JP7435663B2 - Inkjet recording method - Google Patents
Inkjet recording method Download PDFInfo
- Publication number
- JP7435663B2 JP7435663B2 JP2022094826A JP2022094826A JP7435663B2 JP 7435663 B2 JP7435663 B2 JP 7435663B2 JP 2022094826 A JP2022094826 A JP 2022094826A JP 2022094826 A JP2022094826 A JP 2022094826A JP 7435663 B2 JP7435663 B2 JP 7435663B2
- Authority
- JP
- Japan
- Prior art keywords
- solvent
- mass
- resin
- inkjet
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、インクジェット記録方法に関し、より詳しくは、チタン紙上に画像記録する際に寸法安定性、密着性及び画質を向上できるインクジェット記録方法に関する。 The present invention relates to an inkjet recording method, and more particularly to an inkjet recording method that can improve dimensional stability, adhesion, and image quality when recording an image on titanium paper.
従来、化粧板を構成するための化粧紙としてチタン紙が使用されている。このような技術においては、チタン紙上に絵柄を印刷した後、該チタン紙に樹脂を含浸させて化粧紙を得る。かかる化粧紙によって化粧板の表面に所望の絵柄を付与でき、化粧紙の裏面に配置される基材の色を隠蔽できる。 Conventionally, titanium paper has been used as decorative paper for constructing decorative boards. In such a technique, a decorative paper is obtained by printing a pattern on titanium paper and then impregnating the titanium paper with a resin. With such decorative paper, a desired pattern can be imparted to the surface of the decorative board, and the color of the base material placed on the back side of the decorative paper can be hidden.
特許文献１には、インクジェット印刷用のチタン紙が開示されている。また、特許文献２には、チタン紙上にインクジェット法により印刷された印刷層を有する化粧板原紙が開示されている。 Patent Document 1 discloses titanium paper for inkjet printing. Further, Patent Document 2 discloses a decorative board base paper having a printed layer printed on titanium paper by an inkjet method.
一方、特許文献３～５には、インクジェット法に用いられるインクジェットインクが開示されている。 On the other hand, Patent Documents 3 to 5 disclose inkjet inks used in the inkjet method.
本発明者が、インクジェット法によってチタン紙上に画像記録するインクジェット記録方法について検討したところ、寸法安定性、密着性及び画質を向上する観点で更なる改善の余地が見出された。 When the present inventor studied an inkjet recording method for recording an image on titanium paper using an inkjet method, it was found that there is room for further improvement in terms of improving dimensional stability, adhesion, and image quality.
そこで本発明の課題は、チタン紙上に画像記録する際に寸法安定性、密着性及び画質を向上できるインクジェット記録方法を提供することにある。 Therefore, an object of the present invention is to provide an inkjet recording method that can improve dimensional stability, adhesion, and image quality when recording images on titanium paper.
また本発明の他の課題は、以下の記載によって明らかとなる。 Further, other objects of the present invention will become clear from the following description.
上記課題は、以下の各発明によって解決される。 The above problems are solved by the following inventions.
１．
色材、樹脂、両親媒性溶剤及び水を少なくとも含有する水系インクジェットインクを用いてインクジェット法によりチタン紙上に画像記録するインクジェット記録方法であって、
前記樹脂として、酸価を有するブロック共重合体を用い、
前記両親媒性溶剤は、グリコール系溶剤、グリコールモノエーテル系溶剤及びグリコールジエーテル系溶剤から選択され、且つアルキル基を有しないか又は１分子中に含まれるアルキル基の合計炭素数が２以下であり、
前記水系インクジェットインクの全量に対して前記両親媒性溶剤を３５質量％以上含有することを特徴とするインクジェット記録方法。
２．
前記樹脂として、酸価が１～８０ｍｇＫＯＨ／ｇであるブロック共重合体を用いることを特徴とする前記１記載のインクジェット記録方法。
３．
前記樹脂として、酸価が１～４０ｍｇＫＯＨ／ｇであるブロック共重合体を用いることを特徴とする前記１記載のインクジェット記録方法。
４．
前記水系インクジェットインクの全量に対して前記両親媒性溶剤を４５～９０質量％含有することを特徴とする前記１～３の何れかに記載のインクジェット記録方法。
５．
前記水系インクジェットインクの全量に対して、グリコールモノエーテル系溶剤である前記両親媒性溶剤の含有量をＡ質量％、グリコール系溶剤である前記両親媒性溶剤の含有量をＢ質量％、グリコールジエーテル系溶剤である前記両親媒性溶剤の含有量をＣ質量％としたときに、Ａ≧Ｂ、且つＡ≧Ｃの条件を満たすことを特徴とする前記１～４の何れかに記載のインクジェット記録方法。
６．
前記水系インクジェットインクの全量に対して、グリコールモノエーテル系溶剤である前記両親媒性溶剤の含有量が４５質量％以上であることを特徴とする前記１～５の何れかに記載のインクジェット記録方法。
７．
前記水性インクジェットインクの全量に対して、水の含有量が１０～５０質量％であることを特徴とする前記１～６の何れかに記載のインクジェット記録方法。
1.
An inkjet recording method for recording an image on titanium paper by an inkjet method using a water-based inkjet ink containing at least a coloring material, a resin, an amphipathic solvent, and water, the method comprising:
As the resin, a block copolymer having an acid value is used,
The amphiphilic solvent is selected from glycol solvents, glycol monoether solvents, and glycol diether solvents, and does not have an alkyl group or has a total number of carbon atoms of alkyl groups in one molecule of 2 or less. can be,
An inkjet recording method, characterized in that the amphiphilic solvent is contained in an amount of 35% by mass or more based on the total amount of the aqueous inkjet ink.
2.
1. The inkjet recording method as described in 1 above, wherein a block copolymer having an acid value of 1 to 80 mgKOH/g is used as the resin.
3.
1. The inkjet recording method as described in 1 above, wherein a block copolymer having an acid value of 1 to 40 mgKOH/g is used as the resin.
4.
4. The inkjet recording method according to any one of items 1 to 3 above, wherein the amphipathic solvent is contained in an amount of 45 to 90% by mass based on the total amount of the aqueous inkjet ink.
5.
With respect to the total amount of the water-based inkjet ink, the content of the amphiphilic solvent which is a glycol monoether solvent is A mass %, the content of the amphipathic solvent which is a glycol solvent is B mass %, and the content of the amphiphilic solvent which is a glycol monoether solvent is B mass %. 5. The inkjet according to any one of 1 to 4 above, characterized in that the content of the amphiphilic solvent, which is an ether solvent, satisfies the following conditions: A≧B and A≧C, when the content of the amphipathic solvent is C mass %. Recording method.
6.
The inkjet recording method according to any one of items 1 to 5 above, wherein the content of the amphipathic solvent, which is a glycol monoether solvent, is 45% by mass or more based on the total amount of the water-based inkjet ink. .
7.
7. The inkjet recording method according to any one of items 1 to 6 above, wherein the water content is 10 to 50% by mass based on the total amount of the aqueous inkjet ink.
本発明によれば、チタン紙上に画像記録する際に寸法安定性、密着性及び画質を向上できるインクジェット記録方法を提供することができる。 According to the present invention, it is possible to provide an inkjet recording method that can improve dimensional stability, adhesion, and image quality when recording an image on titanium paper.
以下に、本発明を実施するための形態について詳しく説明する。 EMBODIMENT OF THE INVENTION Below, the form for implementing this invention is demonstrated in detail.
１．基本構成
本発明のインクジェット記録方法は、色材、樹脂、両親媒性溶剤及び水を少なくとも含有する水系インクジェットインクをインクジェット記録ヘッドから吐出してチタン紙上に画像記録する。ここで、前記樹脂は、ブロック共重合体又はグラフト共重合体であり、且つ酸価を有する。また、前記両親媒性溶剤は、グリコール系溶剤、グリコールモノエーテル系溶剤及びグリコールジエーテル系溶剤から選択され、且つアルキル基を有しないか又は１分子中に含まれるアルキル基の合計炭素数が２以下である。更に、前記水系インクジェットインクの全量に対して前記両親媒性溶剤を３５質量％以上含有する。
1. Basic Configuration The inkjet recording method of the present invention records an image on titanium paper by ejecting a water-based inkjet ink containing at least a coloring material, a resin, an amphipathic solvent, and water from an inkjet recording head. Here, the resin is a block copolymer or a graft copolymer and has an acid value. The amphipathic solvent is selected from glycol solvents, glycol monoether solvents, and glycol diether solvents, and has no alkyl group or has a total number of carbon atoms of alkyl groups in one molecule of 2. It is as follows. Furthermore, the amphiphilic solvent is contained in an amount of 35% by mass or more based on the total amount of the water-based inkjet ink.
かかる本発明のインクジェット記録方法によれば、チタン紙上に画像記録する際に寸法安定性、密着性及び画質を向上できる効果が得られる。 According to the inkjet recording method of the present invention, it is possible to improve dimensional stability, adhesion, and image quality when recording an image on titanium paper.
ここで、寸法安定性の向上は、画像記録に伴うチタン紙の変形が抑制されることによって達成される。また、密着性の向上は、記録された画像（塗膜）のチタン紙に対する密着性が向上することによって達成される。更に、画質の向上は、画像を十分な高濃度で表現でき、画像の面内ムラ（濃度ムラ）が防止され、且つ画像の滲みが防止されることによって達成される。 Here, the improvement in dimensional stability is achieved by suppressing deformation of the titanium paper accompanying image recording. Further, the improvement in adhesion is achieved by improving the adhesion of the recorded image (coating film) to the titanium paper. Further, improvement in image quality is achieved by being able to express an image with a sufficiently high density, preventing in-plane unevenness (density unevenness) of the image, and preventing blurring of the image.
上記のような効果が得られる機構については、以下のように推定される。 The mechanism by which the above effects are obtained is estimated as follows.
まず、酸化チタンを含むチタン紙上に、酸価を有する樹脂を含む水系インクジェットインク（以下、単にインクともいう。）からなるインク塗膜が形成される。 First, an ink film made of a water-based inkjet ink (hereinafter also simply referred to as ink) containing a resin having an acid value is formed on a titanium paper containing titanium oxide.
インクに含有される酸価を有する樹脂は、カルボキシ基等のアニオン性基を有する。このとき、該樹脂の構造が精密に制御されていること（具体的にはブロック共重合体又はグラフト共重合体であること）によって、該樹脂を構成するポリマー中には、アニオン性基を有する領域と、アニオン性基を有しない領域とが形成されている。 The resin having an acid value contained in the ink has an anionic group such as a carboxy group. At this time, because the structure of the resin is precisely controlled (specifically, it is a block copolymer or a graft copolymer), the polymer constituting the resin has an anionic group. A region and a region having no anionic group are formed.
樹脂を構成するポリマー中のアニオン性基を有する領域は、チタン紙に含まれる酸化チタンに対して水素結合又は配位結合を形成し、酸化チタンに吸着する。金属元素の中でも特にチタンは高周期元素でありｆ軌道などの空の軌道が多く、且つ亜鉛等と比べてｆ軌道にほとんど電子が収容されていないため、上記のような吸着が効率的に進行する。 A region having an anionic group in the polymer constituting the resin forms a hydrogen bond or a coordinate bond with the titanium oxide contained in the titanium paper, and is adsorbed to the titanium oxide. Among metal elements, titanium in particular is a high-period element and has many empty orbitals such as f-orbitals, and compared to zinc, etc., there are almost no electrons accommodated in f-orbitals, so the adsorption described above proceeds efficiently. do.
一方、樹脂を構成するポリマー中のアニオン性基を有しない領域は、インク中へ配向し易くなる。このような配向は、インクが両親媒性溶剤を多く（具体的には３５質量％以上）含有することによって効率的に進行する。両親媒性溶剤は、インク中の水に対して親和性を示すと共に、アニオン性基を有しない領域に対しても親和性を示すからである。 On the other hand, regions that do not have anionic groups in the polymer constituting the resin tend to be oriented into the ink. Such orientation progresses efficiently when the ink contains a large amount of amphipathic solvent (specifically, 35% by mass or more). This is because the amphiphilic solvent exhibits affinity for water in the ink and also for regions that do not have anionic groups.
これらの結果、チタン紙とインクとの界面近傍に樹脂を介在させることができる。界面近傍において樹脂がクッションとして働くことによって、画像記録に伴うチタン紙の変形が抑制される。 As a result, the resin can be present near the interface between the titanium paper and the ink. Since the resin acts as a cushion near the interface, deformation of the titanium paper due to image recording is suppressed.
また、樹脂が酸化チタンに吸着することによって、インクによって記録される画像（印刷層）のチタン紙に対する密着性が向上する。 Furthermore, adsorption of the resin to titanium oxide improves the adhesion of the image (print layer) recorded with the ink to the titanium paper.
更に、樹脂が酸化チタンに吸着することによって、インクがチタン紙の内部に過剰に浸透することが防止され、インクをチタン紙の表面側にとどめることができる。これにより、画像を十分な高濃度で表現できる。また、樹脂は酸化チタンに効率的に（均一に）吸着されるため、画像の面内ムラ（濃度ムラ）が防止される。更に、樹脂によってインクの縁部が固定（ピニング）されるため、画像の滲みが防止される。これらが相乗的に作用して、画質が向上する。 Furthermore, the adsorption of the resin to the titanium oxide prevents the ink from excessively penetrating into the titanium paper, allowing the ink to remain on the surface side of the titanium paper. This allows images to be expressed with sufficiently high density. Furthermore, since the resin is efficiently (uniformly) adsorbed to titanium oxide, in-plane unevenness (density unevenness) in the image is prevented. Furthermore, since the edges of the ink are fixed (pinned) by the resin, bleeding of the image is prevented. These act synergistically to improve image quality.
以下に、本発明について更に詳しく説明する。 The present invention will be explained in more detail below.
２．インク
インクは、色材、樹脂、両親媒性溶剤及び水を少なくとも含有する。
2. Ink The ink contains at least a coloring material, a resin, an amphipathic solvent, and water.
（１）色材
色材としては、例えば、顔料、染料等が挙げられる。
(1) Coloring material Examples of the coloring material include pigments, dyes, and the like.
顔料としては、例えば、公知の無機顔料、有機顔料又はカーボンブラック等が挙げられる。 Examples of the pigment include known inorganic pigments, organic pigments, and carbon black.
カーボンブラックとしては、例えば、ファーネスブラック、ランプブラック、アセチレンブラック、チャンネルブラック等（Ｃ．Ｉ．ピグメントブラック７）が挙げられる。 Examples of carbon black include furnace black, lamp black, acetylene black, channel black, etc. (C.I. Pigment Black 7).
有機顔料としては、例えば、キナクリドン系顔料、キナクリドンキノン系顔料、ジオキサジン系顔料、フタロシアニン系顔料、アントラピリミジン系顔料、アンサンスロン系顔料、インダンスロン系顔料、フラバンスロン系顔料、ペリレン系顔料、ジケトピロロピロール系顔料、ペリノン系顔料、キノフタロン系顔料、アントラキノン系顔料、チオインジゴ系顔料、ベンツイミダゾロン系顔料、イソインドリノン系顔料、アゾメチン系顔料、アゾ系顔料等が挙げられる。 Examples of organic pigments include quinacridone pigments, quinacridonequinone pigments, dioxazine pigments, phthalocyanine pigments, anthrapyrimidine pigments, anthanthrone pigments, indanthrone pigments, flavanthrone pigments, perylene pigments, and dioxazine pigments. Examples include ketopyrrolopyrrole pigments, perinone pigments, quinophthalone pigments, anthraquinone pigments, thioindigo pigments, benzimidazolone pigments, isoindolinone pigments, azomethine pigments, and azo pigments.
有機顔料の具体例として、以下のものが挙げられる。 Specific examples of organic pigments include the following.
シアンインクに使用される顔料としては、例えば、Ｃ．Ｉ．ピグメントブルー１、２、３、１５：３、１５：４、１５：３４、１６、２２、６０等；Ｃ．Ｉ．バットブルー４、６０等が挙げられる。 Examples of pigments used in cyan ink include C.I. I. Pigment Blue 1, 2, 3, 15:3, 15:4, 15:34, 16, 22, 60, etc.; C.I. I. Examples include Bat Blue 4 and 60.
マゼンタインクに使用される顔料としては、例えば、Ｃ．Ｉ．ピグメントレッド５、７、１２、４８（Ｃａ）、４８（Ｍｎ）、５７（Ｃａ）、５７：１、１１２、１２２、１２３、１６８、１８４、２０２、Ｃ．Ｉ．ピグメントバイオレット１９等が挙げられる。 Examples of pigments used in magenta ink include C.I. I. Pigment Red 5, 7, 12, 48 (Ca), 48 (Mn), 57 (Ca), 57:1, 112, 122, 123, 168, 184, 202, C.I. I. Pigment Violet 19 and the like.
イエローインクに使用される顔料としては、例えば、Ｃ．Ｉ．ピグメントイエロー１、２、３、１２、１３、１４Ｃ、１６、１７、７３、７４、７５、８３、９３、９５、９７、９８、１０９、１１０、１１４、１２８、１２９、１３８、１５０、１５１、１５４、１５５、１８０、１８５等が挙げられる。 Examples of pigments used in yellow ink include C.I. I. Pigment Yellow 1, 2, 3, 12, 13, 14C, 16, 17, 73, 74, 75, 83, 93, 95, 97, 98, 109, 110, 114, 128, 129, 138, 150, 151, 154, 155, 180, 185 and the like.
顔料の含有量は格別限定されず、インク全体に対して、例えば１質量％～１０質量％程度とすることができ、好ましくは２質量％～５質量％程度とすることができる。 The content of the pigment is not particularly limited, and can be, for example, about 1% by mass to 10% by mass, preferably about 2% by mass to 5% by mass, based on the entire ink.
染料としては、例えば、水溶性染料、分散染料等が挙げられる。水溶性染料としては、例えば、酸性染料、直接染料、塩基性染料等が挙げられる。分散染料としては、例えば、着色ポリマー、着色ワックス等が挙げられる。 Examples of the dye include water-soluble dyes and disperse dyes. Examples of water-soluble dyes include acid dyes, direct dyes, and basic dyes. Examples of disperse dyes include colored polymers and colored waxes.
染料の含有量は格別限定されず、インク全体に対して、例えば１質量％～１０質量％程度とすることができ、好ましくは２質量％～４．５質量％程度とすることができる。 The content of the dye is not particularly limited, and can be, for example, about 1% by mass to 10% by mass, preferably about 2% by mass to 4.5% by mass, based on the entire ink.
（２）樹脂
樹脂として、酸価を有するブロック共重合体、及び、酸価を有するグラフト共重合体の一方を用いるか、又は両方を併用する。
(2) Resin As the resin, one of a block copolymer having an acid value and a graft copolymer having an acid value is used, or both are used in combination.
酸価を有するブロック共重合体、及び、酸価を有するグラフト共重合体は、何れもポリマー中に、アニオン性基を有する領域と、アニオン性基を有しない領域とが良好に形成される。 In both the block copolymer having an acid value and the graft copolymer having an acid value, a region having an anionic group and a region having no anionic group are well formed in the polymer.
ブロック共重合体である樹脂は、例えば、アニオン性基を有するモノマーが連続的に重合されている領域と、アニオン性基を有しないモノマーが連続的に重合されている領域とが連結されることによって構成され得る。 In a resin that is a block copolymer, for example, a region in which a monomer having an anionic group is continuously polymerized and a region in which a monomer not having an anionic group is continuously polymerized are connected. It can be configured by
グラフト共重合体である樹脂は、例えば、アニオン性基を有するモノマーが連続的に重合されている幹と、アニオン性基を有しないモノマーが連続的に重合されている枝とによって構成されてもよいし、アニオン性基を有しないモノマーが連続的に重合されている幹と、アニオン性基を有するモノマーが連続的に重合されている枝とによって構成されてもよい。 A resin that is a graft copolymer may be composed of, for example, a trunk in which a monomer having an anionic group is continuously polymerized and a branch in which a monomer without an anionic group is continuously polymerized. Alternatively, it may be composed of a trunk in which a monomer having no anionic group is continuously polymerized and a branch in which a monomer having an anionic group is continuously polymerized.
樹脂はグラフト共重合体であることが特に好ましい。これにより、画質を更に向上することができる。 It is particularly preferred that the resin is a graft copolymer. Thereby, image quality can be further improved.
樹脂の酸価は、電位差滴定法により求めることができ、例えば色材協会誌６１，［１２］６９２－６９８（１９８８）に記載の方法で測定できる。「酸価を有する」というのは、酸価の値がゼロではないことを意味する。 The acid value of the resin can be determined by potentiometric titration, for example, by the method described in Color Materials Association Journal 61, [12] 692-698 (1988). "Having an acid value" means that the acid value is not zero.
樹脂の酸価は１～８０ｍｇＫＯＨ／ｇであることが好ましい。即ち、樹脂として、酸価が１～８０ｍｇＫＯＨ／ｇであるブロック共重合体、及び、酸価が１～８０ｍｇＫＯＨ／ｇであるグラフト共重合体の一方を用いるか、又は両方を併用することが好ましい。これにより本発明の効果がより良好に発揮される。特に、酸価が１以上であることによって、アニオン性基を有する領域を酸化チタンに対して良好な強さで吸着することができ、密着性が更に向上する。また、酸価が８０以下であることによって、吸着の強さが過剰になることが防止され、その結果、吸着が局所的に生じることが防止され、チタン紙上に樹脂がより均一に広がる。これにより、画像の面内ムラがより確実に防止され、画質が更に向上する。これらの効果をより好適に発揮する観点で、樹脂の酸価は１～４０ｍｇＫＯＨ／ｇであることがより好ましい。 The acid value of the resin is preferably 1 to 80 mgKOH/g. That is, as the resin, it is preferable to use one of a block copolymer having an acid value of 1 to 80 mgKOH/g and a graft copolymer having an acid value of 1 to 80 mgKOH/g, or to use both in combination. . This allows the effects of the present invention to be better exhibited. In particular, when the acid value is 1 or more, the region having an anionic group can be adsorbed to titanium oxide with good strength, and the adhesion is further improved. Further, by having an acid value of 80 or less, the strength of adsorption is prevented from becoming excessive, and as a result, adsorption is prevented from occurring locally, and the resin is spread more uniformly on the titanium paper. This more reliably prevents in-plane unevenness of the image and further improves the image quality. From the viewpoint of exhibiting these effects more preferably, the acid value of the resin is more preferably 1 to 40 mgKOH/g.
樹脂が有するアニオン性基は格別限定されず、例えば、カルボキシル基、スルホン酸基等が挙げられ、中でもカルボキシル基が好ましい。カルボキシル基は、例えば（メタ）アクリル酸等のようなカルボキシル基を有するモノマーを重合することによって、樹脂中に導入することができる。 The anionic group that the resin has is not particularly limited, and examples thereof include a carboxyl group, a sulfonic acid group, and among them, a carboxyl group is preferable. A carboxyl group can be introduced into the resin by polymerizing a monomer having a carboxyl group, such as (meth)acrylic acid.
樹脂が有するアニオン性基は、例えばアルカリ中和されていてもよい。アニオン性基を中和するアルカリは格別限定されないが、例えば、水酸化ナトリウム、水酸化カリウム、水酸化リチウム、水酸化カルシウム等の金属塩基化合物や、アンモニアや、トリエチルアミン、ピリジン、モルホリン等の有機アミンや、モノエタノールアミン等のアルカノールアミン等が挙げられる。 The anionic group that the resin has may be neutralized with an alkali, for example. The alkali that neutralizes the anionic group is not particularly limited, but examples include metal base compounds such as sodium hydroxide, potassium hydroxide, lithium hydroxide, and calcium hydroxide, and organic amines such as ammonia, triethylamine, pyridine, and morpholine. and alkanolamines such as monoethanolamine.
樹脂は、１種を単独で用いてもよいし、複数種を併用してもよい。インクは、例えば、酸価を有するブロック共重合体として１種又は複数種を含有することができる。また、インクは、例えば、酸価を有するグラフト共重合体として１種又は複数種を含有することができる。 One type of resin may be used alone, or a plurality of types may be used in combination. The ink can contain, for example, one or more block copolymers having an acid value. Further, the ink can contain, for example, one or more graft copolymers having an acid value.
インクの全量に対して、上述した樹脂の含有量は、格別限定されないが、例えば０．５質量％～５質量％程度とすることができ、好ましくは１質量％～２．５質量％とすることができる。 The content of the resin described above is not particularly limited to the total amount of the ink, but can be, for example, about 0.5% by mass to 5% by mass, preferably 1% by mass to 2.5% by mass. be able to.
（３）両親媒性溶剤
両親媒性溶剤としては、グリコール系溶剤、グリコールモノエーテル系溶剤及びグリコールジエーテル系溶剤から選択され、且つアルキル基を有しないか又は１分子中に含まれるアルキル基の合計炭素数が２以下である溶剤が用いられる。
(3) Amphiphilic solvent The amphiphilic solvent is selected from glycol solvents, glycol monoether solvents, and glycol diether solvents, and has no alkyl group or has no alkyl group contained in one molecule. A solvent having a total carbon number of 2 or less is used.
ここで、「１分子中に含まれるアルキル基の合計炭素数」（以下、「アルキル炭素数」ともいう。）は、１分子中に１つのアルキル基を有する場合は、該アルキル基の炭素数であり、１分子中に複数のアルキル基を有する場合には、該複数のアルキル基の合計の炭素数である。なお、アルキレン基（例えば２つの酸素原子間を連結する炭素鎖）は、ここでいうアルキル基に含まれないが、該アルキレン基からアルキル基が分岐している場合は、該アルキル基の炭素数を合計炭素数に加算する。 Here, "the total number of carbon atoms in the alkyl group contained in one molecule" (hereinafter also referred to as "the number of alkyl carbon atoms") refers to the number of carbon atoms in the alkyl group when there is one alkyl group in one molecule. When one molecule has a plurality of alkyl groups, it is the total carbon number of the plurality of alkyl groups. Note that an alkylene group (for example, a carbon chain connecting two oxygen atoms) is not included in the alkyl group referred to here, but if an alkyl group is branched from the alkylene group, the number of carbon atoms in the alkyl group Add to the total number of carbons.
グリコール系溶剤である両親媒性溶剤としては、例えば、アルキレングリコール、ジアルキレングリコール、トリアルキレングリコール、テトラアルキレングリコール、ペンタアルキレングリコール等が挙げられる。これらの化合物が有する各アルキレン基の炭素数は例えば１～４、更には１～３である。このような化合物の具体例として、例えば、トリプロピレングリコール（アルキル基なし（アルキル炭素数０））等のようなジオールが挙げられる。 Examples of amphiphilic solvents that are glycol-based solvents include alkylene glycols, dialkylene glycols, trialkylene glycols, tetraalkylene glycols, pentaalkylene glycols, and the like. The number of carbon atoms in each alkylene group of these compounds is, for example, 1 to 4, and more preferably 1 to 3. Specific examples of such compounds include diols such as tripropylene glycol (no alkyl group (alkyl carbon number: 0)).
グリコールモノエーテル系溶剤である両親媒性溶剤としては、例えば、アルキレングリコールモノエーテル、ジアルキレングリコールモノエーテル、トリアルキレングリコールモノエーテル、テトラアルキレングリコールモノエーテル、ペンタアルキレングリコールモノエーテル等が挙げられる。これらの化合物が有する各アルキレン基の炭素数は例えば１～４、更には１～３である。これらの化合物が有するアルキル基（エーテル結合されているアルキル基）の合計炭素数は１又は２である。このような化合物の具体例として、例えば、トリプロピレングリコールモノメチルエーテル（アルキル炭素数１）、ジプロピレングリコールモノメチルエーテル（アルキル炭素数１）、トリエチレングリコールモノメチルエテール（アルキル炭素数１）等のようなモノアルキルが挙げられる。 Examples of amphiphilic solvents that are glycol monoether solvents include alkylene glycol monoether, dialkylene glycol monoether, trialkylene glycol monoether, tetraalkylene glycol monoether, and pentaalkylene glycol monoether. The number of carbon atoms in each alkylene group of these compounds is, for example, 1 to 4, and more preferably 1 to 3. The total number of carbon atoms in the alkyl groups (ether bonded alkyl groups) of these compounds is 1 or 2. Specific examples of such compounds include tripropylene glycol monomethyl ether (alkyl carbon number 1), dipropylene glycol monomethyl ether (alkyl carbon number 1), triethylene glycol monomethyl ether (alkyl carbon number 1), etc. Examples include monoalkyl.
グリコールジエーテル系溶剤である両親媒性溶剤としては、アルキレングリコールジメチルエーテル、ジアルキレングリコールジメチルエーテル、トリアルキレングリコールジメチルエーテル、テトラアルキレングリコールジメチルエーテル、ペンタアルキレングリコールジメチルエーテル等が挙げられる。これらの化合物が有する各アルキレン基の炭素数は例えば１～４、更には１～３である。このような化合物の具体例として、例えば、トリエチレングリコールジメチルエーテル（アルキル炭素数２）等のようなジアルキルが挙げられる。 Examples of amphipathic solvents that are glycol diether solvents include alkylene glycol dimethyl ether, dialkylene glycol dimethyl ether, trialkylene glycol dimethyl ether, tetraalkylene glycol dimethyl ether, and pentaalkylene glycol dimethyl ether. The number of carbon atoms in each alkylene group of these compounds is, for example, 1 to 4, and more preferably 1 to 3. Specific examples of such compounds include dialkyl such as triethylene glycol dimethyl ether (alkyl carbon number 2).
両親媒性溶剤は、１種を単独で用いてもよいし、複数種を併用してもよい。 The amphiphilic solvents may be used alone or in combination.
インクの全量に対して、両親媒性溶剤は、３５質量％以上含有され、好ましくは４５～９０質量％含有される。 The amphipathic solvent is contained in an amount of 35% by mass or more, preferably 45 to 90% by mass, based on the total amount of the ink.
インクの全量に対して、グリコールモノエーテル系溶剤である両親媒性溶剤の含有量をＡ質量％、グリコール系溶剤である両親媒性溶剤の含有量をＢ質量％、グリコールジエーテル系溶剤である両親媒性溶剤の含有量をＣ質量％としたときに、Ａ≧Ｂ、且つＡ≧Ｃの条件を満たすことが好ましい。これにより、密着性を更に向上することができる。 Based on the total amount of ink, the content of the amphipathic solvent, which is a glycol monoether solvent, is A% by mass, the content of the amphiphilic solvent, which is a glycol solvent, is B% by mass, and it is a glycol diether solvent. When the content of the amphipathic solvent is C mass %, it is preferable that the conditions A≧B and A≧C are satisfied. Thereby, adhesion can be further improved.
また、インクの全量に対して、グリコールモノエーテル系溶剤である両親媒性溶剤の含有量が４５質量％以上であることが好ましい。これにより、寸法安定性を更に向上することができる。 Further, it is preferable that the content of the amphiphilic solvent, which is a glycol monoether solvent, is 45% by mass or more based on the total amount of the ink. Thereby, dimensional stability can be further improved.
（４）水
インクの全量に対して、水の含有量は１０～５０質量％であることが好ましい。これにより、酸化チタンに樹脂が吸着する一方で、インク側にも樹脂鎖の広がりを生じさせることができ、基材密着性や用紙変形が抑制できるという効果が得られる。
(4) Water The content of water is preferably 10 to 50% by mass based on the total amount of ink. As a result, while the resin is adsorbed to the titanium oxide, it is possible to cause the resin chains to spread on the ink side as well, and it is possible to obtain the effect that the adhesion to the substrate and the deformation of the paper can be suppressed.
（５）その他
インクは、本発明の効果を損なわない範囲で、以上に説明した成分に加えて、他の成分を適宜含むことができる。他の成分としては、例えば、防腐剤、界面活性剤等が挙げられる。
(5) Others In addition to the components described above, the ink can appropriately contain other components within a range that does not impair the effects of the present invention. Examples of other components include preservatives, surfactants, and the like.
〔チタン紙〕
画像が記録される記録媒体として、チタン紙が好適に用いられる。チタン紙としては、パルプに二酸化チタンを抄きこんでなる紙を用いることができる。チタン紙は、二酸化チタンに由来して隠蔽力に優れる。そのため、印刷層が形成されたチタン紙を化粧板に用いた場合には、下地や基材の影響が軽減され、印刷層が良好に視認される。
[Titanium paper]
Titanium paper is preferably used as the recording medium on which images are recorded. As the titanium paper, paper made by incorporating titanium dioxide into pulp can be used. Titanium paper is derived from titanium dioxide and has excellent hiding power. Therefore, when titanium paper on which a printed layer is formed is used for a decorative board, the influence of the undercoat and base material is reduced, and the printed layer is clearly visible.
〔インクジェット法〕
インクをチタン紙上に付与する際に用いるインクジェット法は格別限定されず、インクを装填したインクジェットヘッド（インクジェット記録ヘッドともいう）を備えるプリンターを用いることができる。具体的には、デジタル信号に基づいてインクジェットヘッドのノズルからインクを液滴として吐出させ、これをチタン紙上に着弾させて印字を行うことができる。
[Inkjet method]
The inkjet method used to apply ink onto titanium paper is not particularly limited, and a printer equipped with an inkjet head (also referred to as an inkjet recording head) loaded with ink can be used. Specifically, ink can be ejected as droplets from the nozzles of an inkjet head based on digital signals, and the droplets can be landed on titanium paper to perform printing.
インクジェットヘッドからのインク吐出方式は、オンデマンド方式とコンティニュアス方式のいずれでもよい。オンデマンド方式のインクジェットヘッドは、シングルキャビティー型、ダブルキャビティー型、ベンダー型、ピストン型、シェアーモード型及びシェアードウォール型等の電気－機械変換方式、並びにサーマルインクジェット型及びバブルジェット（登録商標）（バブルジェットはキヤノン社の登録商標）型等の電気－熱変換方式等のいずれでもよい。 The method of ejecting ink from the inkjet head may be either an on-demand method or a continuous method. On-demand type inkjet heads include electro-mechanical conversion types such as single cavity type, double cavity type, bender type, piston type, shear mode type and shared wall type, as well as thermal inkjet type and bubble jet (registered trademark). (Bubble jet is a registered trademark of Canon Inc.) type, etc. may be any type of electric-thermal conversion method.
また、インクジェット記録装置として、ライン記録方式（シングルパス記録方式）のものと、シリアル記録方式のものとがあり、求められる画像の解像度や記録速度に応じて適宜選択できる。 Furthermore, there are two types of inkjet recording apparatuses: a line recording type (single pass recording type) and a serial recording type, which can be selected as appropriate depending on the required image resolution and recording speed.
〔その他〕
インクジェット記録方法によって画像（印刷層）が形成されたチタン紙の用途は格別限定されないが、例えば、化粧板を構成するための化粧紙等として使用することができる。この場合、印刷層が形成されたチタン紙に樹脂を含浸させて化粧紙（樹脂含浸化粧紙）が得られる。
〔others〕
The use of titanium paper on which an image (printed layer) is formed by an inkjet recording method is not particularly limited, but it can be used, for example, as a decorative paper for forming a decorative board. In this case, decorative paper (resin-impregnated decorative paper) is obtained by impregnating titanium paper on which a printed layer is formed with a resin.
化粧紙の裏面（印刷層が形成された面に対して反対側の面）には、基材を積層することができる。基材は格別限定されず、例えばパーティクルボード等のような板状の部材等が挙げられる。 A base material can be laminated on the back surface of the decorative paper (the surface opposite to the surface on which the printing layer is formed). The base material is not particularly limited, and includes, for example, a plate-shaped member such as particle board.
また、化粧紙の印刷層上には表面紙を積層することができる。表面紙は、樹脂を含浸させて透明化されたものであり得る。 Moreover, a surface paper can be laminated on the printed layer of the decorative paper. The surface paper may be made transparent by impregnating it with a resin.
チタン紙や表面紙に含浸させる樹脂は格別限定されず、例えば、メラミン樹脂、ポリエステル樹脂、ダップ樹脂等のような熱硬化性樹脂等が挙げられる。 The resin with which the titanium paper or surface paper is impregnated is not particularly limited, and examples thereof include thermosetting resins such as melamine resin, polyester resin, and DAP resin.
樹脂含浸化粧紙に基材や表面紙を積層してなる積層体を、加熱下において積層方向に加圧することによって、ＨＰＬ（High Pressure Laminate）と称される化粧板合板を製造することができる。 A decorative plywood called HPL (High Pressure Laminate) can be manufactured by applying pressure in the lamination direction under heating to a laminate formed by laminating a resin-impregnated decorative paper with a base material and a surface paper.
以下に、本発明の実施例について説明するが、本発明はかかる実施例により限定されない。 Examples of the present invention will be described below, but the present invention is not limited to these Examples.
１．分散液（顔料分散液）の調製
〔分散液１〕
シアン顔料６５質量部に、樹脂（ビックケミー社製「ＤＩＳＰＥＲＳＥ１８４」；グラフト共重合体、酸価０ｍｇＫＯＨ／ｇ）２６質量部と、溶剤としてトリプロピレングリコールモノメチルエーテルを２８５質量部と、イオン交換水を９６質量部加えた混合液をプレミックスした後、０．５ｍｍのジルコニアビーズを体積率で５０％充填したサンドグラインダーを用いて分散し、分散液１を調製した。
1. Preparation of dispersion liquid (pigment dispersion liquid) [Dispersion liquid 1]
65 parts by mass of cyan pigment, 26 parts by mass of resin ("DISPERSE184" manufactured by Bikkemie; graft copolymer, acid value 0 mgKOH/g), 285 parts by mass of tripropylene glycol monomethyl ether as a solvent, and 96 parts by mass of ion-exchanged water. After premixing the mixed solution to which parts by mass were added, it was dispersed using a sand grinder filled with 0.5 mm zirconia beads at a volume ratio of 50% to prepare Dispersion 1.
〔分散液２〕
分散液１において、樹脂（ビックケミー社製「ＤＩＳＰＥＲＳＥ１８４」；グラフト共重合体、酸価０ｍｇＫＯＨ／ｇ）に代えて、樹脂（ビックケミー社製「ＢＹＫＪＥＴ９１５２」；グラフト共重合体、酸価６ｍｇＫＯＨ／ｇ）を用いたこと以外は、分散液１と同様にして、分散液２を調製した。
[Dispersion liquid 2]
In Dispersion 1, instead of the resin ("DISPERSE184" manufactured by BYK Chemie; graft copolymer, acid value 0 mgKOH/g), resin ("BYKJET9152" manufactured by BYK Chemie; graft copolymer, acid value 6 mg KOH/g) was used. Dispersion 2 was prepared in the same manner as Dispersion 1 except that the following was used.
２．インクの調製
上記の分散液を下記のインク成分と共に表１、２に示す処方（インク組成）で配合し、攪拌、混合した。その後、この混合液を１μｍのフィルターにより濾過してインクを得た。なお、濾過前後でインク組成は実質的に変化していない。
2. Preparation of Ink The above dispersion liquid was blended with the following ink components according to the formulation (ink composition) shown in Tables 1 and 2, and stirred and mixed. Thereafter, this liquid mixture was filtered through a 1 μm filter to obtain an ink. Note that the ink composition did not substantially change before and after filtration.
〔溶剤〕
・トリプロピレングリコール（ＴＰＧ、ジオール）
・トリエチレングリコールジメチルエーテル（ＴＥＧＤＭＥ、ジアルキル）
・トリプロピレングリコールモノメチルエーテル（ＴＰＧＭＥ、モノアルキル）
・ジプロピレングリコールモノメチルエーテル（ＤＰＧＭＥ、モノアルキル）
・トリエチレングリコールモノメチルエテール（ＴＥＧＭＥ、モノアルキル）
・トリエチレングリコールモノブチルエーテル（ＴＥＧＢＥ、モノアルキル）
〔樹脂〕
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ１８０」、ブロック共重合体、酸価９４ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ３２０００」、ブロック共重合体、酸価１５ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ１９４」、グラフト共重合体、酸価７０ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＢＹＫＪＥＴ９１５２」、グラフト共重合体、酸価６ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＢＹＫＪＥＴ９１５１」、グラフト共重合体、酸価７ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ１９０」、グラフト共重合体、酸価１０ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ２０１０」、グラフト共重合体、酸価２０ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ２０１５」、グラフト共重合体、酸価１５ｍｇＫＯＨ／ｇ
・共栄社化学社製「フローレンＴＧ－７５０Ｗ」、グラフト共重合体、酸価４０ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ４３０００」、グラフト共重合体、酸価８ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ４４０００」、グラフト共重合体、酸価１２ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ４６０００」、グラフト共重合体、酸価１２ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ４７０００」、グラフト共重合体、酸価８ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ１８４」、グラフト共重合体、酸価０ｍｇＫＯＨ／ｇ
・ビックケミー社製「ＤＩＳＰＥＲＢＹＫ１８５」、ブロック共重合体、酸価０ｍｇＫＯＨ／ｇ
・Ｌｕｂｒｉｚｏｌ社製「ｓｏｌｓｐｅｒｓｅ５４０００」、ランダム共重合体、酸価３５ｍｇＫＯＨ／ｇ
〔防腐剤〕
・ロンザ社製「Ｐｒｏｘｅｌ ＧＸＬ（Ｓ）」
〔水〕
・イオン交換水
〔solvent〕
・Tripropylene glycol (TPG, diol)
・Triethylene glycol dimethyl ether (TEGDME, dialkyl)
・Tripropylene glycol monomethyl ether (TPGME, monoalkyl)
・Dipropylene glycol monomethyl ether (DPGME, monoalkyl)
・Triethylene glycol monomethyl ether (TEGME, monoalkyl)
・Triethylene glycol monobutyl ether (TEGBE, monoalkyl)
〔resin〕
・“DISPERBYK180” manufactured by BYK Chemie, block copolymer, acid value 94mgKOH/g
・"solsperse 32000" manufactured by Lubrizol, block copolymer, acid value 15 mgKOH/g
・“DISPERBYK194” manufactured by BYK Chemie, graft copolymer, acid value 70mgKOH/g
・BYKJET9152 manufactured by BYK Chemie, graft copolymer, acid value 6mgKOH/g
・BYKJET9151 manufactured by BYK Chemie, graft copolymer, acid value 7mgKOH/g
・“DISPERBYK190” manufactured by BYK Chemie, graft copolymer, acid value 10mgKOH/g
・“DISPERBYK2010” manufactured by BYK Chemie, graft copolymer, acid value 20mgKOH/g
・“DISPERBYK2015” manufactured by BYK Chemie, graft copolymer, acid value 15mgKOH/g
・“Floren TG-750W” manufactured by Kyoeisha Chemical Co., Ltd., graft copolymer, acid value 40mgKOH/g
・"solsperse 43000" manufactured by Lubrizol, graft copolymer, acid value 8 mgKOH/g
・"solsperse 44000" manufactured by Lubrizol, graft copolymer, acid value 12 mgKOH/g
・"solsperse 46000" manufactured by Lubrizol, graft copolymer, acid value 12 mgKOH/g
・"solsperse 47000" manufactured by Lubrizol, graft copolymer, acid value 8 mgKOH/g
・“DISPERBYK184” manufactured by BYK Chemie, graft copolymer, acid value 0 mgKOH/g
・“DISPERBYK185” manufactured by BYK Chemie, block copolymer, acid value 0 mgKOH/g
・"solsperse54000" manufactured by Lubrizol, random copolymer, acid value 35 mgKOH/g
〔Preservative〕
・Proxel GXL (S) manufactured by Lonza
〔water〕
・Ion exchange water
３．画像記録（インクジェット記録）
ピエゾ型インクジェットノズルを備えたインクジェット記録ヘッドを有するインクジェット記録装置に、上記調製した各試料を装填し、チタン紙に画像記録を連続して行った。記録材料の搬送速度は、３０ｍ／ｓで行った。
3. Image recording (inkjet recording)
Each sample prepared above was loaded into an inkjet recording device having an inkjet recording head equipped with a piezo type inkjet nozzle, and images were continuously recorded on titanium paper. The conveyance speed of the recording material was 30 m/s.
インク供給系は、図示しないが、インクタンク、供給パイプ、ヘッド直前のサブインクタンク、フィルター付き配管、ピエゾヘッドからなり、ピエゾヘッドは、１０ｐＬの液滴になるように電圧を印加し、解像度７２０ｄｐｉ×７２０ｄｐｉのベタ画像（１０ｃｍ×３０ｃｍ）または３ｐｔ明朝文字を印刷した。 Although not shown, the ink supply system consists of an ink tank, a supply pipe, a sub-ink tank in front of the head, piping with a filter, and a piezo head.The piezo head applies voltage to form droplets of 10 pL and has a resolution of 720 dpi. A solid image (10 cm x 30 cm) of ×720 dpi or 3pt Mincho characters were printed.
４．評価方法
（１）用紙変形（寸法安定性）
上記画像形成方法で記録したベタ画像について、下記の評価基準に従って目視評価により用紙変形の評価を行った。
〔評価基準〕
◎：印刷物に反りなし
〇：印刷物に若干の反りが見られるが、問題ない範囲
△：印刷物に反りが見られるが、許容範囲内
×：硬化物に反りが大きく、ＮＧレベル
4. Evaluation method (1) Paper deformation (dimensional stability)
Regarding the solid images recorded by the above image forming method, paper deformation was evaluated by visual evaluation according to the following evaluation criteria.
〔Evaluation criteria〕
◎: There is no warping on the printed matter. 〇: There is some warping on the printed matter, but it is not a problem. △: There is some warping on the printed matter, but it is within the acceptable range.
（２）密着性（記録材料への密着性評価）
画像ベタ印字部において、碁盤目テープ剥離残留付着試験（ＪＩＳ Ｋ ５４００の碁盤目試験）で得た硬化組成物試料に粘着テープ（スコッチ＃２５０、住友スリーエム社製）を張り合わせて２ｋｇのローラーで一往復圧着した後、一気に剥がし、残留している碁盤目状の試料の数を調査し、付着率を下記評価基準で評価し、密着性の指標の一つとした。△以上が実用上良好な範囲である。
〔評価基準〕
◎：付着残留率９５％以上１００％
○：付着残留率８０％以上９５％
△：付着残留率６０％以上８０％未満
×：付着残留率６０％未満
(2) Adhesion (evaluation of adhesion to recording materials)
In the solid image printing area, adhesive tape (Scotch #250, manufactured by Sumitomo 3M) was pasted onto the cured composition sample obtained in the grid tape peeling residual adhesion test (JIS K 5400 grid test) and rolled with a 2 kg roller. After reciprocating pressure bonding, the samples were peeled off at once, the number of remaining grid-shaped samples was investigated, and the adhesion rate was evaluated using the following evaluation criteria, which was used as an index of adhesion. A value of △ or higher is a practically good range.
〔Evaluation criteria〕
◎: Adhesion residual rate 95% or more 100%
○: Adhesion residual rate 80% or more 95%
△: Adhesive residual rate 60% or more and less than 80% ×: Adhesive residual rate less than 60%
（３）画質：濃度（裏抜け評価）
上記画像形成方法で記録したベタ画像について、光学濃度計（Ｘ－Ｒｉｔｅ社製９３８分光濃度計）を用いて、ベタ画像部の裏面濃度と同紙の非記録部の濃度も同様に測定し、
（ベタ画像部の裏面濃度）－（非画像部の濃度）を求め、下記の評価基準に従って濃度の評価を行った。
〔評価基準〕
◎：濃度差が０．０５未満である
○：濃度差が０．０５以上、０．０８未満である
△：濃度差が０．０８以上、０．１５未満である
×：濃度差が０．１５以上である
(3) Image quality: Density (bleed-through evaluation)
Regarding the solid image recorded by the above image forming method, using an optical densitometer (938 spectrodensitometer manufactured by X-Rite), the back side density of the solid image area and the density of the non-recorded area of the same paper were similarly measured,
(Back side density of solid image area) - (density of non-image area) was determined, and the density was evaluated according to the following evaluation criteria.
〔Evaluation criteria〕
◎: The density difference is less than 0.05. ○: The density difference is 0.05 or more and less than 0.08. △: The density difference is 0.08 or more and less than 0.15. ×: The density difference is 0.08 or more. 15 or more
（４）画質：面内ムラ防止性
上記画像形成方法で記録したベタ画像について、下記の評価基準に従って目視評価により濃度ムラの評価を行った。
〔評価基準〕
◎：１０ｃｍ離れた位置から観測して、画像に濃度ムラが認められない
○：１５ｃｍ離れた位置から観測して、画像に濃度ムラが認められない
△：１５ｃｍ離れた位置から観測すると、画像の一部において濃度ムラが認められるが、３０ｃｍ離した位置からは、濃度ムラが認められない
×：３０ｃｍ離した位置から観測して、濃度ムラが認められる
(4) Image quality: prevention of in-plane unevenness The solid images recorded by the above image forming method were evaluated for density unevenness by visual evaluation according to the following evaluation criteria.
〔Evaluation criteria〕
◎: No density unevenness is observed in the image when observed from a position 10cm away. ○: No density unevenness is observed in the image when observed from a position 15cm away. △: No density unevenness is observed in the image when observed from a position 15cm away. Density unevenness is observed in some areas, but no density unevenness is observed from a position 30cm away. ×: Density unevenness is observed when observed from a 30cm distance.
（５）画質：滲み防止性
上記画像形成方法で記録した３ｐｔ明朝文字について、下記の評価基準に従って目視評価によりにじみ防止性の評価を行った。
〔評価基準〕
◎：文字ににじみがなくはっきり再現されている。
○：ほぼ文字につぶれがなく再現されている。
△：一部の文字のつぶれがみられるが許容範囲内。
×：文字がつぶれている。
(5) Image quality: anti-bleeding properties The anti-bleeding properties of the 3pt Mincho characters recorded by the above image forming method were evaluated by visual evaluation according to the following evaluation criteria.
〔Evaluation criteria〕
◎: Characters are clearly reproduced without blurring.
○: Characters are almost completely reproduced without any distortion.
△: Some characters are blurred, but within the acceptable range.
×: Characters are crushed.
以上の結果を表１、２に示す。 The above results are shown in Tables 1 and 2.
５．評価
表１、２より、実施例１～２１は、比較例１～４との対比で、チタン紙上に画像記録する際に寸法安定性、密着性及び画質を向上できることがわかる。
5. Evaluation From Tables 1 and 2, it can be seen that Examples 1 to 21 can improve dimensional stability, adhesion, and image quality when recording images on titanium paper in comparison with Comparative Examples 1 to 4.
Claims (7)
前記樹脂として、酸価を有するブロック共重合体を用い、
前記ブロック共重合体は、ポリマー中に、アニオン性基を有する領域と、アニオン性基を有しない領域とが形成され、
前記両親媒性溶剤は、グリコール系溶剤、グリコールモノエーテル系溶剤及びグリコールジエーテル系溶剤から選択され、且つアルキル基を有しないか又は１分子中に含まれるアルキル基の合計炭素数が２以下であり、
前記水系インクジェットインクの全量に対して前記両親媒性溶剤を３５質量％以上含有することを特徴とするインクジェット記録方法。 An inkjet recording method for recording an image on titanium paper by an inkjet method using a water-based inkjet ink containing at least a coloring material, a resin, an amphipathic solvent, and water, the method comprising:
As the resin, a block copolymer having an acid value is used,
In the block copolymer, a region having an anionic group and a region having no anionic group are formed in the polymer,
The amphiphilic solvent is selected from glycol solvents, glycol monoether solvents, and glycol diether solvents, and does not have an alkyl group or has a total number of carbon atoms of alkyl groups in one molecule of 2 or less. can be,
An inkjet recording method, characterized in that the amphiphilic solvent is contained in an amount of 35% by mass or more based on the total amount of the aqueous inkjet ink.