JP5682666B2 - Packaging bag - Google Patents
Packaging bag Download PDFInfo
- Publication number
- JP5682666B2 JP5682666B2 JP2013144279A JP2013144279A JP5682666B2 JP 5682666 B2 JP5682666 B2 JP 5682666B2 JP 2013144279 A JP2013144279 A JP 2013144279A JP 2013144279 A JP2013144279 A JP 2013144279A JP 5682666 B2 JP5682666 B2 JP 5682666B2
- Authority
- JP
- Japan
- Prior art keywords
- antioxidant
- packaging bag
- density polyethylene
- layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
本発明は、包装袋に関するものである。特に、過酸化水素を含む水性液体を包装する包装袋に関するものである。 The present invention relates to a packaging bag. In particular, the present invention relates to a packaging bag for packaging an aqueous liquid containing hydrogen peroxide.
染毛剤（脱色剤を含む）や、パーマ液には、二剤式のものがあり、二剤うちの１剤は過酸化水素を含む水性液体からなっているものがある。染毛剤（脱色剤を含む）では、使用前に酸化染料を含む第１剤と、過酸化水素を含む水性液体からなる第２剤を混合して、使用する。 There are two types of hair dyes (including decoloring agents) and perm liquids, and one of the two is made of an aqueous liquid containing hydrogen peroxide. In hair dyes (including decoloring agents), a first agent containing an oxidation dye and a second agent made of an aqueous liquid containing hydrogen peroxide are mixed before use.
一方、パーマ液の場合は、第１剤で毛髪を処理し柔軟にさせ、毛髪の形を整えた後、過酸化水素を含む水性液体からなる第２剤で処理をして、毛髪のウェーブを固定する。いずれにしても、二剤うちの１剤は過酸化水素を含む水性液体からなっている染毛剤（脱色剤を含む）や、パーマ液がある。 On the other hand, in the case of a permanent liquid, the hair is treated with the first agent to make the hair soft, and after the hair is shaped, it is treated with the second agent consisting of an aqueous liquid containing hydrogen peroxide, and the wave of the hair is then treated. Fix it. In any case, one of the two agents includes a hair dye (including a decoloring agent) made of an aqueous liquid containing hydrogen peroxide, and a permanent liquid.
過酸化水素を含む水性液体は、保存中に過酸化水素が分解して酸素と水が発生して、発生した酸素により、包装が膨れてしまう恐れがある。また、包装中より水蒸気が包装外へ逃げてしまうと、過酸化水素やその他の成分の濃度が上がってしまう恐れがある。また、過酸化水素により包装袋が黄変することがある。 An aqueous liquid containing hydrogen peroxide may be decomposed during storage to generate oxygen and water, and the package may swell due to the generated oxygen. In addition, if water vapor escapes from the package during packaging, the concentration of hydrogen peroxide and other components may increase. In addition, the packaging bag may turn yellow due to hydrogen peroxide.
このような、過酸化水素を含む水性液体を包装する包装袋として、基材層とバリア層とヒートシール層とから構成された積層体からなり、該積層体の水蒸気透過度が２ｇ／ｍ２・２４ｈｒ以下、気体透過度が０．５ｃｃ／ｍ２・２４ｈｒ以上である積層体から形成された包装袋があった（特許文献１）。 Such a packaging bag for packaging an aqueous liquid containing hydrogen peroxide comprises a laminate composed of a base material layer, a barrier layer, and a heat seal layer, and the water vapor permeability of the laminate is 2 g / m 2. There was a packaging bag formed from a laminate having a gas permeability of 0.5 cc / m 2 · 24 hr or more for 24 hours or less (Patent Document 1).
そして、この包装袋の積層体の層構成として、蒸着した、ポリエチレンテレフタレートフィルムあるいはナイロンフィルムを、基材層とバリア層として、低密度ポリエチレンをヒートシール層とした積層体や、ポリエチレンテレフタレートフィルムあるいはポリエチレンテレフタレートフィルムにナイロンフィルムを中間層として、蒸着した直鎖状低密度ポリエチレンをヒートシール層とした積層体が例示されている。 Then, as a layer structure of the laminated body of the packaging bag, a vapor-deposited polyethylene terephthalate film or nylon film is used as a base layer and a barrier layer, and a low-density polyethylene is used as a heat seal layer, or a polyethylene terephthalate film or polyethylene. A laminated body using a nylon film as an intermediate layer on a terephthalate film and a deposited linear low density polyethylene as a heat seal layer is illustrated.
また、酸素透過率が過酸化水素の分解により発生する単位時間当りの酸素発生量より大きく、かつ水蒸気透過率が単位時間当たりの過酸化水素の分解する質量を過酸化水素の含有率で除した値に略等しく設定されたフィルムからなる容器があった（特許文献２）。 Moreover, the oxygen permeability is larger than the amount of oxygen generated per unit time generated by the decomposition of hydrogen peroxide, and the water vapor permeability is divided by the hydrogen peroxide content. There was a container made of a film set to be approximately equal to the value (Patent Document 2).
そして、このフィルムとして、ポリエチレンテレフタレートフィルム、ナイロンフィルム及びポリエチレンフィルムを積層してなる積層フィルムを含むこと、また、ポリエチレンテレフタレートフィルムとナイロンフィルムの間に酸化シリコンの蒸着層を備えることも記載されている。 The film includes a laminated film formed by laminating a polyethylene terephthalate film, a nylon film, and a polyethylene film, and also includes a silicon oxide vapor deposition layer between the polyethylene terephthalate film and the nylon film. .
また、このフィルムの他のものとして、ポリエチレンテレフタレートフィルム、エチレンビニルアルコール共重合樹脂フィルム及びポリエチレンフィルムを積層してなる積層フィルムを含むことも記載されている。
公知文献を以下に示す。
Moreover, it describes that the laminated film formed by laminating | stacking a polyethylene terephthalate film, an ethylene vinyl alcohol copolymer resin film, and a polyethylene film as another thing of this film is described.
Known documents are shown below.
過酸化水素を含む水性液体を収納する包装袋は、ガス透過が大きすぎると包装袋内の過酸化水素の分解が進み、ガス透過が小さいと、過酸化水素が分解して発生した酸素が包装内に溜まり、包装袋を膨張させる。また、水蒸気透過が少ないと、包装袋内の水分が逃げてしまう。また、過酸化水素により包装袋が黄変することがある。 Packaging bags that contain aqueous liquids containing hydrogen peroxide will decompose hydrogen peroxide in the packaging bag if the gas permeation is too high, and if the gas permeation is small, the oxygen generated by the decomposition of hydrogen peroxide will be packaged. It collects inside and inflates the packaging bag. Moreover, when there is little water vapor transmission, the water | moisture content in a packaging bag will escape. In addition, the packaging bag may turn yellow due to hydrogen peroxide.
本発明は、過酸化水素を含む水性液体を収納して保存しても、黄変しない、または、黄変し難い包装袋を提供することを課題とする。 An object of the present invention is to provide a packaging bag that does not yellow or hardly yellow even when an aqueous liquid containing hydrogen peroxide is stored and stored.
本発明は係る課題に鑑みなされたものであり、請求項１の発明は、
過酸化水素を含む水性液体を収納する包装袋であって、
包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、
前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、
前記酸化防止剤が、リン系酸化防止剤とフェノール系酸化防止剤の混合物であり、リン系酸化防止剤の重量比率をフェノール系酸化防止剤より多くした混合酸化防止剤であることを特徴とする包装袋である。
The present invention has been made in view of the problems, and the invention of claim 1
A packaging bag for storing an aqueous liquid containing hydrogen peroxide,
As the innermost layer of the packaging bag, a linear low density polyethylene resin layer is laminated,
An antioxidant is blended in the linear low density polyethylene resin layer,
The antioxidant, and wherein the Ri mixture der phosphorous-based antioxidant and a phenolic antioxidant, a mixed antioxidant weight ratio was more than phenolic antioxidants phosphorus-based antioxidant It is a packaging bag.
本発明の請求項１の包装袋は、包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、前記酸化防止剤が、リン系酸化防止剤とフェノール系酸化防止剤の混合物であり、リン系酸化防止剤の重量比率をフェノール系酸化防止剤より多くした混合酸化防止剤であるので、収納した過酸化水素を含む水性液体の過酸化水素により包装袋の最内層のポリオレフィン樹脂層の黄変が防止でき、包装袋が黄ばむことがない。 In the packaging bag of claim 1 of the present invention, a linear low density polyethylene resin layer is laminated as the innermost layer of the packaging bag, and an antioxidant is blended in the linear low density polyethylene resin layer. the antioxidant, Ri mixture der phosphorous-based antioxidant and a phenolic antioxidant, since a mixed antioxidant weight ratio was more than phenolic antioxidants phosphorus-based antioxidant, housing The aqueous liquid hydrogen peroxide containing hydrogen peroxide can prevent yellowing of the innermost polyolefin resin layer of the packaging bag, and the packaging bag does not turn yellow.
そのため、過酸化水素を含む水性液体を収納して保存しても、黄変しない、または、黄変し難い包装袋を提供することができる。 Therefore, it is possible to provide a packaging bag that does not yellow or hardly yellow even when an aqueous liquid containing hydrogen peroxide is stored and stored.
本発明の請求項２の発明は、The invention of
過酸化水素を含む水性液体を収納する包装袋であって、A packaging bag for storing an aqueous liquid containing hydrogen peroxide,
包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、As the innermost layer of the packaging bag, a linear low density polyethylene resin layer is laminated,
前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、An antioxidant is blended in the linear low density polyethylene resin layer,
前記酸化防止剤が、フェノール系酸化防止剤とリン系酸化防止剤の双方の構造を有する酸化防止剤であることを特徴とする包装袋である。The packaging bag is characterized in that the antioxidant is an antioxidant having a structure of both a phenol-based antioxidant and a phosphorus-based antioxidant.
本発明の請求項２の包装袋は、包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、前記酸化防止剤が、フェノール系酸化防止剤とリン系酸化防止剤の双方の構造を有する酸化防止剤であるので、収納した過酸化水素を含む水性液体の過酸化水素により包装袋の最内層のポリオレフィン樹脂層の黄変が防止でき、包装袋が黄ばむことがない。In the packaging bag of
そのため、過酸化水素を含む水性液体を収納して保存しても、黄変しない、または、黄変し難い包装袋を提供することができる。Therefore, it is possible to provide a packaging bag that does not yellow or hardly yellow even when an aqueous liquid containing hydrogen peroxide is stored and stored.
本発明は、過酸化水素を含む水性液体を収納して保存しても、黄変しない、または、黄変し難い包装袋を提供することができる。 The present invention can provide a packaging bag that does not yellow or hardly yellow even when an aqueous liquid containing hydrogen peroxide is stored and stored.
以下本発明を実施するための形態につき説明する。
図１は、本発明の包装袋の一例に用いられる積層フィルムの層構成を模式的に断面で示した説明図である。
Hereinafter, modes for carrying out the present invention will be described.
FIG. 1 is an explanatory view schematically showing the layer structure of a laminated film used in an example of the packaging bag of the present invention in cross section.
図１のように、本発明の包装袋の一例に用いられる積層フィルム１は、包装袋の外側より、ポリエチレンテレフタレート層２、ナイロン層３、密度が０．９５０ｇ／ｃｍ３以上の高密度ポリエチレン層４、密度が０．９３０ｇ／ｃｍ３以上の直鎖状低密度ポリエチレン層５が順次積層されている。各層の間には、必要に応じて図示していない接着層を設けても良い。
As shown in FIG. 1, a laminated film 1 used in an example of the packaging bag of the present invention includes a
ポリエチレンテレフタレート層２は、２軸延伸したポリエチレンテレフタレートフィルムを用いることができる。厚さは、７μｍから５０μｍのものが好適に使用できる。さらに好ましくは１２μｍから２５μｍが使用できる。
The
ナイロン層３は、２軸延伸したナイロンフィルムを用いることができる。厚さは、１５μｍから２５μｍのものが好適に使用できる。そして、ポリエチレンテレフタレート層２の２軸延伸したポリエチレンテレフタレートフィルムと、ナイロン層３の２軸延伸したナイロンフィルムは、ドライラミネート用の接着剤を接着層として、積層することができる。
The
また、ポリエチレンテレフタレート層２とナイロン層３を共押出フィルムで用いることができる。この場合、接着層として、接着性樹脂を用いる。Ｔ型ダイスを用い溶融状態で接着性樹脂を挟んでポリエチレンテレフタレートとナイロンを積層して押出し、製膜することによって、共押出フィルムを作ることができる。
Further, the
密度が０．９５０ｇ／ｃｍ３以上の高密度ポリエチレン層４は、高密度ポリエチレンフィルムを使用することができる。高密度ポリエチレンフィルムは、インフレーションなどで製膜することができる。
As the high
高密度ポリエチレンの密度は一般的に、０．９４２ｇ／ｃｍ３以上、０．９６０ｇ／ｃｍ３以下であるが、本発明においては、０．９５０ｇ／ｃｍ３以上の密度の高密度ポリエチレンを用いて、水蒸気透過性をより低くしている。 The density of the high density polyethylene is generally, 0.942 g / cm 3 or more, but is 0.960 g / cm 3 or less, in the present invention, by using a high density polyethylene 0.950 g / cm 3 or more density , Water vapor permeability is lower.
高密度ポリエチレンには、酸化防止剤として、フェノール系酸化防止剤と、リン系酸化防止剤を併用する。例えば、フェノール系酸化防止剤として、ペンタエリスリトールテトラキス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］を用い、リン系酸化防止剤として、トリス(２，４−ジ−ｔｅｒｔ−ブチルフェニル)フォスファイトを用いる。重量比でリン系酸化防止剤をフェノール系酸化防止剤より多く用いる。比率として１：１．５から１：３程度が好ましい。これにより、過酸化水素が直鎖状低密度ポリエチレン層５を透過して高密度ポリエチレン層４に達しても、高密度ポリエチレン層４が黄変することがない。
For high density polyethylene, a phenolic antioxidant and a phosphorus antioxidant are used in combination as an antioxidant. For example, pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate] is used as the phenolic antioxidant, and tris (2,4-dithiol) is used as the phosphorus antioxidant. -Tert-Butylphenyl) phosphite is used. More phosphorous antioxidant is used than phenolic antioxidant by weight ratio. The ratio is preferably about 1: 1.5 to 1: 3. Thereby, even if hydrogen peroxide permeates the linear low-density polyethylene layer 5 and reaches the high-
高密度ポリエチレン層４の厚さは、３０μｍから８０μｍであることが好ましい。このようにすることによって水蒸気透過性を低くすることができる。高密度ポリエチレン層４は、ナイロン層３に接着層として、ドライラミネート用接着剤を介して積層する。また、
接着層として、ポリエチレン系の樹脂を用いて、サンドイッチラミネーション法によって積層しても良い。
The thickness of the high
As the adhesive layer, a polyethylene-based resin may be used and laminated by a sandwich lamination method.
密度が０．９３０ｇ／ｃｍ３以上の直鎖状低密度ポリエチレン層５は、直鎖状低密度ポリエチレンフィルムを用いることができる。直鎖状低密度ポリエチレンフィルムは、インフレーションやＴ型ダイスを用いた押出製膜法などで製膜することができる。尚、直鎖状低密度ポリエチレンの密度は、一般的には、０．９４ｇ／ｃｍ３以下である。 A linear low density polyethylene film can be used for the linear low density polyethylene layer 5 having a density of 0.930 g / cm 3 or more. The linear low-density polyethylene film can be formed by inflation or an extrusion film forming method using a T-type die. The density of the linear low density polyethylene is generally 0.94 g / cm 3 or less.
直鎖状低密度ポリエチレン層５に用いる直鎖状低密度ポリエチレンには、酸化防止剤として、フェノール系酸化防止剤と、リン系酸化防止剤を併用する。重量比でリン系酸化防止剤をフェノール系酸化防止剤より多く用いる。比率として１：１．５から１：３程度が好ましい。 In the linear low density polyethylene used for the linear low density polyethylene layer 5, a phenolic antioxidant and a phosphorus antioxidant are used in combination as antioxidants. More phosphorous antioxidant is used than phenolic antioxidant by weight ratio. The ratio is preferably about 1: 1.5 to 1: 3.
または、フェノール系酸化防止剤と、リン系酸化防止剤の構造を併せ持つ、酸化防止剤を用いても良い。このような酸化防止剤を用いることによって、過酸化水素による直鎖状低密度ポリエチレン層５の黄変を防ぐことができる。 Alternatively, an antioxidant having both a phenolic antioxidant and a phosphorus antioxidant structure may be used. By using such an antioxidant, yellowing of the linear low density polyethylene layer 5 due to hydrogen peroxide can be prevented.
直鎖状低密度ポリエチレン層５の厚さは、３０μｍから８０μｍの高密度ポリエチレン層４の厚さより、厚いことが好ましい。このようにすることによって、高密度ポリエチレン層４の硬さを緩和し、包装袋としての柔軟性を得ることができ、また、高いシール性も得られる。
The thickness of the linear low density polyethylene layer 5 is preferably thicker than the thickness of the high
直鎖状低密度ポリエチレン層５は、高密度ポリエチレン層４に接着層としてのドライラミネート用接着剤を介して積層する。また、接着層として、ポリエチレン系の樹脂を用いて、サンドイッチラミネーション法によって積層しても良い。
The linear low density polyethylene layer 5 is laminated on the high
この積層フィルム１を用いて、直鎖状低密度ポリエチレン層５同士を対向させて重ね合わせ、周縁部をシールすることによって、本発明の包装袋の一例を得ることができる。 An example of the packaging bag of the present invention can be obtained by using the laminated film 1 so that the linear low-density polyethylene layers 5 face each other and overlap each other and seal the peripheral edge.
包装袋の形状は、３方シール袋や４方シール袋、あるいは、袋に厚みを持たせてコンパクトにしたガゼット袋やスタンディングパウチなどを採用することができる。また、過酸化水素を含む水性液体が開封したときに、手に付かないように、口栓付きの袋にすることが好ましい。特に、口栓付きガゼット袋や、口栓付きスタンディングパウチがより好ましい。 As the shape of the packaging bag, a three-side sealed bag, a four-side sealed bag, or a gusset bag or a standing pouch that is made compact by adding thickness to the bag can be adopted. Moreover, it is preferable to make it a bag with a stopper so that it will not touch when an aqueous liquid containing hydrogen peroxide is opened. In particular, a gusset bag with a plug and a standing pouch with a plug are more preferable.
以下に、本発明の具体的実施例について説明する。 Specific examples of the present invention will be described below.
＜実施例１＞
１２μｍの２軸延伸ポリエチレンテレフタレートフィルム、１５μｍの２軸延伸ナイロンフィルム、７０μｍの高密度ポリエチレンフィルム、１００μｍの直鎖状低密度ポリエチレンフィルムを用意して、それぞれの間をドライラミネート用接着剤を介して、積層フィルム１を得た。
<Example 1>
Prepare a 12 μm biaxially stretched polyethylene terephthalate film, a 15 μm biaxially stretched nylon film, a 70 μm high density polyethylene film, and a 100 μm linear low density polyethylene film. A laminated film 1 was obtained.
高密度ポリエチレンフィルムの高密度ポリエチレンは、密度が０．９５６ｇ／ｃｍ３で、酸化防止剤として、フェノール系酸化防止剤である、ＢＡＳＦジャパン株式会社のイルガノックス（登録商標）１０１０と、リン系酸化防止剤である、同社のイルガフォス（登録商標）１６８とを１：２の重量割合で混合して、１２００ｐｐｍ添加してある。イルガノックス（登録商標）１０１０は、ペンタエリスリトールテトラキス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］であり、イルガフォス（登録商標）１６８は、トリス（２，４−ジ−ｔｅｒｔ−ブチルフェニル）フォスファイトである。 The high-density polyethylene of the high-density polyethylene film has a density of 0.956 g / cm 3 and, as an antioxidant, is a phenolic antioxidant, Irganox (registered trademark) 1010 of BASF Japan Ltd., and a phosphorus-based oxidation The inhibitor, Irgaphos (registered trademark) 168 of the company, is mixed at a weight ratio of 1: 2, and 1200 ppm is added. Irganox® 1010 is pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate], and Irgaphos® 168 is tris (2,4- Di-tert-butylphenyl) phosphite.
直鎖状低密度ポリエチレンフィルムの直鎖状低密度ポリエチレンは、密度が０．９３５ｇ／ｃｍ３で、酸化防止剤として、フェノール系酸化防止剤とリン系酸化防止剤の双方の構造を有する酸化防止剤である、住友化学株式会社のスミライザー（登録商標）ＧＰを１２００ｐｐｍ添加してある。スミライザー（登録商標）ＧＰは、６−ｔｅｒｔ−ブチル−４−［３−［（２，４，８，１０−テトラ−ｔｅｒｔ−ブチルジベンゾ［ｄ，ｆ］［１，３，２］ジオキサホスフェピン−６−イル）オキシ］プロピル］−２−メチルフェノールである。 The linear low density polyethylene of the linear low density polyethylene film has a density of 0.935 g / cm 3 and has both a phenolic antioxidant and a phosphorus antioxidant as antioxidants. 1200 ppm of Sumitizer (registered trademark) GP of Sumitomo Chemical Co., Ltd., which is an agent, is added. Sumilizer® GP is 6-tert-butyl-4- [3-[(2,4,8,10-tetra-tert-butyldibenzo [d, f] [1,3,2] dioxaphos. Fepin-6-yl) oxy] propyl] -2-methylphenol.
この積層フィルム１を用いて、４方シール袋（寸法１６０ｍｍ×２５０ｍｍ）を作成し、実施例１の包装袋とした。 Using this laminated film 1, a four-side sealed bag (size 160 mm × 250 mm) was prepared and used as a packaging bag of Example 1.
＜実施例２＞
ポリエチレンテレフタレート樹脂とナイロン樹脂、及び、接着性樹脂を用意し、Ｔ型ダイスを用い溶融状態で積層して押出し、１２μｍのポリエチレンテレフタレート層２、３μｍの接着性樹脂層、１５μｍのナイロン層３からなる３層の共押出フィルムを製膜した。尚、接着性樹脂として、三菱化学株式会社のモディック（登録商標）を用いた。
<Example 2>
A polyethylene terephthalate resin, a nylon resin, and an adhesive resin are prepared, laminated in a molten state using a T-shaped die, and extruded, and includes a 12 μm
この共押出フィルムのナイロン層３の面に別途用意した７０μｍの高密度ポリエチレンフィルム、１００μｍの直鎖状低密度ポリエチレンフィルムをそれぞれ、ドライラミネート用接着剤を介して、積層フィルム１を得た。
A laminated film 1 was obtained by using a 70 μm high-density polyethylene film and a 100 μm linear low-density polyethylene film separately prepared on the surface of the
高密度ポリエチレンフィルムの高密度ポリエチレンは、密度が０．９５６ｇ／ｃｍ３で、酸化防止剤として、フェノール系酸化防止剤である、ＢＡＳＦジャパン株式会社のイルガノックス（登録商標）１０１０（ペンタエリスリトールテトラキス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］）と、リン系酸化防止剤である、同社のイルガフォス（登録商標）１６８（トリス(２，４−ジ−ｔｅｒｔ−ブチルフェニル)フォスファイト）とを１：２の重量割合で混合して、１２００ｐｐｍ添加してある。 The high-density polyethylene of the high-density polyethylene film has a density of 0.956 g / cm 3 and, as an antioxidant, is a phenolic antioxidant, Irganox (registered trademark) 1010 (pentaerythritol tetrakis [ 3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate]) and Irgaphos® 168 (tris (2,4-di-tert- Butylphenyl) phosphite) is mixed at a weight ratio of 1: 2, and 1200 ppm is added.
直鎖状低密度ポリエチレンフィルムの直鎖状低密度ポリエチレンは、密度が０．９３５ｇ／ｃｍ３で、酸化防止剤として、フェノール系酸化防止剤である、ＢＡＳＦジャパン株式会社のイルガノックス（登録商標）１０１０（ペンタエリスリトールテトラキス［３−（３，５−ジ−ｔｅｒｔ−ブチル−４−ヒドロキシフェニル）プロピオネート］）と、リン系酸化防止剤である、同社のイルガフォス（登録商標）１６８（トリス(２，４−ジ−ｔｅｒｔ−ブチルフェニル)フォスファイト）とを１：２の重量割合で混合して、１２００ｐｐｍ添加してある。 The linear low density polyethylene of the linear low density polyethylene film has a density of 0.935 g / cm 3 and is a phenolic antioxidant as an antioxidant, Irganox (registered trademark) of BASF Japan Ltd. 1010 (pentaerythritol tetrakis [3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate]) and its Irgaphos (registered trademark) 168 (Tris (2, 4-di-tert-butylphenyl) phosphite) at a weight ratio of 1: 2 and 1200 ppm added.
この積層フィルム１を用いて、４方シール袋（寸法１６０ｍｍ×２５０ｍｍ）を作成し、実施例２の包装袋とした。 Using this laminated film 1, a four-side sealed bag (size 160 mm × 250 mm) was prepared and used as a packaging bag of Example 2.
以下に本発明の実施例１及び２と比較する実施例３及び４について説明する。 Examples 3 and 4 to be compared with Examples 1 and 2 of the present invention will be described below.
＜実施例３＞
１２μｍの２軸延伸ポリエチレンテレフタレートフィルム、１５μｍの２軸延伸ナイロンフィルム、１５０μｍの直鎖状低密度ポリエチレンフィルムを用意して、それぞれの間をドライラミネート用接着剤を介して、積層フィルム１を得た。
<Example 3>
A 12 μm biaxially stretched polyethylene terephthalate film, a 15 μm biaxially stretched nylon film, and a 150 μm linear low density polyethylene film were prepared, and a laminated film 1 was obtained via an adhesive for dry lamination between each of them .
直鎖状低密度ポリエチレンフィルムの直鎖状低密度ポリエチレンは、密度が０．９２５ｇ／ｃｍ３で酸化防止剤として、フェノール系酸化防止剤である、ＢＡＳＦジャパン株式会社のイルガノックス（登録商標）１０７６（オクタデシル−３−（３，５−ジ−t−ブチル−4−ヒドロキシフェニル）プロピオネート）と、リン系酸化防止剤である、同社のイルガフォス（登録商標）１６８（トリス(２，４−ジ−ｔｅｒｔ−ブチルフェニル)フォスファイト）とを２：１の重量割合で混合して、１２００ｐｐｍ添加してある。 The linear low density polyethylene of the linear low density polyethylene film has a density of 0.925 g / cm 3 and is a phenolic antioxidant as an antioxidant, Irganox (registered trademark) 1076 of BASF Japan Ltd. (Octadecyl-3- (3,5-di-t-butyl-4-hydroxyphenyl) propionate) and its Irgaphos (registered trademark) 168 (Tris (2,4-di-) tert-butylphenyl) phosphite) in a 2: 1 weight ratio and added at 1200 ppm.
この積層フィルム１を用いて、４方シール袋（寸法１６０ｍｍ×２５０ｍｍ）を作成し、実施例３の包装袋とした。 Using this laminated film 1, a four-side sealed bag (size: 160 mm × 250 mm) was prepared and used as a packaging bag of Example 3.
＜実施例４＞
アルミナが蒸着された１２μｍの２軸延伸ポリエチレンテレフタレートフィルム、１５μｍの２軸延伸ナイロンフィルム、１５０μｍの直鎖状低密度ポリエチレンフィルムを用意して、それぞれの間をドライラミネート用接着剤を介して、積層フィルム１を得た。尚、直鎖状低密度ポリエチレンフィルムは、実施例３に用いたものと同じものを用いた。
<Example 4>
Prepare 12μm biaxially stretched polyethylene terephthalate film with alumina deposited, 15μm biaxially stretched nylon film, 150μm linear low density polyethylene film, and laminate them with an adhesive for dry lamination. Film 1 was obtained. In addition, the same thing as what was used for Example 3 was used for the linear low density polyethylene film.
この積層フィルム１を用いて、４方シール袋（寸法１６０ｍｍ×２５０ｍｍ）を作成し、実施例４の包装袋とした。 Using this laminated film 1, a four-side sealed bag (size: 160 mm × 250 mm) was prepared and used as a packaging bag of Example 4.
実施例１〜４の包装袋の積層フィルムの水蒸気透過率と酸素透過率を表１に示す。 Table 1 shows the water vapor transmission rate and oxygen transmission rate of the laminated films of the packaging bags of Examples 1 to 4.
実施例１〜４の包装袋に過酸化水素を含む水性液体を１０００ｍｌ充填して、４０℃で３ヶ月保存して、１ヶ月毎に以下の評価を行った。 The packaging bags of Examples 1 to 4 were filled with 1000 ml of an aqueous liquid containing hydrogen peroxide, stored at 40 ° C. for 3 months, and the following evaluation was performed every month.
＜包装袋の膨張＞
包装袋が膨張しているかどうかを目視で検査した。明らかに膨張しているものを×とし、それ以外を○とした。その結果を表２に示す。
<Inflation of packaging bag>
It was visually inspected whether the packaging bag was inflated. Those that were clearly inflated were marked with ×, and others were marked with ○. The results are shown in Table 2.
＜包装袋の黄変＞
包装袋が黄変しているかどうかを目視で検査した。明らかに黄変しているものを×とし、それ以外を○とした。その結果を表３に示す。
<Yellowing of packaging bags>
It was visually inspected whether the packaging bag was yellowed. Those that were clearly yellowed were marked with ×, and others were marked with ○. The results are shown in Table 3.
＜充填した水性液体の過酸化水素濃度＞
過酸化水素濃度を測定した。そして、過酸化水素濃度が５．９０重量％を超えてしまったものの評価を×とした。それ以外を○とした。その結果を表３に示す。
<Concentration of hydrogen peroxide in the filled aqueous liquid>
The hydrogen peroxide concentration was measured. And the evaluation of the hydrogen peroxide concentration exceeding 5.90% by weight was evaluated as x. The others were marked with ○. The results are shown in Table 3.
以下に実施例の比較結果について説明する。 Below, the comparison result of an Example is demonstrated.
＜比較結果＞
実施例１及び実施例２は、包装袋の膨張や、包装袋の黄変もなく、また、充填した水性液体の過酸化水素濃度の変化も抑えられており、良好な結果となった。また、包装袋としてシール性と柔軟性があり、包装袋としての物性も良好であった。
<Comparison result>
In Example 1 and Example 2, there was no expansion of the packaging bag and yellowing of the packaging bag, and the change in the hydrogen peroxide concentration of the filled aqueous liquid was suppressed, and good results were obtained. Further, the packaging bag had sealing properties and flexibility, and the physical properties as a packaging bag were also good.
他方、実施例３は、包装袋の膨張はなかったものの、包装袋の黄変が２ヶ月後に発生しており、また、充填した水性液体の過酸化水素濃度が、２ヶ月後に５．９３重量％になり、３ヶ月後では６．００重量％となって、上昇してしまい、過酸化水素を含む水性液体を収納する包装袋には適さないことがわかった。 On the other hand, in Example 3, although the packaging bag did not expand, yellowing of the packaging bag occurred after 2 months, and the hydrogen peroxide concentration of the filled aqueous liquid was 5.93 weight after 2 months. After 3 months, it increased to 6.00% by weight, indicating that it was not suitable for a packaging bag containing an aqueous liquid containing hydrogen peroxide.
実施例４は、２ヶ月後に包装袋の膨張が起こり、過酸化水素を含む水性液体を収納する包装袋には適さないことがわかった。そのため２ヶ月保存後の包装袋の黄変や、充填した水性液体の過酸化水素濃度の測定は行わなかった。 Example 4 was found to be unsuitable for a packaging bag containing an aqueous liquid containing hydrogen peroxide because the packaging bag expanded after two months. Therefore, yellowing of the packaging bag after storage for 2 months and measurement of the hydrogen peroxide concentration of the filled aqueous liquid were not performed.
１・・・積層フィルム
２・・・ポリエチレンテレフタレート層
３・・・ナイロン層
４・・・高密度ポリエチレン層
５・・・直鎖状低密度ポリエチレン層
DESCRIPTION OF SYMBOLS 1 ...
Claims (2)
包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、
前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、
前記酸化防止剤が、リン系酸化防止剤とフェノール系酸化防止剤の混合物であり、リン系酸化防止剤の重量比率をフェノール系酸化防止剤より多くした混合酸化防止剤であることを特徴とする包装袋。 A packaging bag for storing an aqueous liquid containing hydrogen peroxide,
As the innermost layer of the packaging bag, a linear low density polyethylene resin layer is laminated,
An antioxidant is blended in the linear low density polyethylene resin layer,
The antioxidant, and wherein the Ri mixture der phosphorous-based antioxidant and a phenolic antioxidant, a mixed antioxidant weight ratio was more than phenolic antioxidants phosphorus-based antioxidant Packaging bag to do.
包装袋の最内層として、直鎖状低密度ポリエチレン樹脂層が積層されており、As the innermost layer of the packaging bag, a linear low density polyethylene resin layer is laminated,
前記直鎖状低密度ポリエチレン樹脂層に酸化防止剤が配合されており、An antioxidant is blended in the linear low density polyethylene resin layer,
前記酸化防止剤が、フェノール系酸化防止剤とリン系酸化防止剤の双方の構造を有する酸化防止剤であることを特徴とする包装袋。A packaging bag, wherein the antioxidant is an antioxidant having a structure of both a phenolic antioxidant and a phosphorus antioxidant.