JP6377331B2 - Delamination container - Google Patents

Description

  The present invention relates to a laminated peeling container in which an inner layer peels from an outer layer and shrinks with a decrease in contents.

  2. Description of the Related Art Conventionally, there has been known a laminated peeling container that suppresses air from entering the container by peeling and shrinking the inner layer from the outer layer as the contents are reduced (for example, Patent Document 1).

Japanese Patent No. 3650175

  As such a delamination container, there is one in which the innermost layer of the outer layer is a polypropylene layer and the outermost layer of the inner layer is an EVOH layer. By adopting such a layer structure, in addition to the EVOH layer having excellent oxygen barrier properties, the peelability between the polypropylene layer and the EVOH layer is excellent, so that the oxygen barrier property is excellent and the inner layer Can be easily peeled and contracted.

  By the way, the delamination container is usually composed of a main body part for storing the contents and a mouth part for discharging the contents, while the inner layer smoothly peels from the outer layer in the main body part. There is a demand for preventing the inner layer from peeling from the outer layer at the mouth.

  The present invention has been made in view of such circumstances, and a laminated peeling container capable of preventing the inner layer from peeling from the outer layer smoothly in the main body while preventing the inner layer from peeling from the outer layer in the mouth. Is to provide.

  According to the present invention, a main body part for containing contents and a mouth part for discharging the contents from the main body part, and the main body part and the mouth part comprise an outer layer and an inner layer, Provided is a laminated peeling container in which the inner layer peels and shrinks from the outer layer with a decrease, and the inner layer includes a layer having a standard peeling strength of 7 to 12 g / 15 mm as an outermost layer. .

  As a result of diligent study, the present inventor has found that the inner layer is easily separated from the outer layer in the main body by setting the standard peel strength of the outermost layer of the inner layer to 7 to 12 g / 15 mm in the laminated peeling container in which the inner layer peels from the outer layer. As a result, it was found that an ideal delamination container was obtained in which the inner layer was difficult to peel from the outer layer at the mouth, and the present invention was completed.

Hereinafter, various embodiments of the present invention will be exemplified. The following embodiments can be combined with each other.
Preferably, the outermost layer is an EVOH layer.
Preferably, the EVOH layer contains an oxygen absorbent.
Preferably, the EVOH layer has an ethylene content of 30 mol% or less.
Preferably, the outer layer includes a polypropylene layer as an innermost layer.

(A)-(b) is sectional drawing which shows the structure of the lamination peeling container 1 of one Embodiment of this invention, (a) shows the state which the outer layer 3 and the inner layer 5 contacted, (b) The state which the inner layer 5 peeled from the outer layer 3 is shown. It is sectional drawing which shows the structure of the inner layer 5 of the lamination peeling container 1 of one Embodiment of this invention. The measuring method of the peeling strength in the Example of this invention is shown. It is an example of the graph which shows the relationship between the distance at the time of the peeling strength test in the Example of this invention, and a load.

  Hereinafter, embodiments of the present invention will be described. Various characteristic items shown in the following embodiments can be combined with each other. The invention is established independently for each feature.

  As shown in FIGS. 1 (a) to 1 (b), a delamination container 1 according to an embodiment of the present invention includes a main body 1a composed of a cylindrical body and a bottom, and filling and discharging of contents. And a mouth portion 1b. The mouth portion 1b is provided with a male screw portion 1c. A cap or a pump having a female screw is attached to the male screw portion 1c. In addition, you may use a stopper cap not only when attaching a cap with a screw | thread.

  The delamination container 1 includes an outer layer 3 on the container outer surface side and an inner layer 5 on the container inner surface side. The accommodation space 7 surrounded by the inner layer 5 is filled with the contents. FIG. 1A shows a state in which the contents are fully filled in the container and the outer layer 3 and the inner layer 5 are in contact with each other, and FIG. 1B shows that the contents are discharged from the mouth portion 1b. Shows a state in which the inner layer 5 is peeled from the outer layer 3 and the accommodation space 7 is contracted. In the space 9 between the outer layer 3 and the inner layer 5, an air introduction hole is provided in the outer layer 3 of the main body 1a or the mouth 1b, and air can be introduced through the air introduction hole. Note that a check valve may be provided in the air introduction hole so that air is not discharged from the space 9 to the outside.

  The contents are discharged from the storage space 7 by pressing the outer layer 3 like a squeeze container for storing contents such as mayonnaise and soy sauce, so that the inner layer 5 is crushed together and the contents are discharged from the mouth portion 1b. Alternatively, a pump may be attached to the male screw portion 1c and the contents may be discharged by operating the pump. In addition, when a check valve is provided in the air introduction hole, when the outer layer 3 is crushed, the internal pressure of the air between the outer layer 3 and the inner layer 5 increases, so that the inner layer 5 is crushed and the contents are crushed. It can also be discharged.

  When air enters the space 9 between the outer layer 3 and the inner layer 5, the outermost layer of the inner layer 5 is exposed to the air. Here, the detailed structure of the inner layer 5 is shown in FIG. As shown in FIG. 2, the inner layer 5 includes an EVOH layer 5a which is the outermost layer, an inner surface layer 5b provided on the inner surface of the container of the EVOH layer 5a, and an adhesive provided between the EVOH layer 5a and the inner surface layer 5b. A layer 5c is provided. By providing the EVOH layer 5a, the gas barrier property is excellent. In this embodiment, the outermost layer of the inner layer 5 is the EVOH layer 5a, but the outermost layer may be formed of another resin as long as the standard peel strength is 7 to 12 g / 15 mm.

  The EVOH layer 5a is a layer made of an ethylene-vinyl alcohol copolymer (EVOH) resin, and is obtained by hydrolysis of ethylene and vinyl acetate copolymer. The ethylene content of the EVOH resin is, for example, 25 to 50 mol%, and preferably 30 mol% or less from the viewpoint of oxygen barrier properties. Although the minimum of ethylene content is not prescribed | regulated, since the softness | flexibility of EVOH layer 5a is easy to fall, so that ethylene content is small, 25 mol% or more is preferable. The EVOH layer 5a preferably contains an oxygen absorbent. By containing the oxygen absorbent in the EVOH layer 5a, the oxygen barrier property of the EVOH layer 5a can be further improved.

  The EVOH layer 5a has a standard peel strength of 7 to 12 g / 15 mm. When the standard peel strength is within the above range, the ideal laminated peeling container 1 in which the inner layer 5 is easily peeled from the outer layer 3 in the main body 1a and the inner layer 5 is difficult to peel from the outer layer 3 in the mouth 1b. It was experimentally found that Specifically, the standard peel strength is, for example, 7, 7.5, 8, 8.5, 9, 9.5, 10, 10.5, 11, 11.5, 12 g / 15 mm, and is exemplified here. It may be within a range between any two of the numerical values. In addition, the measuring method of standard peeling strength is demonstrated in detail in an Example.

  The EVOH layer 5a preferably has a tensile modulus of 2000 MPa or less, and more preferably 1800 MPa or less. This is because if the tensile elastic modulus is too high, the EVOH layer 5a is difficult to peel off from the outer layer 3 smoothly. The lower limit of the tensile elastic modulus is not particularly specified, but is, for example, 1000 MPa. Specifically, the tensile elastic modulus is, for example, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000 MPa, and within a range between any two of the numerical values exemplified here. There may be.

  The inner surface layer 5b is a layer that comes into contact with the contents of the delamination container 1 and is, for example, a polyolefin such as low density polyethylene, linear low density polyethylene, high density polyethylene, polypropylene, ethylene-propylene copolymer, and a mixture thereof. It is preferably made of low-density polyethylene or linear low-density polyethylene.

  The adhesive layer 5c is a layer having a function of adhering the EVOH layer 5a and the inner surface layer 5b. For example, an acid-modified polyolefin having a carboxyl group introduced into the above-described polyolefin (eg, maleic anhydride-modified polyethylene) And ethylene vinyl acetate copolymer (EVA). An example of the adhesive layer 5c is a mixture of low-density polyethylene or linear low-density polyethylene and acid-modified polyethylene.

  The outer layer 3 is made of, for example, the above-described polyolefin, and polypropylene is preferable. In the present embodiment, the outer layer 3 has a single-layer configuration, but the outer layer 3 may have a multi-layer configuration. In the case of a multi-layer configuration, the innermost layer is preferably a polypropylene layer, and for example, a configuration in which both sides of a repro layer are sandwiched between polypropylene layers can be employed. Here, the repro layer refers to a layer that is recycled from the burr that was produced when the container was molded. Moreover, the outer layer 3 is formed thicker than the inner layer 3 so as to have resilience.

  The manufacturing method of the lamination peeling container 1 of this embodiment is not specifically limited, For example, the laminated parison of a molten state provided with the laminated structure corresponding to the container which should be manufactured is extruded, and this laminated parison of a molten state is blow molded metal It can be obtained by setting in a mold and molding into a desired container shape by blow molding. In addition, although the pinch-off part is not illustrated in FIG. 1, it is appropriately provided at the bottom of the container. In the case of forming the air introduction hole, it can be formed by a punch or a drill after the blow molded body is taken out from the mold.

  The laminated peeling container 1 obtained by blow molding may be filled with the contents as it is, or after the preliminary peeling before filling the contents, the contents may be filled. In the laminated peeling container 1 of the present embodiment, the preliminary peeling is performed, for example, by injecting air between the outer layer 3 and the inner layer 5 from an air introduction hole provided in the outer layer 3 or between the outer layer 3 and the inner layer 5. This can be performed by forcibly injecting air between the outer layer 3 and the inner layer 5 from the interface P. In the method of injecting air from the interface P of the container mouth portion, the cylindrical portion is integrally formed so as to extend further from the tip of the container mouth portion when the container is formed. By crushing part of the cylindrical part toward the center of the cylindrical part, the inner layer in the cylindrical part is partially peeled off, a hole is made in the outer layer corresponding to the peeled part, and air is injected from the hole To do. At this time, in order to prevent the air injected from the interface at the opening end of the cylindrical portion from leaking to the outside, the plug or the like is pushed into the opening end and the inner layer and the outer layer at the opening end are brought into close contact to seal the opening end interface. May be. After this preliminary peeling step is finished, a cylindrical portion unnecessary for the container is cut into the container shown in FIG.

1. Production of Laminated Peeling Container 1 A laminated peeling container having a main body part and a mouth part was produced by blow molding under the following conditions.
(1) Container shape Main body: φ47mm, height 110mm
Mouth: φ30mm, height 16mm

(2) Layer structure Outer layer: Polypropylene (manufactured by Sumitomo Chemical, model: FSX16E9)
Inner layer: Three-layer configuration of outermost layer / adhesive layer / inner surface layer in order from the outer layer side Outermost layer: resin shown in Table 1 Adhesive layer: adhesive component (Mitsubishi Chemical, model: Modic L522): LLDPE (manufactured by Nippon Polyethylene, model: Harmolex F325N) = 1: 1
Inner surface layer: LLDPE (Nippon Polyethylene, Model: Harmolex F325N)

(3) Blow molding conditions A melted laminated parison is prepared by co-extrusion of each molten resin so as to have the above layer structure, and the molten laminated parison is set in a blow molding die. To form a desired container shape. The coextrusion conditions were adjusted so that both the outer layer and inner layer thicknesses were in the range of 70 to 130 μm and the outer layer / inner layer thickness ratio was 0.8 to 1.3. The blow molding conditions were blow pressure: 0.4 MPa, mold temperature: 25 ° C., and blow time: 15 seconds.

2. Peel strength measurement About the lamination peeling container produced on the said conditions, the T-type peel strength was measured using the peelable strength tester (the Shinto Kagaku Co., Ltd. make, HEIDON-17 type | mold). Specifically, a strip of 15 mm (circumference) × 100 mm (height) is cut out from the produced container, and as shown in FIG. 3, the outer layer and the inner layer are formed at a test speed of 200 mm / min so that the strip becomes T-shaped. It was made to peel 40-50 mm. An example of the relationship between the distance and the load at the time of peeling is a graph shown in FIG. 4, and the average strength ignoring the initial rising strength is defined as “standard peel strength”. The results are shown in Table 1.

3. Evaluation (1) Peelability of main body part Preliminary peeling by forming an air introduction hole in the outer layer of the main body part of the laminated peeling container produced under the above conditions and injecting air between the outer layer and the inner layer from the air introduction hole Went. Air was injected for 1.0 second at a pressure of 0.3 MPa. The peeled state in the main body after the preliminary peeling was visually observed and evaluated according to the following criteria.

<Peelability of main body>
○: Unpeeled area is less than 20% of main body part ×: Unpeeled area is 20% or more of main body part

(2) Anti-peeling resistance of the mouth When the pre-peeling is performed and the air introduction hole is closed, the container is crushed with a force of about 30 kg and pressure is applied to the air between the outer layer and the inner layer. In addition, it was confirmed whether air leaks from the interface between the outer layer and the inner layer in the mouth. In addition, since it was not able to carry out preliminary peeling about the comparative example 4, confirmation of the peeling resistance of a mouth part is not performed.
<Peeling resistance of mouth>
○: No air leakage from the mouth interface ×: Air leakage from the mouth interface

The details of the resin shown in Table 1 are as follows.
SF7503B: Nippon Gosei, EVOH resin AP461: Kuraray, EVOH resin EV3010N: Nippon Zeon, EVOH resin DC3212B: Nihon Gosei, EVOH resin D2908: Nihon Gosei, EVOH resin ST230: Nihon Gosei, EVOH resin F108-1 : Sumitomo Chemical, LDPE resin

4). Discussion As shown in Table 1, in Examples 1 to 3 having a standard peel strength of 7 to 12 g / 15 mm, excellent results were obtained in both the peelability of the main body and the peel resistance of the mouth. On the other hand, in Comparative Examples 1 to 3 having a standard peel strength of less than 7 g / 15 mm, the peel resistance of the mouth was not sufficient. Moreover, in Comparative Example 4 in which the standard peel strength exceeds 12 g / 15 mm, the peelability of the main body was poor.

1: Laminated peeling container, 3: outer layer, 5: inner layer, 7: accommodating space, 9: space

Claims (6)

A main body for containing the contents, and a mouth for discharging the contents from the main body, and the main body and the mouth are provided with an outer layer and an inner layer, and the inner layer as the contents decrease. Is a delamination container that peels and shrinks from the outer layer,
The mouth and the main body are formed by blow molding a laminated parison,
The inner layer, standard peel strength between the outer layer in the body portion Ri 8~11gf / 15mm der,
The delamination container, said body portion is pre-peeled and that has an air inlet hole is provided in the outer layer, delamination container. The delamination container according to claim 1, wherein the outermost layer is an EVOH layer. The delamination container according to claim 2, wherein the EVOH layer contains an oxygen absorbent. The laminated peeling container according to claim 2 or 3, wherein the EVOH layer has an ethylene content of 30 mol% or less. The said outer layer is a lamination peeling container as described in any one of Claims 1-4 provided with a polypropylene layer in an innermost layer. The delamination container according to any one of claims 1 to 5, wherein the inner layer and the outer layer are laminated and exposed at an end surface of the mouth portion.