【発明の詳細な説明】Detailed Description of the Invention
【産業上の利用分野】[Industrial applications]
本発明は食器などの絵付き樹脂成形品の印刷用インキに
より形成される絵柄部の耐久性を向上させる技術に関す
る。TECHNICAL FIELD The present invention relates to a technique for improving the durability of a pattern portion formed by a printing ink of a resin molded product with a picture such as tableware.
【従来の技術】[Prior art]
従来より、絵付き樹脂成形品は、樹脂成形品に、オフセ
ット印刷紙にメラミン樹脂ワニスのような樹脂ワニスが
含浸されて形成された模様付き樹脂含浸紙が積層されて
製造されている。2. Description of the Related Art Conventionally, a resin molded product with a picture is manufactured by laminating a resin molded product with a patterned resin-impregnated paper formed by impregnating offset printing paper with a resin varnish such as a melamine resin varnish.
【発明が解決しようとする課題】[Problems to be Solved by the Invention]
この絵付き樹脂成形品は食器などに採用されており、従
って、煮沸・乾燥とか蒸気消毒処理がなされるが、繰り
返して行われることにより絵柄部（インキ部）が膨れが
生じてしまっていた。 本発明は上記課題を解決するためになされたものであ
り、その目的とするところは煮沸・乾燥とか蒸気消毒処
理を繰り返し行っても絵柄部（インキ部）に膨れが生じ
ない絵付き樹脂成形品を提供することにある。This resin molded product with a picture is used for tableware and the like, and therefore, it is boiled and dried, or steam sterilized, but the pattern part (ink part) swells due to repeated processes. The present invention has been made to solve the above problems, and its object is to provide a resin-molded product with a picture in which the pattern part (ink part) does not swell even after repeated boiling and drying or steam disinfection treatment. To provide.
【課題を解決するための手段】[Means for Solving the Problems]
本発明の絵付き樹脂成形品は、樹脂合成時のホルマリン
とメラミンのモル比が１．４〜１．７であるメラミン樹
脂ワニスが紙基材４に含浸されて模様付け樹脂含浸紙１
が形成され、この模様付け樹脂含浸紙１を印刷用インキ
層２側面にてメラミン樹脂成形品３に積層させて成るも
のであり、この構成により上記課題が解決されたもので
ある。 〔作用〕 印刷用インキ層２側がメラミン樹脂成形品３側に位置す
るので、絵付き樹脂成形品Ａの表面に絵柄部（インキ
部）が露出せずに、模様付け樹脂含浸紙１の絵基材４に
より保護されることにより、しかも、模様付け樹脂含浸
紙１の樹脂とメラミン樹脂成形品３とは同種の樹脂であ
ることから、模様付け樹脂含浸紙１とメラミン樹脂成形
品３とは強固に積層されることにより、煮沸・乾燥とか
蒸気消毒処理を繰り返し行っても絵柄部（インキ部）に
膨れが生じないものである。 以下本発明を添付の図面を参照して説明する。 模様付け樹脂含浸紙１の紙基材４としてはマシン仕上げ
紙、スーパー仕上げ紙、アート紙、ボンド紙、カルトン
紙、グラシン紙、セロファン紙等通常採用されている基
材が使用される。 この紙基材４に樹脂合成時のホルマリンとメラミンのモ
ル比が１．４〜１．７であるメラミン樹脂ワニスが含
浸、乾燥され、印刷用インキが印刷され、印刷用インキ
層２が形成されて模様付け樹脂含浸紙１が製造される。
この場合、上記メラミン樹脂ワニスのメラミン樹脂は含
有水分率が高く、水性の印刷用インキと組み合わせて好
適に使用できるものである。印刷用インキは紙基材４と
の関係でその組成が決められる。例えば、ボンド紙であ
れば、ビヒクルは粘度が高く、強い皮膜をつくるアマニ
油ワニス、樹脂ワニス、アルキドワニスが使用される。 模様付け樹脂含浸紙１は印刷用インキ層２側面にてメラ
ミン樹脂成形品３に加熱加圧等により積層されて絵付き
樹脂成形品Ａが形成される。 例えば、樹脂合成時のホルマリンとメラミンのモル比が
１．５であるメラミン樹脂ワニスを使用して模様付け樹
脂含浸紙１を形成し、メラミン樹脂成形品３に積層して
絵付き樹脂成形品を製造し、このものに耐連続煮沸試験
を行ったところ１００時間以上の耐久性を示した。一
方、従来のものにあっては１０〜２０時間で絵柄部（イ
ンキ部）に著しい膨れが現出した。In the resin molded product with a picture of the present invention, the paper base material 4 is impregnated with a melamine resin varnish having a molar ratio of formalin and melamine at the time of resin synthesis of 1.4 to 1.7.
Is formed, and the patterning resin-impregnated paper 1 is laminated on the melamine resin molded product 3 on the side surface of the printing ink layer 2 and the above problem is solved by this configuration. [Function] Since the printing ink layer 2 side is located on the melamine resin molded product 3 side, the pattern portion (ink portion) is not exposed on the surface of the painted resin molded product A, and the picture base of the patterned resin-impregnated paper 1 is not exposed. Since the resin of the patterning resin-impregnated paper 1 and the melamine resin molded product 3 are the same kind of resin by being protected by the material 4, the patterning resin-impregnated paper 1 and the melamine resin molded product 3 are strong. By being laminated on, the pattern portion (ink portion) does not swell even after repeated boiling and drying or steam disinfection treatment. Hereinafter, the present invention will be described with reference to the accompanying drawings. As the paper base material 4 of the patterned resin-impregnated paper 1, usually used base materials such as machine finish paper, super finish paper, art paper, bond paper, carton paper, glassine paper and cellophane paper are used. The paper base material 4 is impregnated with a melamine resin varnish having a formalin / melamine molar ratio of 1.4 to 1.7 during resin synthesis, dried, and printed with a printing ink to form a printing ink layer 2. Thus, the patterned resin-impregnated paper 1 is manufactured.
In this case, the melamine resin of the melamine resin varnish has a high water content and can be suitably used in combination with an aqueous printing ink. The composition of the printing ink is determined in relation to the paper base material 4. For example, in the case of bond paper, the vehicle is linseed oil varnish, resin varnish, or alkyd varnish that has a high viscosity and forms a strong film. The patterned resin-impregnated paper 1 is laminated on the melamine resin molded product 3 on the side surface of the printing ink layer 2 by heating and pressing to form a resin molded product A with a picture. For example, a patterned resin-impregnated paper 1 is formed by using a melamine resin varnish having a formalin / melamine molar ratio of 1.5 at the time of resin synthesis, and the patterned resin-impregnated paper 1 is laminated on a melamine resin molded product 3 to obtain a resin molded product with a picture. When manufactured and subjected to a continuous boiling resistance test, this product showed a durability of 100 hours or more. On the other hand, in the case of the conventional one, remarkable swelling appeared in the pattern part (ink part) in 10 to 20 hours.
【発明の効果】【The invention's effect】
本発明にあっては、樹脂合成時のホルマリンとメラミン
のモル比が１．４〜１．７であるメラミン樹脂ワニスが
紙基材に含浸されて模様付け樹脂含浸紙が形成され、こ
の模様付け樹脂含浸紙を印刷用インキ層側面にてメラミ
ン樹脂成形品に積層させているので、メラミン樹脂ワニ
スのメラミン樹脂は含有水分率が高くなり、水性の印刷
用インキと組み合わせて好適に使用できるものであり、
又、印刷用インキ層側がメラミン樹脂成形品側に位置す
るので、絵付き樹脂成形品の表面に絵柄部（インキ部）
が露出せずに、模様付け樹脂含浸紙の絵基材により保護
されることになり、しかも、模様付け樹脂含浸紙の樹脂
とメラミン樹脂成形品とは同種の樹脂であることから、
模様付け樹脂含浸紙とメラミン樹脂成形品とは強固に積
層されることになり、煮沸・乾燥とか蒸気消毒処理を繰
り返し行っても絵柄部（インキ部）に膨れが生じないも
のである。In the present invention, a melamine resin varnish having a formalin / melamine molar ratio of 1.4 to 1.7 during resin synthesis is impregnated into a paper base material to form a patterned resin-impregnated paper. Since the resin-impregnated paper is laminated on the melamine resin molded product on the side of the printing ink layer, the melamine resin of the melamine resin varnish has a high water content, and can be suitably used in combination with an aqueous printing ink. Yes,
Also, since the printing ink layer side is located on the melamine resin molded product side, the pattern part (ink part) is on the surface of the painted resin molded product.
Will not be exposed and will be protected by the picture base material of the patterned resin-impregnated paper, and since the resin of the patterned resin-impregnated paper and the melamine resin molded article are the same type of resin,
The patterned resin-impregnated paper and the melamine resin molded product are firmly laminated, and the pattern portion (ink portion) does not swell even after repeated boiling and drying or steam disinfection treatment.
【図面の簡単な説明】[Brief description of drawings]
第１図は本発明の一実施例を示す断面図であって、Ａは
絵付き樹脂成形品、１は模様付け樹脂含浸紙、２は印刷
用インキ層、３はメラミン樹脂成形品、４は紙基材であ
る。FIG. 1 is a cross-sectional view showing an embodiment of the present invention, in which A is a resin molded product with a picture, 1 is a resin impregnated with a patterning resin, 2 is an ink layer for printing, 3 is a melamine resin molded product, and 4 is It is a paper substrate.