JP7503307B2 - Manufacturing method of decorative body suitable for outdoor use and decorative body suitable for outdoor use - Google Patents
Manufacturing method of decorative body suitable for outdoor use and decorative body suitable for outdoor use Download PDFInfo
- Publication number
- JP7503307B2 JP7503307B2 JP2020187637A JP2020187637A JP7503307B2 JP 7503307 B2 JP7503307 B2 JP 7503307B2 JP 2020187637 A JP2020187637 A JP 2020187637A JP 2020187637 A JP2020187637 A JP 2020187637A JP 7503307 B2 JP7503307 B2 JP 7503307B2
- Authority
- JP
- Japan
- Prior art keywords
- recording medium
- medium sheet
- inkjet recording
- transparent resin
- receiving layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Description
本発明は、屋外使用に適した装飾体の製造方法及び屋外使用に適した装飾体に関する。 The present invention relates to a method for manufacturing a decorative body suitable for outdoor use and a decorative body suitable for outdoor use.
屋外使用の製品として、例えば、自転車、バイク、ドローン等の輸送機等があり、このような屋外使用の製品の表面には、絵、文字、模様等の装飾が施されている。従来、製品表面の装飾部をインクジェット印刷によって施すものが知られている（特許文献１）。 Examples of products for outdoor use include bicycles, motorbikes, drones and other transport vehicles, and the surfaces of such products for outdoor use are decorated with pictures, letters, patterns, etc. Conventionally, it is known to apply decorations to the surface of products by inkjet printing (Patent Document 1).
屋外使用の製品は、日光、雨等に晒されることが多い。インクジェット印刷用インキとしての染料系インキは、発色の繊細さ再現性に優れるが、日光、雨等に晒されると変色、退色等しやすく、耐光性、耐水性に劣るため、屋外使用の製品の装飾に使用するには不向きであった。 Products for outdoor use are often exposed to sunlight, rain, etc. Dye-based inks for inkjet printing have excellent color reproducibility and subtlety, but they are prone to discoloration and fading when exposed to sunlight, rain, etc., and have poor light and water resistance, making them unsuitable for use in decorating products for outdoor use.
本発明は、以上の事情に鑑みてなされたものであり、その目的は、装飾部の形成にインクジェット印刷用インキとして染料系インキを使用しても、装飾部が屋外使用に十分に耐える機能を備える、屋外使用に適した装飾体の製造方法及び屋外使用に適した装飾体を提供することである。 The present invention has been made in consideration of the above circumstances, and its purpose is to provide a manufacturing method for a decorative body suitable for outdoor use, in which the decorative part has a function sufficient to withstand outdoor use, even when a dye-based ink is used as the inkjet printing ink to form the decorative part, and a decorative body suitable for outdoor use.
本発明に係る装飾体の製造方法は、
輸送機の製品部材である三次元形状を有する金属部材にインクジェット印刷用の染料系インキよりなる色材で装飾部が施された輸送機における装飾体の製造方法であって、
前記金属部材の表面にアルマイト処理を施して防錆層を形成する工程と、
防錆層上に紫外線防止剤を含有する透明樹脂受容層を形成する工程と、
吸水分散性を備えたインクジェット記録用媒体シートにインクジェット印刷により所定の装飾部を施すための染料系インキよりなる色材を内部に入り込ませ、このインクジェット記録用媒体シートを透明樹脂受容層の表面に重ね合わせる工程と、
加熱加圧によりインクジェット記録用媒体シートから色材を昇華させて透明樹脂受容層の内部に入り込ませて定着させる工程と、
色材転写後のインクジェット記録用媒体シートを除去する工程と、
インクジェット記録用媒体シートを除去した透明樹脂受容層上に、耐光性、耐水性及び耐擦傷性を備えた透明なハードコート層を形成する工程と、から構成され、
前記インクジェット記録用媒体シートには、前記金属部材の三次元形状を二次元化した印刷データに基づいて装飾部が印刷されており、
前記インクジェット記録用媒体シートは、細孔が多数形成されている多孔質アルミナ微粒子を基材樹脂に含有する多孔質シートであり、色材である染料系インキ中の溶媒が吸収され色素成分が内部に保持されて色材がドット径の拡大を抑えた状態で保持されており、
前記加熱加圧の工程は、加圧によりインクジェット記録用媒体シートを金属部材の三次元形状にならって透明樹脂受容層に密着させて、加熱によりインクジェット記録用媒体シートに保持された色材がドット径の拡大を抑えた状態で透明樹脂受容層に転写されるように構成されており、
前記透明なハードコート層は、紫外線硬化型樹脂又は熱硬化型樹脂から形成されており、紫外線防止剤と、シリカ、金属又は金属酸化物の微粒子と、酸化防止剤とが含有されている、構成とする。
前記輸送機は、例えば、自転車、バイク又はドローンである。
The method for producing a decorative body according to the present invention comprises the steps of:
A method for manufacturing a decorative body in a transport aircraft, in which a decorative part is applied to a metal member having a three-dimensional shape, which is a product component of the transport aircraft, with a color material made of a dye-based ink for inkjet printing,
A step of forming an anti-rust layer by performing an anodizing treatment on the surface of the metal member;
forming a transparent resin receiving layer containing an ultraviolet inhibitor on the anticorrosive layer ;
A step of impregnating a water-absorbent, water-dispersible ink-jet recording medium sheet with a dye-based ink for forming a desired decorative portion by ink-jet printing, and then laminating the ink-jet recording medium sheet on the surface of a transparent resin receiving layer;
A step of sublimating the color material from the inkjet recording medium sheet by applying heat and pressure, and causing the color material to penetrate into the transparent resin receiving layer and be fixed therein;
removing the inkjet recording medium sheet after the coloring material has been transferred ;
forming a transparent hard coat layer having light resistance, water resistance and scratch resistance on the transparent resin receiving layer from which the inkjet recording medium sheet has been removed;
a decorative portion is printed on the inkjet recording medium sheet based on print data that has been converted from a three-dimensional shape of the metal member;
The inkjet recording medium sheet is a porous sheet containing porous alumina fine particles having a large number of pores formed in a base resin, and the solvent in the dye-based ink, which is a coloring material, is absorbed, and the coloring matter is retained inside the sheet, thereby suppressing the enlargement of the dot diameter of the coloring material.
The heating and pressing step is configured to apply pressure to bring the inkjet recording medium sheet into close contact with the transparent resin receiving layer in accordance with the three-dimensional shape of the metal member, and to transfer the color material held on the inkjet recording medium sheet to the transparent resin receiving layer by heating while suppressing the enlargement of the dot diameter,
The transparent hard coat layer is made of an ultraviolet curable resin or a thermosetting resin, and contains an ultraviolet inhibitor, fine particles of silica, metal or metal oxide, and an antioxidant .
The vehicle may be, for example, a bicycle, a motorbike, or a drone .
以上のように、本発明によれば、装飾部となる色材の染料系インキを紫外線防止剤を含有する透明樹脂受容層の内部に入り込んで定着させるので、染料系インキによる装飾部に対して、紫外線による変色、退色等を防止でき、耐光性を向上することができる。また、色材を透明樹脂受容層の内部に定着させることにより、装飾部に対して耐水性を向上することができる。また、透明樹脂受容層上に透明なハードコート層を形成することにより、装飾部に対して、耐光性、耐水性及び耐擦傷性を向上することができる。従って、色材にインクジェット印刷用インキとして染料系インキを使用しても、屋外使用に十分に耐える機能を備える屋外使用装飾体が得られる。 As described above, according to the present invention, the dye-based ink of the color material for the decorative portion penetrates and is fixed inside the transparent resin receiving layer containing an ultraviolet inhibitor, so that the decorative portion made of the dye-based ink can be prevented from discoloration and fading due to ultraviolet rays, and light resistance can be improved. Furthermore, by fixing the color material inside the transparent resin receiving layer, the water resistance of the decorative portion can be improved. Furthermore, by forming a transparent hard coat layer on the transparent resin receiving layer, the light resistance, water resistance, and scratch resistance of the decorative portion can be improved. Therefore, even if a dye-based ink is used as the color material for inkjet printing ink, a decorative body for outdoor use that has sufficient functionality to withstand outdoor use can be obtained.
また、吸水分散性を備えたインクジェット記録用媒体シートを介して染料系インキの装飾部を転写形成することにより、再現性に優れ、鮮明かつ高解像度に、フルカラーの装飾部を形成することができる。インクジェット記録用媒体シートに部材の三次元形状を二次元化した印刷データに基づいて印刷し、このインクジェット記録用媒体シートにより三次元形状の部材に装飾部を転写形成することにより、三次元形状の部材に対しても簡単に良好な装飾部を形成することができる。 In addition, by transferring and forming a decorative portion using dye-based ink via an inkjet recording medium sheet that has water absorption and dispersibility, a full-color decorative portion can be formed that is clear, high-resolution, and has excellent reproducibility. By printing the three-dimensional shape of a component on an inkjet recording medium sheet based on print data that has been converted into two dimensions, and then transferring and forming a decorative portion on a three-dimensional component using this inkjet recording medium sheet, a good decorative portion can be easily formed even on a three-dimensional component.
以下に、本発明の実施形態について説明する。
図１に示す屋外使用装飾体１は、自転車の車体フレームに適用したものであり、車体フレームの金属部材（アルミ）上に、防錆層１１、透明樹脂受容層１２、透明ハードコート層１３がこの順に形成されたものである。なお、本発明は、自転車の車体フレームに限らず、自転車の他の部材、また、バイク、ドローン等の輸送機等、様々な屋外使用の製品部材に適用することができる。
Hereinafter, an embodiment of the present invention will be described.
The decorative body 1 for outdoor use shown in Fig. 1 is applied to a bicycle body frame, and an anti-rust layer 11, a transparent resin receiving layer 12, and a transparent hard coat layer 13 are formed in this order on the metal member (aluminum) of the body frame. Note that the present invention is not limited to bicycle body frames, but can be applied to other bicycle members, as well as various product members for outdoor use, such as motorbikes, drones, and other transport vehicles.
透明樹脂受容層１２には、その内部に、インクジェット印刷用の染料系インキよりなる色材２１が入り込んで定着した所定の装飾部２が形成されている。透明樹脂受容層１２の材料は、ウレタン系樹脂が使用されるが、これに限らず、例えば、アクリル系樹脂、ポリエステル系樹脂等を使用することができる。 The transparent resin receiving layer 12 has a predetermined decorative portion 2 formed therein, in which a color material 21 made of a dye-based ink for inkjet printing has penetrated and been fixed. The material used for the transparent resin receiving layer 12 is a urethane-based resin, but is not limited to this, and other materials such as acrylic resin, polyester resin, etc. can also be used.
透明樹脂受容層１２には、紫外線防止剤が含有されている。これにより、装飾部２の色材２１に染料系インキを使用しても、紫外線による変色、退色等を防止でき、耐光性を良好に付与できる。 The transparent resin receiving layer 12 contains an ultraviolet light inhibitor. This prevents discoloration and fading caused by ultraviolet light, even if dye-based ink is used for the color material 21 of the decorative part 2, and provides good light resistance.
透明ハードコート層１３にも、紫外線防止剤が含有されて耐光性が付与されている。
これにより、透明樹脂受容層１２の内部の色材２１に対して、透明樹脂受容層１２と透明樹脂受容層１２の表面を覆う透明ハードコート層１３とによって紫外線カットによる耐光性をさらに向上することができる。従って、色材２１にインクジェット印刷用インキとして染料系インキを使用しても、紫外線による変色、退色等を防止でき、屋外使用に十分に耐える機能を備える屋外使用装飾体が得られる。
The transparent hard coat layer 13 also contains an ultraviolet inhibitor to impart light resistance.
As a result, the color material 21 inside the transparent resin receiving layer 12 can be further improved in light resistance by blocking ultraviolet rays through the transparent resin receiving layer 12 and the transparent hard coat layer 13 covering the surface of the transparent resin receiving layer 12. Therefore, even if a dye-based ink is used as the ink for inkjet printing for the color material 21, discoloration, fading, etc. due to ultraviolet rays can be prevented, and a decorative body for outdoor use having a function sufficient to withstand outdoor use can be obtained.
前記紫外線防止剤とは、紫外線吸収剤又は紫外線散乱剤をいう。紫外線吸収剤は、紫外線を吸収し、装飾部２を形成する色材２１に対して紫外線の影響を防ぐものであり、例えば、メトキシケイヒ酸オクチル、メトキシケイヒ酸エチルヘキシル、ジメチルＰＡＢＡオクチル、ジメチルＰＡＢＡエチルヘキシル、ｔ－ブチルメトキシジベンゾイルメタン等が例示される。紫外線散乱剤は、紫外線を乱反射させて、装飾部２を形成する色材２１に対して紫外線の影響を防ぐものであり、例えば、酸化亜鉛、酸化チタン等が例示される。紫外線散乱剤として、酸化亜鉛、酸化チタン等の粉体を使用する場合は白浮きしやすいことから、装飾部２が濁って見えることがないよう上層の透明樹脂保護層１３には使用しない方が好ましく、一方、装飾部２を内部に定着させた透明樹脂受容層１２に対して紫外線散乱剤を含有させた場合は、白浮きにより装飾部２の色を際立たせることができる。 The ultraviolet protection agent refers to an ultraviolet absorbing agent or an ultraviolet scattering agent. The ultraviolet absorbing agent absorbs ultraviolet rays and prevents the color material 21 forming the decorative part 2 from being affected by ultraviolet rays. Examples of the ultraviolet absorbing agent include octyl methoxycinnamate, ethylhexyl methoxycinnamate, octyl dimethyl PABA, ethylhexyl dimethyl PABA, and t-butyl methoxydibenzoylmethane. The ultraviolet scattering agent diffuses ultraviolet rays and prevents the color material 21 forming the decorative part 2 from being affected by ultraviolet rays. Examples of the ultraviolet scattering agent include zinc oxide and titanium oxide. When using powder such as zinc oxide or titanium oxide as an ultraviolet scattering agent, it is easy to cause whitening, so it is preferable not to use it in the upper transparent resin protective layer 13 so that the decorative part 2 does not look cloudy. On the other hand, when an ultraviolet scattering agent is contained in the transparent resin receiving layer 12 in which the decorative part 2 is fixed, the color of the decorative part 2 can be highlighted by whitening.
透明ハードコート層１３は、紫外線吸収剤の含有による耐光性に加え、耐水性及び耐擦傷性を備える。この透明ハードコート層１３は、鉛筆硬度がＨ以上有するものである。透明ハードコート層１３の材料には、アクリル系樹脂、ウレタン系樹脂、メラミン系樹脂、エポキシ系樹脂、有機シリケート化合物、シリコーン系樹脂等を使用することができる。中でも、硬度と耐久性等の点では、シリコーン系樹脂やアクリル系樹脂を使用するのが好ましい。透明ハードコート層１３は、硬化性、可撓性及び生産性の点で、紫外線硬化型樹脂又は熱硬化型樹脂が使用されるが、形成が容易なことから紫外線硬化型樹脂を使用するのが好ましい。また、透明ハードコート層１３には、シリカ微粒子、金属、金属酸化物等の微粒子を含有させることができ、これにより、耐擦傷性をさらに向上することができる。また、透明ハードコート層１３には、酸化防止剤を含有させることができ、これにより、耐候性を向上することができる。 The transparent hard coat layer 13 has water resistance and scratch resistance in addition to light resistance due to the inclusion of an ultraviolet absorber. This transparent hard coat layer 13 has a pencil hardness of H or more. The transparent hard coat layer 13 can be made of acrylic resins, urethane resins, melamine resins, epoxy resins, organic silicate compounds, silicone resins, etc. Among them, in terms of hardness and durability, it is preferable to use silicone resins or acrylic resins. In terms of curability, flexibility, and productivity, ultraviolet curable resins or thermosetting resins are used for the transparent hard coat layer 13, but it is preferable to use ultraviolet curable resins because they are easy to form. In addition, the transparent hard coat layer 13 can contain silica fine particles, metal, metal oxide fine particles, etc., which can further improve scratch resistance. In addition, the transparent hard coat layer 13 can contain an antioxidant, which can improve weather resistance.
次に、製造方法について説明する。
図２を参照して、まず、金属部材１０の表面にアルマイト処理を施して防錆層１１を形成し、次いで、防錆層１１上に紫外線防止剤を含有する透明樹脂からなる塗料を塗布して、透明樹脂受容層１２を形成する（図２（ａ）参照）。なお、金属部材１０でなくプラスチック製の部材の場合は、防錆層１１を形成しなくてもよい。前記透明樹脂塗料の塗布方法としては、例えば、はけ塗り、ローラー塗り等の直接法、エアースプレー塗り、エアーレススプレー塗り等の噴霧法、他にコータ法など、様々な塗装方法により実施できる。
Next, the manufacturing method will be described.
2, first, the surface of the metal member 10 is anodized to form an anti-rust layer 11, and then a paint made of a transparent resin containing an ultraviolet inhibitor is applied onto the anti-rust layer 11 to form a transparent resin receiving layer 12 (see FIG. 2(a)). In the case of a plastic member instead of the metal member 10, it is not necessary to form the anti-rust layer 11. The transparent resin paint can be applied by various coating methods, for example, direct methods such as brush coating and roller coating, spray methods such as air spray coating and airless spray coating, and coater methods.
透明樹脂受容層１２の形成後、透明樹脂受容層１２の表面に、色材２１を内部に入り込ませたインクジェット記録用媒体シート２０を重ね合わせる（図２（ｂ）参照）。インクジェット記録用媒体シート２０は、基材シートに色材２１のインクジェット印刷用インキに染料系インキを用いてインクジェット印刷することで所定の装飾部２を形成したものである。インクジェット印刷に使用するインクジェット印刷機は、複数色（例えば、マゼンタ、シアン、イエロー、ブラック等）のインキを噴射するプリンタヘッドを有し、フルカラー印刷できるものである。 After the transparent resin receiving layer 12 is formed, an inkjet recording medium sheet 20 with color material 21 embedded therein is superimposed on the surface of the transparent resin receiving layer 12 (see FIG. 2(b)). The inkjet recording medium sheet 20 is formed by inkjet printing a base sheet with a dye-based ink as the inkjet printing ink for the color material 21 to form a predetermined decorative portion 2. The inkjet printer used for inkjet printing has a printer head that sprays inks of multiple colors (e.g., magenta, cyan, yellow, black, etc.) and is capable of full-color printing.
インクジェット記録用媒体シート２０の基材シートは、例えば、直線的な細孔が形成されている多孔質アルミナ微粒子を基材樹脂に含有させた多孔質シート等が使用される。この多孔質シートは、吸水分散性、すなわち色材２１のインキを素早く吸収してインクジェットのドットの拡散を防ぐ性質を備えたものである。インクジェットプリンタのプリンタヘッドから噴射された染料系インキよりなる色材２１は、多孔質の基材シートの内部まで浸透して保持される。このとき、インキ中の溶媒（水分）がインクジェット記録用媒体シート２０に吸収されながら色素成分が内部に保持される（図３（ａ）参照）。これにより、インクジェット記録用媒体シート２０におけるインクジェットのドット径の拡大を抑えることができる。従って、インクジェット記録用媒体シート２０には、フルカラーの装飾部２が鮮明かつ高解像度に形成される。 The base sheet of the inkjet recording medium sheet 20 is, for example, a porous sheet containing porous alumina fine particles with linear pores in the base resin. This porous sheet has water absorption and dispersibility, that is, the property of quickly absorbing the ink of the coloring material 21 and preventing the diffusion of the inkjet dots. The coloring material 21 made of dye-based ink sprayed from the printer head of the inkjet printer penetrates into the interior of the porous base sheet and is retained therein. At this time, the solvent (moisture) in the ink is absorbed by the inkjet recording medium sheet 20 while the pigment component is retained inside (see FIG. 3(a)). This makes it possible to suppress the expansion of the inkjet dot diameter in the inkjet recording medium sheet 20. Therefore, the full-color decorative portion 2 is formed on the inkjet recording medium sheet 20 with clear and high resolution.
次いで、透明樹脂受容層１２の表面にインクジェット記録用媒体シート２０を重ね合わせた積層体を加熱加圧する。加熱加圧には、例えば、ホットプレスを用いることができる。加圧により、インクジェット記録用媒体シート２０が基材の形状にならって密着される。従って、基材の３Ｄ形状にもならってインクジェット記録用媒体シート２０が密着される。加熱により、インクジェット記録用媒体シート２０の内部に保持された色材２１の染料系インキが昇華して透明樹脂受容層１２の内部に入り込む（図２（ｃ）参照）。このとき、インクジェット記録用媒体シート２０には、装飾部２の色材２１がドット径の拡大を抑えた状態で保持されている（図３（ｂ）参照）。これにより、色材２１の染料系インキが昇華により透明樹脂受容層１２に転写されるときのドット径も拡大を抑えた状態で透明樹脂受容層１２の内部に入り込ませることができる。従って、透明樹脂受容層１２には、フルカラーの装飾部２が鮮明かつ高解像度に転写形成される。そして、加熱加圧の終了後、色材転写後のインクジェット記録用媒体シート２０を剥がして基材の透明樹脂受容層１２上から除去する。 Next, the laminate in which the inkjet recording medium sheet 20 is superimposed on the surface of the transparent resin receiving layer 12 is heated and pressed. For example, a hot press can be used for the heating and pressing. By pressing, the inkjet recording medium sheet 20 is adhered to the shape of the substrate. Therefore, the inkjet recording medium sheet 20 is adhered to the substrate in accordance with the 3D shape of the substrate. By heating, the dye-based ink of the color material 21 held inside the inkjet recording medium sheet 20 sublimes and penetrates into the transparent resin receiving layer 12 (see FIG. 2(c)). At this time, the inkjet recording medium sheet 20 holds the color material 21 of the decorative portion 2 in a state in which the dot diameter is suppressed from expanding (see FIG. 3(b)). As a result, the dye-based ink of the color material 21 can be transferred to the transparent resin receiving layer 12 by sublimation and can be allowed to penetrate into the transparent resin receiving layer 12 in a state in which the dot diameter is also suppressed from expanding. Therefore, the full-color decorative portion 2 is transferred and formed on the transparent resin receiving layer 12 with clarity and high resolution. After the heating and pressing are completed, the inkjet recording medium sheet 20 after the colorant transfer is peeled off and removed from the transparent resin receiving layer 12 of the substrate.
次いで、透明樹脂受容層１２上に透明ハードコート層１３の形成用塗料を塗布して、透明ハードコート層１３を形成する（図２（ｄ）参照）。透明ハードコート層１３の形成用塗料としては、例えば、紫外線照射によって硬化するとともに含有成分の紫外線防止剤その他の機能剤が有機骨格に結合する樹脂材料と、光開始剤とを有機溶媒又は水に溶解させた塗料を使用するのが好ましい。透明ハードコート層１３の形成用塗料の塗布方法としては、例えば、はけ塗り、ローラー塗り等の直接法、エアースプレー塗り、エアーレススプレー塗り等の噴霧法、他にコータ法など、様々な塗装方法により実施できる。そして、透明ハードコート層１３の形成用塗料を透明樹脂受容層１２上に塗布した後、紫外線照射を行うことにより、透明ハードコート層１３を形成することができる。
以上で、インクジェット印刷用の染料系インキよりなる色材２１で装飾部２が施された屋外使用装飾体１が完成する。
Next, a coating material for forming the transparent hard coat layer 13 is applied onto the transparent resin receiving layer 12 to form the transparent hard coat layer 13 (see FIG. 2(d)). As the coating material for forming the transparent hard coat layer 13, for example, a coating material in which a resin material that is cured by ultraviolet irradiation and contains an ultraviolet inhibitor and other functional agents that are bonded to an organic skeleton, and a photoinitiator are dissolved in an organic solvent or water, is preferably used. The coating material for forming the transparent hard coat layer 13 can be applied by various coating methods, such as direct methods such as brush coating and roller coating, spraying methods such as air spray coating and airless spray coating, and coater methods. Then, the coating material for forming the transparent hard coat layer 13 is applied onto the transparent resin receiving layer 12, and then ultraviolet irradiation is performed to form the transparent hard coat layer 13.
With the above steps, an outdoor decorative article 1 is completed, in which the decorative portion 2 is applied with a color material 21 made of a dye-based ink for ink-jet printing.
以上のように、本実施形態によれば、装飾部２となる色材２１の染料系インキを紫外線防止剤を含有する透明樹脂受容層１２の内部に入り込んで定着させるので、染料系インキによる装飾部２に対して、紫外線による変色、退色等を防止でき、耐光性を向上することができる。また、色材２１を透明樹脂受容層１２の内部に定着させることにより、装飾部２に対して耐水性を向上することができる。また、透明樹脂受容層１２上に透明ハードコート層１３を形成することにより、装飾部２に対して、耐光性、耐水性及び耐擦傷性を向上することができる。従って、色材２１にインクジェット印刷用インキとして染料系インキを使用しても、屋外使用に十分に耐える機能を備える屋外使用装飾体１が得られる。 As described above, according to this embodiment, the dye-based ink of the color material 21 that becomes the decorative part 2 penetrates and is fixed inside the transparent resin receiving layer 12 containing an ultraviolet inhibitor, so that the dye-based ink decorative part 2 can be prevented from discoloring or fading due to ultraviolet rays, and light resistance can be improved. In addition, by fixing the color material 21 inside the transparent resin receiving layer 12, the water resistance of the decorative part 2 can be improved. In addition, by forming a transparent hard coat layer 13 on the transparent resin receiving layer 12, the light resistance, water resistance, and scratch resistance of the decorative part 2 can be improved. Therefore, even if a dye-based ink is used as the inkjet printing ink for the color material 21, an outdoor decorative body 1 that has a function sufficient to withstand outdoor use can be obtained.
また、吸水分散性を備えたインクジェット記録用媒体シート２０を介して染料系インキの装飾部２を転写形成することにより、再現性に優れ、鮮明かつ高解像度に、フルカラーの装飾部２を形成することができる。 In addition, by transferring the dye-based ink decorative portion 2 onto the inkjet recording medium sheet 20 that has water-absorbent and dispersible properties, it is possible to form a full-color decorative portion 2 with excellent reproducibility, clarity, and high resolution.
また、曲面等の三次元形状を有する部材に対してインクジェット印刷機で印刷する場合はプリンタヘッドを三次元形状に沿って動かす制御が複雑であり、また液だれ等のおそれもあるが、インクジェット記録用媒体シート２０に部材の三次元形状を二次元化した印刷データに基づいて印刷し、このインクジェット記録用媒体シート２０により三次元形状の部材に装飾部２を転写形成することにより、三次元形状の部材に対しても簡単に良好な装飾部２を形成することができる。 When printing on a component with a three-dimensional shape such as a curved surface using an inkjet printer, controlling the printer head to move along the three-dimensional shape is complicated, and there is also the risk of dripping. However, by printing on an inkjet recording medium sheet 20 based on print data that has been converted from the three-dimensional shape of the component, and then transferring and forming the decorative portion 2 onto the three-dimensional component using this inkjet recording medium sheet 20, it is possible to easily form a good decorative portion 2 even on a component with a three-dimensional shape.
なお、本発明は、前記実施形態に限定されるものではなく、特許請求の範囲の記載内で様々な変更を施すことが可能である。 The present invention is not limited to the above-described embodiment, and various modifications are possible within the scope of the claims.
１ 屋外使用装飾体
２ 装飾部
１０ 金属部材
１１ 防錆層
１２ 透明樹脂受容層
１３ 透明ハードコート層
２０ インクジェット記録用媒体シート
２１ 色材（染料系インキ）
1 Outdoor decorative body 2 Decorative part 10 Metal member 11 Anti-rust layer 12 Transparent resin receiving layer 13 Transparent hard coat layer 20 Inkjet recording medium sheet 21 Coloring material (dye-based ink)
Claims (2)
前記金属部材の表面にアルマイト処理を施して防錆層を形成する工程と、
防錆層上に紫外線防止剤を含有する透明樹脂受容層を形成する工程と、
吸水分散性を備えたインクジェット記録用媒体シートにインクジェット印刷により所定の装飾部を施すための染料系インキよりなる色材を内部に入り込ませ、このインクジェット記録用媒体シートを透明樹脂受容層の表面に重ね合わせる工程と、
加熱加圧によりインクジェット記録用媒体シートから色材を昇華させて透明樹脂受容層の内部に入り込ませて定着させる工程と、
色材転写後のインクジェット記録用媒体シートを除去する工程と、
インクジェット記録用媒体シートを除去した透明樹脂受容層上に、耐光性、耐水性及び耐擦傷性を備えた透明なハードコート層を形成する工程と、から構成され、
前記インクジェット記録用媒体シートには、前記金属部材の三次元形状を二次元化した印刷データに基づいて装飾部が印刷されており、
前記インクジェット記録用媒体シートは、細孔が多数形成されている多孔質アルミナ微粒子を基材樹脂に含有する多孔質シートであり、色材である染料系インキ中の溶媒が吸収され色素成分が内部に保持されて色材がドット径の拡大を抑えた状態で保持されており、
前記加熱加圧の工程は、加圧によりインクジェット記録用媒体シートを金属部材の三次元形状にならって透明樹脂受容層に密着させて、加熱によりインクジェット記録用媒体シートに保持された色材がドット径の拡大を抑えた状態で透明樹脂受容層に転写されるように構成されており、
前記透明なハードコート層は、紫外線硬化型樹脂又は熱硬化型樹脂から形成されており、紫外線防止剤と、シリカ、金属又は金属酸化物の微粒子と、酸化防止剤とが含有されている、装飾体の製造方法。 A method for manufacturing a decorative body in a transport aircraft, in which a decorative part is applied to a metal member having a three-dimensional shape, which is a product component of the transport aircraft, with a color material made of a dye-based ink for inkjet printing,
A step of forming an anti-rust layer by performing an anodizing treatment on the surface of the metal member;
forming a transparent resin receiving layer containing an ultraviolet inhibitor on the anticorrosive layer ;
A step of impregnating a water-absorbent, water-dispersible ink-jet recording medium sheet with a dye-based ink for forming a desired decorative portion by ink-jet printing, and then laminating the ink-jet recording medium sheet on the surface of a transparent resin receiving layer;
A step of sublimating the color material from the inkjet recording medium sheet by applying heat and pressure, and causing the color material to penetrate into the transparent resin receiving layer and be fixed therein;
removing the inkjet recording medium sheet after the coloring material has been transferred ;
forming a transparent hard coat layer having light resistance, water resistance and scratch resistance on the transparent resin receiving layer from which the inkjet recording medium sheet has been removed;
a decorative portion is printed on the inkjet recording medium sheet based on print data that has been converted from a three-dimensional shape of the metal member;
The inkjet recording medium sheet is a porous sheet containing porous alumina fine particles having a large number of pores formed in a base resin, and the solvent in the dye-based ink, which is a coloring material, is absorbed, and the coloring matter is retained inside the sheet, thereby suppressing the enlargement of the dot diameter of the coloring material.
The heating and pressing step is configured to apply pressure to bring the inkjet recording medium sheet into close contact with the transparent resin receiving layer in accordance with the three-dimensional shape of the metal member, and to transfer the color material held on the inkjet recording medium sheet to the transparent resin receiving layer by heating while suppressing the enlargement of the dot diameter,
The transparent hard coat layer is formed from an ultraviolet curable resin or a thermosetting resin, and contains an ultraviolet inhibitor, fine particles of silica, metal or metal oxide, and an antioxidant .