JPS6335736B2 - - Google Patents
Info
- Publication number
- JPS6335736B2 JPS6335736B2 JP1033679A JP1033679A JPS6335736B2 JP S6335736 B2 JPS6335736 B2 JP S6335736B2 JP 1033679 A JP1033679 A JP 1033679A JP 1033679 A JP1033679 A JP 1033679A JP S6335736 B2 JPS6335736 B2 JP S6335736B2
- Authority
- JP
- Japan
- Prior art keywords
- disk
- twisting
- present
- false
- polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】 〔本発明の技術分野〕 本発明は摩擦仮撚用デイスクに関する。[Detailed description of the invention] [Technical field of the present invention] The present invention relates to friction false-twisting discs.
更に詳しくは、高速仮撚加工の加ネン部材とし
て、デイスク寿命の著しい延長効果を呈するポリ
ウレタンデイスクに関するものである。 More specifically, the present invention relates to a polyurethane disk that can be used as a tightening member for high-speed false twisting and has the effect of significantly extending the disk life.
ここ数年、ポリエステル繊維の仮撚加工の高速
化が進み、市場においては600ｍ／minを越す高
速加工機、特に摩擦仮撚加工機が主流となつてき
ている。その摩擦加ネン部についてはほとんどの
機械が３軸外接型を装着しているものであるが、
最も重要なる糸を加ネンする摩擦部材については
得られる加工糸の品質の点でポリウレタンデイス
クが一般に優れているが、反面、該ポリウレタン
デイスクは耐久性が大きな問題としてクローズア
ツプされている。
In recent years, the speed of false twisting processing of polyester fibers has increased, and high-speed processing machines exceeding 600 m/min, especially friction false twisting machines, have become mainstream in the market. Most machines are equipped with a 3-axis external type for the friction applying part.
As for the most important friction member for adding yarn, polyurethane disks are generally superior in terms of the quality of processed yarn obtained, but on the other hand, the durability of polyurethane disks has been highlighted as a major problem.
すなわち従前から知られている特公昭39−
10688号公報に記載されているフランジ型仮撚機
のポリウレタンを、上記３軸外接型仮撚機のデイ
スクにも用いても耐光性が悪く、長期安定使用が
できず実用上大きな問題であつた。 In other words, the previously known Tokuko Sho 39-
Even if the polyurethane of the flange type false twister described in Publication No. 10688 was used for the disc of the above-mentioned 3-axis circumscribed false twister, the light resistance was poor and it could not be used stably for a long time, which was a big problem in practice. .
そこで、本発明者らは加工糸の品質上最も優れ
ているポリウレタンを主成分とするデイスクの耐
久性を向上すべく鋭意検討を進めた結果、500ｍ
μ以下の短波長の光によつてデイスク表面が劣化
しているという知見を得た。すなわち、デイスク
寿命の問題はこのような短波長の光がデイスクに
照射されないように仮撚デイスク部をカバーする
ことによつて大幅に改善されることを本発明者ら
は既に提案した（特開昭54−11351号公報）が、
糸かけ操作上かなり作業もはん雑になり、またデ
イスクの保管時、組立時など不用意に短波長の光
にされされることがありうるわけであり、全く問
題が解決されてはいないのが現状である。また摩
耗耐久性、硬度、強靭性、仮撚特性においても従
来のものは、実用上不満足なものであつた。 Therefore, the present inventors conducted intensive studies to improve the durability of disks whose main component is polyurethane, which has the highest quality of processed yarn.
We obtained the knowledge that the disk surface is degraded by light with short wavelengths below μ. In other words, the present inventors have already proposed that the problem of disk life can be greatly improved by covering the false-twisted disk portion to prevent such short wavelength light from irradiating the disk (see Japanese Patent Application Laid-Open No. Publication No. 54-11351) is
The threading operation becomes quite complicated, and it is possible that the disc may be exposed to short wavelength light inadvertently when storing or assembling the disc, so this problem has not been solved at all. is the current situation. Furthermore, conventional products were unsatisfactory in terms of abrasion durability, hardness, toughness, and false twisting properties.
このような点から、本発明者らはさらに検討を
重ねた結果、デイスク自身の耐光性を積極的に向
上させ、かつ糸条との耐摩耗性性、仮撚特性を向
上させた本発明の摩擦仮撚用デイスクを見出した
ものである。すなわち、本発明は、特定の素材の
ポリウレタンをデイスクとして用いることにより
耐光性、耐久性を向上するにある。
From this point of view, the inventors of the present invention have conducted further studies and have developed the present invention, which actively improves the light resistance of the disk itself, and also improves the abrasion resistance and false twisting characteristics of the disk itself. We have discovered a disk for friction false twisting. That is, the present invention aims to improve light resistance and durability by using a specific material of polyurethane as a disk.
すなわち、本発明のデイスクは、摩擦仮撚部材
として、次式のモノマーをイソシアネート成分の
主成分とし、かつポリオールとしてポリエステル
を主成分としてなるポリエステルポリウレタンで
成型されてなることを特徴とする摩擦仮撚用デイ
スクである。
That is, the disk of the present invention is a friction false-twisting member made of a polyester polyurethane containing a monomer of the following formula as the main isocyanate component and polyester as the main component. It is a disk for use.
（ただし、R1、R2は有機基。）
〔本発明の作用・効果〕
本発明は、ポリウレタンのイソシアネート成分
に着目し、
（R1、R2：有機基。）
であらわされるジイソシアネートを用いてなるも
のが、耐光性、耐久性、摩擦特性等に著しく優れ
ているという知見を得たものである。 (However, R 1 and R 2 are organic groups.) [Actions and effects of the present invention] The present invention focuses on the isocyanate component of polyurethane, (R 1 , R 2 : Organic groups.) It has been found that products using diisocyanates represented by the following are significantly superior in light resistance, durability, friction characteristics, etc.
上記イソシアネートは、Industrial＆
Engineering Chemistry.Vol6No.1.March.1967年
の第12〜19頁に公知となつているものである。し
かしかかる公知文献のイソシアネートを含むポリ
ウレタンは、エラストマー、すなわちゴム弾性を
示すプラスチツクとしての利用可能性を示すだけ
であり、本発明のような硬度が必要で、少々の力
では変形しないことが必要な成形体への応用は何
ら知られているものではない。まして摩擦素材に
用いるとか、耐光性に優れている等の特性は全く
知られておらず、本発明の技術分野、すなわち繊
維業界においては初めての試みである。特にかか
るイソシアネートは驚くべき耐光性向上効果を奏
する。 The above isocyanates are industrial &
Engineering Chemistry.Vol6No.1.March.1967, pages 12-19. However, the isocyanate-containing polyurethane disclosed in such known documents only shows the possibility of being used as an elastomer, that is, a plastic exhibiting rubber elasticity; Application to molded objects is not known at all. Moreover, its properties such as its use as a friction material and its excellent light resistance are completely unknown, and this is the first attempt in the technical field of the present invention, that is, in the textile industry. In particular, such isocyanates have a surprising effect of improving light resistance.
本発明のデイスクは、上記のイソシアネート成
分とポリエステルとを主成分として重合反応して
得られるポリウレタンを少なくとも摩擦仮撚デイ
スクの施撚部材として使用するものであるが、ポ
リウレタンを製造する工程において、ポリエステ
ルに加えてポリエーテルを少量加えて共重合体と
することもできる。共重合比は、本発明のポリエ
ステルポリウレタンの物性が大きく低下しない程
度であれば任意のものとすることができる。ポリ
エステルとしてはアジピン酸、フタル酸などの２
塩基性酸とジオールとからなる公知のポリエステ
ルを用いることができる。またポリエーテルはポ
リテトラヒドロフラン、エチレンオキシドなどが
用いられる。 The disc of the present invention uses polyurethane obtained by a polymerization reaction of the above-mentioned isocyanate component and polyester as main components, at least as a twisting member of the friction false twist disc. In addition, a small amount of polyether can be added to form a copolymer. The copolymerization ratio can be set to any value as long as the physical properties of the polyester polyurethane of the present invention are not significantly reduced. Polyesters include adipic acid, phthalic acid, etc.
A known polyester consisting of a basic acid and a diol can be used. Further, as the polyether, polytetrahydrofuran, ethylene oxide, etc. are used.
むろん、本発明においてイソシアネート成分の
100％が上記の式で表わされるモノマーである必
要は必ずしもなく、本発明の効果を損わない範囲
内で他のモノマーが含まれていてもよいことは云
うまでもない。 Of course, in the present invention, the isocyanate component is
It goes without saying that 100% of the monomer does not necessarily have to be the monomer represented by the above formula, and other monomers may be included within the range that does not impair the effects of the present invention.
上記のR1、R2の有機基はアルキル基であるも
のが特によい。また、このR1、R2は、イソシア
ネート基に対してオルト位にあるものが、一層の
耐光性向上効果を有するようである。 The above organic groups for R 1 and R 2 are particularly preferably alkyl groups. Furthermore, it appears that R 1 and R 2 in the ortho position relative to the isocyanate group have a further effect of improving light resistance.
本発明者らの知見によれば、上記のイソシアネ
ート成分として、トリジンジイソシアネートを用
いてなるポリウレタンデイスクが最も顕著な耐光
性向上効果を呈する。 According to the findings of the present inventors, a polyurethane disc using tolidine diisocyanate as the above-mentioned isocyanate component exhibits the most remarkable effect of improving light resistance.
また本発明においてポリオールとしてポリエス
テルを主重合成分とせしめたことは、耐光性を更
に大幅に高め、硬度、強靭性を高め、これが耐摩
耗特性を大幅に良好なものとし、併せて仮撚特性
を大幅に向上せしめるという顕著な効果を奏す
る。 In addition, the use of polyester as the main polymerization component in the polyol in the present invention significantly increases light resistance, hardness, and toughness, which greatly improves abrasion resistance and also improves false twisting properties. It has the remarkable effect of significantly improving the results.
次に図面を用いて説明する。 Next, it will be explained using drawings.
第１図は３軸を有する摩擦仮ヨリ装置の見取図
である。ベルト１の走行によつてプーリ２を介し
て回転する軸３，４，５、に装着された円板６，
７，８、の表面の摩擦力によつて走行糸条９を施
撚する。施撚作用は円板６，７，８、と走行糸条
９との接触状態、すなわち摩擦係数、糸経路によ
つて支配される。したがつて、安定した仮撚加工
を長期にわたつて維持するには、円板６，７，
８、の表面状態、形状が初期の設定からできるだ
け変化しないことが重要である。 FIG. 1 is a sketch of a frictional twisting device having three axes. a disk 6 mounted on shafts 3, 4, 5 which rotate through pulleys 2 as the belt 1 runs;
The running thread 9 is twisted by the frictional force on the surfaces of the threads 7 and 8. The twisting action is controlled by the state of contact between the disks 6, 7, 8 and the running yarn 9, that is, the coefficient of friction and the yarn path. Therefore, in order to maintain stable false twisting over a long period of time, the disks 6, 7,
It is important that the surface condition and shape of 8 do not change as much as possible from the initial settings.
第２図は円板６，７，８、の一例を示すもの
で、アルミあるいはプラスチツクで成形された芯
金１０の外周部に本発明のポリエステルポリウレ
タン１１を接着したものである。該ポリエステル
ポリウレタン１１の外周面は安定した所望の仮撚
を施撚するに適した表面粗さ、硬度、形状に作つ
たものである。 FIG. 2 shows an example of the disks 6, 7, and 8, in which the polyester polyurethane 11 of the present invention is adhered to the outer periphery of a core metal 10 made of aluminum or plastic. The outer peripheral surface of the polyester polyurethane 11 is made to have a surface roughness, hardness, and shape suitable for stable and desired false twisting.
本発明の摩擦仮撚用デイスクは、摩擦仮撚本来
の目的である糸条への加撚作用を何らそこなうこ
となく、均斉な高品質の加工糸を得ることができ
るものである。したがつて、通常の摩擦仮撚加工
と同一のとりあつかいにおいて、デイスクの寿命
を著しく延長し得、得られる加工糸の品質を高品
位に、しかも長期間安定して維持することが可能
である。 The disk for frictional false twisting of the present invention is capable of obtaining uniform, high-quality processed yarn without impairing the twisting effect on the yarn, which is the original purpose of frictional false twisting. Therefore, with the same procedure as normal friction false twisting, the life of the disk can be significantly extended, and the quality of the resulting textured yarn can be maintained stably for a long period of time.
実施例
トリジンジイソシアネートとアジピン酸ポリエ
ステル（ポリエチレンアジペート）を重合反応し
て得られたポリエステルポリウレタンをデイスク
状に成型した。Example A polyester polyurethane obtained by polymerizing tolidine diisocyanate and adipic acid polyester (polyethylene adipate) was molded into a disk shape.
比較例としては一般によく使用されているナフ
タレンジイソシアネートとポリテトラヒドロフラ
ンとからなるポリウレタンを用いた。 As a comparative example, a commonly used polyurethane made of naphthalene diisocyanate and polytetrahydrofuran was used.
該デイスクを３軸外接型ツイスタに装着し、特
に遮蔽材等を用いずに、ポリエステルPOY（ポリ
エチレンテレフタレート高配向未延伸糸）をイン
ドロー仮撚し、150Dの加工糸を連続長期間生産
した。デイスクの摩耗が直径で１％進んだところ
をそのデイスクの耐久性限界（寿命）とした。な
おこの摩耗の程度は装置間、錘間のバラツキなど
も多いため200錘以上の平均値でとつた。 The disk was attached to a 3-axis circumscribed twister, and polyester POY (polyethylene terephthalate highly oriented undrawn yarn) was in-draw false twisted without using any particular shielding material, and 150D processed yarn was continuously produced for a long period of time. The point at which the disk wear progressed by 1% in terms of diameter was defined as the durability limit (life) of the disk. The degree of wear was determined as an average value for over 200 spindles, as there were many variations between devices and between spindles.
両者を比較すると本発明のデイスクは比較品の
約３倍の長寿命であつた。 Comparing the two, the disk of the present invention had a lifespan approximately three times longer than that of the comparative product.
すなわち比較品は3.0カ月の寿命しかなかつた
が、本発明のデイスクは9.0カ月の寿命を示し、
耐久性は大幅に延長した。また本発明のデイスク
では、仮撚糸に毛羽が発生せず、極めて優れた品
位の仮撚糸を安定して得ることができる。 In other words, the comparative product had a lifespan of only 3.0 months, but the disk of the present invention had a lifespan of 9.0 months.
Durability has been significantly extended. Further, in the disk of the present invention, no fuzz occurs in the false twisted yarn, and it is possible to stably obtain false twisted yarn of extremely excellent quality.
第１図は本発明のポリエステルポリウレタンデ
イスクを用いた摩擦仮ヨリ装置の一例の全体図を
示す。第２図は本発明のポリエステルポリウレタ
ンデイスクの断面図を示す。
６，７，８……ポリエステルポリウレタンデイ
スク、９……走行糸条、１０……芯金、１１……
ポリエステルポリウレタン部分。
FIG. 1 shows an overall view of an example of a friction temporary twisting device using the polyester polyurethane disk of the present invention. FIG. 2 shows a cross-sectional view of the polyester polyurethane disk of the present invention. 6, 7, 8... Polyester polyurethane disk, 9... Running thread, 10... Core bar, 11...
Polyester polyurethane part.
Claims (1)
シアネート成分の主成分とし、かつポリオールと
してポリエステルを主成分としてなるポリエステ
ルポリウレタンで成型されてなることを特徴とす
る外接型摩擦仮撚用デイスク。 （ただし、R1、R2は有機基である。） ２ R1、R2の有機基がアルキル基であることを
特徴とする特許請求の範囲第１項記載の摩擦仮撚
用デイスク。 ３ R1、R2がイソシアネート基に対してオルト
位にあることを特徴とする特許請求の範囲第１項
記載の摩擦仮撚用デイスク。 ４ イソシアネート成分がトリジンジイソシアネ
ートであることを特徴とする特許請求の範囲第１
項記載の摩擦仮撚用デイスク。 ５ 摩擦仮撚用デイスクが、３軸外接型の摩擦仮
撚用デイスクであることを特徴とする特許請求の
範囲第１項記載の摩擦仮撚用デイスク。[Scope of Claims] 1. A circumscribed friction false twisting member, characterized in that it is molded from polyester polyurethane containing a monomer of the following formula as the main isocyanate component and polyester as the main component: Disc for twisting. (However, R 1 and R 2 are organic groups.) 2. The disk for friction false twisting according to claim 1, wherein the organic groups of R 1 and R 2 are alkyl groups. 3. The disk for friction false twisting according to claim 1, wherein R 1 and R 2 are in ortho positions with respect to the isocyanate group. 4. Claim 1, characterized in that the isocyanate component is tolidine diisocyanate.
Frictional false-twisting disk described in section. 5. The friction false-twisting disk according to claim 1, wherein the friction false-twisting disk is a three-axis circumscribed friction false-twisting disk.