JPH0641396B2 - Manufacturing method of potassium silicate liquid fertilizer - Google Patents
Manufacturing method of potassium silicate liquid fertilizerInfo
- Publication number
- JPH0641396B2 JPH0641396B2 JP62074222A JP7422287A JPH0641396B2 JP H0641396 B2 JPH0641396 B2 JP H0641396B2 JP 62074222 A JP62074222 A JP 62074222A JP 7422287 A JP7422287 A JP 7422287A JP H0641396 B2 JPH0641396 B2 JP H0641396B2
- Authority
- JP
- Japan
- Prior art keywords
- potassium silicate
- acid
- liquid fertilizer
- potassium
- aqueous solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、カリおよびケイ酸を含む液体肥料に関し、詳
しくは中性に近いpHでありながら沈澱を生じないカリお
よびケイ酸を含む液体肥料に関し、さらに詳しくは、水
で希釈して、ほとんど中性のpHにしても沈澱を生じるこ
とのない速効性のカリおよびケイ酸を含む液体肥料に関
する。TECHNICAL FIELD The present invention relates to a liquid fertilizer containing potassium and silicic acid, and more specifically, a liquid fertilizer containing potassium and silicic acid which has a pH close to neutral but does not cause precipitation. More particularly, the present invention relates to a liquid fertilizer containing potassium and silicic acid which is fast-acting and does not cause precipitation even when diluted with water to an almost neutral pH.
カリウム（加里）は、窒素およびリン酸と共に、植物の
生育に必要な元素であることが古くから知られた元素で
あり、ケイ酸が植物の生育において必要な元素であっ
て、病害に対する抵抗力の増大に著るしい効果があるこ
とも古くから知られている。Potassium (potassium) is an element that has long been known to be a necessary element for plant growth, along with nitrogen and phosphoric acid, and silicic acid is a necessary element for plant growth and is resistant to disease. It has long been known that there is a remarkable effect on the increase of the.
硫酸アンモニウムは窒素肥料として古くから知られてい
るが、水田における稲作に、硫酸アンモニウムを連用す
ると、稲の植物体の生育に影響がなくてもその結実に支
障を生じる秋落ち現象が多発する。これは、土壌に施用
された硫酸アンモニウムからアンモニアが植物に吸収利
用されると、硫酸根が土壌に残り、土壌を酸性化する
が、冠水状態にある水田土壌の強い還元力によって硫酸
塩（ＳＯ４ −−）が硫化物（Ｓ−−）に還元され、その
硫化物が酸性化した伝壌の強い酸性によって、土壌中に
硫化水素（Ｈ２Ｓ）を生じ、この硫化水素によって稲の
根が損傷を受け、そのために結実期にある稲の生育を阻
害することにあるといわれている。Ammonium sulphate has long been known as a nitrogen fertilizer, but if ammonium sulphate is continuously used for rice cultivation in paddy fields, there will be many autumn fall phenomena that will hinder the fruiting of rice even if it does not affect the growth of the plant. This is because when ammonium is absorbed and utilized by plants from ammonium sulfate applied to the soil, sulfate radicals remain in the soil and acidify the soil, but the strong reducing power of the flooded paddy soil reduces the sulfate (SO 4 -) sulfide (S - is reduced to) the by a strong acidic sulfides of Den壌acidified, produce hydrogen sulfide (H 2 S) in the soil, the roots of rice by the hydrogen sulfide It is said that it is damaged, and as a result, it inhibits the growth of rice in the fruiting stage.
一方において、稲の植物体は多量のケイ酸を含んでいて
ケイ酸は稲の生育に必要不可欠の元素であるが、秋落ち
現象を生じる稲は、前記の稲の根の損傷からの回復がで
きず、そのために稲は土壌中のケイ酸を吸収利用するこ
とができず、それによって秋落ち現象を生じるといわれ
ている。On the other hand, rice plants contain a large amount of silicic acid, and silicic acid is an essential element for the growth of rice. It is said that rice cannot absorb and utilize silicic acid in the soil, which causes the fall of autumn.
またリン酸液にアンモニアを加えて、速効性の液体肥料
がつくられているが、この種の液体肥料は酸性のもので
ある。Ammonia is added to the phosphoric acid solution to make a liquid fertilizer with a fast-acting effect, but this type of liquid fertilizer is acidic.
ケイ酸（ＳｉＯ２）およびマグネシウム（ＭｇＯ）を多
量に含む蛇紋岩を焼成して、ク溶性（クエン酸可溶性）
のケイ酸マグネシウム肥料を製造する方法が提案されて
いる。（特公昭３２−９３６７号公報、特公昭３８−１
９２号公報、特公昭３８−２２３７３号公報） ケイ酸は、ケイ酸ナトリウム（水ガラス）またはケイ酸
カリウムのような強アルカリ塩の形でなければ、水溶性
とはならないが、ケイ酸カリウム、尿素およびリン酸カ
リウム塩からなる水溶性ケイ酸を含む液体肥料が提案さ
れている。（特開昭６０−２３１４８３号公報） しかしながら、ケイ酸ナトリウム（水ガラス）およびケ
イ酸カリウムは、強アルカリ性（pH：１０以上）にしな
ければ沈澱を生じて液体肥料にはならないが、強アルカ
リ性のケイ酸ナトリウムおよびケイ酸カリウムは、その
強過ぎるアルカリ性のために、そのまま液体肥料とする
ことには、その使用上の難点がある。The serpentinite containing a large amount of silicic acid (SiO 2 ) and magnesium (MgO) is fired to dissolve in soluble (citric acid soluble)
A method for producing the magnesium silicate fertilizer has been proposed. (Japanese Patent Publication No. 32-9367, Japanese Patent Publication No. 38-1)
No. 92, Japanese Examined Patent Publication No. 38-22373) Silicic acid is not water-soluble unless it is in the form of a strong alkali salt such as sodium silicate (water glass) or potassium silicate, but potassium silicate, A liquid fertilizer containing water-soluble silicic acid composed of urea and potassium phosphate has been proposed. (Unexamined-Japanese-Patent No. 60-231483) However, although sodium silicate (water glass) and potassium silicate do not become a liquid fertilizer, although precipitation will occur unless they are made strongly alkaline (pH: 10 or more), they are strongly alkaline. Sodium silicate and potassium silicate have difficulty in use as a liquid fertilizer as they are because of their too strong alkalinity.
本発明者は、ケイ酸カリウムにクエン酸を加えることに
よって１０よりも低いpHにおいても液状を保持する液体
肥料を提案した。（特願昭６０−１９４６８４号（特開
昭６２−５６３８９）） 本発明者はさらに研究を続け、強アルカリ性のケイ酸カ
リウムおよびケイ酸ナトリウムに、酒石酸、マレイン酸
などの有機酸を加えても、クエン酸と同様に１０よりも
低いpHにおいて液状を保持し、ケイ酸の肥料効果を高く
することができることを見出し、さらに、エチレンジア
ミン四酢酸を加えると、液状を安定的に保持することが
できることを見出し、これらの知見にもとづいて本発明
に到達した。The present inventor has proposed a liquid fertilizer which maintains a liquid state even at a pH lower than 10 by adding citric acid to potassium silicate. (Japanese Patent Application No. 60-194684 (Japanese Patent Application Laid-Open No. 62-56389)) The present inventor has conducted further research, and even if organic acids such as tartaric acid and maleic acid are added to strongly alkaline potassium silicate and sodium silicate. It was found that, like citric acid, the liquid state can be maintained at a pH lower than 10 and the fertilizer effect of silicic acid can be enhanced. Furthermore, by adding ethylenediaminetetraacetic acid, the liquid state can be stably maintained. The present invention has been achieved based on these findings.
本発明の目的は、ケイ酸カリウムを含み、pHの低い液体
肥料を提供することにあり、詳しくは水溶性のケイ酸を
含み、pHが低く、肥効の高いケイ酸カリウム液体肥料を
提供することにあり、さらに詳しくは、pHが低く長期間
の保存においても沈澱物を生じることのない安定なケイ
酸カリウム液体肥料を提供することにある。An object of the present invention is to provide a liquid fertilizer containing potassium silicate and having a low pH, and more specifically, to a liquid fertilizer containing potassium silicate having a low pH and a high fertilizing effect, which contains water-soluble silicic acid. More specifically, it is to provide a stable potassium silicate liquid fertilizer which has a low pH and does not cause a precipitate even during long-term storage.
本発明は、ケイ酸カリウム水溶液に、酒石酸、マレイン
酸およびこれらの混合物からなる群より選択された有機
酸を加えて、pHを低下することを特徴とするケイ酸カリ
ウム液体肥料の製造法である。The present invention is a method for producing a potassium silicate liquid fertilizer, which comprises adding an organic acid selected from the group consisting of tartaric acid, maleic acid and a mixture thereof to an aqueous potassium silicate solution to lower the pH. .
本発明の液体肥料の製造において、ケイ酸カリウム水溶
液に対する前記の有機酸の添加を、エチレンジアミン四
酢酸の存在の下に行ない、それによって液状を安定に保
持することができ、またエチレンジアミン四酢酸は、エ
チレンジアミン四酢酸マンガン、エチレンジアミン四酢
酸鉄またはエチレンジアミン四酢酸亜鉛などのようなエ
チレンジアミン四酢酸の微量要素塩を使用し、それによ
って微量要素を液体肥料に入れることができる。In the production of the liquid fertilizer of the present invention, the addition of the organic acid to the aqueous potassium silicate solution can be carried out in the presence of ethylenediaminetetraacetic acid, whereby the liquid state can be stably maintained, and ethylenediaminetetraacetic acid is Trace element salts of ethylenediaminetetraacetic acid, such as manganese ethylenediaminetetraacetate, iron ethylenediaminetetraacetate or zinc ethylenediaminetetraacetate, etc., can be used, whereby the trace elements can be included in the liquid fertilizer.
本発明のケイ酸カリウム液体肥料は、ケイ酸カリウムの
水溶液に、酒石酸、またはマレイン酸などの有機酸の水
溶液を加え、混合して、pHを低下することによってつく
られるが、これらの有機酸水溶液とともに、エチレンジ
アミン四酢酸（ＥＤＴＡ）またはその微量要素塩、たと
えば鉄、亜鉛、コバルトまたはマンガン塩を加えること
もできる。エチレンジアミン四酢酸（ＥＤＴＡ）はキレ
ート化剤であって、水に溶けない塩を形成するイオン錯
塩を形成して、水中に溶存する性能を有し、微量要素の
金属イオンまたはケイ酸カリウムのケイ酸イオンを水中
に安定に溶存するのに効果があると考えられる。The potassium silicate liquid fertilizer of the present invention is prepared by adding an aqueous solution of an organic acid such as tartaric acid or maleic acid to an aqueous solution of potassium silicate and mixing them to lower the pH. In addition, ethylenediaminetetraacetic acid (EDTA) or its trace element salts such as iron, zinc, cobalt or manganese salts can be added. Ethylenediaminetetraacetic acid (EDTA) is a chelating agent and has the ability to dissolve in water by forming an ionic complex salt that forms a salt that is insoluble in water, and is a trace element metal ion or potassium silicate. It is considered to be effective in stably dissolving ions in water.
ケイ酸カリウムは、Ｋ２ＯおよびＳｉＯ２により構成さ
れる塩の水またはアルカリ溶液に溶解するものであれ
ば、どのようなものであっても、これを使用することが
できるが、化学工業の副産物のケイ酸カリウムまたは水
ガラスを水酸化カリウムまたは炭酸カリウム水溶液によ
り溶解したものを使用するのが経済的に好ましい。Any potassium silicate can be used as long as it can be dissolved in water or an alkaline solution of a salt composed of K 2 O and SiO 2 , but it can be used in the chemical industry. It is economically preferable to use the by-product potassium silicate or water glass dissolved in an aqueous solution of potassium hydroxide or potassium carbonate.
ケイ酸カリウム水溶液に対する酒石酸、またはマレイン
酸などの有機酸の水溶液の添加は、ケイ酸カリウム水溶
液を充分に攪拌しながら徐々に行ない、それによって混
合中の局部的なpHの急低下を避ける条件の下に行なうべ
きである。この混合操作における局部的なpHの急上昇
は、局部的なこう状ケイ酸の析出を誘発し、このこう状
ケイ酸の局部的な析出を避ける必要があるからである。Addition of an aqueous solution of an organic acid such as tartaric acid or maleic acid to an aqueous solution of potassium silicate is carried out gradually while sufficiently stirring the aqueous solution of potassium silicate, thereby avoiding a local sharp drop in pH during mixing. Should be done below. This is because the local pH surge in the mixing operation induces the local precipitation of the silicic acid, and it is necessary to avoid the local precipitation of the silicic acid.
酒石酸は、カルボキシル基（−ＣＯＯＨ）の他に水酸基
（−ＯＨ）を有しており、またマレイン酸は二塩基酸で
あって、２個のカルボキシル基を有するから、これらの
官能基の特性によって、pHの低下によるケイ酸の析出、
すなわち巨大分子化を阻止すると考えられる。恐らく、
錯塩または複塩を形成すると想像される。これらの有機
酸の添加によるケイ酸カリウム水溶液のpHの低下の限度
は、有機酸の種類によって異なる。酒石酸ではpH：９．
５程度まで低下することができ、さらにマレイン酸では
pH：１０．５程度まで低下することができる。Tartaric acid has a hydroxyl group (-OH) in addition to the carboxyl group (-COOH), and maleic acid is a dibasic acid and has two carboxyl groups, and therefore, depending on the characteristics of these functional groups. , Precipitation of silicic acid due to decrease in pH,
That is, it is considered to prevent the formation of macromolecules. perhaps,
Envisioned to form a complex or double salt. The limit of the decrease in pH of the aqueous potassium silicate solution due to the addition of these organic acids depends on the type of organic acid. PH of tartaric acid: 9.
It can be reduced to about 5, and with maleic acid
The pH can be lowered to about 10.5.
ケイ酸カリウム水溶液に対する酒石酸、またはマレイン
酸の水溶液の添加とともに、エチレンジアミン四酢酸水
溶液またはその微量要素塩の水溶液を添加すると、これ
らの有機酸の水溶液の添加によるケイ酸カリウム水溶液
のpHの低下の限度をさらに低下することができる。これ
はエチレンジアミン四酢酸（ＥＤＴＡ）の添加によって
ケイ酸（ＳｉＯ２）のpHの低下による巨大分子化（析
出）が妨げられることによると考えられる。Addition of an aqueous solution of ethylenediaminetetraacetic acid or its trace element salt together with the addition of an aqueous solution of tartaric acid or maleic acid to an aqueous solution of potassium silicate limits the decrease in pH of the aqueous solution of potassium silicate due to the addition of the aqueous solution of these organic acids. Can be further reduced. It is considered that this is because the addition of ethylenediaminetetraacetic acid (EDTA) hinders macromolecularization (precipitation) of silicic acid (SiO 2 ) due to a decrease in pH.
ケイ酸カリウム水溶液に対する酒石酸、またはマレイン
酸水溶液の添加以前に、水ガラス、炭酸ケイ酸またはケ
イ酸カリウム水溶液に、水酸化カリウムまたは炭酸カリ
ウム水溶液を加えることができる。この水酸化カリウム
または炭酸カリウム水溶液の添加によりケイ酸カリウム
における（ケイ酸）／（酸化カリウム）の比率が低下す
るが、これによってケイ酸カリウムの巨大分子における
ケイ酸の骨格構造が細分化されるものと考えられる。Prior to the addition of the tartaric acid or maleic acid aqueous solution to the potassium silicate aqueous solution, the potassium hydroxide or potassium carbonate aqueous solution can be added to the water glass, the carbonate silicic acid or the potassium silicate aqueous solution. The addition of this potassium hydroxide or potassium carbonate aqueous solution reduces the ratio of (silicic acid) / (potassium oxide) in potassium silicate, which causes the skeletal structure of silicic acid in the macromolecule of potassium silicate to be subdivided. It is considered to be a thing.
本発明のケイ酸カリウム液体肥料は、水田作の場合、１
０アール当り８〜１６kg（好ましくは１２kg前後）の量
において、施用するのが効果的である。水田作の場合
は、本発明のケイ酸カリウム液体肥料の施用により、そ
の収量が増加し、老朽化水田（秋落水田）における生産
力の回復が著るしい。The potassium silicate liquid fertilizer of the present invention is 1 in the case of paddy field production.
It is effective to apply in an amount of 8 to 16 kg (preferably around 12 kg) per 0 are. In the case of paddy field cultivation, the application of the potassium silicate liquid fertilizer of the present invention increases the yield thereof, and the recovery of productivity in aged paddy fields (Akakuchi paddy field) is remarkable.
以下において、実施例および試験例により本発明をさら
に詳しく説明するが、本発明はこれらの実施例に限定さ
れるものではなく、本明細書の技術の開示によるべきで
ある。Hereinafter, the present invention will be described in more detail with reference to Examples and Test Examples, but the present invention is not limited to these Examples and should be based on the disclosure of the technology of the present specification.
実施例１ ケイ酸カリウム水溶液（Ｋ２Ｏ：１２．５％、Ｓｉ
Ｏ２：２５．０％、pH１１．０）５７ｇに１０％炭酸カ
リウム水溶液１０ｇを加え、これに１０％酒石酸水溶液
１０ｇ、１０％エチレンジアミン四酢酸（ＥＤＴＡ）水
溶液１７ｇを、攪拌しながら徐々に加え、さらに水８ｇ
を加え、よく攪拌した後、濾過してケイ酸カリウム液体
肥料（pH９．０）１００ｇを得た。Example 1 Potassium silicate aqueous solution (K 2 O: 12.5%, Si
O 2 : 25.0%, pH 11.0) 57 g, 10% potassium carbonate aqueous solution 10 g was added, 10% tartaric acid aqueous solution 10 g, 10% ethylenediaminetetraacetic acid (EDTA) aqueous solution 17 g was gradually added with stirring, 8g of water
Was added and well stirred, and then filtered to obtain 100 g of potassium silicate liquid fertilizer (pH 9.0).
ケイ酸カリウム液体肥料は、Ｋ２Ｏ：７．８％、ＳｉＯ
２：１４．３％の分析値のものであった。これに水を加
えて５倍に希釈しても、沈澱を生じることはなく、また
３週間フラスコに保存しても、沈澱を生じなかった。Potassium silicate liquid fertilizer is K 2 O: 7.8%, SiO
2 : with an analytical value of 14.3%. No precipitation occurred even when water was added to the mixture to dilute it 5 times, and no precipitation occurred even when stored in a flask for 3 weeks.
実施例２ ケイ酸カリウム水溶液（工業用、Ｋ２Ｏ：１３．５％、
ＳｉＯ２：２６％、pH１１．０）５７ｇに１０％炭酸カ
リウム水溶液１０ｇを加え、これに１０％酒石酸水溶液
１０ｇおよび水２３ｇを徐々に加え、さらによく攪拌し
た後、濾過してケイ酸カリウム液体肥料（pH８．５）１
００ｇを得た。Example 2 Potassium silicate aqueous solution (for industrial use, K 2 O: 13.5%,
SiO 2 : 26%, pH 11.0) 10 g potassium carbonate aqueous solution 10 g was added to 57 g, 10% tartaric acid aqueous solution 10 g and water 23 g were gradually added, and after further stirring well, it was filtered and potassium silicate liquid fertilizer was added. (PH 8.5) 1
00g was obtained.
ケイ酸カリウム液体肥料はＫ２Ｏ：８．２％、Ｓｉ
Ｏ２：１４．２％の分析値のものであった。これに水を
加えて、３倍に希釈しても、沈澱を生じることはなく、
また３週間フラスコに保存しても、沈澱を生じなかっ
た。Potassium silicate liquid fertilizer is K 2 O: 8.2%, Si
O 2: was of 14.2% of the analyzed values. Even if water is added to this and diluted three-fold, no precipitation occurs,
Further, even when stored in the flask for 3 weeks, no precipitation occurred.
実施例３ ケイ酸カリウム水溶液（Ｋ２Ｏ：１２．５％、Ｓｉ
Ｏ２：２５．０％、pH１１．０）５７ｇに、１０％炭酸
カリウム水溶液１０ｇを加え、これに１０％グリコール
酸水溶液１０ｇ、１０％エチレンジアミン四酢酸（ＥＤ
ＴＡ）水溶液１０ｇおよび１０％エチレンジアミン四酢
酸鉄（ＥＤＴＡ−Ｆｅ）水溶液７ｇを攪拌しながら徐々
に加え、さらに水８ｇを加え、よく攪拌した後、濾過し
てケイ酸カリウム液体肥料（pH８．０）１００ｇを得
た。Example 3 Potassium silicate aqueous solution (K 2 O: 12.5%, Si
O 2: 25.0%, pH11.0) in 57 g, 10% aqueous potassium carbonate 10g added thereto 10% aqueous glycolic acid solution 10g, 10% ethylenediaminetetraacetic acid (ED
TA) aqueous solution 10 g and 10% ethylenediaminetetraacetic acid iron acetate (EDTA-Fe) aqueous solution 7 g were gradually added with stirring, water 8 g was further added, and after stirring well, they were filtered and potassium silicate liquid fertilizer (pH 8.0) was added. 100 g was obtained.
ケイ酸カリウム液体肥料は、Ｋ２Ｏ：７．７％、ＳｉＯ
２：１４．３％の分析値のものであった。これに水を加
えて５倍に希釈しても、沈澱を生じることはなく、また
３週間フラスコに保存しても、沈澱を生じなかった。Potassium silicate liquid fertilizer is K 2 O: 7.7%, SiO
2 : with an analytical value of 14.3%. No precipitation occurred even when water was added to the mixture to dilute it 5 times, and no precipitation occurred even when stored in a flask for 3 weeks.
実施例４ ケイ酸カリウム水溶液（工業用、Ｋ２Ｏ：１３．５％、
ＳｉＯ２：２６％、pH１１）５７ｇに、１０％炭酸カリ
ウム水溶液１０ｇを加え、これに１０％マレイン酸水溶
液１０ｇ、１０％エチレンジアミン四酢酸（ＥＤＴＡ）
水溶液１０ｇおよび１０％エチレンジアミン四酢酸マン
ガン（ＥＤＴＡ−Ｍｎ）水溶液７ｇを攪拌しながら徐々
に加え、さらに水８ｇを加え、よく攪拌した後、濾過し
てケイ酸カリウム液体肥料（pH８．５）１００ｇを得
た。Example 4 Potassium silicate aqueous solution (for industrial use, K 2 O: 13.5%,
SiO 2 : 26%, pH 11) 57 g, 10% potassium carbonate aqueous solution 10 g was added, and 10% maleic acid aqueous solution 10 g, 10% ethylenediaminetetraacetic acid (EDTA)
10 g of the aqueous solution and 7 g of a 10% aqueous solution of manganese ethylenediamine tetraacetate (EDTA-Mn) were gradually added with stirring, 8 g of water was further added, and after stirring well, 100 g of potassium silicate liquid fertilizer (pH 8.5) was added by filtration. Obtained.
ケイ酸カリウム液体肥料は、Ｋ２Ｏ：８．２％、ＳｉＯ
２：１４．３％の分析値のものであった。これに水を加
えて５倍に希釈しても、沈澱を生じることはなく、また
３週間ビーカーに保存しても、沈澱を生じなかった。Potassium silicate liquid fertilizer is K 2 O: 8.2%, SiO
2 : with an analytical value of 14.3%. No precipitation occurred even when water was added to the mixture to dilute it 5 times, and no precipitation occurred even when stored in a beaker for 3 weeks.
試験例 （１）供試試料 （１−１）実施例１の試料 実施例１のケイ酸カリウム液体肥料に、水を加えて２
８．６倍に希釈し、１０mlのＷ−ＳｉＯ２および２５mg
のＷ−Ｋ２Ｏを含む実施例１の試料を調製した。Test Example (1) Sample to be Tested (1-1) Sample of Example 1 Water was added to the potassium silicate liquid fertilizer of Example 1 to give 2
Diluted to 8.6 times, 10ml of W-SiO 2 and 25mg
A sample of Example 1 was prepared which contained 2 % of W-K2O.
（１−２）対照試料（ケイ酸石灰＋硫酸加里） ケイ酸石灰肥料：ＳｉＯ２：３３．９％ 硫酸カリウム：Ｗ−Ｋ２Ｏ：５４．１％ （２）試験方法 ノイバウエルポットに、石英砂４００ｇおよび風乾細土
１００ｇを取り、これに第１表に示す量の供試試料を混
合した後、５０mgのＮおよび５０mgのＰ２Ｏ５の施用量
に相当する量のリン酸一アンモニウムおよび硫酸アンモ
ニウムを加え、よく混合した。(1-2) Control sample (lime silicate + potassium sulfate) Lime silicate fertilizer: SiO 2 : 33.9% Potassium sulfate: W-K 2 O: 54.1% (2) Test method In a Neubauer pot, After taking 400 g of quartz sand and 100 g of air-dried fine soil, and mixing the test samples in the amounts shown in Table 1, the amount of monoammonium phosphate corresponding to the application amount of 50 mg of N and 50 mg of P 2 O 5 was mixed. And ammonium sulfate were added and mixed well.
それぞれのポットに、予め催芽処理をした水稲種子（コ
シヒカリ）１００粒を播種し、灌水して、２５日間生育
させた後、地上部を刈り取り、生体重量、乾物重量、ケ
イ酸含量および加里含量を測定した。 In each pot, 100 seed rice seeds (Koshihikari) that had been pre-germinated were sown, irrigated, and grown for 25 days. It was measured.
これらの試験は２連の並行で行なった。These tests were done in parallel in duplicate.
（３）試験結果 試験結果は第２表に示すとおりであった。(3) Test results The test results are shown in Table 2.
第２表の数値は２連の試験区における平均値である。The numerical values in Table 2 are average values in two test plots.
（４）考察 本発明のケイ酸カリウム液体肥料は、これまでのケイ酸
石灰と硫酸加里の施用に比べて、ケイ酸およびカリウム
の双方共に吸収量および吸収利用率が向上している。 (4) Consideration The potassium silicate liquid fertilizer of the present invention has improved absorption amount and absorption utilization rate of both silicic acid and potassium as compared with the conventional application of lime silicate and potassium sulfate.
植物による吸収利用率の高い肥料が得られる。 A fertilizer with a high absorption utilization rate by plants can be obtained.
長期間の保存において沈澱物を生じない安定な液体肥料
が得られる。A stable liquid fertilizer can be obtained which does not cause precipitation upon long-term storage.
植物によるケイ酸の吸収率が高く、それによって老朽化
水田（秋落ち水田）における根腐れまたは秋落ち現象を
生じない。The absorption rate of silicic acid by plants is high, so that root rot or fallout phenomenon does not occur in aged paddy field (autumn paddy field).
Claims (3)
ン酸およびこれらの混合物からなる群より選択された有
機酸を加えて、pHを低下することを特徴とするケイ酸カ
リウム液体肥料の製造法。1. A method for producing a potassium silicate liquid fertilizer, which comprises adding an organic acid selected from the group consisting of tartaric acid, maleic acid and mixtures thereof to an aqueous potassium silicate solution to lower the pH.
の下に、ケイ酸カリウム水溶液に加えられることを特徴
とする特許請求の範囲第１項に記載のケイ酸カリウム液
体肥料の製造法。2. The process for producing a potassium silicate liquid fertilizer according to claim 1, wherein the organic acid is added to the potassium silicate aqueous solution in the presence of ethylenediaminetetraacetic acid.
ミン四酢酸の微量要素塩であることを特徴とする特許請
求の範囲第２項に記載のケイ酸カリウム液体肥料の製造
法。3. The method for producing a potassium silicate liquid fertilizer according to claim 2, wherein the ethylenediaminetetraacetic acid is a trace element salt of ethylenediaminetetraacetic acid.