JP5539684B2 - Agricultural multi-sheet manufacturing method - Google Patents
Agricultural multi-sheet manufacturing method Download PDFInfo
- Publication number
- JP5539684B2 JP5539684B2 JP2009197672A JP2009197672A JP5539684B2 JP 5539684 B2 JP5539684 B2 JP 5539684B2 JP 2009197672 A JP2009197672 A JP 2009197672A JP 2009197672 A JP2009197672 A JP 2009197672A JP 5539684 B2 JP5539684 B2 JP 5539684B2
- Authority
- JP
- Japan
- Prior art keywords
- roll
- cotton
- sheet
- agricultural multi
- falling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、雑草の生育防止や栽培地の保温のために、地上に直接敷設して使用する農業用マルチシートの製造方法に関し、特に敷設したまま自然環境の中で生分解し、除去する必要のない農業用マルチシートの製造方法に関するものである。 The present invention relates to a method for producing a multi-sheet for agricultural use that is directly laid on the ground to prevent the growth of weeds and keep the cultivation area warm, and in particular, it is necessary to biodegrade and remove it in the natural environment while it is laid. It is related with the manufacturing method of the agricultural multi-sheet which does not have.
従来より、農業用マルチシートとしては、各種の不織布が用いられている。たとえば、フラッシュ紡糸法で得られた網状ポリエチレン極細繊維が集積されてなる不織布（商標タイベック）などが用いられている。この不織布は緻密で、遮光性及び防水性に優れており、このため、果樹や野菜などの根元の地上に敷設されると、太陽光を遮るため雑草の生育防止が図れ、また大量の降雨の場合にも肥料の流出や果樹などの根腐れを防止しうるというものである。また、不織布の他に、ポリエチレンやポリ塩化ビニリデン等の合成樹脂よりなる黒色フィルムも、遮光性及び防水性に優れており、農業用マルチシートとして用いられている。 Conventionally, various nonwoven fabrics are used as agricultural multi-sheets. For example, a nonwoven fabric (trademark Tyvek) in which reticulated polyethylene ultrafine fibers obtained by flash spinning are integrated is used. This non-woven fabric is dense and has excellent light-shielding and waterproofing properties. Therefore, when it is laid on the ground, such as fruit trees and vegetables, it can prevent the growth of weeds because it blocks sunlight, and a large amount of rain. In some cases, it can prevent fertilizer runoff and root rot of fruit trees. In addition to non-woven fabrics, black films made of synthetic resins such as polyethylene and polyvinylidene chloride are also excellent in light shielding properties and waterproof properties, and are used as agricultural multi-sheets.
しかしながら、ポリエチレン極細繊維などの一般の合成繊維よりなる不織布や、合成樹脂製フィルムは、使用後の廃棄処理に問題があった。すなわち、このような不織布又はフィルムは焼却によって廃棄処理するため、地球環境に悪影響を与えるということがあった。特に、農業用マルチシートは、その使用量が多いため、地球環境に過大の負荷を与えるものであった。 However, non-woven fabrics made of general synthetic fibers such as polyethylene ultrafine fibers and synthetic resin films have a problem in disposal after use. That is, since such a non-woven fabric or film is disposed of by incineration, it has an adverse effect on the global environment. In particular, agricultural multi-seats have an excessive load on the global environment because of their large usage.
このため、近年、一般の合成繊維に代えて、生分解性繊維よりなる不織布を、農業用マルチシートに使用することが行われている。たとえば、特許文献１では、生分解性繊維としてセルロース繊維が用いられている。生分解性繊維であるセルロース繊維よりなる不織布を農業用マルチシートとして用いることにより、使用中乃至使用後において、自然に分解・消失し、地球環境に与える負荷を軽減することができるのである。 For this reason, in recent years, a nonwoven fabric made of biodegradable fibers has been used for agricultural multi-sheets in place of general synthetic fibers. For example, in Patent Document 1, cellulose fiber is used as the biodegradable fiber. By using a non-woven fabric made of cellulose fiber, which is a biodegradable fiber, as an agricultural multi-sheet, it can be naturally decomposed / disappeared during or after use, and the load on the global environment can be reduced.
セルロース繊維よりなる不織布に防水性を付与するため、特許文献１記載の技術では、脱脂セルロース繊維と未脱脂セルロース繊維を組み合わせる手段を採用している。しかしながら、脱脂セルロース繊維は、脱脂工程を経て得られるものであるため、高価であるという欠点があった。また、不織布に遮光性及び防水性を付与するためには、セルロース繊維を緻密に集積しなければならず、緻密にすればするほど、セルロース繊維が生分解しにくいという欠点もあった。 In order to impart waterproofness to a nonwoven fabric made of cellulose fibers, the technique described in Patent Document 1 employs means for combining defatted cellulose fibers and non-degreasing cellulose fibers. However, defatted cellulose fibers have been disadvantageous in that they are expensive because they are obtained through a degreasing process. In addition, in order to impart light-shielding properties and waterproofness to the nonwoven fabric, the cellulose fibers must be densely accumulated, and the more dense the cellulose fibers, the more difficult the cellulose fibers are to biodegrade.
本件出願人は、かかる欠点を解決する手段として、特許文献２に記載されている農業用マルチシートを提案した。すなわち、特許文献２記載の農業用マルチシートは、落綿が無作為に集積されてなると共に、該落綿相互の間隙に、綿実、綿の木の茎、綿の木の葉及び綿の木の萼よりなる群から選ばれた夾雑物が含まれている落綿シートに、水を噴霧した後、該落綿シートを一対の太鼓形カレンダーロールに通し、該落綿シートの厚み方向に加熱及び加圧して、落綿相互間を密着させると共に、該夾雑物を圧潰することにより、該夾雑物を扁平化するという方法によって得られたものである。したがって、特許文献２記載の農業用マルチシートは、落綿シート中の綿実等の夾雑物が圧潰され、扁平化しており、当該夾雑物の占有面積が非常に大きくなっている。すなわち、農業用マルチシートが面方向において、扁平化された夾雑物の部位と、落綿が集積した部位とが存在する不均質なものとなっている。よって、農業用マルチシートの若干の生分解によって、扁平化された夾雑物は脱落しやすくなり、生分解の進行が速くなるのである。また、農業用シートの素材として落綿を採用しているので、価格的にも安価なのである。 The applicant of the present application has proposed an agricultural multi-sheet described in Patent Document 2 as a means for solving this drawback. That is, the agricultural multi-sheet described in Patent Document 2 is formed by randomly collecting falling cotton, and in the gap between the falling cotton, cotton seeds, cotton tree stems, cotton tree leaves, and cotton tree After spraying water on the cotton-seed sheet containing impurities selected from the group consisting of cocoons, the cotton-soiled sheet is passed through a pair of drum-shaped calendar rolls and heated in the thickness direction of the cotton-soiled sheet. It is obtained by a method of flattening the foreign matter by applying pressure to bring the falling cotton into close contact with each other and crushing the foreign matter. Therefore, in the agricultural multi-sheet described in Patent Document 2, foreign matters such as cotton seeds in the falling cotton sheet are crushed and flattened, and the occupied area of the foreign matters is very large. In other words, the agricultural multi-sheet is inhomogeneous where there are flattened portions of impurities and portions where falling cotton is accumulated in the surface direction. Therefore, the flattened impurities are easily removed by the slight biodegradation of the agricultural multi-sheet, and the progress of biodegradation is accelerated. In addition, it is cheap in terms of price because it uses falling cotton as a material for agricultural sheets.
本発明は、特許文献２に記載された発明の改良に関するものである。すなわち、特許文献２記載の方法で得られた農業用マルチシートを、より柔らかいものとし、地上に直接敷設しやすいようにしようというものである。 The present invention relates to an improvement of the invention described in Patent Document 2. That is, the agricultural multi-sheet obtained by the method described in Patent Document 2 is made softer and easily laid directly on the ground.
すなわち、本発明は、落綿が無作為に集積されてなると共に、該落綿相互の間隙に、綿実、綿の木の茎、綿の木の葉及び綿の木の萼よりなる群から選ばれた夾雑物が含まれている落綿シートに、水を噴霧した後、該落綿シートを一対の太鼓形カレンダーロールに通し、該落綿シートの厚み方向に加熱及び加圧して、落綿相互間を密着させると共に、該夾雑物を圧潰することにより、該夾雑物を扁平化した後に、一対のエンボスロールに通して、表面に凹凸模様を付与することを特徴とする農業用マルチシートの製造方法に関するものである。 That is, the present invention is selected from the group consisting of cotton seeds, cotton tree stalks, cotton tree leaves, and cotton tree cocoons in the gaps between the cotton cottons. After spraying water on a cotton-strip sheet containing impurities, the cotton-strip sheet is passed through a pair of drum-shaped calender rolls, heated and pressurized in the thickness direction of the cotton-strip sheet, Agricultural multi-sheet manufacturing, characterized in that the impurities are flattened by bringing them into close contact with each other and then passing through a pair of embossing rolls to give an uneven pattern to the surface. It is about the method.
本発明において、「落綿」とは、産地から供給される原綿から綿繊維を採取したり、綿糸を紡績したりする工程で発生する屑綿のことである。従来より、この落綿は廃棄物として焼却処分されていたものである。なお、原綿の中には、綿実、綿の木の茎、綿の木の葉及び綿の木の萼等の多数の夾雑物が含まれている。 In the present invention, “falling cotton” refers to scrap cotton generated in a process of collecting cotton fibers from raw cotton supplied from the production area or spinning cotton yarn. Traditionally, this cotton waste has been incinerated as waste. The raw cotton contains a large number of foreign matters such as cotton seeds, cotton tree stems, cotton tree leaves, and cotton tree cocoons.
本発明では、屑綿である落綿と原綿中の夾雑物が混合されている落綿混合物を、カード機等の開繊機で処理して、無作為に集積し、落綿シートを製造する。落綿混合物を開繊機で処理すると、落綿が無作為に集積されてなると共に、落綿相互の間隙に夾雑物が含まれている落綿シートが得られる。したがって、本発明によれば、屑綿及び夾雑物を廃棄物として焼却処分する必要なく、利用しうるのである。さらに、本発明においては、これらの夾雑物以外に、従来より産業廃棄物として処理されている汚泥、食品の残渣及び／又はオガクズ等を混合することも好ましいことである。さらに、二枚の落綿シートに汚泥等を挟着させることも好ましいことである。汚泥や食品の残渣等のこれら産業廃棄物は、後の加熱及び加圧工程を経ることにより、落綿相互間を結合するためのバインダーとしても機能するからである。なお、食品の残渣としては、豆腐の残渣、カツオブシの削り粕及び／又は米ぬかの残渣等を用いるのが好ましい。 In the present invention, the falling cotton mixture in which the falling cotton, which is waste cotton, and the impurities in the raw cotton are mixed, is processed by a fiber opening machine such as a card machine, and is randomly accumulated to produce a falling cotton sheet. When the cotton mixture is processed by a fiber spreader, cotton cotton is randomly accumulated and a cotton cotton sheet in which impurities are contained in the gap between the cotton cotton is obtained. Therefore, according to the present invention, waste cotton and impurities can be used without being incinerated as waste. Furthermore, in the present invention, it is also preferable to mix sludge, food residue and / or sawdust, which has been conventionally treated as industrial waste, in addition to these contaminants. Furthermore, it is also preferable that sludge or the like is sandwiched between the two cotton falling sheets. This is because these industrial wastes such as sludge and food residues also function as binders for bonding between the falling cottons through the subsequent heating and pressurizing steps. In addition, it is preferable to use the residue of a tofu, the cutlet of a cutlet, and / or the residue of rice bran etc. as a food residue.
落綿シート（落綿シートが汚泥等を含む場合を含む。）の目付は、５０〜３００ｇ／ｍ2程度が好ましい。落綿シートの目付が５０ｇ／ｍ2未満であると、単位面積当たりの落綿量が相対的に少なくなり、得られる農業用マルチシートが緻密なものとならず、十分な遮光性や防水性を与えにくくなる傾向が生じる。また、落綿シートの目付が３００ｇ／ｍ2を超えると、得られる農業用マルチシートが重くなって、取り扱いにくくなる。また、厚みが厚くなる傾向となり、従来のマルチシート敷設機（黒色合成樹脂フィルム用のマルチシート敷設機）を用いて敷設しにくくなる。なお、農業用マルチシートの厚みは、０．１〜０．２ｍｍ程度であれば、従来のマルチシート敷設機を用いて敷設することが可能である。 The basis weight of the cotton soot sheet (including the case where the cotton soot sheet contains sludge) is preferably about 50 to 300 g / m 2 . If the weight per unit area of the soot sheet is less than 50 g / m 2 , the amount of soot per unit area will be relatively small, and the resulting multi-agricultural sheet will not be dense, providing sufficient light shielding and waterproofing. Tend to be difficult to give. On the other hand, if the weight per unit area of the cotton soot sheet exceeds 300 g / m 2 , the resulting agricultural multi-sheet becomes heavy and difficult to handle. Moreover, it becomes the tendency for thickness to become thick, and it becomes difficult to lay using the conventional multi-sheet laying machine (multi-sheet laying machine for black synthetic resin films). In addition, if the thickness of the agricultural multi-sheet is about 0.1 to 0.2 mm, it can be laid using a conventional multi-sheet laying machine.
落綿シートを形成した後、この落綿シート表面に、水を噴霧する。具体的には、スプレー装置を用いて、落綿シートに向けて水を噴霧すればよい。水を噴霧しておくことにより、後の一対の太鼓形カレンダーロールによる加熱及び加圧処理によって、落綿相互間が水素結合によって強固に密着するのである。そして、得られた農業用マルチシートに高強度を発現しうるのである。落綿シートに水を噴霧する前、又は水を噴霧中、又は水を噴霧した後、落綿シートにニードリング処理をして、落綿相互間を交絡させておくのが好ましい。落綿相互間を交絡しておくと、落綿シートにある程度の形態安定性を与えることができ、落綿シートの搬送中に、その形態が崩れにくくなる。 After forming the cotton-washing sheet, water is sprayed on the surface of the cotton-washing sheet. Specifically, the spray device may be used to spray water toward the falling cotton sheet. By spraying water, the falling cottons are firmly adhered to each other by hydrogen bonding by the subsequent heating and pressurizing treatment with a pair of drum calender rolls. And the high intensity | strength can be expressed in the obtained agricultural multi-sheet. It is preferable to perform a needling process on the falling cotton sheet before the water is sprayed on the falling cotton sheet, or during the spraying of water or after the water is sprayed, so that the falling cotton sheets are entangled with each other. When the cotton-striping is entangled with each other, a certain degree of form stability can be imparted to the cotton-striping sheet, and the form is less likely to collapse during conveyance of the cotton-striping sheet.
水を噴霧した後、落綿シートを一対の太鼓形カレンダーロールに通し、落綿シートの厚み方向に加熱及び加圧を施す。この加熱及び加圧によって、落綿シート中の落綿相互間を密着させて、得られる農業用マルチシートに十分な強度を付与することができる。また、一対の太鼓形カレンダーロールを用いた加熱及び加圧処理で、夾雑物を圧潰することにより、夾雑物を扁平化すると同時に、綿実の中に含まれている綿実油や、綿の木の茎や葉や萼に含まれている油分を絞り出すことができる。この綿実油や油分等が、土壌に付与されると、その肥沃度が向上する。 After spraying water, the cotton-fed sheet is passed through a pair of drum calender rolls, and heated and pressurized in the thickness direction of the cotton-fed sheet. By this heating and pressurization, the soots in the soots are brought into close contact with each other, and sufficient strength can be imparted to the resulting agricultural multi-sheet. In addition, by crushing the impurities by heating and pressure treatment using a pair of drum-shaped calendar rolls, the impurities are flattened, and at the same time, the cotton seed oil contained in the cotton seeds and the cotton tree Oils contained in stems, leaves and cocoons can be squeezed out. When this cottonseed oil or oil is applied to soil, its fertility is improved.
一対の太鼓形カレンダーロールに通すときの条件としては、加熱温度が１５０〜２５０℃程度で、加圧圧力が線圧で１５０〜５００ｋｇ／ｃｍ程度であるのが好ましい。加熱温度が１５０℃未満になると、落綿相互間に水素結合が生じにくくなり、得られる農業用マルチシートに高強度を付与しにくくなる傾向が生じる。加熱温度は２５０℃を超えても差し支えないが、高温度の加熱はエネルギー的に合理的ではない。加圧圧力が１５０ｋｇ／ｃｍ未満であると、夾雑物を圧潰して扁平化しにくくなる傾向が生じる。夾雑物を圧潰して扁平化しにくくなると、農業用マルチシートの生分解性が低下する傾向が見られる。加圧圧力は５００ｋｇ／ｃｍを超えても差し支えないが、これ以上の高圧力を負荷することはカレンダーロールの寿命と必要なエネルギーといった観点から、合理的ではない。ここで、本発明において、太鼓形カレンダーロールとは、ロール軸方向の中央部の径が最大となっており、両端に向かうにしたがって徐々にその径が小さくなる形状をしたロールのことである。太鼓形ロールを用いることにより、ロールの中央部も両端部にも、同様に１５０〜５００ｋｇ／ｃｍ程度の高圧力を負荷することが可能となり、幅方向に亙って均一に加熱及び加圧することが可能となる。 As conditions for passing through a pair of drum calender rolls, it is preferable that the heating temperature is about 150 to 250 ° C., and the pressurizing pressure is about 150 to 500 kg / cm 2 in terms of linear pressure. When the heating temperature is less than 150 ° C., hydrogen bonding is unlikely to occur between the cotton soots, and it tends to be difficult to impart high strength to the resulting agricultural multi-sheet. The heating temperature can exceed 250 ° C., but high temperature heating is not energetically reasonable. When the pressurizing pressure is less than 150 kg / cm, there is a tendency that the impurities are crushed and become difficult to flatten. When the foreign matter is crushed and becomes difficult to flatten, the biodegradability of the agricultural multi-sheet tends to decrease. The pressurizing pressure may exceed 500 kg / cm, but applying a higher pressure than this is not reasonable from the viewpoint of the life of the calender roll and the required energy. Here, in the present invention, the drum-shaped calendar roll is a roll having a shape in which the diameter of the central portion in the roll axis direction is maximum and gradually decreases toward both ends. By using a drum-shaped roll, it is possible to apply a high pressure of about 150 to 500 kg / cm to the center and both ends of the roll, and to heat and press uniformly over the width direction. Is possible.
加熱及び加圧工程を経れば、農業用マルチシートとして用い得るシートを得られるが、かかるシートは一般的に柔軟性（ドレープ性）に劣っている。したがって、本発明においては、加熱及び加圧工程の後、当該シートを一対のエンボスロールに通す。そうすると、当該シートの表面にシボ調等の凹凸模様が付与され、柔軟性のある農業用マルチシートになるのである。 A sheet that can be used as an agricultural multi-sheet can be obtained through the heating and pressurizing steps, but such a sheet is generally inferior in flexibility (draping property). Accordingly, in the present invention, after the heating and pressurizing steps, the sheet is passed through a pair of embossing rolls. If it does so, uneven | corrugated patterns, such as a grain-like tone, will be given to the surface of the said sheet | seat, and it will become a flexible multi-sheet for agriculture.
ここで、一対のエンボスロールは、凹凸ロールと平滑ロールの組み合わせ又は凹凸ロールと凹凸ロールの組み合わせのいずれであってもよい。たとえば、上段ロールに凹凸ロールを用い、下段ロールに平滑ロールを用いた場合、一方表面のみに凹凸模様が付与される。また、上段ロール及び下段ロール共に凹凸ロールを用いた場合には、両表面に凹凸模様が付与される。両表面に凹凸模様が付与された方が、柔軟性に富むため好ましい。特に、上段ロール及び下段ロールの両方に凹凸ロールを用い、かつ、両凹凸ロール同士が噛み合うようにすると、両表面に付与された凹凸模様がより大きくなり、より柔軟性に優れた農業用マルチシートになるため、より好ましい。なお、両凹凸ロール同士が噛み合うとは、上段ロールの凸部と下段ロールの凹部、及び上段ロールの凹部と下段ロールの凸部とが合致することをいう。 Here, the pair of embossing rolls may be a combination of an uneven roll and a smooth roll or a combination of an uneven roll and an uneven roll. For example, when an uneven roll is used for the upper roll and a smooth roll is used for the lower roll, the uneven pattern is provided only on one surface. Moreover, when an uneven | corrugated roll is used for both an upper stage roll and a lower stage roll, an uneven | corrugated pattern is provided to both surfaces. Since it is rich in a softness | flexibility, it is preferable that the uneven | corrugated pattern is provided to both surfaces. In particular, if an uneven roll is used for both the upper roll and the lower roll, and the concave and convex rolls mesh with each other, the concave and convex pattern imparted to both surfaces becomes larger and the agricultural multi-sheet is more flexible. Therefore, it is more preferable. In addition, that both uneven | corrugated rolls mesh | engage means that the convex part of an upper stage roll and the recessed part of a lower stage roll, and the recessed part of an upper stage roll, and the convex part of a lower stage roll correspond.
また、本発明で用いる一対のエンボスロールは、シートを柔軟にするためのものであるから、上段ロール及び下段ロールの両方が金属製であるよりも、いずれか一方が紙製又はゴム製であるのが好ましい。たとえば、凹凸ロールよりなる上段ロールが金属製ロールで、平滑ロール又は凹凸ロールよりなる下段ロールが紙製又はゴム製ロールであるのが好ましい。かかる組み合わせにより、下段ロールが上段ロールの凹凸に追随して変形しやすく、より深い凹凸模様を付与でき、より柔軟な農業用マルチシートが得られるからである。 Moreover, since a pair of embossing roll used by this invention is for making a sheet | seat flexible, either one is made of paper or rubber | gum rather than both an upper stage roll and a lower stage roll are metal. Is preferred. For example, it is preferable that the upper roll made of an uneven roll is a metal roll and the lower roll made of a smooth roll or an uneven roll is a paper or rubber roll. This is because such a combination allows the lower roll to easily follow the irregularities of the upper roll to be deformed, provide a deeper irregular pattern, and provide a more flexible agricultural multi-sheet.
上段ロール又は下段ロールに使用する凹凸ロールとしては、従来公知のものが用いられ、たとえば、ダイヤ柄、水玉柄又は楊柳柄等の凹凸ロールが用いられる。この中でも、中楊柳ロールを採用するのが特に好ましい。中楊柳ロールとは、楊柳のサイズが中くらいのロールのことであり、幅１〜３ｍｍ程度の凸部と凹部とが、ロール周方向にしぼ調に設けられているロールのことである。なお、小楊柳ロールとは、中楊柳ロールによりも楊柳のサイズが小さいロールのことである。一対のエンボスロールにシートを通すときの条件は任意であるが、一般的に、温度は常温で、加圧圧力が線圧で２０〜２００ｋｇ／ｃｍ程度であるのが好ましい。一対のエンボスロールは凹凸模様を付与するためのものであるから、特に加熱する必要もなく、また線圧も凹凸模様を付与しうる程度でよい。 A conventionally well-known thing is used as an uneven | corrugated roll used for an upper stage roll or a lower stage roll, For example, uneven | corrugated rolls, such as a diamond pattern, a polka dot pattern, or a candy willow pattern, are used. Among these, it is particularly preferable to employ a middle cocoon willow roll. The medium cocoon willow roll is a roll having a medium size of the cocoon willow, and is a roll in which convex portions and concave portions having a width of about 1 to 3 mm are provided in the roll circumferential direction. In addition, a small persimmon willow roll is a roll with the size of a persimmon willow smaller than a middle persimmon willow roll. The conditions for passing the sheet through the pair of embossing rolls are arbitrary, but in general, the temperature is normal temperature, and the pressurizing pressure is preferably about 20 to 200 kg / cm in terms of linear pressure. Since the pair of embossing rolls is for imparting a concavo-convex pattern, it is not particularly necessary to heat, and the linear pressure may be such that the concavo-convex pattern can be imparted.
一対のエンボスロールを通すと、本発明に係る農業用マルチシートを得られる。本発明に係る農業用マルチシートは、従来のマルチシートと同様に、栽培地の土上に敷設しておけば、雑草の生育防止や土壌の保温を図れるものである。なお、本発明に係る農業用マルチシートの目付は、落綿シートの目付と同様に、５０〜３００ｇ／ｍ2程度である。また、その厚みは、０．１〜０．２ｍｍ程度である。更に、本発明に係る農業用マルチシートの強度は、縦横共に、６〜４０Ｎ／２ｃｍ巾程度である。 If a pair of embossing rolls are passed, the agricultural multi-sheet according to the present invention can be obtained. The agricultural multi-sheet according to the present invention can prevent the growth of weeds and keep the soil warm if it is laid on the soil of the cultivation area, like the conventional multi-sheet. In addition, the fabric weight of the agricultural multi-sheet which concerns on this invention is about 50-300 g / m < 2 > similarly to the weight of the cotton-falling sheet. Moreover, the thickness is about 0.1-0.2 mm. Furthermore, the strength of the agricultural multi-sheet according to the present invention is about 6 to 40 N / 2 cm width in both length and width.
以上説明したように、本発明に係る方法で得られた農業用マルチシートは、落綿シート中の綿実等の夾雑物が圧潰され、扁平化しており、当該夾雑物の占有面積が非常に大きくなっている。すなわち、農業用マルチシートが面方向において、扁平化された夾雑物の部位と、落綿が集積した部位とが存在する不均質なものとなっている。したがって、農業用マルチシートの若干の生分解によって、扁平化された夾雑物は脱落しやすくなり、生分解の進行が速くなるという効果を奏する。特に、表面に凹凸模様が付されているため、表面積が拡大されており、かつ、粗な凸部が存在するので、より生分解の進行が早くなる。 As described above, the agricultural multi-sheet obtained by the method according to the present invention is crushed and flattened with foreign matters such as cotton seeds in the falling cotton sheet, and the occupied area of the foreign matters is very large. It is getting bigger. In other words, the agricultural multi-sheet is inhomogeneous where there are flattened portions of impurities and portions where falling cotton is accumulated in the surface direction. Therefore, the flattened impurities are easily removed by the slight biodegradation of the agricultural multi-sheet, and the biodegradation progresses quickly. In particular, since the surface has a concavo-convex pattern, the surface area is enlarged and there are rough convex portions, so that the biodegradation progresses more quickly.
また、扁平化された夾雑物は、綿実等が圧潰されたものであるため、油分が外部へ絞り出されており、農業用マルチシートには油分が付着している。したがって、この農業用マルチシートを土壌に敷設すると、土壌に油分が付与されることにより、土壌の肥沃度が向上するという予期しえない格別顕著な効果も奏する。また、この夾雑物は、綿実や綿の木の葉或いは茎又は萼であるため、これは堆肥となり、果樹や野菜などの肥料になるという効果も奏する。 Moreover, since the flattened foreign material is a crushed cotton seed or the like, the oil is squeezed out to the outside, and the oil is attached to the agricultural multi-sheet. Therefore, when this agricultural multi-sheet is laid on the soil, an unexpectedly remarkable effect that the fertility of the soil is improved due to the addition of oil to the soil. In addition, since this foreign matter is cottonseed, cotton tree leaves, stems, or straw, it becomes compost and also has the effect of becoming fertilizers such as fruit trees and vegetables.
さらに、本発明に係る方法で得られた農業用マルチシートは、廃棄物である落綿と、廃棄物である原綿に含まれている綿実等の夾雑物よりなるものである。すなわち、全てが廃棄物で形成されているので、非常に安価なものとなる。また、それと同時に廃棄物を有効利用しているので、環境を害することがなく、地球環境に優しい商品であるという効果も奏する。 Furthermore, the agricultural multi-sheet obtained by the method according to the present invention is made of waste cotton as waste and foreign matters such as cotton seeds contained in raw cotton as waste. That is, since everything is formed of waste, it is very inexpensive. At the same time, because waste is effectively used, the environment is harmless and the product is friendly to the global environment.
本発明に係る方法で得られた農業用マルチシートは、その表面に凹凸模様が付与されている。したがって、上記した効果に加えて、柔軟性に優れており、地上に敷設しやすいという効果をも奏するものである。 The agricultural multi-sheet obtained by the method according to the present invention has a concavo-convex pattern on its surface. Therefore, in addition to the above-described effects, it has excellent flexibility and can be easily laid on the ground.
以下、本発明を実施例に基づいて説明するが、本発明は実施例に限定されるものではない。本発明は、特願２００８−５０２１８に係る発明を利用した改良発明であることを基本として、解釈されるべきである。 EXAMPLES Hereinafter, although this invention is demonstrated based on an Example, this invention is not limited to an Example. The present invention should be construed on the basis that it is an improved invention utilizing the invention according to Japanese Patent Application No. 2008-50218.
実施例１
落綿と綿実等の夾雑物等を含有する落綿混合物を、開繊機を用いてシート状にして、目付１００ｇ／ｍ2の落綿シートを作成した。この落綿シート二枚の間に、米ぬかの残渣を６０ｇ／ｍ2を挟着し、目付２６０ｇ／ｍ2の落綿シートを作成した。そして、水を若干量噴霧した後、一対の金属製太鼓形カレンダーロールに通してシートを得た。カレンダー条件は、ロール温度１８０℃で線圧は４００ｋｇ／ｃｍとした。このシートを、一対のエンボスロールに通して、農業用マルチシートを得た。一対のエンボスロールは、上段ロールが金属製中楊柳ロールであり、下段ロールが紙製中楊柳ロールであって、上段ロールと下段ロールとが噛み合うようになっているものを使用した。そして、エンボス条件は、常温で線圧を６０ｋｇ／ｃｍとした。
Example 1
A falling cotton mixture containing impurities such as falling cotton and cotton seeds was made into a sheet using a spreader to prepare a falling cotton sheet having a basis weight of 100 g / m 2 . 60 g / m 2 of rice bran residue was sandwiched between the two cotton soot sheets to prepare a cotton soot sheet having a basis weight of 260 g / m 2 . And after spraying some water, a sheet | seat was obtained through a pair of metal drum calendar rolls. The calendar conditions were a roll temperature of 180 ° C. and a linear pressure of 400 kg / cm. This sheet was passed through a pair of embossing rolls to obtain an agricultural multi-sheet. As the pair of embossing rolls, an upper roll is a metal middle cocoon willow roll, a lower roll is a paper middle cocoon willow roll, and the upper roll and the lower roll are engaged with each other. And embossing conditions made the linear pressure 60 kg / cm at normal temperature.
実施例２
一対のエンボスロールとして、上段ロールが金属製ダイヤ柄ロールであり、下段ロールが紙製平滑ロールのものを使用した他は、実施例１と同一の方法で農業用マルチシートを得た。
Example 2
As a pair of embossing rolls, an agricultural multi-sheet was obtained by the same method as in Example 1 except that the upper roll was a metal diamond pattern roll and the lower roll was a paper smooth roll.
実施例３
一対のエンボスロールとして、上段ロールが金属製水玉柄ロールであり、下段ロールが紙製平滑ロールのものを使用した他は、実施例１と同一の方法で農業用マルチシートを得た。
Example 3
As a pair of embossing rolls, an agricultural multi-sheet was obtained in the same manner as in Example 1 except that the upper roll was a metal polka dot roll and the lower roll was a paper smooth roll.
実施例４
一対のエンボスロールとして、上段ロールが金属製小楊柳ロールであり、下段ロールが紙製小楊柳ロールであって、上段ロールと下段ロールとが噛み合うようになっているものを使用した他は、実施例１と同一の方法で農業用マルチシートを得た。
Example 4
Other than using a pair of embossing rolls, the upper roll is a metal cottage willow roll, the lower roll is a paper cottage willow roll, and the upper roll and the lower roll are engaged with each other. An agricultural multi-sheet was obtained in the same manner as in Example 1.
実施例１〜４で得られた農業用マルチシートを、ＪＩＳ Ｌ １０９６ ８．１９．７Ｇ法（ドレープ係数）記載の方法に準拠して、ドレープ係数（％）を測定した。なお、対照のため、目付２６０ｇ／ｍ2の落綿シートを一対の金属製太鼓形カレンダーロールに通して得られたシート（対照例）のドレープ係数（％）も測定した。この結果を表１に示した。 The drape coefficient (%) was measured for the agricultural multi-sheets obtained in Examples 1 to 4 in accordance with the method described in JIS L 1096 8.19.7G method (drape coefficient). In addition, the drape coefficient (%) of the sheet | seat (control example) obtained by letting a cotton-falling sheet | seat with a fabric weight of 260 g / m < 2 > pass a pair of metal drum calendar rolls for the control was also measured. The results are shown in Table 1.
［表１］
━━━━━━━━━━━━━━━━
ドレープ係数（％） ━━━━━━━━━━━━━━━━
実施例１ ９４．０
実施例２ ９６．９
実施例３ ９５．２
実施例４ ９７．７
対照例 ９８．４
━━━━━━━━━━━━━━━━
[Table 1]
━━━━━━━━━━━━━━━━
Drape coefficient (%) ━━━━━━━━━━━━━━━
Example 1 94.0
Example 2 96.9
Example 3 95.2
Example 4 97.7
Control example 98.4
━━━━━━━━━━━━━━━━
実施例に係る方法で得られた農業用マルチシートは、対照例に係るシートよりも、ドレープ係数が低くなっており、柔軟性の点で向上していることが分かる。また、実施例１〜４のうちで、実施例１に係る方法で得られた農業用マルチシートが最もドレープ係数が低く、柔軟性に優れていることが分かる。なお、楊柳柄の中でも、実施例４で用いた小楊柳柄は深い凹凸を形成しにくいため、実施例１で用いた中楊柳柄に比べて、柔軟性の点では劣るものであった。 It can be seen that the agricultural multi-sheet obtained by the method according to the example has a lower drape coefficient than the sheet according to the control example, and is improved in terms of flexibility. Moreover, it turns out that the agricultural multi-sheet obtained by the method which concerns on Example 1 among Examples 1-4 is the lowest drape coefficient, and is excellent in the softness | flexibility. Among the cocoon willow patterns, the small pine willow pattern used in Example 4 is less likely to form deep irregularities, and therefore is inferior in terms of flexibility compared to the middle cocoon willow pattern used in Example 1.
Claims (5)