JP5453051B2

JP5453051B2 - Manufacturing method of resin products

Info

Publication number: JP5453051B2
Application number: JP2009245868A
Authority: JP
Inventors: 信之進筒野; 正義唐木; 秀介中島
Original assignee: 天馬株式会社
Priority date: 2009-10-26
Filing date: 2009-10-26
Publication date: 2014-03-26
Anticipated expiration: 2029-10-26
Also published as: JP2011088417A

Description

本発明は、例えばキャスターに用いられる樹脂製車輪等の樹脂製品の製造方法に関する。 The present invention, for example a method for producing a resin product of the resin wheel and the like used in the caster.

家庭用家具等には、人力で移動させやすいようにキャスターが使用されており、キャスター用車輪には樹脂製のものが広く用いられている（例えば、特許文献１参照）。 Casters are used for household furniture and the like so as to be easily moved by human power, and resin wheels are widely used for caster wheels (see, for example, Patent Document 1).

このようなキャスターに用いられる樹脂製車輪（以下、キャスター用車輪という。）を製造する場合、単純な割金型を用いて製造することがコスト面から見て一般的である。 When manufacturing a resin wheel used for such a caster (hereinafter, referred to as a caster wheel), it is general from the viewpoint of cost to manufacture using a simple split mold.

実用新案登録第３１１０９２９号公報Utility Model Registration No. 3110929

図１１は、従来のキャスター用車輪１０１、及びキャスター用車輪１０１を割金型１００、１００’を用いて製造（成形）する従来の製造方法を説明する図である。
割金型１００、１００’を用いて製造される従来のキャスター用車輪１０１は、外周面１０２上にパーティングライン１０３を有する。そのため、製造方法の精度によっては、パーティングライン１０３にバリ１０４や段差１０５（図１２参照）が生じてしまう。パーティングライン部１０３に生じたバリ１０４や段差１０５は床に傷をつける恐れがある。
対応策として、成形精度を上げるために、金型の材質変更等が検討されるが、コストがかかる上、バリや段差を完全に解消することは容易ではない。また、樹脂製品製造後の加工によりバリや段差を処理することが一般的に行われているが、その分、作業工程が多くなり、人手、時間を多く要し、コスト面でも不利であるという問題があった。 FIG. 11 is a diagram for explaining a conventional manufacturing method for manufacturing (molding) the conventional caster wheel 101 and the caster wheel 101 using the split molds 100 and 100 ′.
A conventional caster wheel 101 manufactured using the split molds 100 and 100 ′ has a parting line 103 on an outer peripheral surface 102. For this reason, depending on the accuracy of the manufacturing method, a burr 104 or a step 105 (see FIG. 12) may occur in the parting line 103. The burr 104 and the step 105 generated in the parting line part 103 may damage the floor.
As countermeasures, in order to increase the molding accuracy, a change in the material of the mold or the like is considered, but it is costly and it is not easy to completely eliminate burrs and steps. In addition, it is generally performed to process burrs and steps by processing after resin product manufacture, but the work process is increased by that amount, requiring a lot of manpower and time, which is disadvantageous in terms of cost. There was a problem.

本発明は、上記事情に鑑みてなされたものであって、溝部の底部にパーティングラインを有する樹脂製品を低コストで簡単に得られる製造方法を提供することを目的とする。 The present invention was made in view of the above circumstances, and an object thereof is to provide a manufacturing how easily obtained in a resin product cost with parting line at the bottom of the groove.

（１）本発明の樹脂製品の製造方法は、型合わせ面付近にアンダーカットが施された一対の割金型からなる成形金型を用いて、型締めされた前記成形金型内に樹脂を注入し、硬化後、むり抜きすることにより、型開きし、溝部の底部にパーティングラインを有し、さらに、片面に前記溝部が形成された板状部と、前記板状部の前記溝部とは反対側の面に突出する凸部とを有する樹脂製品を得るとともに、前記成形金型は、前記樹脂の収縮現象により生じた前記樹脂製品の外形寸法より前記アンダーカットの高さ寸法が小さいことを特徴とする。
（２）本発明の樹脂製品の製造方法において、前記樹脂製品は、キャスター用車輪であって、外周面全周に前記溝部を有するものであることが好ましい。 (1) In the method for producing a resin product of the present invention, a resin is placed in the mold that has been clamped by using a mold that is a pair of split molds that are undercut near the mold mating surface. injected, after curing, by forcibly drained, mold opening, have a parting line at the bottom of the groove, further, a plate-shaped portion in which the groove on one side is formed, and the groove portion of the plate-like portion Obtains a resin product having a convex portion protruding on the opposite surface, and the molding die has a height dimension of the undercut smaller than the outer dimension of the resin product caused by the shrinkage phenomenon of the resin. It is characterized by .
(2) In the method for producing a resin product of the present invention, the resin product is a wheel for casters, and preferably has the groove on the entire outer circumference.

本発明の樹脂製品の製造方法によれば、構成が単純な割金型を用いて、溝部の底部にパーティングラインを有する樹脂製品を簡単に低コストで得られる。更に、バリや段差の修正といった二次加工の必要がないため、作業工程が省略化される。 According to the method for producing a resin product of the present invention, a resin product having a parting line at the bottom of the groove can be obtained easily and at low cost using a split mold having a simple configuration. Further, since there is no need for secondary processing such as correction of burrs or steps, the work process is omitted.

本発明の実施形態に係るキャスター用車輪の斜視図である。It is a perspective view of the wheel for casters concerning the embodiment of the present invention. 本発明の実施形態に係るキャスター用車輪のハブ部の軸方向に沿う断面図である。It is sectional drawing which follows the axial direction of the hub part of the wheel for casters which concerns on embodiment of this invention. 本発明の実施形態に係るキャスター用車輪の製造方法で用いられる成形金型の断面図である。It is sectional drawing of the shaping die used with the manufacturing method of the wheel for casters concerning embodiment of this invention. 本発明の実施形態に係るキャスター用車輪の製造方法を説明する図であって、型締めされた成形金型内に注入された溶融状態の樹脂を前記成形金型内で硬化させて、キャスター用車輪を成形した状態を示す断面図である。It is a figure explaining the manufacturing method of the wheel for casters concerning the embodiment of the present invention, Comprising: The resin in the molten state poured into the mold which was clamped is hardened in the mold, and it is for casters It is sectional drawing which shows the state which shape | molded the wheel. 本発明の実施形態に係るキャスター用車輪の製造方法におけるむり抜きの工程を示す説明図である。It is explanatory drawing which shows the process of the hollow in the manufacturing method of the wheel for casters which concerns on embodiment of this invention. 本発明の実施形態に係るロック部が枢着されたフタ式ボックスの斜視図である。It is a perspective view of the lid type box to which the lock part concerning the embodiment of the present invention was pivotally attached. 図６のフタ式ボックスのフタの裏側を示す部分拡大斜視図である。It is a partial expansion perspective view which shows the back side of the lid | cover of the lid-type box of FIG. 図７のフタ式ボックスのフタに枢着されたロック部に形成された溝部の説明図である。It is explanatory drawing of the groove part formed in the lock | rock part pivotally attached to the cover of the lid-type box of FIG. 本発明の実施形態に係るハンドル部が備えられた移動式棚の斜視図である。It is a perspective view of a mobile shelf provided with a handle part according to an embodiment of the present invention. 図９のハンドル部に形成された溝部の説明図である。It is explanatory drawing of the groove part formed in the handle | steering-wheel part of FIG. 従来のキャスター用車輪、及びキャスター用車輪を割金型を用いて製造する従来の製造方法を説明する図である。It is a figure explaining the conventional manufacturing method which manufactures the wheel for conventional casters and the wheel for casters using a split mold. 従来の製造方法により得られるキャスター用車輪に段差が生じた例を示す図である。It is a figure which shows the example which the level | step difference produced in the wheel for casters obtained by the conventional manufacturing method.

本発明の樹脂製品の製造方法により得られる樹脂製品の実施形態について説明する。なお、この実施形態は、発明の趣旨をより良く理解させるために具体的に説明するものであり、特に指定のない限り、本発明を限定するものではない。 An embodiment of a resin product obtained by the method for producing a resin product of the present invention will be described. In addition, this embodiment is specifically described in order to make the gist of the invention better understood, and does not limit the present invention unless otherwise specified.

本発明の樹脂製品の製造方法により得られる樹脂製品の一実施形態として、図１に示すキャスター用車輪を説明する。
図１は、本発明の実施形態に係るキャスター用車輪の斜視図である。図１に示すキャスター用車輪１は、ハブ部２、リム部３及び前記ハブ部２と前記リム部３間の支持部４からなる樹脂製品である。キャスター用車輪１は、ハブ部２を介して移動式収納体（例えば図６のフタ式ボックス）に設けられた車輪取付部に回転自在に取り付けられる。 A caster wheel shown in FIG. 1 will be described as an embodiment of a resin product obtained by the method for producing a resin product of the present invention.
FIG. 1 is a perspective view of a caster wheel according to an embodiment of the present invention. A caster wheel 1 shown in FIG. 1 is a resin product including a hub portion 2, a rim portion 3 and a support portion 4 between the hub portion 2 and the rim portion 3. The caster wheel 1 is rotatably attached to a wheel attachment portion provided in a movable storage body (for example, a lid type box in FIG. 6) via a hub portion 2.

図２は本発明の実施形態に係るキャスター用車輪１のハブ部２の軸方向に沿う断面図である。
図２に例示したキャスター用車輪１の支持部４は、円筒状のハブ部２の外周にフランジ状に突設されており、前記ハブ部２と前記リム部３との間を橋絡している。前記リム部３は、前記支持部４を介して、前記ハブ部２の外側に同心状に設けられ、円筒状に形成されている。前記リム部３は、前記支持部４に直行する向きで、支持部４の両側に張り出すように突出する板状に形成されており、本発明に係る板状部として機能する。キャスター用車輪１において、前記支持部４は前記リム部３の片面に形成された前記溝部６とは反対側の面に形成されており、本発明に係る凸部として機能する。 FIG. 2 is a sectional view along the axial direction of the hub portion 2 of the caster wheel 1 according to the embodiment of the present invention.
The support portion 4 of the caster wheel 1 illustrated in FIG. 2 is projected in a flange shape on the outer periphery of the cylindrical hub portion 2, and bridges between the hub portion 2 and the rim portion 3. Yes. The rim portion 3 is provided concentrically outside the hub portion 2 via the support portion 4 and is formed in a cylindrical shape. The rim portion 3 is formed in a plate shape protruding so as to project on both sides of the support portion 4 in a direction perpendicular to the support portion 4 and functions as a plate-like portion according to the present invention. In the caster wheel 1, the support portion 4 is formed on a surface opposite to the groove portion 6 formed on one surface of the rim portion 3, and functions as a convex portion according to the present invention.

前記キャスター用車輪１の材質は、キャスターの分野における一般的な材質であれば、特に限定されないが、ナイロンやポリプロピレンが好ましく、ポリプロピレンがより好ましい。 The material of the caster wheel 1 is not particularly limited as long as it is a general material in the field of casters, but nylon and polypropylene are preferable, and polypropylene is more preferable.

次に本発明の樹脂製品の製造方法の一例として、キャスター用車輪１の製造方法について図３、図４及び図５を用いて説明する。図３は、本発明の実施形態に係るキャスター用車輪の製造方法で用いられる成形金型の断面図である。図４は、本発明の実施形態に係るキャスター用車輪１の製造方法を説明する図であって、型締めされた成形金型１０内に注入された溶融状態の樹脂を前記成形金型内で硬化させて、キャスター用車輪１を成形した状態を示す断面図である。図５は、本発明の実施形態に係るキャスター用車輪１の製造方法におけるむり抜きの工程を示す説明図である。 Next, as an example of the method for producing the resin product of the present invention, a method for producing the caster wheel 1 will be described with reference to FIGS. FIG. 3 is a cross-sectional view of a molding die used in the method for manufacturing a caster wheel according to the embodiment of the present invention. FIG. 4 is a diagram for explaining a method of manufacturing the caster wheel 1 according to the embodiment of the present invention, in which molten resin injected into the mold 10 that has been clamped is injected into the mold. It is sectional drawing which shows the state which it hardened | cured and shape | molded the wheel 1 for casters. FIG. 5 is an explanatory diagram showing a hollowing process in the method for manufacturing the caster wheel 1 according to the embodiment of the present invention.

キャスター用車輪１の製造方法は、型合わせ面８、８’付近にアンダーカットが施された一対の割金型１１、１１’からなる成形金型１０を用いて、型締めされた前記成形金型１０内に樹脂を注入し、樹脂の硬化後、成形金型１０をむり抜きすることにより、型開きし、溝部６の底部にパーティングライン７を有するキャスター用車輪１を得る方法である。 The caster wheel 1 is manufactured by using a molding die 10 composed of a pair of split molds 11 and 11 ′ having an undercut in the vicinity of the die mating surfaces 8 and 8 ′, and then clamping the molding die. In this method, a resin is poured into the mold 10, and after the resin is cured, the mold 10 is peeled off to open the mold and obtain a caster wheel 1 having a parting line 7 at the bottom of the groove 6.

まず、キャスター用車輪１の製造方法で用いられる成形金型１０について説明する。図３に示されるように、型締め状態の成形金型１０は、キャビティー金型である左右一対の割金型１１、１１’から構成されている。型締め後の成形金型１０は、内部にキャスター用車輪１を成形するためのキャビティーを有する。前記キャビティーは、リム部成形用キャビティー１２、支持部成形用キャビティー１３、ハブ部成形用キャビティー１４からなる。支持部成形用キャビティー１３からは、リム部成形用キャビティー１２が張り出し、リム部成形用キャビティー１２には、キャスター用車輪１のリム部３に溝部６を形成するため、型合わせ面８、８’付近にアンダーカットが施されている（アンダーカット部９、９’が形成されている。）。
図３に示されるように、アンダーカット部９、９’は、各割金型１１、１１’の型合わせ面８、８’付近から突出する突起状に形成されている。
本発明で用いられる成形金型１０においては、型開きの際、成形されたキャスター用車輪１をむり抜きによって取出すことができるように、アンダーカット部９、９’の高さ寸法を調整してある。具体的には、樹脂は硬化時に収縮する性質を有するため、樹脂の収縮現象により生じた外形寸法よりアンダーカット部９、９’の高さ寸法が小さくなるように調整することが好ましい。
なお、本明細書および特許請求の範囲において、「むり抜き」とは、金型中にアンダーカット部があるのにもかかわらず、引っかかりを考慮せずに金型から成形樹脂を強制的に抜く工法を意味する。 First, the molding die 10 used with the manufacturing method of the wheel 1 for casters is demonstrated. As shown in FIG. 3, the mold 10 in a clamped state is composed of a pair of left and right split molds 11 and 11 ′ that are cavity molds. The mold 10 after mold clamping has a cavity for molding the caster wheel 1 therein. The cavity includes a rim portion forming cavity 12, a support portion forming cavity 13, and a hub portion forming cavity 14. A rim molding cavity 12 protrudes from the support molding cavity 13, and a groove 6 is formed in the rim 3 of the caster wheel 1 in the rim molding cavity 12, so that the die matching surface 8 is formed. , 8 'is undercut (undercut portions 9, 9' are formed).
As shown in FIG. 3, the undercut portions 9 and 9 ′ are formed in a protruding shape protruding from the vicinity of the mold matching surfaces 8 and 8 ′ of the split molds 11 and 11 ′.
In the molding die 10 used in the present invention, the height dimensions of the undercut portions 9 and 9 ′ are adjusted so that the caster wheel 1 can be removed by peeling when the mold is opened. is there. Specifically, since the resin has a property of shrinking at the time of curing, it is preferable to adjust the height of the undercut portions 9 and 9 ′ to be smaller than the outer dimension caused by the shrinkage phenomenon of the resin.
In the present specification and claims, the term “peeling” means that the molding resin is forcibly removed from the mold without considering the catches even though the mold has an undercut portion. Means construction method.

次に、キャスター用車輪１の製造方法について図４及び図５を利用して説明する。
図４に示されるように、型締め状態の成形金型１０内に溶融した樹脂を注入し、前記成形金型内で樹脂を硬化させる。図４に示されるキャスター用車輪１の射出成形が終了した後、図５に示すように、両割金型１１、１１’を左右に型開きして、キャスター用車輪１の離型を行うが、上述したように、両割金型１１、１１’には、キャスター用車輪１のリム部３に溝部６を形成するために、型合わせ面８、８’付近にアンダーカットが施されており、型開きの際、アンダーカット部９、９’が成形されたキャスター用車輪１のリム部３に引っかかるため、むり抜きにより離型することになる。むり抜きの際には、前述した金型内における樹脂の収縮現象を利用することが好ましい。
成形されたキャスター用車輪１は両割金型１１、１１’の型合わせ面８、８’の接合境界に沿って、パーティングライン７を有し、前記パーティングライン７は、アンダーカット部９、９’によって形成された溝部６の底部に位置する。 Next, the manufacturing method of the wheel 1 for casters is demonstrated using FIG.4 and FIG.5.
As shown in FIG. 4, molten resin is injected into the mold 10 in a clamped state, and the resin is cured in the mold. After the injection molding of the caster wheel 1 shown in FIG. 4 is completed, as shown in FIG. 5, the split molds 11 and 11 ′ are opened left and right to release the caster wheel 1. As described above, the split molds 11 and 11 ′ are undercut near the mold matching surfaces 8 and 8 ′ in order to form the groove 6 in the rim 3 of the caster wheel 1. When the mold is opened, the undercut portions 9 and 9 'are caught on the rim portion 3 of the caster wheel 1 formed, so that the mold is released by peeling. In stripping, it is preferable to use the above-described shrinkage phenomenon of the resin in the mold.
The caster wheel 1 thus formed has a parting line 7 along the joining boundary between the die-matching surfaces 8 and 8 'of the split molds 11 and 11'. , 9 'is located at the bottom of the groove 6 formed.

本発明の樹脂製品の製造方法によれば、既存の金型装置にアンダーカットを施すだけで、溝部を簡単に形成することができるので、金型製作に要する経費を大幅に低減させることが可能となる。
金型中に前記アンダーカットがある場合、通常はスライド構造の金型（スライド型金型）を採用する。このような金型を新たに採用することはコストアップにつながるだけではなく、スライド型金型が位置決めをする時間がかかる場合があり、その結果、一定時間当たりの生産量が低下する。また、スライド型金型を用いることにより更にパーティングラインの数が増えることになる。
本発明の樹脂製品の製造方法は、経済面及び生産性の面からも優れている。 According to the resin product manufacturing method of the present invention, a groove can be easily formed by simply undercutting an existing mold apparatus, so that the cost required for mold manufacture can be greatly reduced. It becomes.
When the mold has the undercut, a slide structure mold (slide mold) is usually employed. Adopting such a mold not only leads to an increase in cost, but it may take time for the slide mold to position, and as a result, the production amount per fixed time decreases. In addition, the number of parting lines is further increased by using a slide mold.
The method for producing a resin product of the present invention is also excellent from the viewpoints of economy and productivity.

本発明の樹脂製品の製造方法は、単純な一対の割金型からなる成形金型を用いて、型締めされた前記成形金型内に樹脂を注入し、樹脂硬化後、型開きし、樹脂製品を取出す方法であるため、成形後の樹脂製品には型合わせ面８、８’の接合境界に沿ってパーティングライン７が生じる。
図１に示すように、キャスター用車輪１は、外周面５全周に溝部６を有し、パーティングライン７は溝部６の底部に生じるため、パーティングライン７上にバリや段差が形成されたとしても、前記キャスター用車輪１を有する移動式収納体（例えば図６のフタ式ボックス）が自由方向に動く際、床などを傷つける恐れがなく、また前記移動式収納体が自由方向に動く時、そのバリや段差が抵抗とならず、各方向に自由に動き回れる。 The method for producing a resin product according to the present invention uses a molding die composed of a simple pair of split molds, injects resin into the clamped mold, cures the resin, and then opens the mold. Since this is a method for taking out the product, a parting line 7 is formed along the joining boundary of the die mating surfaces 8 and 8 'in the molded resin product.
As shown in FIG. 1, the caster wheel 1 has a groove 6 on the entire circumference of the outer peripheral surface 5, and the parting line 7 is formed at the bottom of the groove 6, so that burrs and steps are formed on the parting line 7. Even when the mobile storage body (for example, the lid type box in FIG. 6) having the caster wheels 1 moves in the free direction, there is no risk of damaging the floor or the like, and the mobile storage body moves in the free direction. At that time, the burrs and steps do not act as resistance and can move freely in each direction.

図２は本発明の実施形態に係るキャスター用車輪１のハブ部２の軸方向に沿う断面図である。
前述したように、図２に例示したキャスター用車輪１は、片面に前記溝部が形成された板状部と、前記板状部の前記溝部とは反対側の面に突出する凸部と、を有するものである。
キャスター用車輪１をこのように設計することで、溝部６にヒケが生じ、溝部６をさらに深くしている。このような製品ヒケ現象を利用することにより、割金型のアンダーカット部９，９’のサイズを大きくしなくても確実に溝部６を形成できる。本発明の樹脂製品の製造方法は、このような構成を有する樹脂製品の製造方法であることが好ましい。本発明の樹脂製品の製造方法によると、製造された樹脂製品のバリや段差の修正といった二次加工が不要となる。 FIG. 2 is a sectional view along the axial direction of the hub portion 2 of the caster wheel 1 according to the embodiment of the present invention.
As described above, the caster wheel 1 illustrated in FIG. 2 includes a plate-like portion in which the groove portion is formed on one surface, and a convex portion protruding on the surface of the plate-like portion opposite to the groove portion. It is what you have.
By designing the caster wheel 1 in this way, sink marks are generated in the groove 6 and the groove 6 is further deepened. By utilizing such a product sink phenomenon, the groove 6 can be reliably formed without increasing the size of the undercut portions 9 and 9 'of the split mold. The method for producing a resin product of the present invention is preferably a method for producing a resin product having such a configuration. According to the method for producing a resin product of the present invention, secondary processing such as correction of burrs and steps of the produced resin product is not necessary.

本発明の樹脂製品の製造方法により得られる樹脂製品の他の実施形態として、図６〜図８に示すフタ式ボックス１５のロック部１６を説明する。 As another embodiment of the resin product obtained by the method for producing a resin product of the present invention, a lock portion 16 of a lid type box 15 shown in FIGS. 6 to 8 will be described.

図６は、本発明の実施形態に係るロック部１６が枢着されたフタ式ボックス１５の斜視図である。図６に示されるボックス１７はフタ１８を有し、フタ１８にはロック部１６が枢着されている。ボックス１７及びフタ１８はフタ１８に枢着されたロック部１６を介してロックされる。図７は図６のフタ式ボックスのフタの裏側を示す部分拡大斜視図である。図７に示されるようにロック部１６は主壁１６ａ、係合突部１６ｂ及び指掛け部１６ｃからなる。図８は図７に示されるフタ１８に枢着されたロック部１６に形成された溝部２１の説明図であり、より詳細には図７に示されるロック部１６における指掛け部１６ｃを含む断面図を用いて説明するものである。ロック部１６はＬ字状の主壁１６ａを有し、前記主壁１６ａの屈曲部を介して一端側がフタ１８に枢着されており、他端側には前記ボックス１７に係脱可能な係合突部１６ｂ及び指掛け部１６ｃが形成される。
図８（ａ）は、対比例として示されたロック部の断面図であり、図８（ｂ）は、本発明の実施形態として図７に示されたロック部１６の断面図である。図８（ａ）に示される対比例において、指掛け部２０は、主壁１９と反対側の面にパーティングライン２２を有する。前記パーティングライン２２には、バリ２４が生じる場合があり、前記パーティングライン２２を有する面は指が接触する面である。図８（ｂ）に示されるように、溝部２１を形成することでパーティングライン２３にバリが生じたとしても指を傷つける危険を避けることができ、安全で良好な使用状態を得ることができる。 FIG. 6 is a perspective view of the lid type box 15 to which the lock portion 16 according to the embodiment of the present invention is pivotally attached. The box 17 shown in FIG. 6 has a lid 18, and a lock portion 16 is pivotally attached to the lid 18. The box 17 and the lid 18 are locked via a lock portion 16 pivotally attached to the lid 18. 7 is a partially enlarged perspective view showing the back side of the lid of the lid type box of FIG. As shown in FIG. 7, the lock portion 16 includes a main wall 16a, an engagement protrusion 16b, and a finger hook portion 16c. FIG. 8 is an explanatory view of the groove portion 21 formed in the lock portion 16 pivotally attached to the lid 18 shown in FIG. 7, and more specifically, a cross-sectional view including the finger hook portion 16c in the lock portion 16 shown in FIG. This will be described using. The lock portion 16 has an L-shaped main wall 16a. One end side of the lock portion 16 is pivotally attached to the lid 18 through a bent portion of the main wall 16a, and the other end side is detachable from the box 17. A mating protrusion 16b and a finger hook 16c are formed.
8A is a cross-sectional view of the lock portion shown as being proportional, and FIG. 8B is a cross-sectional view of the lock portion 16 shown in FIG. 7 as an embodiment of the present invention. In the comparison shown in FIG. 8A, the finger-hanging portion 20 has a parting line 22 on the surface opposite to the main wall 19. The parting line 22 may have a burr 24, and the surface having the parting line 22 is a surface with which a finger contacts. As shown in FIG. 8B, by forming the groove portion 21, the risk of damaging a finger can be avoided even if a burr occurs in the parting line 23, and a safe and good use state can be obtained. .

また、本発明の樹脂製品の製造方法により得られる樹脂製品の他の実施形態として、図９、図１０に示す移動式収納体２５に備えられた棒状ハンドル部２６を説明する。 Further, as another embodiment of the resin product obtained by the method for producing a resin product of the present invention, a rod-like handle portion 26 provided in the movable storage body 25 shown in FIGS. 9 and 10 will be described.

図９は本発明の樹脂製品の製造方法により得られる棒状ハンドル部２６（図示例では丸棒状）を有する移動式棚２５の斜視図である。前記移動式棚２５に備えられた棒状ハンドル部２６は図１０に詳細に示される。図１０は図９の棒状ハンドル部に形成された溝部２７の説明図である。図１０（ａ）は、対比例として示された棒状ハンドル部の断面図であり、図１０（ｂ）は、本発明の実施形態として図９に示された棒状ハンドル部２６の断面図である。図１０において、対比例として示された棒状ハンドル部は外周面上にパーティングライン２８を有する。前記パーティングライン２８にはバリ２９が生じる場合があり、前記パーティングライン２８を有する外周面は握り部に相当する。図１０（ｂ）に示されるように、溝部２７を設けることでパーティングライン３０にバリが生じたとしても手の平を傷つける危険を避けることができ、安全で良好な使用状態を得ることができる。 FIG. 9 is a perspective view of a movable shelf 25 having a rod-like handle portion 26 (in the illustrated example, a round bar shape) obtained by the resin product manufacturing method of the present invention. The rod-like handle portion 26 provided on the movable shelf 25 is shown in detail in FIG. FIG. 10 is an explanatory view of the groove portion 27 formed in the rod-like handle portion of FIG. FIG. 10A is a cross-sectional view of a bar-like handle portion shown as a proportional, and FIG. 10B is a cross-sectional view of the bar-like handle portion 26 shown in FIG. 9 as an embodiment of the present invention. . In FIG. 10, the bar-shaped handle portion shown as being proportional has a parting line 28 on the outer peripheral surface. A burr 29 may be formed on the parting line 28, and the outer peripheral surface having the parting line 28 corresponds to a grip portion. As shown in FIG. 10 (b), by providing the groove 27, the risk of hurting the palm can be avoided even if burrs occur in the parting line 30, and a safe and good use state can be obtained.

１、１０１キャスター用車輪
２ハブ部
３リム部
４支持部
５、１０２外周面
６、２１、２７溝部
７、２２、２３、２８、３０、１０３パーティングライン
８、８’ 型合わせ面
９、９’ アンダーカット部
１０成形金型
１１、１１’、１００、１００’ 割金型
１２リム部成形用キャビティー
１３支持部成形用キャビティー
１４ハブ部成形用キャビティー
１５フタ式ボックス
１６ロック部
１６ａ、１９主壁
１６ｂ係合突部
１６ｃ、２０指掛け部
１７ボックス
１８フタ
２５移動式収納棚
２６棒状ハンドル部
２４、２９、１０４バリ
１０５段差 DESCRIPTION OF SYMBOLS 1,101 Wheel for casters 2 Hub part 3 Rim part 4 Support part 5,102 Outer peripheral surface 6,21,27 Groove part 7,22,23,28,30,103 Parting line 8,8 'Mold matching surface 9,9 'Undercut section
10 Mold 11, 11 ′, 100, 100 ′ Split mold
12 Cavity for molding the rim part 13 Cavity for molding the support part 14 Cavity for molding the hub part 15 Lid box 16 Lock part 16a, 19 Main wall 16b Engaging protrusion 16c, 20 Finger hook part 17 Box 18 Lid 25 Moving type Storage shelf 26 Bar-shaped handle parts 24, 29, 104 Burr 105 Step difference

Claims

By using a molding die consisting of a pair of split molds with an undercut in the vicinity of the mold mating surface, a resin is injected into the mold that has been clamped, and after curing, the mold is removed. open, and have a parting line at the bottom of the groove, further, the plate-like portion in which the groove on one side is formed, and the groove of the plate-like portion and a protrusion protruding on the opposite side While obtaining resin products ,
The method for producing a resin product, wherein the molding die has a height dimension of the undercut smaller than an outer dimension of the resin product caused by a shrinkage phenomenon of the resin.

The method for producing a resin product according to claim 1, wherein the resin product is a wheel for casters and has the groove portion on the entire outer peripheral surface.