the mill internal volume. Next, with the atmosphere inside the mill replaced with nitrogen gas, the mill was operated for 4 hours at a frequency of 1250 vpm and an amplitude of 9 mm to mechanically mix the reduced iron powder and copper sulfate salt. Was taken out into the atmosphere.

When the obtained powder was measured with a laser diffraction particle size analyzer, the mass cumulative particle size distribution was 14.6 μm for D10, 58.8 μm for D50, and 121.8 μm for D90. The plate ratio was 8.8, the specific surface area by the BET method was 1.03 m ² / g, and the copper content in the powder was 0.83 mass% . Furthermore, as a result of conducting the organohalogen compound decomposing agent evaluation test on the powder, the concentration of cis-1,2-DCE decreased by 99% from the initial value on the 4th day, and remains 1%. The decomposition reaction rate constant k was 1.2 day ⁻¹ .

[Examples 2 to 8]
Types of copper sulfate used as copper salt powder (copper sulfate with different crystallization water content), mixing ratio of iron powder and copper sulfate (Cu / Fe mass ratio), type of replacement gas in the mill, operation of the mill Example 1 was repeated except that the conditions (frequency, amplitude, time) were changed to the conditions shown in Table 1 for each example (Examples 2 to 8). The powder obtained in each example was evaluated in the same manner as in Example 1, and the results are also shown in Table 1.

  The following can be seen from the results in Table 1.

  Although Examples 1-3 were manufactured on the same conditions except having changed the operation time of the mill, it turns out that plate length ratio becomes large and k value becomes large, so that operation time becomes long.

Examples 5, 7, and 8 were manufactured under the same conditions except that the Cu / Fe mixing ratio was changed. However, the Cu / Fe mixing ratios were as high as 0.01, 0.02, and 0.03. It turns out that k value becomes large in order.

Examples 3 and 6 were manufactured under the same conditions except that the atmosphere gas in the mill was changed to nitrogen gas and air. However, the k value was improved when the nitrogen gas atmosphere was used.

  In addition, about the powder obtained in said Examples 1-8, it replaced with kaolin in the resolution | decomposability test, and when it similarly tested using 50 ml of pure water which was not aerated, after 1 hour passed In the first measurement, the gas concentration C of cis-1,2-DCE was below the analysis limit. From this result, it was confirmed that these decomposition agents had a remarkably high decomposition rate.

[ Reference example ]
Example 1 was repeated except that no copper sulfate was added. The obtained powder was evaluated in the same manner as in Example 1, and the results are also shown in Table 1.

[Comparative Examples 1-2]
For comparison, Table 1 shows the k value of the raw iron powder itself used in Example 1 as “Comparative Example 1” and the k value of the sponge iron powder itself available on the market as “Comparative Example 2”. Also written.

[Comparative Example 3]
A powder obtained by simply adding copper sulfate powder to reduced iron powder was obtained without performing the treatment in a vibrating ball mill. The k value of this powder was as low as 0.08 day ⁻¹ .

[ Example 9 ]
Example 1 was repeated with various changes in the Cu / Fe mixing ratio and the operating time of the vibrating ball mill, and powders having the particle size distribution and BET values shown in Table 2 were obtained. The k values of these powders were measured, and the results are shown in Table 2. The half-value width in Table 2 represents the half-value width of the statistically processed particle size distribution curve, and the smaller the half-value width, the smaller the spread of the particle size distribution.

From the results of Table 2, the powder obtained by the method of the present invention can obtain an organic halogen compound decomposing agent having a high resolution k value by selecting the Cu / Fe mixing ratio and the degree of plastic processing of the particles. I understand that.

Example 10
The raw iron powder has an average particle size of 100 μm, an apparent density of 2.7 g / cm ³ , a specific surface area of 0.17 m ² / g according to the BET method, and a composition of S: 0.012% and C: 0.26%. , O: 1.61%, reduced iron powder with the balance substantially consisting of iron was used. In this reduced iron powder, copper sulfate (CuSO ₄ .5H ₂ O) powder is added in an amount such that the amount of copper is 1% by mass with respect to the amount of iron in the reduced iron powder (ie, the ratio of Cu / Fe = 0.01). Then, the flattening treatment of the iron powder and the joining treatment of the iron powder and copper sulfate were performed using a vibration ball mill. The vibrating ball mill is filled with zirconia balls with a diameter of 5 mm in an amount of 50% by volume with respect to the volume of the mill. The atmosphere in the mill is filled with nitrogen gas, and the mill is operated at a frequency of 1250 vpm and an amplitude of 9 mm. Then, the reduced iron powder and the copper sulfate salt were mechanically mixed, and after the mixing was stopped, the internal powder was taken out into the atmosphere.

In the treatment, the speed of charging the reduced iron powder and the total amount of copper sulfate into the operating vibration ball mill was changed at three levels as in Tests 1 to 3 below. Test 1: Mill charging speed 13.5 kg / h , Test 2: Mill charging speed 40.0 kg / h , Test 3: Mill charging speed 400 kg / h . In all cases, the time from the start of charging to the end of processing was 4 hours. About the obtained powder of each test, average particle diameter, major axis / minor axis ratio (average major axis / average minor axis), plate ratio, and k value were measured. The results are shown in Table 3. For comparison, the measurement results of the mixed powder of reduced iron powder and copper sulfate before charging into the vibration ball mill are also shown in Table 3.

  From the results in Table 3, it can be seen that the plate-like ratio increases as the charging speed is slow, and the k value increases as the plate-like ratio increases. In particular, it can be seen that when the plate ratio is 2 or more, the k value increases rapidly and the decomposition ability increases.

Claims (6)

When the reduced iron powder and copper sulfate powder are mechanically mixed in a ball mill to produce a copper salt-containing iron powder in which the particles of both powders are joined, the mechanical mixing described above causes the particle shape to be flat. A process for producing an organic halogen compound decomposing agent, characterized in that the iron powder is plastically deformed. When the reduced iron powder and the copper sulfate powder are mechanically mixed in a ball mill to produce a copper salt-containing iron powder in which the particles of both powders are joined, A method for producing an organohalogen compound decomposing agent, characterized in that the iron powder is plastically deformed so that the iron base material is exposed on the surface and the particle shape becomes flat.   The method for producing an organohalogen compound decomposing agent according to claim 1 or 2, wherein the iron powder is plastically deformed so that the particle shape becomes a flat shape having a plate ratio of 2 or more. The method for producing an organohalogen compound decomposing agent according to any one of claims 1 to 3, wherein the mechanical mixing of the reduced iron powder and the copper sulfate powder is performed by a dry method.   The decomposition agent of the organic halogen compound obtained by the manufacturing method in any one of Claims 1-4.   The method to decompose | disassemble the organic halogen compound contained in soil or water using the decomposition agent obtained by the manufacturing method in any one of Claims 1-4.