JPH0677299B2 - Magnetic head - Google Patents
Magnetic headInfo
- Publication number
- JPH0677299B2 JPH0677299B2 JP60021511A JP2151185A JPH0677299B2 JP H0677299 B2 JPH0677299 B2 JP H0677299B2 JP 60021511 A JP60021511 A JP 60021511A JP 2151185 A JP2151185 A JP 2151185A JP H0677299 B2 JPH0677299 B2 JP H0677299B2
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- magnetic head
- molded body
- plastic molded
- guide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 産業上の利用分野 本発明は磁気記録再生装置に用いることができる磁気ヘ
ッドに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic head that can be used in a magnetic recording / reproducing apparatus.
従来の技術 近年、磁気記録技術の高度化、特に磁気記録の高度化に
対する要請はきわめて強いものがある。この要請に応じ
るためには、磁気記録媒体の高保磁力化、高磁束密度
化、及び磁気ヘッドの記録特性、再生感度の大巾な改良
とともに、磁気ヘッドを外部からの電磁気ノイズより保
護し、低雑音化を図る必要がある。又、磁気ヘッドは超
精密加工技術を要する為に、生産性が悪く、非常に高価
格なものになっている。2. Description of the Related Art In recent years, there has been an extremely strong demand for the sophistication of magnetic recording technology, especially for sophistication of magnetic recording. In order to meet this demand, the magnetic recording medium has a high coercive force, a high magnetic flux density, and a large improvement in the recording characteristics and reproducing sensitivity of the magnetic head. It is necessary to make noise. Further, since the magnetic head requires ultra-precision processing technology, it has poor productivity and is very expensive.
以下図面を参照しながら従来の磁気ヘッドについて説明
する。第８図（Ａ）は従来の磁気ヘッドの斜視図、第８
図（Ｂ）はその正面図であり、（１）は磁気コアであ
る。（２）はチタン酸バリウム系セラミックスで磁気コ
アのガイドを構成している。（３）は巻線コイルであ
る。ガイドの上面は記録媒体が高速で長時間の接触運動
をする為に、耐摩耗性及び表面平滑性に優れた材料でな
ければならない。又、ガイドは磁気コア（１）と接する
為に、熱膨張係数もできるだけ磁気コア（１）材に近い
ものが選ばれており、磁気コア（１）材にMn−Znフェラ
イト系磁性体（熱膨張係数α＝106×10-7/℃、ビッカー
ス硬度Hv＝650）を使用する場合、チタン酸バリウム系
セラミックス（α＝92×10-7/℃、Hv＝700）を使用して
いる。チタン酸バリウム系セラミックス（２）はMn−Zn
フェライト系磁性体と同様に硬度も高い為に、記録媒体
からの摩耗には充分耐えるものである。A conventional magnetic head will be described below with reference to the drawings. FIG. 8A is a perspective view of a conventional magnetic head, and FIG.
FIG. 1B is a front view thereof, and (1) is a magnetic core. (2) is a barium titanate-based ceramic and constitutes a guide of the magnetic core. (3) is a winding coil. The upper surface of the guide must be made of a material having excellent wear resistance and surface smoothness in order for the recording medium to make high-speed and long-time contact movement. Further, since the guide is in contact with the magnetic core (1), a guide whose thermal expansion coefficient is as close as possible to that of the magnetic core (1) material is selected, and the magnetic core (1) material is made of Mn-Zn ferrite-based magnetic material (thermal When the expansion coefficient α = 106 × 10 -7 / ° C and Vickers hardness Hv = 650) is used, barium titanate-based ceramics (α = 92 × 10 -7 / ° C, Hv = 700) are used. Barium titanate ceramics (2) is Mn-Zn
Since it has a high hardness like a ferrite-based magnetic material, it sufficiently withstands abrasion from the recording medium.
発明が解決しようとする問題点 しかし、このような従来の磁気ヘッドは、その高硬度の
為に機械加工性が悪く、複雑な形状加工や大きな形状加
工になると非常に加工費が高くなるという欠点を有して
いる。Problems to be Solved by the Invention However, such a conventional magnetic head has poor machinability due to its high hardness, and has a drawback that the machining cost becomes very high in the case of complicated shape processing or large shape processing. have.
そこで本発明は、磁気コアのガイドを安価に量産可能と
することを目的とする。Therefore, an object of the present invention is to enable mass production of magnetic core guides at low cost.
問題点を解決するための手段 上記目的を達成するため本発明は、磁気ヘッド本体の磁
気コアをガイドする非磁性体を、チタン酸バリウム系セ
ラミックスとプラスチック成型体とで構成したものであ
る。Means for Solving the Problems In order to achieve the above object, the present invention comprises a non-magnetic body for guiding a magnetic core of a magnetic head body, which is composed of barium titanate-based ceramics and a plastic molded body.
作 用 これによれば、磁気コアのガイドに、プラスチック成型
技術という安価で量産化に適した技術を導入できる。Operation According to this, it is possible to introduce a plastic molding technology, which is cheap and suitable for mass production, into the magnetic core guide.
また、従来の磁気ヘッドにおいては、高密度記録化と共
に外界からの電磁気ノイズを無視できなくなり、記録再
生エラーの発生が極めて高くなる為に、電磁気シールド
を設ける必要があった。従来法によると、磁気コアある
いはそのガイドの周辺をパーマロイ等の磁性材料でキャ
ップ状に覆うという方法によって、電磁気ノイズを除去
していた。しかし、シールド部品を別加工する必要があ
る事、シールド部品が磁気コアから遠く離れる為にシー
ルド効果が小さい事、シールド部品の保持機構が必要な
事など、電磁気シールド効果の割には磁気ヘッドの大型
化と高価格化になっているという欠点を有していた。In addition, in the conventional magnetic head, it is necessary to provide an electromagnetic shield because high density recording cannot be ignored and electromagnetic noise from the outside cannot be ignored and a recording / reproducing error is extremely high. According to the conventional method, electromagnetic noise is removed by a method in which the magnetic core or the periphery of the guide is covered with a magnetic material such as permalloy in a cap shape. However, it is necessary to process the shield component separately, the shield effect is small because the shield component is far from the magnetic core, and the shield component holding mechanism is required. It had the drawbacks of large size and high price.
このため本発明では、プラスチック成型体に銀粉とかカ
ーボンブラック等の導電性材料を混入してプラスチック
成型体を導電率を高くしたもので構成することができ、
またはプラスチック成型体の内部あるいは表層部にパー
マロイ等の磁性体を一体成型したもので構成することが
でき、またはプラスチック成型体の内部あるいは表層部
に金属材料を一体成型したもので構成することができ、
またはチタン酸バリウム系セラミックスとプラスチック
成型体との側面に銀あるいはカーボンブラック等の導電
性材料を塗装して構成することができる。これによれ
ば、電磁気シールドをガイドの内部あるいは表層部に形
成できる為に磁気ヘッドの低雑音化に大きく寄与できる
ものである。Therefore, in the present invention, it is possible to configure the plastic molded body with high conductivity by mixing a conductive material such as silver powder or carbon black into the plastic molded body,
Alternatively, a magnetic material such as permalloy can be integrally formed inside or on the surface of the plastic molded body, or can be formed by integrally molding a metal material inside or on the surface of the plastic molded body. ,
Alternatively, the side surfaces of the barium titanate-based ceramics and the plastic molded body may be coated with a conductive material such as silver or carbon black. According to this, since the electromagnetic shield can be formed inside the guide or in the surface layer portion, it can greatly contribute to the noise reduction of the magnetic head.
実施例 以下本発明の実施例について、図面を参照しながら説明
する。Embodiments Embodiments of the present invention will be described below with reference to the drawings.
第１図は本発明の第１の実施例における磁気ヘッドの正
面図を示すものである。ここで（１）は磁気コアで、Mn
−Znフェライト系磁性体でできている。（２）はチタン
酸バリウム系セラミックスで、ガイド板の薄板を構成し
ている。（３）は巻線コイルである。（４）はプラスチ
ック成型体で、ガラス繊維入りフェノール樹脂でできた
補助ガイドを構成している。チタン酸バリウム系セラミ
ックス（２）とプラスチック成型体（４）はエポキシ系
接着剤で接着し、又磁気コア（１）とこれらガイドもエ
ポキシ系接着剤で接着している。FIG. 1 is a front view of a magnetic head according to the first embodiment of the present invention. Here, (1) is the magnetic core, Mn
-Zn Ferrite magnetic material. (2) is a barium titanate-based ceramic, which constitutes a thin guide plate. (3) is a winding coil. (4) is a plastic molded body and constitutes an auxiliary guide made of phenolic resin containing glass fiber. The barium titanate-based ceramics (2) and the plastic molded body (4) are adhered with an epoxy adhesive, and the magnetic core (1) and these guides are also adhered with an epoxy adhesive.
プラスチック成型体は複雑な形状加工が容易な為、第２
図に示す第２の実施例のように巻線コイル（３）が入る
溝を設けて磁気ヘッドの小型化も図ることができる。Since the plastic molded body can be easily processed into complicated shapes,
The magnetic head can be miniaturized by providing a groove into which the winding coil (3) is inserted as in the second embodiment shown in the figure.
以上のように上記第１及び第２の実施例によれば、ガイ
ドは、記録媒体との接触面の薄い一部のみチタン酸バリ
ウム系セラミックス（２）を用い、ガイドの他の部分、
つまり補助ガイドはプラスチック成型体（４）で構成さ
れている為に、加工が容易で各種の形状に対応できるよ
うになっている。As described above, according to the first and second embodiments, the guide uses the barium titanate-based ceramics (2) only in a part where the contact surface with the recording medium is thin, and in the other part of the guide,
That is, since the auxiliary guide is made of the plastic molded body (4), it can be easily processed and can be adapted to various shapes.
次に、前述の電磁気シールドを施した本発明の他の実施
例について、図面を参照しながら説明する。Next, another embodiment of the present invention having the above-mentioned electromagnetic shield will be described with reference to the drawings.
第３図（Ａ）（Ｂ）（Ｃ）は本発明の第３の実施例にお
ける磁気ヘッドの製造加工順を示す斜視図を示す。第３
図（Ａ）において、（11）は磁気ヘッドを支持する金属
板（ステンレス製）であり、（12）は磁気コア（１）が
入る挿入窓、（13）はプラスチック成型体（４）と一体
成型される固定用ツメである。第３図（Ｂ）は金属板
（11）とプラスチック成型体（４）とを一体成型した状
態を示す。プラスチック成型体（４）は、補助ガイドと
してガラス繊維入りフェノール樹脂を使用している。第
３図（Ｃ）は予め磁気コア（１）とチタン酸バリウム系
セラミックス（２）とを接着していたガイドをプラスチ
ック成型体（４）の上に接着固化し、巻線コイル（３）
を形成して完成した状態を示す。この実施例によれば、
補助ガイド材料のプラスチック成型体（４）の特徴を生
かして、金属板（11）と一体成型できて加工の自動化、
量産化、低価格化に大きく寄与できるようになる。3 (A), (B) and (C) are perspective views showing the manufacturing process sequence of the magnetic head in the third embodiment of the present invention. Third
In the figure (A), (11) is a metal plate (made of stainless steel) for supporting the magnetic head, (12) is an insertion window into which the magnetic core (1) is inserted, and (13) is integrated with a plastic molding (4). It is a fixed claw that is molded. FIG. 3 (B) shows a state in which the metal plate (11) and the plastic molded body (4) are integrally molded. The plastic molded body (4) uses glass fiber-containing phenol resin as an auxiliary guide. FIG. 3 (C) shows a guide in which the magnetic core (1) and the barium titanate-based ceramics (2) are previously adhered to each other, which is adhered and solidified on the plastic molded body (4) to form the winding coil (3).
Shows the completed state. According to this example,
Taking advantage of the characteristics of the plastic molded body (4) of the auxiliary guide material, it can be integrally molded with the metal plate (11) to automate processing,
It will be able to greatly contribute to mass production and cost reduction.
第４図は本発明の第４の実施例における磁気ヘッドの正
面図を示すものである。第４図において、プラスチック
成型体（４）はエポキシ樹脂を使い、そのエポキシ樹脂
の中に銀粉あるいはカーボンブラック等の導電性材料
（５）を混入し、エポキシ樹脂の導電率の向上を図って
いる。（６）はシールド電極で、補助ガイドとしてのプ
ラスチック成型体（４）の表層部に銀ペーストで塗布形
成されている。FIG. 4 is a front view of a magnetic head according to the fourth embodiment of the present invention. In FIG. 4, an epoxy resin is used for the plastic molded body (4), and a conductive material (5) such as silver powder or carbon black is mixed in the epoxy resin to improve the conductivity of the epoxy resin. . Reference numeral (6) is a shield electrode, which is formed by applying silver paste on the surface layer of the plastic molded body (4) as an auxiliary guide.
第５図（Ａ）は本発明の第５の実施例における磁気ヘッ
ドの正面図を示すものである。この第５図（Ａ）におい
て、電磁気シールド材としてパーマロイ等の高透磁率の
磁性体（７）をプラスチック成型体（４）に一体成型し
ており、かつシールド電極（６）を形成している。第５
図（Ｂ）は第５図（Ａ）の補助ガイドを構成するプラス
チック成型体（４）の斜視図である。FIG. 5 (A) is a front view of a magnetic head according to the fifth embodiment of the present invention. In FIG. 5 (A), a magnetic material (7) having a high magnetic permeability such as permalloy is integrally molded with a plastic molding (4) as an electromagnetic shield material, and a shield electrode (6) is formed. . Fifth
FIG. 5B is a perspective view of the plastic molded body (4) forming the auxiliary guide of FIG. 5 (A).
第６図は第５図（Ａ）のガイドの製造工程を示すもので
あり、第６図（Ａ）で、薄板のチタン酸バリウム系セラ
ミックス（22）と、パーマロイ製の磁性体（27）を一体
成型したプラスチック成型体（ガラス繊維入りフェノー
ル樹脂）（24）のバーとを準備し、第６図（Ｂ）にてそ
れぞれをエポキシ系接着剤で接着し、第６図（Ｃ）にて
外周刃切断機により切断し、ガイドとして完成する。FIG. 6 shows the manufacturing process of the guide of FIG. 5 (A). In FIG. 6 (A), a thin barium titanate-based ceramics (22) and a magnetic material (27) made of permalloy are used. Prepare a bar of integrally molded plastic molded body (phenolic resin containing glass fiber) (24), and bond each with an epoxy adhesive in FIG. 6 (B), and the outer periphery in FIG. 6 (C). It is cut by a blade cutting machine and completed as a guide.
また、第４図〜第５図において、上述の磁性体（７）
（27）に代え、銅等の金属材料をプラスチック成型体
（４）（24）に一体成型してもよい。In addition, in FIGS. 4 to 5, the magnetic body (7) described above is used.
Instead of (27), a metal material such as copper may be integrally molded with the plastic molded body (4) (24).
第７図は本発明の第６の実施例における磁気ヘッドの斜
視図を示すものである。第７図において、ハッチング部
は、磁気コア（１）及びガイドの側面に電磁気シールド
の為に塗装された、銀あるいはカーボンブラック等の導
電性材料（８）を示している。FIG. 7 is a perspective view of a magnetic head according to the sixth embodiment of the present invention. In FIG. 7, the hatched portion shows a conductive material (8) such as silver or carbon black coated on the side surfaces of the magnetic core (1) and the guide for electromagnetic shielding.
上述の実施例では、電磁気シールドをガイドの内部ある
いは表層部に形成している為に、シールド効果が大き
く、しかも安価にガイドを製造する事ができる。In the above-mentioned embodiment, since the electromagnetic shield is formed inside or on the surface layer of the guide, the shield effect is great and the guide can be manufactured at low cost.
なお、上述の実施例では、電磁気シールド用磁性材料と
してパーマロイを使用したが、磁性材料はパーマロイに
限定されるものではなく、アモルファス磁性材でも効果
が大きく、電磁シールドという機能を有するものであれ
ば何でも良い。又、ガイド材のプラスチック成型体
（４）の応用として、ガイドと磁気ヘッドの水平保持・
移動の機能を有するヘッドキャリッジとの一体成型も可
能である。In the above-mentioned embodiment, although Permalloy was used as the magnetic material for electromagnetic shield, the magnetic material is not limited to Permalloy, and even amorphous magnetic material has a large effect and has a function as an electromagnetic shield. anything is fine. As an application of the plastic molded body (4) of the guide material, the guide and the magnetic head can be held horizontally
Integral molding with a head carriage having a moving function is also possible.
以上の説明から明らかなように、上述の実施例によれ
ば、磁気コアのガイド材料としてチタン酸バリウム系セ
ラミックスとプラスチックス成型体を接着構成し、ある
いは磁気ヘッドを支持する金属板とプラスチック成型体
を一体成型により構成し、あるいはガイド自体に電磁気
シールド材としてパーマロイ等の磁性材や銅等の金属材
料を一体成型し、あるいは、ガイド自体の導電率を高く
したり、表層部に導電性材料を塗布してシールド形成す
ることにより、磁気コアのガイドを、量産性の高いプラ
スチック成型技術を用いて安価に、しかも電磁気シール
ドをガイドの内部あるいは表層部に施して形成できる為
に、磁気コアが外界から受ける雑音の低下に大きな効果
が得られる。As is clear from the above description, according to the above-mentioned embodiment, the barium titanate-based ceramics and the plastic molded body are bonded as the guide material of the magnetic core, or the metal plate and the plastic molded body supporting the magnetic head are bonded. Is integrally molded, or the guide itself is integrally molded with a magnetic material such as permalloy or a metal material such as copper as an electromagnetic shield material, or the conductivity of the guide itself is increased or a conductive material is formed on the surface layer portion. By applying and forming a shield, the guide of the magnetic core can be formed inexpensively by using the plastic molding technology with high mass productivity, and furthermore, the electromagnetic shield can be formed inside or on the surface layer of the guide, so that the magnetic core can be formed in the external environment. A great effect can be obtained in reducing the noise received from.
発明の効果 以上述べたように本発明によると、ガイドにおける記録
媒体側の面をチタン酸バリウムで構成しているため、硬
度が高く、耐摩耗性及び表面平滑性に優れ、記録媒体に
よる摩耗に耐えるようにすることができ、また記録媒体
側には配置されない部分をプラスチック成型体で構成し
ているため、加工が容易でなおかつ量産性に優れ、各種
の形状に対応でき、例えば巻線コイルが入る溝を設ける
ことにより磁気ヘッドの小型化も図ることができる。As described above, according to the present invention, since the surface of the guide on the recording medium side is made of barium titanate, the hardness is high, the abrasion resistance and the surface smoothness are excellent, and the abrasion by the recording medium is prevented. It can withstand, and because the part that is not placed on the recording medium side is made of plastic molding, it is easy to process and has excellent mass productivity, and can be used in various shapes. The size of the magnetic head can be reduced by providing the groove.
第１図は本発明の第１の実施例の正面図、第２図は本発
明の第２の実施例の斜視図、第３図（Ａ）（Ｂ）（Ｃ）
は本発明の第３の実施例をその製造工程とともに示す斜
視図、第４図は本発明の第４の実施例の正面図、第５図
（Ａ）（Ｂ）は本発明の第５の実施例を示す図、第６図
（Ａ）（Ｂ）（Ｃ）は第５図に示すガイドの製造工程を
示す斜視図、第７図は本発明の第６の実施例の斜視図、
第８図（Ａ）は従来例の斜視図、同図（Ｂ）はその正面
図である。 （１）……磁気コア、（２）（22）……チタン酸バリウ
ム系セラミックス、（４）（24）……プラスチック成型
体、（５）（８）……導電性材料、（６）……シールド
電極、（７）（27）……磁性体、（11）……金属板FIG. 1 is a front view of the first embodiment of the present invention, FIG. 2 is a perspective view of the second embodiment of the present invention, and FIGS. 3 (A) (B) (C).
Is a perspective view showing a third embodiment of the present invention together with its manufacturing process, FIG. 4 is a front view of the fourth embodiment of the present invention, and FIGS. 5 (A) and 5 (B) are the fifth embodiment of the present invention. 6 is a perspective view showing a manufacturing process of the guide shown in FIG. 5, and FIG. 7 is a perspective view of a sixth embodiment of the present invention.
FIG. 8 (A) is a perspective view of a conventional example, and FIG. 8 (B) is a front view thereof. (1) ... magnetic core, (2) (22) ... barium titanate-based ceramics, (4) (24) ... plastic molded body, (5) (8) ... conductive material, (6) ... … Shield electrode, (7) (27) …… Magnetic material, (11) …… Metal plate
───────────────────────────────────────────────────── フロントページの続き (72)発明者 河津 隆春 大阪府門真市大字門真1006番地 松下電器 産業株式会社内 (56)参考文献 特開 昭59−3743（ＪＰ，Ａ) ─────────────────────────────────────────────────── ─── Continuation of front page (72) Inventor Takaharu Kawazu 1006 Kadoma, Kadoma City, Osaka Prefecture Matsushita Electric Industrial Co., Ltd. (56) Reference JP-A-59-3743 (JP, A)
Claims (6)
磁性体を、記録媒体側の面を構成するチタン酸バリウム
系セラミックスと、記録媒体側には配置されずに補助ガ
イドの役割りを果たすプラスチック成型体とで構成した
ことを特徴とする磁気ヘッド。1. A non-magnetic material for guiding a magnetic core of a magnetic head main body, and a barium titanate-based ceramics constituting a surface on the recording medium side, and a non-magnetic member not disposed on the recording medium side, but serving as an auxiliary guide. A magnetic head comprising a molded plastic body.
支持する金属板と一体成型されていることを特徴とする
特許請求の範囲第１項記載の磁気ヘッド。2. The magnetic head according to claim 1, wherein the plastic molded body is integrally molded with a metal plate that supports the magnetic head body.
るための銀粉あるいはカーボンブラック等の導電性材料
が混入され、かつその表面にシールド電極が設けられて
いることを特徴とする特許請求の範囲第１項または第２
項記載の磁気ヘッド。3. A plastic molded body is mixed with a conductive material such as silver powder or carbon black for enhancing its conductivity, and a shield electrode is provided on the surface thereof. Item 1 or item 2
A magnetic head according to the item.
表層部にパーマロイ等の高透磁率の磁性体が一体成型さ
れていることを特徴とする特許請求の範囲第１項または
第２項記載の磁気ヘッド。4. The magnetic material according to claim 1 or 2, wherein the plastic molded body is integrally molded with a magnetic material having a high magnetic permeability such as permalloy inside or on the surface layer portion. head.
表層部に金属材料が一体成型されていることを特徴とす
る特許請求の範囲第１項または第２項記載の磁気ヘッ
ド。5. The magnetic head according to claim 1 or 2, wherein the plastic molded body is integrally molded with a metal material inside or on a surface layer portion thereof.
チック成型体との側面に銀あるいはカーボンブラック等
の導電性材料を塗布したことを特徴とする特許請求の範
囲第１項または第２項記載の磁気ヘッド。6. The magnetic head according to claim 1 or 2, wherein a conductive material such as silver or carbon black is applied to the side surfaces of the barium titanate-based ceramics and the plastic molded body. .