JPH0641993B2 - Microwave melting and solidification method for liquid waste - Google Patents
Microwave melting and solidification method for liquid wasteInfo
- Publication number
- JPH0641993B2 JPH0641993B2 JP14646286A JP14646286A JPH0641993B2 JP H0641993 B2 JPH0641993 B2 JP H0641993B2 JP 14646286 A JP14646286 A JP 14646286A JP 14646286 A JP14646286 A JP 14646286A JP H0641993 B2 JPH0641993 B2 JP H0641993B2
- Authority
- JP
- Japan
- Prior art keywords
- liquid waste
- microwave
- solidifying
- melting
- liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 〔産業上の利用分野〕 本発明は、液体廃棄物のマイクロ波溶融固化方法に関す
る。TECHNICAL FIELD The present invention relates to a microwave melting and solidifying method for liquid waste.
近時、例えば、特開昭５５−１２１８９７号公報に開示
されるように、マイクロ波を用いて廃棄物を処理するこ
とが行なわれている。Recently, for example, as disclosed in Japanese Patent Application Laid-Open No. 55-121897, a microwave is used to treat waste.
従来、例えば、ナトリウム塩を含有する放射性液体廃棄
物（例えば、洗濯廃液）を処理するため、マイクロ波溶
融炉のレトルト内に、液体廃棄物を供給し、このレトル
ト内で液体廃棄物の水分等を蒸発し、液体廃棄物を乾燥
処理することが行なわれている。Conventionally, for example, in order to treat radioactive liquid waste containing sodium salt (for example, laundry waste liquid), liquid waste is supplied into the retort of a microwave melting furnace, and the water content of the liquid waste, etc. is fed into the retort. Are evaporated and the liquid waste is dried.
しかしながら、上述したような方法で液体廃棄物を乾燥
処理する場合には、レトルト内に液体廃棄物を供給した
時に、液体廃棄物の蒸発過程においてミスト化したナト
リウム塩が、熱エネルギーおよびマイクロ波エネルギに
より原子化し、レトルト内に導電性雰囲気が形成され、
アークが発生し、液体廃棄物へのエネルギの伝達が行な
われなくなるという問題がある。However, when the liquid waste is dried by the method as described above, when the liquid waste is supplied into the retort, the sodium salt mist formed in the evaporation process of the liquid waste has thermal energy and microwave energy. Atomizes, forming a conductive atmosphere in the retort,
There is a problem that an arc is generated and energy is not transferred to the liquid waste.
そこで、従来、このようなアークが発生した時には、マ
イクロ波の供給を制限あるいは停止することが行なわれ
ているが、この場合には、全運転時間に占めるマイクロ
波の供給可能時間が少なくなり、処理能力が低下すると
いう問題がある。Therefore, conventionally, when such an arc occurs, the supply of microwaves is limited or stopped, but in this case, the available supply time of the microwaves in the entire operating time is reduced, There is a problem that the processing capacity decreases.
本発明は、上記のような問題を解決したもので、従来よ
り大幅に処理能力を向上することができる液体廃棄物の
マイクロ波溶融固化方法を提供することを目的とする。The present invention solves the above problems, and an object of the present invention is to provide a microwave melting and solidifying method for liquid waste, which can significantly improve the processing capacity as compared with the prior art.
本発明にかかわる液体廃棄物のマイクロ波溶融固化方法
は、レトルト内に収容される固化物質をマイクロ波の照
射により溶融状態とした後、前記マイクロ波の照射を停
止あるいは制限した状態で、前記溶融状態の上記固化物
質上面に、液体廃棄物を直接供給し水分を蒸発させ、供
給終了後に、前記マイクロ波の照射を開始し、前記固化
物質を溶融するものである。The microwave melting and solidifying method of liquid waste according to the present invention is a method in which a solidified substance contained in a retort is made into a molten state by irradiation with microwaves, and then, the melting is performed with the irradiation of the microwaves stopped or limited. The liquid waste is directly supplied to the upper surface of the solidified substance in the state to evaporate the water content, and after the supply is completed, the irradiation of the microwave is started to melt the solidified substance.
本発明においては、マイクロ波の照射を、予め、停止あ
るいは制限した状態で、溶融状態の固化物質上面に、液
体廃棄物を直接供給するようにしたので、水分の蒸発に
必要な熱エネルギを、溶融状態の固化物質から有効に得
ることができる。そして、この時には、マイクロ波の照
射が、停止あるいは制限されているため、ミスト化した
ナトリウム塩等が、マイクロ波エネルギにより原子化す
ることはない。従って、レトルト内に導電性雰囲気が形
成され、アークが発生することを有効に防止することが
できる。In the present invention, the microwave irradiation is stopped or limited in advance, and the liquid waste is directly supplied to the upper surface of the solidified substance in a molten state. It can be effectively obtained from a solidified substance in a molten state. At this time, since the irradiation of microwaves is stopped or limited, the misted sodium salt or the like is not atomized by the microwave energy. Therefore, it is possible to effectively prevent an arc from being generated by forming a conductive atmosphere in the retort.
以下、本発明の詳細を図面を用いて説明する。第１図
は、本発明方法で使用される液体廃棄物のマイクロ波溶
融固化装置を示すもので、図において符号１１は、レト
ルト１３を下部に取り付けるマイクロ波溶融炉を示して
いる。このマイクロ波溶融炉１１には、コントローラ１
５により制御されるマイクロ波発生装置１７の導電管１
８が接続されている。図において、符号１９は、液体廃
棄物２１を貯蔵するフィードタンクを示しており、この
フィードタンク１９からの液体廃棄物２１は、フィード
ポンプ２３により、ノズル部２５を介して、レトルト１
３内に供給される。Hereinafter, details of the present invention will be described with reference to the drawings. FIG. 1 shows a microwave melting and solidifying apparatus for liquid waste used in the method of the present invention. In the figure, reference numeral 11 denotes a microwave melting furnace in which a retort 13 is attached to the lower part. The microwave melting furnace 11 includes a controller 1
Conductive tube 1 of microwave generator 17 controlled by 5
8 is connected. In the figure, reference numeral 19 indicates a feed tank for storing a liquid waste 21, and the liquid waste 21 from the feed tank 19 is fed by a feed pump 23 via a nozzle portion 25 to the retort 1.
3 is supplied.
第２図は、ノズル部２５の一例を示すもので、この例で
は、ノズル２９は、固定されており、ノズル２９からの
液体廃棄物２１は図の点線Ａで示すように、固化物質３
１上面に直接供給される。FIG. 2 shows an example of the nozzle part 25. In this example, the nozzle 29 is fixed, and the liquid waste 21 from the nozzle 29 is solidified substance 3 as shown by the dotted line A in the figure.
1 Directly supplied to the upper surface.
第３図は、他の例を示すもので、この例では、ノズル３
３が水平方向に移動可能とされており、図の点線Ｂで示
すように、固化物質３１上面に直接供給される。FIG. 3 shows another example. In this example, the nozzle 3
3 is movable in the horizontal direction, and is directly supplied to the upper surface of the solidified substance 31, as shown by the dotted line B in the figure.
しかして、本発明方法は、以上のような装置を用いて以
下述べるようにして行なわれる。Therefore, the method of the present invention is carried out as described below by using the above apparatus.
すなわち、本発明方法では、先ず、レトルト１３内に収
容される、例えば、ガラスからなる固化物質３１が、マ
イクロ波発生装置１７によるマイクロ波の照射により溶
融状態とされる。この後、コントローラ１５によりマイ
クロ波の照射を停止あるいは制限した状態で、溶融状態
の固化物質３１上面に、例えば、硫酸ナトリウム，硝酸
ナトリウム等のナトリウム塩を含む放射性洗濯廃棄から
なる液体廃棄物２１が直接供給され、水分が蒸発され
る。この液体廃棄物２１の供給終了後に、コントローラ
１５によりマイクロ波の照射が開始され、固化物質３１
が溶融され、この固化物質３１の上部に乾燥状態で存在
していた液体廃棄物２１が固化物質３１内に混入され
る。That is, in the method of the present invention, first, the solidified substance 31 made of, for example, glass contained in the retort 13 is brought into a molten state by the irradiation of microwaves by the microwave generator 17. After that, with the controller 15 stopping or limiting the irradiation of microwaves, the liquid waste 21 formed of radioactive laundry waste containing, for example, sodium salts such as sodium sulfate and sodium nitrate is provided on the upper surface of the solidified substance 31 in a molten state. It is supplied directly and the water is evaporated. After the supply of the liquid waste 21 is completed, the controller 15 starts the irradiation of microwaves, and the solidified material 31
Is melted, and the liquid waste 21 existing in a dry state above the solidified substance 31 is mixed into the solidified substance 31.
以上のような処理を、レトルト１３内が、乾燥した液体
廃棄物２１により充填されるまで繰り返すことにより、
安定なガラス固化体を得ることができる。By repeating the above processing until the inside of the retort 13 is filled with the dried liquid waste 21,
A stable vitrified body can be obtained.
しかして、本発明方法では、マイクロ波の照射を、予
め、停止あるいは制限した状態で、溶融状態の固化物質
３１上面に、液体廃棄物２１を直接供給するようにした
ので、水分の蒸発に必要な熱エネルギを、溶融状態の固
化物質３１から有効に得ることができる。そして、この
時には、マイクロ波の照射が、停止あるいは制限されて
いるため、ミスト化したナトリウム塩等が、マイクロ波
エネルギにより原子化することはない。従って、レトル
ト内に導電性雰囲気が形成され、アークが発生すること
を有効に防止することができる。In the method of the present invention, the liquid waste 21 is directly supplied to the upper surface of the solidified substance 31 in the molten state in a state where the microwave irradiation is stopped or limited in advance. A large amount of heat energy can be effectively obtained from the solidified substance 31 in a molten state. At this time, since the irradiation of microwaves is stopped or limited, the misted sodium salt or the like is not atomized by the microwave energy. Therefore, it is possible to effectively prevent an arc from being generated by forming a conductive atmosphere in the retort.
次表は、本発明方法によりナトリウム塩を含んだ液体廃
棄物を処理した時の実験結果を示すもので、マイクロ波
出力４kwで2.0／Ｈの処理量を得ることができた。な
お、運転サイクル６分の内、１５秒が、マイクロ波の出
力停止時間とされている。The following table shows the experimental results when the liquid waste containing sodium salt was treated by the method of the present invention, and the throughput of 2.0 / H could be obtained at the microwave output of 4 kw. Note that, of the 6 minutes of the operation cycle, 15 seconds is the microwave output stop time.
なお、以上述べた実施例では、本発明方法をナトリウム
塩を含む液体廃棄物に用いた例について説明したが、本
発明はかかる実施例に限定されるものではなく、そのミ
スト化によりアークを発生する成分を含む液体廃棄物で
あれば良いことは勿論である。 In addition, in the above-mentioned embodiment, the example in which the method of the present invention is used for the liquid waste containing sodium salt has been described, but the present invention is not limited to such an embodiment, and an arc is generated by the mist formation. Needless to say, any liquid waste containing a component to be used may be used.
以上のように本発明によれば、マイクロ波の照射を、予
め、停止あるいは制限した状態で、溶融状態の固化物質
上面に、液体廃棄物を直接供給するようにしたので、レ
トルト内に導電性雰囲気が形成され、アークが発生する
ことを有効に防止することができるという利点がある。As described above, according to the present invention, the liquid waste is directly supplied to the upper surface of the solidified substance in the molten state in a state where the microwave irradiation is stopped or limited in advance. There is an advantage that an atmosphere is formed and an arc can be effectively prevented.
第１図は本発明方法に用いられる液体廃棄物のマイクロ
波溶融固化装置を示す配管系統図、第２図および第３図
はそれぞれノズル部を示す縦断面図である。 １３……レトルト、２１……液体廃棄物、３１……固化
物質。FIG. 1 is a piping system diagram showing a microwave melting and solidifying apparatus for liquid waste used in the method of the present invention, and FIGS. 2 and 3 are vertical sectional views showing nozzle portions. 13 ... Retort, 21 ... Liquid waste, 31 ... Solidifying substance.
Claims (5)
ロ波の照射により溶融状態とした後、前記マイクロ波の
照射を停止あるいは制限した状態で、前記溶融状態の前
記固化物質上面に、液体廃棄物を直接供給し水分を蒸発
させ、供給終了後に、前記マイクロ波の照射を開始し、
前記固化物質を溶融することを特徴とする液体廃棄物の
マイクロ波溶融固化方法。1. A liquid waste is disposed on the upper surface of the solidified substance in the molten state after the solidified substance contained in the retort is melted by irradiation with microwaves and then the irradiation of the microwave is stopped or limited. The substance is directly supplied to evaporate the water content, and after the supply is completed, the irradiation of the microwave is started,
A microwave melting and solidifying method for liquid waste, which comprises melting the solidified substance.
る特許請求の範囲第１項記載の液体廃棄物のマイクロ波
溶融固化方法。2. The microwave melting and solidifying method for liquid waste according to claim 1, wherein the liquid waste is a sodium salt-containing waste liquid.
第１項または第２項記載の液体廃棄物のマイクロ波溶融
固化方法。3. The microwave melting and solidifying method for liquid waste according to claim 1 or 2, wherein the solidifying substance is glass.
求の範囲第１項ないし第３項のいずれか一項記載の液体
廃棄物のマイクロ波溶融固化方法。4. The method of microwave melting and solidifying liquid waste according to any one of claims 1 to 3, wherein the liquid waste is radioactive waste.
請求の範囲第４項記載の液体廃棄物のマイクロ波溶融固
化方法。5. The method of microwave melting and solidifying liquid waste according to claim 4, wherein the liquid waste is radioactive laundry waste liquid.