JP7213486B2 - Positive electrode for lead-acid battery and lead-acid battery using the same - Google Patents
Positive electrode for lead-acid battery and lead-acid battery using the same Download PDFInfo
- Publication number
- JP7213486B2 JP7213486B2 JP2019015956A JP2019015956A JP7213486B2 JP 7213486 B2 JP7213486 B2 JP 7213486B2 JP 2019015956 A JP2019015956 A JP 2019015956A JP 2019015956 A JP2019015956 A JP 2019015956A JP 7213486 B2 JP7213486 B2 JP 7213486B2
- Authority
- JP
- Japan
- Prior art keywords
- positive electrode
- lead
- carbon
- acid battery
- mass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、鉛蓄電池用正極及びそれを用いた鉛蓄電池に関する。 The present invention relates to a positive electrode for a lead-acid battery and a lead-acid battery using the same.
鉛蓄電池は、安定した品質と経済性を有し、主に自動車用バッテリーとして用いられ、日本での二次電池生産額の三割近くを占めている。特に、昨今実用化が進められているハイブリッドカー及びアイドリングストップ車には、高性能の鉛蓄電池が不可欠であり、鉛蓄電池の需要は急激に増大している。また、近年、電力貯蔵用のための研究が活発になっている。鉛蓄電池は、開発されてから現在まで長い歴史があるが、未だ電池内部の反応に関して不明な点が残っている。 Lead-acid batteries have stable quality and economic efficiency, are mainly used as automobile batteries, and account for nearly 30% of the production value of secondary batteries in Japan. In particular, high-performance lead-acid batteries are indispensable for hybrid cars and idling-stop cars, which have recently been put to practical use, and the demand for lead-acid batteries is rapidly increasing. Moreover, in recent years, researches for electric power storage have become active. Lead-acid batteries have a long history from their development to the present.
鉛蓄電池は放電し過ぎると、その後の充電が困難になるため、完全に放電する前に充電する必要がある。このため、現時点では、鉛蓄電池は理論容量のわずか10%以下程度しか有効に利用できていない。 If a lead-acid battery is discharged too much, it becomes difficult to charge it afterwards, so it must be charged before it is completely discharged. For this reason, at present, lead-acid batteries can be effectively used only about 10% or less of their theoretical capacity.
上記のような鉛蓄電池は、正極としては、通常、正極集電体としての鉛の上に、正極活物質として酸化鉛の層が形成されており、充放電の際の反応式は以下のように表される。 In the lead-acid battery as described above, the positive electrode is usually formed by forming a layer of lead oxide as a positive electrode active material on lead as a positive current collector, and the reaction formula during charging and discharging is as follows. is represented by
正極：PbO2+ 4H+ + SO4
2- + 2e－ ⇔ PbSO4 + 2H2O 負極：Pb + SO4
2- ⇔ PbSO4 + 2e－
正極活物質として使用されているPbO2は、α型PbO2とβ型PbO2とが存在し、pHの低い領域（酸性領域）においてはβ型PbO2として存在し、pHの高い領域（アルカリ性領域）においてはα型PbO2として存在することが知られている（例えば、非特許文献１参照）。鉛蓄電池の電解液としては、通常硫酸水溶液を使用するため、pHが低い状態で充放電が行われることからβ型PbO2が存在することが期待されるが、実際には、α型PbO2とβ型PbO2とが混在することが知られている。しかしながら、α型PbO2とβ型PbO2とが混在することと、理論容量を十分に有効活用できないこととの関係は未だ不明である。
Positive electrode: PbO 2 + 4H + + SO 4 2- + 2e - ⇔ PbSO 4 + 2H 2 O Negative electrode: Pb + SO 4 2- ⇔ PbSO 4 + 2e -
PbO 2 used as a positive electrode active material exists in α-type PbO 2 and β-type PbO 2 , exists as β-type PbO 2 in the low pH region (acidic region), region) is known to exist as α-type PbO 2 (see, for example, Non-Patent Document 1). Since an aqueous solution of sulfuric acid is normally used as the electrolyte for lead-acid batteries, the charge and discharge are performed at a low pH, so the presence of β-type PbO 2 is expected, but in reality, α-type PbO 2 is expected to exist. and β-type PbO 2 are known to coexist. However, the relationship between the coexistence of α-type PbO 2 and β-type PbO 2 and the inability to fully effectively utilize the theoretical capacity is still unclear.
上記のように、鉛蓄電池においては、理論容量を十分に有効活用できているとは言い難いため、十分に放電した後にも充電することができれば、有効活用できる容量を増大させることが期待される。また、鉛蓄電池を繰り返し充放電することを考慮した場合には、正極集電体と正極活物質との接着性にも優れた構造を採用することが求められる。このような観点から、本発明は、十分に放電し長期間停止した後でも再度充電することができ、且つ、正極集電体と正極活物質との接着性に優れるため耐久性が高い鉛蓄電池用正極を提供することを目的とする。 As described above, it is difficult to say that the theoretical capacity of a lead-acid battery is fully utilized effectively, so if it is possible to charge the battery after it has been fully discharged, it is expected that the effectively utilized capacity will be increased. . In addition, when it is considered that the lead-acid battery is repeatedly charged and discharged, it is required to adopt a structure having excellent adhesiveness between the positive electrode current collector and the positive electrode active material. From this point of view, the present invention provides a lead-acid battery that can be recharged even after being sufficiently discharged and stopped for a long period of time, and has high durability due to excellent adhesion between the positive electrode current collector and the positive electrode active material. The purpose is to provide a positive electrode for
本発明者らは、鋭意研究を積み重ねた結果、鉛蓄電池の開回路時（不使用時）において、正極活物質であるPbO2（特にβ型PbO2）と、正極集電体である鉛との間で局部電池反応が起こることを見出した。具体的には、β型PbO2が正極、鉛が負極となり、電池反応が起こることによってα型PbO2が生成し、鉛蓄電池の性能に悪影響を及ぼすことを見出した。本発明者らは、正極集電体と正極活物質層との間に、正極集電体とは異なる層として、導電性炭素材料及び高分子化合物を含有する炭素含有層を介在させることで、開回路時の局部電池反応が抑制されるため、十分に放電し長期間停止した後でも再度充電することができ、また、正極集電体と正極活物質との接着性にも優れるため耐久性が高いことを見出した。本発明者らは、さらに研究を重ね、本発明を完成した。すなわち、本発明は、以下の構成を包含する。
項１．正極集電体、炭素含有層及び正極活物質層がこの順で配置されており、
前記炭素含有層は、導電性炭素材料及び高分子化合物を含有し、
前記正極活物質層は、二酸化鉛を含有する、鉛蓄電池用正極。
項２．前記導電性炭素材料は、黒鉛及びカーボンブラックを含有する、項１に記載の鉛蓄電池用正極。
項３．前記炭素含有層は、総量を100質量%として、カーボンブラックを5～20質量%含有する、項１又は２に記載の鉛蓄電池用正極。
項４．前記炭素含有層は、総量を100質量%として、黒鉛を40～75質量%含有する、項１～３のいずれか1項に記載の鉛蓄電池用正極。
項５．前記炭素含有層は、総量を100質量%として、高分子化合物を10～40質量%含有する、項１～４のいずれか1項に記載の鉛蓄電池用正極。
項６．前記高分子化合物がゴム系樹脂である、項１～５のいずれか1項に記載の鉛蓄電池用正極。
項７．項１～６のいずれか1項に記載の鉛蓄電池用正極を備える鉛蓄電池。
As a result of extensive research, the present inventors have found that PbO 2 (especially β-type PbO 2 ), which is a positive electrode active material, and lead, which is a positive electrode current collector, when a lead-acid battery is open-circuited (when not in use). It was found that a local cell reaction occurs between Specifically, β-type PbO 2 becomes the positive electrode and lead becomes the negative electrode, and a battery reaction occurs to generate α-type PbO 2 , which adversely affects the performance of the lead-acid battery. The present inventors interposed a carbon-containing layer containing a conductive carbon material and a polymer compound as a layer different from the positive electrode current collector between the positive electrode current collector and the positive electrode active material layer, Since the local battery reaction at the time of open circuit is suppressed, it can be fully discharged and recharged even after being stopped for a long time.In addition, the adhesion between the positive electrode current collector and the positive electrode active material is excellent, so it is durable. found to be high. The inventors of the present invention have completed the present invention through further research. That is, the present invention includes the following configurations.
The carbon-containing layer contains a conductive carbon material and a polymer compound,
The positive electrode for a lead-acid battery, wherein the positive electrode active material layer contains lead dioxide.
Section 4. 4. The positive electrode for a lead-acid battery according to any one of
Item 5. Item 5. The positive electrode for a lead-acid battery according to any one of
Item 6. Item 6. The positive electrode for a lead-acid battery according to any one of
Item 7. A lead-acid battery comprising the positive electrode for a lead-acid battery according to any one of
本発明によれば、正極集電体と正極活物質層との間に、正極集電体とは異なる層として、導電性炭素材料及び高分子化合物を含有する炭素含有層を介在させることで、開回路時の局部電池反応が抑制されるため、十分に放電し長期間停止した後でも再度充電することができ、また、正極集電体と正極活物質との接着性にも優れるため耐久性が高い。このような構成を採用しているため、正極活物質層の正極集電体として通常使用される鉛を使用しながら十分に放電し長期間停止した後でも再度充電することも可能である。 According to the present invention, by interposing a carbon-containing layer containing a conductive carbon material and a polymer compound as a layer different from the positive electrode current collector between the positive electrode current collector and the positive electrode active material layer, Since the local battery reaction at the time of open circuit is suppressed, it can be fully discharged and recharged even after being stopped for a long time.In addition, the adhesion between the positive electrode current collector and the positive electrode active material is excellent, so it is durable. is high. Since such a structure is adopted, it is possible to sufficiently discharge the battery while using lead, which is normally used as the positive electrode current collector of the positive electrode active material layer, and to recharge the battery even after the battery has been stopped for a long period of time.
１．鉛蓄電池用正極
本発明の鉛蓄電池用正極は、正極集電体、炭素含有層及び正極活物質層がこの順で配置されており、前記炭素含有層は、導電性炭素材料及び高分子化合物を含有し、前記正極活物質層は、二酸化鉛を含有する。
1. Positive electrode for lead-acid battery In the positive electrode for lead-acid battery of the present invention, a positive electrode current collector, a carbon-containing layer and a positive electrode active material layer are arranged in this order, and the carbon-containing layer comprises a conductive carbon material and a polymer compound. and the positive electrode active material layer contains lead dioxide.
（１－１）正極集電体
正極集電体としては、特に制限はなく、種々様々なものを使用することができる。ただし、鉛蓄電池の電解液である硫酸に対して不活性な材料を用いることが好ましい。具体的には、鉛、金、パラジウム、白金等を使用することができる。硫酸に対する耐食性を考慮し、鉛と、スズ、銀等の少なくとも1種との合金を採用することもできる。また、カーボンシートを正極集電体として使用することも可能である。
(1-1) Positive Electrode Current Collector The positive electrode current collector is not particularly limited, and various materials can be used. However, it is preferable to use a material that is inert to sulfuric acid, which is the electrolytic solution of lead-acid batteries. Specifically, lead, gold, palladium, platinum and the like can be used. Considering corrosion resistance to sulfuric acid, an alloy of lead and at least one of tin, silver, and the like may be used. It is also possible to use a carbon sheet as the positive electrode current collector.
このような正極集電体の厚みは、後述する正極活物質層の支持体として機能させる観点から、0.1～1.5mmが好ましく、0.2～1.0mmがより好ましい。 The thickness of such a positive electrode current collector is preferably 0.1 to 1.5 mm, more preferably 0.2 to 1.0 mm, from the viewpoint of functioning as a support for the positive electrode active material layer described later.
上記した正極集電体は、単独で使用することもできるし、他の基材の上に積層させることもできる。特に、正極集電体の厚みが上記した範囲より薄い場合であっても、他の基材の上に積層させて使用することも可能である。例えば、正極集電体の厚みが薄く（1μm～0.1mm程度）単独で後述する正極活物質層の支持体として自立しにくいような場合には、他の基材の上に積層させることが好ましい。このような他の基材としては、例えば、アルミナ等のセラミックス；ポリエーテルサルフォン樹脂等のポリマー等が挙げられる。このような他の基材の厚みは、0.1mm～10mm程度が好ましい。 The positive electrode current collector described above can be used alone, or can be laminated on another base material. In particular, even when the thickness of the positive electrode current collector is thinner than the above range, it can be used by being laminated on another base material. For example, when the thickness of the positive electrode current collector is thin (about 1 μm to 0.1 mm) and it is difficult for it to stand alone as a support for the positive electrode active material layer described later, it is preferable to laminate it on another base material. . Examples of such other base materials include ceramics such as alumina; polymers such as polyethersulfone resins. The thickness of such other base material is preferably about 0.1 mm to 10 mm.
（１－２）炭素含有層
本発明において、炭素含有層は、導電性炭素材料及び高分子化合物を含有する。
(1-2) Carbon-Containing Layer In the present invention, the carbon-containing layer contains a conductive carbon material and a polymer compound.
導電性炭素材料は、電解液である硫酸に対して不活性な物質であり、また、上記した正極集電体や、後述する正極活物質である二酸化鉛との間での局部電池反応も起らない。このため、炭素含有層中に導電性炭素材料を含ませることにより、開回路時の局部電池反応を抑制することができ、十分に放電し長期間停止した後でも再度充電することができる。このような導電性炭素材料としては、特に制限はなく、チャンネルブラック、ファーネスブラック、ケッチェンブラック、アセチレンブラック、ランプブラック等のカーボンブラック；天然黒鉛、人造黒鉛、膨張黒鉛等の黒鉛（膨張黒鉛シート、等方性黒鉛等）；活性炭；アモルファスカーボン等を好ましく採用できる。これらの導電性炭素材料は単独で用いることもでき、2種以上を組合せて用いることもできる。なかでも、黒鉛（特に燐片状黒鉛）とカーボンブラックとを併用して使用した場合には、黒鉛同士の間に微小なカーボンブラック粒子が位置することで、導電経路を三次元的に無数に形成することができ、特に導電性を向上させることが可能である。 The conductive carbon material is a substance that is inactive with respect to the sulfuric acid that is the electrolytic solution, and also causes a local battery reaction between the positive electrode current collector described above and lead dioxide that is the positive electrode active material described later. not. Therefore, by including a conductive carbon material in the carbon-containing layer, it is possible to suppress the local battery reaction at the time of open circuit, and it is possible to recharge the battery even after it has been fully discharged and stopped for a long period of time. Such conductive carbon material is not particularly limited, carbon black such as channel black, furnace black, ketjen black, acetylene black, lamp black; graphite such as natural graphite, artificial graphite, expanded graphite (expanded graphite sheet , isotropic graphite, etc.); activated carbon; amorphous carbon, etc. can be preferably employed. These conductive carbon materials can be used alone, or two or more of them can be used in combination. In particular, when graphite (particularly flaky graphite) and carbon black are used in combination, microscopic carbon black particles are positioned between the graphite particles to create an infinite number of three-dimensional conductive paths. It can be formed, and in particular it is possible to improve the conductivity.
導電性炭素材料の含有量は特に制限されない。開回路時の局部電池反応をより抑制しつつ導電性をより向上させる観点から、炭素含有層の総量を100質量%とした時の導電性炭素材料の含有量は、45～90質量%が好ましく、50～85質量%がより好ましい。導電性炭素材料を複数含有させる場合は、その合計量が上記範囲内になるように調整することが好ましい。なお、導電性炭素材料としてカーボンブラックを含有する場合、開回路時の局部電池反応をより抑制しつつ導電性をより向上させる観点から、その含有量は、炭素含有層の総量を100質量%として、5～20質量%が好ましく、7～15質量%がより好ましい。また、導電性炭素材料として黒鉛を含有する場合、開回路時の局部電池反応をより抑制しつつ導電性をより向上させる観点から、その含有量は、炭素含有層の総量を100質量%として、40～75質量%が好ましく、45～70質量%がより好ましい。 The content of the conductive carbon material is not particularly limited. From the viewpoint of further improving the electrical conductivity while suppressing the local battery reaction at the time of open circuit, the content of the conductive carbon material is preferably 45 to 90% by mass when the total amount of the carbon-containing layer is 100% by mass. , 50 to 85% by mass is more preferred. When a plurality of conductive carbon materials are contained, it is preferable to adjust the total amount within the above range. When carbon black is contained as the conductive carbon material, the content thereof is based on the total amount of the carbon-containing layer being 100% by mass, from the viewpoint of further improving the conductivity while suppressing the local battery reaction at the time of open circuit. , preferably 5 to 20% by mass, more preferably 7 to 15% by mass. In addition, when graphite is contained as the conductive carbon material, from the viewpoint of further improving conductivity while suppressing local battery reaction at the time of open circuit, the content is set to 100% by mass based on the total amount of the carbon-containing layer. 40 to 75% by mass is preferred, and 45 to 70% by mass is more preferred.
高分子化合物としては、特に制限されないが、正極活物質であるPbO2や電解液である硫酸に対して不活性な高分子化合物を使用することが好ましい。高分子化合物は、元来バインダーとして機能し、正極集電体と正極活物質層との間の接着性を向上させることを目的として含ませるが、正極活物質であるPbO2や電解液である硫酸に対して不活性な高分子化合物を使用することで、硫酸非湿潤性でPbO2に不活性な炭素含有層となり、鉛蓄電池の劣化をさらに抑制することも可能である。このような高分子化合物としては、例えば、ゴム系樹脂、ポリオレフィン樹脂、ポリエチレンテレフタレート樹脂（PET樹脂）、アクリロニトリルブタジエンスチレン樹脂（ABS樹脂）、ポリフッ化ビニリデン樹脂（PVDF樹脂）、ポリテトラフッ化エチレン樹脂（PTFE樹脂）、ポリエーテルサルフォン樹脂（PES樹脂）、導電性高分子（特に導電性有機高分子）等が挙げられる。ゴム系樹脂としてはジエン系ゴムであるスチレンブタジエン樹脂、非ジエン系ゴムであるエチレンプロピレンジエン樹脂等が挙げられる。ポリオレフィン樹脂としては、例えば、ポリエチレン樹脂、ポリプロピレン樹脂等が挙げられ、導電性高分子としては特に制限はなく、ポリチオフェン、ポリアセチレン、ポリアニリン、ポリピロール、ポリチアジル等を好ましく採用することができる。これらの物質は、1種単独で用いることもでき、2種以上組合せて用いることもできる。なかでも、正極集電体と正極活物質（PbO2）との間の接着性をさらに向上させることができる観点から、ゴム系樹脂等が好ましく、ゴム系樹脂であるスチレンブタジエン樹脂及びエチレンプロピレンジエン樹脂がより好ましい。スチレンブタジエン樹脂、エチレンプロピレンジエン樹脂等は、ゴム弾性を有するため正極集電体と正極活物質（PbO2）との間の接着性を特に向上させることができる。また、炭素含有層全体に導電性炭素材料が均一に分散しやすい。このため、液体（特に電解質である硫酸）の侵入を抑止する効果をより高め、鉛蓄電池の劣化をより抑制し、深く充放電した際の電位幅をより大きくすることもでき、開回路で静置した後の充放電もより良好に行うことができる。さらに導電性炭素材料が均一に分散しやすいために炭素含有層内での高い導電性を確保できる。 Although the polymer compound is not particularly limited, it is preferable to use a polymer compound that is inert to PbO 2 as the positive electrode active material and sulfuric acid as the electrolytic solution. The polymer compound originally functions as a binder and is included for the purpose of improving the adhesiveness between the positive electrode current collector and the positive electrode active material layer. By using a polymer compound inert to sulfuric acid, it becomes a carbon-containing layer that is non-wetting with sulfuric acid and inert to PbO 2 , and it is possible to further suppress deterioration of the lead-acid battery. Examples of such polymer compounds include rubber resins, polyolefin resins, polyethylene terephthalate resins (PET resins), acrylonitrile butadiene styrene resins (ABS resins), polyvinylidene fluoride resins (PVDF resins), polytetrafluoroethylene resins (PTFE resin), polyether sulfone resin (PES resin), conductive polymer (especially conductive organic polymer), and the like. Examples of rubber-based resins include styrene-butadiene resin, which is a diene-based rubber, and ethylene-propylene-diene resin, which is a non-diene-based rubber. Polyolefin resins include, for example, polyethylene resins and polypropylene resins, and the conductive polymer is not particularly limited, and polythiophene, polyacetylene, polyaniline, polypyrrole, polythiazyl, and the like can be preferably used. These substances can be used singly or in combination of two or more. Among them, from the viewpoint of further improving the adhesiveness between the positive electrode current collector and the positive electrode active material (PbO 2 ), rubber-based resins are preferable, and rubber-based resins such as styrene-butadiene resin and ethylene propylene diene Resin is more preferred. Styrene-butadiene resin, ethylene-propylene-diene resin, and the like have rubber elasticity, and can particularly improve the adhesiveness between the positive electrode current collector and the positive electrode active material (PbO 2 ). Also, the conductive carbon material tends to be uniformly dispersed throughout the carbon-containing layer. For this reason, the effect of suppressing the intrusion of liquids (especially sulfuric acid, which is an electrolyte) is further enhanced, deterioration of the lead-acid battery is further suppressed, the potential range during deep charging and discharging can be increased, and the battery is static in an open circuit. Charging and discharging after placing can also be performed more satisfactorily. Furthermore, since the conductive carbon material is easily dispersed uniformly, high conductivity can be ensured in the carbon-containing layer.
高分子化合物の含有量は特に制限されない。正極集電体と正極活物質層との間の接着性をより向上させる観点から、その含有量は、炭素含有層の総量を100質量%として、10～40質量%が好ましく、15～35質量%がより好ましい。高分子化合物を複数含有させる場合は、その合計量が上記範囲内になるように調整することが好ましい。 The content of the polymer compound is not particularly limited. From the viewpoint of further improving the adhesion between the positive electrode current collector and the positive electrode active material layer, the content thereof is preferably 10 to 40% by mass, more preferably 15 to 35% by mass, based on the total amount of the carbon-containing layer being 100% by mass. % is more preferred. When a plurality of polymer compounds are contained, it is preferable to adjust the total amount within the above range.
このような炭素含有層の厚みは、特に制限されず、局部電池反応による正極の劣化をより抑制して耐久性と容量をより向上させつつ、正極集電体と正極活物質（PbO2）との間の接着性をより向上させる観点から、5nm～10mmが好ましく、10nm～1mmがより好ましい。 The thickness of such a carbon - containing layer is not particularly limited. 5 nm to 10 mm is preferable, and 10 nm to 1 mm is more preferable, from the viewpoint of further improving the adhesion between the layers.
炭素含有層を形成する方法は特に制限されない。例えば、塗布法等を採用することができる。塗布法を採用する場合は、例えば、アプリケーターロール等のローラーコーティング；スクリーンコーティング；ドクターブレード方式；スピンコーティング；バーコータ等の手段を用いて塗布することができる。具体的には、導電性炭素材料、高分子化合物及び有機溶媒を含有する塗料を、例えば正極集電体の上に塗布し、常法で乾燥させることにより得ることができる。この際使用できる有機溶媒は特に制限されず、一般的な有機溶媒を幅広く使用することができる。なお、高分子化合物としてゴム系樹脂を使用する場合には溶解性の観点からキシレン、トルエン等が好ましく、キシレンがより好ましい。 A method for forming the carbon-containing layer is not particularly limited. For example, a coating method or the like can be adopted. When a coating method is employed, it can be coated using means such as roller coating such as applicator roll; screen coating; doctor blade method; spin coating; and bar coater. Specifically, it can be obtained by applying a paint containing a conductive carbon material, a polymer compound and an organic solvent, for example, onto a positive electrode current collector and drying it by a conventional method. The organic solvent that can be used at this time is not particularly limited, and a wide range of common organic solvents can be used. When a rubber-based resin is used as the polymer compound, xylene, toluene, and the like are preferable from the viewpoint of solubility, and xylene is more preferable.
（１－３）正極活物質層
本発明の鉛蓄電池用正極は、前記炭素含有層の上に、二酸化鉛を含有する正極活物質層が形成されている。上記したように、炭素含有層中に含まれる炭素質材料は、前記正極活物質層との間の局部電池反応（特に開回路時の局部電池反応）を抑制することができるため、開回路時に局部電池反応によりα型PbO2が生成することを抑制することができ、十分に放電し長期間停止した（開回路とした）後でも再度充放電することができる。また、炭素含有層中に含まれる高分子化合物の作用により、正極集電体と正極活物質層との間の接着性を向上させることもできる。
(1-3) Positive Electrode Active Material Layer In the positive electrode for a lead-acid battery of the present invention, a positive electrode active material layer containing lead dioxide is formed on the carbon-containing layer. As described above, the carbonaceous material contained in the carbon-containing layer can suppress the local battery reaction (especially the local battery reaction at the time of open circuit) with the positive electrode active material layer. It can suppress the generation of α-PbO 2 due to local cell reaction, and can be charged and discharged again even after being fully discharged and stopped for a long time (open circuit). Moreover, the action of the polymer compound contained in the carbon-containing layer can improve the adhesiveness between the positive electrode current collector and the positive electrode active material layer.
本発明の鉛蓄電池において、正極活物質層中に含まれる正極活物質は、従来から使用されている二酸化鉛（PbO2）を採用することが好ましい。正極活物質層中の正極活物質の含有量は特に制限されず、従来から、鉛蓄電池の正極に適用される程度とすることができ、正極活物質層の総量を100質量%として、50～95質量%が好ましく、70～90質量%がより好ましい。 In the lead-acid battery of the present invention, the positive electrode active material contained in the positive electrode active material layer is preferably lead dioxide (PbO 2 ), which has been conventionally used. The content of the positive electrode active material in the positive electrode active material layer is not particularly limited, and can be conventionally applied to the positive electrode of a lead-acid battery. 95% by mass is preferred, and 70-90% by mass is more preferred.
本発明において、正極活物質層には、導電助剤を含ませることもできる。導電助剤としては、電子伝導性材料であり、且つ、局部電池反応が起こりにくい材料（二酸化鉛及び硫酸に対し電気化学的に不活性な物質）を採用することが好ましい。具体的には、天然黒鉛、人造黒鉛等の黒鉛（等方性黒鉛等）；カーボンブラック；アセチレンブラック；ケッチェンブラック；カーボンウイスカー；炭素繊維；気相成長炭素等の導電性材料を1種又はそれらの混合物として含ませることができる。正極活物質層中の導電助剤の含有量は特に制限されず、従来から、鉛蓄電池の正極に適用される程度とすることができ、正極活物質層の総量を100質量%として、5～35質量%が好ましく、10～20質量%がより好ましい。 In the present invention, the positive electrode active material layer can also contain a conductive aid. As the conductive aid, it is preferable to use a material that is electronically conductive and that is unlikely to cause a local cell reaction (substance that is electrochemically inactive with respect to lead dioxide and sulfuric acid). Specifically, graphite such as natural graphite and artificial graphite (isotropic graphite, etc.); carbon black; acetylene black; Ketjen black; carbon whisker; It can be included as a mixture thereof. The content of the conductive agent in the positive electrode active material layer is not particularly limited, and can be conventionally applied to the positive electrode of a lead-acid battery. 35% by mass is preferred, and 10 to 20% by mass is more preferred.
他にも、正極活物質層には、上記成分の他に、結着剤、増粘剤等を含ませることもできる。 In addition to the above components, the positive electrode active material layer can also contain a binder, a thickener, and the like.
結着剤としては、通常、ポリテトラフルオロエチレン（PTFE）、ポリフッ化ビニリデン、ポリエチレン、ポリプロピレン等の熱可塑性樹脂；エチレン－プロピレン－ジエンターポリマー（EPDM）、スルホン化EPDM、スチレンブタジエンゴム（SBR）、フッ素ゴム等のゴム弾性を有するポリマーを1種又は2種以上の混合物として用いることができる。 Binders are usually thermoplastic resins such as polytetrafluoroethylene (PTFE), polyvinylidene fluoride, polyethylene, polypropylene; ethylene-propylene-diene terpolymer (EPDM), sulfonated EPDM, styrene-butadiene rubber (SBR) , a polymer having rubber elasticity such as fluororubber can be used singly or as a mixture of two or more.
増粘剤としては、通常、カルボキシメチルセルロース、メチルセルロース等の多糖類等を1種又は2種以上の混合物として用いることができる。 As the thickening agent, polysaccharides such as carboxymethyl cellulose and methyl cellulose can usually be used singly or as a mixture of two or more.
正極活物質層中の結着剤及び増粘剤の含有量は特に制限されず、従来から、鉛蓄電池の正極に適用される程度とすることができ、正極活物質層の総量を100質量%として、結着剤及び増粘剤の合計量として2～15質量%が好ましく、3～10質量%がより好ましい。 The content of the binder and thickener in the positive electrode active material layer is not particularly limited, and can be conventionally applied to the positive electrode of a lead-acid battery, and the total amount of the positive electrode active material layer is 100% by mass. As such, the total amount of the binder and thickener is preferably 2 to 15% by mass, more preferably 3 to 10% by mass.
これら各成分の混合方法は、物理的な混合であり、均一混合が好ましい。そのため、V型混合機、S型混合機、擂かい機、ボールミル、遊星ボールミル等のような粉体混合機を乾式又は湿式で使用することが可能である。 The method for mixing these components is physical mixing, and uniform mixing is preferred. It is therefore possible to use dry or wet powder mixers such as V-blenders, S-blenders, grinders, ball mills, planetary ball mills and the like.
本発明において、正極活物質層を形成する方法は特に制限されない。例えば、正極活物質等の各種成分を水に混合させて、正極活物質層形成用ペースト組成物を作製し、その後、該ペースト組成物を炭素含有層に含浸又は塗布し、乾燥する方法等が挙げられる。 In the present invention, the method for forming the positive electrode active material layer is not particularly limited. For example, various components such as a positive electrode active material are mixed with water to prepare a paste composition for forming a positive electrode active material layer, and then the carbon-containing layer is impregnated or coated with the paste composition, followed by drying. mentioned.
塗布方法については、例えば、アプリケーターロール等のローラーコーティング；スクリーンコーティング；ドクターブレード方式；スピンコーティング；バーコータ等の手段を用いて塗布することができる。また、乾燥条件も特に制限はなく、通常鉛蓄電池において採用されている範囲で採用することができる。 As for the coating method, for example, roller coating such as applicator roll; screen coating; doctor blade method; spin coating; Also, the drying conditions are not particularly limited, and can be employed within the range normally employed in lead-acid batteries.
２．鉛蓄電池
本発明の鉛蓄電池は、本発明の鉛蓄電池用正極を備える。
2. Lead-acid battery The lead-acid battery of the present invention comprises the lead-acid battery positive electrode of the present invention.
正極以外の部材としては、鉛蓄電池用負極、鉛蓄電池用電解液、鉛蓄電池用セパレータ等が挙げられる。これらは、適宜製造したものでもよく、市販品でもよく、公知の鉛蓄電池における部材、材料を採用できる。 Examples of members other than the positive electrode include negative electrodes for lead-acid batteries, electrolytic solutions for lead-acid batteries, separators for lead-acid batteries, and the like. These may be manufactured appropriately or may be commercially available products, and members and materials used in known lead-acid batteries may be employed.
以下に実施例及び比較例を挙げて、本発明をより詳細に説明する。なお、本発明は、以下の実施例に限定されるものではない。 The present invention will be described in more detail below with reference to examples and comparative examples. In addition, the present invention is not limited to the following examples.
実施例1
正極集電体である鉛（（株）ニラコ製の鉛99.9%）は、プレート状で厚さ0.3mmに仕上げ準備した。
Example 1
Lead (99.9% lead manufactured by The Nilaco Corporation), which is a positive electrode current collector, was plate-shaped and prepared to have a thickness of 0.3 mm.
炭素含有層を形成するための原料として、キシレン81質量%、（燐片状）天然黒鉛9～13質量%、ゴム系樹脂（スチレンブタジエン樹脂）5～8質量%、カーボンブラック2.09質量%を含む導電性塗料を使用した。この導電性塗料を正極集電体である鉛上に、乾燥後の厚みが0.05mmとなるように塗布した。 81% by mass of xylene, 9-13% by mass of (scaly) natural graphite, 5-8% by mass of rubber-based resin (styrene-butadiene resin), and 2.09% by mass of carbon black as raw materials for forming the carbon-containing layer. Conductive paint was used. This conductive paint was applied onto lead as a positive electrode current collector so that the thickness after drying was 0.05 mm.
活物質は二酸化鉛とし、二酸化鉛、カーボンブラック及びポリテトラフルオロエチレン（PTFE）を混合した。具体的には、β型PbO2（Johnson Matthey製の二酸化鉛）に、カーボンブラック及びPTFEを、β型PbO2: カーボンブラック: PTFEが80: 15: 5（質量%）の割合でそれぞれ加え、よく混合し、正極活物質層形成用ペースト組成物を作製した。この正極活物質層形成用ペースト組成物を炭素含有層上に、炭素含有層を形成するための原料に含まれる溶媒が蒸発する前に、正極活物質層の厚みが0.15mmとなるように塗布した。その後、炭素含有層を形成するための原料に含まれる溶媒を乾燥させて除去することで正極活物質層を炭素含有層上に形成した。このようにして、実施例1の鉛蓄電池用正極を得た。なお、炭素含有層の組成は表１の通りである。 Lead dioxide was used as the active material, and lead dioxide, carbon black and polytetrafluoroethylene (PTFE) were mixed. Specifically, carbon black and PTFE were added to β-type PbO 2 (lead dioxide manufactured by Johnson Matthey) in a ratio of β-type PbO 2 : carbon black: PTFE of 80:15:5 (% by mass), respectively. They were well mixed to prepare a paste composition for forming a positive electrode active material layer. This paste composition for forming a positive electrode active material layer is applied onto the carbon-containing layer so that the thickness of the positive electrode active material layer becomes 0.15 mm before the solvent contained in the raw material for forming the carbon-containing layer evaporates. bottom. After that, the solvent contained in the raw material for forming the carbon-containing layer was dried and removed to form the positive electrode active material layer on the carbon-containing layer. Thus, a positive electrode for a lead-acid battery of Example 1 was obtained. The composition of the carbon-containing layer is shown in Table 1.
このようにして得た実施例1の鉛蓄電池用正極の炭素含有層では燐片状黒鉛がきれいに配向するため、導電性が向上し、且つ、深く放電後に開回路で静置した後にも再度充放電できる。 In the carbon-containing layer of the positive electrode for a lead-acid battery of Example 1 obtained in this way, the flake-like graphite is oriented neatly, so that the conductivity is improved, and the battery is recharged even after being left standing in an open circuit after deep discharge. Discharge is possible.
実施例２
炭素含有層を形成するための原料として、キシレン81質量%、（燐片状）天然黒鉛9～13質量%、ゴム系樹脂（スチレンブタジエン樹脂）3質量%、カーボンブラック2.09質量%を含む導電性塗料を使用したこと、およびこの導電性塗料を正極集電体である鉛上に、乾燥後の厚みが0.01mmとなるように塗布した以外は実施例１と同様にして実施例２の鉛蓄電池用正極を得た。なお、炭素含有層の組成は表１の通りである。
Example 2
Conductive material containing 81% by mass of xylene, 9-13% by mass of (scaly) natural graphite, 3% by mass of rubber-based resin (styrene-butadiene resin), and 2.09% by mass of carbon black as raw materials for forming the carbon-containing layer. A lead-acid battery of Example 2 was prepared in the same manner as in Example 1, except that the paint was used, and the conductive paint was applied onto the lead, which is the positive electrode current collector, so that the thickness after drying was 0.01 mm. obtained a positive electrode for The composition of the carbon-containing layer is shown in Table 1.
このようにして得た実施例2の鉛蓄電池用正極の炭素含有層では燐片状黒鉛がきれいに配向するため、導電性が向上し、且つ、深く放電後に開回路で静置した後にも再度充放電できる。 In the carbon-containing layer of the positive electrode for a lead-acid battery of Example 2 obtained in this way, the flake-like graphite is oriented neatly, so that the conductivity is improved, and the battery is charged again even after being left standing in an open circuit after deep discharge. Discharge is possible.
比較例1
炭素含有層を形成しなかったこと以外は実施例1と同様に、比較例1の鉛蓄電池用正極を得た。
Comparative example 1
A positive electrode for a lead-acid battery of Comparative Example 1 was obtained in the same manner as in Example 1, except that no carbon-containing layer was formed.
製造例1：評価試験用セル
以下の評価試験用セルとしては、二極式ガラスセルを採用した。正極としては上記した実施例1又は2の正極をそれぞれ用い、負極としては鉛プレート（（株）ニラコ製の鉛99.9%；厚み0.3mm）を用い、電解液としては35質量%硫酸水溶液を用い、図１に示すセルを作製した。
Production Example 1 Evaluation Test Cell A bipolar glass cell was used as the evaluation test cell below. As the positive electrode, the positive electrode of Example 1 or 2 was used, and as the negative electrode, a lead plate (99.9% lead manufactured by Nilaco Co., Ltd.; thickness: 0.3 mm) was used. , the cell shown in FIG. 1 was produced.
試験例2：充放電試験
実施例1、実施例2及び比較例1の正極を用いた評価試験用セルについて、以下の条件で充放電を行った。なお、充放電試験には、北斗電工（株）製の充放電装置（HJ1001SD8）を用いた。
Test Example 2: Charging and Discharging Test Evaluation test cells using the positive electrodes of Examples 1, 2 and Comparative Example 1 were charged and discharged under the following conditions. For the charge/discharge test, a charge/discharge device (HJ1001SD8) manufactured by Hokuto Denko Co., Ltd. was used.
比較例1の正極を用いた充放電試験には、まず、電池反応を安定化させるため、9mA/gで放電30分間及び18mA/gで充電20分間を1サイクルとして約12時間（14サイクル）充放電を繰り返し、次いで、最終サイクルの放電が終わった後2時間はそのまま静置し、次いで0Vまで9mA/gで深く放電した。次に、上記のように深く放電した後に、開回路の状態で48時間静置した後に、18mA/gで1時間充電し、再度充放電が可能かどうか評価した。充放電曲線を図２に示す。最後に電位が急激に上昇しているのは、充電が出来なかったことを示している。この結果、比較例1の正極を用いた場合には、α型PbO2が生成されているからか、深く放電し開回路で静置した後には再度充放電を行うことはできなかった。 In the charge-discharge test using the positive electrode of Comparative Example 1, first, in order to stabilize the battery reaction, one cycle was discharged at 9 mA / g for 30 minutes and charged at 18 mA / g for 20 minutes for about 12 hours (14 cycles). The charge and discharge were repeated, then left to stand for 2 hours after the final cycle of discharge was completed, and then deeply discharged to 0 V at 9 mA/g. Next, after being deeply discharged as described above, the battery was allowed to stand in an open circuit state for 48 hours, and then charged at 18 mA/g for 1 hour to evaluate whether charging and discharging were possible again. A charge-discharge curve is shown in FIG. The sudden rise in the potential at the end indicates that charging was not possible. As a result, when the positive electrode of Comparative Example 1 was used, perhaps because α-type PbO 2 was generated, it was not possible to perform charging and discharging again after it was deeply discharged and allowed to stand in an open circuit.
一方、実施例1の正極を用いたこと以外は上記図２の試験と同様に試験を行った（0Vまで深く放電し開回路で48時間静置した後に充放電）場合の充放電試験を図３～４に示す。図４は、0Vまで深く放電し開回路で48時間静置した後に充放電を行う際（65～72時間後）における再充放電チャートの詳細を示す。この結果、実施例1の正極を用いた場合には、深く放電し開回路で静置した後にも、1サイクルあたり約5時間の充放電サイクルで再度充放電を行うことが可能であった。また、試験後の実施例1の正極を目視で確認したところ、正極集電体と正極活物質との間の剥離は確認できないことから、接着性に優れ、耐久性も高いことが理解できる。 On the other hand, except for using the positive electrode of Example 1, the test was performed in the same manner as the test in FIG. 3-4. FIG. 4 shows the details of the recharge/discharge chart when charging/discharging after deep discharging to 0V and standing in an open circuit for 48 hours (after 65 to 72 hours). As a result, when the positive electrode of Example 1 was used, even after being deeply discharged and allowed to stand in an open circuit, it was possible to charge and discharge again in a charge and discharge cycle of about 5 hours per cycle. In addition, when the positive electrode of Example 1 after the test was visually checked, no separation between the positive electrode current collector and the positive electrode active material was observed.
次に実施例2の正極を用いたこと以外は上記図２の試験と同様に試験を行った（0Vまで深く放電し開回路で48時間静置した後に充放電）場合の充放電試験を図５～６に示す。図６は、0Vまで深く放電し開回路で48時間静置した後に充放電を行う際（63～67時間後）における再充放電チャートの詳細を示す。この結果、実施例2の正極を用いた場合には、深く放電し開回路で静置した後にも、1サイクルあたり約3時間の充放電サイクルで再度充放電を行うことが可能であった。また、試験後の実施例2の正極を目視で確認したところ、正極集電体と正極活物質との間の剥離は確認できないことから、接着性に優れ、耐久性も高いことが理解できる。 Next, the test was conducted in the same manner as the test in FIG. 2 above except that the positive electrode of Example 2 was used (deeply discharged to 0 V, left to stand in an open circuit for 48 hours, and then charged and discharged). 5-6. FIG. 6 shows the details of the recharge/discharge chart when charging/discharging after deep discharging to 0V and standing in an open circuit for 48 hours (after 63-67 hours). As a result, when the positive electrode of Example 2 was used, even after being deeply discharged and allowed to stand in an open circuit, it was possible to charge and discharge again in a charge and discharge cycle of about 3 hours per cycle. In addition, when the positive electrode of Example 2 after the test was visually checked, no separation between the positive electrode current collector and the positive electrode active material was observed.
Claims (6)
前記炭素含有層は、導電性炭素材料及び高分子化合物を含有し、
前記導電性炭素材料は、黒鉛及び／又はカーボンブラックを含有し、
前記高分子化合物は、ゴム系樹脂であり、且つ、
前記正極活物質層は、二酸化鉛を含有する、鉛蓄電池用正極。 The positive electrode current collector, the carbon-containing layer and the positive electrode active material layer are arranged in this order,
The carbon-containing layer contains a conductive carbon material and a polymer compound,
The conductive carbon material contains graphite and/or carbon black,
The polymer compound is a rubber-based resin, and
The positive electrode for a lead-acid battery, wherein the positive electrode active material layer contains lead dioxide.