JPH0134966B2 - - Google Patents
Info
- Publication number
- JPH0134966B2 JPH0134966B2 JP14701279A JP14701279A JPH0134966B2 JP H0134966 B2 JPH0134966 B2 JP H0134966B2 JP 14701279 A JP14701279 A JP 14701279A JP 14701279 A JP14701279 A JP 14701279A JP H0134966 B2 JPH0134966 B2 JP H0134966B2
- Authority
- JP
- Japan
- Prior art keywords
- nacl
- hydroxyapatite
- mgcl
- composition
- test
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は歯磨組成物に関する。
本発明によれば、合成ハイドロキシアパタイト
粉末を含む練歯磨組成物であつて、この組成物の
重量に対して0.1〜20重量％のNaClと0.003〜３重
量％のMgCl2とを含有することを特徴とする歯磨
組成物が提供される。 本発明に係る歯磨組成物は歯に付着したプラー
ク（細菌塊）の除去に有効であるとともに、歯牙
表面の強化及び再石灰化の促進に極めて有効であ
るということが見出されたものである。 即ち、本発明の歯磨組成物は歯質表面に対し
て、極めて効果的に、ハイドロキシアパタイトの
結晶を析出せしめて、これをコーテイングするの
である。これは、上記の如き塩化物の存在によつ
てハイドロキシアパタイトの水に対する溶解度が
増大することによるものと考えられる。即ち、ハ
イドロキシアパタイトは水に超難溶性の塩である
から、歯磨中ではイオン化している〔Ca++〕
〔HPO4 --〕などのイオンのイオン積量は小さい。
即ち歯質表面のコーテイング即ち歯質表面におけ
るハイドロキシアパタイト結晶の析出のための推
進力としてのイオン積量が小さいのである。しか
るに、このようなハイドロキシアパタイトを含む
歯磨中にNaCl及びMgCl2が加わると、Ca++と
HPO4 --の溶解度が急激に増大し、これによつて
コーテイング効果がより促進されるのであると考
えられるのである。 本発明の歯磨組成物中に含まれるNaCl及び
MgCl2の量がそれぞれ上記に規定した量よりも小
さい場合にはコーテイング効果は不十分となり、
逆に上記規定量よりも大きい場合には使用に際し
て満足すべきフイーリングを与えることが困難と
なる。 尚本発明の歯磨組成物は通常用いられる種々の
添加剤を含んでいてもよく、また所望ならばクエ
ン酸、乳酸、酢酸、ピロリン酸やグルタミン、プ
ロリン、セリン、グリシンなどを含んでいてもよ
い。 以下、例によつて本発明を更に説明する。 以下の例において、例１〜６は歯磨組成物の組
成例を重量部で示すものであつて、例４，５及び
６は本発明歯磨組成物の効果を明らかにするため
のものである。 例 １ 練歯磨 アパタイト粉末 10.0 燐酸カルシウム 25.0 CMCナトリウム塩 0.3 カラギーナン 1.2 グリセリン 10.0 ソルビツト 15.0 ラウリル硫酸ナトリウム 2.0 香 料 1.2 サツカリンナトリウム 0.1 二酸化珪素 2.0 NaCl 0.27 MgCl2 0.01 水 32.92 例 ２ 練歯磨 アパタイト粉末 5.0 燐酸カルシウム 10.0 ピロリン酸カルシウム 20.0 CMCナトリウム塩 1.0 アルギン酸ナトリウム 0.1 グリセリン 10.0 ソルビツト 10.0 ラウリル硫酸ナトリウム 1.5 ラウロイルザルコシンナトリウム 0.5 香 料 0.5 サツカリンナトリウム 0.1 二酸化珪素 2.5 NaCl 3.0 MgCl2 0.2 水 35.0 例 ３ 練歯磨 アパタイト粉末 35.0 CMCナトリウム塩 1.0 カラギーナン 0.3 グリセリン 35.0 ラウリル硫酸ナトリウム 2.0 香 料 1.0 サツカリンナトリウム 0.1 二酸化珪素 2.5 NaCl 2.0 MgCl2 0.1 KCl 1.0 水 20.0 例 ４ 37℃の蒸留水1000mlに１ｇのハイドロキシアパ
タイト粉末を投入し、NaCl及びMgCl2を異なる
濃度で添加してカルシウムイオン濃度を測定して
ハイドロキシアパタイトの溶解度がNaCl及び
MgCl2の添加により増大することを確認した。液
の調製10日後のカルシウムイオン濃度は、それぞ
れ次のようであつた。
粉末を含む練歯磨組成物であつて、この組成物の
重量に対して0.1〜20重量％のNaClと0.003〜３重
量％のMgCl2とを含有することを特徴とする歯磨
組成物が提供される。 本発明に係る歯磨組成物は歯に付着したプラー
ク（細菌塊）の除去に有効であるとともに、歯牙
表面の強化及び再石灰化の促進に極めて有効であ
るということが見出されたものである。 即ち、本発明の歯磨組成物は歯質表面に対し
て、極めて効果的に、ハイドロキシアパタイトの
結晶を析出せしめて、これをコーテイングするの
である。これは、上記の如き塩化物の存在によつ
てハイドロキシアパタイトの水に対する溶解度が
増大することによるものと考えられる。即ち、ハ
イドロキシアパタイトは水に超難溶性の塩である
から、歯磨中ではイオン化している〔Ca++〕
〔HPO4 --〕などのイオンのイオン積量は小さい。
即ち歯質表面のコーテイング即ち歯質表面におけ
るハイドロキシアパタイト結晶の析出のための推
進力としてのイオン積量が小さいのである。しか
るに、このようなハイドロキシアパタイトを含む
歯磨中にNaCl及びMgCl2が加わると、Ca++と
HPO4 --の溶解度が急激に増大し、これによつて
コーテイング効果がより促進されるのであると考
えられるのである。 本発明の歯磨組成物中に含まれるNaCl及び
MgCl2の量がそれぞれ上記に規定した量よりも小
さい場合にはコーテイング効果は不十分となり、
逆に上記規定量よりも大きい場合には使用に際し
て満足すべきフイーリングを与えることが困難と
なる。 尚本発明の歯磨組成物は通常用いられる種々の
添加剤を含んでいてもよく、また所望ならばクエ
ン酸、乳酸、酢酸、ピロリン酸やグルタミン、プ
ロリン、セリン、グリシンなどを含んでいてもよ
い。 以下、例によつて本発明を更に説明する。 以下の例において、例１〜６は歯磨組成物の組
成例を重量部で示すものであつて、例４，５及び
６は本発明歯磨組成物の効果を明らかにするため
のものである。 例 １ 練歯磨 アパタイト粉末 10.0 燐酸カルシウム 25.0 CMCナトリウム塩 0.3 カラギーナン 1.2 グリセリン 10.0 ソルビツト 15.0 ラウリル硫酸ナトリウム 2.0 香 料 1.2 サツカリンナトリウム 0.1 二酸化珪素 2.0 NaCl 0.27 MgCl2 0.01 水 32.92 例 ２ 練歯磨 アパタイト粉末 5.0 燐酸カルシウム 10.0 ピロリン酸カルシウム 20.0 CMCナトリウム塩 1.0 アルギン酸ナトリウム 0.1 グリセリン 10.0 ソルビツト 10.0 ラウリル硫酸ナトリウム 1.5 ラウロイルザルコシンナトリウム 0.5 香 料 0.5 サツカリンナトリウム 0.1 二酸化珪素 2.5 NaCl 3.0 MgCl2 0.2 水 35.0 例 ３ 練歯磨 アパタイト粉末 35.0 CMCナトリウム塩 1.0 カラギーナン 0.3 グリセリン 35.0 ラウリル硫酸ナトリウム 2.0 香 料 1.0 サツカリンナトリウム 0.1 二酸化珪素 2.5 NaCl 2.0 MgCl2 0.1 KCl 1.0 水 20.0 例 ４ 37℃の蒸留水1000mlに１ｇのハイドロキシアパ
タイト粉末を投入し、NaCl及びMgCl2を異なる
濃度で添加してカルシウムイオン濃度を測定して
ハイドロキシアパタイトの溶解度がNaCl及び
MgCl2の添加により増大することを確認した。液
の調製10日後のカルシウムイオン濃度は、それぞ
れ次のようであつた。
【表】
例５ （参考例）
(1) 試験方法
成人永久歯をそのエナメル小柱に切り、約
200μｍの厚さの切片とし、そのエナメル質部分
を取り除き、象牙質部分を露出させた。その切片
に対し、それぞれ Ａ：蒸留水； Ｂ：蒸留水にハイドロキシアパタイトを飽和させ
た溶液、及び Ｃ：0.001％のMgCl2及び0.9％のNaClを含む蒸留
水にハイドロキシアパタイトを飽和させた溶
液 を0.6ml／minの流速で通過させ、１日後に表面
を偏光顕微鏡により観察した。 (2) 試験結果 Ａの場合には、歯質表面のコーテイング層（石
灰化層）は全く認められなかつた。 Ｂの場合には、厚さ約2μｍのコーテイング層
が認められた。 Ｃの場合には、厚さ約5μｍのコーテイング層
が歯質表面全面に認められた。 このことはMgCl2，NaClの存在でハイドロキ
シアパタイトの再石灰化が促進されることを示し
ている。 例 ６ 例５と同様に、成人永久歯をそのエナメル小柱
に平行に切り、約200μｍの厚さの切片とし、そ
のエナメル質部分を取り除き、象牙質部分を露出
させた、その切片に0.003％のMgCl及び0.3％の
NaClを含む蒸留水にハイドロキシアパタイトを
飽和させた溶液を用いて、例５と同様の試験を行
なつた結果、例５と同様の結果をえた。 例 ７ (1) 試験方法 実施例２）の組成よりリン酸塩、NaCl，
MgCl2以外の添加物を除いた組成(B)とこの組成よ
りNaCl，MgCl2を除いた組成(A)とを用いて例５）
と同様の試験方法で以下の試験を行なつた。 テスト１：ハイドロキシアパタイト、リン酸カル
シウム、ピロリン酸カルシウムを１：２：
４の割り合いで蒸留水に加えて飽和させた
溶液(A) テスト２：3.0％のNaClおよび0.2％のMgCl2を含
む蒸留水にＡと同じ組成物を飽和させた溶
液(B) (2) 試験結果 テスト１：厚さ1μｍ以下のコーテイング層が認
められた。 テスト２：厚さ約2μｍのコーテイング層が認め
られた。 このことはハイドロキシアパタイトだけを飽和
させた溶液に比べて石灰化は起こり難いが、
NaCl，MgCl2の存在で石灰化が促進されること
を示している。
200μｍの厚さの切片とし、そのエナメル質部分
を取り除き、象牙質部分を露出させた。その切片
に対し、それぞれ Ａ：蒸留水； Ｂ：蒸留水にハイドロキシアパタイトを飽和させ
た溶液、及び Ｃ：0.001％のMgCl2及び0.9％のNaClを含む蒸留
水にハイドロキシアパタイトを飽和させた溶
液 を0.6ml／minの流速で通過させ、１日後に表面
を偏光顕微鏡により観察した。 (2) 試験結果 Ａの場合には、歯質表面のコーテイング層（石
灰化層）は全く認められなかつた。 Ｂの場合には、厚さ約2μｍのコーテイング層
が認められた。 Ｃの場合には、厚さ約5μｍのコーテイング層
が歯質表面全面に認められた。 このことはMgCl2，NaClの存在でハイドロキ
シアパタイトの再石灰化が促進されることを示し
ている。 例 ６ 例５と同様に、成人永久歯をそのエナメル小柱
に平行に切り、約200μｍの厚さの切片とし、そ
のエナメル質部分を取り除き、象牙質部分を露出
させた、その切片に0.003％のMgCl及び0.3％の
NaClを含む蒸留水にハイドロキシアパタイトを
飽和させた溶液を用いて、例５と同様の試験を行
なつた結果、例５と同様の結果をえた。 例 ７ (1) 試験方法 実施例２）の組成よりリン酸塩、NaCl，
MgCl2以外の添加物を除いた組成(B)とこの組成よ
りNaCl，MgCl2を除いた組成(A)とを用いて例５）
と同様の試験方法で以下の試験を行なつた。 テスト１：ハイドロキシアパタイト、リン酸カル
シウム、ピロリン酸カルシウムを１：２：
４の割り合いで蒸留水に加えて飽和させた
溶液(A) テスト２：3.0％のNaClおよび0.2％のMgCl2を含
む蒸留水にＡと同じ組成物を飽和させた溶
液(B) (2) 試験結果 テスト１：厚さ1μｍ以下のコーテイング層が認
められた。 テスト２：厚さ約2μｍのコーテイング層が認め
られた。 このことはハイドロキシアパタイトだけを飽和
させた溶液に比べて石灰化は起こり難いが、
NaCl，MgCl2の存在で石灰化が促進されること
を示している。
Claims (1)
- １ 合成ハイドロキシアパタイト粉末を含む歯磨
組成物であつて、この組成物の練成物の重量に対
して0.1〜20重量％のNaClと0.003〜３重量％の
MgCl2とを含有することを特徴とする歯磨組成
物。