JP5859997B2 - Agricultural multilayer multi-film - Google Patents
Agricultural multilayer multi-film Download PDFInfo
- Publication number
- JP5859997B2 JP5859997B2 JP2013052425A JP2013052425A JP5859997B2 JP 5859997 B2 JP5859997 B2 JP 5859997B2 JP 2013052425 A JP2013052425 A JP 2013052425A JP 2013052425 A JP2013052425 A JP 2013052425A JP 5859997 B2 JP5859997 B2 JP 5859997B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- layer
- present
- fine particles
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、農業用多層マルチフィルムに関し、詳しくは、地温を抑制し病害虫を忌避する農業用多層マルチフィルムに関する。 The present invention relates to an agricultural multilayer multifilm, and more particularly to an agricultural multilayer multifilm that suppresses soil temperature and avoids pests.
一般に、多くの農作物(落花生、トウモロコシ、ニンジン、大根を始め各種野菜、花卉、果樹等)の栽培に、農業用マルチフィルムが用いられている。 In general, agricultural multi-films are used for the cultivation of many crops (such as peanuts, corn, carrots, radishes, various vegetables, flower buds, fruit trees, etc.).
かかるマルチフィルムを用いたマルチ栽培によって、土中水分保持、土壌膨軟性の保持、肥料流亡防止、地温の上昇と抑制、初期成育の促進、初期収量の増加、生産の多収安定化等の諸効果が達成される。 Multi-cultivation using such multi-films, such as retention of soil moisture, retention of soil softness, prevention of fertilizer loss, rise and suppression of soil temperature, promotion of initial growth, increase of initial yield, stabilization of high yield of production, etc. The effect is achieved.
かかるマルチフィルムの一種として、従来、二酸化チタンやアルミ微粒子をフィルムに配合して太陽光線を反射させて、地温の上昇を防ぐ反射フィルムが知られている（特許文献１）。 As one type of such a multi-film, conventionally, a reflective film is known in which titanium dioxide or aluminum fine particles are blended into a film to reflect sunlight and prevent an increase in ground temperature (Patent Document 1).
二酸化チタンを配合したフィルムは、地温の上昇は抑制できるが、害虫が飛来する欠点があり、またアルミ微粒子を配合したフィルムは害虫の飛来を防止できるが、地温の抑制は不十分であった。 A film containing titanium dioxide can suppress an increase in the ground temperature, but has a drawback that insects fly. A film containing aluminum fine particles can prevent the insects from flying, but the earth temperature is not sufficiently suppressed.
特許文献１では、三層構造で、黒層の上に、二酸化チタン層とアルミ微粒子層を順番に重ねたフィルムが提案されたが、構造が複雑になり、実用化困難であった。
In
地温の抑制と害虫の飛来防止のために、二酸化チタンとアルミ微粒子を混合して配合した層を黒層の上に重ねる手法が考えられるが、二酸化チタンとアルミ微粒子が互いに干渉して濁った灰色になり、太陽光線の反射率が低下する問題がある。反射率が低下すると、地温の抑制と害虫の飛来防止に効果が無くなる問題がある。 In order to suppress the earth temperature and prevent the pests from flying, a method of layering a mixture of titanium dioxide and aluminum fine particles on top of the black layer can be considered, but the titanium dioxide and aluminum fine particles interfere with each other and become cloudy gray Therefore, there is a problem that the reflectance of sunlight is reduced. When the reflectance is lowered, there is a problem that the effect of suppressing the earth temperature and preventing the pests from flying is lost.
そこで、本発明は、太陽光線の反射を最適に制御して地温上昇抑制と害虫飛来防止に優れた農業用多層マルチフィルムを提供することを課題とする。 Then, this invention makes it a subject to provide the multilayer multifilm for agriculture excellent in control of a solar temperature rise and the prevention of a pest flying by optimally controlling the reflection of sunlight.
また、本発明の他の課題は以下の記載によって明らかとなる。 Other problems of the present invention will become apparent from the following description.
上記課題は、以下の発明によって解決される。 The above problems are solved by the following invention.
１．
一方の面がカーボンブラックを含有する光吸収層で、他方の面が二酸化チタンと金属微粒子を含有する光反射層である農業用マルチフィルムにおいて、
全層の厚みが１０〜４０μｍの範囲にあり、
さらに前記光反射層の厚みが５〜３０μｍの範囲にあり、
前記二酸化チタンの含有濃度Ｃ１は１０〜２５ｗt％の範囲であり、
該光反射層の反射率が波長３６０ｎｍで１０％以上、波長４５０ｎｍで６０〜８０％であることを特徴とする農業用多層マルチフィルム。
1.
In an agricultural multi-film in which one side is a light absorbing layer containing carbon black and the other side is a light reflecting layer containing titanium dioxide and metal fine particles,
The thickness of all layers is in the range of 10-40 μm,
Furthermore, the thickness of the light reflecting layer is in the range of 5 to 30 μm,
The titanium dioxide content concentration C1 is in the range of 10 to 25 wt%,
A multilayer multilayer film for agricultural use, wherein the reflectance of the light reflecting layer is 10% or more at a wavelength of 360 nm and 60 to 80% at a wavelength of 450 nm.
２．
金属微粒子の含有濃度Ｃ２は０．０５〜０．２ｗt％であることを特徴とする前記１記載の農業用多層マルチフィルム。
2.
2. The agricultural multi-layered multifilm according to 1 above, wherein the content concentration C2 of the metal fine particles is 0.05 to 0.2 wt%.
３．
金属微粒子が、アルミ微粒子である前記１または２記載の農業用多層マルチフィルム。
3.
The agricultural multi-layered multifilm according to 1 or 2, wherein the metal fine particles are aluminum fine particles.
本発明によれば、太陽光線の反射を最適に制御して地温上昇抑制と害虫飛来防止に優れた農業用多層マルチフィルムを提供することができる。 ADVANTAGE OF THE INVENTION According to this invention, the multilayer multilayer film for agriculture excellent in control of a solar temperature rise and prevention of a pest flying can be provided by optimally controlling the reflection of sunlight.
以下、本発明の実施の形態を説明する。 Embodiments of the present invention will be described below.
図１は本発明の農業用多層マルチフィルムの一例を示す断面図である。 FIG. 1 is a cross-sectional view showing an example of an agricultural multilayer multifilm of the present invention.
同図において、１はベース樹脂としてポリオレフィン系樹脂を用いた軟質の多層マルチフィルムであり、１０は光反射層（白銀層ともいう）、１１は光吸収層（黒色層ともいう）である。 In the figure, 1 is a soft multi-layer multi-film using a polyolefin resin as a base resin, 10 is a light reflecting layer (also referred to as a white silver layer), and 11 is a light absorbing layer (also referred to as a black layer).
ポリオレフィン系樹脂としては、低密度ポリエチレン(ＬＤＰＥ)、直鎖状低密度ポリエチレン(ＬＬＤＰＥ)、高密度ポリエチレン(ＨＤＰＥ)、エチレン−酢酸ビニル共重合体(ＥＶＡ)、ポリ塩化ビニル(ＰＶＣ)等が挙げられ、その他軟質材料であればよい。 Examples of polyolefin resins include low density polyethylene (LDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE), ethylene-vinyl acetate copolymer (EVA), and polyvinyl chloride (PVC). Other soft materials may be used.
軟質材料としては、ポリプロピレン、エチレン−プロピレン共重合体、エチレン−ブテン１共重合体、エチレン−４−メチル−１−ペンテン共重合体、エチレン−ヘキセン共重合体、エチレン−オクテン共重合体、エチレン−デセン共重合体等のエチレン−α−オレフィン共重合体、エチレン−アクリル酸共重合体、エチレン−メチルメタクリレート共重合体、エチレン−酢酸ビニル−メチルメタクリレート共重合体、アイオノマー共重合体等が挙げられる。
Examples of the soft material include polypropylene, ethylene-propylene copolymer, ethylene-
ポリオレフィン系樹脂として好ましいのは、低密度ポリエチレン(ＬＤＰＥ)、直鎖状低密度ポリエチレン(ＬＬＤＰＥ）、高密度ポリエチレン(ＨＤＰＥ)、エチレン−酢酸ビニル共重合体（ＥＶＡ）、ポリ塩化ビニル（ＰＶＣ）であり、より好ましいのは、強度、柔軟性、耐候性、あるいはある程度の耐熱性を発揮する観点から、直鎖状低密度ポリエチレン(ＬＬＤＰＥ)である。 Preferred examples of the polyolefin resin include low density polyethylene (LDPE), linear low density polyethylene (LLDPE), high density polyethylene (HDPE), ethylene-vinyl acetate copolymer (EVA), and polyvinyl chloride (PVC). Among them, more preferred is linear low density polyethylene (LLDPE) from the viewpoint of exhibiting strength, flexibility, weather resistance, or a certain degree of heat resistance.
フィルムの全層の厚みは、フィルムの反射性能と強度の観点から、１０〜４０μｍの範囲であり、望ましくは１５〜３０μｍの範囲である。 The thickness of all layers of the film is in the range of 10 to 40 μm, and preferably in the range of 15 to 30 μm, from the viewpoint of the reflection performance and strength of the film.
光反射層１０は、二酸化チタン(Ｔｉ０２)と金属微粒子（たとえば、アルミ微粒子）を含有する層である。
The
光反射層１０の厚みは、５〜３０μｍの範囲であり、好ましくは１０〜２５μｍの範囲である。厚みはフィルム断面の光学顕微鏡観察によって測定することができる。
The thickness of the
二酸化チタンの含有濃度Ｃ１は１０〜２５ｗt％の範囲である。 The content concentration C1 of titanium dioxide is in the range of 10 to 25 wt%.
光反射層（白銀色層）に含有される二酸化チタンは、粉末として含有することが好ましい。粉末の粒径は、太陽光を効率よく乱反射させるため、可視光波長、即ち波長０．４〜０．８μの光を乱反射するべく、平均粒径は０．１〜１．０μｍの範囲が好ましい。ここで平均粒径とは、電子顕微鏡写真に基づく算術的平均値である。 The titanium dioxide contained in the light reflection layer (white silver layer) is preferably contained as a powder. The particle size of the powder is preferably in the range of 0.1 to 1.0 μm in order to diffusely reflect light having a visible light wavelength, that is, a wavelength of 0.4 to 0.8 μm, in order to efficiently diffuse sunlight. . Here, the average particle diameter is an arithmetic average value based on an electron micrograph.
光反射層の反射率は、波長３６０ｎｍで１０％以上、波長４５０ｎｍで６０〜８０％である。かかる反射率であると、太陽光線の反射を最適に制御して地温上昇抑制と害虫飛来防止に優れた多層マルチフィルムを提供可能となる。 The reflectance of the light reflecting layer is 10% or more at a wavelength of 360 nm and 60 to 80% at a wavelength of 450 nm. With such a reflectance, it is possible to provide a multilayer multi-film excellent in controlling the rise of the ground temperature and preventing the pest from flying by optimally controlling the reflection of sunlight.
また、金属微粒子の含有濃度Ｃ２は０．０５〜０．２ｗt％が好ましい。 The content concentration C 2 of metal fine particles is preferably 0.05~0.2wt%.
この範囲内であると、二酸化チタンと金属微粒子（アルミ微粒子）の互いの干渉により、本発明の目的である地温上昇抑制と害虫飛来防止の効果が発揮され易く、好ましい。 Within this range, it is preferable because titanium dioxide and metal fine particles (aluminum fine particles) interfere with each other, and the effects of the present invention, which are the purpose of the present invention, are to suppress the rise in ground temperature and prevent the pests from flying.
本発明において、金属微粒子は、アルミ微粒子であることが好ましい。 In the present invention, the metal fine particles are preferably aluminum fine particles.
二酸化チタンの結晶型は、ルチルとアナタースの２型があるが、アナタースはフィルム耐候性を大きく低下させるので、通常はルチル型を用いる。 There are two types of crystal forms of titanium dioxide, rutile and anatase. Since anatase greatly reduces the weather resistance of the film, the rutile type is usually used.
二酸化チタンは、紫外線光を吸収し、活性酸素を発生する特性があり、このためフィルム耐候性を低下させるので、本発明で用いる二酸化チタンは、ＴｉＯ２粒子表面をＡｌ、Ｓｉなどの金属酸化膜でコート処理することが好ましい。 Titanium dioxide absorbs ultraviolet light and generates active oxygen, which lowers the film weather resistance. Therefore, titanium dioxide used in the present invention has a metal oxide film such as Al or Si on the surface of TiO 2 particles. It is preferable to coat with.
金属微粒子として含有されるアルミ微粒子は、鱗片状粉末として含有することが好ましい。粉末の粒径は、紫外線を効率よく乱反射させるため、アスペクト比は１０〜１００００の範囲が好ましい。 The aluminum fine particles contained as metal fine particles are preferably contained as scale-like powder. The particle diameter of the powder is preferably in the range of 10 to 10,000 in order to efficiently diffuse and reflect ultraviolet rays.
更に光反射層（白銀色層）には、二酸化チタンやアルミ微粒子以外に本発明の目的を損なわない範囲で、耐候安定剤、酸化防止剤、滑剤、アンチブロッキング剤、無滴剤等の農業用フィルムに使われる添加剤を含有することもできる。 Furthermore, the light reflecting layer (white silver color layer) is used for agricultural purposes such as weather resistance stabilizers, antioxidants, lubricants, anti-blocking agents, and no-drop agents, as long as the object of the present invention is not impaired other than titanium dioxide and aluminum fine particles. Additives used in the film can also be included.
光吸収層（黒色層）１１は、厚みが２〜２８μｍの範囲であることが好ましく、より好ましくは、５〜２０μｍの範囲である。厚みはフィルム断面の光学顕微鏡観察によって測定することができる。なお、白色層の厚みも同様にして測定することができる。 The light absorption layer (black layer) 11 preferably has a thickness in the range of 2 to 28 μm, more preferably in the range of 5 to 20 μm. The thickness can be measured by optical microscope observation of the film cross section. The thickness of the white layer can be measured in the same manner.
黒色層には、カーボンブラックが含有される。かかるカーボンブラックの添加量は、特に限定されないが、１〜１５ｗｔ％の範囲が好ましい。 The black layer contains carbon black. The amount of carbon black added is not particularly limited, but is preferably in the range of 1 to 15 wt%.
本発明の農業用多層マルチフィルムに含有できる添加剤としては、耐侯安定剤、酸化防止剤、滑剤、アンチブロッキング剤、無滴剤等農業用多層マルチフィルムに使われる各種添加剤を使用することができる。 As additives that can be contained in the agricultural multilayer multifilm of the present invention, it is possible to use various additives used in agricultural multilayer multifilms such as wrinkle resistance stabilizers, antioxidants, lubricants, antiblocking agents, and non-dropping agents. it can.
次に、本発明の多層マルチフィルム、具体的には、二層マルチフィルムを製造する方法について以下に説明する。 Next, the method for producing the multilayer multifilm of the present invention, specifically, the two-layer multifilm will be described below.
本発明の二層マルチフィルムを製造するには、インフレーション成形法又はＴダイ成形法が好ましく採用される。 In order to produce the two-layer multifilm of the present invention, an inflation molding method or a T-die molding method is preferably employed.
例えば、光反射層（白銀色層）と光吸収層（黒色層）の２層構造を形成するダイラミ成形で成膜する。 For example, the film is formed by the die forming that forms a two-layer structure of a light reflection layer (white silver color layer) and a light absorption layer (black layer).
前述した各層の条件を満たすように配合された熱可塑性樹脂配合物を、それぞれ別々の押出機で溶融混合して同一の多層ダイに供給して、ダイ内またはダイ外で各層を溶融状態で積層して、次いで冷却して成形する。 The thermoplastic resin compounded to satisfy the conditions of each layer described above is melt-mixed by separate extruders and supplied to the same multilayer die, and each layer is laminated in the molten state inside or outside the die. Then, it is cooled and molded.
以下、本発明の実施例について説明するが、かかる実施例によって本発明が限定されるものではない。 Examples of the present invention will be described below, but the present invention is not limited to these examples.
（フィルム試料の作成）
１）本発明のフィルム１
＜光反射層の配合＞
直鎖状低密度ポリエチレン（ＬＬＤＰＥ）（ＭＩ：１．０、密度０．９２０）に、アルミ微粉末（アスペクト比：５０）を０．１ｗt％、二酸化チタン粉末（平均粒径：０．３μｍ）を１５ｗt％配合した。
(Creation of film sample)
1)
<Composition of light reflection layer>
Linear low density polyethylene (LLDPE) (MI: 1.0, density 0.920), aluminum fine powder (aspect ratio: 50) 0.1 wt%, titanium dioxide powder (average particle size: 0.3 μm) Of 15 wt%.
＜光吸収層の配合＞
光吸収層は光反射層と同じ直鎖状低密度ポリエチレンに、カーボンブラックを５ｗt％配合した。
<Composition of light absorption layer>
For the light absorption layer, 5 wt% of carbon black was mixed with the same linear low density polyethylene as the light reflection layer.
＜フィルム成形＞
上記の配合条件のもと、ダイラミ成形法で、光反射層を１５μｍ、光吸収層を１０μｍの厚さに成形し、厚さ２５μｍの本発明のフィルム１を得た。
<Film forming>
Under the above blending conditions, the
２）本発明のフィルム２
上記本発明のフィルム１の製造において、アルミ微粉末を０．０５ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム２を得た。
2) Film 2 of the present invention
In the production of the
３）本発明のフィルム３
上記本発明のフィルム１の製造において、アルミ微粉末を０．１５ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム３を得た。
3) Film 3 of the present invention
In the production of the
４）本発明のフィルム４
上記本発明のフィルム１の製造において、アルミ微粉末を０．２ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム４を得た。
4) Film 4 of the present invention
In the production of the
５）本発明のフィルム５
上記本発明のフィルム１の製造において、二酸化チタン粉末を１０ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム５を得た。
5) Film 5 of the present invention
In the production of the
６）本発明のフィルム６
上記本発明のフィルム１の製造において、二酸化チタン粉末を２０ｗt％に、アルミ微粉末を０．０５ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム６を得た。
6) Film 6 of the present invention
In the production of the
７）本発明のフィルム７
上記本発明のフィルム１の製造において、二酸化チタン粉末を２０ｗt％に、アルミ微粉末を０．２ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム７を得た。
7) Film 7 of the present invention
In the production of the
８）本発明のフィルム８
上記本発明のフィルム１の製造において、二酸化チタン粉末を２５ｗt％にした他は同様に成形し、厚さ２５μｍの本発明のフィルム８を得た。
8) Film 8 of the present invention
In the production of the
９）比較フィルム１
上記本発明のフィルム１の製造において、アルミ微粉末を０．４ｗt％にした他は同様に成形し、厚さ２５μｍの比較フィルム１を得た。
9)
In the production of the
１０）比較フィルム２
上記本発明のフィルム１の製造において、アルミ微粉末を０．０１ｗt％にした他は同様に成形し、厚さ２５μｍの比較フィルム２を得た。
10) Comparative film 2
In the production of the
１１）比較フィルム３
上記本発明のフィルム１の製造において、アルミ微粉末を加えずに同様に成形し、厚さ２５μｍの比較フィルム３を得た。
11) Comparative film 3
In the production of the
１２）比較フィルム４
直鎖状低密度ポリエチレン（ＬＬＤＰＥ）（ＭＩ：１．０、密度０．９２０）にアルミ微粉末を０．５ｗｔ％配合し、これを単層成形法で成形して、厚さ２５μｍの比較フィルム４を得た。
12) Comparative film 4
Linear low density polyethylene (LLDPE) (MI: 1.0, density 0.920) is mixed with 0.5 wt% of aluminum fine powder, which is molded by a single layer molding method, and a comparative film having a thickness of 25 μm. 4 was obtained.
（実験）
それぞれのフィルムを、巾ｌｍ長さ２ｍの畝に展張して、畝の中央に黄色水盤を置き、飛来して来る有翅アブラムシの数を測定し、各フィルムの害虫忌避効果を調べ、その結果を表１に示した。
(Experiment)
Spread each film on a cocoon with a width of 1m and a length of 2m, place a yellow basin in the center of the cocoon, measure the number of flying aphids, and examine the pest repellent effect of each film. Are shown in Table 1.
また測定期間中の畝頂部１０ｃｍ地点の地温をＴａｎｄＤ社製「おんどとり」を用いて測定した。測定開始から５日間測定した測定値の平均値を表１に示した。 In addition, the soil temperature at the 10 cm peak of the summit during the measurement period was measured using “Andori” manufactured by TandD. Table 1 shows the average value of the measured values measured for 5 days from the start of measurement.
さらに、各フィルム試料について、波長３６０ｎｍ、４５０ｎｍの反射率を、日立分光光度計を用いて測定・算出した。その結果を表１に示した。 Further, for each film sample, the reflectance at wavelengths of 360 nm and 450 nm was measured and calculated using a Hitachi spectrophotometer. The results are shown in Table 1.
（評価）
以上の試験より、一方の面がカーボンブラックを含有する光吸収層で、他方の面が二酸化チタンと金属微粒子を含有する光反射層である農業用マルチフィルムにおいて、二酸化チタンの含有濃度Ｃ１が１０〜２５ｗt％の範囲であり、光反射層の反射率が波長３６０ｎｍで１０％以上、波長４５０ｎｍで６０〜８０％であるときに、飛来して来る有翅アブラムシの数は１０匹未満となり、害虫飛来防止に優れていることが立証された。
(Evaluation)
From the above test, a light absorbing layer one surface of which contains carbon black, the other surface is in agriculture multi-film for a light reflective layer containing titanium dioxide and metal particles, the content concentration C 1 of the titanium dioxide When the reflectivity of the light reflecting layer is 10% or more at a wavelength of 360 nm and 60 to 80% at a wavelength of 450 nm, the number of horny aphids that come in is less than 10 It was proved that it is excellent in preventing pests.
また、実施例１〜８と比較フィルム１、４を比較すると、光反射層の反射率が波長４５０ｎｍで６０〜８０％の範囲内であるときに、地温上昇が抑制されていることがわかった。
Moreover, when Examples 1-8 were compared with the
さらに、金属微粒子の含有濃度Ｃ２が０．０５〜０．２ｗt％である際に、二酸化チタンと金属微粒子（アルミ微粒子）の互いの干渉により、本発明の目的である地温上昇抑制と害虫飛来防止の効果が発揮され易いことが確認できた。 Further, when containing a concentration C 2 of metal fine particles are 0.05～0.2Wt%, by mutual interference of titanium and the metal fine particles dioxide (aluminum particles), soil temperature rise suppression and pests flying is an object of the present invention It was confirmed that the effect of prevention was easily exhibited.
１：多層マルチフィルム
１０：光反射層
１１：光吸収層
1: Multilayer film 10: Light reflection layer 11: Light absorption layer
Claims (3)
全層の厚みが１０〜４０μｍの範囲にあり、
さらに前記光反射層の厚みが５〜３０μｍの範囲にあり、
前記二酸化チタンの含有濃度Ｃ１は１０〜２５ｗt％の範囲であり、
該光反射層の反射率が波長３６０ｎｍで１０％以上、波長４５０ｎｍで６０〜８０％であることを特徴とする農業用多層マルチフィルム。 In an agricultural multi-film in which one side is a light absorbing layer containing carbon black and the other side is a light reflecting layer containing titanium dioxide and metal fine particles,
The thickness of all layers is in the range of 10-40 μm,
Furthermore, the thickness of the light reflecting layer is in the range of 5 to 30 μm,
The titanium dioxide content concentration C1 is in the range of 10 to 25 wt%,
A multilayer multilayer film for agricultural use, wherein the reflectance of the light reflecting layer is 10% or more at a wavelength of 360 nm and 60 to 80% at a wavelength of 450 nm.
The agricultural multi-layered multifilm according to claim 1 or 2, wherein the metal fine particles are aluminum fine particles.