JPS5813499B2 - 水和酸化チタンの製造方法 - Google Patents
水和酸化チタンの製造方法Info
- Publication number
- JPS5813499B2 JPS5813499B2 JP11361976A JP11361976A JPS5813499B2 JP S5813499 B2 JPS5813499 B2 JP S5813499B2 JP 11361976 A JP11361976 A JP 11361976A JP 11361976 A JP11361976 A JP 11361976A JP S5813499 B2 JPS5813499 B2 JP S5813499B2
- Authority
- JP
- Japan
- Prior art keywords
- water
- titanium oxide
- acid
- washing
- precipitate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
本発明は、チタンの塩酸酸性水溶液を加熱加水分解して
得られる水利酸化チタンの精製方法に関する。
得られる水利酸化チタンの精製方法に関する。
水利酸化チタンの工業的製造は、専らチタンの硫酸酸性
水溶液の加熱加水分解によっていたが、この場合は生成
する水利酸化チタンが凝集性沈澱物であって、常法によ
って水洗精製するのにさほどの困難性はない。
水溶液の加熱加水分解によっていたが、この場合は生成
する水利酸化チタンが凝集性沈澱物であって、常法によ
って水洗精製するのにさほどの困難性はない。
一方、チタンの塩酸酸性水溶液を加熱加水分解し℃水和
酸化チタンを製造する手段もよく知られているが、生成
する沈澱物を水洗しようとすると解膠による微細コロイ
ド粒子が生じ、沖過不能となったり、著るしい戸過洩れ
が起ったりして、工業的実施が困難である。
酸化チタンを製造する手段もよく知られているが、生成
する沈澱物を水洗しようとすると解膠による微細コロイ
ド粒子が生じ、沖過不能となったり、著るしい戸過洩れ
が起ったりして、工業的実施が困難である。
高分子凝集剤を添加して沖過性を改良することが考えら
れるが、水洗すればやはり解膠が起り、前記の不都合を
解消できない。
れるが、水洗すればやはり解膠が起り、前記の不都合を
解消できない。
ところか、水利酸化チタン吸着性の多官能保有物質と有
機高分子凝集剤とを併用すれば沈澱を凝集させたま＼で
水洗することができ、容易にかつ十分に付着不純物を除
去できることがわかった。
機高分子凝集剤とを併用すれば沈澱を凝集させたま＼で
水洗することができ、容易にかつ十分に付着不純物を除
去できることがわかった。
本発明は、チタンの塩酸酸性水溶液を加熱加水分解し生
成する沈澱物を水洗する水和酸化チタンの製造方法にお
いて、加水分解生成沈澱物を、多塩基鉱酸、カルボキシ
ル基及び（又は）水酸基を２以上有する有機酸又はフェ
ノール類、並にそれらの塩の少くとも１種と、有機高分
子凝集剤の少くとも１種とで処理した後に水洗すること
を特徴とする水利酸化チタンの製造方法である。
成する沈澱物を水洗する水和酸化チタンの製造方法にお
いて、加水分解生成沈澱物を、多塩基鉱酸、カルボキシ
ル基及び（又は）水酸基を２以上有する有機酸又はフェ
ノール類、並にそれらの塩の少くとも１種と、有機高分
子凝集剤の少くとも１種とで処理した後に水洗すること
を特徴とする水利酸化チタンの製造方法である。
チタンの塩酸酸性水溶液は、工業的に生産されている四
塩化チタンを水に溶解させたり、水利酸化チタンを塩酸
に溶解させたりして得られる。
塩化チタンを水に溶解させたり、水利酸化チタンを塩酸
に溶解させたりして得られる。
加熱加水分解は、よく知られているように、これらの液
を沸点又はその近くの温度に加熱することによっておこ
なわれ、生成する水利酸化チタン沈澱は、微細なコロイ
ド粒子がいくつか凝集してできた集合粒子からなる。
を沸点又はその近くの温度に加熱することによっておこ
なわれ、生成する水利酸化チタン沈澱は、微細なコロイ
ド粒子がいくつか凝集してできた集合粒子からなる。
普通は加水分解時に種晶を用いるが、種晶を用いたとき
は、それを用いないときにくらべてコロイド粒子がより
微細になり、水洗によって解膠が起るとより−そう取扱
いにくくなる。
は、それを用いないときにくらべてコロイド粒子がより
微細になり、水洗によって解膠が起るとより−そう取扱
いにくくなる。
従って加熱加水分解に種晶を用いた場合には本発明を適
用する価値が太きいといえる。
用する価値が太きいといえる。
加熱加水分解によって、母液中に凝集性水利酸化チタン
が析出、沈澱したスラリーが生成する。
が析出、沈澱したスラリーが生成する。
この沈澱を戸別し、水洗して解膠が起った後に本発明の
処理を適用しても再凝集はそれ程期待できない。
処理を適用しても再凝集はそれ程期待できない。
従って本発明においては、前記スラリーやそれを水で希
釈したもの、前記スラリーを水で希釈するか１たけ希釈
しない沖過し母液を除去したケーキなどに水利酸化チタ
ン吸着性の多官能基保有物質と有機高分子凝集剤とを添
加し、攪拌均一化する。
釈したもの、前記スラリーを水で希釈するか１たけ希釈
しない沖過し母液を除去したケーキなどに水利酸化チタ
ン吸着性の多官能基保有物質と有機高分子凝集剤とを添
加し、攪拌均一化する。
多官能基保有物質とは、多塩基鉱酸例えば硫酸、リン酸
、カルボキシル基、水酸基を２以上有する有機酸又はフ
ェノール類例えばクエン酸、酒石酸、マレイン酸、フタ
ル酸、カテコール、ハイトロキノン、ピロガ節一ル、タ
ンニン酸、並びにそれらの塩例えばナトリウム塩、カリ
ウム塩、アンモニウム塩である。
、カルボキシル基、水酸基を２以上有する有機酸又はフ
ェノール類例えばクエン酸、酒石酸、マレイン酸、フタ
ル酸、カテコール、ハイトロキノン、ピロガ節一ル、タ
ンニン酸、並びにそれらの塩例えばナトリウム塩、カリ
ウム塩、アンモニウム塩である。
これらの少くとも１種を塩の場合は酸又はフェノールに
換算して、水和酸化チタンのＴｉ０２基準で１〜１０係
、望ましくは２〜５係添加する。
換算して、水和酸化チタンのＴｉ０２基準で１〜１０係
、望ましくは２〜５係添加する。
この添加は有機高分子凝集剤の添加と同時に或はその後
におこなってもよいが、それに先立つ℃添加し水和酸化
チタン粒子と均一に混合、よく吸着させておく方が、よ
り少い添加量でより懸著な効果をもたらす。
におこなってもよいが、それに先立つ℃添加し水和酸化
チタン粒子と均一に混合、よく吸着させておく方が、よ
り少い添加量でより懸著な効果をもたらす。
併用される有機高分子凝集剤は、一般に凝集剤として使
用されているもので、アニオン系、カチオン系凝集剤が
広く用いられる。
用されているもので、アニオン系、カチオン系凝集剤が
広く用いられる。
例えばチオフロックＷ−０（アライド・コロイド商品）
、クリフロックＸＫ−７７及びＰＡ−３４１（共に栗田
工業商品）、サンポリーＡ−５２０及びＡ−５３０（共
に三共化成商品）、サンフロックＡＨ−２００Ｐ（三洋
化成商品）などをあげることができるが、ノニオン系の
ものは効果が期待できない。
、クリフロックＸＫ−７７及びＰＡ−３４１（共に栗田
工業商品）、サンポリーＡ−５２０及びＡ−５３０（共
に三共化成商品）、サンフロックＡＨ−２００Ｐ（三洋
化成商品）などをあげることができるが、ノニオン系の
ものは効果が期待できない。
これらの少くとも１種を、水利酸化チタンのＴｉ０２基
準で０．０３〜３係、望ましくは０．０５〜１係添加し
、攪拌し均一化する。
準で０．０３〜３係、望ましくは０．０５〜１係添加し
、攪拌し均一化する。
このように処理した水和酸化チタンは、常用の手段で戸
過水洗しても、沈澱粒子の解膠が起らず、戸布漏れや炉
布の目づまりをひきおこすことなく水洗を続けることが
でき、高度に精製された水利酸化チタンが得られる。
過水洗しても、沈澱粒子の解膠が起らず、戸布漏れや炉
布の目づまりをひきおこすことなく水洗を続けることが
でき、高度に精製された水利酸化チタンが得られる。
顔料、触媒、吸着剤、感光材料に使用される場合には普
通蝦焼処理を経るが、その工程で本発明で使用した処理
剤は大部分、分解、気化するので、酸化チタンの基本的
な性質を阻害する恐れはない。
通蝦焼処理を経るが、その工程で本発明で使用した処理
剤は大部分、分解、気化するので、酸化チタンの基本的
な性質を阻害する恐れはない。
実施例 １
濃度が１．５モル／ｌの四塩化チタン溶液に、常用の加
水分解促進用種晶をＴｉＯ２換算で１０係加え、沸点で
２時間加熱して加水分解し、水利酸化チタンを沈澱させ
た。
水分解促進用種晶をＴｉＯ２換算で１０係加え、沸点で
２時間加熱して加水分解し、水利酸化チタンを沈澱させ
た。
生成したスラリーを水で２倍に稀釈した後、５０ｇ／１
水溶液としたタンニン酸をスラリー中のＴｉ０２基準で
２％添加、攪拌した。
水溶液としたタンニン酸をスラリー中のＴｉ０２基準で
２％添加、攪拌した。
タンニン酸の吸着によって淡黄褐色を示すようになった
沈澱を含むスラリーに、０．５ｇ／１水溶液としたカチ
オン系高分子凝集剤チオフロックＷ−０をスラリー中の
Ｔｉｅ２基準で０．１係添加した。
沈澱を含むスラリーに、０．５ｇ／１水溶液としたカチ
オン系高分子凝集剤チオフロックＷ−０をスラリー中の
Ｔｉｅ２基準で０．１係添加した。
このスラリーを沢過、水洗したが、沈澱の解膠は起らず
、沢過洩れや沢布の目づまりによる障害は認められなか
った。
、沢過洩れや沢布の目づまりによる障害は認められなか
った。
比較のために、タンニン酸を添加しないことを除いて同
様の操作をおこなったところ、水洗中に解膠による沢過
洩れが起り、同時にｒ過速度が低下、十分な水洗は不可
能であった。
様の操作をおこなったところ、水洗中に解膠による沢過
洩れが起り、同時にｒ過速度が低下、十分な水洗は不可
能であった。
実施例 ２
タンニン酸を２％添加するのに代えて酒石酸を３係添加
した以外は実施例１と同様にして、十分に水洗された水
和酸化チタンを得た。
した以外は実施例１と同様にして、十分に水洗された水
和酸化チタンを得た。
実施例 ３
タンニン酸２係に代えてクエン酸３係を用いた以外は実
施例１と同様にして、十分に水洗された水和酸化チタン
を得た。
施例１と同様にして、十分に水洗された水和酸化チタン
を得た。
実施例 ４
タンニン酸２帽こ代えて硫安９係（硫酸換算量）を用い
た以外は実施例１と同様にして、十分に水洗された水利
酸化チタンを得た。
た以外は実施例１と同様にして、十分に水洗された水利
酸化チタンを得た。
Claims (1)
- １ チタンの塩酸酸性水溶液を加熱加水分解し生成する
沈澱物を水洗する水利酸化チタンの製造方法において、
加水分解生成沈澱物を、多塩基鉱酸、カルボキシル基及
び（又は）水酸基を２以上有する有機酸又はフェノール
類い並にそれらの塩の少くとも１種と、有機高分子凝集
剤の少くとも１種とで処理した後に水洗することを特徴
とする水利酸化チタンの製造方法。