JPH0544108B2 - - Google Patents
Info
- Publication number
- JPH0544108B2 JPH0544108B2 JP59217981A JP21798184A JPH0544108B2 JP H0544108 B2 JPH0544108 B2 JP H0544108B2 JP 59217981 A JP59217981 A JP 59217981A JP 21798184 A JP21798184 A JP 21798184A JP H0544108 B2 JPH0544108 B2 JP H0544108B2
- Authority
- JP
- Japan
- Prior art keywords
- recording
- protective film
- optical
- recording layer
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】
発明の背景
技術分野
本発明は、光カード、特にヒートモードの光記
録を行う光カードに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an optical card, and particularly to an optical card that performs heat mode optical recording.
先行技術とその問題点
一般に、情報の記録および再生として磁気記録
方式が広く知られている。例えば、磁気テープ、
磁気デイスク、磁気記録カード等の磁気記録媒体
が挙げられる。この一つの利用例としてキヤツシ
ユカード等として使用されている磁気カードがあ
る。Prior Art and its Problems Generally, magnetic recording methods are widely known for recording and reproducing information. For example, magnetic tape,
Examples include magnetic recording media such as magnetic disks and magnetic recording cards. An example of this use is a magnetic card used as a cash card or the like.
周知のように磁気記録再生方式は、情報の記
録、消去および再記録を容易に行なうことができ
る。従つて、この方式を利用した磁気カードは、
悪用されたりまたは磁石等による磁場の中に置か
れると記録されている情報に変化が生ずるなど情
報の信頼性は低い。また、磁気カードは磁気ヘツ
ドの制約から低密度の情報の記録しかできず、さ
らにカードの大きさに基づく制限から、極めて少
量の情報しか記録できないという欠点がある。 As is well known, the magnetic recording/reproducing method allows information to be easily recorded, erased, and re-recorded. Therefore, magnetic cards using this method are
If it is misused or placed in a magnetic field such as a magnet, the recorded information may change, making the information unreliable. Further, magnetic cards have the disadvantage that they can only record information at a low density due to limitations of the magnetic head, and furthermore, they can only record a very small amount of information due to limitations based on the size of the card.
従つて、悪用防止のために複雑な信号形態を取
るという手段も、以上の磁気カード上の制限から
不可能である。 Therefore, it is impossible to take a complicated signal form to prevent misuse due to the above-mentioned limitations on magnetic cards.
これらの欠点を改善するものとして、光学的原
理による記録および再生方式が最近提案されてい
る。この光学的記録および再生方式によるものに
は、光カードが挙げられる。 Recording and reproducing methods based on optical principles have recently been proposed to improve these drawbacks. Optical cards are examples of devices based on this optical recording and reproducing method.
この光カードの応用範囲は広く、銀行のキヤツ
シユカードをはじめ、クレジツトカード、身分証
明書、運転免許証、定期券、公衆電話カード、ガ
ソリン購入カード等、多種にわたつて、その実用
化が期待されている。 This optical card has a wide range of applications, and is expected to be put to practical use in a wide variety of applications, including bank cash cards, credit cards, identification cards, driver's licenses, commuter passes, public phone cards, and gasoline purchase cards. has been done.
ところで、光カードに適用しうる光記録媒体と
してはヒートモードのものがある。 By the way, there is a heat mode optical recording medium that can be applied to an optical card.
このヒートモードの光記録媒体は、記録光を熱
として利用する光記録媒体であり、その１例とし
て、レーザー等の記録光で媒体の一部を融解、除
去等して、ピツトと称される小穴を形成し書き込
みを行い、このピツトにより情報を記録し、この
ピツトを読み出し光で検出して読み出しを行うピ
ツト形成タイプのものがある。 This heat mode optical recording medium is an optical recording medium that uses recording light as heat. One example is a heat mode optical recording medium that uses recording light such as a laser to melt or remove a part of the medium, which is called a pit. There is a pit-forming type in which writing is performed by forming small holes, information is recorded using the pits, and reading is performed by detecting the pits with a readout light.
このようなピツト形成タイプの媒体、特にその
うち、装置を小型化できる半導体レーザーを光源
とするものにおいては、これまで、Teを主体と
する材料を記録層とするものが大半をしめてい
る。 Until now, most of these pit-forming type media, especially those using a semiconductor laser as a light source that can make the device smaller, have a recording layer made of a material mainly composed of Te.
しかし、近年、Te系材料が有害であること、
そしてより高感度化する必要があること、より製
造コストを安価にする必要があることから、Te
系にかえ、各種色素を主とした有機材料系の記録
層を用いる媒体についての提案や報告が増加して
いる。 However, in recent years, it has become clear that Te-based materials are harmful.
In addition, due to the need for higher sensitivity and lower manufacturing costs, Te
Instead, there are an increasing number of proposals and reports on media using recording layers made of organic materials containing various dyes.
ところで、光カードでは、記録層の損傷防止の
ため、記録層上に保護膜を形成する必要がある。
そして、この保護膜は、基材とラミネートされる
ので、記録層と保護膜間は密着される。 By the way, in optical cards, it is necessary to form a protective film on the recording layer in order to prevent damage to the recording layer.
Since this protective film is laminated with the base material, the recording layer and the protective film are in close contact with each other.
しかし、このように記録層と保護層とを密着す
ると、色素系の記録層では反射率が低下し、コン
トラストおよびＳ／Ｎ比が小さいという欠点があ
る。 However, when the recording layer and the protective layer are brought into close contact with each other in this way, the dye-based recording layer has the disadvantage that the reflectance is lowered and the contrast and S/N ratio are low.
発明の目的
本発明の目的は、コントラストおよびＳ／Ｎ比
の高い色素系の記録層を有する光カードを提供す
ることにある。 OBJECT OF THE INVENTION An object of the present invention is to provide an optical card having a dye-based recording layer with high contrast and S/N ratio.
発明の開示
このような目的は、下記の本発明によつて達成
される。 DISCLOSURE OF THE INVENTION These objects are achieved by the invention described below.
すなわち、本発明は
基板と、色素または色素組成物からなる記録層
を有する光記録部と、保護膜とを有する光カード
において、
基板と保護膜間にスペーサーを介在させ、この
スペーサーにより、光記録部と保護膜との間に、
0.01mm以上の空隙が形成されていることを特徴と
する光カードである。 That is, the present invention provides an optical card having a substrate, an optical recording section having a recording layer made of a dye or a dye composition, and a protective film, in which a spacer is interposed between the substrate and the protective film, and the spacer allows optical recording. between the part and the protective film,
This optical card is characterized by having a gap of 0.01 mm or more.
発明の具体的構成
以下、本発明の具体的構成について詳細に説明
する。 Specific Configuration of the Invention The specific configuration of the present invention will be described in detail below.
第１図には、本発明の実施例が示される。 FIG. 1 shows an embodiment of the invention.
第１図に示されるように、本発明の光カード１
は、基板２を有する。 As shown in FIG. 1, an optical card 1 of the present invention
has a substrate 2.
基板２は、通常、樹脂材質とし、アクリル樹
脂、ポリカーボネート、ナイロン、ポリオレフイ
ン等のいずれであつてもよい。 The substrate 2 is usually made of a resin material, and may be made of acrylic resin, polycarbonate, nylon, polyolefin, or the like.
ただ、印刷性、積層性、耐湿性、強度等を考慮
すると、ポリ塩化ビニル系のポリマーが好適であ
る。ポリ塩化ビニル系のポリマーとしては、塩化
ビニルのホモポリマーの他、塩化ビニル−酢酸ビ
ニル、塩化ビニル−マレイン酸等の塩化ビニルコ
ポリマーであつてよい。 However, in consideration of printability, lamination properties, moisture resistance, strength, etc., polyvinyl chloride-based polymers are preferred. The polyvinyl chloride-based polymer may be a vinyl chloride homopolymer or a vinyl chloride copolymer such as vinyl chloride-vinyl acetate or vinyl chloride-maleic acid.
基板２の厚さは、0.1〜1.0mm程度とする。基板
２上には、記録層３が設層される。 The thickness of the substrate 2 is approximately 0.1 to 1.0 mm. A recording layer 3 is provided on the substrate 2 .
記録層としては、色素単独からなるか、色素組
成物からなるものである。 The recording layer may be made of a dye alone or a dye composition.
用いる色素としては、書き込み光および読み出
し光の波長に応じ、これを有効に吸収するものの
なかから、適宜決定すればよい。この場合、これ
らの光源としては、装置を小型できる点で、半導
体レーザーを用いることが好ましいので、色素は
シアニン系、フタロシアニン系、アントラキノン
系、アゾ系、トリフエニルメタン系、ピリリウム
ないしチアピリリウム塩系等が好ましい。 The dye to be used may be appropriately determined from among those that effectively absorb the wavelengths of the writing light and reading light. In this case, it is preferable to use a semiconductor laser as the light source because the device can be made smaller, so the dye may be cyanine-based, phthalocyanine-based, anthraquinone-based, azo-based, triphenylmethane-based, pyrylium or thiapyrylium salt-based, etc. is preferred.
また、色素組成物を記録層とする場合、ニトロ
セルロース等の自己酸化性の樹脂や、ポリスチレ
ン、ナイロン等の熱可塑性樹脂を含有させること
ができる。また、色素の酸化劣化を防止するた
め、クエンチヤーを含有させることもできる。さ
らには、この他の添加剤を含有させてもよい。 Further, when the dye composition is used as a recording layer, it can contain a self-oxidizing resin such as nitrocellulose, or a thermoplastic resin such as polystyrene or nylon. Furthermore, a quencher may be included in order to prevent oxidative deterioration of the dye. Furthermore, other additives may also be included.
このような場合、特に好ましくは、インドレニ
ン系のシアニン色素とビスフエニルジチオール系
等のクエンチヤーとの混合物が好ましい。 In such a case, a mixture of an indolenine cyanine dye and a quencher such as bisphenyldithiol is particularly preferred.
またこれらを色素のカチオンと、クエンチヤー
のアニオンとのイオン結合体として用いるのも好
ましい。 It is also preferable to use these as an ionic bond between a dye cation and a quencher anion.
記録層の設層は、ケトン系、エステル系、エー
テル系、芳香族系、ハロゲン化アルキル系、アル
コール系等の溶媒を用いてスピンナーコート等の
塗布を行えばよい。 The recording layer may be formed by spinner coating using a ketone, ester, ether, aromatic, halogenated alkyl, or alcohol solvent.
このような記録層は0.01〜10μｍの厚さとすれ
ばよく、特に0.05〜0.1μｍの厚さとすることが好
ましい。 Such a recording layer may have a thickness of 0.01 to 10 μm, preferably 0.05 to 0.1 μm.
なお、トラツキング制御用の溝を設けることも
できるがその場合、記録層における記録トラツク
部の厚さは、0.2μｍ以下、より好ましくは0.05〜
0.15μｍとすることが好ましい。 Note that a groove for tracking control can be provided, but in that case, the thickness of the recording track portion in the recording layer is 0.2 μm or less, more preferably 0.05 μm or less.
It is preferable to set it to 0.15 μm.
このような光記録層はそれのみで光記録部とし
てもよい。あるいは記録層の上層あるいは下地層
を設層して、光記録部とすることもできる。 Such an optical recording layer may be used as an optical recording section by itself. Alternatively, an optical recording section can be formed by providing an upper layer or a base layer on the recording layer.
上層または下地層としては、記録層の上下に半
透膜（ハーフミラー層）や反射層等を設けてもよ
い。 As the upper layer or underlayer, a semi-transparent film (half mirror layer), a reflective layer, etc. may be provided above and below the recording layer.
このような光記録部は、カードの用途に応じ、
基板上にて、その全面または一部に、ストライプ
状、矩形状等の形状に設けられる。 This type of optical recording section can be used depending on the purpose of the card.
It is provided on the entire surface or a part of the substrate in a shape such as a stripe shape or a rectangular shape.
光記録部の上には保護膜４が設けられる。 A protective film 4 is provided on the optical recording section.
保護膜４は、塗布によつて形成することもでき
るが、通常、フイルム体を融着ないし接着して形
成する。 Although the protective film 4 can be formed by coating, it is usually formed by fusing or adhering a film body.
保護膜４の材質としては、各種樹脂が好適であ
るが、特に吸湿性、耐ヒツカキ性等の点で、前記
のポリ塩化ビニル系のポリマーが好適である。 Various resins are suitable as the material for the protective film 4, but the above-mentioned polyvinyl chloride polymer is particularly suitable in terms of moisture absorption and scratch resistance.
そして、その厚さは、0.1〜1.0mm程度とする。
これは、0.1mm未満となると、ホコリやゴミの影
響で記録・再生が阻害され、また1.0mmをこえる
と実用上不適となるからである。 The thickness thereof is approximately 0.1 to 1.0 mm.
This is because if it is less than 0.1 mm, recording and playback will be inhibited by the influence of dust and dirt, and if it exceeds 1.0 mm, it will be unsuitable for practical use.
なお、保護膜４は、各種ヒツカキ防止用の被覆
層を有していてもよい。 In addition, the protective film 4 may have various coating layers for preventing scratches.
また、基板２は、その両面に光記録部および保
護膜を有してもよく、これらは片面のみに設けら
れていてもよい。 Further, the substrate 2 may have an optical recording section and a protective film on both sides thereof, or these may be provided only on one side.
後者の場合、基板裏面には保護膜が形成されて
いてもよい。 In the latter case, a protective film may be formed on the back surface of the substrate.
このような保護膜と光記録部との間にはスペー
サー６が介在される。 A spacer 6 is interposed between such a protective film and the optical recording section.
このスペーサー６は、空隙５を形成するための
ものである。 This spacer 6 is for forming a void 5.
そして、空隙長は0.01mm以上とする。 The void length shall be 0.01 mm or more.
これは、0.01mm未満となると、コントラスト向
上効果の実効がないからである。 This is because if it is less than 0.01 mm, the contrast improvement effect will not be effective.
また、空隙は、光記録部上の全面に亘つて設け
られてもよく、部分的に設けられてもよい。 Further, the gap may be provided over the entire surface of the optical recording section, or may be provided partially.
部分的に設けるときには、その部分を通常記録
トラツクとする。 When a portion is provided, that portion is used as a normal recording track.
すなわち、スペーサー６に所望の窓部を形成
し、この窓部以外の部分にて、記録層ないし基板
と融着ないし接着すればよい。 That is, a desired window portion may be formed in the spacer 6, and the portion other than the window portion may be fused or adhered to the recording layer or the substrate.
なお、スペーサー６の厚さは、通常空隙５の厚
さを決定するものであるが、一般に0.01〜0.5mm
程度とする。 The thickness of the spacer 6 normally determines the thickness of the void 5, and is generally 0.01 to 0.5 mm.
degree.
また、上記の窓部は、連続状のストリツプ等と
しても散点状としてもよい。 Furthermore, the above-mentioned window portion may be formed into a continuous strip or the like, or may be formed into a dotted shape.
スペーサー６は、ポリエステル、ポリ塩化ビニ
ル等の各種樹脂から形成すればよい。そして、窓
部の形成は、成形時に形成したり、打抜いたりす
ればよい。 The spacer 6 may be formed from various resins such as polyester and polyvinyl chloride. The window portion may be formed during molding or by punching.
また、スペーサー６と保護膜および基板との固
着は融着、接着等いずれによつてもよい。 Further, the spacer 6 may be fixed to the protective film and the substrate by any method such as fusion bonding or adhesion.
発明の具体的効果
本発明によれば、光記録部と保護膜との間に
0.01mm以上の空隙が形成されているので、コント
ラストおよびＳ／Ｎ比が向上する。 Specific Effects of the Invention According to the present invention, between the optical recording section and the protective film,
Since voids of 0.01 mm or more are formed, contrast and S/N ratio are improved.
本発明者らは、本発明の効果を確認するため
種々実験を行つた。以下に１例を示す。 The present inventors conducted various experiments to confirm the effects of the present invention. An example is shown below.
実験例
85×54×0.3mmの塩化ビニル樹脂製シート上に
0.06μｍ厚にて１，1′，３，３，3′，3′−ヘキサメ
チル−４，4′，５，5′−ジベンゾ−２，2′−イン
ドトリカルボシアニン パークロレート（２重量
部）と、
NIR−PA1006〔三井東圧化学株式会社製ビス
フエニルジチオールNi錯体〕（１重量部）とかな
らる記録層を設層した。Experimental example: On a PVC resin sheet of 85 x 54 x 0.3 mm.
1,1',3,3,3',3'-hexamethyl-4,4',5,5'-dibenzo-2,2'-indotricarbocyanine perchlorate (2 parts by weight) at 0.06 μm thickness A recording layer consisting of NIR-PA1006 [bisphenyldithiol Ni complex manufactured by Mitsui Toatsu Chemical Co., Ltd.] (1 part by weight) was formed.
この上に、0.1mm厚で、３mm巾、３mm間隔の窓
部を有するポリエステルスペーサーを融着した。 On top of this, a polyester spacer having a thickness of 0.1 mm, a width of 3 mm, and windows spaced at 3 mm intervals was fused.
さらに、この上に、塩化ビニル樹脂製、0.3mm
厚のシートを熱融着した。 Furthermore, on top of this, made of vinyl chloride resin, 0.3 mm
A thick sheet was heat-sealed.
半導体レーザーを用いて記録・再生を行つたと
ころ、空隙を形成しないときと比較して、コント
ラストは２倍向上した。 When recording and reproducing were performed using a semiconductor laser, the contrast was twice as high as when no voids were formed.
第１図は、本発明の光カードの断面図である。
符号の説明、１……光カード、２……基板、３
……記録層、４……保護部材、５……空隙、６…
…スペーサー。
FIG. 1 is a sectional view of the optical card of the present invention. Explanation of symbols, 1... Optical card, 2... Board, 3
...Recording layer, 4...Protection member, 5...Void, 6...
…spacer.
Claims (1)
層を有する光記録部と、保護膜とを有する光カー
ドにおいて、 基板と保護膜間にスペーサーを介在させ、この
スペーサーにより、光記録部と保護膜との間に、
0.01mm以上の空隙が形成されていることを特徴と
する光カード。[Scope of Claims] 1. In an optical card having a substrate, an optical recording section having a recording layer made of a dye or a dye composition, and a protective film, a spacer is interposed between the substrate and the protective film, and by this spacer, Between the optical recording section and the protective film,
An optical card characterized by having a gap of 0.01 mm or more.