JPH0573174B2 - - Google Patents
Info
- Publication number
- JPH0573174B2 JPH0573174B2 JP61214319A JP21431986A JPH0573174B2 JP H0573174 B2 JPH0573174 B2 JP H0573174B2 JP 61214319 A JP61214319 A JP 61214319A JP 21431986 A JP21431986 A JP 21431986A JP H0573174 B2 JPH0573174 B2 JP H0573174B2
- Authority
- JP
- Japan
- Prior art keywords
- blood
- tube
- rubber stopper
- blood collection
- mol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
〈産業上の利用分野〉
本発明は、血液を採取し、生化学検査や血清学
検査、血液学検査、血沈検査など血液を検体とし
た各種の検査に使用される改良された真空採血管
に関する。
〈従来の技術〉
血液検査に使用される採血管は、通常ゴム栓体
によつて密閉された内部が所定の真空度に維持さ
れた一般にガラス製の試験管であり、管内の陰圧
を利用して採血針を通して自動的に所定量の血液
を採取することができ、一般に真空採血管と呼称
されている。このような真空採血管には、その検
査目的に応じて検査前の煩雑な準備操作を省くた
めに、あらかじめ血液凝固阻止剤や血液凝固促進
剤、解糖阻止剤などの薬剤が収容されたものや、
管壁やゴム栓への血液の付着を防ぐ目的で管壁や
ゴム栓にシリコーンが塗布されたものなどがあ
る。
〈発明が解決しようとする問題点〉
一般に従来の真空採血管は、
血清学検査および生化学検査用採血管の場
合、遠心分離後ゴム栓に血液が付着して残るた
め（以下付着して残つた血液を、残血という）、
ゴム栓を取り外した時に残血の一部が試験管の
方に移行することがあり、従つて上澄みの血清
部分に血球が混入することがあり、正確な検査
を行うことができない。
あらかじめ管内に薬剤を封入した採血管の場
合、封入薬剤と血液とを混和させるために採血
管を交互に逆転させるいわゆる転倒混和を行う
必要があり、その際血液に泡が立ち、その泡が
いつまでも消えないために、自動検査機で検査
を行つた場合、液面センサーの誤動作が起る。
ゴム栓にシリカ等の消泡剤を塗布した採血管
の場合、採血管に収容された血液をガラス板に
塗抹する操作を行つた際に、ガラス板上で血液
がはじかれてしまうた、検鏡が面倒である。
などの問題があり、その解決が望まれていた。
本発明は上記問題点に鑑みてなされたもので、
その目的とするところは、ゴム栓に残血を生ずる
ことがなく、消泡性が良く、さらにガラス板に塗
布された血液がはじかれることのない真空採血管
を提供することにある。
〈問題点を解決するための手段〉
本発明者らは、ある種の界面活性剤を塗布した
固体表面では血液の付着が起り難く、また一般に
シリコーン系界面活性剤は曇点を有しており、曇
点付近のある一定の範囲で消泡性を有する（経験
的に確認されている）という２点に着目し、鋭意
研究の結果、ある種のポリオキシアルキレン変性
シリコーン化合物が上記問題点をすべて解決する
ことを見出し、本発明を完成した。
すなわち本発明は、一端の開口した有底筒状の
管と、該管の開口端に気密に挿着されたゴム栓と
で構成され、かつ管内腔が減圧されてなる採血管
において、前記ゴム栓の管内腔側表面に下記一般
式（）で示されるポリオキシアルキレン変性シ
リコーン化合物の皮膜が形成されたことを特徴と
する真空採血管に関する。
<Industrial Application Field> The present invention relates to an improved vacuum blood collection tube used to collect blood and perform various tests using blood as a sample, such as biochemical tests, serology tests, hematology tests, and blood sedimentation tests. . <Prior art> Blood collection tubes used for blood tests are generally glass test tubes that are sealed with a rubber stopper and maintained at a predetermined degree of vacuum. A predetermined amount of blood can be automatically collected through the blood collection needle, and is generally called a vacuum blood collection tube. These vacuum blood collection tubes are pre-filled with drugs such as blood clotting inhibitors, blood coagulation promoters, and glycolytic inhibitors, in order to eliminate complicated pre-test preparation operations depending on the purpose of the test. or,
Some tube walls and rubber plugs are coated with silicone to prevent blood from adhering to the tube walls and rubber plugs. <Problems to be Solved by the Invention> In general, conventional vacuum blood collection tubes for serology and biochemistry tests have problems because blood adheres to and remains on the rubber stopper after centrifugation (hereinafter referred to as adherent and residual blood). The ivy blood is called residual blood),
When the rubber stopper is removed, some of the remaining blood may migrate into the test tube, and therefore blood cells may be mixed into the supernatant serum portion, making it impossible to conduct accurate tests. In the case of a blood collection tube with medicine sealed in the tube in advance, it is necessary to alternately turn the blood collection tube upside down in order to mix the medicine and blood. Because it does not disappear, when an automatic inspection machine is used to inspect it, the liquid level sensor malfunctions. In the case of a blood collection tube with a rubber stopper coated with an antifoaming agent such as silica, when the blood contained in the blood collection tube is smeared onto a glass plate, the blood may be repelled on the glass plate, making it difficult for the test to be performed. Mirrors are a pain. There were problems such as these, and it was hoped that they would be resolved. The present invention has been made in view of the above problems, and
The purpose is to provide a vacuum blood collection tube that does not leave residual blood on the rubber stopper, has good defoaming properties, and does not repel blood applied to a glass plate. <Means for Solving the Problems> The present inventors have discovered that blood is less likely to adhere to a solid surface coated with a certain type of surfactant, and that silicone surfactants generally have a cloud point. focused on the two points of having antifoaming properties within a certain range near the cloud point (which has been confirmed empirically), and as a result of intensive research, certain polyoxyalkylene-modified silicone compounds have been found to solve the above problems. They found a solution to all of these problems and completed the present invention. That is, the present invention provides a blood collection tube consisting of a bottomed cylindrical tube with one end open and a rubber stopper airtightly inserted into the open end of the tube, and in which the inner lumen of the tube is depressurized. The present invention relates to a vacuum blood collection tube characterized in that a film of a polyoxyalkylene-modified silicone compound represented by the following general formula () is formed on the surface of the stopper on the tube lumen side.
【化】
〔ただし、式中Ｇは一般式（）：
−R′−Ｏ（―C2H4O）n――（―C3H6O）o――Ａ
……（）
（ここでR′は炭素原子数１〜８の二価炭化水
素基、Ａは水素原子またはアセチル基、ｍ、ｎは
20≦ｍ＋ｎ≦70を満足する正の整数）で示される
ポリオキシエチレン−ポリオキシプロピレンブロ
ツク共重合基；ａは２又は３、ｂは０又は１であ
り、かつａ＋ｂ＝３を満足する；Ｘ、Ｙは不等式
20≦Ｘ＋Ｙ≦70を満足する正の整数であり、かつ
全体のモル数に対するシロキサン単位およびエチ
レンオキサイド単位の割合がそれぞれ15〜30モル
％および30〜60モル％である。〕
〈実施例〉
次に図面に基づいて本発明の実施例について説
明する。
第１図は本発明の一実施例に関わる真空採血管
を示す中央縦断面図である。
第１図に示すように本発明の真空採血管は、一
端の開口した有底筒状の試験管２と、この試験管
２の開口部を密封するゴム栓３とから構成されて
おり、ゴム栓３の管内腔側表面にはたとえばデイ
ツピングなどの方法により次の条件を満足するポ
リオキシアルキレン変性シリコーン化合物の皮膜
４が形成されている。
すなわち、本発明を構成するポリオキシアルキ
レン変性シリコーン化合物は一般式（）：[Formula G is the general formula (): -R'-O(-C 2 H 4 O) n --(-C 3 H 6 O) o --A
...() (Here, R' is a divalent hydrocarbon group having 1 to 8 carbon atoms, A is a hydrogen atom or an acetyl group, m and n are
A polyoxyethylene-polyoxypropylene block copolymer group represented by a positive integer satisfying 20≦m+n≦70; a is 2 or 3, b is 0 or 1, and satisfies a+b=3; , Y is an inequality
It is a positive integer satisfying 20≦X+Y≦70, and the proportions of siloxane units and ethylene oxide units to the total number of moles are 15 to 30 mol% and 30 to 60 mol%, respectively. ] <Example> Next, an example of the present invention will be described based on the drawings. FIG. 1 is a central vertical sectional view showing a vacuum blood collection tube according to an embodiment of the present invention. As shown in FIG. 1, the vacuum blood collection tube of the present invention is composed of a cylindrical test tube 2 with an open end and a rubber stopper 3 for sealing the opening of the test tube 2. A film 4 of a polyoxyalkylene-modified silicone compound satisfying the following conditions is formed on the surface of the plug 3 on the tube lumen side by a method such as dipping. That is, the polyoxyalkylene-modified silicone compound constituting the present invention has the general formula ():
【化】
で示されるもので、式中Ｇは一般式（）：
−R′−Ｏ（―C2H4O）n――（―C3H6O）o――Ａ
……（）
（ここでR′は炭素原子数１〜８の二価炭化水
素基、Ａは水素原子またはアセチル基、ｍ、ｎは
20≦ｍ＋ｎ≦70を満足する正の整数）で示される
ポリオキシエチレン−ポリオキシプロピレンブロ
ツク共重合基；ａは２又は３、ｂは０又は１であ
り、かつａ＋ｂ＝３を満足する；Ｘ、Ｙは不等等
式20≦Ｘ＋Ｙ≦70を満足する正の整数であり、か
つ全体のモル数に対するシロキサン単位およびエ
チレンオキサイド単位の割合がそれぞれ15〜30モ
ル％および30〜60モル％である。
一般にポリオキシアルキレン変性シリコーン化
合物は種々の方法によつて合成することができ、
例えば分子鎖末端に不飽和結合を有する有機基を
含有するポリオキシアルキレン化合物とメチルハ
イドロジエンポリシロキサンとを白金化合物の存
在下に付加反応させることにより容易に合成する
ことができる。
第１表はこのようにして合成されたポリオキシ
アルキレン変性シリコーン化合物の一般物性を示
すものである。[C] In the formula, G is the general formula (): -R'-O(-C 2 H 4 O) n --(-C 3 H 6 O) o --A
...() (Here, R' is a divalent hydrocarbon group having 1 to 8 carbon atoms, A is a hydrogen atom or an acetyl group, m and n are
A polyoxyethylene-polyoxypropylene block copolymer group represented by a positive integer satisfying 20≦m+n≦70; a is 2 or 3, b is 0 or 1, and satisfies a+b=3; , Y is a positive integer that satisfies the inequality 20≦X+Y≦70, and the proportions of siloxane units and ethylene oxide units with respect to the total number of moles are 15 to 30 mol% and 30 to 60 mol%, respectively. . Generally, polyoxyalkylene-modified silicone compounds can be synthesized by various methods.
For example, it can be easily synthesized by subjecting a polyoxyalkylene compound containing an organic group having an unsaturated bond at the end of its molecular chain to an addition reaction with methylhydrodiene polysiloxane in the presence of a platinum compound. Table 1 shows the general physical properties of the polyoxyalkylene-modified silicone compounds synthesized in this way.
【表】 第１表においてシロキサンＡ〜Ｈの化学式は、 シロキサンＡ：【table】 In Table 1, the chemical formulas of siloxanes A to H are: Siloxane A:
【化】 シロキサンＢ：[ka] Siloxane B:
【化】 シロキサンＣ：[ka] Siloxane C:
【化】 シロキサンＤ：[ka] Siloxane D:
【化】 シロキサンＥ：[ka] Siloxane E:
【化】 シロキサンＦ：[ka] Siloxane F:
【化】 シロキサンＧ：[ka] Siloxane G:
【化】 シロキサンＨ：[ka] Siloxane H:
【化】
であり、これらシロキサンＡ〜Ｈを塗布したゴム
栓を用いて採血管における消泡性、血液のはじ
き、残血について試験を行つたところ第２表のよ
うな結果が得られた。When rubber stoppers coated with these siloxanes A to H were tested for antifoaming properties, blood repellency, and residual blood in blood collection tubes, the results shown in Table 2 were obtained.
【表】
第２表における評価は、消泡性については
◎……消泡性が非常に良い
○……消泡性が良い
△……消泡性がやや悪い
×……消泡性が悪い
血液のはじきについては
◎……血液のはじきが非常に少ない
○……血液のはじきが少ない
×……血液のはじきが多い
残血については
◎……残血を全く認めず
○……わずかに残血を認める
×……非常に多くの残血を認める
となつている。
第２表から、全体のモル数に対するシロキサン
単位およびエチレンオキサイド単位の割合がそれ
ぞれ15〜25モル％および35〜45モル％であるもの
が好ましく、またポリオキシアルキレン変性シリ
コーンとしてはポリエチレン変性シリコーン（表
のシロキサンＡ）が好ましいことが分かる。
〈試験例 １〉
各種シリコーンについて、これを打栓及び嵌合
力規格に合格する濃度で塗布したゴム栓を用いて
残血の試験を行つたところ第３表のような結果が
得られた。ここで試験管は薬剤の入つていないも
の（プレーン管という）を用いており、溶剤型シ
リコーンとしては信越シリコーンKF−96（ジメチ
ルポリシロキサン）を、エマルジヨン型シリコー
ンとしては信越シリコーンポロンMGを使用して
いる。
また、表中の評価は、次のようになつている。
◎……残血を全く認めず
○……わずかに残血を認める
△……ガラス管に移行するほどの残血を認め
る
×……非常に多くの残血を認める
第３表から、ゴム栓にシロキサンＡを塗布した
場合、残血が全く生じないことが分かる。[Table] Regarding the antifoaming properties, the evaluations in Table 2 are as follows: ◎...Very good antifoaming properties ○...Good antifoaming properties △...Slightly poor antifoaming properties ×...Poor antifoaming properties Regarding blood repellency: ◎...Very little blood repellency ○...Low blood repellency ×...A lot of blood repellency Regarding residual blood: ◎...No residual blood observed ○...Slightly residual blood Blood is recognized ×...A large amount of residual blood is recognized. From Table 2, it is preferable that the ratio of siloxane units and ethylene oxide units to the total number of moles is 15 to 25 mol% and 35 to 45 mol%, respectively. It can be seen that siloxane A) is preferred. <Test Example 1> When various silicones were tested for residual blood using rubber plugs coated with a concentration that passed the plugging and fitting force specifications, the results shown in Table 3 were obtained. The test tubes used here do not contain chemicals (called plain tubes), and the solvent-type silicone used is Shin-Etsu Silicone KF-96 (dimethylpolysiloxane), and the emulsion-type silicone used is Shin-Etsu Silicone Polon MG. are doing. The evaluations in the table are as follows. ◎...No residual blood observed ○...Small residual blood observed △...Remained blood to the extent that it migrated to the glass tube ×...Extreme amount of residual blood observed From Table 3, rubber stopper It can be seen that when Siloxane A is applied to the surface, no residual blood is generated.
【表】
間
〈試験例 ２〉
各種シリコーンについて、試験例１と同様のゴ
ム栓および、抗凝固剤としてEDTA塩やNaFな
どを封入した試験管を用いて、真空採血後薬剤と
血液との混和を行い、消泡性の試験を行つたとこ
ろ、第４表のような結果が得られた。薬剤と血液
との混和は、管を上下に軽く10回振盪して行つ
た。
表中の評価は次のようになつている。
◎……立泡後10分以内に消泡した
×……まつたく消泡せず
表から、シリカ含有シリコーンを塗布したゴム
栓とシロキサンＡを塗布したゴム栓が消泡性を満
足することが分かる。[Table] <Test Example 2> For various silicones, mix the drug and blood after vacuum blood collection using the same rubber stopper as in Test Example 1 and a test tube sealed with EDTA salt, NaF, etc. as an anticoagulant. When an antifoaming test was carried out, the results shown in Table 4 were obtained. The drug and blood were mixed by gently shaking the tube up and down 10 times. The evaluation in the table is as follows. ◎...The foam disappeared within 10 minutes after foaming ×...The foam did not disappear immediately From the table, it can be seen that the rubber stopper coated with silica-containing silicone and the rubber stopper coated with siloxane A satisfy the defoaming property. I understand.
【表】
〈試験例 ３〉
各種シリコーンについて、試験例２と同様のゴ
ム栓およびEDTA塩封入試験管を用いて、採血
後血液をスライドガラス上に薄く塗抹して血液の
はじきの有無を試験したところ第５表のような結
果が得られた。
各試験項目における試料数はそれぞれ20個であ
り、数字は平均値である。
表からシロキサンＡを塗布したゴム栓の場合に
非常に血液のはじきが少ないことががわかる。[Table] <Test Example 3> For various silicones, using the same rubber stopper and EDTA salt-filled test tube as in Test Example 2, blood was collected and then smeared thinly on a slide glass to test whether or not the blood repelled. However, the results shown in Table 5 were obtained. The number of samples for each test item was 20, and the numbers are average values. It can be seen from the table that the rubber stopper coated with Siloxane A has very little blood repellency.
【表】
〈発明の効果〉
以上述べてきたことから明らかなように、本発
明の真空採血管は、ゴム栓に特殊なポリオキシア
ルキレン変性シリコーン化合物の皮膜が形成され
ているので、遠心分離後にゴム栓に血液が付着し
て残ることがなく、また消泡性が良く、さらに採
血管に収容された血液をスライドガラス上に塗抹
した際に血液がはじかれることが少ないという利
点を有する。[Table] <Effects of the Invention> As is clear from the above, the vacuum blood collection tube of the present invention has a film of a special polyoxyalkylene-modified silicone compound formed on the rubber stopper, so that after centrifugation, It has the advantage that blood does not adhere to and remain on the rubber stopper, has good defoaming properties, and is less likely to be repelled when the blood contained in the blood collection tube is smeared onto a slide glass.
第１図は本発明の一実施例に関わる真空採血管
の中央縦断面図である。
主な符号の説明、１：真空採血管、２：試験
管、３：ゴム栓、４：皮膜。
FIG. 1 is a central vertical sectional view of a vacuum blood collection tube according to an embodiment of the present invention. Explanation of main symbols: 1: Vacuum blood collection tube, 2: Test tube, 3: Rubber stopper, 4: Film.
Claims (1)
端に気密に挿着されたゴム栓とで構成され、かつ
管内腔が減圧されてなる採血管において、前記ゴ
ム栓の管内腔側表面に下記一般式（）で示され
るポリオキシアルキレン変性シリコーン化合物の
被膜が形成されたことを特徴とする真空採血管。 【化】 〔ただし、式中Ｇは一般式（）： −R′−Ｏ（―C2H4O）n――（―C3H6O）o――Ａ
……（） （ここでＲは炭素原子数１〜８の二価炭化水素
基、Ａは水素原子またはアセチル基、ｍ、ｎは20
≦ｍ＋ｎ≦70を満足する正の整数）で示されるポ
リオキシエチレン−ポリオキシプロピレンブロツ
ク共重合基；ａは２又は３、ｂは０又は１であ
り、かつａ＋ｂ＝３を満足する；Ｘ、Ｙは不等式
20≦Ｘ＋Ｙ≦70を満足する正の整数であり、かつ
全体のモル数に対するシロキサン単位およびエチ
レンオキサイド単位の割合がそれぞれ15〜30モル
％および30〜60モル％である。〕 ２ 全体のモル数に対するシロキサン単位および
エチレンオキサイド単位の割合がそれぞれ15〜25
モル％および35〜45モル％である特許請求の範囲
第１項に記載の真空採血管。[Scope of Claims] 1. A blood collection tube consisting of a bottomed cylindrical tube with one end open and a rubber stopper airtightly inserted into the open end of the tube, the inner lumen of which is evacuated, A vacuum blood collection tube characterized in that a coating of a polyoxyalkylene-modified silicone compound represented by the following general formula () is formed on the tube lumen side surface of the rubber stopper. [Formula G is the general formula (): -R'-O(-C 2 H 4 O) n --(-C 3 H 6 O) o --A
...() (Here, R is a divalent hydrocarbon group having 1 to 8 carbon atoms, A is a hydrogen atom or an acetyl group, m and n are 20
A polyoxyethylene-polyoxypropylene block copolymer group represented by a positive integer satisfying ≦m+n≦70; a is 2 or 3, b is 0 or 1, and satisfies a+b=3; Y is an inequality
It is a positive integer satisfying 20≦X+Y≦70, and the proportions of siloxane units and ethylene oxide units to the total number of moles are 15 to 30 mol% and 30 to 60 mol%, respectively. ] 2 The ratio of siloxane units and ethylene oxide units to the total number of moles is 15 to 25, respectively.
% and 35 to 45 mol %.