JP7567333B2 - Gas barrier laminate and packaging bag - Google Patents

Description

The present invention relates to a gas barrier laminate and a packaging bag.

In many fields, including food, beverages, pharmaceuticals, and chemicals, packaging materials are used according to the contents. Packaging materials are required to have gas barrier properties that prevent the permeation of oxygen and water vapor, which can cause deterioration of the contents.

In recent years, there has been a growing trend to move away from plastic due to growing environmental awareness sparked by the problem of marine plastic waste. From the perspective of reducing the amount of plastic material used, the use of paper instead of plastic materials has been considered in various fields. For example, the following Patent Document 1 discloses a gas barrier laminate in which a barrier layer is laminated on paper.

JP 2020-62973 A

Paper has the characteristic of being easy to process because it has crease retention (also called dead-hold property). However, according to the inventors' research, it has been found that there is still room for improvement in that cracks occur in the barrier layer and the gas barrier properties decrease when packaging bags with sharper creases (pillow packaging, three-sided seal packaging, and gusset packaging).

In addition, from the perspective of the Law for Promoting Effective Utilization of Resources, there is a demand to reduce the amount of plastic materials used in gas barrier laminates as well.

The present invention was made in consideration of the above-mentioned circumstances, and aims to provide a gas barrier laminate that has the crease retention characteristic of paper, has sufficient gas barrier properties even after being folded, and contributes to reducing the amount of plastic material used, as well as a packaging bag that includes the gas barrier laminate.

The present invention provides a gas barrier laminate comprising, in this order, a paper substrate, a first resin layer, a first vapor deposition layer, a second resin layer, a second vapor deposition layer, and a third resin layer.

The third resin layer may be a layer containing a polyolefin having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester.

At least one of the first and second vapor deposition layers may be an aluminum vapor deposition layer having a thickness of 30 nm or more and 100 nm or less.

At least one of the first and second vapor deposition layers may be a silicon oxide or aluminum oxide vapor deposition film.

The thickness of the paper substrate may be 30 μm or more and 100 μm or less, and the thickness of the paper substrate may be 60% or more of the total thickness of the gas barrier laminate.

The present invention also provides a packaging bag including the gas barrier laminate according to the present invention.

The packaging bag may have a folded portion.

The present invention provides a gas barrier laminate that has the crease retention characteristic of paper, has sufficient gas barrier properties even after being folded, and contributes to reducing the amount of plastic material used, as well as a packaging bag that includes the gas barrier laminate.

1 is a schematic cross-sectional view showing a gas barrier laminate according to one embodiment of the present invention. FIG. 1 is a perspective view showing a package according to an embodiment of the present invention.

Below, an embodiment of the present invention will be described in detail, with reference to the drawings where necessary. However, the present invention is not limited to the following embodiment.

<Gas Barrier Laminate>
1 is a schematic cross-sectional view showing a gas barrier laminate according to one embodiment. The gas barrier laminate 10 according to one embodiment includes a paper substrate 1, a first resin layer 2, a first vapor-deposited layer 3, a second resin layer 4, a second vapor-deposited layer 5, and a third resin layer 6, in this order.

[Paper base material]
The paper substrate 1 is not particularly limited and may be appropriately selected depending on the application of the packaging material to which the gas barrier laminate 10 is applied. Specific examples of the paper substrate 1 include fine paper, special fine paper, coated paper, art paper, cast coated paper, glassine paper, imitation paper, and kraft paper. The thickness of the paper substrate 1 may be, for example, 20 μm or more and 200 μm or less, or 30 μm or more and 100 μm or less. The thickness of the paper substrate may be 60% or more, or 70% or more of the thickness of the entire gas barrier laminate. If the thickness of the paper substrate is 60% or more of the thickness of the entire gas barrier laminate, it can be said that the environmental compatibility is excellent.

The paper base material 1 may have a coating layer at least on the side that contacts the first resin layer 2 described below. The coating layer can prevent the first resin layer 2 from soaking into the paper, and can also fill in the unevenness of the paper, allowing the first resin layer 2 to be formed uniformly without defects. The coating layer may contain various types of copolymers such as styrene-butadiene, styrene-acrylic, and ethylene-vinyl acetate, polyvinyl alcohol resin, cellulose resin, paraffin (wax), etc. as binder resins, and may contain clay, kaolin, calcium carbonate, talc, mica, etc. as fillers.

The thickness of the coating layer is not particularly limited, but may be, for example, 1 μm to 10 μm, or 3 μm to 8 μm.

The weight of the paper is preferably 50% by mass or more, more preferably 70% by mass or more, and even more preferably 80% by mass or more, based on the weight of the entire gas barrier laminate. If the weight of the paper is 50% by mass or more based on the weight of the entire gas barrier laminate, the amount of plastic material used can be sufficiently reduced, the entire gas barrier laminate can be said to be made of paper, and the recyclability is excellent.

[First resin layer]
The first resin layer 2 is provided on the surface of the paper substrate, and is provided to improve adhesion between the paper substrate 1 and the first deposition layer 3 described below, to smooth the surface of the first deposition layer 3, and to prevent the first deposition layer from cracking due to bending. Materials constituting the first resin layer 2 include polyolefin-based emulsions, silane coupling agents, organic titanates, polyacrylics, polyesters, polyurethanes, polycarbonates, polyureas, polyamides, polyimides, melamines, phenols, and polyvinyl alcohol-based resins. Among these, polyolefin-based emulsions are preferred in terms of water vapor barrier properties, bending resistance, and adhesion to the first deposition layer 3.

From the viewpoint of adhesion to the first deposition layer 3, the polyolefin emulsion is preferably a polyolefin having at least one selected from, for example, a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester. By including such a polyolefin, a dense film is formed due to hydrogen bonds of the carboxyl group, aggregation due to metal ions of the ionomer, and crystallinity of the polyolefin, and the barrier properties are excellent. Such a first resin layer 2 has excellent flexibility and can suppress cracking of the first deposition layer 3 described later after bending (folding). The smaller the particle size of the polyolefin emulsion, the better, and specifically, it may be 1 μm or less, 0.7 μm or less, or 0.5 μm or less. The lower limit of the average particle size of the first polyolefin is not particularly limited, but may be, for example, 1 nm or more. As a result, the coating surface after drying becomes smooth, the deposition surface becomes uniform, and the initial barrier properties are ensured.

The thickness of the first resin layer 2 may be, for example, 1 μm or more and 20 μm or less. If the thickness is 1 μm or more, the unevenness of the paper is filled in, and the deposition layer can be laminated evenly. Furthermore, if the thickness is 20 μm or less, costs can be reduced.

The first resin layer 2 can be provided by applying a coating liquid containing the first resin layer and a solvent onto a paper substrate and drying it. Examples of the solvent contained in the coating liquid include water, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-propyl alcohol, n-butyl alcohol, n-pentyl alcohol, dimethyl sulfoxide, dimethylformamide, dimethylacetamide, toluene, hexane, heptane, cyclohexane, acetone, methyl ethyl ketone, diethyl ether, dioxane, tetrahydrofuran, ethyl acetate, and butyl acetate. These solvents may be used alone or in combination of two or more. Among these, from the viewpoint of characteristics, methyl alcohol, ethyl alcohol, isopropyl alcohol, toluene, ethyl acetate, methyl ethyl ketone, and water are preferred. From the viewpoint of the environment, methyl alcohol, ethyl alcohol, isopropyl alcohol, and water are preferred. The coating liquid may also contain additives such as surfactants, preservatives, storage stabilizers, silane coupling agents, organic titanates, and defoamers.

[First deposition layer]
The first deposited layer 3 is a layer formed by depositing a metal or an inorganic oxide, and serves to provide a water vapor barrier property and to complement the water vapor barrier property when the second deposited layer 5 (described later) is cracked due to bending. The first deposited layer 3 may be obtained by depositing aluminum, or may contain aluminum oxide (AlO _x ), silicon oxide (SiO _x ), or the like.

The thickness of the first deposition layer 3 may be set appropriately depending on the intended use, but may be preferably 10 nm or more, 30 nm or more, 50 nm or more, and 500 nm or less, 100 nm or less, 80 nm or less. By setting the thickness of the first deposition layer 3 to 10 nm or more, it is easy to ensure sufficient continuity of the first deposition layer 3, and by setting the thickness to 500 nm or less, it is easy to sufficiently suppress the occurrence of curling and cracking, and it is easy to achieve sufficient gas barrier performance and flexibility.

The first deposition layer 3 is preferably formed by a vacuum deposition method from the viewpoint of oxygen gas barrier performance and film uniformity. There are known deposition methods such as vacuum deposition, sputtering, and chemical vapor deposition (CVD), but vacuum deposition is preferred because of its fast deposition rate and high productivity. Among the vacuum deposition methods, deposition by electron beam heating is particularly effective because the deposition rate can be easily controlled by the irradiation area and electron beam current, and the deposition material can be heated and cooled in a short time.

[Second Resin Layer]
The second resin layer 4 is provided to improve adhesion between the first vapor deposition layer 3 and the second vapor deposition layer 5 described later, to prevent cracking of the first vapor deposition layer 3 and the second vapor deposition layer 5 due to bending, or to improve the oxygen barrier properties of the gas barrier laminate.

In the gas barrier laminate according to this embodiment, when the third resin layer described later is folded on the outside, even if the second vapor deposition layer cracks due to the stretching of the third resin layer, the presence of the flexible second resin layer 4 can reduce the risk of the first vapor deposition layer cracking. Furthermore, in the gas barrier laminate according to this embodiment, when the third resin layer is folded on the inside, even if the first vapor deposition layer cracks due to the stretching of the crack in the first resin layer or coat layer, the presence of the flexible second resin layer 4 can reduce the risk of the second vapor deposition layer cracking.

The second resin layer may be made of the same material as the first resin layer described above.

The second resin layer 4 can be formed by applying a coating liquid containing the material constituting the second resin layer and a solvent on the first vapor deposition layer 3 and drying it. Examples of the solvent contained in the coating liquid include water, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-propyl alcohol, n-butyl alcohol, n-pentyl alcohol, dimethyl sulfoxide, dimethylformamide, and dimethylacetamide, and a mixed solvent of water and an alcohol such as methyl alcohol, ethyl alcohol, or isopropyl alcohol is particularly preferred. The coating liquid may also contain additives such as surfactants, preservatives, storage stabilizers, silane coupling agents, organic titanates, and defoamers.

The film thickness of the second resin layer 4 may be, for example, 0.05 μm or more and 10 μm or less. If the film thickness is 0.05 μm or more, the effect of improving the oxygen barrier property is easily obtained, and if it is 10 μm or less, the cost can be reduced and the ratio of paper in the gas barrier laminate according to this embodiment can be increased.

[Second vapor deposition layer]
The second deposited layer 5 is a layer deposited by depositing a metal or an inorganic oxide, and has the role of imparting water vapor barrier properties and complementing the water vapor barrier properties when the first deposited layer 3 is cracked due to bending. The second deposited layer 5 may be obtained by depositing aluminum, or may contain aluminum oxide (AlO _x ), silicon oxide (SiO _x ), or the like.

The thickness of the second deposition layer 5 may be set appropriately depending on the intended use, but may be preferably 10 nm or more, 30 nm or more, 50 nm or more, and 500 nm or less, 100 nm or less, 80 nm or less. By setting the thickness of the second deposition layer 5 to 10 nm or more, it is easy to ensure sufficient continuity of the second deposition layer 5, and by setting the thickness to 500 nm or less, it is easy to sufficiently suppress the occurrence of curling and cracking, and to easily achieve sufficient gas barrier performance and flexibility.

The second deposition layer 5 is preferably formed by a vacuum deposition method from the viewpoint of oxygen gas barrier performance and film uniformity. There are known deposition methods such as vacuum deposition, sputtering, and chemical vapor deposition (CVD), but vacuum deposition is preferred because of its fast deposition rate and high productivity. Among the vacuum deposition methods, deposition by electron beam heating is particularly effective because the deposition rate can be easily controlled by the irradiation area and electron beam current, and the deposition material can be heated and cooled in a short time.

[Third resin layer]
The third resin layer 6 improves adhesion with the second vapor deposition layer 5 and prevents the second vapor deposition layer 5 from cracking due to bending, and also imparts heat sealability to the third resin layer 6.

The material constituting the third resin layer 6 may be a layer containing a polyolefin having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester. The third resin layer 6 is preferably an aqueous emulsion, and preferably contains a polyolefin emulsion having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester. Polyolefins have excellent flexibility and can suppress cracking of deposition after bending, and the crystallinity of polyolefins provides excellent water vapor barrier properties.

The third resin layer 6 can be formed by applying a coating liquid containing the resin and solvent constituting the third resin layer on the second vapor deposition layer and drying it. Examples of the solvent contained in the coating liquid include water, methyl alcohol, ethyl alcohol, isopropyl alcohol, n-propyl alcohol, n-butyl alcohol, n-pentyl alcohol, dimethyl sulfoxide, dimethylformamide, dimethylacetamide, toluene, hexane, heptane, cyclohexane, acetone, methyl ethyl ketone, diethyl ether, dioxane, tetrahydrofuran, ethyl acetate, and butyl acetate. These solvents may be used alone or in combination of two or more. Among these, from the viewpoint of characteristics, methyl alcohol, ethyl alcohol, isopropyl alcohol, toluene, ethyl acetate, methyl ethyl ketone, and water are preferred. From the viewpoint of the environment, methyl alcohol, ethyl alcohol, isopropyl alcohol, and water are preferred. The coating liquid may also contain additives such as surfactants, preservatives, storage stabilizers, silane coupling agents, organic titanates, defoamers, and blocking inhibitors.

The film thickness of the third resin layer 6 may be 0.05 μm or more and 20 μm or less, 0.5 μm or more and 10 μm or less, or 1 μm or more and 5 μm or less.

<Water vapor permeability>
The gas barrier laminate according to this embodiment can exhibit sufficient gas barrier properties even after being folded. In this specification, gas barrier properties refers to a sufficiently low water vapor permeability.

The water vapor permeability of the gas barrier laminate according to this embodiment, when measured by the MOCON method, is preferably 1 g/m ² ·day or less at a temperature of 40° C. and a relative humidity of 90% RH.

The gas barrier laminate according to this embodiment has the third resin layer 6 side facing inward. When a roller weighing 1,500 g is rolled once over the gas barrier laminate and the fold is opened to measure the water vapor permeability, the water vapor permeability is preferably 2 g/ ^m2 ·day or less at a temperature of 40° C. and a relative humidity of 90% RH.

The gas barrier laminate according to this embodiment has the third resin layer 6 side facing outward. When a roller weighing 1,500 g is rolled over it once and the fold is opened to measure the water vapor permeability, the water vapor permeability is preferably 2 g/ ^m2 ·day or less at a temperature of 40° C. and a relative humidity of 90% RH.

<Packaging bag>
2 is a perspective view showing a gusset bag 20 made of the gas barrier laminate 10. A packaging bag is produced by sealing the opening at the top of the gusset bag 20. The gusset bag 20 has portions where the gas barrier laminate 10 is folded (folded portions B1, B2). The folded portion B1 is a portion where the gas barrier laminate is folded in a valley when viewed from the innermost layer side, while the folded portion B2 is a portion where the gas barrier laminate 10 is folded in a mountain when viewed from the innermost layer side.

The packaging bag may be made by folding one gas barrier laminate in half so that the third resin layers 6 face each other, then folding it appropriately into the desired shape and heat sealing it to form a bag shape, or it may be made by stacking two gas barrier laminates so that the third resin layers 6 face each other, and then heat sealing it to form a bag shape.

In the packaging bag according to this embodiment, the heat seal strength may be 2N or more, or 4N or more. The upper limit of the heat seal strength is not particularly limited, but may be, for example, 10N or less.

The packaging bag can contain food, medicine, and other contents. It is particularly suitable for containing food such as sweets. The packaging bag according to this embodiment can maintain high gas barrier properties even when it has a shape with a folded portion.

In this embodiment, a gusset bag is given as an example of a packaging bag, but the gas barrier laminate according to this embodiment may be used to produce, for example, a pillow bag, a three-sided sealed bag, or a standing pouch.

The present invention will be described in more detail below with reference to examples, but the present invention is not limited to these examples.

<Preparation of Gas Barrier Laminate>
(Examples 1 to 9, Comparative Examples 1 to 9)
A gas barrier laminate was obtained by forming a first resin layer, a first vapor-deposited layer, a second resin layer, a second vapor-deposited layer, and a third resin layer on the clay-coated surface of paper (clay-coated paper, paper thickness: 50 μm, clay-coat layer thickness: 5 μm) as shown in Tables 1 to 5 below. The materials used are as follows:
Chemipearl S100: A solution containing a salt of a carboxyl group (manufactured by Mitsui Chemicals)
Chemipearl S500: A solution containing a salt of a carboxyl group (manufactured by Mitsui Chemicals)
Chemipearl V300: Coating liquid containing vinyl acetate polyolefin resin (manufactured by Mitsui Chemicals)

<Measurement of Water Vapor Permeability>
The water vapor permeability of the gas barrier laminates according to the examples and comparative examples was measured by the MOCON method. The measurement conditions were a temperature of 40° C. and a relative humidity of 90%. The gas barrier laminate was creased while rotating once with a 1500 g roller at a speed of 300 mm/min, and the water vapor permeability of the gas barrier laminate after opening was also measured in the same manner. In Tables 1 to 5, "valley fold" refers to the gas barrier laminate after the gas barrier laminate has been valley-folded as viewed from the paper substrate side, and "mountain fold" refers to the gas barrier laminate after the gas barrier laminate has been mountain-folded as viewed from the paper substrate side. The results are shown in Tables 1 to 5 in the unit [g/ ^m2 ·day].

<Measurement of heat seal strength>
Two gas barrier laminates were stacked with the paper substrate facing outward, and heat sealed with a heat sealer at 120°C, 0.2 MPa, and 1 second, and then cut into strips 15 mm wide, and the maximum load when T-peeled at a peel speed of 300 mm/min was measured. The results are shown in Tables 1 to 5 in the unit [N/15 mm].

1...paper base material, 2...first resin layer, 3...first vapor deposition layer, 4...second resin layer, 5...second vapor deposition layer, 6...third resin layer, 10...gas barrier laminate, 20...gusset bag, B1, B2...folded portion.

Claims (8)

A gas barrier laminate comprising, in this order, a paper substrate, a first resin layer, a first vapor deposition layer, a second resin layer, a second vapor deposition layer, and a third resin layer,
the first resin layer contains a polyolefin having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester;
the second resin layer contains a polyolefin having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester;
the third resin layer contains a polyolefin having at least one selected from a carboxyl group, a salt of a carboxyl group, a carboxylic anhydride group, and a carboxylic acid ester;
A gas barrier laminate , wherein the first vapor-deposited layer is an aluminum vapor-deposited layer (however, this excludes gas barrier laminates in which the first resin layer contains a melamine resin, an alkyd resin, a polyphenol resin or an acrylic resin) . The gas barrier laminate according to claim 1 , wherein the second resin layer has a thickness of 0.05 μm or more and 10 μm or less. The gas barrier laminate according to claim 1 or 2 , wherein the second vapor-deposited layer is an aluminum vapor-deposited layer. The gas barrier laminate according to claim 1 or 2, wherein the second vapor-deposited layer is a vapor-deposited film of silicon oxide or aluminum oxide. The gas barrier laminate according to any one of claims 1 to 4, wherein the first vapor-deposited layer and the second vapor-deposited layer each have a thickness of 30 nm or more and 100 nm or less. 6. The gas barrier laminate according to claim 1 , wherein the thickness of the paper substrate is 30 μm or more and 100 μm or less, and the thickness of the paper substrate is 60% or more of the total thickness of the gas barrier laminate. A packaging bag comprising the gas barrier laminate according to any one of claims 1 to 6 . The packaging bag according to claim 7 , having a folded portion.