JPH0655490B2 - Packaging films and bags - Google Patents
Packaging films and bagsInfo
- Publication number
- JPH0655490B2 JPH0655490B2 JP9739288A JP9739288A JPH0655490B2 JP H0655490 B2 JPH0655490 B2 JP H0655490B2 JP 9739288 A JP9739288 A JP 9739288A JP 9739288 A JP9739288 A JP 9739288A JP H0655490 B2 JPH0655490 B2 JP H0655490B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- bag
- sheet
- flat tubular
- packaging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は、米袋、ブロイラー袋その他の食品用包装袋、
肥料用包装袋等に使用される包装用フィルム及び袋に関
する。DETAILED DESCRIPTION OF THE INVENTION [Industrial field of application] The present invention relates to a rice bag, a broiler bag and other food packaging bags,
The present invention relates to a packaging film and bag used for a fertilizer packaging bag and the like.
［従来の技術］ 例えば、食品包装用のフィルムとして、透明性と光沢性
が優れていることから、従来直鎖状低密度ポリエチレン
（Ｌ−ＬＤＰＥ）等のポリオレフィン製フィルムが市場
で使用されている。そして本出願人は、偏平チューブ状
に形成したこのポリオレフィン製フィルムに、印刷面を
内側にしてシート状の延伸フィルムをドライラミネート
法で接着することにより、外観が良好であり、且つ擦れ
に強い包装用フィルム及びその製造方法を提案した（特
願昭６２−７５４１０）。[Prior Art] For example, as a film for food packaging, a polyolefin film such as a linear low-density polyethylene (L-LDPE) has been conventionally used in the market because of its excellent transparency and gloss. . The applicant of the present invention, by adhering a sheet-shaped stretched film with the printing surface inside by a dry lamination method to this polyolefin film formed into a flat tube shape, has a good appearance and is resistant to rubbing. Film and a method for producing the film have been proposed (Japanese Patent Application No. 62-75410).
［発明が解決しようとする課題］ 上述したように、偏平チューブ状のポリオレフィン製フ
ィルムにシート状延伸フィルムをドライラミネート法に
より接着して包装用フィルムを構成し、これを使用して
作製した、例えば米袋には空気抜き用の小さな穴を複数
個設けている。そして、このような米袋は、運搬の途中
で落下などによる衝撃を受けた場合、この穴から袋が破
れ易いという問題点があった。[Problems to be Solved by the Invention] As described above, a sheet-shaped stretched film is adhered to a flat tubular polyolefin film by a dry lamination method to form a packaging film, which is produced by using, for example, The rice bag has several small holes for venting air. In addition, such a rice bag has a problem that the bag is easily broken from the hole when it is subjected to an impact such as a drop during transportation.
本発明は、落下などの衝撃があっても破れる虞れのない
包装用フィルム及び袋を提供することを目的とする。An object of the present invention is to provide a packaging film and a bag that are not likely to be broken even if there is an impact such as a drop.
［課題を解決するための手段］ 本発明に係る包装用フィルムは、エチレンとα−オレフ
ィンとの共重合体より成る偏平チューブ状フィルムの少
なくとも一方の表面にシート状フィルムを接着し、かつ
小穴を形成した包装用フィルムにおいて、α−オレフィ
ンの炭素数を５〜１０に設定すると共に、偏平チューブ
状フィルムとシート状フィルムとの接着強度を２００〜
８００ｇ／15mm幅の範囲に設定したことを特徴とする。[Means for Solving the Problem] The packaging film according to the present invention has a sheet-like film bonded to at least one surface of a flat tubular film made of a copolymer of ethylene and α-olefin, and has small holes. In the formed packaging film, the carbon number of the α-olefin is set to 5 to 10, and the adhesive strength between the flat tubular film and the sheet film is set to 200 to
It is characterized by being set within the range of 800 g / 15 mm width.
また、本発明に係る袋は、エチレンとα−オレフィンと
の共重合体より成る偏平チューブ状フィルムの少なくと
も一方の表面にシート状フィルムを接着した包装用フィ
ルムから構成され、かつ小穴が形成された袋において、
α−オレフィンの炭素数を５〜１０に設定すると共に、
偏平チューブ状フィルムとシート状フィルムとの接着強
度を２００〜８００ｇ／15mm幅の範囲に設定したことを
特徴とする。Further, the bag according to the present invention is composed of a packaging film in which a sheet film is adhered to at least one surface of a flat tubular film made of a copolymer of ethylene and α-olefin, and small holes are formed. In the bag,
While setting the carbon number of the α-olefin to 5 to 10,
It is characterized in that the adhesive strength between the flat tubular film and the sheet film is set in the range of 200 to 800 g / 15 mm width.
炭素数５〜１０のα−オレフィンとは、具体的には１−
ペンテン、１−ヘキセン、１−ヘプテン、１−オクテ
ン、１−ノネン、１−デセン等である。The α-olefin having 5 to 10 carbon atoms is specifically 1-
Pentene, 1-hexene, 1-heptene, 1-octene, 1-nonene, 1-decene and the like.
シート状フィルムの材料としては特に限定はないが、ポ
リエチレン、ポリプロピレン、ナイロン等殆ど全てのプ
ラスチックフィルムを用いることができる。The material of the sheet film is not particularly limited, but almost all plastic films such as polyethylene, polypropylene and nylon can be used.
接着強度を上記範囲に設定することは、接着剤の塗布量
及び／又は接着剤の組成を制御したり、又は偏平チュー
ブ状フィルムに対して施す表面酸化のためのコロナ放電
の強度を制御することにより可能である。例えば、接着
剤として２液硬化型ウレタン系接着剤であるアドコート
３００Ａ（Ａとする）、アドコート３００Ｂ（Ｂとす
る）、溶剤としてＳＴ１０８（いずれも商品名で東洋モ
ートン（株）製）を使用した場合、次の表１に示すよう
に、これらの混合比率及び／又は塗布ロール深度を変え
ることにより、接着強度を制御することができる。Setting the adhesive strength within the above range controls the amount of adhesive applied and / or the composition of the adhesive, or the strength of corona discharge for surface oxidation applied to the flat tubular film. Is possible. For example, Adcoat 300A (referred to as A) and Adcoat 300B (referred to as B), which are two-component curing type urethane adhesives, were used as the adhesive, and ST108 (all are trade names, manufactured by Toyo Morton Co., Ltd.) was used as the solvent. In this case, as shown in Table 1 below, the adhesive strength can be controlled by changing the mixing ratio and / or the coating roll depth.
印刷が施されたシート状フイルムをその印刷面を偏平チ
ューブ状フィルム側に向けて接着する面は、偏平チュー
ブ状フィルムの表側の表面又は裏側の表面のいずれか一
方もしくは両側の表面とすることができる。なお、印刷
はチューブ状フィルムに直接施こしても良く、又はこの
ように印刷が施された透明なシート状フィルムを接着し
ても良い。 The surface on which the printed surface of the printed film is adhered with its printed surface facing the flat tubular film side may be either the front surface or the back surface of the flat tubular film, or both surfaces. it can. The printing may be performed directly on the tubular film, or a transparent sheet film thus printed may be adhered.
［作用］ エチレンと炭素数が４以下のα−オレフィンとの共重合
体より成る包装用フィルムの場合には、耐落下強度が不
充分である。そして、エチレンと炭素数が５以上のα−
オレフィンとの共重合体であっても、偏平チューブ状フ
ィルムとシート状フィルムとの接着強度が２００ｇ／15
mm幅より下の場合には、接着強度が弱く、容易に剥がれ
る。また、逆に接着強度が８００ｇ／15mm幅より上の場
合には、衝撃に弱く、落下によって、小穴から破れ易
い。従って、エチレンと炭素数が５〜１０のα−オレフ
ィンとの共重合体より成る偏平チューブ状フィルムを使
用すると共に、偏平チューブ状フィルムと包装フィルム
との接着強度を２００〜８００ｇ／15mm幅の範囲に設定
することにより、衝撃に強く、容易には破れない包装用
フィルムが得られる。なお、通常のこの種の包装用フィ
ルムの接着強度は、１０００〜１５００ｇ／15mm幅であ
る。[Operation] In the case of a packaging film made of a copolymer of ethylene and an α-olefin having 4 or less carbon atoms, the drop resistance is insufficient. And ethylene and α- having 5 or more carbon atoms
Even if it is a copolymer with olefin, the adhesive strength between the flat tubular film and the sheet film is 200 g / 15
If the width is less than mm, the adhesive strength is weak and it can be easily peeled off. On the contrary, when the adhesive strength is more than 800 g / 15 mm width, it is weak against impact and is easily broken from a small hole when dropped. Therefore, a flat tubular film made of a copolymer of ethylene and an α-olefin having 5 to 10 carbon atoms is used, and the adhesive strength between the flat tubular film and the packaging film is in the range of 200 to 800 g / 15 mm width. By setting to, a packaging film that is resistant to impact and is not easily broken can be obtained. The usual adhesive strength of this type of packaging film is 1000 to 1500 g / 15 mm width.
［実施例］ 実施例１ エチレンと炭素数８のα−オレフィンとの共重合体であ
るＬ−ＬＤＰＥ（「モアテック ０１３８」（商品名）
出光石油化学（株）製、ＭＩ：１、密度：０．９２）よ
り成る偏平チューブ状フィルム（厚さ８０μ）を使用
し、この表側の表面に２液硬化型ウレタン系接着剤（ア
ドコートＡとアドコートＢ、いずれも商品名で東洋モー
トン（株）製）を接着強度が３１０ｇ／15mm幅となるよ
うにその塗布量を調整して塗布した後、印刷面を裏面側
にしてシート状延伸ナイロンフィルム（厚さ１５μ）を
ドライラミネートすることにより、包装用フィルムを製
造した。そして、この包装用フィルムを使用してオート
パッカーで米を１０kg充填し、シールすることにより米
袋を得た。第１図に示すように、この米袋１は、幅が３
４５mm、長さが５７０mmであり、上部と下部に空気流通
用の針穴２をそれぞれ３箇所形成してある。[Examples] Example 1 L-LDPE (“Moretech 0138” (trade name), which is a copolymer of ethylene and an α-olefin having 8 carbon atoms.
A flat tubular film (80 μm thick) made of Idemitsu Petrochemical Co., Ltd., MI: 1, density: 0.92) was used, and a two-component curing type urethane adhesive (Adcoat A and Adcoat B, manufactured by Toyo Morton Co., Ltd. under the trade name, is applied by adjusting the application amount so that the adhesive strength is 310 g / 15 mm width, and then the sheet-shaped stretched nylon film with the printing surface on the back side. A film for packaging was manufactured by dry laminating (thickness 15 μm). Then, using this packaging film, 10 kg of rice was filled with an auto packer and sealed to obtain a rice bag. As shown in FIG. 1, this rice bag 1 has a width of 3
The length is 45 mm and the length is 570 mm, and three needle holes 2 for air circulation are formed in the upper and lower portions, respectively.
この米袋１を使用して、第１図に示すように、常温下、
1.5ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、５回までの落袋では破
袋しないで、６回目の落袋によって針穴２から袋１が破
れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 1.5 m in the vertical direction. As a result, the bag 1 was torn from the needle hole 2 by the sixth dropping, without breaking the bag by dropping the bag up to 5 times.
実施例２ エチレンと炭素数８のα−フレームとの共重合体である
Ｌ−ＬＤＰＥ（モアテック １０３８」（商品名）出光
石油化学（株）製、ＭＩ：１、密度：０．９２）より成
る偏平チューブ状フィルム（厚さ８０μ）を使用し、こ
の表側の表面に２液硬化型ウレタン系接着剤（アドコー
トＡとアドコートＢ、いずれも商品名で東洋モートン
（株）製）を接着強度が６８０ｇ／15mm幅となるように
その塗布量を調整して塗布した後、印刷面を裏面側とし
てシート状延伸ナイロンフィルム（厚さ１５μ）をドラ
イラミネートすることにより、包装用フィルムを製造し
た。そして、この包装用フィルムを使用してオートパッ
カーで米を１０kg充填し、シールすることにより、実施
例１と同様の米袋を得た（第１図参照）。Example 2 L-LDPE (more tech 1038 "(trade name) manufactured by Idemitsu Petrochemical Co., Ltd., MI: 1, density: 0.92) which is a copolymer of ethylene and an α-frame having 8 carbon atoms A flat tubular film (thickness: 80μ) is used, and a two-component curing type urethane adhesive (Ad Coat A and Ad Coat B, both manufactured by Toyo Morton Co., Ltd. under the trade name) has an adhesive strength of 680 g on the front surface. A coating film was manufactured by adjusting the coating amount so as to have a width of / 15 mm and applying it, and then dry laminating a sheet-shaped stretched nylon film (thickness 15 μm) with the printing surface as the back side. Then, using this packaging film, 10 kg of rice was filled with an auto packer and sealed to obtain a rice bag similar to that of Example 1 (see FIG. 1).
この米袋１を使用して、第１図に示すように、常温下、
1.5ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、４回目の落袋により針
穴２から袋１が破れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 1.5 m in the vertical direction. As a result, the bag 1 was broken from the needle hole 2 by the fourth dropping bag.
実施例３ エチレンと炭素数６のα−オレフィン（４−メチルペン
テン−１）との共重合体であるＬ−ＬＤＰＥ（「ウルト
ゼックス ２０２１Ｌ」（商品名）三井石油化学（株）
製、ＭＩ：2.0、密度：０．９２）より成る偏平チュー
ブ状フィルム（厚さ８０μ）を使用し、この表側の表面
に２液硬化型ウレタン系接着剤（アドコートＡとアドコ
ートＢ、いずれも商品名で東洋モートン（株）製）を接
着強度が２８０ｇ／15mm幅となるようにその塗布量を調
整して塗布した後、印刷面を裏面側としてシート状延伸
ナイロンフィルム（厚さ１５μ）をドライラミネートす
ることにより、包装用フィルムを製造した。そして、こ
の包装用フィルムを使用してオートパッカーで米を１０
kg充填し、シールすることにより、実施例１と同様の米
袋を得た（第１図参照）。Example 3 L-LDPE (“Ultozex 2021L” (trade name) Mitsui Petrochemical Co., Ltd.) which is a copolymer of ethylene and an α-olefin (4-methylpentene-1) having 6 carbon atoms
Manufactured by MI, 2.0, density: 0.92), a flat tubular film (80μ thick) is used, and a two-component curing type urethane adhesive (ad coat A and ad coat B, both of which is a product Toyo Morton Co., Ltd. is applied under the name by adjusting the coating amount so that the adhesive strength is 280 g / 15 mm width, and then the sheet-shaped stretched nylon film (thickness 15μ) is dried with the printing side as the back side. A packaging film was produced by laminating. Then, use this packaging film to remove rice with an autopacker.
By filling in kg and sealing, a rice bag similar to that in Example 1 was obtained (see FIG. 1).
この米袋１を使用して、第１図に示すように、常温下、
1.5ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、５回までの落袋では破
袋しないで、６回目の落袋によって針穴２から袋１が破
れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 1.5 m in the vertical direction. As a result, the bag 1 was torn from the needle hole 2 by the sixth dropping, without breaking the bag by dropping the bag up to 5 times.
比較例１ エチレンと炭素数８のα−オレフィンとの共重合体であ
るＬ−ＬＤＰＥ（「モアテック ０１３８」（商品名）
出光石油化学（株）製、ＭＩ：１、密度：０．９２）よ
り成る偏平チューブ状フィルム（厚さ８０μ）を使用
し、この表側の表面に２液硬化型ウレタン系接着剤（ア
ドコートＡとアドコートＢ、いずれも商品名で東洋モー
トン（株）製）を接着強度が1200ｇ／15mm幅となるよう
にその塗布量を調整して塗布した後、印刷面が裏面とな
るようにシート状延伸ナイロンフィルム（厚さ１５μ）
をドライラミネートすることにより、包装用フィルムを
製造した。そして、この包装用フィルムを使用してオー
トパッカーで米を１０kg充填し、シールすることによ
り、実施例１と同様の米袋を得た（第１図参照）。Comparative Example 1 L-LDPE (“Moretech 0138” (trade name), which is a copolymer of ethylene and an α-olefin having 8 carbon atoms
A flat tubular film (80 μm thick) made of Idemitsu Petrochemical Co., Ltd., MI: 1, density: 0.92) was used, and a two-component curing type urethane adhesive (Adcoat A and Adcoat B, both manufactured by Toyo Morton Co., Ltd., under the trade name, is applied in a sheet-shaped stretched nylon so that the printed surface is the back surface after the application amount is adjusted so that the adhesive strength is 1200 g / 15 mm width. Film (thickness 15μ)
A film for packaging was manufactured by dry laminating. Then, using this packaging film, 10 kg of rice was filled with an auto packer and sealed to obtain a rice bag similar to that of Example 1 (see FIG. 1).
この米袋１を使用して、第１図に示すように、常温下、
1.0ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、１回目の落袋で針穴２
から袋１が破れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 1.0 m in the vertical direction. As a result, needle hole 2
The bag 1 was torn.
比較例２ エチレンと炭素数４のα−オレフィンとの共重合体であ
るＬ−ＬＤＰＥ（「出光ポリエチレン−Ｌ ０１３４」
（商品名）出光石油化学（株）製、ＭＩ：１、密度：
０．９２）より成る偏平チューブ状フィルム（厚さ８０
μ）を使用し、この表側の表面に２液硬化型ウレタン系
接着剤（アドコートＡとアドコートＢ、いずれも商品名
で東洋モートン（株）製）を接着強度が２７０ｇ／15mm
幅となるようにその塗布量を調整して塗布した後、印刷
面を裏面側としてシート状延伸ナイロンフィルム（厚さ
１５μ）をドライラミネートすることにより、包装用フ
ィルムを製造した。そして、この包装用フィルムを使用
してオートパッカーで米を１０kg充填し、シールするこ
とにより、実施例１と同様の米袋を得た（第１図参
照）。Comparative Example 2 L-LDPE (“Idemitsu Polyethylene-L 0134”) which is a copolymer of ethylene and an α-olefin having 4 carbon atoms.
(Brand name) Idemitsu Petrochemical Co., Ltd., MI: 1, density:
0.92) made of flat tubular film (thickness 80
μ), and a two-component curing type urethane adhesive (Ad Coat A and Ad Coat B, both manufactured by Toyo Morton Co., Ltd.) on the surface of this side has an adhesive strength of 270 g / 15 mm.
The coating amount was adjusted so as to have a width, and the sheet was stretched, and the sheet-shaped stretched nylon film (thickness: 15 μm) was dry-laminated to prepare a packaging film. Then, using this packaging film, 10 kg of rice was filled with an auto packer and sealed to obtain a rice bag similar to that of Example 1 (see FIG. 1).
この米袋１を使用して、第１図に示すように、常温下、
0.8ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、１回目の落袋で針穴２
から袋１が破れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 0.8 m in the vertical direction. As a result, needle hole 2
The bag 1 was torn.
比較例３ エチレンの高圧法による重合体である低密度ポリエチレ
ン（ＬＤＰＥ）（「宇部ＬＤＰＥ Ｒ５００」（商品
名）宇部興産（株）製、ＭＩ：0.5、密度：０．９２）
より成る偏平チューブ状フィルム（厚さ８０μ）を使用
し、この表側の表面に２液硬化型ウレタン系接着剤（ア
ドコートＡとアドコートＢ、いずれも商品名で東洋モー
トン（株）製）を接着強度が３８０ｇ／15mm幅となるよ
うにその塗布量を調整して塗布した後、印刷面を裏面側
としてシート状延伸ナイロンフィルム（厚さ１５μ）を
ドライラミネートすることにより、包装用フィルムを製
造した。そして、この包装用フィルムを使用してオート
パッカーで米を１０kg充填し、シールすることにより、
実施例１と同様の米袋を得た（第１図参照）。Comparative Example 3 Low density polyethylene (LDPE) which is a polymer of ethylene by a high pressure method (“Ube LDPE R500” (trade name) manufactured by Ube Industries, Ltd., MI: 0.5, density: 0.92)
Adhesive strength of a two-component curing type urethane adhesive (Ad Coat A and Ad Coat B, both manufactured by Toyo Morton Co., Ltd. under the trade name) is used on the front surface of the flat tubular film (80 μm thick) The coating amount was adjusted so as to be 380 g / 15 mm width, and then the sheet-shaped stretched nylon film (thickness 15 μm) was dry-laminated with the printing surface as the back side to produce a packaging film. Then, using this packaging film, 10 kg of rice is filled with an auto packer and sealed,
A rice bag similar to that of Example 1 was obtained (see FIG. 1).
この米袋１を使用して、第１図に示すように、常温下、
0.5ｍの高さから垂直方向に落とすことにより、耐落下
強度の試験を行った。この結果、１回目の落袋で針穴２
から袋１が破れた。Using this rice bag 1, as shown in FIG. 1, at room temperature,
A drop resistance strength test was performed by dropping from a height of 0.5 m in the vertical direction. As a result, needle hole 2
The bag 1 was torn.
［発明の効果］ 本発明により、落下等の衝撃に強く、容易には破れない
包装用フィルム及び袋を得ることができる。EFFECTS OF THE INVENTION The present invention makes it possible to obtain a packaging film and a bag that are resistant to impacts such as dropping and are not easily broken.
【図面の簡単な説明】 第１図は米袋及び米袋の耐落下強度の試験方法を示す図
である。 １……米袋。BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a diagram showing a rice bag and a test method for drop strength of the rice bag. 1 ... rice bag.
Claims (2)
り成る偏平チューブ状フィルムの少なくとも一方の表面
にシート状フィルムを接着し、かつ小穴を形成した包装
用フィルムにおいて、 該α−オレフィンの炭素数を５〜１０に設定すると共
に、 該偏平チューブ状フィルムと該シート状フィルムとの接
着強度を２００〜８００ｇ／15mm幅の範囲に設定したこ
とを特徴とする包装用フィルム。1. A packaging film in which a sheet-shaped film is adhered to at least one surface of a flat tubular film made of a copolymer of ethylene and α-olefin, and small holes are formed in the film. A packaging film, wherein the number is set to 5 to 10 and the adhesive strength between the flat tubular film and the sheet film is set to a range of 200 to 800 g / 15 mm width.
り成る偏平チューブ状フィルムの少なくとも一方の表面
にシート状フィルムを接着した包装用フィルムから構成
され、かつ小穴が形成された袋において、 該α−オレフィンの炭素数を５〜１０に設定すると共
に、 該偏平チューブ状フィルムと該シート状フィルムとの接
着強度を２００〜８００ｇ／15mm幅の範囲に設定したこ
とを特徴とする袋。2. A bag comprising a packaging film in which a sheet-shaped film is adhered to at least one surface of a flat tubular film made of a copolymer of ethylene and α-olefin, wherein a small hole is formed in the bag. A bag characterized in that the carbon number of the α-olefin is set to 5 to 10 and the adhesive strength between the flat tubular film and the sheet film is set to a range of 200 to 800 g / 15 mm width.