JP7127499B2 - makeup sheet - Google Patents
makeup sheet Download PDFInfo
- Publication number
- JP7127499B2 JP7127499B2 JP2018212863A JP2018212863A JP7127499B2 JP 7127499 B2 JP7127499 B2 JP 7127499B2 JP 2018212863 A JP2018212863 A JP 2018212863A JP 2018212863 A JP2018212863 A JP 2018212863A JP 7127499 B2 JP7127499 B2 JP 7127499B2
- Authority
- JP
- Japan
- Prior art keywords
- resin layer
- layer
- polyethylene terephthalate
- decorative sheet
- thickness
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、木質系基材、無機質系基材、合成樹脂基材、金属系基材等々の基材へ貼り合わせる化粧シートに関するものである。 TECHNICAL FIELD The present invention relates to a decorative sheet to be attached to a base material such as a wood base material, an inorganic base material, a synthetic resin base material, a metal base material, or the like.
従来、このような用途に使用される化粧シートとしては、ポリ塩化ビニル樹脂フィルムに適宜の絵柄の印刷を施してなるものが主流であった。また近年ではそれに加えて、環境問題への対応を考慮して、燃焼時の塩化水素又はダイオキシン等の有害物質の発生のおそれのない、ポリオレフィン系樹脂等の非塩素系樹脂フィルムを使用した化粧シートも開発され、広く使用される様になりつつある。 Conventionally, decorative sheets used for such purposes mainly consist of polyvinyl chloride resin films printed with appropriate patterns. In addition to this, in recent years, in consideration of environmental issues, decorative sheets using non-chlorine resin films such as polyolefin resins that do not generate harmful substances such as hydrogen chloride or dioxins when burned have been developed and are in widespread use.
また、たとえば化粧シートにおいては、耐傷付き性・耐摩耗性が求められる。具体的には、物をぶつけたり、移動の際に擦ったりした際に、表面に傷がつかないことが求められる。 Further, for example, decorative sheets are required to have scratch resistance and abrasion resistance. Specifically, the surface is required not to be scratched when it is hit with an object or rubbed during movement.
そのほか、一般に化粧シートは、板状の基材に貼りあわせて、化粧板として商品化され、現場で施工されることが多く、その場合には、切削加工性やそのほかの施工性も求められることになる。 In addition, in general, decorative sheets are laminated to a plate-like base material, commercialized as decorative boards, and often installed on site. In that case, cutting workability and other workability are also required. become.
特許文献１には、耐傷付き性・耐摩耗性に配慮して、中空ビーズを用いた化粧シートが提案されているが、耐傷付き性・耐摩耗性に加えて断熱性にも優れた化粧シートであるもの、切削加工性にまで配慮したものではなかった。
本発明はかかる状況に鑑みてなされたものであり、熱可塑性樹脂を基材とする化粧シートにおいて、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる、化粧シートを提供することを課題とする。 The present invention has been made in view of this situation, and the decorative sheet made of thermoplastic resin has excellent wear resistance when made into a decorative board, and is resistant to cutting using a circular saw or hand router. To provide a decorative sheet having excellent machinability.
上記の課題を解決するための手段として、請求項１に記載の発明は、
化粧シートにおいて、
化粧シート表面側から、表面保護層、透明熱可塑性樹脂層、第２接着剤層、ポリエチレンテレフタレート樹脂層、第１接着剤層、絵柄模様層、熱可塑性基材樹脂シートがこの順に積層されており、
表面保護層は電離放射線硬化型樹脂を含んでおり、
透明熱可塑性樹脂層は、エンボス加工による凹凸を有しており、
この透明熱可塑性樹脂層の厚さは、５０μｍ以上、１５０μｍ以下の範囲であって、
ポリエチレンテレフタレート樹脂層は、延伸処理をしていないフィルムで形成され、
このポリエチレンテレフタレート樹脂層の厚さは、１５０μｍ以上、３００μｍ以下の範囲であって、
ポリエチレンテレフタレート樹脂層と、透明熱可塑性樹脂層との合計の厚さは、２００μｍ以上、３５０μｍ以下の範囲であることを特徴とする化粧シートである。
As a means for solving the above problems, the invention according to
In the cosmetic sheet,
A surface protective layer, a transparent thermoplastic resin layer, a second adhesive layer, a polyethylene terephthalate resin layer, a first adhesive layer, a picture pattern layer, and a thermoplastic base resin sheet are laminated in this order from the surface side of the decorative sheet. ,
The surface protective layer contains an ionizing radiation curable resin,
The transparent thermoplastic resin layer has unevenness due to embossing,
The thickness of the transparent thermoplastic resin layer is in the range of 50 μm or more and 150 μm or less,
The polyethylene terephthalate resin layer is formed of a film that has not been stretched,
The thickness of the polyethylene terephthalate resin layer is in the range of 150 μm or more and 300 μm or less,
The decorative sheet is characterized in that the total thickness of the polyethylene terephthalate resin layer and the transparent thermoplastic resin layer is in the range of 200 µm or more and 350 µm or less.
また、請求項２に記載の発明は、
前記透明熱可塑性樹脂層は、第１の樹脂層と第２の樹脂層とから構成され、
第１の樹脂層は、ポリエチレンテレフタレート樹脂層側に配置されて、透明マレイン酸変性ポリプロピレン樹脂であって、
第２の樹脂層は、表面保護層側に配置されて、透明ポリプロピレン樹脂であることを特徴とする、請求項１に記載の化粧シートである。
In addition, the invention according to claim 2,
The transparent thermoplastic resin layer is composed of a first resin layer and a second resin layer,
The first resin layer is arranged on the side of the polyethylene terephthalate resin layer and is a transparent maleic acid-modified polypropylene resin,
2. The decorative sheet according to
また、請求項３に記載の発明は、
前記第１の樹脂層の厚さは、１０μｍ以上であって、かつ透明熱可塑性樹脂層の厚さの２０％以下であることを特徴とする、請求項２に記載の化粧シートである。
In addition, the invention according to claim 3,
3. The decorative sheet according to claim 2, wherein the thickness of the first resin layer is 10 [mu]m or more and 20% or less of the thickness of the transparent thermoplastic resin layer.
本発明によれば、熱可塑性樹脂を基材とする化粧シートにおいて、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる、化粧シートを提供することが可能である。 According to the present invention, a decorative sheet having a thermoplastic resin as a base material has excellent abrasion resistance when made into a decorative board, and has excellent cutting workability for cutting using a circular saw or a hand router. It is possible to provide a sheet.
また、特に請求項２に記載の発明においては、透明熱可塑性樹脂層は、ポリエステル系樹脂層側から、第１の樹脂を含んでなる層と、第１の樹脂とは異なる第２の樹脂を含んでなる層とがこの順に積層されて形成されており、第１の樹脂は透明マレイン酸変性ポリプロピレンを含んでなる層であり、第２の樹脂は透明ポリプロピレンを含んでなる層であることを特徴とするものである。 Further, particularly in the invention according to claim 2, the transparent thermoplastic resin layer comprises a layer containing a first resin and a second resin different from the first resin from the polyester resin layer side. and a layer containing transparent polypropylene are laminated in this order, the first resin is a layer containing transparent maleic acid-modified polypropylene, and the second resin is a layer containing transparent polypropylene. It is characterized.
すなわち、第１の樹脂の層が基材シートとの接着性を担保し、第２の層が層の主要部分となって、その他の物性を担うなど、材料の設計の巾を広げることが可能となる。第１の層を透明マレイン酸変性ポリプロピレンとすることで、熱可塑性基材樹脂シートとの接着性を良くすることができる。また、第２の層を透明ポリプロピレンを含んでなる層とすることで、樹脂内部の耐脆化に効果をあらわすことができる。 In other words, the first resin layer ensures adhesion to the base sheet, and the second layer becomes the main part of the layer, and is responsible for other physical properties, making it possible to expand the range of material design. becomes. By using transparent maleic acid-modified polypropylene for the first layer, the adhesiveness to the thermoplastic base resin sheet can be improved. Further, by forming the second layer as a layer containing transparent polypropylene, it is possible to exhibit an effect of resistance to embrittlement inside the resin.
また、特に請求項３に記載の発明においては、第１の樹脂層の厚みは、１０μｍ以上であり、且つ、透明熱可塑性樹脂層全体の厚みの２０％以下であることを特徴とするものである。 Further, in the invention according to claim 3, the thickness of the first resin layer is 10 μm or more, and is 20% or less of the total thickness of the transparent thermoplastic resin layer. be.
上記の構成のシートを作成することにより、透明熱可塑性樹脂層の密着性能を担保しつつ、十分な表面硬度をあらわすことが可能である。 By producing the sheet having the above structure, it is possible to exhibit sufficient surface hardness while ensuring the adhesion performance of the transparent thermoplastic resin layer.
以下、本発明を図１を参照しながら、更に詳しい説明を加える。ただし本発明は、ここに示す例にのみ限定されるものではない。本発明は、請求項によって限定されるものである。 Hereinafter, the present invention will be described in more detail with reference to FIG. However, the invention is not limited to the examples shown here. The invention is limited by the claims.
図１は本発明に係る化粧シートの一実施態様を説明するための、部分断面模式図である。 FIG. 1 is a schematic partial cross-sectional view for explaining one embodiment of the decorative sheet according to the present invention.
本発明による化粧シート（２０）の層構成は、化粧シート表面側から、表面保護層（９）、透明熱可塑性樹脂層（８）、第２接着剤層（５）、ポリエチレンテレフタレート樹脂層（４）、第１接着剤層（３）、絵柄模様層（２）、熱可塑性基材樹脂シート（１）がこの順に積層されている。 The layer structure of the decorative sheet (20) according to the present invention comprises, from the surface side of the decorative sheet, a surface protective layer (9), a transparent thermoplastic resin layer (8), a second adhesive layer (5), a polyethylene terephthalate resin layer (4). ), the first adhesive layer (3), the pattern layer (2), and the thermoplastic base resin sheet (1) are laminated in this order.
このうち、表面保護層は電離放射線硬化型樹脂を含んでおり、化粧シートの最表面にあって、化粧シートに対する直接の外力、たとえば物がぶつかったり、移動の際に擦ったりといった外力に対して化粧シートを保護する役割を果たす。 Among them, the surface protective layer contains an ionizing radiation curable resin, and is located on the outermost surface of the decorative sheet and protects the decorative sheet from direct external forces such as objects colliding with it and rubbing it during movement. Plays a role in protecting the cosmetic sheet.
したがって、電離放射線硬化型樹脂によって表面の硬度を上げることは、耐傷性の向上に効果的である。 Therefore, increasing the hardness of the surface with an ionizing radiation curable resin is effective in improving the scratch resistance.
また、透明熱可塑性樹脂層（８）は、エンボス加工による凹凸（１０）を有しており、これは意匠性の向上を目的とする。たとえば、絵柄模様層（２）が木目の場合には、自然木の持つ導管を凹みで表現したり、木目以外の場合でも砂目や幾何学模様の凹凸で意匠性を高めることが可能である。なお、このエンボス加工による凹凸（１０）は、表面保護層（９）を形成する前に形成したものでも良く、あるいは表面保護層（９）を形成した後に形成したものでもよい。 Further, the transparent thermoplastic resin layer (8) has unevenness (10) by embossing for the purpose of improving the design. For example, if the pattern layer (2) has a wood grain, it is possible to express the conduits of natural wood with dents, and even if the pattern layer (2) is not a wood grain, it is possible to enhance the design by embossing grain or geometric patterns. . The embossed unevenness (10) may be formed before the surface protective layer (9) is formed, or may be formed after the surface protective layer (9) is formed.
この透明熱可塑性樹脂層（８）の厚さは、５０μｍ以上、１５０μｍ以下の範囲であって、この厚さであれば、エンボス加工による凹凸（１０）を形成することに支障がないことのほか、耐摩耗性において、物理的な磨耗に対して十分実用範囲である。あるいは、意匠性の面でも、透明熱可塑性樹脂層（８）の存在が、絵柄模様層（２）と相俟って、より深みや奥行きを感じさせる効果を持つ。 The thickness of the transparent thermoplastic resin layer (8) is in the range of 50 µm or more and 150 µm or less. In terms of abrasion resistance, it is sufficiently practical for physical abrasion. Alternatively, in terms of design, the presence of the transparent thermoplastic resin layer (8), together with the picture pattern layer (2), has the effect of giving a sense of depth and depth.
透明熱可塑性樹脂層（８）は、第２接着剤層（５）を介して、ポリエチレンテレフタレート樹脂層（４）と積層されている。 The transparent thermoplastic resin layer (8) is laminated with the polyethylene terephthalate resin layer (4) via the second adhesive layer (5).
ポリエチレンテレフタレート樹脂層（４）は、延伸処理をしていないフィルムで形成される。本発明において、このポリエチレンテレフタレート樹脂層（４）の厚さは、１５０μｍ以上、３００μｍ以下の範囲である。 The polyethylene terephthalate resin layer (4) is formed of a non-stretched film. In the present invention, the thickness of the polyethylene terephthalate resin layer (4) is in the range of 150 µm or more and 300 µm or less.
我々は本発明を検討する過程において、このポリエチレンテレフタレート樹脂層（４）に、延伸処理をしていないポリエチレンテレフタレートフィルムフィルムを用いることが、化粧シート（２０）の機械的強度を向上させるほか、本発明の課題である、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる、化粧シート（２０）の実現に極めて効果的であることを見出した。 In the process of studying the present invention, we found that the use of a polyethylene terephthalate film film that has not been stretched as the polyethylene terephthalate resin layer (4) improves the mechanical strength of the decorative sheet (20), It is extremely effective in realizing a decorative sheet (20) that has excellent abrasion resistance when made into a decorative board and excellent machinability for cutting using a circular saw or a hand router, which is the subject of the invention. I found out.
またポリエチレンテレフタレート樹脂層（４）と、透明熱可塑性樹脂層（８）との合計の厚さは、２００μｍ以上、３５０μｍ以下の範囲である。我々はこの範囲であることにより、化粧シート（２０）としての可撓性と機械的強度を損なうことがなく、またインラインでのロールラミネートなど化粧板への加工性、さらに化粧板としての加工性などに支障をきたすことがなく、使い勝手がよいことを見出した。 The total thickness of the polyethylene terephthalate resin layer (4) and the transparent thermoplastic resin layer (8) is in the range of 200 µm or more and 350 µm or less. We have found that this range does not impair the flexibility and mechanical strength of the decorative sheet (20), and the processability into a decorative board such as in-line roll lamination, as well as the processability as a decorative board. It was found that it is easy to use without causing any trouble.
また、透明熱可塑性樹脂層は、第１の樹脂層（６）と第２の樹脂層（７）とから構成することができる。第１の樹脂層（６）は、ポリエチレンテレフタレート樹脂層（４）側に配置されて、透明マレイン酸変性ポリプロピレン樹脂とすることができ、第２の樹脂層（７）は、表面保護層（９）側に配置されて、透明ポリプロピレン樹脂とすることができる。また、これらの層形成には、たとえば押出機などを用いて製膜、積層する方法などによることができる。 Also, the transparent thermoplastic resin layer can be composed of a first resin layer (6) and a second resin layer (7). The first resin layer (6) is arranged on the polyethylene terephthalate resin layer (4) side and can be made of a transparent maleic acid-modified polypropylene resin, and the second resin layer (7) is a surface protective layer (9 ) side and can be transparent polypropylene resin. In addition, for forming these layers, for example, a method of film formation and lamination using an extruder or the like can be used.
これによって、第１の樹脂層（６）が基材シートとの接着性を担保し、第２の樹脂層（
７）が主要部分となって、その他の物性を担うなど、材料の設計の巾を広げることが可能となる。第１の樹脂層（６）を透明マレイン酸変性ポリプロピレンとすることで、層間の接着性を良くすることができる。また、第２の樹脂層（７）を透明ポリプロピレンを含んでなる層とすることで、樹脂内部の耐脆化に効果をあらわすことができる。
Thereby, the first resin layer (6) secures adhesion to the base sheet, and the second resin layer (
7) becomes the main part, and it becomes possible to expand the range of material design, such as taking responsibility for other physical properties. Adhesion between layers can be improved by using transparent maleic acid-modified polypropylene for the first resin layer (6). Further, by using a layer containing transparent polypropylene as the second resin layer (7), an effect can be exhibited in terms of resistance to embrittlement inside the resin.
すなわち、化粧シート（２０）を構成する積層体の層間強度の向上に資するのであり、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる化粧シート（２０）の実現において効果的である。 That is, it contributes to the improvement of the interlaminar strength of the laminate constituting the decorative sheet (20). It is effective in realization of the decorative sheet (20) excellent in
また、第１の樹脂層（６）の厚さは、１０μｍ以上であって、かつ透明熱可塑性樹脂層全体の厚さの２０％以下とすることができる。この構成の化粧シート（２０）とすることにより、透明熱可塑性樹脂層（８）の密着性能を担保しつつ、十分な表面硬度をあらわすことが可能である。 Also, the thickness of the first resin layer (6) can be 10 μm or more and 20% or less of the total thickness of the transparent thermoplastic resin layer. By using the decorative sheet (20) having this structure, it is possible to exhibit sufficient surface hardness while ensuring the adhesion performance of the transparent thermoplastic resin layer (8).
このようにして、本発明が課題とするところの、熱可塑性樹脂を基材とする化粧シート（２０）において、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる、化粧シート（２０）を提供することが可能である。 In this way, the decorative sheet (20) made of a thermoplastic resin, which is the object of the present invention, has excellent wear resistance when made into a decorative board, and can be cut using a circular saw or a hand router. It is possible to provide a decorative sheet (20) that is excellent in machinability against.
以下本発明を、実施例１～実施例５、および比較例１によって更に具体的な説明を加える。ただし本発明は、ここに示す例にのみ限定されるものではない。本発明は、請求項によって限定されるものである。 The present invention will be described in more detail with reference to Examples 1 to 5 and Comparative Example 1 below. However, the invention is not limited to the examples shown here. The invention is limited by the claims.
実施例１～実施例５、および比較例１の化粧シートを作成し、化粧シートについて評価、また木質基材に貼りあわせて、化粧板としても評価を行なった。 The decorative sheets of Examples 1 to 5 and Comparative Example 1 were prepared, evaluated for the decorative sheet, and also evaluated as a decorative board by bonding to a wooden substrate.
化粧板の構成は以下のとおりである。
厚さ６ｍｍのＭＤＦに、エチレン－酢酸ビニル共重合エマルジョン型接着剤を塗布し、化粧シートと貼り合せ化粧板とした。
The configuration of the decorative board is as follows.
An ethylene-vinyl acetate copolymer emulsion type adhesive was applied to MDF having a thickness of 6 mm to prepare a decorative sheet and a laminated decorative board.
評価項目、評価対象および評価基準は以下のとおりである。
いずれも△評価以上で、実用可能レベルである。
Evaluation items, evaluation targets, and evaluation criteria are as follows.
All of them are △ evaluation or more, and are practically possible levels.
１．耐摩耗性：化粧板
化粧板を、ＪＡＳ フローリングの日本農林規格に規定される耐磨耗試験を実施した。
絵柄の消失が始まるまでの回転数を確認した。
なお、磨耗紙の交換は１０００回転毎とした。
◎：３０００回転以上
〇：２５００～２９９９回転
△：２０００～２４９９回転
×：２０００回転未満。
1. Abrasion resistance: The decorative board was subjected to an abrasion resistance test specified in the Japanese Agricultural Standards for JAS flooring.
The number of rotations until the pattern started to disappear was confirmed.
The worn paper was exchanged every 1000 revolutions.
◎: 3000 rpm or more ○: 2500 to 2999 rpm △: 2000 to 2499 rpm ×: less than 2000 rpm.
２．耐傷性：化粧板
化粧板を、ＪＩＳ Ｋ ５６００に規定される鉛筆硬度試験機にかけ、傷のつき方を確認した。
◎：７Ｈ以上
〇：４Ｈ～６Ｈで傷なし
△：Ｈ～３Ｈで傷なし
×：Ｈより柔らかいレベルで傷なし。
2. Scratch resistance: The decorative board was subjected to a pencil hardness tester specified in JIS K 5600 to confirm how it was scratched.
⊚: 7H or more ∘: No damage at 4H to 6H △: No damage at H to 3H ×: No damage at a level softer than H.
３．加工性：化粧シート
化粧シートを化粧板に加工する際の適性について評価した。
◎：インラインでのロールラミネートが可能。
〇：インラインでのロールラミネートが可能だが、やや慎重性を要する。
△：インラインでのロールラミネートが可能だが、かなりの慎重性を要する。
×：ロールラミネート不可。枚葉のみで可能。
3. Processability: The suitability of processing the decorative sheet into a decorative board was evaluated.
A: In-line roll lamination is possible.
◯: In-line roll lamination is possible, but requires a little caution.
Δ: In-line roll lamination is possible, but considerable caution is required.
x: Roll lamination not possible. Single wafer only.
４．切削性（１）：化粧板
化粧板を丸ノコで切断加工、およびハンドルータにより表面が基材であるＭＤＦに達する切削加工試験を行ない、化粧シートのバリの発生の有無を確認した。
◎：バリが発生しない。
〇：バリが一部見られるが、容易に修正可能。
△：バリが一部見られ、修正が必要。
×：バリがほぼ全面に発生し、手作業での修正は困難。
4. Machinability (1): Decorative plate A decorative plate was cut with a circular saw, and a cutting test was performed with a hand router so that the surface reached the base material MDF, and the presence or absence of burrs on the decorative sheet was confirmed.
⊚: No burr occurs.
◯: Some burrs are observed, but can be easily corrected.
△: Some burrs are observed and need to be corrected.
x: Burrs occur almost all over the surface, and manual correction is difficult.
５．切削性（２）：化粧板
化粧板を丸ノコで切断加工、およびハンドルータにより表面が基材であるＭＤＦに達する切削加工試験を行ない、化粧シートのポリエチレンテレフタレート樹脂層の凝集破壊の発生の有無を確認した。
◎：ポリエチレンテレフタレート樹脂層の凝集破壊は発生しない。
〇：ポリエチレンテレフタレート樹脂層の凝集破壊が一部見られるが、容易に修正可能。△：ポリエチレンテレフタレート樹脂層の凝集破壊が一部見られ、修正が必要。
×：ポリエチレンテレフタレート樹脂層の凝集破壊がほぼ全端部に発生し、修正は困難。
5. Machinability (2): A decorative board was cut with a circular saw, and a cutting test was conducted with a hand router so that the surface reached the base material MDF, and whether cohesive failure occurred in the polyethylene terephthalate resin layer of the decorative sheet. It was confirmed.
A: Cohesive failure of the polyethylene terephthalate resin layer does not occur.
○: Cohesive failure of the polyethylene terephthalate resin layer is partially observed, but can be easily corrected. Δ: Some cohesive failure of the polyethylene terephthalate resin layer is observed, and correction is required.
x: Cohesive failure of the polyethylene terephthalate resin layer occurs at almost all edges, and correction is difficult.
６．密着強度：化粧シート
◎：密着強度が２．０ｋｇｆ／ｃｍ２より大きい。
×：密着強度が２．０ｋｇｆ／ｃｍ２以下である。
6. Adhesion strength: Decorative sheet ⊚: Adhesion strength is greater than 2.0 kgf/cm 2 .
x: Adhesion strength is 2.0 kgf/cm 2 or less.
７．生産性：化粧シート
透明熱可塑性樹脂層を押し出し積層する際の生産適性を確認した。
◎：安定した生産が可能。
〇：安定した生産が可能であるが、気を配る必要がある。
△：ロングラン生産においてロール取られなどの可能性が有り慎重性を要する。
×：シワの発生や、ロール取られなどがあり、生産は困難。
7. Productivity: The production aptitude for extruding and laminating the transparent thermoplastic resin layer of the decorative sheet was confirmed.
A: Stable production is possible.
○: Stable production is possible, but care is required.
△: In long-run production, there is a possibility that the roll will be taken, so caution is required.
x: Production is difficult due to occurrence of wrinkles, roll removal, and the like.
＜実施例１＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：９０μｍ
ポリエチレンテレフタレート樹脂層（４）：１９０μｍ
上記合計：２９０μｍ
である。
<Example 1>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 90 μm
Polyethylene terephthalate resin layer (4): 190 μm
Total above: 290 μm
is.
＜実施例２＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：１００μｍ
ポリエチレンテレフタレート樹脂層（４）：２５０μｍ
上記合計：３５０μｍ
である。
<Example 2>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 100 μm
Polyethylene terephthalate resin layer (4): 250 μm
Total above: 350 μm
is.
＜実施例３＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：１００μｍ
ポリエチレンテレフタレート樹脂層（４）：１５０μｍ
上記合計：２５０μｍ
である。
<Example 3>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 100 μm
Polyethylene terephthalate resin layer (4): 150 μm
Total above: 250 μm
is.
＜実施例４＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：１５０μｍ
ポリエチレンテレフタレート樹脂層（４）：１９０μｍ
上記合計：３４０μｍ
である。
<Example 4>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 150 μm
Polyethylene terephthalate resin layer (4): 190 μm
Total above: 340 μm
is.
＜実施例５＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：５０μｍ
ポリエチレンテレフタレート樹脂層（４）：１９０μｍ
上記合計：２４０μｍ
である。
<Example 5>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 50 μm
Polyethylene terephthalate resin layer (4): 190 μm
Total above: 240 μm
is.
＜比較例１＞
化粧シートを構成する積層体の各層の厚さは下記のとおりである。
透明熱可塑性樹脂層（８）：１００μｍ
ポリエチレンテレフタレート樹脂層（４）：１２５μｍ
上記合計：２２５μｍ
である。
ポリエステル樹脂層を、２軸延伸処理を施したポリエチレンテレフタレートとした以外は、実施例１と同様にしてエンボス化粧シートと形成した。
<Comparative Example 1>
The thickness of each layer of the laminate constituting the decorative sheet is as follows.
Transparent thermoplastic resin layer (8): 100 μm
Polyethylene terephthalate resin layer (4): 125 μm
Total above: 225 μm
is.
An embossed decorative sheet was formed in the same manner as in Example 1, except that biaxially stretched polyethylene terephthalate was used as the polyester resin layer.
評価結果を表１に示す。 Table 1 shows the evaluation results.
表１から、見て取れるように、本発明による実施例１～実施例５は全ての評価項目において△評価以上であるが、ポリエチレンテレフタレート樹脂層（４）の厚さが、本発明による厚さの範囲を下回っている比較例１においては、切削性（２）、密着強度において×評価であり、実用性に乏しい結果となった。 As can be seen from Table 1, Examples 1 to 5 according to the present invention are evaluated as Δ or higher in all evaluation items, but the thickness of the polyethylene terephthalate resin layer (4) is within the thickness range according to the present invention. In Comparative Example 1, which is lower than , the machinability (2) and adhesion strength were evaluated as x, and the results were poor in practical use.
このように、本発明によれば、熱可塑性樹脂を基材とする化粧シートにおいて、化粧板にした際の耐摩耗性に優れ、丸ノコあるいはハンドルータを用いた切削に対しての切削加工性に優れる、化粧シートを提供することか可能であることを、検証することができた。 As described above, according to the present invention, the decorative sheet using a thermoplastic resin as a base material has excellent wear resistance when used as a decorative board, and is capable of being cut with a circular saw or a hand router. It was verified that it is possible to provide a decorative sheet that is excellent in
１・・・熱可塑性基材樹脂シート
２・・・絵柄模様層
３・・・第１接着剤層
４・・・ポリエチレンテレフタレート樹脂層
５・・・第２接着剤層
６・・・第１の樹脂層
７・・・第２の樹脂層
８・・・透明熱可塑性樹脂層
９・・・表面保護層
１０・・・エンボス加工による凹凸
２０・・・化粧シート
Claims (3)
化粧シート表面側から、表面保護層、透明熱可塑性樹脂層、第２接着剤層、ポリエチレンテレフタレート樹脂層、第１接着剤層、絵柄模様層、熱可塑性基材樹脂シートがこの順に積層されており、
表面保護層は電離放射線硬化型樹脂を含んでおり、
透明熱可塑性樹脂層は、エンボス加工による凹凸を有しており、
この透明熱可塑性樹脂層の厚さは、５０μｍ以上、１５０μｍ以下の範囲であって、
ポリエチレンテレフタレート樹脂層は、延伸処理をしていないフィルムで形成され、
このポリエチレンテレフタレート樹脂層の厚さは、１５０μｍ以上、３００μｍ以下の範囲であって、
ポリエチレンテレフタレート樹脂層と、透明熱可塑性樹脂層との合計の厚さは、２００μｍ以上、３５０μｍ以下の範囲であることを特徴とする化粧シート。 In the cosmetic sheet,
A surface protective layer, a transparent thermoplastic resin layer, a second adhesive layer, a polyethylene terephthalate resin layer, a first adhesive layer, a picture pattern layer, and a thermoplastic base resin sheet are laminated in this order from the surface side of the decorative sheet. ,
The surface protective layer contains an ionizing radiation curable resin,
The transparent thermoplastic resin layer has unevenness due to embossing,
The thickness of the transparent thermoplastic resin layer is in the range of 50 μm or more and 150 μm or less,
The polyethylene terephthalate resin layer is formed of a film that has not been stretched,
The thickness of the polyethylene terephthalate resin layer is in the range of 150 μm or more and 300 μm or less,
A decorative sheet, wherein the total thickness of the polyethylene terephthalate resin layer and the transparent thermoplastic resin layer is in the range of 200 µm or more and 350 µm or less.
第１の樹脂層は、ポリエチレンテレフタレート樹脂層側に配置されて、透明マレイン酸変性ポリプロピレン樹脂であって、
第２の樹脂層は、表面保護層側に配置されて、透明ポリプロピレン樹脂であることを特徴とする、請求項１に記載の化粧シート。 The transparent thermoplastic resin layer is composed of a first resin layer and a second resin layer,
The first resin layer is arranged on the side of the polyethylene terephthalate resin layer and is a transparent maleic acid-modified polypropylene resin,
2. The decorative sheet according to claim 1, wherein the second resin layer is arranged on the surface protection layer side and is made of a transparent polypropylene resin.