JP5379438B2

JP5379438B2 - Roof tile

Info

Publication number: JP5379438B2
Application number: JP2008255211A
Authority: JP
Inventors: 泰久東堤; 信博田井; 真依子小野
Original assignee: Kubota Matsushitadenko Exterior Works Ltd; KMEW Co Ltd
Current assignee: KMEW Co Ltd
Priority date: 2008-09-30
Filing date: 2008-09-30
Publication date: 2013-12-25
Anticipated expiration: 2028-09-30
Also published as: JP2010084437A

Abstract

<P>PROBLEM TO BE SOLVED: To provide a roof tile 1 which forms a roof with proper beauty by making a gap made in the overlap portion of the roof tile 1 with a flat surface inconspicuous and making a stain made on the overlap portion of the roof tile 1 by rainwater inconspicuous. <P>SOLUTION: This roof tile 1 with the flat surface is used to be laid on the roof. In the roof tile 1, the height (T) of the eaves-side end 2 of the roof tile 1, in a state in which the roof tile is laid on the roof, is in the range of 15-35 mm; a notched portion 3 opened on an eaves side and a backside is formed at the eaves-side end 2 of the roof tile 1; the eaves-ridge-direction length (B) of the notched portion 3 is in the range of 1/5-2/7 with respect to the height (T); and the height (H) of the notched portion 3 is in the range of 1/6-2/3 with respect to the height (T), and 5 mm or more. <P>COPYRIGHT: (C)2010,JPO&INPIT

Description

本発明は、建築用の屋根瓦に関するものであり、さらに詳しくは、表面が平坦な屋根瓦に関するものである。 The present invention relates to a roof tile for construction, and more particularly to a roof tile having a flat surface.

近年、建物の屋根に敷設する屋根瓦として、セメント系成形材料等を成形して得られる表面の平坦な屋根瓦が要望されている。このような屋根瓦は平瓦とも呼ばれ、シンプルな意匠の屋根を形成できることができるという特徴がある。表面が平坦な屋根瓦としては、例えば、特許文献１及び２の屋根瓦が開示されている。 In recent years, a roof tile with a flat surface obtained by molding a cement-based molding material or the like is desired as a roof tile laid on the roof of a building. Such a roof tile is also called a flat tile and has a feature that a roof with a simple design can be formed. As roof tiles having a flat surface, for example, the roof tiles of Patent Documents 1 and 2 are disclosed.

図９は、このような屋根瓦１が敷設された屋根構造の一例を示している。この屋根瓦１は、表面が平坦に形成されると共に、屋根瓦１の軒側端部２の前端は平面状に形成されている。そして、屋根瓦１を屋根下地６に敷設する際には、軒側の屋根瓦１の上面に棟側の屋根瓦１を重ねて、屋根瓦１を隙間なく載置させて屋根を形成する。このような屋根には段差が付与されて、この段差により屋根の水切が行われ、雨水が激しく流れるのを防いでいる。 FIG. 9 shows an example of a roof structure in which such a roof tile 1 is laid. The roof tile 1 has a flat surface, and the front end of the eaves side end 2 of the roof tile 1 is formed in a flat shape. Then, when the roof tile 1 is laid on the roof base 6, the ridge-side roof tile 1 is placed on the upper surface of the eave-side roof tile 1, and the roof tile 1 is placed without a gap to form a roof. Such a roof is provided with a step, which drains the roof and prevents rainwater from flowing violently.

しかし、屋根瓦１の敷設後、野地の不陸や屋根瓦１の反り等によって、軒側の屋根瓦１と棟側の屋根瓦１の軒側端部２との間に隙間（口開き）が形成されることがある。このような隙間が形成されていると、美観上問題となり、クレームの発生原因になったりする。とりわけ平坦な屋根瓦１、特に表面が全くフラットな屋根瓦１の場合、形状等による目隠し作用がなく隙間が目立ちやすくなるため、美観をさらに損なうことになるとともに、場合によっては施工者が屋根瓦１の裏面の屋根下地６と接触する支持部１０等を加工して、隙間を目立たなくなるように調整するため、余計な施工の手間を生じさせることがある。さらに、屋根瓦１が粘土質材料を成形・焼成して得られるものである場合は、焼成により屋根瓦１の反りやねじれ、寸法のばらつきがいっそう発生しやすく、そのため、隙間が生じて美観を悪化させる傾向がより顕著となる。 However, after the roof tile 1 is laid, there is a gap (open mouth) between the eaves-side roof tile 1 and the eaves-side end 2 of the ridge-side roof tile 1 due to unevenness in the field or warping of the roof tile 1. May be formed. If such a gap is formed, it becomes an aesthetic problem and may cause a complaint. In particular, in the case of a flat roof tile 1, particularly a roof tile 1 with a completely flat surface, there is no blinding action due to the shape and the like, and the gap becomes more conspicuous. Since the support part 10 etc. which contact the roof base | substrate 6 of 1 back surface are processed, and it adjusts so that a clearance gap may become inconspicuous, the effort of extra construction may be produced. Further, when the roof tile 1 is obtained by molding and firing a clay material, the roof tile 1 is more likely to be warped, twisted, or dimensional variation due to the firing, so that a gap is created and the aesthetic appearance is increased. The tendency to worsen becomes more prominent.

また、棟側の屋根瓦１の軒側端部２はその軒側の前端が軒側の屋根瓦１の上に重ねられて敷設されており、図９の矢印に示すように、雨水は屋根瓦１の露出面に沿って流れる。そのため、軒側の屋根瓦１と棟側の屋根瓦１の重ね合わせ部分に、ほこりが堆積しやすく、このほこりの堆積により白い汚れが付着することがある。このとき、屋根瓦１は通常、有色であるために白い汚れが目立ちやすく、屋根の美観を損ねるという問題が生じている。
特開平１０−１８３８７０号公報特開２００６−１８８９００号公報 In addition, the eaves side end 2 of the roof tile 1 on the ridge side is laid with the front end of the eave side overlapped on the roof tile 1 on the eave side. As shown by the arrows in FIG. It flows along the exposed surface of the tile 1. Therefore, dust is likely to accumulate on the overlapping portion of the roof tile 1 on the eaves side and the roof tile 1 on the ridge side, and white dirt may adhere to the accumulated dust. At this time, since the roof tile 1 is usually colored, white stains are easily noticeable, resulting in a problem that the aesthetic appearance of the roof is impaired.
JP-A-10-183870 JP 2006-188900 A

本発明は上記の点に鑑みてなされたものであり、屋根瓦の重ね合わせ部分で発生する隙間を目立たなくすると共に、雨水により屋根瓦の重ね合わせ部分に発生する汚れを目立たなくして美観のよい屋根を形成する屋根瓦を提供することを目的とする The present invention has been made in view of the above points, and makes the gap generated in the overlapping portion of the roof tile inconspicuous, and makes the dirt generated in the overlapping portion of the roof tile due to rainwater inconspicuous and has a good appearance. Aim to provide roof tiles that form the roof

本発明の請求項１に係る屋根瓦１は、屋根に敷設される、表面が平坦な屋根瓦１であって、屋根瓦１の軒側端部２に、軒側端面の下部において軒側と裏面側に開口する切欠部３が形成され、前記切欠部３の棟側の内面が平面状に形成され、前記切欠部３の上部の内面が、前記切欠部３の軒側の内面の上端から軒側に向けて上方向に軒棟方向に対する傾斜角（α）０〜３５°（ただしαは０°でない）で延伸することを特徴とするものである。 The roof tile 1 according to claim 1 of the present invention is a roof tile 1 that is laid on a roof and has a flat surface . The roof tile 1 is connected to the eave side end portion 2 of the roof tile 1 at the lower side of the eave side end surface. A notch 3 opening on the back side is formed, the inner surface on the ridge side of the notch 3 is formed in a flat shape, and the upper inner surface of the notch 3 extends from the upper end of the inner surface on the eaves side of the notch 3 It is characterized by extending toward the eaves side at an inclination angle (α) of 0 to 35 ° (where α is not 0 °) with respect to the eaves direction .

請求項２に係る屋根瓦１は、屋根に敷設される、表面が平坦な屋根瓦１であって、屋根瓦１の軒側端部２に軒側と裏面側に開口する切欠部３が形成され、前記切欠部３が、屋根瓦１の軒側と裏面側に開口する第１切欠部３ａと、第１切欠部３ａよりも棟側に形成され第１切欠部側３ａと裏面側に開口する、第１切欠部３ａよりも高さの低い第２切欠部３ｂとからなり、第１切欠部３ａの棟側の内面が平面状に形成され、第１切欠部３ａの上部の内面が、第１切欠部３ａの軒側の内面の上端から軒側に向けて上方向に軒棟方向に対する傾斜角（α）０〜３５°で延伸し、第２切欠部３ｂの棟側の内面が平面状に形成され、第２切欠部３ｂの上部の内面が、第２切欠部３ｂの軒側の内面の上端から軒側に向けて上方向に軒棟方向に対する傾斜角（β）０〜３５°で延伸していることを特徴とするものである。 The roof tile 1 according to claim 2 is a roof tile 1 that is laid on the roof and has a flat surface, and a cutout portion 3 that opens to the eave side and the back side is formed at the eave side end portion 2 of the roof tile 1. The notch 3 is formed on the eave side and the back side of the roof tile 1 on the eaves side and the back side, and is formed on the ridge side with respect to the first notch 3a and opened on the first notch side 3a and the back side. The second cutout portion 3b having a lower height than the first cutout portion 3a, the inner surface of the first cutout portion 3a on the ridge side is formed in a planar shape, and the upper inner surface of the first cutout portion 3a is The first cutout portion 3a extends upward from the upper end of the inner surface of the eave side toward the eaves side at an inclination angle (α) of 0 to 35 ° with respect to the eave building direction, and the inner surface of the second cutout portion 3b on the ridge side is flat. The upper inner surface of the second cutout portion 3b is inclined in the upward direction from the upper end of the inner surface of the second cutout portion 3b toward the eaves side (β And it is characterized in that it is stretched at 0 to 35 °.

請求項３に係る屋根瓦１は、請求項１又は２の構成に加え、屋根瓦１は、屋根に敷設された状態での軒側端部２の高さ（Ｔ）が１５〜３５ｍｍであり、前記切欠部３の軒棟方向長さ（Ｂ）が前記高さ（Ｔ）に対して１／５〜２／７であると共に、前記切欠部３の高さ（Ｈ）が前記高さ（Ｔ）に対して１／６〜２／３、且つ、５ｍｍ以上であることを特徴とするものである。 In addition to the structure of Claim 1 or 2 , the roof tile 1 which concerns on Claim 3 is 15-35 mm in height (T) of the eaves side edge part 2 in the state laid in the roof. The length (B) of the cutout portion 3 in the eaves ridge direction is 1/5 to 2/7 with respect to the height (T), and the height (H) of the cutout portion 3 is the height ( T) is 1/6 to 2/3 and 5 mm or more .

本発明の請求項１による屋根瓦１によれば、その軒側端部２に切欠部３が形成されていることにより、屋根瓦１の敷設後にはこの切欠部３に影が形成されるので、軒側の屋根瓦１と棟側の屋根瓦１との間に隙間が形成されたとしても、隙間を目立たなくすることができ、屋根の美観が悪化するのを防止することができる。また、雨水によりほこりが堆積して白い汚れが付着したとしても、切欠部３により形成される影によってこの汚れを目立たなくすることができ、屋根の美観が悪化するのを防止することができる。 According to the roof tile 1 according to claim 1 of the present invention, since the notch 3 is formed at the eaves side end 2, a shadow is formed in the notch 3 after the roof tile 1 is laid. Even if a gap is formed between the roof tile 1 on the eaves side and the roof tile 1 on the ridge side, the gap can be made inconspicuous and the appearance of the roof can be prevented from deteriorating. Moreover, even if dust accumulates due to rain water and white dirt adheres, the dirt can be made inconspicuous by the shadow formed by the cutout portion 3, and the appearance of the roof can be prevented from deteriorating.

また、風が切欠部３に吹き込んだとしても、乱流が発生して切欠部３のない形状よりも雨水が隙間に流れにくくなるので、十分な防水性を屋根に付与して屋根の水仕舞を向上させることができる。また、浅い角度から差し込む光に対しても影を形成することができるので、重ね合わせ部分に生じる隙間や雨水による汚れをより目立たなくさせて屋根の美観が悪化するのを防止することができる。 In addition , even if wind blows into the notch 3, turbulence occurs and rainwater is less likely to flow into the gap than the shape without the notch 3. Can be improved. Further, since a shadow can be formed even for light entering from a shallow angle, the appearance of the roof can be prevented from deteriorating by making the gap generated in the overlapped portion and dirt due to rainwater less noticeable.

請求項２による屋根瓦１によれば、その軒側端部２に切欠部３が形成されていることにより、屋根瓦１の敷設後にはこの切欠部３に影が形成されるので、軒側の屋根瓦１と棟側の屋根瓦１との間に隙間が形成されたとしても、隙間を目立たなくすることができ、屋根の美観が悪化するのを防止することができる。また、雨水によりほこりが堆積して白い汚れが付着したとしても、切欠部３により形成される影によってこの汚れを目立たなくすることができ、屋根の美観が悪化するのを防止することができる。 According of claim 2 in roof tiles 1, by the notch 3 on the eaves side end portion 2 is formed, since after laying roof tiles 1 a shadow is formed in the notch 3, eaves side Even if a gap is formed between the roof tile 1 and the roof tile 1 on the ridge side, the gap can be made inconspicuous, and the appearance of the roof can be prevented from deteriorating. Moreover, even if dust accumulates due to rain water and white dirt adheres, the dirt can be made inconspicuous by the shadow formed by the cutout portion 3, and the appearance of the roof can be prevented from deteriorating.

また、二段階の切欠部３を形成することにより、風が切欠部３に吹き込んだとしても、乱流が発生して切欠部３のない形状よりも雨水が隙間に流れにくくなるので、十分な防水性を屋根に付与して屋根の水仕舞を向上させることができる。また、浅い角度から差し込む光に対しても影を形成することができると共に、隙間や汚れが見えたとしてもこの影がスリット状の模様を形成することにより、重ね合わせ部分に生じる隙間や雨水による汚れをより目立たなくさせて屋根の美観が悪化するのをさらに防止することができる。 Moreover , even if wind blows into the notch 3 by forming the two-stage notch 3, turbulence is generated and rainwater is less likely to flow into the gap than the shape without the notch 3. Water resistance of the roof can be improved by adding waterproofness to the roof. In addition, shadows can be formed even for light entering from a shallow angle, and even if gaps or dirt are seen, the shadows form slit-like patterns, resulting in gaps and rainwater generated in the overlapping part. It is possible to further prevent the appearance of the roof from deteriorating by making the dirt less noticeable.

図１は、本発明の屋根瓦１の一例を敷設した屋根構造を示した断面図であり、図１（ａ）は概略図、図１（ｂ）は要部拡大図である。また、図２及び図３は、図１で示した屋根瓦１を示しており、図２は平面図、図３はＡ−Ａ断面図である。 FIG. 1 is a cross-sectional view showing a roof structure in which an example of a roof tile 1 of the present invention is laid, FIG. 1 (a) is a schematic view, and FIG. 1 (b) is an enlarged view of a main part. 2 and 3 show the roof tile 1 shown in FIG. 1, FIG. 2 is a plan view, and FIG. 3 is an AA cross-sectional view.

この屋根瓦１は平面視矩形状でその表面が平坦に形成されており、敷設時には屋根下地６の上に載置される。屋根瓦１の軒側には、敷設時に隣接する他の屋根瓦の棟側の端部の上に重ねられる部位として軒側端部２が備えられている。この軒側端部２の軒側の前端の裏面には、屋根瓦の軒棟方向と直交する方向の一端から他端に亘って下方に突出した前垂部７が形成されている。 The roof tile 1 has a rectangular shape in plan view and a flat surface, and is placed on the roof base 6 when laid. On the eaves side of the roof tile 1, an eaves side end portion 2 is provided as a portion that is overlaid on the ridge side end portion of another roof tile that is adjacent when laid. A front hanging portion 7 is formed on the back surface of the front end of the eave side of the eave side end portion 2 so as to protrude downward from one end to the other end in a direction orthogonal to the eave ridge direction of the roof tile.

一方、屋根瓦１の棟側の端部には、屋根瓦１の他の部分よりも上下方向に、屋根瓦１の軒棟方向と直交する方向の一端から他端に亘って突出させて形成された立ち上がり部８が形成されている。 On the other hand, at the end of the roof tile 1 on the ridge side, it is formed so as to project from one end to the other end in the direction perpendicular to the eave ridge direction of the roof tile 1 in the vertical direction from the other part of the roof tile 1. The raised portion 8 is formed.

また、屋根瓦１の軒棟方向と直交する方向の一端縁には、裏面に突出すると共に表面が屋根瓦１の他の部分の表面よりも下方に位置した下重ね部４が形成され、他端縁には、敷設時に下重ね部４に上から重ねられる上重ね部５が形成されている。この屋根瓦１を平面上に載置した状態では、上重ね部５及び下重ね部４の裏面は前記平面から浮いた状態となっている。 Further, at one end edge of the roof tile 1 in the direction orthogonal to the eaves ridge direction, a lower overlap portion 4 is formed which protrudes from the back surface and whose surface is located below the surface of the other part of the roof tile 1. An upper overlap portion 5 is formed on the end edge so as to overlap the lower overlap portion 4 from above when laying. In a state where the roof tile 1 is placed on a plane, the back surfaces of the upper overlap portion 5 and the lower overlap portion 4 are in a state of floating from the plane.

また、屋根瓦１の棟側寄りの部分の、棟側端縁よりも軒側の部分には、下方に突出する支持部１０が突設されている。この支持部１０は、敷設時に屋根瓦１を屋根下地６に支持する部分となっている。 Further, a support portion 10 that protrudes downward is projected from a portion of the roof tile 1 near the ridge side, which is closer to the eaves side than the ridge side edge. This support part 10 is a part which supports the roof tile 1 to the roof base 6 at the time of laying.

屋根瓦１の棟側の端縁と、下重ね部４とには、それぞれビスや釘等の固着具が打入される固着孔１１が設けられている。この固着孔１１に固着具が打入されることにより、屋根瓦１は屋根下地６に固着される。 The edge of the roof tile 1 on the ridge side and the lower overlap portion 4 are provided with fixing holes 11 into which fixing tools such as screws and nails are respectively inserted. The roof tile 1 is fixed to the roof base 6 by driving a fixing tool into the fixing hole 11.

屋根瓦１は、屋根に敷設された状態での屋根瓦１の軒側端部２の高さ（Ｔ）が１５〜３５ｍｍに形成されている。軒側端部２の高さ（Ｔ）が１５ｍｍ未満では、木口が薄く見えて重厚感や高級感に乏しく美観を損なうおそれがあり、一方、軒側端部２の高さ（Ｔ）が３５ｍｍを超えると、一般的な住宅の二階に敷設した際には屋根瓦１の厚みが大きすぎて美観上好ましくない。なお、軒側端部２の高さ（Ｔ）とは、軒側に隣接する他の屋根瓦１との高低差のことであり、軒側端部２における屋根瓦１の表面から、軒側に隣接する他の屋根瓦１の表面までの屋根瓦１の表裏方向の長さのことである。また、図示の例では、軒側端部２における屋根瓦１の厚みということもできる。 The roof tile 1 is formed so that the height (T) of the eaves side end portion 2 of the roof tile 1 in a state laid on the roof is 15 to 35 mm. If the height (T) of the eaves side end portion 2 is less than 15 mm, the end of the eaves side portion 2 may appear thin and the sturdiness and luxury may be poor and the appearance may be impaired. On the other hand, the height (T) of the eaves side end portion 2 is 35 mm. If it exceeds 1, the thickness of the roof tile 1 is too large when it is laid on the second floor of a general house, which is not aesthetically pleasing. In addition, the height (T) of the eaves side edge part 2 is a height difference with other roof tiles 1 adjacent to the eaves side. It is the length of the front and back direction of the roof tile 1 to the surface of the other roof tile 1 adjacent to. In the illustrated example, the thickness of the roof tile 1 at the eaves side end 2 can also be said.

屋根瓦１の軒側端部２には、軒側と裏面側に開口する切欠部３が形成されており、この切欠部３は、軒棟方向と直交する方向の一端から他端に亘って屋根瓦１に設けられている。そして、この切欠部３は、切欠部３の軒棟方向長さ（Ｂ）が前記高さ（Ｔ）に対して１／５〜２／７となるように形成されている。切欠部３の軒棟方向長さ（Ｂ）が前記軒側端部２の高さ（Ｔ）に対して１／５よりも小さいと、切欠部３によって十分な影が形成されにくくなり、隙間や汚れを目立たなくさせることができなくなる。一方、切欠部３の軒棟方向長さ（Ｂ）が前記軒側端部２の高さ（Ｔ）に対して２／７を超えると、軒側端部２の前端の強度が低下して踏割が発生するおそれがある。なお、切欠部３の軒棟方向長さ（Ｂ）とは、切欠部３が屋根瓦１の軒側に開口する位置から切欠部３が屋根瓦１の裏面側に開口する位置までの軒棟方向の長さのことである。 The eaves side end 2 of the roof tile 1 is formed with a notch 3 that opens to the eave side and the back side, and this notch 3 extends from one end to the other end in the direction perpendicular to the eaves ridge direction. It is provided on the roof tile 1. And this notch part 3 is formed so that the eaves-ridge direction length (B) of the notch part 3 may become 1/5-2/7 with respect to the said height (T). If the eaves ridge direction length (B) of the notch portion 3 is smaller than 1/5 with respect to the height (T) of the eaves side end portion 2, a sufficient shadow is hardly formed by the notch portion 3, and the gap And dirt cannot be made inconspicuous. On the other hand, if the eaves ridge direction length (B) of the notch 3 exceeds 2/7 with respect to the height (T) of the eaves side end 2, the strength of the front end of the eaves side end 2 decreases. There is a risk that the trance will occur. Note that the length (B) of the notch 3 in the eaves direction is the eaves from the position where the notch 3 opens to the eave side of the roof tile 1 to the position where the notch 3 opens to the back side of the roof tile 1. It is the length of the direction.

さらに、この切欠部３は、切欠部３の高さ（Ｈ）が前記高さ（Ｔ）に対して１／６〜２／３、且つ、５ｍｍ以上となるように形成されている。切欠部３の高さ（Ｈ）が前記軒側端部２の高さ（Ｔ）に対して１／６より低いと、影の上下方向の厚みが少なくなるため、重ね合わせ部分に生じる隙間や汚れを目立たなくすることができにくくなる。一方、切欠部３の高さ（Ｈ）が前記軒側端部２の高さ（Ｔ）に対して２／３より高いと、切欠部３の上下方向の開口範囲が広くなりすぎて重ね合わせ部分に影を形成することができにくくなり、隙間や汚れを目立たなくすることができなくなる。また、切欠部３の高さ（Ｈ）が５ｍｍ未満では、影の上下方向の厚みが少なくなるため、影が十分にできず重ね合わせ部分に生じる隙間や汚れを目立たなくすることができなくなる。なお、切欠部３の高さ（Ｈ）とは、切欠部３が屋根瓦１の裏面側に開口する位置から切欠部３が屋根瓦１の軒側に開口する位置までの軒棟方向と垂直な方向の長さのことである。 Further, the notch 3 is formed such that the height (H) of the notch 3 is 1/6 to 2/3 of the height (T) and 5 mm or more. When the height (H) of the notch 3 is lower than 1/6 with respect to the height (T) of the eaves side end 2, the thickness in the vertical direction of the shadow decreases, It becomes difficult to make the dirt inconspicuous. On the other hand, if the height (H) of the notch 3 is higher than 2/3 with respect to the height (T) of the eaves side end 2, the opening range in the vertical direction of the notch 3 becomes too wide and overlapped. It becomes difficult to form a shadow on the part, and the gap and dirt cannot be made inconspicuous. Further, if the height (H) of the notch 3 is less than 5 mm, the thickness of the shadow in the vertical direction is reduced, so that the shadow cannot be sufficiently formed and the gaps and dirt generated in the overlapped portion cannot be made inconspicuous. Note that the height (H) of the notch 3 is perpendicular to the eaves ridge direction from the position where the notch 3 opens on the back side of the roof tile 1 to the position where the notch 3 opens on the eave side of the roof tile 1. It is the length in the right direction.

屋根瓦１は、切欠部３の軒棟方向の長さ（Ｂ）及び高さ（Ｈ）が、上記のような範囲になることにより、屋根瓦１の敷設後に生じる隙間や雨水による汚れを目立たなくさせるのに適した影を形成することができるものである。 The roof tile 1 has a length (B) and a height (H) in the eaves ridge direction of the cutout portion 3 in the above-described range, so that gaps generated after the roof tile 1 is laid and dirt due to rainwater are conspicuous. A shadow suitable to be eliminated can be formed.

図１の例では、切欠部３の棟側の内面が平面状に形成されている。この切欠部３の棟側の内面は、屋根瓦１の表面に対して略直交する平面として形成されているが、厳密には、抜け勾配があるため軒棟方向と垂直な方向から軒側に約３〜５°程度傾斜した平面となっている。また、前記切欠部３の上部の内面が、前記切欠部３の軒側の内面の上端から軒側に向けて上方向に軒棟方向に対する傾斜角（α）０〜３５°で延伸するように形成されている。傾斜角（α）が０°より小さいと、雨水を屋根瓦１の露出面に沿って流すことができにくくなり、雨水による汚れを目立たなくすることができなくなるおそれがある。一方、傾斜角（α）が３５°を超えると、浅い角度から差し込む光に対して影を十分に形成しにくくなるおそれがある。この傾斜角（α）は０°よりも大きいのがさらに好ましい。それにより、雨水をさらに確実に、屋根瓦１の露出面に沿って（図１（ｂ）の矢印）、流すことができる。 In the example of FIG. 1, the inner surface of the notch 3 on the ridge side is formed in a flat shape. The inner surface of the notch 3 on the ridge side is formed as a plane that is substantially orthogonal to the surface of the roof tile 1, but strictly speaking, since there is a draft, the direction from the direction perpendicular to the eave ridge direction to the eave side The plane is inclined by about 3 to 5 °. Further, the inner surface of the upper portion of the notch portion 3 extends upward from the upper end of the inner surface of the eaves side of the notch portion 3 toward the eave side at an inclination angle (α) of 0 to 35 ° with respect to the eaves direction. Is formed. If the inclination angle (α) is smaller than 0 °, it becomes difficult for rainwater to flow along the exposed surface of the roof tile 1, and there is a possibility that dirt due to rainwater cannot be made inconspicuous. On the other hand, when the inclination angle (α) exceeds 35 °, there is a possibility that it is difficult to sufficiently form a shadow for light entering from a shallow angle. More preferably, the inclination angle (α) is larger than 0 °. Thereby, rainwater can be more reliably flowed along the exposed surface of the roof tile 1 (arrow in FIG. 1B).

また、切欠部３の軒棟方向長さ（Ｂ）は３〜１０ｍｍの範囲となっている。切欠部３の軒棟方向長さ（Ｂ）が３ｍｍより短いと十分な影が形成されにくくなり、隙間や汚れを目立たなくさせることができなくなるおそれがある。一方、前記切欠部３の軒棟方向長さ（Ｂ）が１０ｍｍより長いと軒側端部２の前端の強度が低下して踏割が発生するおそれがある。 Moreover, the eaves-ridge direction length (B) of the notch part 3 is the range of 3-10 mm. If the length (B) of the cutout portion 3 in the eaves ridge direction is shorter than 3 mm, it is difficult to form a sufficient shadow, and there is a possibility that gaps and dirt cannot be made inconspicuous. On the other hand, if the length (B) in the eaves ridge direction of the notch portion 3 is longer than 10 mm, the strength of the front end of the eaves side end portion 2 is lowered, and there is a possibility that a split is generated.

このような切欠部３が形成されることにより、風が切欠部３に吹き込んだとしても、乱流が発生して切欠部３のない形状よりも雨水が隙間に流れにくくなるので、十分な防水性を得て屋根の水仕舞を向上させることができる。また、浅い角度から差し込む光に対しても影を形成することができるので、重ね合わせ部分に生じる隙間や雨水による汚れをより目立たなくさせて屋根の美観が悪化するのを防止することができる。 By forming such a notch 3, even if wind blows into the notch 3, turbulence occurs and rainwater is less likely to flow into the gap than the shape without the notch 3. It can improve the water finish of the roof by gaining properties. Further, since a shadow can be formed even for light entering from a shallow angle, the appearance of the roof can be prevented from deteriorating by making the gap generated in the overlapped portion and dirt due to rainwater less noticeable.

また、図４の例のように、切欠部３の内面が、軒棟方向に対して棟側に向けて上り傾斜している傾斜面であると共に、前記切欠部３の軒棟方向長さ（Ｂ）が３〜１０ｍｍに形成されているものであることも好ましい。それにより、傾斜面を形成するという簡単な構成により切欠部３を形成することができるので、切欠部３を容易に屋根瓦１に形成することができ、簡単に屋根の美観が悪化するのを防止することができる。切欠部３の軒棟方向長さ（Ｂ）が３ｍｍより短いと十分な影が形成されにくくなり、隙間や汚れを目立たなくさせることができなくなるおそれがある。一方、前記切欠部３の軒棟方向長さ（Ｂ）が１０ｍｍより長いと軒側端部２の前端の強度が低下して踏割が発生するおそれがある。 Further, as in the example of FIG. 4, the inner surface of the notch portion 3 is an inclined surface that is inclined upward toward the ridge side with respect to the eaves ridge direction, and the length of the notch portion 3 in the eaves ridge direction ( It is also preferable that B) is formed to be 3 to 10 mm. Thereby, since the notch part 3 can be formed by the simple structure of forming an inclined surface, the notch part 3 can be easily formed in the roof tile 1, and the aesthetics of the roof easily deteriorates. Can be prevented. If the length (B) of the cutout portion 3 in the eaves ridge direction is shorter than 3 mm, it is difficult to form a sufficient shadow, and there is a possibility that gaps and dirt cannot be made inconspicuous. On the other hand, if the length (B) in the eaves ridge direction of the notch portion 3 is longer than 10 mm, the strength of the front end of the eaves side end portion 2 is lowered, and there is a possibility that a split is generated.

また、図５の例のように、切欠部３が、屋根瓦１の軒側と裏面側に開口する第１切欠部３ａと、第１切欠部３ａよりも棟側に形成され第１切欠部３ａ側と裏面側に開口する第２切欠部３ｂとから形成され、切欠部３が全体として二段になっていることも好ましい。それにより、風が切欠部３に吹き込んだとしても、図１に示す場合よりも複雑な乱流が発生して切欠部３がない形状よりも雨水がさらに隙間に流れにくくなるので、十分な防水性を得て屋根の水仕舞を向上させることができる。また、浅い角度から差し込む光に対しても影を形成することができると共に、隙間や汚れが見えたとしてもこの影がスリット状の模様を形成することにより、重ね合わせ部分に生じる隙間や雨水による汚れをより目立たなくさせて屋根の美観が悪化するのをさらに防止することができる。 In addition, as in the example of FIG. 5, the cutout portion 3 is formed on the ridge side of the first cutout portion 3a and the first cutout portion 3a that opens to the eave side and the back surface side of the roof tile 1, and the first cutout portion. It is also preferable that the cutout portion 3 is formed in two steps as a whole, which is formed from the second cutout portion 3b that opens to the back side and the 3a side. Thereby, even if the wind blows into the notch 3, the turbulent flow is more complicated than the case shown in FIG. 1, and rainwater is more unlikely to flow into the gap than the shape without the notch 3, so that it is sufficiently waterproof. It can improve the water finish of the roof by gaining properties. In addition, shadows can be formed even for light entering from a shallow angle, and even if gaps or dirt are seen, the shadows form slit-like patterns, resulting in gaps and rainwater generated in the overlapping part. It is possible to further prevent the appearance of the roof from deteriorating by making the dirt less noticeable.

第１切欠部３ａと第２切欠部３ｂとを合わせた切欠部３の軒棟方向長さ（Ｂ）は５〜１０ｍｍの範囲となっている。切欠部３の軒棟方向長さ（Ｂ）が５ｍｍより短いと十分な影が形成されにくくなり、隙間や汚れを目立たなくさせることができなくなるおそれがある。一方、前記切欠部３の軒棟方向長さ（Ｂ）が１０ｍｍより長いと軒側端部２の前端の強度が低下して踏割が発生するおそれがある。 The length (B) in the eaves-ridge direction of the notch 3 combining the first notch 3a and the second notch 3b is in the range of 5 to 10 mm. If the length (B) in the eaves ridge direction of the notch 3 is shorter than 5 mm, it is difficult to form a sufficient shadow, and there is a possibility that gaps and dirt cannot be made inconspicuous. On the other hand, if the length (B) in the eaves ridge direction of the notch portion 3 is longer than 10 mm, the strength of the front end of the eaves side end portion 2 is lowered, and there is a possibility that a split is generated.

第１切欠部３ａの棟側の内面は平面状に形成されている。第１切欠部３ａの上部の内面は、第１切欠部３ａの軒側の内面の上端から軒側に向けて上方向に傾斜角（α）０〜３５°で延伸している。また、第２切欠部３ｂの棟側の内面は平面状に形成されている。第２切欠部３ｂの上部の内面は、第２切欠部３ｂの軒側の内面の上端から軒側に向けて上方向に傾斜角（β）０〜３５°で延伸している。 The inner surface of the first cutout portion 3a on the ridge side is formed in a flat shape. The upper inner surface of the first notch 3a extends upward at an inclination angle (α) of 0 to 35 ° from the upper end of the inner surface of the first notch 3a toward the eave. Further, the inner surface of the second cutout portion 3b on the ridge side is formed in a flat shape. The upper inner surface of the second notch 3b extends upward at an inclination angle (β) of 0 to 35 ° from the upper end of the inner surface of the second notch 3b toward the eave.

このように傾斜角（α）（β）の範囲は０〜３５°である。傾斜角（α）（β）が０°より小さいと、雨水を屋根瓦１の露出面に沿って流すことができにくくなり、雨水による汚れを目立たなくすることができなくなるおそれがある。一方、傾斜角（α）（β）が３５°を超えると、浅い角度から差し込む光に対して影を十分に形成しにくくなるおそれがある。この傾斜角（α）（β）は０°よりも大きいのがさらに好ましい。それにより、雨水をさらに確実に、屋根瓦１の露出面に沿って流すことができる。なお、第１切欠部３ａ及び第２切欠部３ｂの棟側の内面は、屋根瓦１の表面に対して略直交する平面として形成されているが、厳密には、抜け勾配があるため軒棟方向と垂直な方向から軒側に約３〜５°程度傾斜した平面となっている。 Thus, the range of the inclination angle (α) (β) is 0 to 35 °. If the inclination angles (α) and (β) are smaller than 0 °, it becomes difficult for rainwater to flow along the exposed surface of the roof tile 1, and there is a possibility that dirt due to rainwater cannot be made inconspicuous. On the other hand, when the inclination angles (α) and (β) exceed 35 °, there is a possibility that it is difficult to form a sufficient shadow for light entering from a shallow angle. More preferably, the inclination angle (α) (β) is larger than 0 °. Thereby, rainwater can be made to flow along the exposed surface of the roof tile 1 more reliably. In addition, although the inner surface of the ridge side of the 1st notch part 3a and the 2nd notch part 3b is formed as a plane substantially orthogonal to the surface of the roof tile 1, strictly speaking, since there is a draft, the eaves ridge It is a plane inclined about 3 to 5 ° from the direction perpendicular to the direction to the eaves side.

また、第２切欠部３ｂの高さ（Ｈ２）は、第１切欠部３ａの高さ（Ｈ１）よりも小さいものであれば適宜設定し得るが、この高さ（Ｈ２）は第１切欠部の３ａ高さ（Ｈ１）に対して１／３〜２／３であるのが好ましい。また、第２切欠部３ｂの高さ（Ｈ２）は、屋根瓦１の軒側端部２の高さ（Ｔ）に対して１／６以上となることが好ましい。また、第１切欠部３の軒棟方向長さ（ｂ１）と第２切欠部３ｂの軒棟方向長さ（ｂ２）は、少なくともいずれか一方が１ｍｍ以上であることが好ましく、（ｂ１）／（ｂ２）＝１／３〜３／１となるように切欠部３が形成されているのがより好ましく、（ｂ１）＝（ｂ２）となるように切欠部３が形成されているのがさらに好ましい。 Further, the height (H2) of the second notch 3b can be set as appropriate as long as it is smaller than the height (H1) of the first notch 3a, but this height (H2) is the first notch. It is preferable that it is 1/3 to 2/3 with respect to 3a height (H1). Moreover, it is preferable that the height (H2) of the 2nd notch part 3b will be 1/6 or more with respect to the height (T) of the eaves side edge part 2 of the roof tile 1. FIG. Moreover, it is preferable that at least one of the eaves ridge direction length (b1) of the 1st notch part 3 and the eaves ridge direction length (b2) of the 2nd notch part 3b is 1 mm or more, (b1) / More preferably, the notch 3 is formed so that (b2) = 1/3 to 3/1, and the notch 3 is further formed so as to satisfy (b1) = (b2). preferable.

なお、第１切欠部３ａの高さ（Ｈ１）は、切欠部３全体の高さ（Ｈ）と等しく、軒側端部２の高さ（Ｔ）に対して１／６〜２／３、且つ、５ｍｍ以上となるように形成されている。そして、第２切欠部３ｂの高さ（Ｈ２）は、第１切欠部３ａよりも低く、軒側端部２の高さ（Ｔ）の２／３未満である。また、第１切欠部３ａの軒棟方向長さ（ｂ１）と第２切欠部３ｂの軒棟方向長さ（ｂ２）の合計が切欠部３全体の軒棟方向長さ（Ｂ）となっている。 In addition, the height (H1) of the first notch 3a is equal to the height (H) of the entire notch 3 and is 1/6 to 2/3 with respect to the height (T) of the eaves side end 2. And it is formed so that it may become 5 mm or more. And the height (H2) of the 2nd notch part 3b is lower than the 1st notch part 3a, and is less than 2/3 of the height (T) of the eaves side edge part 2. FIG. Moreover, the sum total of the eaves ridge direction length (b1) of the 1st notch part 3a and the eaves ridge direction length (b2) of the 2nd notch part 3b becomes the eaves ridge direction length (B) of the notch part 3 whole. Yes.

このように切欠部３の好ましい例として、具体的な三つの実施の形態を例示したが、本発明はこれに限られるものではない。例えば、切欠部３を曲面状に形成してもよいし、異なる傾斜角度を有する複数の傾斜面が設けられた形状として形成してもよい。また、三以上の切欠部３を備えるような切欠部３を設けてもよい。 As described above, three specific embodiments have been illustrated as preferable examples of the notch 3, but the present invention is not limited to this. For example, the cutout portion 3 may be formed in a curved surface shape, or may be formed in a shape provided with a plurality of inclined surfaces having different inclination angles. Moreover, you may provide the notch part 3 provided with the 3 or more notch part 3. FIG.

屋根瓦１は、適宜の材料及び方法にて形成することができるが、セメント系成形材料を成形した後に養生硬化したセメント系成型品であることや、粘土質材料を成形及び焼成した焼成品（粘度瓦）であることが好ましい。セメント系成形材料を用いた場合、屋根瓦１の厚みが増した場合でも屋根瓦１が重くなるのを抑えて、屋根瓦１を軽量化することができる。一方、屋根瓦１が焼成品である場合、焼成時にあばれが生じても、敷設時にこのあばれを吸収することができる。すなわち、焼成して得た屋根瓦１は、瓦の反りやねじれ、寸法のばらつきがいっそう発生しやすく、そのため、隙間が生じて美観を悪化させる傾向がより顕著となる。しかしながら、本発明によれば、切欠部３が影を形成するので、屋根瓦１が焼成品である場合であっても、隙間を目立たなくすることができ、美観の悪化を防止することができる。 The roof tile 1 can be formed by an appropriate material and method. The roof tile 1 is a cement-based molded product cured and cured after molding the cement-based molding material, or a fired product obtained by molding and firing a clay material ( Viscous roof tiles) are preferred. When the cement-based molding material is used, the roof tile 1 can be reduced in weight by suppressing the roof tile 1 from becoming heavy even when the thickness of the roof tile 1 is increased. On the other hand, in the case where the roof tile 1 is a fired product, even if a blowout occurs during firing, the blowout can be absorbed during laying. That is, the roof tile 1 obtained by firing is more susceptible to warping, twisting, and dimensional variation of the tile, and therefore, the tendency to create gaps and deteriorate the aesthetics becomes more prominent. However, according to the present invention, since the notch 3 forms a shadow, even if the roof tile 1 is a fired product, the gap can be made inconspicuous, and deterioration of aesthetics can be prevented. .

セメント系成形材料としては、セメントと水と油性物質とを主成分としてＷ／Ｏエマルションが形成されたセメント含有逆エマルション組成物を用いるのが好ましい。このようなセメント系成形材料は保形性が高く、屋根瓦１の作製に好適に用いることができる。 As the cement-based molding material, it is preferable to use a cement-containing inverse emulsion composition in which a W / O emulsion is mainly formed of cement, water, and an oily substance. Such a cement-based molding material has high shape retention, and can be suitably used for the production of the roof tile 1.

セメントとしては、特に制限されるものではないが、ポルトランドセメント、フライアッシュセメント、高炉セメント、アルミナセメント、ハイアルミナセメント、シリカフュームセメント、スラグセメント、早強セメント等を用いることができ、これらを一種単独で用いたり、二種以上を併用したりすることができる。セメント含有逆エマルション組成物におけるセメントと水の比率は任意に設定することができるが、重量比率で、セメント１に対して水０．３〜２の範囲であるのが一般的に好ましい。 The cement is not particularly limited, but Portland cement, fly ash cement, blast furnace cement, alumina cement, high alumina cement, silica fume cement, slag cement, early-strength cement, and the like can be used alone. Or can be used in combination of two or more. Although the ratio of cement and water in the cement-containing inverse emulsion composition can be arbitrarily set, it is generally preferred that the weight ratio is in the range of 0.3 to 2 water with respect to cement 1.

油性物質としては、特に制限されるものではないが、通常は疎水状の液状物質が利用され、例えばトルエン、キシレン、灯油、スチレン、ジビニルベンゼン、メチルメタクリレート、トリメチロールプロパントリメタクリレート、不飽和ポリエステル樹脂等を挙げることができ、これらを一種単独で用いたり、二種以上を併用したりすることができる。油性物質の配合量は任意に設定することができるが、セメント含有逆エマルション組成物中の水と固形分の総量に対して５〜１０体積％の範囲であるのが好ましい。 The oily substance is not particularly limited, but usually a hydrophobic liquid substance is used. For example, toluene, xylene, kerosene, styrene, divinylbenzene, methyl methacrylate, trimethylolpropane trimethacrylate, unsaturated polyester resin. These may be used alone or in combination of two or more. Although the compounding quantity of an oily substance can be set arbitrarily, it is preferable that it is the range of 5-10 volume% with respect to the total amount of the water and solid content in a cement containing inverse emulsion composition.

セメント含有逆エマルション組成物には、乳化剤を配合することが好ましい。乳化剤を配合することにより逆エマルションを安定化することができる。乳化剤としては、特に限定されるものではないが、例えば、ソルビタンセスキオール、グリセロールモノステアレート、ソルビタンモノオレート、ジエチレングリコールモノステアレート、ソルビタンモノステアレート、ジグリセロールモノオレート等の非イオン性界面活性剤、各種のアニオン系界面活性剤、カチオン系界面活性剤等を用いることができ、これらを一種単独で用いたり、二種以上を併用したりすることができる。乳化剤の配合量は任意に設定することができるが、セメント含有逆エマルション組成物中の水と固形分の総量に対して１〜３体積％の範囲であるのが好ましい。 It is preferable to add an emulsifier to the cement-containing inverse emulsion composition. By incorporating an emulsifier, the inverse emulsion can be stabilized. Although it does not specifically limit as an emulsifier, For example, nonionic surfactants, such as sorbitan sesquiol, glycerol monostearate, sorbitan monooleate, diethylene glycol monostearate, sorbitan monostearate, diglycerol monooleate Various anionic surfactants, cationic surfactants, and the like can be used, and these can be used alone or in combination of two or more. Although the compounding quantity of an emulsifier can be set arbitrarily, it is preferable that it is the range of 1-3 volume% with respect to the total amount of the water and solid content in a cement containing inverse emulsion composition.

セメント含有逆エマルションにはさらに、補強材、軽量化材、架橋剤、重合開始剤、各種添加剤などの材料・成分を適宜の量で配合することができる。補強材としては、例えば砂利、パーライト、シラスバルーン、ガラス粉、アルミナシリケートなどの骨材、ポリプロピレン繊維、アクリル繊維、ビニロン繊維、アラミド繊維等の合成繊維や、炭素繊維、ガラス繊維、パルプなどの補強繊維を挙げることができる。軽量化材としては、例えばパーライト等の無機系軽量化材や、アクリロニトリル発泡体、発泡ポリスチレン、ポリ塩化ビニリデン発泡体等の有機系軽量化材を用いることができる。架橋剤としては、例えばトリメチロールプロパントリメタクリレート等を用いることができる。重合開始剤としては、有機過酸化物や過硫酸塩等の重合開始剤、例えばｔ−ヘキシルパーオキシ−２−エチルヘキサノエート等を用いることができる。 Materials and components such as a reinforcing material, a weight reducing material, a crosslinking agent, a polymerization initiator, and various additives can be further blended in an appropriate amount in the cement-containing inverse emulsion. Examples of reinforcing materials include aggregates such as gravel, perlite, shirasu balloon, glass powder, and alumina silicate, synthetic fibers such as polypropylene fiber, acrylic fiber, vinylon fiber, and aramid fiber, and reinforcement such as carbon fiber, glass fiber, and pulp. Mention may be made of fibers. As the lightening material, for example, an inorganic lightening material such as pearlite, or an organic lightening material such as acrylonitrile foam, expanded polystyrene, or polyvinylidene chloride foam can be used. As the crosslinking agent, for example, trimethylolpropane trimethacrylate or the like can be used. As the polymerization initiator, a polymerization initiator such as an organic peroxide or persulfate, for example, t-hexylperoxy-2-ethylhexanoate can be used.

セメント含有逆エマルションの作製にあたっては、まず、乳化剤、スチレンモノマー、水、架橋剤及び重合開始剤を混合して逆エマルションを調製する。このとき、例えば、乳化剤（ヤシ油１〜２重量部）、スチレンモノマー４〜６重量％、水３５〜５０重量部、架橋剤適量、重合開始剤適量の配合比率にする。次に、この逆エマルションとセメントと軽量化材と補強繊維とを強制撹拌機又は連続混合機にて混合する。このとき、例えば、逆エマルション１００重量部に対して、セメント７０〜９０重量部、有機系軽量化材０．３〜５．０重量部、補強繊維１〜２重量部の配合比率としたり、逆エマルション１００重量部に対して、セメント５５〜７５重量部、無機系軽量化材１５〜３５重量部、補強繊維１〜２重量部の配合比率としたりする。これにより、屋根瓦１の作製に適したセメント含有逆エマルションを作製することができる。 In producing a cement-containing inverse emulsion, first, an emulsifier, a styrene monomer, water, a crosslinking agent and a polymerization initiator are mixed to prepare an inverse emulsion. At this time, for example, the blending ratio of emulsifier (1 to 2 parts by weight of palm oil), 4 to 6% by weight of styrene monomer, 35 to 50 parts by weight of water, an appropriate amount of a crosslinking agent, and an appropriate amount of a polymerization initiator is used. Next, the inverse emulsion, the cement, the lightening material, and the reinforcing fiber are mixed with a forced stirrer or a continuous mixer. At this time, for example, with respect to 100 parts by weight of the inverse emulsion, the blending ratio of 70 to 90 parts by weight of cement, 0.3 to 5.0 parts by weight of an organic lightening material, and 1 to 2 parts by weight of reinforcing fibers, For example, the blending ratio is 55 to 75 parts by weight of cement, 15 to 35 parts by weight of an inorganic lightening material, and 1 to 2 parts by weight of reinforcing fibers with respect to 100 parts by weight of the emulsion. Thereby, the cement containing inverse emulsion suitable for preparation of the roof tile 1 can be produced.

屋根瓦１の作製にあたっては、まず、上記のセメント系成形材料を、注型法、押出成形法、射出成形法、プレス成形法等の適宜の方法で成形する。その際、切欠部３は、切欠部３に対応する部分を突出させた成形型が用いられることにより成形されてもよいし、成形後に削り取るなどして切欠部３を形成してもよい。次に、例えば８０〜１００℃で６〜１５時間蒸気養生する。このようにして屋根瓦１を得ることができる。 In producing the roof tile 1, first, the cement-based molding material is molded by an appropriate method such as a casting method, an extrusion molding method, an injection molding method, or a press molding method. In that case, the notch part 3 may be shape | molded by using the shaping | molding die which protruded the part corresponding to the notch part 3, and may form the notch part 3 by scraping off after shaping | molding. Next, for example, steam curing is performed at 80 to 100 ° C. for 6 to 15 hours. In this way, the roof tile 1 can be obtained.

次に、本発明の屋根瓦１を屋根下地６に敷設して屋根を形成する方法について説明する。図６は屋根瓦１を敷設する様子を示した平面図である。 Next, a method for forming the roof by laying the roof tile 1 of the present invention on the roof base 6 will be described. FIG. 6 is a plan view showing how the roof tile 1 is laid.

屋根下地６は屋根瓦を載置するための下地である。屋根下地６は野地にて形成することができ、この場合、野地には必要に応じてアスファルトルーフィング等の防水シートを設けることができる。この屋根下地６上に、順次屋根瓦１を敷設する。 The roof base 6 is a base for placing roof tiles. The roof base 6 can be formed in a field, and in this case, a waterproof sheet such as asphalt roofing can be provided in the field as needed. The roof tiles 1 are sequentially laid on the roof base 6.

屋根瓦１を敷設するにあたっては、まず、複数の屋根瓦１を軒棟方向と直交する方向に順次載置する。このとき、まず屋根瓦１を屋根下地６上に配置し、この状態で固着孔１１にビスや釘等の固着具を打入して屋根下地６上に屋根瓦１を固定する。次いで、固定した屋根瓦１の、下重ね部４が設けられている側の側方に、別の屋根瓦１を配置する。このとき固定された屋根瓦１の下重ね部４に、別の屋根瓦１の上重ね部５を重ねるようにし、下重ね部４における固着具の固着位置を上重ね部５で覆うようにする。この状態で、前記別の屋根瓦１の固着孔１１に前記と同様にして固着具を打入して屋根下地６に固定する。この動作を複数回繰り返すことで、複数の屋根瓦１を軒棟方向と直交する方向に並べて敷設する。 In laying the roof tile 1, first, the plurality of roof tiles 1 are sequentially placed in a direction orthogonal to the eaves-ridge direction. At this time, the roof tile 1 is first arranged on the roof base 6, and in this state, a fixing tool such as a screw or a nail is driven into the fixing hole 11 to fix the roof tile 1 on the roof base 6. Next, another roof tile 1 is arranged on the side of the fixed roof tile 1 on the side where the lower overlap portion 4 is provided. At this time, the upper overlapping portion 5 of another roof tile 1 is overlapped with the lower overlapping portion 4 of the fixed roof tile 1, and the fixing position of the fixing tool in the lower overlapping portion 4 is covered with the upper overlapping portion 5. . In this state, the fixing tool is driven into the fixing hole 11 of the other roof tile 1 in the same manner as described above and fixed to the roof base 6. By repeating this operation a plurality of times, a plurality of roof tiles 1 are arranged in a direction orthogonal to the eaves-ridge direction.

次に、上記のように敷設された屋根瓦１（以下、一列目の屋根瓦１という）の棟側の屋根下地６上に、別の屋根瓦１（以下、二列目の屋根瓦１という）を配置する。図６に示す例では、二列目の屋根瓦１の横方向位置を一列目の屋根瓦１からずらして、千鳥状に配置している。このとき、一列目の屋根瓦１の棟側端縁における固着具の固着位置が、二列目の屋根瓦１にて覆われるように配置する。この状態で、二列目の屋根瓦１の固着孔１１に上記一列目の屋根瓦１の場合と同様に固着具を打入して、二列目の屋根瓦１を固定する。 Next, another roof tile 1 (hereinafter referred to as the second row roof tile 1) is placed on the roof base 6 on the ridge side of the roof tile 1 (hereinafter referred to as the first row roof tile 1) laid as described above. ). In the example shown in FIG. 6, the horizontal position of the roof tile 1 in the second row is shifted from the roof tile 1 in the first row and arranged in a staggered manner. At this time, it arrange | positions so that the adhering position of the fixing tool in the ridge side edge of the roof tile 1 of the 1st row may be covered with the roof tile 1 of the 2nd row. In this state, a fixing tool is driven into the fixing holes 11 of the second roof tile 1 in the same manner as the first roof tile 1 to fix the second roof tile 1.

次いで、一列目の屋根瓦１の場合と同様に、この二列目の固定した屋根瓦１の、下重ね部４が設けられている側に、別の屋根瓦１を載置する。このとき、先に固着された屋根瓦１と軒棟方向における位置を合わせると共に、一列目の屋根瓦１の棟側端縁における固着具の固着位置が二列目の屋根瓦１にて覆われるように配置する。 Next, as in the case of the roof tile 1 in the first row, another roof tile 1 is placed on the side of the fixed roof tile 1 in the second row where the lower overlap portion 4 is provided. At this time, the first roof tile 1 and the roof tile 1 are aligned with each other, and the fixing position of the fixing tool at the edge of the first roof tile 1 is covered with the second roof tile 1. Arrange as follows.

この動作を複数回繰り返すことにより、複数の二列目の屋根瓦１を軒棟方向と直交する方向に並べて敷設する。 By repeating this operation a plurality of times, a plurality of second-row roof tiles 1 are laid in a direction orthogonal to the eaves-ridge direction.

そして、同様に三列目、四列目と繰り返し屋根瓦１を複数列敷設することにより、屋根下地６上に複数の屋根瓦１を敷設する。そして、さらに棟包１４と差棟１５とを取り付ける等の作業が行われて、図７に示すような屋根を形成することができる。 Similarly, a plurality of roof tiles 1 are laid on the roof base 6 by laying a plurality of rows of roof tiles 1 in the third and fourth rows. Further, a work such as attaching the ridge package 14 and the difference ridge 15 is performed, and a roof as shown in FIG. 7 can be formed.

このように屋根瓦１を敷設した状態では、軒棟方向に隣り合う屋根瓦１同士では、図１に示すように軒側の屋根瓦１の表面に棟側の屋根瓦１の軒側端部２が重ねられている。このとき、屋根瓦１の表面と軒側端部２の下部との間は、美観を損ねないようにすると共に、雨水の吹き込みを防止するため、隙間が形成されないようにするか、隙間があってもその間隔が小さいことが望ましい。 In the state in which the roof tiles 1 are laid in this way, the roof tiles 1 adjacent to each other in the eave building direction, as shown in FIG. 2 are stacked. At this time, the gap between the surface of the roof tile 1 and the lower part of the eaves side end portion 2 should not be formed in order to prevent the appearance of rainwater and to prevent the rainwater from blowing. However, it is desirable that the interval is small.

しかしながら、野地の不陸や屋根瓦１の反り等によって、軒側の屋根瓦１の表面と棟側の屋根瓦１の軒側端部２の下部との間に隙間が形成されることがある。特に、図９の従来例のように屋根瓦１の軒側端部２の前端が重ね合わせ部分となった屋根瓦１の場合、屋根瓦１の表面が平坦なため形状等による目隠し作用がなく隙間が目立ちやすくなる。また、屋根瓦１が粘土質材料等を成形して得られるものである場合は、焼成して作製するため、瓦の反りやねじれ、寸法のばらつきがいっそう発生しやすく、そのため、隙間が生じて美観を悪化させる傾向がより顕著となる。また、屋根瓦１の露出面に沿って流れる雨水により作られた白い汚れが目立ちやすく、屋根の美観を損ねてしまう。 However, a gap may be formed between the surface of the eaves-side roof tile 1 and the lower part of the eaves-side end portion 2 of the ridge-side roof tile 1 due to unevenness in the field or warping of the roof tile 1. . In particular, in the case of the roof tile 1 in which the front end of the eaves side end portion 2 of the roof tile 1 is an overlapping portion as in the conventional example of FIG. The gap becomes conspicuous. In addition, when the roof tile 1 is obtained by molding a clay-like material or the like, the roof tile 1 is produced by firing, so that the warp, twist, and dimensional variation of the tile are more likely to occur. The tendency to deteriorate aesthetics becomes more prominent. Moreover, the white stain | pollution | contamination made with the rain water which flows along the exposed surface of the roof tile 1 tends to be conspicuous, and the aesthetics of the roof are impaired.

そのような場合であっても、本発明によれば、この屋根を軒側（木口）から見ると切欠部３の奥行き（Ｂ）により、屋根の段差の一部がセットバックした状態となり、この部分に影が形成され、全体としてスリット状の模様を形成して隙間や汚れを目立たなくすることができる。 Even in such a case, according to the present invention, when the roof is viewed from the eave side (the end), a part of the step of the roof is set back due to the depth (B) of the notch 3. A shadow is formed on the portion, and a slit-like pattern can be formed as a whole so that gaps and dirt can be made inconspicuous.

図８は、本発明の屋根瓦１（１ａ）と従来の屋根瓦１（１ｂ）とが敷設された屋根を軒側から見た要部の説明図である。図８の左側には従来の屋根瓦１ｂが、右側には本発明の屋根瓦１ａが、それぞれ敷設されている。従来の屋根瓦１ｂでは影Ｓが形成されておらず、隙間や汚れが目立つ構造となっている。それに対し、本発明の屋根瓦１ａでは重ね合わせ部分に影Ｓが形成されているので、隙間や汚れが目立たない。 FIG. 8 is an explanatory diagram of a main part when a roof on which the roof tile 1 (1a) of the present invention and the conventional roof tile 1 (1b) are laid is viewed from the eaves side. The conventional roof tile 1b is laid on the left side of FIG. 8, and the roof tile 1a of the present invention is laid on the right side. In the conventional roof tile 1b, no shadow S is formed, and a gap or dirt is conspicuous. On the other hand, in the roof tile 1a of the present invention, since the shadow S is formed in the overlapping portion, the gap and dirt are not noticeable.

このように、本発明によれば、軒側の屋根瓦１と棟側の屋根瓦１との間に隙間が形成されたり、雨水によりほこりが堆積して白い汚れが付着したりしても、屋根瓦１の敷設後にはこの切欠部３に影が形成されるので、隙間や汚れを目立たなくすることができ、屋根の美観が悪化するのを防止することができる。 Thus, according to the present invention, even if a gap is formed between the roof tile 1 on the eaves side and the roof tile 1 on the ridge side, or dust accumulates due to rainwater and white dirt adheres, Since the shadow is formed in the notch 3 after the roof tile 1 is laid, gaps and dirt can be made inconspicuous, and the appearance of the roof can be prevented from deteriorating.

本発明の屋根瓦の一例を敷設した屋根構造を示す断面図であり、（ａ）は概略図、（ｂ）は要部拡大図である。It is sectional drawing which shows the roof structure which laid down an example of the roof tile of this invention, (a) is schematic and (b) is a principal part enlarged view. 本発明の屋根瓦の一例を示す平面図である。It is a top view which shows an example of the roof tile of this invention. 本発明の屋根瓦の一例を示し、図２のＡ−Ａ断面図である。An example of the roof tile of this invention is shown, and it is AA sectional drawing of FIG. 本発明の屋根瓦の他の一例を敷設した屋根構造を示す要部の断面図である。It is sectional drawing of the principal part which shows the roof structure which laid another example of the roof tile of this invention. 本発明の屋根瓦の他の一例を敷設した屋根構造を示す要部の断面図である。It is sectional drawing of the principal part which shows the roof structure which laid another example of the roof tile of this invention. 本発明の屋根瓦の一例を敷設する様子を示す平面図である。It is a top view which shows a mode that an example of the roof tile of this invention is laid. 本発明の屋根瓦の一例を敷設した屋根の一例を示す斜視図である。It is a perspective view which shows an example of the roof which laid down an example of the roof tile of this invention. 本発明の屋根瓦の一例を敷設した屋根と従来の屋根瓦を敷設した屋根とを比較する説明図である。It is explanatory drawing which compares the roof which laid down an example of the roof tile of this invention, and the roof which laid the conventional roof tile. 従来例の屋根瓦を敷設した屋根構造を示す概略断面図である。It is a schematic sectional drawing which shows the roof structure which laid the roof tile of the prior art example.

Explanation of symbols

１屋根瓦
２軒側端部
３切欠部
４下重ね部
５上重ね部
６屋根下地
７前垂部
８立ち上がり部
１０支持部
１１固着孔 DESCRIPTION OF SYMBOLS 1 Roof tile 2 Eaves side edge part 3 Notch part 4 Lower overlapping part 5 Upper overlapping part 6 Roof base 7 Front hanging part 8 Standing part 10 Support part 11 Fixing hole

Claims

A roof tile that is laid on the roof and has a flat surface , and at the eave side end of the roof tile, a notch that opens to the eave side and the back side is formed at the lower part of the eave side end surface .
The inner surface on the ridge side of the notch portion is formed in a flat shape, and the inner surface of the upper portion of the notch portion is inclined upwardly from the upper end of the inner surface on the eave side of the notch portion with respect to the eaves ridge direction ( [alpha]) A roof tile that extends at 0 to 35 [deg.] ([alpha] is not 0 [deg.]) .

A roof tile with a flat surface that is laid on the roof, and a notch that opens to the eave side and the back side is formed at the eave side end of the roof tile,
From the 1st notch part which the said notch part opens to the eaves side and back side of a roof tile, and the 1st notch part formed in the ridge side rather than the 1st notch part, and opens to the 1st notch part side and back side The second notch with a low height,
The inner surface on the ridge side of the first notch is formed in a flat shape, and the inner surface of the upper portion of the first notch is directed upward from the upper end of the inner surface of the eaves side of the first notch toward the eaves. Stretched at an inclination angle (α) of 0 to 35 °,
The inner surface on the ridge side of the second notch is formed in a planar shape, and the inner surface of the upper portion of the second notch is directed upward from the upper end of the inner surface of the eaves side of the second notch toward the eaves. inclination angle (beta) 0 to 35 roof tiles characterized in that it stretched °.

The roof tile is 15 to 35 mm in height (T) at the eave side end in a state laid on the roof,
The length (B) in the eaves ridge direction of the notch is 1/5 to 2/7 with respect to the height (T), and the height (H) of the notch is set to the height (T). The roof tile according to claim 1 or 2 , wherein the roof tile is 1/6 to 2/3 and 5 mm or more .