JPH0436178B2 - - Google Patents
Info
- Publication number
- JPH0436178B2 JPH0436178B2 JP60142436A JP14243685A JPH0436178B2 JP H0436178 B2 JPH0436178 B2 JP H0436178B2 JP 60142436 A JP60142436 A JP 60142436A JP 14243685 A JP14243685 A JP 14243685A JP H0436178 B2 JPH0436178 B2 JP H0436178B2
- Authority
- JP
- Japan
- Prior art keywords
- resin
- pearlescent
- styrene
- acrylonitrile
- pellet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
産業上の利用分野
本発明はマーブル模様の成型物およびその成型
方法に係るものであつて、化粧品容器、宝石箱、
美容用具、家具の部品、その他の日用雑貨品等の
装飾性を重視される成型物に用いる場合に好都合
なものである。[Detailed Description of the Invention] Industrial Field of Application The present invention relates to a marble-patterned molded product and a method for molding the same, including cosmetic containers, jewelry boxes,
It is convenient for use in molded products where decorativeness is important, such as beauty tools, furniture parts, and other daily necessities.
従来の技術
化粧用コンパクト容器、宝石箱等の装飾性を重
視される成型物には、従来よりマーブル模様を施
したものが存在する。BACKGROUND ART Conventionally, molded products such as compact cosmetic containers and jewelry boxes where decorativeness is important have been given a marble pattern.
しかし、このマーブル模様は不透明な着色物を
用いて、二色成型型、または多色成型型により成
型を行なつていた。そのため、成型物のマーブル
模様に光沢がないとともに立体感がなく、装飾性
をを重視される化粧用コンパクト容器、宝石箱、
美容容器、家具の部品、その他の日用雑貨品等に
於いて趣味感に乏しいものとなり、商品価値を高
めることが出来ないものであつた。 However, this marble pattern has been molded using a two-color mold or a multi-color mold using an opaque colored material. As a result, the marble pattern of the molded product lacks luster and three-dimensionality, and is used in cosmetic compact containers, jewelry boxes, etc. where decorativeness is important.
Beauty containers, furniture parts, and other daily necessities lacked a sense of taste, making it impossible to increase their product value.
発明が解決しようとする問題点
本発明は上述のごとき問題点を解決しようとす
るものであつて、化粧用コンパクト容器、宝石
箱、美容用具、家具の部品、その他の日用雑貨品
等の装飾性を重視される成型物に、光沢と立体感
を有するマーブル模様を施すことを可能とし、趣
味感に優れた成型物を得ることができ、商品価値
を高めることが出来るものである。Problems to be Solved by the Invention The present invention aims to solve the above-mentioned problems, and it is an object of the present invention to solve the above-mentioned problems. To make it possible to apply a marble pattern having luster and three-dimensional effect to a molded product whose appearance is emphasized, to obtain a molded product with an excellent sense of taste, and to increase the commercial value.
問題点を解決するための手段
本発明は上述のごとき問題点を解決するため、
ポリメチル・メタアクリレート樹脂30〜70wt％
と、アクリロニトリル含有量25〜32wt％のスチ
レン・アクリロニトリル共重合体樹脂30〜70wt
％とからなる、ペレツト状の真珠光沢状樹脂組成
物１〜25wt％と、ペレツト状の透明樹脂75〜
99wt％とを不完全混合し、この不完全混合物を
射出成型方法により成型型内に射出することによ
り行なうことを特徴とするものである。Means for Solving the Problems The present invention solves the above problems by:
Polymethyl methacrylate resin 30-70wt%
and 30-70wt styrene-acrylonitrile copolymer resin with acrylonitrile content of 25-32wt%
%, a pellet-like pearlescent resin composition of 1 to 25 wt%, and a pellet-shaped transparent resin of 75 to 25 wt%.
This method is characterized by incompletely mixing 99 wt % of the mixture and injecting this incomplete mixture into a mold using an injection molding method.
また、他の発明は、ポリメチル・メタアクリレ
ート樹脂30〜70wt％と、アクリロニトリル含有
量25〜32wt％のスチレン・アクリロニトリル共
重合体樹脂30〜70wt％とからなる混合物50〜
95wt％と、アクリロニトリル・ブタジエン・ス
チレン樹脂５〜50wt％とからなるペレツト状の
真珠光沢樹脂１〜25wt％と、ペレツト状の透明
樹脂75〜99wt％とを不完全混合し、この不完全
混合物を射出成型方法により成型型内に射出する
ことにより行なうことを特徴とするものである。 Further, another invention provides a mixture consisting of 30 to 70 wt% of polymethyl methacrylate resin and 30 to 70 wt% of styrene-acrylonitrile copolymer resin having an acrylonitrile content of 25 to 32 wt%.
95 wt%, 1 to 25 wt% of a pellet-shaped pearlescent resin consisting of 5 to 50 wt% of acrylonitrile-butadiene-styrene resin, and 75 to 99 wt% of a pellet-shaped transparent resin, and this incomplete mixture is This is characterized in that it is performed by injecting into a mold using an injection molding method.
上記各発明に於いて透明樹脂とは、スチレン・
アクリロニトリル共重合体樹脂、ポリメチル・メ
タアクリレート樹脂、透明アクリロニトリル・ブ
タジエン・スチレン樹脂、又はこれらの混合、若
しくは共重合によつて得られる透明樹脂の何れで
も良い。 In each of the above inventions, the transparent resin refers to styrene,
Any of an acrylonitrile copolymer resin, a polymethyl methacrylate resin, a transparent acrylonitrile-butadiene-styrene resin, or a transparent resin obtained by mixing or copolymerizing these may be used.
また、真珠光沢樹脂は、特開昭50−155556号公
報に記載されている、スチレン・アクリロニトリ
ル共重合体とポリメチル・メタアクリレートの混
合によつて得られる真珠光沢樹脂である。又は特
開昭51−41749号公報に記載されている、スチレ
ン・アクリロニトリル共重合体、ポリメチル・メ
タアクリレート樹脂、アクリロニトリル・ブタジ
エン・スチレン樹脂、の混合物からなる真珠光沢
樹脂である。 The pearlescent resin is a pearlescent resin obtained by mixing a styrene-acrylonitrile copolymer and polymethyl methacrylate, which is described in JP-A-50-155556. Alternatively, it is a pearlescent resin made of a mixture of a styrene-acrylonitrile copolymer, a polymethyl-methacrylate resin, and an acrylonitrile-butadiene-styrene resin, as described in JP-A-51-41749.
これ等の透明樹脂75〜99wt％と、真珠光沢樹
脂１〜25wt％をペレツト状で混合する。これを
プランジヤー成型機等の射出成型機から、樹脂が
金型内へ吐出される時に、透明樹脂と真珠光沢樹
脂が完全に混合しない様に、成型機のスクリユ
ー、金型構造、成型条件を考慮して不完全混合状
態で成型する。 75 to 99 wt% of these transparent resins and 1 to 25 wt% of a pearlescent resin are mixed in pellet form. When the resin is discharged into the mold from an injection molding machine such as a plunger molding machine, the screw of the molding machine, mold structure, and molding conditions are considered so that the transparent resin and pearlescent resin do not completely mix. and mold it in an incompletely mixed state.
この不完全混合状態とするためには、種々の条
件がある。例えば射出成型機のシリンダーの温度
を高くすれば混合率が高くなり、温度を低くすれ
ば、不完全混合状態となる。また、射出成型機の
シリンダー内のスクリユウの溝間隔を小さくすれ
ば、混合率が高くなり、溝間隔を大きくすれば不
完全混合状態となる。このような条件を適宜組み
合わせる事により、任意の混合率を得ることがで
きるものである。 There are various conditions to achieve this incompletely mixed state. For example, increasing the temperature of the cylinder of an injection molding machine will increase the mixing ratio, and lowering the temperature will result in incomplete mixing. Furthermore, if the groove spacing of the screws in the cylinder of the injection molding machine is made small, the mixing ratio will be increased, and if the groove spacing is made large, the mixture will be incompletely mixed. By appropriately combining such conditions, an arbitrary mixing ratio can be obtained.
本発明は上述のごとく、透明樹脂層の中に真珠
光沢樹脂が、乱雲状、浮雲状、流れ雲等のマーブ
ル状の外観になる。そのため、透明樹脂を介して
真珠光沢樹脂に光線が当たると、真珠光沢樹脂の
射出成型時の樹脂の流れによるマーブル模様が、
光線により、その流れ模様、深さ等により微妙に
乱反射する。その結果、真珠光沢樹脂が立体感の
ある乱雲、浮雲、流れ雲状等の、美しいマーブル
状の外観模様を生じる。 As described above, in the present invention, the pearlescent resin in the transparent resin layer has a marble-like appearance such as a turbulent cloud, a floating cloud, or a flowing cloud. Therefore, when a light beam hits the pearlescent resin through the transparent resin, the marble pattern created by the resin flow during injection molding of the pearlescent resin will appear.
Light rays cause subtle diffuse reflection depending on the flow pattern, depth, etc. As a result, the pearlescent resin produces a beautiful marble-like exterior pattern, such as a three-dimensional turbulent cloud, floating cloud, or flowing cloud shape.
この方法は、透明樹脂に真珠光沢樹脂をペレツ
ト状で混入するため、一般のプランジヤー射出成
型機等の射出成型機を使用する。しかし、成型機
から金型内へ樹脂が吐出される時、および成型機
中で、透明樹脂と真珠光沢状樹脂が完全に混合し
ない様に、射出成型機のスクリユー、金型の構
造、成型条件を考慮する必要がある。 In this method, an injection molding machine such as a general plunger injection molding machine is used to mix the pearlescent resin into the transparent resin in the form of pellets. However, when the resin is discharged from the molding machine into the mold, and in the molding machine, the screw of the injection molding machine, the structure of the mold, the molding conditions, etc. need to be considered.
また、真珠光沢樹脂と透明樹脂の混合割合は、
透明樹脂の配合割合が少なくなる程、真珠光沢樹
脂のみの場合に外観が近くなる。そのため、少な
くとも透明樹脂と真珠光沢樹脂を、重量比で75：
25の割合とし、好ましくは84：16程度にすること
により、良好な外観を得ることが出来る。 In addition, the mixing ratio of pearlescent resin and transparent resin is
The smaller the proportion of the transparent resin mixed, the closer the appearance becomes when only the pearlescent resin is used. Therefore, the weight ratio of at least transparent resin and pearlescent resin is 75:
A good appearance can be obtained by setting the ratio to 25:1, preferably about 84:16.
また、透明樹脂と真珠光沢樹脂の割合が重量比
で99：１程度を超え、透明樹脂が多く、真珠光沢
樹脂が少なくなると、真珠光沢樹脂による浮雲
状、流れ雲状等のマーブル状外観を呈しにくく成
り、そして、マーブル模様の形状のバラツキを生
じ易くなる。そのため、透明樹脂と真珠光沢樹脂
を、重量比で99：１以内、好ましくは98.6：1.4
以内の配合とするのが好ましい。 In addition, if the ratio of transparent resin to pearlescent resin exceeds about 99:1 by weight, with a large amount of transparent resin and a small amount of pearlescent resin, the pearlescent resin will exhibit a marble-like appearance such as floating clouds or flowing clouds. The marble pattern becomes difficult to form, and variations in the shape of the marble pattern are likely to occur. Therefore, the weight ratio of transparent resin and pearlescent resin is within 99:1, preferably 98.6:1.4.
It is preferable that the composition be within the following range.
また透明樹脂と真珠光沢樹脂とを成型物とした
場合の一例を、図面に表わせば、第１図および第
２図に示すごときものとなり、真珠光沢樹脂１は
透明樹脂２によつて外周を被覆されるように、透
明樹脂２の中に点在するか、流れを描く様に位置
するものとなる。 An example of a molded product made of a transparent resin and a pearlescent resin is shown in FIGS. 1 and 2, where the pearlescent resin 1 is covered with a transparent resin 2. As shown in FIG.
実施例 １
透明樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含量21wt％） 96.8wt％
真珠光沢樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含有量28wt％） 1.6wt％
ポリメチルメタアクリレート樹脂 1.6wt％
上記の各ペレツト状樹脂をスクリユウ式射出成
型機により、不完全混合状態で成型したところ、
目視により極めて優れたマーブル模様を得ること
ができた。Example 1 Transparent resin Styrene/acrylonitrile copolymer resin (acrylonitrile content 21wt%) 96.8wt% Pearlescent resin Styrene/acrylonitrile copolymer resin (acrylonitrile content 28wt%) 1.6wt% Polymethyl methacrylate resin 1.6wt% Each of the above When pelletized resin was molded in an incompletely mixed state using a screw-type injection molding machine,
Visually, it was possible to obtain an extremely excellent marble pattern.
実施例 ２
透明樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含量24wt％） 99wt％
真珠光沢樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含有量28wt％）
0.05wt％
ポリメチルメタアクリレート樹脂 0.05wt％
上記の各ペレツト状樹脂をスクリユウ式射出成
型機により、不完全混合状態で成型したところ、
目視により、優れたマーブル模様を得ることがで
きた。Example 2 Transparent resin Styrene/acrylonitrile copolymer resin (acrylonitrile content 24wt%) 99wt% Pearlescent resin Styrene/acrylonitrile copolymer resin (acrylonitrile content 28wt%)
0.05wt% Polymethyl methacrylate resin 0.05wt% Each of the above pellet-shaped resins was molded in an incompletely mixed state using a screw-type injection molding machine.
Visually, it was possible to obtain an excellent marble pattern.
実施例 ３
透明樹脂
ポリメチルメタアクリレート樹脂 95.3wt％
真珠光沢樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含量28wt％） 2.6wt％
アクリロニトリル・ブタジエン・スチレン樹
脂 0.2wt％
ポリメチルメタアクリレート 1.9wt％
上記の各ペレツト状樹脂を、スクリユウ式射出
成型機により、不完混合全状態で成型したとこ
ろ、目視により極めて優れたマーブル模様を得る
ことができた。Example 3 Transparent resin Polymethyl methacrylate resin 95.3wt% Pearlescent resin Styrene/acrylonitrile copolymer resin (acrylonitrile content 28wt%) 2.6wt% Acrylonitrile/butadiene/styrene resin 0.2wt% Polymethylmethacrylate 1.9wt% Each of the above When pelletized resin was molded in an incompletely mixed state using a screw-type injection molding machine, an extremely excellent marble pattern could be obtained by visual inspection.
実施例 ４
透明樹脂
ポリメチルメタアクリレート樹脂 97.5wt％
真珠光沢樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含量28wt％） 1.5wt％
ポリメチルメタアクリレート樹脂 1.0wt％
上記の各ペレツト状樹脂をスクリユウ式射出成
型機により、不完全混合状態で成型したところ、
目視により極めて優れたマーブル模様を得ること
ができた。Example 4 Transparent resin Polymethyl methacrylate resin 97.5wt% Pearlescent resin Styrene-acrylonitrile copolymer resin (acrylonitrile content 28wt%) 1.5wt% Polymethylmethacrylate resin 1.0wt% Each of the above pellet-shaped resins was molded by screw injection molding. When molded in an incompletely mixed state using a machine,
Visually, it was possible to obtain an extremely excellent marble pattern.
実施例 ５
ポリメチルメタアクリレート樹脂 95.3wt％
真珠光沢樹脂
スチレン・アクリロニトリル共重合樹脂
（アクリロニトリル含量28wt％） 1.4wt％
アクリロニトリル・ブタジエン・スチレン樹
脂 1.4wt％
ポリメチルメタアクリレート樹脂 1.9wt％
上記の各ペレツト状樹脂を、スクリユウ式射出
成型機により、不完全混合状態で成型したとこ
ろ、目視により極めて優れたマーブル模様を得る
ことができた。Example 5 Polymethyl methacrylate resin 95.3wt% Pearlescent resin Styrene-acrylonitrile copolymer resin (acrylonitrile content 28wt%) 1.4wt% Acrylonitrile-butadiene-styrene resin 1.4wt% Polymethylmethacrylate resin 1.9wt% Each of the above pellets When the resin was molded in an incompletely mixed state using a screw-type injection molding machine, an extremely excellent marble pattern could be obtained by visual inspection.
発明の効果
本発明は上述のごとく構成したものであるか
ら、化粧用コンパクト容器、宝石箱、美容用具、
家具の部品、その他の日用雑貨品等の装飾性を重
視される成型物に、光沢と立体感を有するマーブ
ル模様を施すことを可能とする。そして、趣味感
に優れた成型物を得ることができ、商品価値を高
めることが出来るものである。Effects of the Invention Since the present invention is configured as described above, it can be used as a compact container for cosmetics, a jewelry box, a beauty tool, etc.
To make it possible to apply a marble pattern having luster and three-dimensional effect to molded products such as furniture parts and other daily necessities where decorativeness is important. Moreover, it is possible to obtain a molded product with an excellent sense of taste, and the product value can be increased.
図面は本発明の一実施例を示すものであつて、
第１図は平面図、第２図は断面図である。
１……真珠光沢樹脂、２……透明樹脂。
The drawings show one embodiment of the invention,
FIG. 1 is a plan view, and FIG. 2 is a sectional view. 1... Pearlescent resin, 2... Transparent resin.
Claims (1)
70wt％と、アクリロニトリル含有量25〜32wt％
のスチレン・アクリロニトリル共重合体樹脂30〜
70wt％とからなる、ペレツト状の真珠光沢状樹
脂組成物１〜25wt％と、ペレツト状の透過樹脂
75〜99wt％とを不完全混合し、この不完全混合
物を射出成型方法により成型型内に射出すること
により行なうことを特徴とするマーブル模様の成
型物の成型方法。 ２ ポリメチル・メタアクリレート樹脂30〜
70wt％と、アクリロニトリル含有量25〜32wt％
のスチレン・アクリロニトリル共重合体樹脂30〜
70wt％とからなる混合物50〜95wt％と、アクリ
ロニトリル・ブタジエン・スチレン樹脂５〜
50wt％とからなるペレツト状の真珠光沢樹脂１
〜25wt％と、ペレツト状の透明樹脂75〜99wt％
とを不完全混合し、この不完全混合物を射出成型
方法により成型型内に射出することにより行なう
ことを特徴とするマーブル模様の成型物成型方
法。[Claims] 1. Polymethyl methacrylate resin 30~
70wt% and acrylonitrile content 25-32wt%
Styrene-acrylonitrile copolymer resin 30~
1 to 25 wt% of a pellet-shaped pearlescent resin composition consisting of 70 wt%, and a pellet-shaped transparent resin.
75 to 99 wt%, and the incomplete mixture is injected into a mold by an injection molding method. 2 Polymethyl methacrylate resin 30~
70wt% and acrylonitrile content 25-32wt%
Styrene-acrylonitrile copolymer resin 30~
50-95wt% of a mixture consisting of 70wt% and 5-95wt% of acrylonitrile-butadiene-styrene resin.
Pellet-like pearlescent resin 1 consisting of 50wt%
~25wt% and pellet-like transparent resin 75~99wt%
1. A method for molding a marble-patterned product, characterized in that the process is carried out by incompletely mixing the following: and injecting the incomplete mixture into a mold using an injection molding method.