JP7619979B2 - Nickel manganese cobalt composite hydroxide - Google Patents

Description

The present invention relates to a nickel-manganese-cobalt composite hydroxide, which is a precursor of a positive electrode active material and is composed of secondary particles formed by agglomeration of primary particles containing nickel, manganese, and cobalt, or of primary particles and secondary particles.

In recent years, with the widespread use of portable electronic devices such as smartphones, tablet devices, and laptop computers, there has been a growing need to develop high-power secondary batteries, including small, lightweight non-aqueous electrolyte secondary batteries with high energy density, as well as batteries for hybrid and electric vehicles.

Lithium-ion secondary batteries are an example of a secondary battery that can meet these needs. Lithium-ion secondary batteries are composed of a positive electrode, a negative electrode, and an electrolyte, and the active materials used for the positive and negative electrodes are materials that can extract and insert lithium. Lithium-ion secondary batteries are still being actively researched and developed, and among these, lithium-ion secondary batteries that use layered or spinel-type lithium metal composite oxides as the positive electrode active material can obtain a high voltage of about 4V, and are therefore being put into practical use as batteries with high energy density.

Among these, lithium nickel manganese cobalt composite oxide has attracted attention as a material that has good cycle characteristics of battery capacity and can provide high output with low resistance. In recent years, it is also suitable as a power source for electric vehicles and hybrid vehicles, which are constrained by mounting space, and is considered important as an on-board power source. Generally, lithium nickel manganese cobalt composite oxide is produced by mixing the precursor nickel manganese cobalt composite hydroxide with a lithium compound and baking it.

This nickel manganese cobalt composite hydroxide contains impurities such as sulfate radicals, chlorine radicals, and sodium derived from the raw materials and chemicals used in the manufacturing process. These impurities induce side reactions and worsen the reaction with lithium during the process of mixing the nickel manganese cobalt composite hydroxide with a lithium compound and firing it, thereby reducing the crystallinity of the lithium nickel manganese cobalt composite oxide, which has a layered structure.

When lithium nickel manganese cobalt composite oxide with low crystallinity due to the influence of impurities is used as a positive electrode active material to construct a battery, it inhibits the diffusion of lithium in the solid phase, resulting in a decrease in battery capacity. In addition, since these impurities hardly contribute to the charge/discharge reaction, it is necessary to use extra negative electrode material in the battery to cover the irreversible capacity of the positive electrode material. As a result, the capacity per weight or volume of the entire battery becomes smaller, and excess lithium accumulates in the negative electrode as irreversible capacity, which poses a safety problem.

Impurities include sulfate radicals, chlorine radicals, sodium, etc., and techniques for removing these impurities have been disclosed.

For example, Patent Document 1 discloses a method for reducing sulfate and chlorine radicals by performing a crystallization process to obtain a niobium-containing transition metal composite hydroxide and washing the obtained niobium-containing transition metal composite hydroxide with an aqueous solution of a carbonate such as potassium carbonate, sodium carbonate, or ammonium carbonate.

Patent Document 2 also discloses that in the process of producing nickel manganese cobalt composite hydroxide from a crystallization reaction, the alkaline solution used for adjusting the pH is a mixed solution of an alkali metal hydroxide and a carbonate, thereby reducing the impurities of sulfate, chlorine, and carbonate.

Patent Documents 3 and 4 disclose that the nickel-manganese composite hydroxide particles or nickel composite hydroxide particles having a void structure inside the particles obtained in the crystallization process are washed with an aqueous solution of a carbonate such as potassium carbonate, sodium carbonate, potassium hydrogen carbonate, or sodium hydrogen carbonate, thereby reducing the sulfate radicals, chlorine radicals, and sodium.

Patent Document 5 also discloses that a nickel-cobalt-M element-containing aqueous solution or aqueous dispersion obtained by mixing a nickel ammine complex, a cobalt ammine complex, and an M element source is heated to thermally decompose the nickel ammine complex and the cobalt ammine complex, and a nickel-cobalt-M element-containing composite compound with a low content of impurities such as sulfate radicals, chlorine radicals, sodium, and iron is used.

JP 2015-122269 A JP 2016-117625 A International Publication No. 2015/146598 JP 2015-191848 A International Publication No. 2012/020768

However, Patent Documents 1 and 2 make no mention at all of the removal of sodium. Furthermore, in Patent Documents 3 and 4, even in solid precursors with a porosity of about 3%, 0.001 to 0.015 mass % of sodium still remains, and sodium reduction is insufficient. Furthermore, in Patent Document 5, a nickel-cobalt-M element-containing composite compound is obtained by thermal decomposition, and from the standpoint of particle sphericity, particle size distribution, and specific surface area, it is questionable whether sufficient battery characteristics will be achieved when used as a positive electrode active material.

Therefore, an object of the present invention is to provide a nickel-manganese-cobalt composite hydroxide, which is a precursor of a positive electrode active material for a lithium-ion secondary battery that can reliably reduce the content of impurities , particularly sodium, which hardly contributes to charge/discharge reactions, and improve battery characteristics.

A nickel manganese cobalt composite hydroxide according to one embodiment of the present invention is a nickel manganese cobalt composite hydroxide that is a precursor of a positive electrode active material and is composed of secondary particles in which primary particles containing nickel, manganese, and cobalt are aggregated, or the primary particles and the secondary particles, and is characterized in that the nickel manganese cobalt composite hydroxide has a sodium content of less than 0.0005 mass% and a chlorine radical content of 0.01 mass% or less .

In this way, it is possible to provide a nickel-manganese-cobalt composite hydroxide, which is a precursor of a positive electrode active material for a lithium-ion secondary battery, capable of reliably reducing the contents of sodium and chlorine radicals and improving battery characteristics.

In this case, in one aspect of the present invention, the nickel manganese cobalt composite hydroxide may have a specific surface area of 10 to 20 m ² /g.

In this way, it is possible to provide a nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material that can be used to obtain a lithium ion secondary battery with improved battery characteristics by increasing the specific surface area.

In this case, in one aspect of the present invention, the content of sulfate radicals contained in the nickel manganese cobalt composite hydroxide may be 0.2 mass % or less .

In this way, it is possible to provide a nickel-manganese-cobalt composite hydroxide, which is a precursor of a positive electrode active material for a lithium-ion secondary battery, capable of reliably reducing the sulfate group content and improving battery characteristics.

In this case, in one embodiment of the present invention, the index showing the spread of the particle size distribution of the nickel manganese cobalt composite hydroxide, [(d90-d10)/average particle size], may be 0.55 or less.

In this way, the proportion of fine particles and large particles is reduced when the positive electrode active material is used, so that a lithium-ion secondary battery using this positive electrode active material in the positive electrode is safe and can achieve good cycle characteristics and battery output.

In this case, in one aspect of the present invention, the nickel manganese cobalt composite hydroxide may be represented by the general formula: Ni _x Co _y Mn _z M _t (OH) _2+a (wherein x + y + z + t = 1, 0.20 ≤ x ≤ 0.80, 0.10 ≤ y ≤ 0.50, 0.10 ≤ z ≤ 0.90, 0 ≤ t ≤ 0.10, 0 ≤ a ≤ 0.5, and M is one or more of Mg, Ca, Al, Ti, V, Cr, Zr, Nb, Mo, and W).

In this way, it is possible to reliably reduce the sodium content of the nickel manganese cobalt composite hydroxide and provide a nickel manganese cobalt composite hydroxide that is a precursor of the positive electrode active material of a lithium ion secondary battery and can improve the battery characteristics.

According to the present invention, it is possible to provide a nickel-manganese-cobalt composite hydroxide , which is a precursor of a positive electrode active material for a lithium-ion secondary battery, capable of reliably reducing the sodium content in particular and improving the battery characteristics.

FIG. 1 is a cross-sectional SEM photograph of a nickel manganese cobalt composite hydroxide according to one embodiment of the present invention, showing that the internal structure is a solid structure. FIG. 2 is a process diagram showing an outline of a method for producing a nickel manganese cobalt composite hydroxide according to one embodiment of the present invention.

The inventors have conducted extensive research to solve the above problems, and have discovered that in the production of nickel-manganese-cobalt composite hydroxide, the reaction atmosphere in the crystallization process can be controlled, the alkaline solution used in the crystallization process is a mixed solution of an alkali metal hydroxide and a carbonate, and the transition metal composite hydroxide obtained in the crystallization process is washed in the washing process with an ammonium hydrogen carbonate solution, which is a washing solution containing hydrogen carbonate (bicarbonate), thereby more efficiently reducing the impurities, sulfate radicals, chlorine radicals, and sodium, and thus completing the present invention. The following describes preferred embodiments of the present invention.

The present embodiment described below does not unduly limit the contents of the present invention described in the claims, and can be modified within the scope of the present invention. In addition, not all of the configurations described in the present embodiment are necessarily essential as a means for solving the problems of the present invention. The nickel manganese cobalt composite hydroxide, the method for producing the nickel manganese cobalt composite hydroxide, and the lithium nickel manganese cobalt composite oxide according to one embodiment of the present invention will be described in the following order.
1. Nickel manganese cobalt composite hydroxide 2. Lithium nickel manganese cobalt composite oxide 3. Method for producing nickel manganese cobalt composite hydroxide 3-1. Crystallization process 3-1-1. Nucleation process 3-1-2. Particle growth process 3-2. Washing process

<1. Nickel manganese cobalt composite hydroxide>
A nickel manganese cobalt composite hydroxide according to one embodiment of the present invention is a precursor of a positive electrode active material, which is composed of secondary particles in which primary particles containing nickel, manganese, and cobalt are aggregated, or the primary particles and the secondary particles.

The nickel manganese cobalt composite hydroxide is characterized in that the sodium content is less than 0.0005% by mass. The nickel manganese cobalt composite hydroxide according to one embodiment of the present invention will be specifically described below.

[Particle composition]
The nickel manganese cobalt composite hydroxide is preferably adjusted so that its composition is represented by the general formula: Ni _x Co _y Mn _z M _t (OH) _2+a (wherein x + y + z + t = 1, 0.20 ≤ x ≤ 0.80, 0.10 ≤ y ≤ 0.50, 0.10 ≤ z ≤ 0.90, 0 ≤ t ≤ 0.10, 0 ≤ a ≤ 0.5, and M is one or more of Mg, Ca, Al, Ti, V, Cr, Zr, Nb, Mo, and W).

In the above general formula, x, which indicates the nickel content, is preferably 0.20≦x≦0.80. In addition, taking into consideration electrical properties and thermal stability, x, which indicates the nickel content, is more preferably x≦0.6.

In addition, in the above general formula, y, which indicates the cobalt content, is preferably 0.10≦y≦0.50. By adding an appropriate amount of cobalt, it is possible to improve cycle characteristics and reduce the expansion and contraction behavior of the crystal lattice due to the desorption and insertion of Li during charging and discharging. However, if y is less than 0.10, it is difficult to obtain a sufficient effect of reducing the expansion and contraction behavior of the crystal lattice, which is not preferable. On the other hand, if too much cobalt is added and y exceeds 0.5, the initial discharge capacity may decrease significantly, and there is also a problem of being disadvantageous in terms of cost, which is also not preferable.

In addition, z, which indicates the manganese content, is preferably 0.10≦z≦0.90. Adding manganese within this range can further improve the durability and safety of a battery when used as a positive electrode active material. If z is less than 0.10, the effect of improving the durability and safety of the battery cannot be fully obtained, while if it exceeds 0.9, the metal elements that contribute to the Redox reaction are reduced, which may reduce the battery capacity, which is not preferable.

The additive element M is one or more of Mg, Al, Ca, Ti, V, Cr, Zr, Nb, Mo, and W, and is added to improve battery characteristics such as cycle characteristics and output characteristics. The content of the additive element M, t, is preferably 0≦t≦0.10. If t exceeds 0.1, the amount of metal elements that contribute to the Redox reaction decreases, which may result in a decrease in battery capacity, and this is not preferable.

Other analytical methods for the particle composition are not particularly limited, but can be determined by chemical analysis methods such as acid decomposition-ICP emission spectrometry.

[Particle structure]
The nickel manganese cobalt composite hydroxide is composed of spherical secondary particles formed by agglomeration of multiple primary particles. The primary particles constituting the secondary particles may have various shapes such as plate-like, needle-like, rectangular, elliptical, and rhombohedral. In addition, the present invention can be applied to the case where multiple primary particles are aggregated in random directions, as well as the case where the particles are aggregated in the major axis direction radially from the center.

As for the agglomeration state, it is preferable that plate-like or needle-like primary particles are agglomerated in random directions to form secondary particles. In the case of such a structure, almost uniform voids are generated between the primary particles, and when mixed with a lithium compound and fired, the molten lithium compound spreads throughout the secondary particles, allowing sufficient diffusion of lithium.

The method for observing the shapes of the primary particles and secondary particles is not particularly limited, but they can be measured by observing the cross section of the nickel manganese cobalt composite hydroxide using a scanning electron microscope (SEM) or the like.

[Particle internal structure]
The nickel manganese cobalt composite hydroxide according to one embodiment of the present invention has a solid structure and does not have a hollow structure or a porous structure inside the secondary particles. Since there are no voids inside the secondary particles, the particle strength is the best. Therefore, the life of the positive electrode active material is extended.

This solid structure can be confirmed by observing the cross section of the nickel manganese cobalt composite hydroxide particles with a scanning electron microscope (SEM). In the nickel manganese cobalt composite hydroxide according to one embodiment of the present invention, the secondary particles have a solid structure. For example, by further adjusting the crystallization conditions, it is possible to mix solid, hollow, and porous structures in the desired combination and ratio according to the customer's needs for production, specifications, and characteristics. This has the advantage of stabilizing the overall composition and particle size compared to simply mixing solid, hollow, and porous products.

[Average particle size (MV)]
The nickel manganese cobalt composite hydroxide is preferably adjusted to have an average particle size of 3 to 20 μm. If the average particle size is less than 3 μm, the particle packing density decreases when the positive electrode is formed. On the other hand, if the average particle size exceeds 20 μm, the specific surface area of the positive electrode active material decreases, and the interface with the electrolyte of the battery decreases. This is not preferable because it may increase the resistance of the positive electrode and reduce the output characteristics of the battery. Therefore, the nickel manganese cobalt composite hydroxide has an average particle size of 3 to 20 μm, preferably 3 to 15 μm. If the thickness is adjusted to 4 to 12 μm, it is possible to increase the battery capacity per volume in a lithium ion secondary battery using this positive electrode active material as a positive electrode material, and the battery capacity per volume can be increased, and the safety and cycle life can be improved. It has good characteristics.

The method for measuring the average particle size is not particularly limited, but it can be determined, for example, from the volume-based distribution measured using a laser diffraction/scattering method.

[Impurity content]
In general, nickel manganese cobalt composite hydroxide contains sulfate radicals, chlorine radicals, and sodium as impurities. These impurities cause the reaction with lithium to deteriorate and hardly contribute to the charge/discharge reaction, so it is preferable to remove them as much as possible and reduce their content. Conventionally, techniques for removing these impurities have been disclosed, but they are still insufficient.

The nickel manganese cobalt composite hydroxide according to one embodiment of the present invention is characterized in that the sodium content contained therein is less than 0.0005% by mass. In this way, it is possible to provide a nickel manganese cobalt composite hydroxide that is a precursor of a positive electrode active material for a lithium ion secondary battery that can reliably reduce the sodium content and improve battery characteristics.

It is also preferable that the sulfate radical content in the nickel manganese cobalt composite hydroxide is 0.2 mass % or less, and the chlorine radical content is 0.01 mass % or less. In this way, it is possible to reliably reduce the sulfate radical, chlorine radical, and sodium content, and provide a nickel manganese cobalt composite hydroxide that is a precursor of a positive electrode active material for a lithium ion secondary battery that can improve battery characteristics.

The content of each impurity can be determined, for example, by the following analytical methods. Sodium can be determined by acid decomposition-atomic absorption spectrometry, acid decomposition-ICP emission spectrometry, or the like. Sulfate radicals can be determined by analyzing the total sulfur content of the nickel manganese cobalt composite hydroxide by combustion infrared absorption spectrometry, acid decomposition-ICP emission spectrometry, or the like, and converting this total sulfur content into sulfate radicals (SO ₄ ²⁻ ). Chlorine radicals can be determined by analyzing the nickel manganese cobalt composite hydroxide directly, or by separating the chlorine radicals contained in the nickel manganese cobalt composite hydroxide by a distillation operation in the form of silver chloride or the like, and analyzing the separated chlorine radicals by X-ray fluorescence (XRF) analysis.

[Particle size distribution]
The nickel manganese cobalt composite hydroxide is preferably adjusted so that the index showing the spread of the particle size distribution of the particles, [(d90-d10)/average particle size], is 0.55 or less.

If the particle size distribution is wide and the index showing the spread of the particle size distribution, [(d90-d10)/average particle size], exceeds 0.55, there will likely be many fine particles whose particle size is very small compared to the average particle size, and many particles whose particle size is very large compared to the average particle size (large diameter particles).

These characteristics of the particle size distribution at the precursor stage also have a significant effect on the positive electrode active material obtained after the firing process. If a positive electrode is formed using a positive electrode active material containing many fine particles, not only may there be a risk of heat generation due to local reactions of the fine particles, which may reduce safety, but also the fine particles with a large specific surface area may be selectively deteriorated, which may result in poor cycle characteristics, which is undesirable. On the other hand, if a positive electrode is formed using a positive electrode active material containing many large-diameter particles, there may not be enough reaction area between the electrolyte and the positive electrode active material, which may result in a decrease in battery output due to an increase in reaction resistance, which is undesirable.

Therefore, in the particle size distribution of the precursor nickel manganese cobalt composite hydroxide, it is preferable that [(d90-d10)/average particle size] is 0.55 or less, and since the proportion of fine particles and large particles is reduced when it is used as a positive electrode active material, a lithium ion secondary battery using this positive electrode active material in the positive electrode is safer and can achieve good cycle characteristics and battery output.

In the index showing the spread of particle size distribution [(d90-d10)/average particle size], d10 means the particle size at which the cumulative volume of the number of particles at each particle size, when accumulated from the smallest particle size, is 10% of the total volume of all particles. In contrast, d90 means the particle size at which the cumulative volume of the number of particles at each particle size, when accumulated from the smallest particle size, is 90% of the total volume of all particles. There are no particular limitations on the method for determining the average particle size, d90, and d10, but they can be determined, for example, from a volume-based distribution measured using a laser diffraction/scattering method.

[Specific surface area]
The nickel manganese cobalt composite hydroxide is preferably adjusted to have a specific surface area of 10 to 80 m ² /g, and if the particles are solid and have no voids, it is more preferably adjusted to 10 to 20 m ² /g in order to further stabilize the battery characteristics. If the specific surface area is within the above range, a sufficient particle surface area can be secured to be in contact with the molten lithium compound when mixed with the lithium compound and fired, and the particle strength when formed into a positive electrode active material can also be satisfied.

On the other hand, if the specific surface area is less than 10 ^m2 /g, when mixed with a lithium compound and fired, the contact with the molten lithium compound becomes insufficient, the crystallinity of the resulting lithium nickel manganese cobalt composite oxide decreases, and when used as a positive electrode material to form a lithium ion secondary battery, there is a concern that the diffusion of lithium in the solid phase is hindered and the capacity decreases. Also, if the specific surface area exceeds 80 ^m2 /g, when mixed with a lithium compound and fired, the crystal growth proceeds too much, causing cation mixing in which nickel is mixed into the lithium layer of the lithium transition metal composite oxide, which is a layered compound, and the charge/discharge capacity may decrease, which is not preferable.

The method for measuring the specific surface area is not particularly limited, but it can be determined, for example, by the BET multipoint method, the BET single point method, or the nitrogen gas adsorption/desorption method.

Figure 1 shows a cross-sectional SEM photograph of a nickel manganese cobalt composite hydroxide according to one embodiment of the present invention. As shown in Figure 1, the nickel manganese cobalt composite hydroxide according to one embodiment of the present invention has a solid internal structure.

The nickel manganese cobalt composite hydroxide according to one embodiment of the present invention can provide a precursor for a positive electrode active material for a lithium ion secondary battery that can reliably reduce the sodium content and improve battery characteristics.

<2. Lithium Nickel Manganese Cobalt Composite Oxide>
The lithium nickel manganese cobalt composite oxide according to one embodiment of the present invention is composed of secondary particles formed by agglomeration of primary particles containing lithium, nickel, manganese, and cobalt, or the primary particles and the secondary particles, and is characterized in that the sodium content in the lithium nickel manganese cobalt composite oxide is less than 0.0005 mass%.

It is also preferable that the content of sulfate radicals contained in the lithium nickel manganese cobalt composite oxide is 0.15 mass% or less, the content of chlorine radicals is 0.005 mass% or less, and the Me site occupancy is 93.0% or more.

The nickel manganese cobalt composite hydroxide can be mixed with a lithium compound and fired to produce a lithium nickel manganese cobalt composite oxide. The lithium nickel manganese cobalt composite oxide can be used as a raw material for the positive electrode active material of lithium ion secondary batteries.

The lithium nickel manganese cobalt composite oxide used as the positive electrode active material is obtained by mixing the precursor nickel manganese cobalt composite hydroxide with lithium compounds such as lithium _carbonate ( _Li2CO3 : melting point 723°C), lithium hydroxide (LiOH: melting point 462°C), lithium nitrate ( _LiNO3 : melting point 261°C), lithium chloride (LiCl: melting point 613°C), and lithium sulfate _{( Li2SO4} : melting point 859°C), and then subjecting the mixture to a firing process.

As for the lithium compound, it is particularly preferable to use lithium carbonate or lithium hydroxide, taking into consideration ease of handling and stability of quality.

In this firing process, the carbonate, hydroxyl, nitrate, chlorine, and sulfate radicals, which are also components of the lithium compound, volatilize, but a small portion remains in the positive electrode active material. In addition to the non-volatile components such as sodium, the particle size distribution, specific surface area, and solid structure of the secondary particles, the product retains most of the characteristics of the precursor nickel manganese cobalt composite hydroxide.

The lithium nickel manganese cobalt composite oxide according to one embodiment of the present invention can provide a positive electrode active material for lithium ion secondary batteries that can reliably reduce the sodium content and improve battery characteristics.

<3. Method for producing nickel manganese cobalt composite hydroxide>
Next, a method for producing a nickel manganese cobalt composite hydroxide according to one embodiment of the present invention will be described with reference to Fig. 2. The method for producing a nickel manganese cobalt composite hydroxide according to one embodiment of the present invention is a method for producing a precursor of a positive electrode active material, which is composed of secondary particles formed by agglomeration of primary particles containing nickel, manganese, and cobalt, or the primary particles and the secondary particles. As shown in Fig. 2, the method includes a crystallization step S10 and a washing step S20.

In the crystallization step S10, a raw material solution containing nickel, manganese, and cobalt, a solution containing an ammonium ion donor, and an alkaline solution are added to obtain a reaction solution, and crystallization occurs to obtain a transition metal composite hydroxide. In the washing step S20, the transition metal composite hydroxide obtained in the crystallization step S10 is washed with a washing solution.

The alkaline solution in the crystallization step S10 is a mixed solution of an alkali metal hydroxide and a carbonate, and the molar ratio of the carbonate to the alkali metal hydroxide in the mixed solution, [CO ₃ ²⁻ ]/[OH ⁻ ], is 0.002 to 0.050, the crystallization step S10 is performed in a non-oxidizing atmosphere, and the washing solution in the washing step S20 is an ammonium hydrogen carbonate solution having a concentration of 0.05 mol/L or more. Each step will be described in detail below.

<3-1. Crystallization process>
In the crystallization step S10, a raw material solution containing nickel, manganese, and cobalt, a solution containing an ammonium ion donor, and an alkaline solution are added to obtain a reaction solution, and crystallization is performed in the reaction solution to obtain a transition metal composite hydroxide. get.

The crystallization step S10 preferably further includes a nucleation step S11 and a particle growth step S12. In the nucleation step S11, an alkaline solution is added to generate nuclei in the reaction solution so that the pH measured at a liquid temperature of 25°C is 12.0 to 14.0, and in the particle growth step S12, an alkaline solution is preferably added to the reaction solution containing the nuclei formed in the nucleation step S11 so that the pH measured at a liquid temperature of 25°C is 10.5 to 12.0. Details will be described later.

In conventional continuous crystallization methods, the nucleation reaction and the nucleus growth reaction proceed simultaneously in the same reaction tank, resulting in a wide range of particle size distribution of the precursor. In contrast, the method for producing nickel manganese cobalt composite hydroxide in the present invention clearly separates the time during which the nucleation reaction mainly occurs (nucleation process) from the time during which the particle growth reaction mainly occurs (particle growth process), thereby obtaining a transition metal composite hydroxide with a narrow particle size distribution even if both processes are carried out in the same reaction tank. In addition, by using a mixed solution of an alkali metal hydroxide and a carbonate as the alkaline solution, impurities such as sulfate radicals can be reduced.

The materials and conditions used in the method for producing nickel manganese cobalt composite hydroxide of the present invention are described in detail below.

[Raw material solution containing nickel, manganese, and cobalt]
Metal salts such as nickel salts, manganese salts, and cobalt salts used in the raw material solution containing nickel, manganese, and cobalt are not particularly limited as long as they are water-soluble compounds, and examples of such salts include sulfates, nitrates, chlorides, etc. For example, nickel sulfate, manganese sulfate, and cobalt sulfate are preferably used.

If necessary, compounds containing one or more additive elements M can be mixed in a predetermined ratio to prepare the raw material solution. In this case, in the crystallization step S10, it is preferable to use a compound containing one or more of Mg, Ca, Al, Ti, V, Cr, Zr, Nb, Mo, and W, and examples of compounds that can be used include titanium sulfate, ammonium peroxotitanate, potassium titanium oxalate, vanadium sulfate, ammonium vanadate, chromium sulfate, potassium chromate, zirconium sulfate, zirconium nitrate, niobium oxalate, ammonium molybdate, sodium tungstate, and ammonium tungstate.

The nickel manganese cobalt composite hydroxide obtained by crystallization may be mixed with an aqueous solution containing one or more additive elements M to form a slurry, and the pH may be adjusted to coat the nickel manganese cobalt composite hydroxide with a compound containing one or more additive elements M.

The concentration of the raw material solution is preferably 1.0 to 2.6 mol/L, more preferably 1 to 2.2 mol/L, in terms of the total metal salts. If it is less than 1 mol/L, the resulting hydroxide slurry will have a low concentration and will be less productive. On the other hand, if it exceeds 2.6 mol/L, crystal precipitation or freezing will occur at temperatures below -5°C, which may clog the piping of the equipment, and the piping will need to be kept warm or heated, which will be costly.

Furthermore, the amount of raw material solution supplied to the reaction tank is preferably such that the crystallized product concentration at the end of the crystallization reaction is approximately 30 to 250 g/L, preferably 80 to 150 g/L. If the crystallized product concentration is less than 30 g/L, the primary particles may not aggregate sufficiently, and if it exceeds 250 g/L, the mixed aqueous solution added may not diffuse sufficiently in the reaction tank, resulting in uneven particle growth.

[Ammonium ion donor]
The ammonium ion donor in the reaction solution is not particularly limited as long as it is a water-soluble compound, and examples of the donor include ammonia water, ammonium sulfate, ammonium chloride, ammonium carbonate, and ammonium fluoride. For example, it is preferable to use ammonia water or ammonium sulfate.

The ammonium ion concentration in the reaction solution is adjusted to preferably 3 to 25 g/L, more preferably 5 to 20 g/L, and even more preferably 5 to 15 g/L. The presence of ammonium ions in the reaction solution causes metal ions, particularly nickel ions, to form ammine complexes, increasing the solubility of the metal ions and promoting the growth of primary particles, making it easier to obtain dense nickel manganese cobalt composite hydroxide particles. Furthermore, since the solubility of the metal ions is stable, nickel manganese cobalt composite hydroxide particles with a uniform shape and particle size are easily obtained. And, by setting the ammonium ion concentration in the reaction solution to 3 to 25 g/L, it is easier to obtain composite hydroxide particles that are denser and have a uniform shape and particle size.

If the ammonium ion concentration in the reaction solution is less than 3 g/L, the solubility of the metal ions may become unstable, and primary particles with uniform shape and particle size may not be formed, and gel-like nuclei may be generated, resulting in a wide particle size distribution. In contrast, if the ammonium ion concentration exceeds 25 g/L, the solubility of the metal ions may become too high, and the amount of metal ions remaining in the reaction solution may increase, causing a deviation in the composition. The concentration of ammonium ions can be measured using an ion electrode method (ion meter).

[Alkaline solution]
The alkaline solution is prepared by mixing an alkali metal hydroxide and a carbonate. The molar ratio of the alkali metal hydroxide to the carbonate, [CO ₃ ²⁻ ]/[OH ⁻ ], is 0.002 to 0.050. It is more preferable that the ratio is 0.005 to 0.030, and further more preferable that the ratio is 0.010 to 0.025.

By using a mixed solution of an alkali metal hydroxide and a carbonate as the alkaline solution, it is possible to replace and remove anions such as sulfate and chlorine that remain as impurities in the nickel manganese cobalt composite hydroxide obtained in the crystallization step S10 with carbonate. Carbonate is more easily volatilized by ignition than sulfate and chlorine, and is preferentially volatilized in the process of mixing and firing the nickel manganese cobalt composite hydroxide with a lithium compound, so that almost no carbonate remains in the lithium nickel manganese cobalt composite oxide, which is the positive electrode material.

If [CO ₃ ²⁻ ]/[OH ⁻ ] is less than 0.002, the replacement of the impurities sulfate and chlorine derived from the raw materials with carbonate ions becomes insufficient in the crystallization step S10, and these impurities become easily incorporated into the nickel-cobalt-manganese composite hydroxide. On the other hand, even if [CO ₃ ²⁻ ]/[OH ⁻ ] exceeds 0.050, the reduction in the impurities sulfate and chlorine derived from the raw materials remains unchanged, and the excess carbonate added increases costs.

The alkali metal hydroxide is preferably one or more of lithium hydroxide, sodium hydroxide, and potassium hydroxide, and compounds that are easily soluble in water are preferred because the amount added is easy to control.

The carbonate is preferably one or more of sodium carbonate, potassium carbonate, and ammonium carbonate, and compounds that are easily soluble in water are preferred because the amount added is easy to control.

The method for adding the alkaline solution to the reaction tank is not particularly limited, and it may be added using a pump capable of controlling the flow rate, such as a metering pump, so that the pH of the reaction solution is maintained within the range described below.

[pH Control]
It is more preferable that the crystallization step S10 comprises a nucleation step S11 in which an alkaline solution is added to generate nuclei so that the pH of the reaction solution measured at a liquid temperature of 25° C. is 12.0 to 14.0, and a particle growth step S12 in which an alkaline solution is added to the particle growth solution containing the nuclei formed in the nucleation step S11 so that the pH of the solution measured at a liquid temperature of 25° C. is 10.5 to 12.0, thereby growing the nuclei.

In other words, the nucleation reaction and the particle growth reaction do not proceed at the same time in the same tank, but rather the time during which the nucleation reaction (nucleation step S11) mainly occurs and the time during which the particle growth reaction (particle growth step S12) mainly occurs are clearly separated. The nucleation step S11 and the particle growth step S12 are described in detail below.

<3-1-1. Nucleation process>
In the nucleation step S11, it is preferable to control the pH of the reaction solution to be in the range of 12.0 to 14.0 at a liquid temperature of 25° C. If the pH exceeds 14.0, the nuclei generated If the pH is less than 12.0, the nuclei will grow together with the nuclei formation, resulting in a wide range of particle size distribution of the nuclei. It may become inhomogeneous.

That is, in the nucleation step S11, by controlling the pH of the reaction solution in the range of 12.0 to 14.0, it is possible to suppress the growth of nuclei and cause only nucleation to occur, and the nuclei formed are homogeneous and have a narrower particle size distribution range.

<3-1-2. Particle growth process>
In the particle growth step S12, the pH of the reaction solution is preferably 10.5 to 12.0, more preferably 11.0 to 12.0, based on a liquid temperature of 25° C. If the pH exceeds 0.0, the number of newly generated nuclei increases, resulting in the generation of fine secondary particles, and it may not be possible to obtain hydroxides with a good particle size distribution. In the case of ammonium ions, the solubility of the metal ions is high, and the amount of metal ions that remain in the solution without being precipitated increases, which may result in a decrease in production efficiency.

In other words, by controlling the pH of the reaction solution in the particle growth step S12 to a range of 10.5 to 12.0, it is possible to preferentially cause the growth of only the nuclei generated in the nucleation step S11 and suppress the formation of new nuclei, and to obtain a nickel-cobalt-manganese composite hydroxide that is homogeneous and has a narrower particle size distribution range.

In addition, since a pH of 12.0 is the boundary condition between nucleation and nucleus growth, the conditions can be set to either the nucleation process or the particle growth process depending on the presence or absence of nuclei in the reaction solution. In other words, if the pH of the nucleation process S11 is made higher than 12.0 to generate a large amount of nuclei, and then the pH is made 12.0 in the particle growth process S12, the large amount of nuclei is present in the reaction aqueous solution, so nucleus growth takes precedence, and the above hydroxide with a narrower particle size distribution and a relatively large particle size is obtained.

On the other hand, when no nuclei are present in the reaction solution, that is, when the pH is set to 12.0 in the nucleation step S11, there are no nuclei to grow, and nucleation takes precedence. By setting the pH in the particle growth step S12 to a value less than 12.0, the generated nuclei grow, resulting in a better hydroxide.

In either case, the pH of the particle growth process S12 may be controlled to a value lower than the pH of the nucleation process S11. In order to clearly separate nucleation and particle growth, it is preferable to set the pH of the particle growth process S12 at least 0.5 lower than the pH of the nucleation process S11, and more preferably at least 1.0 lower.

As described above, by clearly separating the nucleation step S11 and the particle growth step S12 by pH, nucleation takes precedence in the nucleation step S11, with almost no nucleus growth, and conversely, in the particle growth step S12, only nucleus growth occurs, with almost no new nuclei being generated. As a result, in the nucleation step S11, homogeneous nuclei with a narrow particle size distribution range can be formed, and in the particle growth step S12, the nuclei can be grown homogeneously. Therefore, in the method for producing nickel manganese cobalt composite hydroxide, homogeneous nickel manganese cobalt composite hydroxide particles with a narrower particle size distribution range can be obtained.

[Reaction solution temperature]
In the reaction tank, the temperature of the reaction solution is preferably set to 20 to 80° C., more preferably 30 to 70° C., and even more preferably 35 to 60° C. If the temperature of the reaction solution is less than 20° C., the solubility of metal ions is low, so nucleation is likely to occur and control is difficult. On the other hand, if the temperature exceeds 80° C., the volatilization of ammonia is promoted, so that an excess of ammonium ion donor must be added to maintain a predetermined ammonia concentration, resulting in high costs.

[Reaction atmosphere]
The particle size and particle structure of the nickel-cobalt-manganese composite hydroxide are also controlled by the reaction atmosphere in the crystallization step S10. Therefore, in the crystallization step S10, crystallization is performed in a non-oxidizing atmosphere. When the atmosphere in the reaction tank during the crystallization step S10 is controlled to a non-oxidizing atmosphere, the growth of the primary particles forming the nickel-cobalt-manganese composite hydroxide is promoted, and the primary particles are large and dense, and secondary particles having a moderately large particle size are formed. Therefore, a solid-type nickel-cobalt-manganese composite hydroxide as shown in FIG. 1 is obtained. On the other hand, when the atmosphere in the reaction tank during the crystallization step is controlled to an oxidizing atmosphere, the growth of the primary particles forming the nickel-cobalt-manganese composite hydroxide is suppressed, and secondary particles consisting of fine primary particles and having a large number of spaces or fine voids dispersed in the particle center are formed.

A non-oxidizing atmosphere refers to a mixed atmosphere of oxygen with an oxygen concentration of 5.0% by volume or less, preferably 2.5% by volume or less, and more preferably 1.0% by volume or less, and an inert gas. Means for maintaining such a non-oxidizing atmosphere within the reaction vessel include circulating an inert gas such as nitrogen into the reaction vessel space, and further bubbling an inert gas into the reaction solution. The preferred flow rate of bubbling in the crystallization step S10 is 3 to 7 L/min, and more preferably about 5 L/min.

On the other hand, an oxidizing atmosphere refers to an atmosphere in which the oxygen concentration exceeds 5.0% by volume, preferably 10.0% by volume or more, and more preferably 15.0% by volume or more. Means for maintaining the space inside the reaction vessel in such an oxidizing atmosphere include circulating air or the like into the space inside the reaction vessel, and further bubbling air or the like into the reaction solution.

When creating a solid structure such as the nickel manganese cobalt composite hydroxide according to one embodiment of the present invention, it is preferable to make the atmosphere in the reaction tank an inert atmosphere or a non-oxidizing atmosphere in which the oxygen concentration is controlled to 0.2% by volume or less during the crystallization step S10.

The nucleation step S11 and the particle growth step S12 have been described above, but the reaction atmosphere is controlled simultaneously while nucleation and particle growth are taking place.

<2-2. Cleaning process>
In the washing step S20, the transition metal composite hydroxide obtained in the crystallization step S10 is washed with a washing liquid.

[Cleaning fluid type]
In the washing step S20, washing is performed with a washing solution based on an alkali metal salt or ammonium salt of a carbonate, hydrogen carbonate (bicarbonate), or hydroxide. Preferably, the transition metal composite hydroxide is washed with a washing solution in which a carbonate, hydrogen carbonate (bicarbonate), or a mixture thereof is dissolved in water.

By doing so, it is possible to efficiently remove impurity anions such as sulfate and chlorine radicals by utilizing a substitution reaction with the carbonate ions and hydrogen carbonate ions (bicarbonate ions) in the cleaning solution. In addition, by using carbonates and hydrogen carbonates (bicarbonates), it is possible to suppress the inclusion of alkali metals such as sodium compared to when hydroxides are used. In addition, when hydroxides are used in transition metal composite hydroxides that have a porous structure, it is difficult to remove impurities inside the particles, and in this respect, too, it is more effective to use carbonates and hydrogen carbonates (bicarbonates).

As the carbonate, it is preferable to select sodium carbonate, potassium carbonate, or ammonium carbonate, and as the hydrogen carbonate (bicarbonate), it is preferable to select sodium hydrogen carbonate, potassium hydrogen carbonate, or ammonium hydrogen carbonate. Furthermore, by selecting an ammonium salt from among the carbonates and hydrogen carbonates (bicarbonates), it is possible to efficiently remove cations such as sodium, which are impurities, by utilizing a substitution reaction with the ammonium ions in the cleaning solution. Furthermore, by selecting ammonium hydrogen carbonate from among the ammonium salts, it is possible to most efficiently remove cations such as sodium.

This is because, in addition to the substitution reaction between cations such as sodium and ammonium ions, the superior properties of ammonium bicarbonate compared to other salts, namely the high foaming efficiency of carbon dioxide gas when used as a cleaning solution, are thought to contribute greatly to the removal of cations such as sodium.

[Concentration and pH]
The concentration of the ammonium bicarbonate solution, which is the cleaning solution, is 0.05 mol/L or more. If the concentration is less than 0.05 mol/L, the effect of removing impurities such as sulfate radicals, chlorine radicals, and sodium may decrease. If the concentration is 0.05 mol/L or more, the effect of removing these impurities remains unchanged. Therefore, adding an excess of ammonium bicarbonate (ammonium bicarbonate) increases costs and affects environmental loads such as wastewater standards, so it is preferable to set the upper limit concentration at about 1.0 mol/L.

The pH of the ammonium bicarbonate solution does not need to be adjusted if the concentration is 0.05 mol/L or more, and can be left at its natural pH. If the concentration is 0.05 to 1.0 mol/L, the pH will be in the range of approximately 8.0 to 9.0.

[Liquid temperature]
The temperature of the ammonium bicarbonate solution, which is the cleaning solution, is not particularly limited, but is preferably 15 to 50° C. If the temperature of the solution is within the above range, the substitution reaction with impurities and the bubbling effect of carbon dioxide gas generated from ammonium bicarbonate are more favorable, and the removal of impurities proceeds efficiently.

[Liquid volume]
The amount of the ammonium hydrogen carbonate solution, which is the cleaning solution, is preferably 1 to 20 L per 1 kg of nickel manganese cobalt composite hydroxide (slurry concentration is 50 to 1000 g/L). If the amount is less than 1 L, sufficient impurity removal effect may not be obtained. Even if a liquid amount exceeding 20 L is used, the impurity removal effect remains unchanged, and an excessive liquid amount increases costs, affects environmental loads such as wastewater standards, and is also a factor in increasing the load of wastewater volume in wastewater treatment.

[Washing time]
The washing time with the ammonium hydrogen carbonate solution is not particularly limited as long as it can sufficiently remove impurities, but it is usually 0.5 to 2 hours.

[Cleaning method]
The washing method may be 1) a general washing method in which nickel manganese cobalt composite hydroxide is added to an ammonium hydrogen carbonate solution, the slurry is stirred and washed, and then filtered, or 2) a liquid-passing washing method may be performed in which a slurry containing nickel manganese cobalt composite hydroxide produced by neutralization crystallization is supplied to a filter such as a filter press and an ammonium hydrogen carbonate solution is passed through the slurry. Liquid-passing washing is more preferable because it has a high impurity removal effect, can perform filtration and washing continuously in the same equipment, and is highly productive.

After washing with the ammonium bicarbonate solution, the washing liquid containing impurities washed out by the substitution reaction may adhere to the nickel manganese cobalt composite hydroxide, so it is preferable to finally wash with water. Furthermore, after washing with water, it is preferable to perform a drying process (not shown) to dry the adhering water from the filtered nickel manganese cobalt composite hydroxide.

The nickel manganese cobalt composite hydroxide obtained through the washing step S20 is a nickel manganese cobalt composite hydroxide, which is a precursor of a positive electrode active material, and is composed of secondary particles in which primary particles containing nickel, manganese, and cobalt are aggregated, or the primary particles and the secondary particles, and is characterized in that the sodium content contained in the nickel manganese cobalt composite hydroxide is less than 0.0005 mass%.

The method for producing nickel manganese cobalt composite hydroxide according to one embodiment of the present invention can provide a method for producing nickel manganese cobalt composite hydroxide, which is a precursor of the positive electrode active material of lithium ion secondary batteries, capable of reliably reducing the sodium content and improving battery characteristics.

Next, the nickel manganese cobalt composite hydroxide, the method for producing the nickel manganese cobalt composite hydroxide, and the lithium nickel manganese cobalt composite oxide according to one embodiment of the present invention will be described in detail with reference to examples. Note that the present invention is not limited to these examples.

For Examples 1 to 13 and Comparative Examples 1 to 9, the transition metal composite hydroxide obtained in the crystallization process was washed, filtered, and dried to recover the precursor nickel manganese cobalt composite hydroxide, and then various analyses were performed using the following methods.

[composition]
The composition was analyzed by acid decomposition-ICP emission spectrometry, and a multi-type ICP emission spectrometry analyzer, ICPE-9000 (manufactured by Shimadzu Corporation), was used for the measurements.

[Sodium content]
The sodium content was analyzed by acid decomposition-atomic absorption spectrometry, and an atomic absorption spectrophotometer 240AA (manufactured by Agilent Technologies, Inc.) was used as an atomic absorption analyzer for the measurement.

[Sulfate content]
The sulfate radical content was determined by analyzing the total sulfur content by acid decomposition-ICP atomic emission spectrometry and converting the total sulfur content into sulfate radical (SO ₄ ²⁻ ). The measurement was performed using a multi-type ICP atomic emission spectrometry analyzer, ICPE-9000 (manufactured by Shimadzu Corporation).

[Chlorine content]
The chlorine radical content was analyzed by X-ray fluorescence spectrometry (XRF) either directly from the sample or by separating the chlorine radical contained in the sample in the form of silver chloride by distillation. For the measurement, an X-ray fluorescence analyzer, Axios (manufactured by Spectris, Inc.), was used.

[Average particle size and particle size distribution]
The average particle size (MV) and particle size distribution [(d90-d10)/average particle size] were determined from the volume-based distribution measured using a laser diffraction/scattering method, using a Microtrac MT3300EXII (manufactured by Microtrac Bell Co., Ltd.), a particle size distribution measuring device using a laser diffraction/scattering method.

[Specific surface area]
The specific surface area was analyzed by a nitrogen gas adsorption/desorption method according to the BET single point method, and a gas flow type specific surface area measuring device, Macsorb 1200 series (manufactured by Mountec Co., Ltd.), was used for the measurement.

[Production and evaluation of positive electrode active material]
Furthermore, the lithium metal composite oxide, more specifically the lithium nickel manganese cobalt composite oxide, which is the positive electrode active material made from the nickel manganese cobalt composite hydroxide of the present invention as a raw material, was produced and evaluated by the following method.

[A. Production of positive electrode active material]
The precursor nickel manganese cobalt composite hydroxide was heat-treated at 700°C for 6 hours in an air stream (oxygen: 21% by volume), and the metal composite oxide was recovered. Next, lithium hydroxide, a lithium compound, was weighed out so that Li/Me was 1.025, and mixed with the recovered metal composite oxide to prepare a lithium mixture. A shaker mixer (TURBULA-Type T2C manufactured by WAB) was used for the mixing operation.

Next, the lithium mixture was calcined at 500°C for 4 hours in an oxygen (oxygen: 100% by volume) stream, then sintered at 730°C for 24 hours, cooled, and crushed to obtain lithium nickel manganese cobalt composite oxide.

[B. Evaluation of Positive Electrode Active Material]
The above-mentioned analytical method and analytical equipment were used to analyze the sodium content, sulfate content, and chlorine content of the obtained lithium nickel manganese cobalt composite oxide. The Me site occupancy rate, which indicates the crystallinity of the lithium nickel manganese cobalt composite oxide, was calculated by performing Rietveld analysis from a diffraction pattern measured using an X-ray diffraction analyzer (XRD). An X-ray diffraction analyzer X'Pert-PRO (manufactured by Spectris Co., Ltd.) was used for the measurement. The Me site occupancy rate indicates the presence ratio of metal elements that nickel, manganese, cobalt, and additive element M of the lithium nickel manganese cobalt composite oxide occupy in the metal layer (Me site) of the layered structure. The Me site occupancy rate is correlated with battery characteristics, and the higher the Me site occupancy rate, the better the battery characteristics.

The conditions for the examples and comparative examples are explained below.

Example 1
In Example 1, 0.9 L of water was placed in a crystallization reaction tank (5 L) in the crystallization step, and the temperature inside the tank was set to 40° C. while stirring. Nitrogen gas was circulated through the reaction tank to create a nitrogen atmosphere. The oxygen concentration in the reaction tank space at this time was 2.0% by volume.

An appropriate amount of 25% sodium hydroxide aqueous solution and 25% ammonia water, which is an ammonium ion donor, were added to the water in the reaction tank, and the pH of the reaction solution in the tank was adjusted to 12.8, measured based on a liquid temperature of 25°C. The ammonium ion concentration of the reaction solution was also adjusted to 10 g/L.

Next, nickel sulfate, manganese sulfate, and cobalt chloride were dissolved in water to prepare a 2.0 mol/L raw material solution. In this raw material solution, the elemental molar ratio of each metal was adjusted to Ni:Mn:Co = 1:1:1. Furthermore, sodium hydroxide, which is an alkali metal hydroxide, and sodium carbonate, which is a carbonate, were dissolved in water so that [CO ₃ ^2- ]/[OH ^- ] was 0.025 to prepare an alkaline solution.

The raw material solution was added to the reaction solution in the reaction tank at 12.9 ml/min, and the ammonium ion donor and alkaline solution were also added to the reaction solution at a constant rate. Nucleation was performed by controlling the pH to 12.8 (nucleation process pH) and carrying out crystallization for 2 minutes and 30 seconds while maintaining the ammonium ion concentration in the reaction solution at 10 g/L.

After that, 64% sulfuric acid was added until the pH of the reaction solution reached 11.6 (particle growth process pH) measured at a liquid temperature of 25°C. After the pH of the reaction solution reached 11.6, measured at a liquid temperature of 25°C, the supply of the raw material solution, ammonium ion donor, and alkaline solution was resumed, and the pH was controlled at 11.6 while crystallization was continued for 4 hours to grow particles, thereby obtaining a transition metal composite hydroxide.

The obtained transition metal composite hydroxide was subjected to solid-liquid separation using a filter press filter, and impurities were removed by passing 5 L of washing solution through the filter press filter for every 1 kg of transition metal composite hydroxide, using a 0.05 mol/L ammonium bicarbonate solution as a washing solution, and then washing was performed by passing water through the filter press filter. The water adhering to the washed transition metal composite hydroxide was then dried to obtain the precursor nickel manganese cobalt composite hydroxide.

Example 2
In Example 2, when nickel sulfate, manganese sulfate, and cobalt chloride were dissolved in water to prepare a 2.0 mol/L raw material solution, a molar ratio of nickel, manganese, and cobalt in the raw material solution was adjusted to Ni:Mn:Co=6:2:2, and a nickel-cobalt-manganese composite hydroxide was obtained in the same manner as in Example 1, except that the molar ratio was adjusted to Ni:Mn:Co=6:2:2 in the raw material solution.

Example 3
In Example 3, when nickel sulfate, manganese sulfate, and cobalt chloride were dissolved in water to prepare a 2.0 mol/L raw material solution, a molar ratio of nickel, manganese, and cobalt in the raw material solution was adjusted to Ni:Mn:Co=2:7:1, and a nickel-cobalt-manganese composite hydroxide was obtained in the same manner as in Example 1, except that the molar ratio was adjusted to Ni:Mn:Co=2:7:1 in the raw material solution.

Example 4
In Example 4, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that when preparing the alkaline solution, the ratio [CO ₃ ²⁻ ]/[OH ⁻ ] was adjusted to 0.003.

Example 5
In Example 5, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the alkaline solution was adjusted so that [CO ₃ ²⁻ ]/[OH ⁻ ] was 0.048.

Example 6
In Example 6, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the pH in the nucleation step was 13.6.

(Example 7)
In Example 7, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the pH in the nucleation step was 12.3.

(Example 8)
In Example 8, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the pH in the particle growth step was 11.8.

(Example 9)
In Example 9, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the pH in the particle growth step was 10.6.

(Example 10)
In Example 10, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that when preparing the alkaline solution, potassium hydroxide was used as the alkali metal hydroxide and potassium carbonate was used as the carbonate.

Example 11
In Example 11, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that, when preparing the alkaline solution, ammonium carbonate was used as the carbonate and the ammonium ion concentration was adjusted to 20 g/L.

Example 12
In Example 12, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the temperature inside the tank was set to 35°C.

Example 13
In Example 13, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that an ammonium bicarbonate solution with a concentration of 1.00 mol/L was used as the cleaning liquid.

(Comparative Example 1)
In Comparative Example 1, when nickel sulfate, manganese sulfate, and cobalt chloride were dissolved in water to prepare a 2.0 mol/L raw material solution, the molar ratio of nickel, manganese, and cobalt in the raw material solution was adjusted to Ni:Mn:Co=2:6:2, and the ratio [CO ₃ ²⁻ ]/[OH ⁻ ] was adjusted to 0.001. A nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1.

(Comparative Example 2)
In Comparative Example 2, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that only sodium hydroxide was used to adjust the alkaline solution and [CO ₃ ²⁻ ]/[OH ⁻ ] was not taken into consideration.

(Comparative Example 3)
In Comparative Example 3, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the alkaline solution was adjusted so that [CO ₃ ²⁻ ]/[OH ⁻ ] was 0.001.

(Comparative Example 4)
In Comparative Example 4, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the alkaline solution was adjusted so that [CO ₃ ²⁻ ]/[OH ⁻ ] was 0.055.

(Comparative Example 5)
In Comparative Example 5, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that the washing step was omitted and washing with an ammonium hydrogen carbonate solution was not performed.

(Comparative Example 6)
In Comparative Example 6, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that an ammonium bicarbonate solution with a concentration of 0.02 mol/L was used as the cleaning liquid.

(Comparative Example 7)
In Comparative Example 7, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that an ammonium carbonate solution was used as the cleaning liquid.

(Comparative Example 8)
In Comparative Example 8, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that a sodium hydrogen carbonate solution was used as the cleaning liquid.

(Comparative Example 9)
In Comparative Example 9, a nickel manganese cobalt composite hydroxide was obtained in the same manner as in Example 1, except that a sodium carbonate solution was used as the cleaning liquid.

The above conditions and results are shown in Tables 1 and 2.

(comprehensive evaluation)
As shown in Tables 1 and 2, in Examples 1 to 13, the conditions of the crystallization step and the washing step in the nickel manganese cobalt composite hydroxide, which is the precursor, were all within the preferred range. Therefore, not only the nickel manganese cobalt composite hydroxide but also the lithium nickel manganese cobalt composite oxide, which is the positive electrode active material, had the sodium content, sulfate radical content, and chlorine radical content sufficiently reduced in the impurity removal. Furthermore, in the lithium nickel manganese cobalt composite oxide, the Me site occupancy rate exceeded 93.0%, resulting in excellent crystallinity and improved battery characteristics.

In particular, the sodium content of both the precursor and the positive electrode active material showed very good results, with all example data being below the lower limit of quantification (analysis) (0.0005% by mass).

The lower limit of quantification here means the minimum amount or minimum concentration at which a target component can be analyzed (quantified) using a certain analytical method. The minimum amount (value) at which a signal of the target component can be detected in a measurement is called the detection limit, and the minimum amount (value) at which the signal of the target component obtained in a measurement is reliable is called the lower limit of measurement. Furthermore, the lower limit of quantification can be calculated by multiplying the lower limit of measurement by the dilution factor, which indicates how much the original analytical sample has been concentrated or diluted in the process of preparing the analytical sample into the measurement specimen liquid.

In other words, the sodium content in this invention is 0.05 μg/mL, which is the lower limit of measurement for an atomic absorption spectrometer, and because 1 g of the analytical sample was acid-decomposed to prepare 100 mL of measurement specimen liquid (dilution ratio: 100 times), the lower limit of quantification is 5 ppm (μg/g), or 0.0005% by mass.

In contrast, in Comparative Examples 1 to 9, the [CO ₃ ²⁻ ]/[OH ⁻ ] ratio when preparing the alkaline solution and the concentration of the ammonium bicarbonate solution used as the cleaning liquid were not within the preferred range, or a cleaning liquid other than ammonium bicarbonate solution was used, so that the excellent effects of the Examples were not obtained.

As a result, we have been able to provide nickel manganese cobalt composite hydroxide, a method for producing nickel manganese cobalt composite hydroxide, and lithium nickel manganese cobalt composite oxide, which are precursors of positive electrode active materials for lithium ion secondary batteries that can reliably reduce the sodium content in particular and improve battery characteristics. It is also expected that this will lead to the provision of lithium ion secondary batteries with excellent characteristics.

Although each embodiment and each example of the present invention has been described in detail above, it will be readily apparent to those skilled in the art that many modifications are possible that do not substantially deviate from the novel features and effects of the present invention. Therefore, all such modifications are intended to be included within the scope of the present invention.

For example, a term described at least once in the specification or drawings together with a different term having a broader or synonymous meaning may be replaced with that different term anywhere in the specification or drawings. Furthermore, the nickel manganese cobalt composite hydroxide, the method for producing the nickel manganese cobalt composite hydroxide, and the configuration and operation of the lithium nickel manganese cobalt composite oxide are not limited to those described in the embodiments and examples of the present invention, and various modifications are possible.

S10 Crystallization process, S11 Nucleation process, S12 Particle growth process, S20 Washing process

Claims (5)

A nickel-manganese-cobalt composite hydroxide, which is a precursor of a positive electrode active material, is composed of secondary particles in which primary particles containing nickel, manganese, and cobalt are aggregated, or the primary particles and the secondary particles,
The nickel manganese cobalt composite hydroxide has a sodium content of less than 0.0005 mass% and a chlorine content of 0.01 mass% or less. 2. The nickel manganese cobalt composite hydroxide according to claim 1, wherein the nickel manganese cobalt composite hydroxide has a specific surface area of 10 to 20 m ² /g. The nickel manganese cobalt composite hydroxide according to claim 1 or 2, characterized in that the content of sulfate radicals contained in the nickel manganese cobalt composite hydroxide is 0.2 mass% or less. The nickel manganese cobalt composite hydroxide according to any one of claims 1 to 3, characterized in that the index showing the spread of the particle size distribution of the nickel manganese cobalt composite hydroxide, [(d90-d10)/average particle size], is 0.55 or less. The nickel manganese cobalt composite hydroxide according to any one of claims 1 to 4, characterized in that the nickel manganese cobalt composite hydroxide is represented by the general formula: Ni _x Co _y Mn _z M _t (OH) _2+a (wherein x + y + z + t = 1, 0.20 ≤ x ≤ 0.80, 0.10 ≤ y ≤ 0.50, 0.10 ≤ z ≤ 0.90, 0 ≤ t ≤ 0.10, 0 ≤ a ≤ 0.5, and M is one or more of Mg, Ca, Al, Ti, V, Cr, Zr, Nb, Mo, and W).