JPH0154472B2 - - Google Patents
Info
- Publication number
- JPH0154472B2 JPH0154472B2 JP61109173A JP10917386A JPH0154472B2 JP H0154472 B2 JPH0154472 B2 JP H0154472B2 JP 61109173 A JP61109173 A JP 61109173A JP 10917386 A JP10917386 A JP 10917386A JP H0154472 B2 JPH0154472 B2 JP H0154472B2
- Authority
- JP
- Japan
- Prior art keywords
- coating layer
- fabric
- moisture
- coating
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
【発明の詳細な説明】
〔産業上の利用分野〕
この発明は、防水性および透湿性が要求される
衣料等の素材として用いられるコーテイング布帛
の製造方法に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Application Field] The present invention relates to a method for manufacturing a coating fabric used as a material for clothing and the like that requires waterproofness and moisture permeability.
スキーウエア、アスレチツクウエア、ゴルフウ
エア等においては、雨水等が衣服を通して人体側
に浸透することがなく、また人体から発散される
汗等の水分を含む湿気が、衣服を通して外部に発
散させるようになつていることが望ましい。
Ski wear, athletic wear, golf wear, etc. are designed to prevent rainwater from penetrating into the human body through the clothing, and to allow moisture, including sweat and other moisture emitted from the human body, to evaporate to the outside through the clothing. It is desirable to be familiar.
このため、従来においては、これらの衣服の素
材として用いる布帛の一面に防水性および透湿性
を有するコーテイング層を形成し、このコーテイ
ング層が人体側に位置するようにして着用させ、
外部から雨水等が人体側に浸透するのを、このコ
ーテイング層によつて防止すると共に、人体から
発散される汗等の水分を含む湿気が、このコーテ
イング層を通して外部に発散されるようにしてい
た。 For this reason, in the past, a waterproof and moisture permeable coating layer was formed on one side of the fabric used as the material for these clothes, and the clothing was worn with this coating layer positioned on the human body side.
This coating layer prevents rainwater, etc. from penetrating into the human body from the outside, and also allows moisture, including sweat and other moisture emitted from the human body, to be radiated to the outside through this coating layer. .
しかし、人体から発散される汗等の水分の量が
多く、このコーテイング層の透湿性能を上回る場
合や、外気温度が低い場合等には、外部に発散さ
れなかつた水分が凝縮され、人体側のコーテイン
グ層の上に水滴となつてたまり、またこのように
水滴となつたものは、その表面積が小さくて蒸発
効率が悪いため、発散されにくくコーテイング層
上において長く残り、このように残つた水滴が人
体や下着を濡らし、非常に着用感が悪くなると共
に、風邪を引く等の原因にもなつていた。 However, if the amount of moisture such as sweat released from the human body is large and exceeds the moisture permeability of this coating layer, or if the outside temperature is low, the moisture that was not released to the outside will condense and Water droplets accumulate on the coating layer, and these water droplets have a small surface area and low evaporation efficiency, so they are difficult to evaporate and remain on the coating layer for a long time. This wets the human body and underwear, making it extremely uncomfortable to wear and causing people to catch colds.
この発明は、従来の防水性および透湿性を有す
るコーテイング布帛における上記のような問題を
解決せんとしてなされたものであり、防水性およ
び透湿性を有するコーテイング布帛を以下に示す
方法で製造することにより、従来のように外部に
発散されなかつた水分が、コーテイング層上に水
滴となつて残るということがないようにしたので
ある。
This invention was made to solve the above-mentioned problems with conventional coating fabrics that are waterproof and breathable. This prevents moisture that has not been diffused to the outside from remaining as water droplets on the coating layer, as in the conventional case.
すなわち、この発明においては、第１図に示す
ように、布帛１の一面に、ポリウレタンを主体と
する極性有機溶剤溶液を塗布して湿式凝固により
第１コーテイング層２を形成し、次に、この第１
コーテイング層２の上に、親水性のポリウレタン
を含有するポリウレタンのＷ／Ｏ型エマルジヨン
を塗布して加熱乾燥により第２コーテイング層３
を形成するのである。 That is, in the present invention, as shown in FIG. 1, a first coating layer 2 is formed by coating a polar organic solvent solution mainly composed of polyurethane on one surface of the fabric 1 and wet coagulating it. 1st
A W/O emulsion of polyurethane containing hydrophilic polyurethane is applied onto the coating layer 2 and dried by heating to form the second coating layer 3.
It forms.
ここで、ポリウレタンを主体とする極性有機溶
剤溶液を用いて湿式凝固により第１コーテイング
層２を形成するため、第１コーテイング層２に
は、極性有機溶剤が凝固液中に溶出した跡の多数
の微細な通気孔が形成されている。このため、第
１コーテイング層２は、防水性および透湿性を有
する。 Here, since the first coating layer 2 is formed by wet coagulation using a polar organic solvent solution mainly composed of polyurethane, the first coating layer 2 has many traces of the polar organic solvent eluted into the coagulation liquid. Fine ventilation holes are formed. Therefore, the first coating layer 2 has waterproofness and moisture permeability.
また、親水性のポリウレタンを含有するポリウ
レタンのＷ／Ｏ型エマルジヨンを用いて、加熱乾
燥により第２コーテイング層３を形成する（乾式
凝固）ため、この第２コーテイング層３は、分散
媒が蒸発した跡の多数のポリウレタン微細粒によ
つて形成されている。そのため、粒子間のすき間
空間が大きいので、吸着力が大きく、吸水性が優
れている。また、この第２コーテイング層３に
は、通気性を有する微細孔が多数形成されてお
り、水分がこれらの微細孔に吸収されて第１コー
テイング層２側に導かれるようになつている。更
に、この第２コーテイング層３は親水性のポリウ
レタンを含有しているので、水分が広範囲にわた
つて浸透され優れた吸水性を有する。 In addition, since the second coating layer 3 is formed by heating and drying (dry coagulation) using a polyurethane W/O emulsion containing hydrophilic polyurethane, the second coating layer 3 is formed by evaporating the dispersion medium. The traces are formed by numerous polyurethane fine particles. Therefore, since the interparticle spaces are large, the adsorption force is large and water absorption is excellent. Further, this second coating layer 3 has a large number of air permeable micropores formed therein, so that moisture is absorbed by these micropores and guided to the first coating layer 2 side. Furthermore, since the second coating layer 3 contains hydrophilic polyurethane, water permeates over a wide range and has excellent water absorbency.
なお、第１コーテイング層２を形成する際に、
溌水剤を付着させる等によつて、より一層の防水
性を与えるようにしてもよい。 Note that when forming the first coating layer 2,
Further waterproofness may be imparted by attaching a water repellent agent or the like.
また、布帛１の一面に第１コーテイング層２を
形成するにあたつては、予め布帛１の一面に下引
き樹脂層を形成しておき、この下引き樹脂により
布帛１と第１コーテイング層２との接着性を高め
るようにしてもよい。 In addition, when forming the first coating layer 2 on one side of the fabric 1, an undercoat resin layer is formed on one side of the fabric 1 in advance, and this undercoat resin coats the fabric 1 and the first coating layer 2. It may also be possible to enhance the adhesion with.
なお、第２コーテイング層３に、より一層の吸
水性を与えるために、表面活性剤を含有させても
よい。 Note that a surfactant may be contained in the second coating layer 3 in order to provide further water absorption.
また、この第２コーテイング層３を形成するに
あたり、その厚さをあまり薄くすると、過剰の水
分を充分に吸収することができなくなる一方、そ
の厚さを必要以上に厚くすると、コーテイング布
帛自体が厚くなる等の問題があるため、通常は１
〜200μm程度の厚さにし、好ましくは10〜150μm
程度に形成する。 In addition, when forming the second coating layer 3, if the thickness is made too thin, it will not be able to absorb excess moisture, while if the thickness is made too thick, the coating fabric itself will become thick. Since there are problems such as
~200μm thick, preferably 10~150μm
Form to a certain degree.
以上のようにして製造されたコーテイング布帛
においては、、その布帛１の一面に形成された防
水性および透湿性を有する第１コーテイング層２
が、外部から人体側に雨水等が浸透するのを防止
すると共に、人体から発散される汗等の水分を含
む湿気は、これら第２および第１のコーテイング
層３，２を通して外部に発散されるようになつて
いる。 In the coating fabric manufactured as described above, the first coating layer 2 having waterproofness and moisture permeability is formed on one side of the fabric 1.
However, it prevents rainwater etc. from penetrating into the human body from the outside, and moisture containing moisture such as sweat released from the human body is released to the outside through the second and first coating layers 3 and 2. It's becoming like that.
また、人体から発散される汗等の水分を含む湿
気が、これらのコーテイング層２，３の透湿性能
を上回る場合等においては、外部に発散されなか
つた過剰の水分が、吸水性を有する第２コーテイ
ング層３に広い範囲で吸収され、従来のように、
凝縮して水滴化することがないようになつてい
る。またこのように、第２コーテイング層３の広
い範囲に吸収された過剰の水分は、その広い範囲
において順次蒸発され、第１コーテイング層２を
通して外部に発散されるようになつている。 In addition, in cases where the moisture containing moisture such as sweat released from the human body exceeds the moisture permeability of these coating layers 2 and 3, the excess moisture that has not been released to the outside may be 2 is absorbed in a wide range by the coating layer 3, and as before,
This prevents it from condensing into water droplets. In addition, in this way, the excess water absorbed in a wide area of the second coating layer 3 is sequentially evaporated in that wide area and diffused to the outside through the first coating layer 2.
次に、この発明の具体的な実施例について説明
する。
Next, specific embodiments of the present invention will be described.
（実施例）
布帛として、ナイロン70d−68フイラメントマ
ルチ糸を使用した210本ナイロンタフタを染色し、
仕上げセツトした後、これをフツソ系溌水剤溶液
中に浸漬し、溌水剤溶液が生地重量に対して60％
付着するようにマングルで絞り、これを80℃で乾
燥させ、160℃で40秒間仕上げセツトした溌水剤
が付着されたものを用いた。(Example) As a fabric, 210 pieces of nylon taffeta using nylon 70d-68 filament multi yarn were dyed.
After finishing and setting, it is immersed in a soft water repellent solution, and the water repellent solution is 60% of the weight of the fabric.
The water repellent agent was used, which was squeezed with a mangle to ensure adhesion, dried at 80°C, and finished and set at 160°C for 40 seconds.
そして、この布帛の一面に、ポリウレタンを主
成分とするDMF溶液であるクリスボン7667EL
〔大日本インキ化学工業(株)の商品〕が100重量部、
無水ケイ酸を主成分とするサイロイド＃162〔富士
デヴイソン(株)の商品〕が８重量部、シリコン系溌
水剤である東レシリコーンBY16−839〔東レシリ
コーン(株)の商品〕が1.5重量部、チタン白と樹脂
とを練り合せたダイラツク白＃1305〔大日本イン
キ化学工業(株)の商品〕が10重量部、架橋剤として
トリメチロールプロパン−ヘキサメチレンジイソ
シアネート（モル比１：３）付加物が２重量部、
ジメチルホルムアミドが45重量部からなる塗布液
を110g／m2の割合で塗布した。そして、これを
30℃の水中に浸漬させて２分間放置した後、80℃
の水で10分間湯洗し、これをマングルで絞り、
120℃で乾燥させた後、さらにこれを160℃で30秒
間巾出しセツトし、防水性および透湿性を有する
第１コーテイング層を形成した。 Then, one side of this fabric was coated with Crisbon 7667EL, a DMF solution whose main component is polyurethane.
100 parts by weight of [product of Dainippon Ink and Chemicals Co., Ltd.],
8 parts by weight of Thyroid #162 (product of Fuji Davison Co., Ltd.) whose main component is silicic anhydride, and 1.5 parts by weight of Toray Silicone BY16-839 (product of Toray Silicone Co., Ltd.), a silicone water repellent. , 10 parts by weight of Dairakku White #1305 (product of Dainippon Ink & Chemicals Co., Ltd.), which is a mixture of titanium white and resin, and trimethylolpropane-hexamethylene diisocyanate (molar ratio 1:3) adduct as a crosslinking agent. is 2 parts by weight,
A coating solution containing 45 parts by weight of dimethylformamide was applied at a rate of 110 g/m 2 . And this
After immersing it in water at 30℃ and leaving it for 2 minutes, it was heated to 80℃.
Wash with hot water for 10 minutes, squeeze this with a mangle,
After drying at 120°C, this was further set at 160°C for 30 seconds to form a waterproof and moisture permeable first coating layer.
このようにして、第１コーテイング層を形成し
た布帛は、JISL−1092（低水圧法）の方法で測定
した耐水圧が1600mmH2O／cm2であり、また、
JISL−1099A1の方法で測定した透湿度は、
230g／m2／時間であつた。 The fabric on which the first coating layer was formed in this way has a water pressure resistance of 1600 mmH 2 O/cm 2 as measured by the method of JISL-1092 (low water pressure method), and
The moisture permeability measured by the method of JISL-1099A1 is
It was 230g/m 2 /hour.
そして、このように形成された第１コーテイン
グ層の上に、ポリウレタンを主成分とするＷ／Ｏ
型エマルジヨンのハイムレンＸ−39〔大日精化工
業(株)の商品〕が100重量部、水が20重量部、親水
性を有するポリウレタンを主成分とするエマルジ
ヨンであるエラストロンＷ−11〔第一工業製薬(株)
の商品〕が22重量部、メチルエチルケトンが20重
量部からなるエマルジヨン塗布液を70g／m2の割
合で塗布し、これを加熱乾燥させ、親水性を有し
多数の通気性微細孔が形成された吸水性の第２コ
ーテイング層を形成した。 Then, on the first coating layer formed in this way, W/O containing polyurethane as a main component is applied.
The mold emulsion Heimlen Pharmaceutical Co., Ltd.
An emulsion coating solution consisting of 22 parts by weight of [product] and 20 parts by weight of methyl ethyl ketone was applied at a rate of 70 g/ m2 , and this was heated and dried to form a large number of hydrophilic and breathable micropores. A second water-absorbing coating layer was formed.
また、これらのコーテイング層を形成した布帛
の反対側の面に、さらにフツソ系溌水剤溶液を塗
布し、乾燥させて溌水剤を付着させ、この反対側
の面、すなわち、これらのコーテイング層を人体
側にして着用したときに、外部にあらわれる面に
も防水性を与え、雨水等が浸入するのを確実に防
止できるようにした。 Further, on the opposite side of the fabric on which these coating layers have been formed, a futsuso-based water repellent solution is further applied and dried to adhere the water repellent agent. When worn on the body side, the surface that is exposed to the outside is also waterproof, ensuring that rainwater and other substances are prevented from penetrating.
なお、以上のようにして製造されたコーテイン
グ布帛は、JISL−1092（低水圧法）の方法で測定
した耐水圧が2000mmH2O／cm2以上であり、また、
JISL−1099A1の方法で測定した透湿度は、
250g／m2／時間であつた。すなわち、第２コー
テイング層を形成することによつて、形成する前
と比べてこれらの性能が悪くなるということはな
く、むしろ性能が向上していた。 The coated fabric manufactured as described above has a water pressure resistance of 2000 mmH 2 O/cm 2 or more as measured by the method of JISL-1092 (low water pressure method), and
The moisture permeability measured by the method of JISL-1099A1 is
It was 250g/m 2 /hour. That is, by forming the second coating layer, these performances did not deteriorate compared to before formation, but rather improved.
（比較例）
次に、上記のように、第１コーテイング層の上
に吸水性を有する第２コーテイング層が形成され
た実施例のコーテイング布帛が、第２コーテイン
グ層が形成されていない従来のコーテイング布帛
に比べ、水に対する性能やコーテイング布帛の透
湿性能を越える過剰の水分を含む湿気に対する性
能について優れていることを明確にするため、次
のような試験を行なつた。(Comparative Example) Next, as described above, the coating fabric of the example in which the water-absorbing second coating layer was formed on the first coating layer was compared with the conventional coating fabric in which the second coating layer was not formed. In order to clarify that it is superior to cloth in terms of performance against water and against moisture containing excess water that exceeds the moisture permeability of the coating fabric, the following tests were conducted.
第１の試験では、0.05ccの水を夫々のコーテイ
ング層上に滴下し、夫々コーテイング布帛におけ
る水滴の状態を調べた。 In the first test, 0.05 cc of water was dropped onto each coating layer, and the condition of the water droplets on each coating fabric was examined.
この結果、第２コーテイング層が形成されてい
ない従来のコーテイング布帛は、30分経過後も水
滴がその状態のままで残つていたのに対し、第２
コーテイング層が形成された実施例のコーテイン
グ布帛においては、滴下された水滴が10数秒で吸
収されて広範囲に広がり、10分後には蒸発して消
失した。 As a result, water droplets remained in the same state even after 30 minutes had passed with the conventional coated fabric in which the second coating layer was not formed;
In the coated fabric of the example in which the coating layer was formed, the dropped water droplets were absorbed in a few seconds and spread over a wide area, and evaporated and disappeared after 10 minutes.
また、第２の試験では、人が着用する状態と略
同様の状態にするため、温度が22℃、相対湿度
（R.H.）が65％、風速が1m／ｓの条件の下で、
第２図に示すように、容器１０中に水１１を40℃
の状態で保ち、コーテイング層を容器側にして
夫々のコーテイング布帛で容器１０の口を覆い、
容器１０中から水分がこれらのコーテイング布帛
を通して外部に発散される状態を調べた。 In the second test, the temperature was 22℃, the relative humidity (RH) was 65%, and the wind speed was 1m/s, in order to make the clothes almost similar to those worn by humans.
As shown in Figure 2, water 11 is placed in a container 10 at 40°C.
, and cover the mouth of the container 10 with each coating fabric with the coating layer facing the container,
The state in which moisture is released from the container 10 to the outside through these coating fabrics was investigated.
この結果、第２コーテイング層が形成されてい
ない従来のコーテイング布帛では、コーテイング
層の面に水滴が玉状に付着し、布帛を通して外部
に発散された水の量は30g／m2／時間であつた。 As a result, in the conventional coated fabric on which the second coating layer is not formed, water droplets adhere to the surface of the coating layer in the form of beads, and the amount of water released through the fabric to the outside is 30 g/m 2 /hour. Ta.
これに対し、吸水性を有する第２コーテイング
層が形成された実施例のコーテイング布帛では、
コーテイング層の面に水滴が玉状に付着するとい
うことがなく、布帛を通して外部に発散された水
の量は95g／m2／時間であつた。 On the other hand, in the coating fabric of the example in which the second coating layer having water absorbency was formed,
There was no beading of water droplets on the surface of the coating layer, and the amount of water released through the fabric to the outside was 95 g/m 2 /h.
これらの結果から明らかなように、第１コーテ
イング層の上に、吸水性の第２コーテイング層が
形成された実施例のものは、人体から発散される
汗等の水分を含む湿気が、コーテイング布帛の透
湿性能を上回る場合においても、従来のように、
過剰の水分が水滴となつてコーテイング層の上に
溜つて残るということなく、過剰の水分は、吸水
性の第２コーテイング層に広い範囲で吸収される
ようになつている。そして、このように第２コー
テイング層の広い範囲に吸収された過剰の水分
は、適当な時期にその広い範囲において順次蒸発
され、、第１コーテイング層を通して外部に発散
されるようになつている。 As is clear from these results, in the example in which the water-absorbing second coating layer was formed on the first coating layer, moisture containing moisture such as sweat emitted from the human body was absorbed into the coating fabric. Even if it exceeds the moisture permeability of
Excess moisture is adapted to be absorbed to a large extent by the water-absorbing second coating layer, without the excess moisture remaining as droplets on the coating layer. The excess moisture thus absorbed in a wide area of the second coating layer is sequentially evaporated in that wide area at an appropriate time and radiated to the outside through the first coating layer.
以上詳述したように、この発明の方法で製造さ
れたコーテイング布帛には、布帛の一面に防水性
および透湿性を有する第１コーテイング層が形成
され、さらにこの第１コーテイング層の上に、吸
水性を有する第２コーテイング層が形成されてい
るため、これを衣服の素材として用い、第１及び
第２のコーテイング層が形成された面を人体側に
して着用させた場合には、雨水等が衣服を通して
外部から人体側に浸透するのを、防水性を有する
第１コーテイング層が防止し、また、人体から発
散された汗等の水分を含む湿気は、第２コーテイ
ング層および透湿性を有する第１コーテイング層
を通して外部に発散されるようになつている。
As detailed above, in the coated fabric produced by the method of the present invention, a first coating layer having waterproofness and moisture permeability is formed on one side of the fabric, and a water-absorbing layer is further formed on the first coating layer. Since a second coating layer with a protective property is formed, if this is used as a material for clothing and worn with the side on which the first and second coating layers are formed facing the human body, rainwater etc. The first waterproof coating layer prevents moisture from penetrating into the human body from the outside through clothing, and the second coating layer and the moisture permeable second coating layer prevent moisture containing moisture such as sweat emitted from the human body. 1 coating layer to the outside.
また、人体から発散される汗等の水分を含む湿
気の量が、これらのコーテイング層を通して外部
に発散させる透湿量を上回り、外部に発散されな
い過剰の水分が残つたとしても、吸水性を有する
第２コーテイング層が、このような過剰の水分を
広い範囲で吸収し、従来のコーテイング布帛のよ
うに、過剰の水分が凝縮して水滴化することがな
く、、また、このように第２コーテイング層の広
い範囲に吸収された過剰の水分は、広い範囲にお
いて適宜蒸発され、第１コーテイング層を通して
外部に発散されるようになつている。 In addition, even if the amount of moisture containing moisture such as sweat released from the human body exceeds the amount of moisture permeable to the outside through these coating layers, and the excess moisture that is not released to the outside remains, it still has water absorption properties. The second coating layer absorbs such excess moisture over a wide range, and the excess moisture does not condense into water droplets as in conventional coating fabrics. Excess moisture absorbed in a wide area of the layer is appropriately evaporated over a wide area and radiated to the outside through the first coating layer.
この結果、この発明によつて得られたコーテイ
ング布帛を用いた場合には、人体から発散される
汗等の水分を含む湿気の量が、コーテイング布帛
の透湿性能を上回る条件の下でも、従来のコーテ
イング布帛のように、コーテイング層上に水滴が
長く残つて人体や下着を濡らし、着用感が非常に
悪くなつたり、これによつて風邪を引いたりする
ということがないようになつている。 As a result, when the coating fabric obtained according to the present invention is used, even under conditions where the amount of moisture containing moisture such as sweat emitted from the human body exceeds the moisture permeability of the coating fabric, Unlike the coating fabric of 2005, water droplets do not remain on the coating layer for a long time and wet the human body and underwear, making it extremely uncomfortable to wear and causing colds.
第１図は、この発明の実施例に係るコーテイン
グ布帛の断面図、第２図は、コーテイング布帛の
透湿量を、人が着用する状態と略同様の状態で測
定する方法を示す図である。
符号の説明、１……布帛、、２……第１コーテ
イング層、３……第２コーテイング層。
FIG. 1 is a cross-sectional view of a coating fabric according to an embodiment of the present invention, and FIG. 2 is a diagram showing a method for measuring the moisture permeability of the coating fabric in a state substantially similar to that worn by a person. . Explanation of symbols: 1...Fabric, 2...First coating layer, 3...Second coating layer.
Claims (1)
極性有機溶剤溶液を塗布して湿式凝固により第１
コーテイング層２を形成し、次に、この第１コー
テイング層２の上に、親水性のポリウレタンを含
有するポリウレタンのＷ／Ｏ型エマルジヨンを塗
布して加熱乾燥により第２コーテイング層３を形
成することを特徴とするコーテイング布帛の製造
方法。 ２ 布帛の第１コーテイング層２及び第２コーテ
イング層３を形成しない側の面に、溌水処理を施
すことを特徴とする特許請求の範囲第１項記載の
コーテイング布帛の製造方法。[Claims] 1. A polar organic solvent solution mainly composed of polyurethane is applied to one side of the fabric 1, and a first layer is formed by wet coagulation.
A coating layer 2 is formed, and then a W/O emulsion of polyurethane containing hydrophilic polyurethane is applied on the first coating layer 2, and a second coating layer 3 is formed by heating and drying. A method for producing a coated fabric characterized by: 2. The method for producing a coated fabric according to claim 1, wherein a water repellent treatment is performed on the side of the fabric on which the first coating layer 2 and the second coating layer 3 are not formed.